JP2680480B2 - Monolithic ceramic capacitors - Google Patents
Monolithic ceramic capacitorsInfo
- Publication number
- JP2680480B2 JP2680480B2 JP3009961A JP996191A JP2680480B2 JP 2680480 B2 JP2680480 B2 JP 2680480B2 JP 3009961 A JP3009961 A JP 3009961A JP 996191 A JP996191 A JP 996191A JP 2680480 B2 JP2680480 B2 JP 2680480B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- electrodes
- aluminum
- copper
- electrode
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION
【０００１】[0001]
【産業上の利用分野】本発明は、電極材料に改良を施し
た積層セラミックコンデンサに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a laminated ceramic capacitor having an improved electrode material.
【０００２】[0002]
【従来の技術】この種の積層セラミックコンデンサは、
平板状をなす複数の内部電極をセラミックを介して積層
して形成された積層チップと、該積層チップの対向壁に
付設された一対の外部電極とから構成されている。チッ
プ内の内部電極は交互に逆方向の外部電極に接続されて
おり、内部電極間で得られた所定の静電容量を外部電極
から取り出せるようになっている。2. Description of the Related Art A monolithic ceramic capacitor of this type is
It is composed of a laminated chip formed by laminating a plurality of flat plate-shaped internal electrodes via ceramics, and a pair of external electrodes attached to opposing walls of the laminated chip. The internal electrodes in the chip are alternately connected to the external electrodes in opposite directions so that a predetermined capacitance obtained between the internal electrodes can be taken out from the external electrodes.
【０００３】上記の内部電極及び外部電極は、耐熱性及
び耐食性の関係から一般に銀や銀−パラジウム等の銀合
金から形成されている。しかし、これら金属は電極とし
て優れた特性を有する反面、材料価格が高く、このため
コンデンサ自体のコストが高価になる欠点があり、とり
わけ全体コストの３０〜４０％が内部電極に依存してい
る。The internal electrodes and the external electrodes are generally formed of silver or a silver alloy such as silver-palladium in view of heat resistance and corrosion resistance. However, while these metals have excellent characteristics as electrodes, they have the drawback that the material cost is high and the cost of the capacitor itself is high, and in particular, 30 to 40% of the total cost depends on the internal electrodes.
【０００４】積層セラミックコンデンサに係わる価格的
な問題を解消するため、内部電極を安価な卑金属から形
成する試みもなされている。しかし、内部電極をニッケ
ル等の卑金属で形成した場合では、外部電極に銀または
銀合金を用いると両電極の馴染みが悪く、両電極に導通
不良を生じ易くなる欠点がある。In order to solve the price problem associated with the monolithic ceramic capacitor, attempts have been made to form the internal electrodes from an inexpensive base metal. However, when the internal electrodes are formed of a base metal such as nickel, if silver or a silver alloy is used for the external electrodes, there is a drawback that the two electrodes are not well-adapted to each other and a conduction failure easily occurs in both electrodes.
【０００５】電極相互の馴染みの問題を解消するものと
して、内部電極を卑金属から形成する一方、外部電極
を、内部電極と同一または合金化した金属で形成され、
且つ内部電極に接続される第１層と、銀または銀合金で
形成され、且つ該第１層の外面に付設される第２層とか
ら構成したものも提案されている（特開昭５９−１６３
２３号公報参照）。つまり、この積層セラミックコンデ
ンサでは、内部電極に接続される外部電極部分を内部電
極と同一系の金属から形成することで、両電極の馴染み
を向上させ導通の改善を図っている。In order to solve the problem of mutual familiarity between the electrodes, the internal electrodes are made of a base metal, while the external electrodes are made of the same or alloyed metal as the internal electrodes.
Also proposed is one comprising a first layer connected to the internal electrode and a second layer formed of silver or a silver alloy and attached to the outer surface of the first layer (JP-A-59-59). 163
No. 23). In other words, in this monolithic ceramic capacitor, the external electrode portion connected to the internal electrode is formed of the same metal as the internal electrode, so that the familiarity between both electrodes is improved and conduction is improved.
【０００６】[0006]
【発明が解決しようとする課題】しかしながら、上記の
積層セラミックコンデンサでは、内部電極と外部電極の
第１層との馴染みを向上できる反面、卑金属から成る第
１層と、銀または銀合金から成る第２層との馴染みが悪
いために、外部電極を構成する両層の境界部分に導通不
良を生じ、ｔａｎδが劣化したり、温度サイクルにより
静電容量抜けが発生する欠点がある。However, in the above-mentioned multilayer ceramic capacitor, the familiarity between the internal electrode and the first layer of the external electrode can be improved, while the first layer made of a base metal and the first layer made of silver or a silver alloy are used. Due to the poor compatibility with the two layers, there are disadvantages that conduction failure occurs at the boundary between the two layers forming the external electrode, tan δ is deteriorated, and capacitance loss occurs due to temperature cycle.
【０００７】本発明は上記問題点に鑑みてなされたもの
で、その目的とするところは、コンデンサ自体を安価に
形成できることは勿論のこと、外部電極の引張り強度を
維持しつつ、外部電極と内部電極の相互並びに外部電極
を構成する第１層と第２層との間に高い導通性を確保で
き、静電容量やｔａｎδ等の特性が劣化しない積層セラ
ミックコンデンサを提供することにある。The present invention has been made in view of the above problems, and it is an object of the present invention that the capacitor itself can be formed at low cost, and the tensile strength of the external electrode is maintained while the external electrode and the internal electrode are maintained. It is an object of the present invention to provide a monolithic ceramic capacitor which can secure high electrical conductivity between the electrodes and the first and second layers constituting the external electrodes, and which does not deteriorate characteristics such as capacitance and tan δ.
【０００８】[0008]
【課題を解決するための手段】上記目的を達成するた
め、請求項１の発明は、セラミックを介して積層された
複数の内部電極と、内部電極と所定の接続関係をもって
導通する一対の外部電極とを具備した積層セラミックコ
ンデンサにおいて、上記内部電極をニッケル，銅，鉛，
亜鉛，鉄，錫，アルミニウム，コバルト，クロムから選
択された卑金属の１種またはその合金から形成すると共
に、上記外部電極を、パラジウム，白金，ロジウム，イ
リジウム，オスミウム，ルテニウムから選択された白金
族金属の１種から成り内部電極に接続される第１層と、
ニッケル，銅，亜鉛，鉄，アルミニウム，コバルト，ク
ロムから選択された卑金属の１種またはその合金から成
り第１層の外面に付設された第２層とから形成した、こ
とをその特徴としている。In order to achieve the above-mentioned object, the invention of claim 1 provides a plurality of internal electrodes laminated via ceramics, and a pair of external electrodes which are electrically connected to the internal electrodes in a predetermined connection relationship. In the monolithic ceramic capacitor comprising:
A platinum group metal selected from one of base metals selected from zinc, iron, tin, aluminum, cobalt and chromium or an alloy thereof, and the external electrode is selected from palladium, platinum, rhodium, iridium, osmium and ruthenium. A first layer consisting of one of the following and connected to the internal electrode:
It is characterized in that it is formed from a second layer which is made of one of base metals selected from nickel, copper, zinc, iron, aluminum , cobalt and chromium or an alloy thereof and which is attached to the outer surface of the first layer.
【０００９】また、請求項２の発明は、セラミックを介
して積層された複数の内部電極と、内部電極と所定の接
続関係をもって導通する一対の外部電極とを具備した積
層セ ラミックコンデンサにおいて、上記内部電極をニッ
ケル，銅，鉛，亜鉛，鉄，錫，アルミニウム，コバル
ト，クロムから選択された卑金属の１種またはその合金
から形成すると共に、上記外部電極を、白金，ロジウ
ム，イリジウム，オスミウム，ルテニウムから選択され
た白金族金属の１種から成り内部電極に接続される第１
層と、ニッケル，銅，亜鉛，鉄，アルミニウム，コバル
ト，クロムから選択された卑金属の１種またはその合金
から成り第１層の外面に付設された第２層とから形成し
た、ことをその特徴としている。 According to the invention of claim 2, the ceramic is interposed.
Multiple internal electrodes that are stacked by
A product having a pair of external electrodes that conduct in a continuous relationship
In Sose la ceramic capacitor, Stevenage the internal electrodes
Kell, copper, lead, zinc, iron, tin, aluminum, kobar
One of the base metals selected from aluminum and chromium or its alloys
The external electrode is made of platinum,
Selected from aluminum, iridium, osmium, and ruthenium
A platinum group metal that is connected to the internal electrode
Layers and nickel, copper, zinc, iron, aluminum, kovar
One of the base metals selected from aluminum and chromium or its alloys
And a second layer attached to the outer surface of the first layer
It is characterized by
【００１０】[0010]
【作用】請求項１の発明に係る積層セラミックコンデン
サでは、外部電極の第１層が、内部電極を形成するニッ
ケル，銅，鉛，亜鉛，鉄，錫，アルミニウム，コバル
ト，クロムから選択された卑金属の１種またはその合金
と馴染みのよいパラジウム，白金，ロジウム，イリジウ
ム，オスミウム，ルテニウムから選択された白金族金属
の１種から形成されているので、両者の境界部分に高い
導通性を確保できる。また、外部電極の第２層が、第１
層を形成するパラジウム，白金，ロジウム，イリジウ
ム，オスミウム，ルテニウムから選択された白金族金属
の１種と馴染みのよいニッケル，銅，亜鉛，鉄，アルミ
ニウム，コバルト，クロムから選択された卑金属の１種
またはその合金から形成されているので、両者の境界部
分に高い導通性を確保できる。In the monolithic ceramic capacitor according to the first aspect of the present invention, the first layer of the external electrode is a base metal selected from nickel, copper, lead, zinc, iron, tin, aluminum, cobalt and chromium forming the internal electrode. Of the platinum group metal selected from palladium, platinum, rhodium, iridium, osmium, and ruthenium, which are well-known to the above alloys and their alloys, so high conductivity can be secured at the boundary between the two. Also, the second layer of the external electrode is the first
One of the platinum group metals selected from palladium, platinum, rhodium, iridium, osmium, and ruthenium forming a layer and nickel, copper, zinc, iron, and aluminum that are familiar
Since it is formed from one of the base metals selected from the group consisting of nickel, cobalt and chromium, or an alloy thereof, high conductivity can be secured at the boundary between the two.
【００１１】また、請求項２の発明に係る積層セラミッ
クコンデンサでは、外部電極の第１層が、内部電極を形
成するニッケル，銅，鉛，亜鉛，鉄，錫，アルミニウ
ム，コバルト，クロムから選択された卑金属の１種また
はその合金と馴染みのよい白金，ロジウム，イリジウ
ム，オスミウム，ルテニウムから選択された白金族金属
の１種から形成されているので、両者の境界部分に高い
導通性を確保できる。また、外部電極の第２層が、第１
層を形成する白金，ロジウム，イリジウム，オスミウ
ム，ルテニウムから選択された白金族金属の１種と馴染
みのよいニッケル，銅，亜鉛，鉄，アルミニウム，コバ
ルト，クロムから選択された卑金属の１種またはその合
金から形成されているので、両者の境界部分に高い導通
性を確保できる 。 The laminated ceramic according to the invention of claim 2
In a condenser, the first layer of the outer electrode forms the inner electrode.
Nickel, copper, lead, zinc, iron, tin, aluminum
One of the base metals selected from aluminum, cobalt, and chromium
Is platinum, rhodium, and iridium that are familiar with the alloy
Platinum group metal selected from aluminum, osmium and ruthenium
Since it is formed from one type, it is high at the boundary between both
The conductivity can be secured. Also, the second layer of the external electrode is the first
Layer-forming platinum, rhodium, iridium, osmiu
Familiar with one of the platinum group metals selected from Ru and Ru
Fine nickel, copper, zinc, iron, aluminum, edge
One or a combination of base metals selected from Ruth and Chromium
Since it is made of gold, it has high conductivity at the boundary between the two.
You can secure the sex .
【００１２】[0012]
【実施例】図１は本発明を適用した積層セラミックコン
デンサの断面図である。1 is a sectional view of a monolithic ceramic capacitor to which the present invention is applied.
【００１３】この積層セラミックコンデンサは、平板状
をなす複数（図中は５枚）の内部電極１をセラミック２
を介して積層して形成された角形の積層チップ３と、該
積層チップ３の内部電極方向の対向壁に付設された一対
の外部電極４とから構成されている。In this monolithic ceramic capacitor, a plurality of (five in the figure) internal electrodes 1 having a flat plate shape are connected to a ceramic 2
It is composed of a rectangular multilayer chip 3 formed by stacking via a via, and a pair of external electrodes 4 attached to opposing walls in the internal electrode direction of the multilayer chip 3.
【００１４】上記内部電極１は間隔をおいて交互に位置
をずらせて平行に配置されており、その内の３枚の端縁
を図中右側の対向壁から露出し、また２枚の端縁を図中
左側の対向壁から露出している。The internal electrodes 1 are arranged parallel to each other with a space therebetween, and the three edges thereof are exposed from the facing wall on the right side in the drawing, and the two edges are also exposed. Is exposed from the opposing wall on the left side in the figure.
【００１５】この内部電極１は、ニッケル，銅，鉛，亜
鉛，鉄，錫，アルミニウム，コバルト，クロムから選択
される卑金属の１種またはその合金から成り、好ましく
はニッケル，銅，鉛及びこれらの合金が使用される。[0015] Selection The inner electrode 1 is nickel, copper, lead, zinc, iron, tin, aluminum, cobalt, chromium
One of the base metals mentioned above or an alloy thereof, preferably nickel, copper, lead and their alloys are used.
【００１６】上記各外部電極４は、積層チップ３の壁面
にその周縁に及んで付設された第１層４ａと、該第１層
４ａの外面を覆うようにして付設された第２層４ｂとか
ら構成されている。各外部電極４の第１層４ａは夫々の
対向壁から露出する内部電極１の端縁に接合している。Each of the external electrodes 4 has a first layer 4a attached to the wall surface of the laminated chip 3 so as to extend to the periphery thereof, and a second layer 4b attached so as to cover the outer surface of the first layer 4a. It consists of The first layer 4a of each outer electrode 4 is joined to the edge of the inner electrode 1 exposed from the respective opposing wall.
【００１７】この外部電極４の第１層４ａは、パラジウ
ム，白金，ロジウム，イリジウム，オスミウム，ルテニ
ウムから選択される白金族金属の１種から成り、好まし
くはパラジウム，白金が使用される。The first layer 4a of the external electrode 4 is made of one of platinum group metals selected from palladium, platinum, rhodium, iridium, osmium and ruthenium, and preferably palladium or platinum is used.
【００１８】また、外部電極４の第２層４ｂは、ニッケ
ル，銅，亜鉛，鉄，アルミニウム，コバルト，クロムか
ら選択される卑金属の１種またはその合金から成る。 The second layer 4b of the external electrode 4 is made of nickel.
Le, copper, zinc, iron, aluminum, cobalt, chrome
It is composed of one of the base metals selected from the above or an alloy thereof.
【００１９】以下に、本発明に係る積層セラミックコン
デンサの好適な具体例をその製造方法を交えて説明す
る。A preferred specific example of the monolithic ceramic capacitor according to the present invention will be described below together with its manufacturing method.
【００２０】まず、非還元性のセラミック組成物から成
る厚さ１０〜６０μｍのセラミックシ−トの一面に、内
部電極となるニッケル粉末のペ−ストを数μｍの厚み
で、しかも多数の長方形が規則的に並ぶようにして印刷
する。First, a surface of a ceramic sheet made of a non-reducing ceramic composition and having a thickness of 10 to 60 μm is coated with a paste of nickel powder as an internal electrode to a thickness of several μm and a large number of rectangles. Print in regular rows.
【００２１】次に、印刷後のセラミックシ−トを１枚宛
平面方向に位置をずらして２０〜１００枚積層し、これ
を積層方向に所定の大きさで切断してチップ材を形成す
る。切断されたチップ材の対向壁には内部電極となるニ
ッケル層が露出する。Next, 20 to 100 sheets of the printed ceramic sheet are displaced in the plane direction to one sheet, and the sheets are cut in a predetermined size in the stacking direction to form a chip material. A nickel layer which will be an internal electrode is exposed on the opposing wall of the cut chip material.
【００２２】次に、このチップ材のニッケル層が露出す
る対向壁夫々に、外部電極の第１層となるパラジウム粉
末のペ−ストを数μｍ〜数十μｍの厚みをもって塗布す
る。Next, a paste of palladium powder to be the first layer of the external electrode is applied to each of the facing walls of the chip material where the nickel layer is exposed with a thickness of several μm to several tens of μm.
【００２３】次に、ペ−スト塗布後のチップ材を中性ま
たは還元性雰囲気中で１３００℃程度の温度で焼成す
る。この焼成によってセラミック焼成体が得られると同
時に、内部電極と外部電極第１層のペ−ストの焼付けが
行なわれる。Next, the chip material after applying the paste is fired at a temperature of about 1300 ° C. in a neutral or reducing atmosphere. By this firing, a fired ceramic body is obtained, and at the same time, the paste of the inner electrode and the outer electrode first layer is fired.
【００２４】次に、外部電極の第１層の外面に外部電極
の第２層となる銅粉末のペ−ストを第１層と同程度の厚
みをもって塗布する。Next, a paste of copper powder to be the second layer of the external electrode is applied to the outer surface of the first layer of the external electrode with the same thickness as the first layer.
【００２５】次に、ペ−スト塗布後のチップ材を中性ま
たは還元性雰囲気中で８００℃程度の温度で焼成する。
この焼成によって外部電極第２層のペ−ストの焼付けが
行なわれる。Next, the chip material coated with the paste is fired at a temperature of about 800 ° C. in a neutral or reducing atmosphere.
The baking of the external electrode second layer is performed by this baking.
【００２６】以上で、内部電極１がニッケルから成り、
また外部電極４の第１層４ａがパラジウムで第２層４ｂ
が銅から成る、図１に示すような積層セラミックコンデ
ンサが製造される。As described above, the internal electrode 1 is made of nickel,
In addition, the first layer 4a of the external electrode 4 is palladium and the second layer 4b is
A monolithic ceramic capacitor as shown in FIG.
【００２７】上記の積層セラミックコンデンサでは、外
部電極４の第１層４ａが、内部電極１を形成するニッケ
ルと馴染みのよいパラジウムから形成されているので、
両者の境界部分に高い導通性を確保できる。また、外部
電極４の第２層４ｂが、第１層４ａを形成するパラジウ
ムと馴染みのよい銅から形成されているので、両者の境
界部分に高い導通性を確保できる。In the above-mentioned laminated ceramic capacitor, the first layer 4a of the external electrode 4 is formed of nickel which forms the internal electrode 1 and palladium which is well-suited.
High conductivity can be secured at the boundary between the two. Further, since the second layer 4b of the external electrode 4 is formed of copper that is well compatible with palladium forming the first layer 4a, high conductivity can be secured at the boundary between the two.
【００２８】因みに、先に述べた方法に従って、内部電
極がニッケルで外部電極の第１層がパラジウムで第２層
が銅から成り、長さ，幅及び高さが３．２ｍｍ，１．６
ｍｍ，１．２５ｍｍで設計容量が１．０μＦのＦ特性積
層セラミックコンデンサ（発明品）と、内部電極及び外
部電極の第１層がニッケルで第２層が銀から成り、同寸
法で同容量のＦ特性積層セラミックコンデンサ（従来
品）とを夫々１００個宛製造し、製品中で容量が０．９
μＦ以下のものとｔａｎδが５％以上のものの個数を調
べると共に、各々の製品にＪＩＳ Ｃ５１０２で定めら
れる温度サイクル試験を行なってから同個数を調べたと
ころ、発明品では温度サイクル試験の前後で不良品の発
生が全く見られなかったのに対し、従来品では温度サイ
クル試験後に容量０．９μＦ以下のものが３個、ｔａｎ
δ５％以上のものが８個現われた。By the way, according to the method described above, the inner electrode is made of nickel, the first layer of the outer electrode is made of palladium, and the second layer is made of copper, and the length, width and height are 3.2 mm and 1.6 mm.
mm, 1.25 mm, F-capacitance multilayer ceramic capacitor with a design capacity of 1.0 μF (invention product), and the first and inner electrodes of the internal and external electrodes are made of nickel and the second layer is made of silver. 100 F-type monolithic ceramic capacitors (conventional product) are manufactured, each with a capacity of 0.9.
The number of μF or less and tan δ of 5% or more were checked, and the same number was checked after each product was subjected to the temperature cycle test specified by JIS C5102. While no good products were found, the conventional products had 3 with a capacity of 0.9 μF or less after the temperature cycle test.
Eight of the samples with δ5% or more appeared.
【００２９】尚、内部電極としてニッケル以外に先に列
挙した卑金属の１種またはその合金を用いる場合や、外
部電極の第１層としてパラジウム以外に先に列挙した白
金族金属の１種を用いる場合や、外部電極の第２層とし
て銅以外に先に列挙した卑金属の１種またはその合金を
用いる場合も上記と同様の製造方法で積層セラミックコ
ンデンサを得ることができ、しかも同様の効果を得るこ
とができる。In addition to nickel, the internal electrodes are first
When one of the base metals listed above or an alloy thereof is used, when one of the white-gold group metals listed above other than palladium is used as the first layer of the external electrode, or when the second layer of the external electrode is used. Also , when one of the base metals listed above or an alloy thereof other than copper is used as the above, a laminated ceramic capacitor can be obtained by the same manufacturing method as described above, and the same effect can be obtained.
【００３０】[0030]
【発明の効果】以上詳述したように、本発明によれば、
内部電極の材料価格を抑えてコンデンサ自体を安価に形
成できることに加え、外部電極と内部電極の相互並びに
外部電極を構成する第１層と第２層との間に高い導通性
と引張り強度を確保して、静電容量やｔａｎδ等の特性
劣化を防止できる。As described in detail above, according to the present invention,
In addition to being able to form the capacitor itself at low cost by suppressing the material cost of the internal electrodes, it also ensures high electrical conductivity and tensile strength between the external electrodes and the internal electrodes and between the first and second layers forming the external electrodes. As a result, it is possible to prevent characteristic deterioration such as capacitance and tan δ.
【図面の簡単な説明】[Brief description of the drawings]
【図１】本発明を適用した積層セラミックコンデンサの
断面図FIG. 1 is a sectional view of a monolithic ceramic capacitor to which the present invention is applied.
１…内部電極、２…セラミック、３…積層チップ、４…
外部電極、４ａ…第１層、４ｂ…第２層。1 ... Internal electrode, 2 ... Ceramic, 3 ... Layered chip, 4 ...
External electrodes, 4a ... 1st layer, 4b ... 2nd layer.
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平２−206108（ＪＰ，Ａ) 特開 昭57−148331（ＪＰ，Ａ) 特開 昭59−16323（ＪＰ，Ａ) 特開 平２−150010（ＪＰ，Ａ) 特開 平２−150008（ＪＰ，Ａ) ─────────────────────────────────────────────────── ─── Continuation of the front page (56) Reference JP-A-2-206108 (JP, A) JP-A-57-148331 (JP, A) JP-A-59-16323 (JP, A) JP-A-2- 150010 (JP, A) JP-A-2-150008 (JP, A)
Claims (2)
部電極と、内部電極と所定の接続関係をもって導通する
一対の外部電極とを具備した積層セラミックコンデンサ
において、 上記内部電極をニッケル，銅，鉛，亜鉛，鉄，錫，アル
ミニウム，コバルト，クロムから選択された卑金属の１
種またはその合金から形成すると共に、 上記外部電極を、パラジウム，白金，ロジウム，イリジ
ウム，オスミウム，ルテニウムから選択された白金族金
属の１種から成り内部電極に接続される第１層と、ニッ
ケル，銅，亜鉛，鉄，アルミニウム，コバルト，クロム
から選択された卑金属の１種またはその合金から成り第
１層の外面に付設された第２層とから形成した、 ことを特徴とする積層セラミックコンデンサ。1. A monolithic ceramic capacitor comprising a plurality of internal electrodes laminated via ceramics, and a pair of external electrodes conducting with a predetermined connection relationship with the internal electrodes, wherein the internal electrodes are made of nickel, copper or lead. , One of the base metals selected from zinc, iron, tin, aluminum, cobalt and chromium
A first layer formed of a seed or an alloy thereof and having the external electrode connected to the internal electrode, the first layer being made of one of platinum group metals selected from palladium, platinum, rhodium, iridium, osmium and ruthenium; A monolithic ceramic capacitor, characterized in that it is formed from one base metal selected from copper, zinc, iron, aluminum , cobalt and chromium or an alloy thereof, and a second layer attached to the outer surface of the first layer.
部電極と、内部電極と所定の接続関係をもって導通するConducts electrical connection with the internal electrode and the internal electrode with a specified connection
一対の外部電極とを具備した積層セラミックコンデンサMultilayer ceramic capacitor having a pair of external electrodes
において、At 上記内部電極をニッケル，銅，鉛，亜鉛，鉄，錫，アルThe internal electrodes are nickel, copper, lead, zinc, iron, tin, aluminum
ミニウム，コバルト，クロムから選択された卑金属の１One of base metals selected from minium, cobalt and chromium
種またはその合金から形成すると共に、Formed from seeds or their alloys, 上記外部電極を、白金，ロジウム，イリジウム，オスミThe external electrodes are platinum, rhodium, iridium, osmi
ウム，ルテニウムから選択された白金族金属の１種からFrom one of the platinum group metals selected from um and ruthenium
成り内部電極に接続される第１層と、ニッケル，銅，亜The first layer connected to the internal electrode, nickel, copper,
鉛，鉄，アルミニウム，コバルト，クロムから選択されSelected from lead, iron, aluminum, cobalt, chrome
た卑金属の１種またはその合金から成り第１層の外面にOn the outer surface of the first layer consisting of one of the base metals or its alloys
付設された第２層とから形成した、Formed from the attached second layer, ことを特徴とする積層セラミックコンデンサ。A multilayer ceramic capacitor characterized by the above.