JP2023033350A - Decorative sheet - Google Patents

Decorative sheet Download PDF

Info

Publication number
JP2023033350A
JP2023033350A JP2022211252A JP2022211252A JP2023033350A JP 2023033350 A JP2023033350 A JP 2023033350A JP 2022211252 A JP2022211252 A JP 2022211252A JP 2022211252 A JP2022211252 A JP 2022211252A JP 2023033350 A JP2023033350 A JP 2023033350A
Authority
JP
Japan
Prior art keywords
layer
resin
mass
decorative sheet
recycled
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2022211252A
Other languages
Japanese (ja)
Other versions
JP7386311B2 (en
Inventor
純 金子
Jun Kaneko
慎太郎 伊藤
Shintaro Ito
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Takiron Co Ltd
Original Assignee
Takiron Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Takiron Co Ltd filed Critical Takiron Co Ltd
Priority to JP2022211252A priority Critical patent/JP7386311B2/en
Publication of JP2023033350A publication Critical patent/JP2023033350A/en
Application granted granted Critical
Publication of JP7386311B2 publication Critical patent/JP7386311B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide a decorative sheet capable of enhancing content percentage of a recycled resin, high in brightness, less in unevenness of color tone, capable of suppressing reduction of strength or reduction of surface appearance, and further capable of suppressing reduction of adhesiveness.
SOLUTION: A decorative sheet has a first resin component containing a first layer containing a recycled PET-based resin derived from a PET bottle of 70 mass% or more, and a white pigment, a second layer having a second resin component arranged by layering in one surface side of the first layer, and containing a virgin resin of 70 mass% or more, and the white pigment, and having a thickness in a range of 25 μm to 75 μm, and a third resin composition arranged by layering in another surface side of the first layer and containing the virgin resin of 80 mass% or more, in which the white pigment is 5 pts.mass or less based on 100 pts.mass of the third resin component.
SELECTED DRAWING: Figure 1
COPYRIGHT: (C)2023,JPO&INPIT

Description

本発明は、化粧シートに関する。 The present invention relates to a decorative sheet.

壁材、床材、建具（扉、戸等）、家具、シンク台、洗面化粧台等の表層に用いられる化粧シートとしては、かつてはポリ塩化ビニルシートが主流であった。近年、環境問題への関心の高まりから、化粧シートとしては、ポリエチレン等のポリオレフィンを主体とするシートやポリエチレンテレフタレート（以下、「ＰＥＴ」とも記す。）等のポリエステルを主体とするシートが主流となっている。また、廃プラスチックからなる再生樹脂を用いた化粧シートの開発が強く要望されている。
しかし、再生樹脂は様々な色に着色されたものが多く、再生樹脂を用いた化粧シートは、色にバラツキが生じやすい。 BACKGROUND ART In the past, polyvinyl chloride sheets were the mainstream as decorative sheets used for surface layers of wall materials, floor materials, fittings (doors, doors, etc.), furniture, sink stands, bathroom vanities, and the like. In recent years, due to growing interest in environmental issues, sheets mainly made of polyolefin such as polyethylene and sheets mainly made of polyester such as polyethylene terephthalate (hereinafter also referred to as "PET") have become mainstream decorative sheets. ing. There is also a strong demand for the development of decorative sheets using recycled resins made from waste plastics.
However, many recycled resins are colored in various colors, and decorative sheets using recycled resins tend to have color variations.

再生樹脂を用い、かつ色のバラツキが抑えられた化粧シートとしては、下記のものが提案されている。
（１）再生ポリ塩化ビニルシートと、着色層を有する新生ポリ塩化ビニルシートとをラミネートした化粧シート（特許文献１を参照）。
（２）再生ポリエステル３～７０質量％とバージンポリエステル３０～９７質量％とからなるポリエステルに対して、着色顔料を０．１～３０質量％含む化粧シート（特許文献２を参照）。
しかし、（１）、（２）の化粧シートは、色のバラツキを抑えるため、バージン樹脂（新生樹脂）原料の割合を多くする必要があり、再生樹脂の割合が低い。 The following are proposed as a decorative sheet that uses recycled resin and suppresses color variation.
(1) A decorative sheet obtained by laminating a recycled polyvinyl chloride sheet and a new polyvinyl chloride sheet having a colored layer (see Patent Document 1).
(2) A decorative sheet containing 0.1 to 30% by mass of a coloring pigment with respect to polyester composed of 3 to 70% by mass of recycled polyester and 30 to 97% by mass of virgin polyester (see Patent Document 2).
However, the decorative sheets of (1) and (2) require a large proportion of virgin resin (new resin) raw materials in order to suppress variations in color, and the proportion of recycled resin is low.

再生樹脂の割合の高いシートとしては、下記のものが提案されている。
（３）再生ＰＥＴ／再生ポリエチレン／相溶化剤／青色顔料＝８５／１５／５／１質量比の樹脂層（化粧シートに相当）が鋼板の表面にラミネートされた化粧板（特許文献３の段落［０１４８］を参照）。
（４）再生ＰＥＴ１００質量部に、特定の結合材３～１０質量部、および酸化チタンからなる改質剤２～５質量部を配合した再生プラスチックシート（特許文献４を参照）。 The following sheets have been proposed as sheets with a high percentage of recycled resin.
(3) Recycled PET/recycled polyethylene/compatibilizer/blue pigment=85/15/5/1 resin layer (equivalent to decorative sheet) laminated on the surface of a steel plate (paragraph of Patent Document 3) See [0148]).
(4) A recycled plastic sheet in which 3 to 10 parts by mass of a specific binder and 2 to 5 parts by mass of a modifier consisting of titanium oxide are mixed with 100 parts by mass of recycled PET (see Patent Document 4).

特開昭５６－０８０４１７号公報JP-A-56-080417 特開平１１－１３０８７７号公報JP-A-11-130877 特開２００９－０３００６２号公報Japanese Patent Application Laid-Open No. 2009-030062 特開２００２－３４８４４８号公報JP-A-2002-348448

特許文献３に開示された化粧板における樹脂層は、再生樹脂による色のバラツキを抑えるため、青色に着色されている。このため、特許文献３の化粧板における樹脂層のような配合の場合は、再生樹脂による色のバラツキが判別しにくい濃い青色、黒色、灰色等の明度の低い色に限定されてしまい、白色、淡色等の明度の高い色の採用が困難である。 The resin layer in the decorative board disclosed in Patent Document 3 is colored blue in order to suppress color variations due to the recycled resin. For this reason, in the case of a formulation such as the resin layer in the decorative board of Patent Document 3, it is limited to colors with low brightness such as dark blue, black, and gray, in which color variations due to recycled resin are difficult to distinguish. It is difficult to adopt a color with high lightness such as a light color.

また、特許文献４に開示された再生プラスチックシートは、冷却塔用充填材として用いることを前提としており、酸化チタンは、耐候性を付与するための改質剤として少量添加されている。こうした酸化チタンの含有量が少ない再生プラスチックシートも、化粧シートとして利用する場合、明度が低くなるために白色、淡色等の明度の高い色を採用できない。また、シートの向こう側が透けてしまい、化粧シートとしての隠蔽性が不十分である。また、原料ロット間やシートの場所ごとの色のバラツキが大きく、均一な色調にすることが困難である。 Further, the recycled plastic sheet disclosed in Patent Document 4 is premised on being used as a cooling tower filler, and a small amount of titanium oxide is added as a modifier for imparting weather resistance. Such a recycled plastic sheet with a low content of titanium oxide also has a low brightness when used as a decorative sheet, so that high brightness colors such as white and pale colors cannot be used. In addition, the opposite side of the sheet is transparent, and the concealability as a decorative sheet is insufficient. In addition, there is a large variation in color between raw material lots and between locations on the sheet, making it difficult to achieve a uniform color tone.

さらに、特許文献３や特許文献４に開示されたような、再生樹脂の含有割合を高めた化粧板や再生プラスチックシートは、再生樹脂原料に含まれる微細な異物や不純物が溶剤や薬品（酸・塩基）に曝された時にクラックの起点となりやすく、化粧シートの美観や強度を低下させる原因となっていた。 Furthermore, decorative panels and recycled plastic sheets with a high content of recycled resin, such as those disclosed in Patent Documents 3 and 4, contain fine foreign matter and impurities contained in the recycled resin raw material, and solvents and chemicals (acids, When exposed to a base), it tends to be the starting point of cracks, which causes deterioration of the appearance and strength of the decorative sheet.

また、特許文献３や特許文献４に開示されたような、再生樹脂の含有割合を高めた化粧板や再生プラスチックシートは、再生樹脂が壁面に対する接着性を低下させる原因となっていた。 In addition, decorative sheets and recycled plastic sheets with a high content of recycled resin, such as those disclosed in Patent Documents 3 and 4, cause the recycled resin to lower the adhesiveness to the wall surface.

本発明は、前述した事情に鑑みてなされたものであって、再生樹脂の含有割合を高めることが可能であり、かつ明度が高く、色調のムラが少なく、強度低下や表面の美観の低下を抑制可能であり、更に接着性の低下を防止することが可能な化粧シートを提供する。 The present invention has been made in view of the above-mentioned circumstances. To provide a decorative sheet capable of suppressing and further preventing deterioration of adhesiveness.

本発明は、下記の態様を有する。
＜１＞ＰＥＴボトルに由来する再生ＰＥＴ系樹脂を７０質量％以上含む第１樹脂成分、および白色系顔料を含む第１層と、前記第１層の一面側に重ねて配され、バージン樹脂を７０質量％以上含む第２樹脂成分、および白色系顔料を有し、厚みが２５μｍ以上、７５μｍ以下の範囲である第２層と、前記第１層の他面側に重ねて配され、バージン樹脂を８０質量％以上含む第３樹脂成分を有し、白色系顔料が前記第３樹脂成分１００質量部に対して５質量部以下であることを特徴とする化粧シート。
＜２＞前記第１層に含まれる白色系顔料は、前記第１樹脂成分１００質量部に対して５質量部以上、１５質量部以下の範囲であり、前記第２層に含まれる白色系顔料は、前記第２樹脂成分１００質量部に対して、５質量部以上、１５質量部以下の範囲であることを特徴とする＜１＞記載の化粧シート。
＜３＞前記第２樹脂成分には、前記再生ＰＥＴ系樹脂を３０質量％以下の範囲で更に含むことを特徴とする＜１＞または＜２＞記載の化粧シート。
＜４＞前記第３樹脂成分は、前記再生ＰＥＴ系樹脂を５質量％以下の範囲で更に含むことを特徴とする＜１＞ないし＜３＞いずれか記載の化粧シート。
＜５＞前記第２層の表面側において、ＣＩＥ １９７６ Ｌ＊ａ＊ｂ＊色空間におけるＬ＊が９２以上であることを特徴とする＜１＞ないし＜４＞いずれか記載の化粧シート。 The present invention has the following aspects.
<1> A first resin component containing 70% by mass or more of a recycled PET resin derived from a PET bottle and a first layer containing a white pigment are superimposed on one side of the first layer, and a virgin resin is added. A second layer having a second resin component containing 70% by mass or more and a white pigment and having a thickness in the range of 25 μm or more and 75 μm or less, and a virgin resin disposed on the other surface side of the first layer and a white pigment in an amount of 5 parts by mass or less per 100 parts by mass of the third resin component.
<2> The white pigment contained in the first layer is in the range of 5 parts by mass or more and 15 parts by mass or less with respect to 100 parts by mass of the first resin component, and the white pigment contained in the second layer is in the range of 5 parts by mass or more and 15 parts by mass or less with respect to 100 parts by mass of the second resin component.
<3> The decorative sheet according to <1> or <2>, wherein the second resin component further contains the recycled PET resin in an amount of 30% by mass or less.
<4> The decorative sheet according to any one of <1> to <3>, wherein the third resin component further contains the recycled PET resin in an amount of 5% by mass or less.
<5> The decorative sheet according to any one of <1> to <4>, wherein L* in the CIE 1976 L*a*b* color space is 92 or more on the surface side of the second layer.

本発明によれば、再生樹脂の含有割合を高めることが可能であり、かつ明度が高く、色調のムラが少なく、強度低下や表面の美観の低下を抑制可能であり、更に、接着性の低下を防止することが可能な化粧シートを提供することができる。 According to the present invention, it is possible to increase the content of the recycled resin, have high brightness, have little unevenness in color tone, can suppress deterioration in strength and appearance of the surface, and furthermore, has a decrease in adhesiveness. It is possible to provide a decorative sheet capable of preventing

本発明の一実施形態の化粧シートの層構成を示す断面図である。1 is a cross-sectional view showing the layer structure of a decorative sheet according to one embodiment of the present invention; FIG.

以下の用語の定義は、本明細書及び特許請求の範囲にわたって適用される。
「Ｌ＊」は、ＪＩＳ Ｚ ８７８１－４：２０１３「測色－第４部：ＣＩＥ １９７６
Ｌ＊ａ＊ｂ＊色空間」（対応国際規格ＩＳＯ １１６６４－４：２００８）に定義される明度の相関量である。
「ａ＊」および「ｂ＊」は、ＪＩＳ Ｚ ８７８１－４：２０１３「測色－第４部：ＣＩＥ １９７６ Ｌ＊ａ＊ｂ＊色空間」（対応国際規格ＩＳＯ １１６６４－４：２００８）に定義される色座標である。
数値範囲を示す「～」は、その前後に記載された数値を下限値及び上限値として含むことを意味する。 The following term definitions apply throughout the specification and claims.
"L*" is JIS Z 8781-4: 2013 "Colorimetry - Part 4: CIE 1976
L*a*b* color space” (corresponding international standard ISO 11664-4:2008).
"a*" and "b*" are defined in JIS Z 8781-4:2013 "Colorimetry - Part 4: CIE 1976 L*a*b* color space" (corresponding international standard ISO 11664-4:2008) are the color coordinates to be used.
"~" indicating a numerical range means that the numerical values before and after it are included as lower and upper limits.

以下、本発明の一実施形態の化粧シートについて説明する。なお、以下に示す実施形態は、発明の趣旨をより良く理解させるために具体的に説明するものであり、特に指定のない限り、本発明を限定するものではない。 A decorative sheet according to one embodiment of the present invention will be described below. It should be noted that the embodiments shown below are specifically described for better understanding of the gist of the invention, and do not limit the invention unless otherwise specified.

＜化粧シート＞
図１は、本発明の一実施形態の化粧シートの層構成を示す断面図である。
本実施形態の化粧シート１０は、第１層１１と、この第１層１１の一面１１ａ側に重ねて形成された第２層１２と、第１層１１の他面１１ｂ側に重ねて形成された第３層１３とを有する複層構成とされている。この実施形態では、化粧シート１０は、第３層１３側が、例えは接着層１４を介して壁面Ｗに取り付けられ、第２層１２側が外部に露呈される。 <Decorative sheet>
FIG. 1 is a cross-sectional view showing the layer structure of a decorative sheet according to one embodiment of the present invention.
The decorative sheet 10 of this embodiment includes a first layer 11, a second layer 12 formed over one surface 11a of the first layer 11, and a second layer 12 overlaid on the other surface 11b of the first layer 11. It has a multi-layer structure including a third layer 13. In this embodiment, the third layer 13 side of the decorative sheet 10 is attached to the wall surface W via, for example, an adhesive layer 14, and the second layer 12 side is exposed to the outside.

（第１層）
第１層１１は、ＰＥＴボトルに由来する再生ＰＥＴ系樹脂を７０質量％以上含む第１樹脂成分と、白色系顔料とを少なくとも含んでいる。なお、第１層１１は、本発明の効果を損なわない範囲において、必要に応じて第１樹脂成分および白色顔料以外の成分（以下、「他の成分（第１層）」とも記す。）を含んでいてもよい。 (first layer)
The first layer 11 contains at least a first resin component containing 70% by mass or more of recycled PET resin derived from PET bottles, and a white pigment. The first layer 11 may contain components other than the first resin component and the white pigment (hereinafter also referred to as "other components (first layer)") as necessary, as long as the effects of the present invention are not impaired. may contain.

「第１樹脂成分（第１層）」
第１樹脂成分は、ＰＥＴボトルに由来する再生ＰＥＴ系樹脂を７０質量％以上含んでいる。また、第１樹脂成分は、再生ＰＥＴ系樹脂以外の樹脂（以下、「他の樹脂（第１層）」とも記す。）を例えば３０質量％以下、好ましくは１０質量％以下の範囲で含んでいてもよい。 "First resin component (first layer)"
The first resin component contains 70% by mass or more of recycled PET resin derived from PET bottles. In addition, the first resin component contains a resin other than the recycled PET-based resin (hereinafter also referred to as "another resin (first layer)") in an amount of, for example, 30% by mass or less, preferably 10% by mass or less. You can

また、化粧シート１０全体の質量に対して、再生ＰＥＴ系樹脂は２５質量％以上含まれていることも好ましい。再生ＰＥＴ系樹脂が２５質量％未満では、後述する第２層１２に含まれるバージン樹脂の割合が相対的に多くなり、環境対策として再生ＰＥＴ系樹脂を使用する意義が低下する。 Moreover, it is also preferable that the recycled PET-based resin is contained in an amount of 25% by mass or more with respect to the mass of the entire decorative sheet 10 . If the recycled PET-based resin is less than 25% by mass, the ratio of the virgin resin contained in the second layer 12, which will be described later, becomes relatively large, and the significance of using the recycled PET-based resin as an environmental measure decreases.

再生ＰＥＴ系樹脂は、ＰＥＴボトルに由来する再生樹脂であり、安価でかつ入手しやすい点から、ＰＥＴボトルの粉砕物が好ましい。再生ＰＥＴ系樹脂は、本発明の効果を損なわない範囲において、ＰＥＴボトルに付属していたラベル（印刷・接着剤等を含む）、キャップ等の粉砕物を含んでいてもよい。 The recycled PET-based resin is a recycled resin derived from PET bottles, and pulverized PET bottles are preferable because they are inexpensive and readily available. The recycled PET-based resin may contain pulverized materials such as labels attached to PET bottles (including printing, adhesives, etc.) and caps, as long as the effects of the present invention are not impaired.

例えば、日本国においては、再利用品の品質低下を防ぐために、以下に説明する自主設計ガイドラインに、指定ＰＥＴボトルについては、ＰＥＴ単体（ＰＥＴ主材以外の物質を添加、複合等をして用いていない。）と定められ、着色はしない（口栓部の結晶化による白色は除く。）と定められている。したがって、現在、日本国内では着色ＰＥＴボトルは生産されておらず、海外で生産される日本国向けの着色ＰＥＴボトルについても無着色ＰＥＴボトルへの変更が要請されている（ｈｔｔｐ：／／ｗｗｗ．ｐｅｔｂｏｔｔｌｅ－ｒｅｃ．ｇｒ．ｊｐ／ｑａｎｄａ／ｓｅｃ１３．ｈｔｍｌ）。 For example, in Japan, in order to prevent the quality of recycled products from deteriorating, the voluntary design guidelines explained below stipulate that PET alone (substances other than PET as the main material are added, compounded, etc.) for designated PET bottles. not colored), and not to be colored (excluding white color due to crystallization of the mouth plug). Therefore, at present, colored PET bottles are not produced in Japan, and it is requested that colored PET bottles produced overseas for Japan be changed to non-colored PET bottles (http://www. petbottle-rec.gr.jp/qanda/sec13.html).

日本国内で流通するＰＥＴボトルについては、国の指導を受けてＰＥＴボトルリサイクル推進協議会によって制定された「指定ＰＥＴボトルの自主設計ガイドライン」に詳細が規定されている（ｈｔｔｐ：／／ｗｗｗ．ｐｅｔｂｏｔｔｌｅ－ｒｅｃ．ｇｒ．ｊｐ／ｇｕｉｄｅｌｉｎｅ／ｊｉｓｙｕ．ｈｔｍｌ）。 PET bottles distributed in Japan are stipulated in detail in the "Self-designed guidelines for designated PET bottles" enacted by the PET Bottle Recycling Promotion Council under the guidance of the government (http://www.petbottle. -rec.gr.jp/guideline/jisyu.html).

こうした自主設計ガイドラインは、ＰＥＴボトルリサイクル推進協議会が、資源有効利用促進法規定の指定表示製品（清涼飲料、乳飲料、酒類、特定調味料）に使用されているＰＥＴボトル（指定ＰＥＴボトル）を、使用後の再処理、衛生性を含めた再利用適性に優れた容器とするために、使用するボトル、ラベル（印刷・接着剤等を含む）、キャップ等について規定したものである。 These voluntary design guidelines are based on the PET Bottle Recycling Promotion Council, which uses PET bottles (designated PET bottles) used for designated display products (soft drinks, milk drinks, alcoholic beverages, and specific seasonings) as stipulated by the Law for the Promotion of Effective Utilization of Resources (designated PET bottles). , bottles, labels (including printing, adhesives, etc.), caps, etc. to be used in order to make containers excellent in reprocessing after use and reusability including hygiene.

ＰＥＴボトルリサイクル推進協議会の会員（団体、企業）が自主設計ガイドラインを遵守することは当然として、会員以外においても、指定ＰＥＴボトル入り飲料・酒類・特定調味料を製造・輸入・販売する場合、あるいは指定ＰＥＴボトルおよび附属包材を製造・輸入する場合は、日本国内で販売・使用されるものであれば、自主設計ガイドラインに適合することが必要とされている。 Members (organizations, companies) of the PET Bottle Recycling Promotion Council must, of course, comply with the voluntary design guidelines. Alternatively, when manufacturing or importing designated PET bottles and their accompanying packaging materials, if they are to be sold and used in Japan, they must conform to the voluntary design guidelines.

したがって、国内で流通するＰＥＴボトルは、無着色のものがほとんどであり、また、ＰＥＴボトルに由来する再生ＰＥＴ系樹脂は、ほぼ透明である。
なお、再生ＰＥＴ系樹脂は、ほぼ透明であるものの、熱成形加工時に受ける熱履歴や、ラベル等の混在によって、黄黒い（ＣＩＥ １９７６ Ｌ＊ａ＊ｂ＊色空間におけるｂ＊の値が高く、Ｌ＊の値が低い）傾向にある。そのため、これまでは、明度が高い白色系や淡色系の化粧シートの材料に再生ＰＥＴ系樹脂を用いることは躊躇われていた。 Therefore, most of the PET bottles distributed in Japan are colorless, and the recycled PET-based resin derived from PET bottles is almost transparent.
Although the recycled PET resin is almost transparent, it becomes yellowish black (the value of b* in the CIE 1976 L*a*b* color space is high, low value of L*). For this reason, until now, people hesitated to use recycled PET-based resins as materials for white or light-colored decorative sheets with high brightness.

本発明においては、後述するように、第１層１１に重ねて、外部に露出する第２層１２を形成し、この第２層１２にバージン樹脂を主体とする第２樹脂成分を含ませることで、明度の低下を気にせずに、高い白色や淡色の化粧シート１０の構成材料として再生ＰＥＴ系樹脂を用いることを可能にしている。 In the present invention, as will be described later, the second layer 12 is formed on the first layer 11 and exposed to the outside, and the second layer 12 contains a second resin component mainly composed of virgin resin. Therefore, it is possible to use the recycled PET-based resin as a constituent material of the highly white or light-colored decorative sheet 10 without worrying about a decrease in brightness.

再生ＰＥＴ系樹脂の結晶化温度は、１４５℃以下が好ましく、１２０～１４５℃がより好ましく、１２５～１４０℃がさらに好ましい。
再生ＰＥＴ系樹脂の結晶化温度は、熱分析装置（示差走査熱量計（ＤＳＣ）等）を用いて測定される。 The crystallization temperature of the recycled PET resin is preferably 145°C or less, more preferably 120 to 145°C, even more preferably 125 to 140°C.
The crystallization temperature of the recycled PET-based resin is measured using a thermal analysis device (differential scanning calorimeter (DSC), etc.).

再生ＰＥＴ系樹脂の固有粘度（ＩＶ値）は、例えば、０．６０以上が好ましく、０．６５～０．８５がより好ましく、０．７０～０．８３がさらに好ましい。再生ＰＥＴ系樹脂の固有粘度（ＩＶ値）が前記範囲の下限値未満では、顔料添加時の溶融粘度低下により、押出成形性に問題が生じるおそれがある。再生ＰＥＴ系樹脂の固有粘度（ＩＶ値）が前記範囲の上限値超では、粘度が高くて押出成形性に問題が生じるおそれがある。
再生ＰＥＴ系樹脂の固有粘度（ＩＶ値）は、ＪＩＳ Ｋ ７３９０：２００３に記載の試験方法によって測定される。 The intrinsic viscosity (IV value) of the recycled PET resin is, for example, preferably 0.60 or more, more preferably 0.65 to 0.85, even more preferably 0.70 to 0.83. If the intrinsic viscosity (IV value) of the recycled PET-based resin is less than the lower limit of the above range, there is a possibility that a problem may arise in extrusion moldability due to a decrease in melt viscosity when pigments are added. If the intrinsic viscosity (IV value) of the recycled PET-based resin exceeds the upper limit of the above range, the viscosity is high and there is a risk of causing problems in extrusion moldability.
The intrinsic viscosity (IV value) of the recycled PET resin is measured by the test method described in JIS K 7390:2003.

再生ＰＥＴ系樹脂のＣＩＥ １９７６ Ｌ＊ａ＊ｂ＊色空間におけるｂ＊は、９以下が好ましく、－６～８がより好ましく、０～７がさらに好ましい。
再生ＰＥＴ系樹脂のｂ＊は、ＪＩＳ Ｋ ７３９０：２００３に記載の試験方法によって測定される。
再生ＰＥＴ系樹脂の、ＣＩＥ １９７６ Ｌ＊ａ＊ｂ＊色空間におけるＬ＊は、６５以上が好ましく、６８以上がより好ましく、７０以上がさらに好ましい。再生ＰＥＴ系樹脂のＬ＊が前記範囲の下限値以上であれば、明度が高い白色や淡色の化粧シート１０を製造しやすい。 b* in the CIE 1976 L*a*b* color space of the recycled PET resin is preferably 9 or less, more preferably -6 to 8, and even more preferably 0 to 7.
b* of the recycled PET resin is measured by the test method described in JIS K 7390:2003.
L* of the recycled PET resin in CIE 1976 L*a*b* color space is preferably 65 or more, more preferably 68 or more, and even more preferably 70 or more. If L* of the recycled PET-based resin is equal to or higher than the lower limit of the above range, it is easy to manufacture white or light-colored decorative sheet 10 with high brightness.

第１樹脂成分に含まれる他の樹脂（第１層）としては、白色顔料を含むマスターバッチに用いられる樹脂、化粧シートの色のバラツキを抑える、化粧シートの特性を改善する等の目的で添加された樹脂等が挙げられる。他の樹脂の具体例としては、バージンＰＥＴ系樹脂、再生ＰＥＴ系樹脂以外の再生樹脂（ポリ塩化ビニルを除く。）、バージンＰＥＴ系樹脂以外のバージン樹脂（ポリ塩化ビニルを除く。）等が挙げられる。 Other resins (first layer) contained in the first resin component include resins used in master batches containing white pigments, and are added for the purpose of suppressing color variation of the decorative sheet and improving the characteristics of the decorative sheet. and the like. Specific examples of other resins include virgin PET-based resins, recycled resins other than recycled PET-based resins (excluding polyvinyl chloride), and virgin resins other than virgin PET-based resins (excluding polyvinyl chloride). be done.

「白色顔料（第１層）」
第１層１１の白色顔料としては、酸化チタン、酸化亜鉛、炭酸カルシウム、酸化マグネシウム、リトボン等が挙げられる。白色顔料としては、隠蔽力が高い点から、酸化チタンが好ましい。
酸化チタンとしては、ルチル型酸化チタン、アナターゼ型酸化チタン等が挙げられ、触媒としての活性が低い点から、ルチル型酸化チタンが好ましい。 "White pigment (first layer)"
Examples of white pigments for the first layer 11 include titanium oxide, zinc oxide, calcium carbonate, magnesium oxide, and litbon. As the white pigment, titanium oxide is preferable because of its high hiding power.
Examples of titanium oxide include rutile-type titanium oxide and anatase-type titanium oxide, and rutile-type titanium oxide is preferable because of its low activity as a catalyst.

第１層１１の白色顔料の含有量は、第１樹脂成分１００質量部に対して５～１５質量部であり、７～１３質量部が好ましく、９～１２質量部がより好ましい。後述する第２層１２の下層となる第１層１１に白色顔料を含ませることにより、外部に露呈する第２層１２の厚みを薄くしても、色の透過によって化粧シート１０の明度が低下することを防止できる。白色顔料の含有量が前記範囲の下限値以上であれば、原料ロット間やシートの場所ごとの色のバラツキが少ない、明度が高い白色や淡色の化粧シート１０が得られる。白色顔料の含有量が前記範囲の上限値以下であれば、押出挙動異常（溶融粘度低下に伴う幅異常等）が抑えられ、化粧シート１０を製造する際の成形性がよい。 The content of the white pigment in the first layer 11 is 5 to 15 parts by mass, preferably 7 to 13 parts by mass, more preferably 9 to 12 parts by mass, based on 100 parts by mass of the first resin component. By including a white pigment in the first layer 11, which is the lower layer of the second layer 12, which will be described later, even if the thickness of the second layer 12 exposed to the outside is reduced, the brightness of the decorative sheet 10 is reduced due to the transmission of color. can be prevented. If the content of the white pigment is at least the lower limit of the above range, a white or light-colored decorative sheet 10 with high brightness and little variation in color between raw material lots or between locations on the sheet can be obtained. When the content of the white pigment is equal to or less than the upper limit of the above range, abnormal extrusion behavior (abnormal width due to a decrease in melt viscosity, etc.) is suppressed, and moldability when manufacturing the decorative sheet 10 is good.

「他の成分（第１層）」
第１層１１の他の成分としては、白色顔料以外の顔料、相溶化剤、紫外線吸収剤、光安定剤、酸化防止剤、帯電防止剤、保存安定剤、滑剤、充填材等が挙げられる。
他の成分の含有量は、第１樹脂成分１００質量部に対して１５質量部以下が好ましく、１０質量部以下がより好ましく、５質量部以下がさらに好ましい。 "Other components (first layer)"
Other components of the first layer 11 include pigments other than white pigments, compatibilizers, ultraviolet absorbers, light stabilizers, antioxidants, antistatic agents, storage stabilizers, lubricants, fillers, and the like.
The content of other components is preferably 15 parts by mass or less, more preferably 10 parts by mass or less, and even more preferably 5 parts by mass or less with respect to 100 parts by mass of the first resin component.

（第２層）
第２層１２は、バージン樹脂（新生樹脂）を７０質量％以上含む第２樹脂成分と、白色系顔料とを少なくとも含んでいる。なお、第２層１２は、本発明の効果を損なわない範囲において、必要に応じて第２樹脂成分および白色顔料以外の成分（以下、「他の成分（第２層）」とも記す。）を含んでいてもよい。 (Second layer)
The second layer 12 contains at least a second resin component containing 70% by mass or more of a virgin resin (new resin) and a white pigment. The second layer 12 may contain components other than the second resin component and the white pigment (hereinafter also referred to as "other components (second layer)") as necessary, as long as the effects of the present invention are not impaired. may contain.

「第２樹脂成分（第２層）」
第２樹脂成分は、バージン樹脂を７０質量％以上含んでいる。また、第２樹脂成分は、バージン樹脂以外の樹脂（以下、「他の樹脂（第２層）」とも記す。）を３０質量％以下、好ましくは１０質量％以下の範囲で含んでいてもよい。 "Second resin component (second layer)"
The second resin component contains 70% by mass or more of virgin resin. In addition, the second resin component may contain a resin other than the virgin resin (hereinafter also referred to as "another resin (second layer)") in an amount of 30% by mass or less, preferably 10% by mass or less. .

バージン樹脂は、不純物を殆ど含まない樹脂原料から新規に製造された樹脂であり、第１層１１に対する接合性を良好にする点から、エチレングリコールとテレフタル酸を主モノマーとする共重合体（ＰＥＴ，ＰＥＴ－Ｇ）、ポリカーボネート、ポリアクリル酸重合体が好ましい。 The virgin resin is a resin newly produced from a resin raw material containing almost no impurities, and is a copolymer (PET , PET-G), polycarbonate and polyacrylic acid polymers are preferred.

化粧シート１０のうち、第１層１１を覆う第２層１２の第２樹脂成分として、バージン樹脂を７０質量％以上含ませることにより、外部に露出する第２層１２の明度を、再生ＰＥＴ系樹脂を７０質量％以上含む第１層の明度よりも高めることができる。これにより、化粧シート１０の全樹脂成分の２５％以上の質量の再生ＰＥＴ系樹脂を用いた化粧シート１０であっても、外観上、高い明度を保つことができる。 By including 70% by mass or more of virgin resin as the second resin component of the second layer 12 covering the first layer 11 of the decorative sheet 10, the brightness of the second layer 12 exposed to the outside is reduced to that of the recycled PET-based resin. The brightness can be higher than that of the first layer containing 70% by mass or more of the resin. As a result, even the decorative sheet 10 using the recycled PET-based resin with a mass of 25% or more of the total resin component of the decorative sheet 10 can maintain a high brightness in appearance.

第２樹脂成分に含まれる他の樹脂としては、白色顔料を含むマスターバッチに用いられる樹脂、化粧シートの色のバラツキを抑える、化粧シートの特性を改善する等の目的で添加された樹脂等が挙げられる。他の樹脂の具体例としては、バージンＰＥＴ系樹脂以外のバージン樹脂（ポリ塩化ビニルを除く。）、再生ＰＥＴ系樹脂、再生ＰＥＴ系樹脂以外の再生樹脂（ポリ塩化ビニルを除く。）等が挙げられる。例えば、第２樹脂成分に含まれる他の樹脂として、再生ＰＥＴ系樹脂を３０質量％以下の範囲で含むことができる。 Other resins contained in the second resin component include resins used in masterbatches containing white pigments, and resins added for the purpose of suppressing variation in the color of the decorative sheet and improving the characteristics of the decorative sheet. mentioned. Specific examples of other resins include virgin resins other than virgin PET resins (excluding polyvinyl chloride), recycled PET resins, and recycled resins other than recycled PET resins (excluding polyvinyl chloride). be done. For example, as another resin contained in the second resin component, a recycled PET resin can be contained in a range of 30% by mass or less.

「白色顔料（第２層）」
第２層１２の白色顔料としては、第１層１１と同様に、酸化チタン、酸化亜鉛、炭酸カルシウム、酸化マグネシウム、リトボン等が挙げられる。白色顔料としては、隠蔽力が高い点から、酸化チタンが好ましい。
酸化チタンとしては、ルチル型酸化チタン、アナターゼ型酸化チタン等が挙げられ、触媒としての活性が低い点から、ルチル型酸化チタンが好ましい。
なお、第２層１２の白色顔料は、第１層１１の白色樹脂と同一のものを選択しても、あるいは互いに異なるものを選択しても良い。 "White pigment (second layer)"
Similar to the first layer 11, the white pigment for the second layer 12 includes titanium oxide, zinc oxide, calcium carbonate, magnesium oxide, litbon, and the like. As the white pigment, titanium oxide is preferable because of its high hiding power.
Examples of titanium oxide include rutile-type titanium oxide and anatase-type titanium oxide, and rutile-type titanium oxide is preferable because of its low activity as a catalyst.
The white pigment for the second layer 12 may be the same as the white resin for the first layer 11, or may be different from each other.

第２層１２の白色顔料の含有量は、第２樹脂成分１００質量部に対して５～１５質量部であり、７～１３質量部が好ましく、９～１２質量部がより好ましい。白色顔料の含有量が前記範囲の下限値以上であれば、原料ロット間やシートの場所ごとの色のバラツキが少ない、明度が高い白色や淡色の化粧シート１０が得られる。白色顔料の含有量が前記範囲の上限値以下であれば、押出挙動異常（溶融粘度低下に伴う幅異常等）が抑えられ、化粧シート１０を製造する際の成形性がよい。 The content of the white pigment in the second layer 12 is 5 to 15 parts by mass, preferably 7 to 13 parts by mass, more preferably 9 to 12 parts by mass, based on 100 parts by mass of the second resin component. If the content of the white pigment is at least the lower limit of the above range, a white or light-colored decorative sheet 10 with high brightness and little variation in color between raw material lots or between locations on the sheet can be obtained. When the content of the white pigment is equal to or less than the upper limit of the above range, abnormal extrusion behavior (abnormal width due to a decrease in melt viscosity, etc.) is suppressed, and moldability when manufacturing the decorative sheet 10 is good.

「他の成分（第２層）」
第２層１２の他の成分としては、白色顔料以外の顔料、相溶化剤、紫外線吸収剤、光安定剤、酸化防止剤、帯電防止剤、保存安定剤、滑剤、充填材等が挙げられる。
他の成分の含有量は、第２樹脂成分１００質量部に対して１５質量部以下が好ましく、１０質量部以下がより好ましく、５質量部以下がさらに好ましい。 "Other ingredients (second layer)"
Other components of the second layer 12 include pigments other than white pigments, compatibilizers, ultraviolet absorbers, light stabilizers, antioxidants, antistatic agents, storage stabilizers, lubricants, fillers, and the like.
The content of other components is preferably 15 parts by mass or less, more preferably 10 parts by mass or less, and even more preferably 5 parts by mass or less with respect to 100 parts by mass of the second resin component.

以上の様な組成の第２層１２の厚みは、再生ＰＥＴ系樹脂を７０質量％以上含む第１層１１を覆い、耐薬品性、耐溶剤性の低い第１層１１への浸透を防ぐために、一定以上の厚みを有することが望ましい。
第２層１２の厚み範囲としては、例えば、２５～７５μｍ、好ましくは２５～４０μｍの範囲にする。 The thickness of the second layer 12 having the composition as described above is such that it covers the first layer 11 containing 70% by mass or more of the recycled PET resin and prevents penetration into the first layer 11, which has low chemical resistance and solvent resistance. , it is desirable to have a certain thickness or more.
The thickness range of the second layer 12 is, for example, 25 to 75 μm, preferably 25 to 40 μm.

こうした厚み範囲にすることで、化粧シート１０のうち外部に露出する第２層１２を介して、再生ＰＥＴ系樹脂を含む明度の低い第１層１１が透けて、化粧シート１０の外観上の明度が低下することを防止する。また、第２層１２が厚すぎると、化粧シート１０全体での再生ＰＥＴ系樹脂の使用割合が低下して、再生ＰＥＴ系樹脂を使用する意義が低下する。 By setting the thickness in such a range, the first layer 11 containing the recycled PET-based resin having a low brightness can be seen through the second layer 12 of the decorative sheet 10 exposed to the outside, and the brightness of the appearance of the decorative sheet 10 can be improved. to prevent a decrease in On the other hand, if the second layer 12 is too thick, the use ratio of the recycled PET-based resin in the entire decorative sheet 10 will decrease, and the significance of using the recycled PET-based resin will decrease.

（第３層）
第３層１３は、バージン樹脂（新生樹脂）を８０質量％以上含む第３樹脂成分を少なくとも含んでいる。また、第３層１３は、更に白色系顔料を、第３樹脂成分１００質量部に対して５質量部以下の範囲で含んでいてもよい。更に、第３層１３は、本発明の効果を損なわない範囲において、必要に応じて第３樹脂成分や選択的に含まれる白色系顔料以外の成分（以下、「他の成分（第３層）」とも記す。）を含んでいてもよい。 (third layer)
The third layer 13 contains at least a third resin component containing 80% by mass or more of virgin resin (new resin). The third layer 13 may further contain a white pigment in an amount of 5 parts by mass or less with respect to 100 parts by mass of the third resin component. Furthermore, the third layer 13 includes components other than the third resin component and the white pigment optionally included as necessary (hereinafter referred to as "other components (third layer) ) may be included.

「第３樹脂成分（第３層）」
第３樹脂成分は、バージン樹脂を８０質量％以上含んでいる。また、第３樹脂成分は、バージン樹脂以外の樹脂（以下、「他の樹脂（第３層）」とも記す。）を、例えば２０質量％以下、好ましくは１０質量％以下の範囲で含んでいてもよい。 "Third resin component (third layer)"
The third resin component contains 80% by mass or more of virgin resin. In addition, the third resin component contains a resin other than the virgin resin (hereinafter also referred to as "another resin (third layer)") in an amount of, for example, 20% by mass or less, preferably 10% by mass or less. good too.

バージン樹脂は、不純物を殆ど含まない樹脂原料から新規に製造された樹脂であり、第１層１１に対する接合性、および接着層１４を介した壁面Ｗに対する接着性を良好にする点から、エチレングリコールとテレフタル酸を主モノマーとする共重合体（ＰＥＴ，ＰＥＴ－Ｇ）、ポリカーボネート、ポリアクリル酸重合体が好ましい。
なお、第３層１３に用いるバージン樹脂は、第２層１２に用いるバージン樹脂と同一のものを用いても良く、また、互いに異なる種類のバージン樹脂を用いても良い。 The virgin resin is a resin newly produced from a resin raw material that contains almost no impurities, and from the viewpoint of improving the bondability to the first layer 11 and the adhesion to the wall surface W via the adhesive layer 14, ethylene glycol is used. and terephthalic acid as main monomers (PET, PET-G), polycarbonates and polyacrylic acid polymers are preferred.
The virgin resin used for the third layer 13 may be the same as the virgin resin used for the second layer 12, or different types of virgin resins may be used.

化粧シート１０のうち、第１層１１を覆う第３層１３の第３樹脂成分として、バージン樹脂を８０質量％以上含ませることにより、化粧シート１０が壁面Ｗに接着される面を成す第３層１３の壁面Ｗに対する接着性を向上させる。また、白色系顔料を含まないか、あるいは第３樹脂成分１００質量部に対して５質量部以下に制限することにより、白色系顔料に含まれる分散剤による接着性の低下を防止できる。 The third layer 13 covering the first layer 11 of the decorative sheet 10 contains 80% by mass or more of virgin resin as the third resin component. It improves the adhesion of the layer 13 to the wall W. Further, by not containing the white pigment or by limiting the content to 5 parts by mass or less with respect to 100 parts by mass of the third resin component, it is possible to prevent deterioration of adhesion due to the dispersant contained in the white pigment.

第３樹脂成分に含まれる他の樹脂としては、バージンＰＥＴ系樹脂以外のバージン樹脂（ポリ塩化ビニルを除く。）、再生ＰＥＴ系樹脂、再生ＰＥＴ系樹脂以外の再生樹脂（ポリ塩化ビニルを除く。）等が挙げられる。例えば、第３樹脂成分に含まれる他の樹脂として、再生ＰＥＴ系樹脂を２０質量％以下の範囲で含むことができる。 Other resins contained in the third resin component include virgin resins other than virgin PET resins (excluding polyvinyl chloride), recycled PET resins, and recycled resins other than recycled PET resins (excluding polyvinyl chloride). ) and the like. For example, as another resin contained in the third resin component, a recycled PET resin can be contained in a range of 20% by mass or less.

「白色顔料（第３層）」
第３層１３の白色顔料は含まないことが好ましいが、含ませる場合には、第１層１１と同様に、酸化チタン、酸化亜鉛、炭酸カルシウム、酸化マグネシウム、リトボン等が挙げられる。白色顔料としては、隠蔽力が高い点から、酸化チタンが好ましい。
酸化チタンとしては、ルチル型酸化チタン、アナターゼ型酸化チタン等が挙げられ、触媒としての活性が低い点から、ルチル型酸化チタンが好ましい。
なお、第３層１３の白色顔料は、第１層１１や第２層１２の白色樹脂と同一のものを選択しても、あるいは互いに異なるものを選択しても良い。 "White pigment (third layer)"
It is preferable that the third layer 13 does not contain a white pigment, but if it contains a white pigment, similar to the first layer 11, titanium oxide, zinc oxide, calcium carbonate, magnesium oxide, litbon, and the like can be used. As the white pigment, titanium oxide is preferable because of its high hiding power.
Examples of titanium oxide include rutile-type titanium oxide and anatase-type titanium oxide, and rutile-type titanium oxide is preferable because of its low activity as a catalyst.
The white pigment for the third layer 13 may be the same as the white resin for the first layer 11 or the second layer 12, or may be different from each other.

「他の成分（第３層）」
第３層１３の他の成分としては、白色顔料以外の顔料、相溶化剤、紫外線吸収剤、光安定剤、酸化防止剤、帯電防止剤、保存安定剤、滑剤、充填材等が挙げられる。
他の成分の含有量は、第３樹脂成分１００質量部に対して２０質量部以下が好ましく、１０質量部以下がより好ましく、５質量部以下がさらに好ましい。 "Other ingredients (third layer)"
Other components of the third layer 13 include pigments other than white pigments, compatibilizers, ultraviolet absorbers, light stabilizers, antioxidants, antistatic agents, storage stabilizers, lubricants, fillers, and the like.
The content of other components is preferably 20 parts by mass or less, more preferably 10 parts by mass or less, and even more preferably 5 parts by mass or less with respect to 100 parts by mass of the third resin component.

以上の様な組成の第３層１３の厚みは、再生ＰＥＴ系樹脂を７０質量％以上含む第１層１１を覆い、耐薬品性、耐溶剤性の低い第３層１３への浸透を防ぐために、一定以上の厚みを有することが望ましい。
第３層１３の厚み範囲としては、例えば、１５～７０μｍ、好ましくは２５～４０μｍの範囲にする。 The thickness of the third layer 13 having the composition as described above is such that it covers the first layer 11 containing 70% by mass or more of the recycled PET resin and prevents permeation into the third layer 13, which has low chemical resistance and solvent resistance. , it is desirable to have a certain thickness or more.
The thickness range of the third layer 13 is, for example, 15 to 70 μm, preferably 25 to 40 μm.

こうした厚み範囲にすることで、第１層１１の再生ＰＥＴ系樹脂に含まれる顔料中の分散剤が第３層１３の接着層１４側まで浸透してブリードアウトすることによって生じる接着性の低下を防止することができる。
また、第３層１３が厚すぎると、化粧シート１０全体での再生ＰＥＴ系樹脂の使用割合が低下して、再生ＰＥＴ系樹脂を使用する意義が低下する。 By setting the thickness within such a range, the dispersant in the pigment contained in the recycled PET-based resin of the first layer 11 permeates up to the adhesive layer 14 side of the third layer 13 and bleeds out, thereby reducing adhesion. can be prevented.
On the other hand, if the third layer 13 is too thick, the usage ratio of the recycled PET-based resin in the entire decorative sheet 10 will decrease, and the significance of using the recycled PET-based resin will decrease.

（化粧シート全体の構成）
以上のような第１層１１、第２層１２、および第３層１３からなる化粧シート１０全体の厚さは、０．１～０．５ｍｍが好ましく、０．２～０．４ｍｍがより好ましい。化粧シート１０の厚さが前記範囲の下限値以上であれば、化粧シート１０の機械的強度、隠蔽力を高くしやすい。化粧シート１０の厚さが前記範囲の上限値以下であれば、化粧シート１０の三次元加工性、可とう性等が良好になる。 (Structure of entire decorative sheet)
The overall thickness of the decorative sheet 10 composed of the first layer 11, the second layer 12, and the third layer 13 is preferably 0.1 to 0.5 mm, more preferably 0.2 to 0.4 mm. . If the thickness of the decorative sheet 10 is at least the lower limit of the above range, the mechanical strength and hiding power of the decorative sheet 10 can be easily increased. If the thickness of the decorative sheet 10 is equal to or less than the upper limit of the above range, the three-dimensional workability, flexibility, etc. of the decorative sheet 10 are improved.

また、化粧シート１０の第２層１２の表面側において、ＣＩＥ １９７６ Ｌ＊ａ＊ｂ＊色空間におけるＬ＊が９２以上であることが好ましい。これにより、明度が高い白色や淡色の化粧シート１０にすることができる。化粧シート１０のＬ＊は、ＪＩＳ Ｚ ８７８１－４：２０１３に基づいて測定される。 Also, on the surface side of the second layer 12 of the decorative sheet 10, L* in the CIE 1976 L*a*b* color space is preferably 92 or more. As a result, the decorative sheet 10 can be made white or light-colored with high lightness. L* of the decorative sheet 10 is measured based on JIS Z 8781-4:2013.

本実施形態の化粧シート１０は、本発明の効果を損なわない範囲において、必要に応じて各種機能を付与するための機能層を有していてもよい。機能層としては、耐汚染性、耐候性を付与するためのコーティング層、転写層、意匠性を付与するための印刷層等が挙げられる。
化粧シート１０の表面を成す第２層の表面形状は、特に限定されず、平滑であってもよく、エンボス加工等による凹凸を有する形状であってもよい。 The decorative sheet 10 of the present embodiment may have a functional layer for imparting various functions as necessary, as long as the effects of the present invention are not impaired. Examples of the functional layer include a coating layer for imparting stain resistance and weather resistance, a transfer layer, and a printing layer for imparting design.
The surface shape of the second layer forming the surface of the decorative sheet 10 is not particularly limited, and may be smooth or may have unevenness due to embossing or the like.

本実施形態の化粧シート１０は、例えば、第１層１１、第２層１２、および第３層１３をそれぞれ構成する樹脂成分や白色顔料などを含む樹脂混合物を、それぞれ加熱溶融、混練し、多層シート状に共押出することによって得られる。例えば、第１層１１を構成する樹脂と、第２層１２を構成する樹脂と、第３層１３を構成する樹脂とを共押出成形機に供給し、フィードブロック方式のＴダイを用いて、２００℃程度で共押出して、第１層１１、第２層１２、および第３層１３とからなる化粧シート１０を成形する。 For example, the decorative sheet 10 of the present embodiment is obtained by heating, melting, and kneading a resin mixture containing a resin component and a white pigment that constitute the first layer 11, the second layer 12, and the third layer 13, respectively, to form a multilayer. Obtained by co-extrusion in sheet form. For example, the resin constituting the first layer 11, the resin constituting the second layer 12, and the resin constituting the third layer 13 are supplied to a co-extrusion molding machine, and a feed block type T die is used to Co-extrusion is carried out at about 200° C. to form the decorative sheet 10 comprising the first layer 11 , the second layer 12 and the third layer 13 .

もしくは、前記樹脂混合物をそれぞれシート状に成形し、得られた第１層１１の一面１１ａ側に第２層１２を、また他面１１ｂ側に第３層１３を、それぞれ接合することによっても、化粧シート１０が得られる。
樹脂混合物の成形方法としては、押出成形法、カレンダー成形法等が挙げられる。
化粧シート１０は、無延伸であってもよく、延伸されていてもよい。 Alternatively, each of the resin mixtures is molded into a sheet, and the second layer 12 is bonded to one surface 11a of the obtained first layer 11, and the third layer 13 is bonded to the other surface 11b. A decorative sheet 10 is obtained.
Methods for molding the resin mixture include extrusion molding and calendar molding.
The decorative sheet 10 may be unstretched or stretched.

なお、上述した実施形態では、化粧シート１０を第１層１１、第２層１２、および第３層１３の３層から構成しているが、それぞれの層の間に、任意の機能層を更に形成することもできる。また、第２層１２の表面に、透明な保護膜などを更に形成することもできる。 In the above-described embodiment, the decorative sheet 10 is composed of three layers, the first layer 11, the second layer 12, and the third layer 13, but an optional functional layer is further provided between each layer. can also be formed. Also, a transparent protective film or the like can be further formed on the surface of the second layer 12 .

（作用機序）
以上説明した本実施形態の化粧シート１０にあっては、第１層１１の第１樹脂成分がＰＥＴボトルに由来する再生ＰＥＴ系樹脂を７０質量％以上含む第１樹脂成分を有するため、ポリ塩化ビニルを含む化粧シートや、全樹脂成分中の再生樹脂の割合が低い化粧シートに比べ、親環境的である。 (Mechanism of action)
In the decorative sheet 10 of the present embodiment described above, since the first resin component of the first layer 11 has a first resin component containing 70% by mass or more of recycled PET resin derived from PET bottles, polychlorination It is more environmentally friendly than vinyl-containing decorative sheets or decorative sheets with a low percentage of recycled resin in the total resin component.

そして、本実施形態の化粧シート１０にあっては、再生ＰＥＴ系樹脂を多く含む第１層１１に重ねて、バージン樹脂を７０質量％以上含む第２樹脂成分を有する第２層１２を配したことにより、化粧シート１０が外部に露呈する面がこの第２層１２になるので、外観上、高い明度を保つことができ、色調のムラが少ない化粧シート１０を実現できる。 In the decorative sheet 10 of the present embodiment, the second layer 12 having the second resin component containing 70% by mass or more of the virgin resin is placed on the first layer 11 containing a large amount of the recycled PET resin. As a result, the surface of the decorative sheet 10 exposed to the outside becomes the second layer 12, so that the decorative sheet 10 can maintain a high brightness in appearance and has little color tone unevenness.

そして、化粧シート１０の外面に露呈する第２層１２は、バージン樹脂を７０質量％以上含む第２樹脂成分を有することにより、再生樹脂の割合が多い場合に生じる、不純物中の塩基が原因のクラックが発生しにくく、表面の美観の低下や強度の低下を防止することが可能な化粧シート１０を実現できる。 The second layer 12 exposed on the outer surface of the decorative sheet 10 has a second resin component containing 70% by mass or more of virgin resin. It is possible to realize the decorative sheet 10 that is less susceptible to cracking and that can prevent deterioration of the appearance of the surface and deterioration of strength.

また、本実施形態の化粧シート１０にあっては、再生ＰＥＴ系樹脂を多く含む第１層１１に重ねて、バージン樹脂を８０質量％以上含む第３樹脂成分を有する第３層１３を設ければ、化粧シート１０はこの第３層１３が壁面Ｗと接着されるので、再生樹脂の割合が多い場合に生じる、顔料中の分散剤が化粧シート表面にブリードアウトすることによって生じる接着性の低下を防止することができる。よって、再生ＰＥＴ系樹脂を多く含む第１層１１を有していても、接着性の良好な化粧シート１０を実現できる。 Further, in the decorative sheet 10 of the present embodiment, the third layer 13 having the third resin component containing 80% by mass or more of the virgin resin is provided over the first layer 11 containing a large amount of the recycled PET resin. For example, since the third layer 13 of the decorative sheet 10 is adhered to the wall surface W, there is a decrease in adhesion caused by bleeding out of the dispersant in the pigment to the surface of the decorative sheet, which occurs when the proportion of recycled resin is high. can be prevented. Therefore, even if the first layer 11 contains a large amount of recycled PET-based resin, the decorative sheet 10 with good adhesion can be realized.

本発明の化粧シートは、壁材、床材、建具（扉、戸等）、家具、シンク台、洗面化粧台等の表層に用いられ、好適には家具、シンク台、洗面化粧台等の扉の表層に用いられる。 The decorative sheet of the present invention is used for surface layers of wall materials, floor materials, fittings (doors, doors, etc.), furniture, sink stands, bathroom vanities, etc., and is preferably used for doors of furniture, sink stands, bathroom vanities, etc. used for the surface layer of

以上、本発明の実施形態を具体的に説明したが、これらの実施形態は、例として提示したものであり、発明の範囲を限定することは意図していない。これら実施形態は、その他の様々な形態で実施されることが可能であり、発明の要旨を逸脱しない範囲で、種々の省略、置き換え、変更を行うことができる。これら実施形態やその変形は、発明の範囲や要旨に含まれると同様に、特許請求の範囲に記載された発明とその均等の範囲に含まれるものである。 Although the embodiments of the present invention have been specifically described above, these embodiments are presented as examples and are not intended to limit the scope of the invention. These embodiments can be implemented in various other forms, and various omissions, replacements, and modifications can be made without departing from the scope of the invention. These embodiments and their modifications are included in the scope and spirit of the invention, as well as the scope of the invention described in the claims and equivalents thereof.

以下、実施例を挙げて、本発明をより具体的に説明するが、本発明はこれら実施例に限定されるものではない。 EXAMPLES The present invention will be described in more detail below with reference to Examples, but the present invention is not limited to these Examples.

「評価方法」
・表面色調
分光光度計（ＣＣＭ）（クラボウ社製、ＣＯＬＯＲ－７）を用い、光源Ｄ６５、視野角１０°の条件にて、化粧シートの３ヶ所を測定し、ＣＩＥ １９７６ Ｌ＊ａ＊ｂ＊色空間におけるＬ＊、ａ＊、ｂ＊を求め、３箇所の平均値を用いた。 "Evaluation method"
・ Surface color tone Using a spectrophotometer (CCM) (Kurabo Co., Ltd., COLOR-7), 3 points of the decorative sheet are measured under the conditions of a light source of D65 and a viewing angle of 10 °, CIE 1976 L * a * b * L*, a*, and b* in the color space were obtained, and the average value of three locations was used.

・耐塩基性
２．５ｃｍ角に切った脱脂綿に１０％ＮａＯＨ水溶液を含ませたものを、１０ｃｍ四方に切った化粧シートの試料上に置き、温度２３℃，湿度５０％環境下で２４時間静置する。その後、脱脂綿を取り除き、表面を水洗いしてから２４時間乾燥させ、化粧シートの試料上のクラック有無を観察した。
（初期）化粧シートを製造した後に、１０ｃｍ四方に切った化粧シートの試料を用いて、前記の対塩基性評価を行った。
（エイジング後）１０ｃｍ四方に切った化粧シートの試料を、温度４５℃，湿度９５％に設定した恒温恒湿槽で１４日間保管した後、前記の対塩基性評価を行った。 ・Base resistance Absorbent cotton cut into 2.5 cm squares soaked with 10% NaOH aqueous solution is placed on a sample of a decorative sheet cut into 10 cm squares, and left for 24 hours at a temperature of 23°C and a humidity of 50%. place. Thereafter, the absorbent cotton was removed, the surface was washed with water and dried for 24 hours, and the presence or absence of cracks on the sample of the decorative sheet was observed.
After manufacturing the (initial stage) decorative sheet, the above-mentioned base resistance evaluation was performed using a sample of the decorative sheet cut into a 10 cm square.
(After aging) A 10 cm square sample of the decorative sheet was stored for 14 days in a constant temperature and humidity chamber set at a temperature of 45° C. and a humidity of 95%, and then evaluated for base resistance.

・接着性
化粧シートの試料を温度４５℃，湿度９５％に設定した恒温高湿槽で１４日間保管した後、パーチクルボードにシンコーボンドＴＡ４３５を塗布し、化粧シートの試料を圧着後２４時間保管し、各温度条件（０℃、―１０℃、－２０℃）下で化粧シートの試料を剥離する。剥離した化粧シートの試料の裏面に付着した木材を観察し、化粧シートの試料の面積に対する木材の付着面積の百分率を木部破断率（％）とした。
木部破断率 １００％～８０％ ・・・ 評価Ａ
木部破断率 ８０％～５０％ ・・・ 評価Ｂ
木部破断率 ５０％～０％ ・・・ 評価Ｃ
評価がＡであれば、十分な接着が得られていると考えられる。 Adhesion After storing the sample of the decorative sheet in a constant temperature and high humidity chamber set at a temperature of 45 ° C. and a humidity of 95% for 14 days, Shinko Bond TA435 was applied to the particle board, and the sample of the decorative sheet was stored for 24 hours after crimping. A sample of the decorative sheet is peeled off under each temperature condition (0° C., −10° C., −20° C.). The wood adhering to the back surface of the peeled decorative sheet sample was observed, and the percentage of the adhered area of the wood to the area of the decorative sheet sample was taken as the wood breakage rate (%).
Xylem fracture rate 100% to 80% ・・・ Evaluation A
Xylem fracture rate 80% to 50% ・・・ Evaluation B
Xylem fracture rate 50% to 0% ・・・ Evaluation C
If the evaluation is A, it is considered that sufficient adhesion is obtained.

（実施例１）
第１層：
再生ＰＥＴ系樹脂 ＡＬＩＰＬＡＳＴ社製「Ａｌｉｍｐｅｔ」（イタリア産 回収ペットボトル再生樹脂）にマスターバッチ（酸化チタンおよびバージンＡ－ＰＥＴ樹脂を含む。）を添加した樹脂混合物を用いた。
樹脂成分に対する白色顔料の含有量を表１に示す。
第２層：
ＰＥＴ－Ｇ樹脂（バージン樹脂） ＳＫケミカル社製「Ｋ２０１２」にマスターバッチ（酸化チタンおよびバージンＰＥＴ－Ｇを含む。）を添加した樹脂混合物を用いた。
樹脂成分に対する白色顔料の含有量を表１に示す。
第３層：
ＰＥＴ－Ｇ樹脂（バージン樹脂） ＳＫケミカル社製「Ｋ２０１２」を用いた。
上記の原料を３種３層押出機を用いて共押出法によってＴダイから２６５℃で押出し、４０℃の冷却ロール上にキャストして、第２層／第１層／第３層の各層がそれぞれ３３μｍ／１８４μｍ／３３μｍの層厚２５０μｍのシートを得た。 (Example 1)
First layer:
Recycled PET-based resin A resin mixture was used in which a masterbatch (including titanium oxide and virgin A-PET resin) was added to “Alimpet” manufactured by ALIPLAST (recycled resin from recycled PET bottles made in Italy).
Table 1 shows the content of the white pigment with respect to the resin component.
Second layer:
PET-G resin (virgin resin) A resin mixture obtained by adding a masterbatch (including titanium oxide and virgin PET-G) to “K2012” manufactured by SK Chemicals was used.
Table 1 shows the content of the white pigment with respect to the resin component.
Third layer:
PET-G resin (virgin resin) “K2012” manufactured by SK Chemicals was used.
The above raw materials are extruded at 265 ° C. from a T-die by a co-extrusion method using a three-kind three-layer extruder, cast on a cooling roll at 40 ° C., and each layer of the second layer / first layer / third layer is formed. A sheet with a layer thickness of 250 μm was obtained with a layer thickness of 33 μm/184 μm/33 μm respectively.

（実施例２）
第２層のバージン樹脂、第２層のマスターバッチの樹脂成分、及び第３層のバージン樹脂をＰＥＴ－Ｇ樹脂から、ＰＥＴ樹脂（Ａ－ＰＥＴ） 華潤有限公司製「ＣＲ８８１６」に変更した以外は、実施例１と同様にして実施例２の化粧シートを得た。 (Example 2)
The virgin resin of the second layer, the resin component of the masterbatch of the second layer, and the virgin resin of the third layer were changed from PET-G resin to PET resin (A-PET) "CR8816" manufactured by Huarun Co., Ltd. A decorative sheet of Example 2 was obtained in the same manner as in Example 1.

（実施例３）
第２層のバージン樹脂、第２層のマスターバッチの樹脂成分、及び第３層のバージン樹脂をＰＥＴ－Ｇ樹脂から、ポリメタクリル酸メチル樹脂（ＰＭＭＡ１） 旭化成社製「デルペット（登録商標）６０Ｎ」に変更した以外は実施例１と同様にして、実施例３の化粧シートを得た。 (Example 3)
The virgin resin of the second layer, the resin component of the masterbatch of the second layer, and the virgin resin of the third layer from PET-G resin, polymethyl methacrylate resin (PMMA1) manufactured by Asahi Kasei Corporation "Delpet (registered trademark) 60N A decorative sheet of Example 3 was obtained in the same manner as in Example 1, except for changing to .

（実施例４）
第２層のバージン樹脂、第２層のマスターバッチの樹脂成分、及び第３層のバージン樹脂をＰＥＴ－Ｇ樹脂から、ポリメタクリル酸メチル樹脂（ＰＭＭＡ２） 三菱ケミカル社製「アクリペット（登録商標）ＩＲＳ２０４」に変更した以外は、実施例１と同様にして、実施例４の化粧シートを得た。 (Example 4)
The virgin resin of the second layer, the resin component of the masterbatch of the second layer, and the virgin resin of the third layer from PET-G resin, polymethyl methacrylate resin (PMMA2) Mitsubishi Chemical Corporation "Acrypet (registered trademark) A decorative sheet of Example 4 was obtained in the same manner as in Example 1, except that the sheet was changed to IRS204.

（実施例５）
第２層／第１層／第３層の各層をそれぞれ２５μｍ／１８４μｍ／３３μｍにして層厚２４２μｍに変更した以外は、実施例１と同様にして、実施例５の化粧シートを得た。 (Example 5)
A decorative sheet of Example 5 was obtained in the same manner as in Example 1, except that the layer thickness of the second layer/first layer/third layer was changed to 25 μm/184 μm/33 μm and the layer thickness was changed to 242 μm.

（実施例６、８、１１）
第２層／第１層／第３層の各層の厚さ、再生ＰＥＴ系樹脂とバージン樹脂の割合（質量％）、樹脂成分に対する白色顔料の含有量を表２に示すように変更した以外は、実施例１と同様にして、実施例６、８、１１の化粧シートを得た。 (Examples 6, 8, 11)
Except for changing the thickness of each layer of the second layer/first layer/third layer, the ratio (% by mass) of the recycled PET resin and the virgin resin, and the content of the white pigment to the resin component as shown in Table 2. The decorative sheets of Examples 6, 8 and 11 were obtained in the same manner as in Example 1.

（実施例７、９、１０）
第２層／第１層／第３層の各層の再生ＰＥＴ系樹脂とバージン樹脂の割合（質量％）を表２に示すように変更した以外は実施例２と同様にして、実施例７、９、１０の化粧シートを得た。 (Examples 7, 9, 10)
Example 7, Example 7, 9 and 10 decorative sheets were obtained.

（比較例１）
実施例１の第２層，第３層を設けず、再生樹脂を用いた第１層のみで押出成型して、比較例１の化粧シートを得た。
得られた化粧シートは再生樹脂の着色により明度が低く、耐塩基性の評価では、再生樹脂が塩基に曝されることによってクラックが発生し、木材に対する接着力も実施例１～１１と比較して弱い。 (Comparative example 1)
A decorative sheet of Comparative Example 1 was obtained by extruding only the first layer using the recycled resin without providing the second and third layers of Example 1.
The resulting decorative sheet had a low brightness due to the coloring of the recycled resin, and in the evaluation of the base resistance, cracks occurred due to the exposure of the recycled resin to a base, and the adhesive strength to wood was also lower than that of Examples 1 to 11. weak.

（比較例２）
第２層／第１層／第３層の各層をそれぞれ１７μｍ／８８μｍ／１７μｍにして層厚１２２μｍに変更した以外は実施例１と同様にして、比較例２の化粧シートを得た。
得られた化粧シートは、第２層が薄いため、再生樹脂を用いた第１層の着色を隠蔽できない。また、耐塩基性の評価では、塩基が第１層の再生樹脂まで浸透し、クラックが発生した。 (Comparative example 2)
A decorative sheet of Comparative Example 2 was obtained in the same manner as in Example 1, except that the layer thickness of the second layer/first layer/third layer was changed to 17 μm/88 μm/17 μm and the layer thickness was changed to 122 μm.
Since the obtained decorative sheet has a thin second layer, it cannot hide the coloring of the first layer using the recycled resin. In addition, in the evaluation of base resistance, the base penetrated into the recycled resin of the first layer, and cracks were generated.

（比較例３）
第２層／第１層／第３層の各層をそれぞれ１７μｍ／８８μｍ／１７μｍにして層厚１２２μｍに変更した以外は実施例３と同様にして、比較例３の化粧シートを得た。
得られた化粧シートは、第２層が薄いため、再生樹脂を用いた第１層の着色を隠蔽できない。また、耐塩基性の評価では、塩基が第１層まで浸透し、クラックが発生した。 (Comparative Example 3)
A decorative sheet of Comparative Example 3 was obtained in the same manner as in Example 3, except that the layer thickness of the second layer/first layer/third layer was changed to 17 μm/88 μm/17 μm and the layer thickness was changed to 122 μm.
Since the obtained decorative sheet has a thin second layer, it cannot hide the coloring of the first layer using the recycled resin. In addition, in the evaluation of base resistance, the base permeated to the first layer and cracks were generated.

（比較例４）
第３層をＰＥＴ－Ｇ樹脂にマスターバッチ（酸化チタンおよびバージンＰＥＴ－Ｇを含む。）を添加した樹脂混合物に変更した以外は実施例１と同様にして、比較例４の化粧シートを得た。樹脂成分に対する白色顔料の含有量を表３に示す。
得られた化粧シートは木材に対する接着力が実施例１～１１と比較して低下した。 (Comparative Example 4)
A decorative sheet of Comparative Example 4 was obtained in the same manner as in Example 1, except that the third layer was changed to a resin mixture in which a masterbatch (including titanium oxide and virgin PET-G) was added to PET-G resin. . Table 3 shows the content of the white pigment with respect to the resin component.
The resulting decorative sheet had lower adhesive strength to wood compared to Examples 1-11.

（比較例５）
第３層をバージン樹脂（Ａ－ＰＥＴ）７０質量％と再生ＰＥＴ系樹脂３０質量％の混合に変更した以外は実施例１と同様にして、比較例５の化粧シートを得た。
得られた化粧シートは木材に対する接着力が実施例１～１１と比較して低下した。 (Comparative Example 5)
A decorative sheet of Comparative Example 5 was obtained in the same manner as in Example 1, except that the third layer was changed to a mixture of 70% by mass of virgin resin (A-PET) and 30% by mass of recycled PET resin.
The resulting decorative sheet had lower adhesive strength to wood compared to Examples 1-11.

（比較例６）
比較例１と同様に第１層のみで押出成型したが、第１層を再生ＰＥＴ系樹脂７０質量％とバージン樹脂（Ａ－ＰＥＴ）３０質量％の混合に変更して、比較例６の化粧シートを得た。
得られた化粧シートは、耐塩基性の評価では、塩基によってクラックが発生し、木材に対する接着力も実施例１～１１と比較して低下した。 (Comparative Example 6)
Only the first layer was extruded in the same manner as in Comparative Example 1, but the first layer was changed to a mixture of 70% by mass of recycled PET resin and 30% by mass of virgin resin (A-PET). got a sheet.
In the evaluation of base resistance, the obtained decorative sheet had cracks due to the presence of base, and the adhesion to wood was also lower than in Examples 1-11.

実施例１～５の試料の構成および評価結果を表１に、実施例６～１１の試料の構成および評価結果を表２に、また、比較例１～６の試料の構成および評価結果を表３に、それぞれ示す。 The configurations and evaluation results of the samples of Examples 1 to 5 are shown in Table 1, the configurations and evaluation results of the samples of Examples 6 to 11 are shown in Table 2, and the configurations and evaluation results of the samples of Comparative Examples 1 to 6 are shown. 3, respectively.

Figure 2023033350000002
Figure 2023033350000002

Figure 2023033350000003
Figure 2023033350000003

Figure 2023033350000004
Figure 2023033350000004

実施例１～１１の化粧シートは、いずれも表面色調に優れ、耐塩基性、接着性ともに比較例１～６よりも優れていた。
一方、比較例１で得られた化粧シートは再生樹脂の着色により明度が低く、再生樹脂が塩基に曝されることよってクラックが発生し、木材に対する接着力も実施例１～１１と比較して弱い。
また、比較例２、３で得られた化粧シートは、第２層が薄いため、再生樹脂を用いた第１層の着色を隠蔽できない。また、耐塩基性の評価では、塩基が第１層の再生樹脂まで浸透し、クラックが発生した。比較例４で得られた化粧シートは木材に対する接着力が実施例１～１１と比較して低下した。比較例５で得られた化粧シートは木材に対する接着力が実施例１～１１と比較して低下した。比較例６で得られた化粧シートは、耐塩基性の評価では、塩基によってクラックが発生し、木材に対する接着力が実施例１～１１と比較して低下した。
以上の実施例から、本発明の化粧シートの優れた表面色調、耐塩基性、および接着性が確認された。 The decorative sheets of Examples 1-11 were all excellent in surface color tone, and superior to Comparative Examples 1-6 in both base resistance and adhesiveness.
On the other hand, the decorative sheet obtained in Comparative Example 1 has low brightness due to the coloring of the recycled resin, cracks occur due to the exposure of the recycled resin to base, and the adhesive strength to wood is weaker than that of Examples 1 to 11. .
In addition, the decorative sheets obtained in Comparative Examples 2 and 3 have a thin second layer, and therefore cannot conceal the coloring of the first layer using the recycled resin. In addition, in the evaluation of base resistance, the base penetrated into the recycled resin of the first layer, and cracks were generated. The decorative sheet obtained in Comparative Example 4 had lower adhesion to wood than those of Examples 1-11. The decorative sheet obtained in Comparative Example 5 had lower adhesion to wood than those of Examples 1-11. In the base resistance evaluation, the decorative sheet obtained in Comparative Example 6 had cracks due to the presence of a base, and the adhesion to wood was lower than in Examples 1 to 11.
From the above examples, it was confirmed that the decorative sheet of the present invention has excellent surface color tone, base resistance and adhesiveness.

本発明の化粧シートは、親環境的であり、かつ明度が高い白色や淡色の化粧シートとして有用である。 The decorative sheet of the present invention is environmentally friendly and useful as a bright white or light colored decorative sheet.

１０…化粧シート
１１…第１層
１２…第２層
１３…第３層
Ｗ…壁面 DESCRIPTION OF SYMBOLS 10... Decorative sheet 11... 1st layer 12... 2nd layer 13... 3rd layer W... Wall surface

本発明は、下記の態様を有する。
＜１＞ＰＥＴボトルに由来する再生ＰＥＴ系樹脂を７０質量％以上含む第１樹脂成分、および白色系顔料を有し、厚みが１８４μｍ以下の範囲である第１層と、前記第１層の一面側に重ねて配され、バージン樹脂を７０質量％以上含む第２樹脂成分、および白色系顔料を有し、厚みが２５μｍ以上である第２層と、前記第１層の他面側に重ねて配されるとともに壁面側にあり、バージン樹脂を８０質量％以上含む第３樹脂成分、および前記第３樹脂成分１００質量部に対して５質量部以下の範囲の白色系顔料を含む第３層と、を有し、前記第１層と前記第２層と前記第３層の合計厚みが２５０μｍ以下であり、前記第１層に含まれる白色系顔料と前記第２層に含まれる白色系顔料との合計は、前記第１樹脂成分と前記第２樹脂成分との合計２００質量部に対して１１．１質量部以上であることを特徴とする化粧シート。
＜２＞前記第１層に含まれる白色系顔料は、前記第１樹脂成分１００質量部に対して５質量部以上、１５質量部以下の範囲であり、前記第２層に含まれる白色系顔料は、前記第
２樹脂成分１００質量部に対して、５質量部以上、１５質量部以下の範囲であることを特徴とする＜１＞記載の化粧シート。
＜３＞前記第２樹脂成分には、前記再生ＰＥＴ系樹脂を３０質量％以下の範囲で更に含むことを特徴とする＜１＞または＜２＞記載の化粧シート。
＜４＞前記第３樹脂成分は、前記再生ＰＥＴ系樹脂を５質量％以下の範囲で更に含むことを特徴とする＜１＞ないし＜３＞いずれか記載の化粧シート。
＜５＞前記第２層の表面側において、ＣＩＥ １９７６ Ｌ＊ａ＊ｂ＊色空間におけるＬ＊が９２以上であることを特徴とする＜１＞ないし＜４＞いずれか記載の化粧シート。 The present invention has the following aspects.
<1> A first layer having a first resin component containing 70% by mass or more of recycled PET resin derived from PET bottles and a white pigment and having a thickness of 184 μm or less , and one surface of the first layer A second layer having a thickness of 25 μm or more and having a second resin component containing 70% by mass or more of a virgin resin and a white pigment and having a thickness of 25 μm or more; a third resin component disposed on the wall side and containing 80% by mass or more of a virgin resin; and wherein the total thickness of the first layer, the second layer, and the third layer is 250 μm or less, and the white pigment contained in the first layer and the white pigment contained in the second layer is 11.1 parts by mass or more with respect to a total of 200 parts by mass of the first resin component and the second resin component .
<2> The white pigment contained in the first layer is in the range of 5 parts by mass or more and 15 parts by mass or less with respect to 100 parts by mass of the first resin component, and the white pigment contained in the second layer is in the range of 5 parts by mass or more and 15 parts by mass or less with respect to 100 parts by mass of the second resin component.
<3> The decorative sheet according to <1> or <2>, wherein the second resin component further contains the recycled PET resin in an amount of 30% by mass or less.
<4> The decorative sheet according to any one of <1> to <3>, wherein the third resin component further contains the recycled PET resin in an amount of 5% by mass or less.
<5> The decorative sheet according to any one of <1> to <4>, wherein L* in the CIE 1976 L*a*b* color space is 92 or more on the surface side of the second layer.

Claims (5)

ＰＥＴボトルに由来する再生ＰＥＴ系樹脂を７０質量％以上含む第１樹脂成分、および白色系顔料を含む第１層と、
前記第１層の一面側に重ねて配され、バージン樹脂を７０質量％以上含む第２樹脂成分、および白色系顔料を有し、厚みが２５μｍ以上、７５μｍ以下の範囲である第２層と、
前記第１層の他面側に重ねて配され、バージン樹脂を８０質量％以上含む第３樹脂成分を有し、白色系顔料が前記第３樹脂成分１００質量部に対して５質量部以下であることを特徴とする化粧シート。 a first layer containing a first resin component containing 70% by mass or more of a recycled PET-based resin derived from a PET bottle and a white pigment;
a second layer disposed on one side of the first layer, having a second resin component containing 70% by mass or more of a virgin resin and a white pigment, and having a thickness in the range of 25 μm or more and 75 μm or less;
It has a third resin component that is superimposed on the other surface of the first layer and contains 80% by mass or more of a virgin resin, and the white pigment is 5 parts by mass or less with respect to 100 parts by mass of the third resin component. A cosmetic sheet characterized by: 前記第１層に含まれる白色系顔料は、前記第１樹脂成分１００質量部に対して５質量部以上、１５質量部以下の範囲であり、
前記第２層に含まれる白色系顔料は、前記第２樹脂成分１００質量部に対して、５質量部以上、１５質量部以下の範囲であることを特徴とする請求項１記載の化粧シート。 The white pigment contained in the first layer is in the range of 5 parts by mass or more and 15 parts by mass or less with respect to 100 parts by mass of the first resin component,
2. The decorative sheet according to claim 1, wherein the white pigment contained in said second layer is in the range of 5 parts by mass or more and 15 parts by mass or less with respect to 100 parts by mass of said second resin component. 前記第２樹脂成分には、前記再生ＰＥＴ系樹脂を３０質量％以下の範囲で更に含むことを特徴とする請求項１または２記載の化粧シート。 3. The decorative sheet according to claim 1, wherein the second resin component further contains the recycled PET-based resin in an amount of 30% by mass or less. 前記第３樹脂成分は、前記再生ＰＥＴ系樹脂を５質量％以下の範囲で更に含むことを特徴とする請求項１ないし３いずれか一項記載の化粧シート。 4. The decorative sheet according to any one of claims 1 to 3, wherein the third resin component further contains the recycled PET resin in an amount of 5% by mass or less. 前記第２層の表面側において、ＣＩＥ １９７６ Ｌ＊ａ＊ｂ＊色空間におけるＬ＊が９２以上であることを特徴とする請求項１ないし４いずれか一項記載の化粧シート。 5. The decorative sheet according to any one of claims 1 to 4, wherein L* in the CIE 1976 L*a*b* color space is 92 or more on the surface side of the second layer.
JP2022211252A 2018-12-10 2022-12-28 makeup sheet Active JP7386311B2 (en)