JP2022534232A - リチウム二次電池用正極、その製造方法、及びそれを含むリチウム二次電池 - Google Patents
リチウム二次電池用正極、その製造方法、及びそれを含むリチウム二次電池 Download PDFInfo
- Publication number
- JP2022534232A JP2022534232A JP2021569532A JP2021569532A JP2022534232A JP 2022534232 A JP2022534232 A JP 2022534232A JP 2021569532 A JP2021569532 A JP 2021569532A JP 2021569532 A JP2021569532 A JP 2021569532A JP 2022534232 A JP2022534232 A JP 2022534232A
- Authority
- JP
- Japan
- Prior art keywords
- positive electrode
- active material
- layer
- secondary battery
- positive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明のさらに他の側面は、前記二次電池用正極を採用したリチウム二次電池を提供することである。
前記正極集電体の少なくとも一面上に配され、第1正極活物質を含む第1層と、
前記第1層上に配され、第2正極活物質を含む第2層と、を含み、
前記第1正極活物質は、下記化学式1で表され、
前記第2正極活物質は、下記化学式1または下記化学式2で表され、
前記第1正極活物質及び前記第2正極活物質は、互いに異なる、二次電池用正極が提供される:
[化1]
LixNiyM1-yO2
[化2]
LiαCoβM’1-βO2
前記化学式1,2で、
0.9≦x≦1.2、0.1≦y≦0.98であり、
0.9≦α≦1.2、0≦β≦1.0であり、
M及びM’は、互いに独立して、1種以上の酸化数+2価または酸化数+3価の金属または遷移金属元素である。
前記第1層上に、第2正極活物質を含む第2組成物を塗布し、第2層を形成する段階と、を含み、
前記第1正極活物質は、下記化学式1で表され、
前記第2正極活物質は、下記化学式1または下記化学式2で表され、
前記第1正極活物質及び前記第2正極活物質は、互いに異なる、二次電池用正極の製造方法が提供される:
[化1]
LixNiyM1-yO2
[化2]
LiαCoβM’1-βO2
前記化学式1,2で、
0.9≦x≦1.2、0.1≦y≦0.98であり、
0.9≦α≦1.2、0≦β≦1.0であり、
M及びM’は、互いに独立して、1種以上の酸化数+2価または酸化数+3価の金属または遷移金属元素である。
前記正極に対向して配される負極と、
前記正極と前記負極との間に配される電解質と、を含むリチウム二次電池が提供される。
以下、図2を参照し、本発明の一実施例による二次電池用正極について説明する。図2は、例示的な具現例による二次電池用正極の模式図である。図2を参照すれば、一側面による二次電池用正極10は、正極集電体11と、前記正極集電体11の少なくとも一面上に配され、第1正極活物質を含む第1層12と、前記第1層12上に配され、第2正極活物質を含む第2層13と、を含む。
[化1]
LixNiyM1-yO2
前記化学式1で、
0.9≦x≦1.2、0.1≦y≦0.98であり、
Mは、1種以上の酸化数+2価または酸化数+3価の金属または遷移金属元素である。
ただし、前記Mは、Niではない元素である。
[化1A]
Lix1Niy1M11-y1O2
前記化学式1Aで、
[化1B]
Lix2Niy2M1-y2O2
前記化学式1A,1Bで、M1、x1、y1、M2、x2、y2に係わる定義は、本明細書において、M、x、yについて定義されたところを参照し、
ただし、y1>y2である。
[化1-1]
Lix’Niy’Co1-y’-z’Alz’O2
[化1-2]
Lix’Niy’Co1-y’-z’Mnz’O2
前記化学式1-1及び前記化学式1-2で、0.9≦x’≦1.2、0.1≦y’≦0.98、0<z’<0.5、0<1-y’-z’<0.5である。
一具現例において、前記第1層11及び第2層12を含む正極活物質層の厚みは、40μm以上でもある。
例えば、前記正極活物質層の厚みは、40μmないし110μmでもある。
[化1]
LixNiyM1-yO2
[化2]
LiαCoβM’1-βO2
前記化学式1,2で、
0.9≦x≦1.2、0.1≦y≦0.98であり、
0.9≦α≦1.2、0≦β≦1.0であり、
M及びM’は、互いに独立して、1種以上の酸化数+2価または酸化数+3価の金属または遷移金属元素である。
[化1-1]
Lix’Niy’Co1-y’-z’Alz’O2
[化1-2]
Lix’Niy’Co1-y’-z’Mnz’O2
前記化学式1-1及び前記化学式1-2で、0.9≦x’≦1.2、0.1≦y’≦0.98、0<z’<0.5、0<1-y’-z’<0.5である。
一具現例において、前記第2層13に含まれる第2正極活物質は、LiCoO2でもある。
一具現例において、前記第1層12対第2層13の活物質ローディング量比は、3:7ないし7:3でもある。一具現例において、前記第1層12のローディング量は、3ないし40mg/cm2でもある。他の具現例において、前記第2層13のローディング量は、40ないし3mg/cm2でもある。
[化1]
LixNiyM1-yO2
前記化学式1で、
0.9≦x≦1.2、0.1≦y≦0.98であり、
Mは、1種以上の酸化数+2価または酸化数+3価の金属または遷移金属元素である。
[化1A]
Lix1Niy1M11-y1O2
前記化学式1Aで、
[化1B]
Lix2Niy2M21-y2O2
[化1C]
Lix3Niy3M31-y3O2
前記化学式1A,1B,1Cで、M1、x1、y1、M2、x2、y2、M3、x3、y3に係わる定義は、本明細書において、M、x、yについて定義されたところを参照し、
ただし、y1>y2>y3である。
[化1]
LixNiyM1-yO2
[化2]
LiαCoβM’1-βO2
前記化学式1,2で、
0.9≦x≦1.2、0.1≦y≦0.98であり、
0.9≦α≦1.2、0≦β≦1.0であり、
M及びM’は、互いに独立して、1種以上の酸化数+2価または酸化数+3価の金属または遷移金属元素である。
前記溶媒としては、N-メチルピロリドン、アセトンまたは水などが使用されうるが、それらに限定されるものではなく、当該技術分野で使用されうるものであるならば、いずれも使用されうる。
例えば、負極活物質、導電材、バインダ及び溶媒を混合し、負極活物質組成物が準備される。前記負極活物質組成物が、金属集電体上に、直接コーティングされて乾燥され、負極板が製造される。代案としては、前記負極活物質組成物が、別途の支持体上にキャスティングされた後、前記支持体から剥離されたフィルムが金属集電体上にラミネーションされても負極板が製造される。
次に、前記正極と前記負極との間に挿入されるセパレータが準備される。
例えば、前記電解質は、有機電解液でもある。また、前記電解質は、固体でもある。例えば、ボロン酸化物、リチウムオキシナイトライドなどでもあるが、それらに限定されるものではなく、当該技術分野において、固体電解質として使用されうるものであるならば、いずれも使用可能である。前記固体電解質は、スパッタリングのような方法で、前記負極上にも形成される。
例えば、該有機電解液は、有機溶媒にリチウム塩が溶解されても製造される。
実施例1
(正極の製造)
第1正極活物質として、LiNi0.8Mn0.1Co0.1O2 96重量%、導電材として、super-p 2重量%、及びバインダとして、ポリフッ化ビニリデン2重量%を混合し、第1組成物を製造した。前記第1組成物を、厚みが20μmほどの正極集電体であるアルミニウム(Al)薄膜に塗布し、約80℃で20分間乾燥させた後、ロールプレス(roll press)を施し、第1層が塗布された正極を得た。
前記正極の構造を示す模式図は、図5に図示されている。
リチウム塩として、1.15M LiPF6を含み、エチレンカーボネート(EC)、プロピレンカーボネート(PC)、エチルプロピオネート(EP)及びプロピレンプロピオネート(PP)の2:1:2:5体積比混合溶媒に、フルオロエチレンカーボネート(FEC)7重量%を添加し、リチウム二次電池用電解質を製造した。
前記正極、リチウムメタル負極及びセラミックスがコーティングされた厚み18μmポリエチレンセパレータ及び前記電解液を使用し、ハーフセル形態のリチウム二次電池を製造した。このとき、前記リチウム二次電池の作動電圧は、3.0ないし4.35Vであった。
前記第1層の電流密度は、約1.2mAh/cm2であり、第2層の電流密度は、約0.9mAh/cm2であり、第3層の電流密度は、約0.9mAh/cm2であり、前記第1層、前記第2層及び前記第3層の電流密度比は、4:3:3ほどに調節したことを除いては、実施例1と同一方法で、リチウム二次電池を製造した。
このとき、前記正極のローディングレベルは、15mg/cm2であった。
下記のような方法によって製造された正極を使用したことを除いては、実施例1と同一方法で、リチウム二次電池を製造した。
第1正極活物質として、LiNi0.8Mn0.1Co0.1O2 96重量%、導電材として、super-p 2重量%、及びバインダとして、ポリフッ化ビニリデン2重量%を混合し、第1組成物を製造した。前記第1組成物を、厚みが20μmほどの正極集電体であるアルミニウム(Al)薄膜に塗布し、約80℃で20分間乾燥させた後、ロールプレスを施し、第1層が塗布された正極を得た。
このとき、前記正極のローディングレベルは、28mg/cm2であった。
下記のような方法によって製造された正極を使用したことを除いては、実施例1と同一方法で、リチウム二次電池を製造した。
正極活物質として、LiNi0.6Mn0.2Co0.2O2 96重量%、導電材として、super-p 2重量%、及びバインダとして、ポリフッ化ビニリデン2重量%を混合し、正極組成物を製造した。前記正極組成物を、厚みが20μmほどの正極集電体であるアルミニウム(Al)薄膜に塗布し、約80℃で20分間乾燥させた後、ロールプレスを施し、正極を得た。このとき、前記正極において、正極活物質層の厚みは、約80μmであり、正極の電流密度は、5.6mAh/cm2であり、ローディングレベルは、28mg/cm2であった。
前記正極の構造を示す模式図は、図6に図示されている。
下記のような方法によって製造された正極を使用したことを除いては、実施例1と同一方法で、リチウム二次電池を製造した。
正極活物質として、LiNi0.6Mn0.2Co0.2O2 96重量%、導電材として、super-p 2重量%、及びバインダとして、ポリフッ化ビニリデン2重量%を混合し、正極組成物を製造した。前記正極組成物を、厚みが20μmほどの正極集電体であるアルミニウム(Al)薄膜に塗布し、約80℃で20分間乾燥させた後、ロールプレスを施し、正極を得た。このとき、前記正極において、正極活物質層の厚みは、約43μmであり、正極の電流密度は、3mAh/cm2であり、ローディングレベルは、15mg/cm2であった。
下記のような方法によって製造された正極を使用したことを除いては、実施例1と同一方法で、リチウム二次電池を製造した。
第1正極活物質として、LiNi0.33Mn0.33Co0.33O2 96重量%、導電材として、super-p 2重量%、及びバインダとして、ポリフッ化ビニリデン2重量%を混合し、第1組成物を製造した。前記第1組成物を、厚みが20μmほどの正極集電体であるアルミニウム(Al)薄膜に塗布し、約80℃で20分間乾燥させた後、ロールプレスを施し、第1層が塗布された正極を得た。
このとき、前記正極のローディングレベルは、28mg/cm2であった。
前記実施例1及び前記比較例1で製造されたリチウム二次電池につき、2.8ないし4.3Vの電圧範囲内において、0.2Cの定電流で1サイクル充電し、電圧変化による容量変化を示す充電プロファイル特性を評価した。
前記実施例1及び前記比較例1で製造されたリチウム二次電池につき、充電条件(0.7C/4.35Vの定電流/定電圧、0.025Cカットオフ電流、10分休息)下と放電条件(1.0Cの定電圧、3.0Vカットオフ電圧、10分休息)下とにおいて充放電し、40サイクル間の容量を測定し、図8に示した。
(正極の製造)
第1正極活物質として、LiNi0.8Mn0.1Co0.1O2 96重量%、導電材として、super-p 2重量%、及びバインダとして、ポリフッ化ビニリデン2重量%を混合し、第1組成物を製造した。前記第1組成物を、厚みが20μmほどの正極集電体であるアルミニウム(Al)薄膜に塗布し、約80℃で20分間乾燥させた後、ロールプレスを施し、第1層が塗布された正極を得た。
負極活物質として、黒鉛98重量%、バインダ2重量%を混合し、蒸溜水に投入した後、機械式撹拌器を使用して60分間分散させ、負極活物質組成物を製造した。前記負極活物質組成物を、ドクターブレードを使用し、厚み10μmの銅集電体上に、約60μm厚に塗布し、100℃の熱風乾燥器で、0.5時間乾燥させた後、真空、120℃の条件で、4時間さらに1回乾燥させて圧延し、集電体上に、負極活物質層が形成された負極を製造した。
リチウム塩として、1.15M LiPF6を含み、エチレンカーボネート(EC)、プロピレンカーボネート(PC)、エチルプロピオネート(EP)及びプロピレンプロピオネート(PP)の2:1:2:5体積比混合溶媒に、フルオロエチレンカーボネート(FEC)7重量%を添加し、リチウム二次電池用電解質を製造した。
前記正極、前記負極、セラミックスがコーティングされた厚み18μmポリエチレンセパレータ、及び前記電解液を使用し、リチウム二次電池を製造した。このとき、前記リチウム二次電池の作動電圧は、3.0ないし4.35Vであった。
前記正極の電流密度が2.6mAh/cm2になるように、第1正極活物質及び第2正極活物質の含量を調節したことを除いては、実施例4と同一方法で、リチウム二次電池を製造した。このとき、前記リチウム二次電池の作動電圧は、3.0ないし4.35Vであった。正極において、該第1正極活物質と該第2正極活物質との含量比は、7:3であった。
前記正極の電流密度が3.4mAh/cm2になるように、第1正極活物質及び第2正極活物質の含量を調節したことを除いては、実施例4と同一方法で、リチウム二次電池を製造した。このとき、前記リチウム二次電池の作動電圧は、3.0ないし4.35Vであった。正極において、該第1正極活物質と該第2正極活物質との含量比は、7:3であった。
前記リチウム二次電池の作動電圧を3.0ないし4.4Vに調節したことを除いては、実施例4と同一方法で、リチウム二次電池を製造した。正極において、第1正極活物質と第2正極活物質との含量比は、7:3であった。
前記第1層のローディング量が約8.75mg/cm2であり、前記第2層のローディング量が約8.75mg/cm2であり、該第1層と該第2層とのローディング量比が5:5ほどになるように調節したことを除いては、実施例4と同一方法で、リチウム二次電池を製造した。正極において、該第1正極活物質と該第2正極活物質との含量比は、5:5であった。
(正極の製造)
第1正極活物質として、LiNi0.8Mn0.1Co0.1O2 28.8重量%、第2正極活物質として、LiCoO2 67.2重量%、導電材として、super-p 2重量%、及びバインダとして、ポリフッ化ビニリデン2重量%を混合し、正極組成物を製造した。前記正極組成物を、厚みが20μmほどの正極集電体であるアルミニウム(Al)薄膜に塗布し、約80℃で20分間乾燥させた後、ロールプレスを施し、正極を製造した。このとき、前記正極活物質層の厚みは、約40μmであった。また、正極の電流密度は、3.0mAh/cm2であった。
実施例4で使用された負極を使用した。
実施例4で使用された電解質を使用した。
前記正極、前記負極、セラミックスがコーティングされた厚み18μmポリエチレンセパレータ、及び前記電解液を使用し、リチウム二次電池を製造した。このとき、前記リチウム二次電池の作動電圧は、3.0ないし4.35Vであった。
前記正極の電流密度が2.6mAh/cm2になるように、第1正極活物質及び第2正極活物質の含量を調節したことを除いては、比較例4と同一方法で、リチウム二次電池を製造した。このとき、前記リチウム二次電池の作動電圧は、3.0ないし4.35Vであった。
前記正極の電流密度が3.4mAh/cm2になるように、第1正極活物質及び第2正極活物質の含量を調節したことを除いては、比較例4と同一方法で、リチウム二次電池を製造した。このとき、前記リチウム二次電池の作動電圧は、3.0ないし4.35Vであった。
前記リチウム二次電池の作動電圧を3.0ないし4.4Vに調節したことを除いては、比較例4と同一方法で、リチウム二次電池を製造した。
第1正極活物質として、LiNi0.8Mn0.1Co0.1O2 48重量%、第2正極活物質として、LiCoO2 48重量%、導電材として、super-p 2重量%、及びバインダとして、ポリフッ化ビニリデン2重量%を混合し、正極組成物を製造したことを除いては、比較例4と同一方法で、リチウム二次電池を製造した。
前記実施例4及び前記比較例4で製造されたリチウム二次電池につき、充電条件(0.2C/4.35Vの定電流/定電圧、0.025Cカットオフ電流、10分休息)下と放電条件(0.2Cの定電圧、3.0Vカットオフ電圧、10分休息)下とで充放電し、放電プロファイルを測定し、図9に示した。
図9を参照すれば、実施例4によるリチウム二次電池は、複層の正極活物質を適用しながら、容量特性に比較的劣るLCOを正極活物質の中に含んでいても、NCM系正極活物質を適用した比較例4によるリチウム二次電池に比べ、大きく劣らないレベルの放電容量を発揮するということを確認することができる。
前記実施例4及び前記比較例4で製造されたリチウム二次電池につき、充電条件(0.7C/4.35Vの定電流/定電圧、0.025Cカットオフ電流、10分休息)下と放電条件(1.0Cの定電圧、3.0Vカットオフ電圧、10分休息)下とで充放電し、300サイクル間の容量を測定し、図10に示した。
2 負極
3 正極
4 セパレータ
5 電池ケース
6 キャップアセンブリ
10 二次電池用正極
11 正極集電体
12 第1層
13 第2層
20 二次電池用正極
21 正極集電体
22 第1層
23 第2層
24 第3層
Claims (20)
- 正極集電体と、
前記正極集電体の少なくとも一面上に配され、第1正極活物質を含む第1層と、
前記第1層上に配され、第2正極活物質を含む第2層と、を含み、
前記第1正極活物質は、下記化学式1で表され、
前記第2正極活物質は、下記化学式1または下記化学式2で表され、
前記第1正極活物質及び前記第2正極活物質は、互いに異なる、二次電池用正極:
[化1]
LixNiyM1-yO2
[化2]
LiαCoβM’1-βO2
前記化学式1,2で、
0.9≦x≦1.2、0.1≦y≦0.98であり、
0.9≦α≦1.2、0≦β≦1.0であり、
M及びM’は、互いに独立して、1種以上の酸化数+2価または酸化数+3価の金属または遷移金属元素である。 - 前記M及び前記M’は、互いに独立して、Al、Mg、Mn、Co、Fe、Cr、V、Ti、Cu、B、Ca、Zn、Zr、Nb、Mo、Sr、Sb、W及びBiからなる群うちから選択される1以上の元素である、請求項1に記載の二次電池用正極。
- 前記第1正極活物質は、下記化学式1Aで表され、前記第2正極活物質は、下記化学式1Bで表される、請求項1に記載の二次電池用正極:
[化1A]
Lix1Niy1M11-y1O2
[化1B]
Lix2Niy2M1-y2O2
前記化学式1A,1Bで、M1、x1、y1、M2、x2、y2に係わる定義は、請求項1において、M、x、yについて定義されたところを参照し、
ただし、y1>y2である。 - 前記第1正極活物質は、下記化学式1-1または下記化学式1-2で表され、
前記第2正極活物質は、下記化学式1-1または下記化学式1-2で表されるか、またはLiCoO2であり、前記第1正極活物質及び前記第2正極活物質は、互いに異なる、請求項1に記載の二次電池用正極:
[化1-1]
Lix’Niy’Co1-y’-z’Alz’O2
[化1-2]
Lix’Niy’Co1-y’-z’Mnz’O2
前記化学式1-1及び前記化学式1-2で、0.9≦x’≦1.2、0.1≦y’≦0.98、0<z’<0.5、0<1-y’-z’<0.5である。 - 前記第1正極活物質においてNiの含量は、遷移金属総モル数を基準に、0.6モル以上である、請求項1に記載の二次電池用正極。
- 前記第2正極活物質が化学式1で表されるとき、前記第2正極活物質におけるNi含量は、遷移金属総モル数を基準に、0.6モル以下である、請求項1に記載の二次電池用正極。
- 前記第1正極活物質及び第2正極活物質の重量比は、3:7ないし7:3である、請求項1に記載の二次電池用正極。
- 前記第1層対第2層の活物質ローディング量比は、3:7ないし7:3である、請求項1に記載の二次電池用正極。
- 前記第1層対第2層の電流密度比は、2:8ないし8:2である、請求項1に記載の二次電池用正極。
- 前記第1層対第2層の厚み比は、2:8ないし8:2である、請求項1に記載の二次電池用正極。
- 前記第1層のローディング量は、3mg/cm2ないし40mg/cm2である、請求項1に記載の二次電池用正極。
- 前記第2層のローディング量は、40mg/cm2ないし3mg/cm2である、請求項1に記載の二次電池用正極。
- 前記正極の電流密度は、2ないし10mAh/cm2である、請求項1に記載の二次電池用正極。
- 前記第2層上に配され、第3正極活物質を含む第3層をさらに含み、
前記第3正極活物質は、下記化学式1で表され、前記第3正極活物質は、前記第1正極活物質及び前記第2正極活物質と異なる組成を有する、請求項1に記載の二次電池用正極:
[化1]
LixNiyM1-yO2
前記化学式1で、
0.9≦x≦1.2、0.1≦y≦0.98であり、
Mは、1種以上の酸化数+2価または酸化数+3価の金属または遷移金属元素である。 - 前記第1正極活物質は、下記化学式1Aで表され、前記第2正極活物質は、下記化学式1Bで表され、前記第3正極活物質は、下記化学式1Cで表される、請求項14に記載の二次電池用正極:
[化1A]
Lix1Niy1M11-y1O2
[化1B]
Lix2Niy2M21-y2O2
[化1C]
Lix3Niy3M31-y3O2
前記化学式1A,1B,1CでM1、x1、y1、M2、x2、y2、M3、x3、y3に係わる定義は、請求項1において、M、x、yについて定義されたところを参照し、
ただし、y1>y2>y3である。 - 前記第3層の電流密度は、第2層の電流密度以下であり、前記第2層の電流密度は、前記第1層の電流密度以下である、請求項14に記載の二次電池用正極。
- 前記第1層及び前記第2層を含む正極活物質層の厚みは、40μm以上である、請求項1に記載の二次電池用正極。
- 前記二次電池用正極の総重量を基準に、前記第1正極活物質及び前記第2正極活物質の含量の和は、80ないし98重量%である、請求項1に記載の二次電池用正極。
- 請求項1ないし18のうちいずれか1項に記載の二次電池用正極と、
前記正極に対向して配される負極と、
前記正極と前記負極との間に配される電解質と、を含むリチウム二次電池。 - 前記リチウム二次電池の作動電圧は、2.5ないし4.5Vである、請求項19に記載のリチウム二次電池。