JP2022025308A - Antistatic, antibacterial and antifungal film material - Google Patents

Abstract

To provide a film material (coated film, film, sheet, tarpaulin, canvas, synthetic leather, etc.) which is a film material made of a soft vinyl chloride resin that stably and persistently exhibits antistatic properties, can suppress electrostatic adsorption of allergenic substances and has antibacterial and antifungal properties, antiviral properties and antiallergenic properties, which does not cause a blocking problem such as contamination by bleeding, and accretion between film materials.SOLUTION: As a soft vinyl chloride resin sheet containing at least an ionic liquid compound and a plasticizer having a molecular weight of 390 or more, the ionic liquid contains is formed of a counter ion with an organic cation, an inorganic anion and/or an organic anion, and the organic cation is one or more selected from an imidazolium base, an imidazolinium base, a pyridinium base, a pyrazolium base, a pyrrolidinium base, a piperidinium base, an ammonium base, a phosphonium base and a sulfonium base.SELECTED DRAWING: None

Description

本発明は、健康阻害要因、及び悪臭発生要因となり得る雑菌や黴の増殖を抑止する抗菌防黴性、さらにウイルスの飛沫感染予防となる抗ウイルス性を安定持続し、しかも黴、ダニダスト（死骸、糞塵）、花粉などのアレルゲン物質を静電吸着する心配のない帯電防止性を備えた膜材に関する。本発明の帯電防止性抗菌防黴膜材は、フィルム、シート、テープの形態、織物、ターポリン、メッシュシート、合成皮革、帆布などの形態で用いられ、これらの原反パーツを熱融着法で縫製し、天井膜、空間仕切り、巻上昇降式シートシャッター、クリーンルームカーテン、壁紙、敷物、カバー、ブラインド、防護衣、フェイスガード、など加工されて、工場、オフィス、学校、商業施設、病院、介護施設、式場、ごみ集積場、公衆トイレ、動物園などに広く使用される。特にターポリン、帆布などは、医療検査用パーティション、空気注入式仮設膜構造による医療検査用陰圧テントシェルターに適して用いることができる。 INDUSTRIAL APPLICABILITY The present invention stably maintains antibacterial and antifungal properties that suppress the growth of germs and molds that can cause health-inhibiting factors and malodors, and also prevents virus droplet infections, and molds and mite dust (dead bodies, etc.). It relates to a film material having antistatic properties that does not have to worry about electrostatically adsorbing allergen substances such as feces) and pollen. The antistatic antibacterial antifungal film material of the present invention is used in the form of a film, a sheet, a tape, a woven fabric, a tarpaulin, a mesh sheet, a synthetic leather, a canvas, etc. Sewing, ceiling film, space partition, hoisting lift sheet shutter, clean room curtain, wallpaper, rug, cover, blind, protective clothing, face guard, etc. are processed, factory, office, school, commercial facility, hospital, nursing care Widely used in facilities, ceremonial halls, garbage collection areas, public toilets, zoos, etc. In particular, tarpaulins, canvas and the like can be suitable for medical examination partitions and negative pressure tent shelters for medical examinations due to an inflatable temporary membrane structure.

静電気の除去を促すために界面活性剤を利用する方法は古くから行われ、埃の付着防止が目的であれば表面固有抵抗値を１０¹²Ω台以下にすれば十分となる。界面活性剤の分子は親水基と親油基を持ち、合成樹脂成型品の表面に塗布すると親油基が合成樹脂成型品の表面に向き、外部を向いた親水基が空気中の水分を吸着し、その水分子の層がわずかな電気伝導性を発現することで電荷を漏洩させる機構であるが、この効果発現は湿度依存性とする難点を有している。界面活性剤などの帯電防止剤を合成樹脂成型品に適用するには、１）合成樹脂成型品の表面に塗布する方法、２）合成樹脂成型品内部に練り込む方法がある。塗布用(外部用)帯電防止剤は使用法が簡便であるが、表面を拭き取ったり洗浄したりすると、その制電性が著しく低下する欠点がある。また練り込み用(内部用帯電防止剤)では練り込まれた帯電防止剤は少しずつ表面に浸出(ブリードアウト)することで帯電防止作用を持続するが、合成樹脂のガラス転移点以下の温度では拡散が起こりにくい欠点を有している。一方、カーボンブラックを導電性フィラーとして添加する方法が汎用的であるが、この方法だと、合成樹脂成型品中に濃密に分散したカーボンブラック粒子の連結が電荷の通り道となる導電回路を形成することで優れた導電性を付与するものであり、効果の持続性や湿度依存性に優れている。しかし、カーボンブラック自体の黒色の影響で合成樹脂成型品外観を黒色として、透明品、任意の着色品が得られない難点があった。 The method of using a surfactant to promote the removal of static electricity has been used for a long time, and if the purpose is to prevent the adhesion of dust, it is sufficient to set the surface intrinsic resistance value to 10 ¹² Ω or less. Surfactant molecules have a hydrophilic group and a lipophilic group, and when applied to the surface of a synthetic resin molded product, the lipophilic group faces the surface of the synthetic resin molded product, and the outwardly facing hydrophilic group adsorbs moisture in the air. However, the mechanism is such that the layer of water molecules leaks electric charge by exhibiting a slight electric conductivity, but the manifestation of this effect has a drawback of being humidity-dependent. To apply an antistatic agent such as a surfactant to a synthetic resin molded product, there are 1) a method of applying it to the surface of the synthetic resin molded product, and 2) a method of kneading it into the synthetic resin molded product. The antistatic agent for application (for external use) is easy to use, but has the drawback that its antistatic property is significantly reduced when the surface is wiped or washed. For kneading (internal antistatic agent), the kneaded antistatic agent gradually seeps out (bleeds out) to the surface to maintain the antistatic effect, but at temperatures below the glass transition point of the synthetic resin, It has the drawback that diffusion is unlikely to occur. On the other hand, a method of adding carbon black as a conductive filler is generally used, but in this method, a conductive circuit is formed in which the connection of carbon black particles densely dispersed in a synthetic resin molded product serves as an electric charge path. As a result, excellent conductivity is imparted, and the effect is excellent in sustainability and humidity dependence. However, due to the influence of the black color of carbon black itself, the appearance of the synthetic resin molded product is black, and there is a problem that a transparent product or an arbitrary colored product cannot be obtained.

そこで、界面活性剤やカーボンブラックなどの一長一短のある帯電防止剤を使用せずに、帯電防止性を付与する手段として、織布の両面に軟質合成樹脂層を設けてなるフレキシブルコンテナで、軟質合成樹脂層に導電性可塑剤(リチウムイオン系可塑剤)を含有するフレキシブルコンテナ（特許文献１）が提案されている。しかしリチウムイオン系可塑剤は可塑化効率が悪く、所望の表面固有抵抗１０¹⁰ Ω以下導電性を得るために多量の配合量を必要とし、さらに汎用可塑剤も相当量必要とする（実施例１、実施例２）ため、軟質合成樹脂層が軟弱化、かつ脆弱化する傾向がありフレキシブルコンテナとして実用的ではない。また帯電防止性のフレキシブルコンテナとして、エチレン－酢酸ビニル共重合体樹脂１００質量部に高分子型永久帯電防止剤（ポリエチレンオキサイド系高分子）を１０～５０質量部含有したフレキシブルコンテナ用ターポリンの発明（特許文献２）が開示されている。しかし、ポリエチレンオキサイド系高分子は、軟質塩化ビニル樹脂との相溶性に劣り、本質的にこの２つをブレンドすること、透明化することはできず、また溶融温度の差によりシート加工することも困難である。従って、界面活性剤、カーボンブラック、高分子型永久帯電防止剤などの種々難点を有する帯電防止剤を使用せずに帯電防止性が安定持続的な軟質塩化ビニル樹脂製の汎用膜材が存在すれば、黴、ダニダスト（死骸、糞塵）、花粉などのアレルゲン物質が膜材に静電吸着して蓄積され、日常生活を脅かす心配の解消となる。そしてさらに抗菌防黴性、抗ウイルス性の兼備ともなれば、菌、黴、ウイルスなどが膜材に付着したとしても、これらの活性・増殖の抑止となることで、医療検査用パーティション、空気注入式仮設膜構造による医療検査用陰圧テントシェルターなどの膜構造物の部材に適した膜材に特化する。以前に本出願人はこの課題に対して、分子中に１個以上のエーテル結合を有する液状エステル化合物、及びイオン液体化合物を併用する帯電防止性樹脂層を備えた可撓性積層体（特許文献３）の提案を行った。この提案による可撓性積層体は確かに帯電防止性を有しアレルゲン物質を静電吸着し難く、抗菌防黴性を兼備するものであったが、イオン液体化合物と液状エステル化合物（分子中に１個以上のエーテル結合を有する）を多量含有させた場合に、経時的にこれらの液体が膜材表面にブリードし、このブリード液体に煤塵が付着蓄積する汚れ問題、ブリードで膜材同士が癒着するブロッキング問題を生じていた。昨今においてはこれらの汚れ問題、ブロッキング問題の解決に加え、抗ウイルス性、抗アレルゲン性（黴、ダニダスト、花粉）を有する膜材開発の要望が大きいものとなっている。 Therefore, as a means of imparting antistatic properties without using an antistatic agent such as a surfactant or carbon black, which has advantages and disadvantages, a flexible container provided with a soft synthetic resin layer on both sides of the woven fabric is used for soft synthesis. A flexible container (Patent Document 1) containing a conductive plasticizer (lithium ion-based plasticizer) in a resin layer has been proposed. However, the lithium-ion-based plasticizer has poor plasticization efficiency, requires a large amount to be blended in order to obtain a desired surface intrinsic resistance of 10 ¹⁰ Ω or less, and also requires a considerable amount of a general-purpose plasticizer (Example 1). Because of Example 2), the soft synthetic resin layer tends to be softened and fragile, which is not practical as a flexible container. Further, as an antistatic flexible container, an invention of a tarpaulin for a flexible container containing 10 to 50 parts by mass of a polymer-type permanent antistatic agent (polyethylene oxide-based polymer) in 100 parts by mass of an ethylene-vinyl acetate copolymer resin ( Patent Document 2) is disclosed. However, the polyethylene oxide polymer is inferior in compatibility with the soft vinyl chloride resin, and it is essentially impossible to blend the two, make them transparent, and process the sheet due to the difference in melting temperature. Have difficulty. Therefore, there is a general-purpose film material made of soft vinyl chloride resin that has stable and long-lasting antistatic properties without using antistatic agents having various drawbacks such as surfactants, carbon blacks, and polymer-type permanent antistatic agents. For example, allergen substances such as mold, mite dust (dead body, manure dust), and pollen are electrostatically adsorbed and accumulated on the membrane material, eliminating the concern that threatens daily life. Furthermore, if it also has antibacterial and anti-virus properties, even if bacteria, molds, viruses, etc. adhere to the membrane material, it will suppress the activity and proliferation of these, so that it will be a partition for medical examinations and air injection. Specializes in membrane materials suitable for members of membrane structures such as negative pressure tent shelters for medical examinations with a temporary membrane structure. Previously, the applicant has addressed this issue with a flexible laminate having an antistatic resin layer in which a liquid ester compound having one or more ether bonds in the molecule and an ionic liquid compound are used in combination (Patent Document). We made the proposal of 3). The flexible laminate according to this proposal certainly has antistatic properties, is difficult to electrostatically adsorb allergen substances, and also has antibacterial and antifungal properties. However, ionic liquid compounds and liquid ester compounds (in the molecule) When a large amount of (having one or more ether bonds) is contained, these liquids bleed on the surface of the membrane material over time, and soot and dust adhere to and accumulate on the bleed liquid. There was a blocking problem. In recent years, in addition to solving these stain problems and blocking problems, there is a great demand for the development of film materials having antiviral and antiallergenic properties (mold, mite dust, pollen).

特開２００２－２４０８８４号公報Japanese Unexamined Patent Publication No. 2002-240884 特開２０１７－０１９１４５号公報Japanese Unexamined Patent Publication No. 2017-019145 特開２０１９－０９３６２５号公報Japanese Unexamined Patent Publication No. 2019-093625

本発明は帯電防止性が安定持続的に発揮され、アレルゲン性（黴、ダニダスト、花粉）物質の静電吸着が抑止可能、かつ抗菌防黴性、抗ウイルス性、抗アレルゲン性（黴、ダニダスト、花粉）を兼備する軟質塩化ビニル樹脂製の膜材で、ブリードによる汚れ、膜材同士が癒着するブロッキング問題を生じることのない膜材（塗膜、フィルム、シート、ターポリン、帆布、合成皮革など）の提供を課題とする。 In the present invention, antistatic properties are stably and continuously exhibited, electrostatic adsorption of allergenic substances (mold, mite dust, pollen) can be suppressed, and antibacterial anti-mold, anti-viral, anti-allergenic properties (mold, mite dust, etc.) A film material made of soft vinyl chloride resin that also serves as pollen) and does not cause stains due to bleeding or blocking problems where the film materials adhere to each other (coating film, film, sheet, tarpaulin, sail cloth, synthetic leather, etc.) The issue is to provide.

本発明は上記の現状に鑑みて研究、検討を重ねた結果、少なくともイオン液体化合物、及び可塑剤を含有する軟質塩化ビニル樹脂シートであって、イオン液体化合物が、特定のカチオン及びアニオンのイオン対で形成されたものであることによって、上記従来技術で困難であった、帯電防止性が安定持続的に発揮され、アレルゲン性（黴、ダニダスト、花粉）物質の静電吸着が抑止可能、かつ抗菌防黴性、抗ウイルス性、抗アレルゲン性（黴、ダニダスト、花粉）を兼備する軟質塩化ビニル樹脂製の膜材で、ブリードによる汚れ、膜材同士が癒着するブロッキング問題を生じることのない膜材（塗膜、フィルム、シート、ターポリン、帆布、合成皮革など）が得られることを見出して本発明を完成するに至った。 As a result of repeated studies and studies in view of the above-mentioned current situation, the present invention is a soft vinyl chloride resin sheet containing at least an ionic liquid compound and a plasticizer, wherein the ionic liquid compound is an ion pair of a specific cation and anion. By being formed of, the antistatic property, which was difficult with the above-mentioned conventional technique, is stably and continuously exhibited, electrostatic adsorption of allergenic substances (mold, mite dust, pollen) can be suppressed, and antibacterial. A film material made of soft vinyl chloride resin that has anti-mold, anti-virus, and anti-allergenic properties (mold, mite dust, pollen), and does not cause stains due to bleeding or blocking problems in which the film materials adhere to each other. We have found that (coatings, films, sheets, tarpaulins, canvases, synthetic leathers, etc.) can be obtained, and have completed the present invention.

すなわち本発明の帯電防止性抗菌防黴膜材は、少なくともイオン液体化合物、及び分子量３９０以上の可塑剤を含有する軟質塩化ビニル樹脂シートであって、前記イオン液体化合物が、無機系アニオン、及び／または有機系アニオンの対イオンで形成され、前記有機系カチオンが、イミダゾリウム系、イミダゾリニウム系、ピリジニウム系、ピラゾリウム系、ピロリジニウム系、ピペリジニウム系、アンモニウム系、ホスホニウム系、スルホニウム系、から選ばれた１種以上、かつ前記アニオンが、ＢＦ₄ ^-、ＰＦ₆ ^-、ＴａＦ₆ ^-、ＮｂＦ₆ ^-、ＳｉＦ₆ ^-、ＡｌＦ₄ ^-、ＡｌＣｌ₄ ^-、ＮＯ₂ ^-、ＮＯ₃ ^-、Ｆ^-、Ｃｌ^-、Ｂｒ^-、Ｉ^-、ＣＮ^-、ＡｓＦ₆ ^-、ＳｂＦ₆ ^-、ＮｂＦ₆ ^-、ＴａＦ₆ ^-、ＣＦ₃ＳＯ₂ ^-、（ＣＦ₃ＳＯ₂）₂Ｎ^-、ｐ－ＣＨ₃ＰｈＳＯ₃ ^-、ＣＨ₃ＣＯ₂ ^-、ＣＨ₃ＳＯ₃ ^-、ＣＦ₃ＳＯ₃ ^-、（ＣＦ₃ＳＯ₂）₃Ｃ^-、Ｃ₃Ｆ₇ＣＯ₂ ^-、Ｃ₄Ｆ₉ＳＯ₃ ^-、（Ｃ₂Ｆ₅ＳＯ₂）₂Ｎ^-、（ＣＦ₃ＳＯ₂）（ＣＦ₃ＣＯ）Ｎ^-、（ＣＮ）₂Ｎ^-から選ばれた１種以上、であることが好ましい。これによって、帯電防止性が安定持続的に発揮され、アレルゲン性（黴、ダニダスト、花粉）物質の静電吸着が抑止可能、かつ抗菌防黴性、抗ウイルス性、抗アレルゲン性（黴、ダニダスト、花粉）を兼備する軟質塩化ビニル樹脂製の膜材で、ブリードによる汚れ、膜材同士が癒着するブロッキング問題を生じることのない膜材を得ることができる。 That is, the antistatic antibacterial and antifungal film material of the present invention is a soft vinyl chloride resin sheet containing at least an ionic liquid compound and a plasticizer having a molecular weight of 390 or more, and the ionic liquid compound is an inorganic anion and / Alternatively, the organic cation is formed by a pair ion of an organic anion, and the organic cation is selected from imidazolium-based, imidazolinium-based, pyridinium-based, pyrazolium-based, pyrrolidinium-based, piperidinium-based, ammonium-based, phosphonium-based, and sulfonium-based. One or more of the above-mentioned anions are BF _4- ^, PF _6- ^, TaF _6- ^, NbF _6- ^, SiF _6- ^, AlF _4- ^, AlCl _4- ^, NO ^{2- ,} NO _{3- ,} F- ^, Cl. ^- , Br- ^, I- ^, CN- ^, AsF _6- ^, SbF _6- ^, NbF _6- ^, TaF _6- , CF ₃ SO ^{2- ,} (CF ₃ SO ₂ ) ₂ N- ^, p _- CH ₃ ^PhSO _3- , CH ₃ CO _2- ^, CH ₃ SO _3- ^, CF ₃ SO _3- ^, (CF ₃ SO ₂ ) ₃ C- ^, C ₃ F ₇ CO _2- ^, C ₄ F ₉ SO _3- ^, (C ₂ F ₅ ) It is preferably one or more selected from SO ₂ ) ₂ N- ^, (CF ₃ SO ₂ ) (CF ₃ CO) N- ^{, and} (CN) ₂ N-. As a result, antistatic properties are stably and continuously exhibited, electrostatic adsorption of allergenic substances (mold, mite dust, pollen) can be suppressed, and antibacterial anti-mold, antiviral, anti-allergenic properties (mold, mite dust, pollen, etc.) It is a film material made of a soft vinyl chloride resin that also serves as pollen), and it is possible to obtain a film material that does not cause stains due to bleeding or blocking problems in which the film materials adhere to each other.

本発明の帯電防止性抗菌防黴膜材は、前記可塑剤が、〔化１〕、〔化２〕から選ばれた１種以上の液状エステル化合物（アルキル鎖中に１個以上のエーテル結合を有する分子量３９０以上の可塑剤）を３０質量％以上含むことが好ましい。このような液状エステル化合物の存在によって、より帯電防止性に優れた膜材を得ることができる。
〔化１〕
Ｒ（ＡＯ）_ｎＯＯＣ－Ｘ－ＣＯＯ（ＡＯ）_ｍＲ
（式中、Ｘは：Ｃ_６Ｈ_４、Ｃ_６Ｈ_８、Ｃ_６Ｈ_１０、Ｃ_２Ｈ_４～Ｃ_８Ｈ_１６、Ｒは：Ｃ_３～１５の直鎖または分岐鎖のアルキル基(Ｒは互いに同一または異なる)、Ａは：Ｃ_２～４の アルキレン基、ｍとｎは１～１０の整数(互いに同一または異なる)で表される化合物）
〔化２〕
Ｒ_１ＣＯ（ＯＣＨ_２ＣＨ-Ｒ_２）_ｎＣＯＯＲ_３
（式中、Ｒ_１及びＲ_３は：Ｃ_３～１５の直鎖または分岐鎖のアルキル基、またはアルケニル基、Ｒ_２は：Ｈ、ＣＨ_３、Ｃ_２Ｈ_５、ｎは３～２０の整数で表される化合物） In the antistatic antibacterial antimold film material of the present invention, the plasticizer is one or more liquid ester compounds selected from [Chemical formula 1] and [Chemical formula 2] (one or more ether bonds in an alkyl chain). It is preferable that the plasticizer having a molecular weight of 390 or more is contained in an amount of 30% by mass or more. Due to the presence of such a liquid ester compound, a film material having more excellent antistatic properties can be obtained.
[Chemical 1]
R (AO) _n OOC-X-COO (AO) _m R
(In the formula, X is: C ₆ H ₄ , C ₆ H ₈ , C ₆ H ₁₀ , C ₂ H ₄ to C ₈ H ₁₆ , R is: C _{3 to 15} linear or branched alkyl group (R). Are the same or different from each other), A is: an alkylene group of C2-4, m and n are integers of _1-10 (compounds represented by the same or different from each other).
[Chemical 2]
R ₁ CO (OCH ₂ CH-R ₂ ) _n COOR ₃
(In the formula, R ₁ and R ₃ are: C _{3 to 15} linear or branched alkyl or alkenyl groups, R ₂ is: H, CH ₃ , C ₂ H ₅ , n is an integer of 3 to 20. Compound represented by)

本発明の帯電防止性抗菌防黴膜材は、前記イオン液体化合物、及び前記可塑剤との併用質量比が、１：１００～１：５であることが好ましい。このようなイオン液体化合物と可塑剤の併用によって、帯電防止性が安定持続的に発揮され、アレルゲン性（黴、ダニダスト、花粉）物質の静電吸着が抑止可能、かつ抗菌防黴性、抗ウイルス性、抗アレルゲン性（黴、ダニダスト、花粉）を兼備する軟質塩化ビニル樹脂製の膜材で、ブリードによる汚れ、膜材同士が癒着するブロッキング問題を生じることのない膜材を得ることができる。 The antistatic antibacterial and antifungal film material of the present invention preferably has a combined mass ratio of the ionic liquid compound and the plasticizer of 1: 100 to 1: 5. By using such an ionic liquid compound and a plasticizer in combination, antistatic properties can be stably and sustainably exhibited, electrostatic adsorption of allergenic (mold, tick dust, pollen) substances can be suppressed, and antibacterial antifungal properties and antiviruses can be suppressed. It is a film material made of a soft vinyl chloride resin that has both properties and anti-allergenic properties (mold, mite dust, pollen), and it is possible to obtain a film material that does not cause stains due to bleeding or blocking problems in which the film materials adhere to each other.

本発明の帯電防止性抗菌防黴膜材は、前記軟質塩化ビニル樹脂シートの一面上に、紫外線（２００ｎｍ～３９９ｎｍ）励起または可視光線（４００ｎｍ～７８０ｎｍ）励起が可能なラジカル発生層が設けられ、このラジカル発生層が、酸化チタン、過酸化チタン、酸化亜鉛、酸化錫、チタン酸ストロンチウム、酸化タングステン、酸化ビスマス、及び酸化鉄、から選ばれた１種以上の光触媒性金属酸化物であることが好ましい。このようなラジカル発生層の存在によって、黴、菌の細胞壁をラジカル攻撃し、またウイルスの核酸（ＤＮＡ、ＲＮＡ）を損傷させることで、これらの活性、増殖を封止することにより抗菌防黴性、抗ウイルス性を相乗強化することができる。 In the antistatic antibacterial antimolding film material of the present invention, a radical generation layer capable of being excited by ultraviolet rays (200 nm to 399 nm) or visible light (400 nm to 780 nm) is provided on one surface of the soft vinyl chloride resin sheet. The radical generation layer may be one or more photocatalytic metal oxides selected from titanium oxide, titanium peroxide, zinc oxide, tin oxide, strontium titanate, tungsten oxide, bismuth oxide, and iron oxide. preferable. The presence of such a radical-generating layer radically attacks the cell walls of molds and fungi, and damages viral nucleic acids (DNA, RNA) to block their activity and proliferation, thereby providing antibacterial and antifungal properties. , Antiviral properties can be synergistically enhanced.

本発明の帯電防止性抗菌防黴膜材は、前記ラジカル発生層にゾルゲル縮合体を含み、このゾルゲル縮合体が、シラノール基含有有機シラン化合物のゾルゲル縮合、またはチタノール基含有有機チタン化合物のゾルゲル縮合によって形成されたもので、前記光触媒性金属酸化物を担持していることが好ましい。これによって軟質塩化ビニル樹脂シートに対するラジカル発生層の密着性、及びラジカル発生層内での光触媒性金属酸化物担持の密着性を高めると同時に、ブリードによる汚れ、膜材同士が癒着するブロッキング問題を生じることのない膜材を得ることができる。 The antistatic antibacterial antimold film material of the present invention contains a sol-gel condensate in the radical generation layer, and the sol-gel condensate is a sol-gel condensation of a silanol group-containing organic silane compound or a sol-gel condensation of a titanol group-containing organic titanium compound. It is preferably formed by carrying the photocatalytic metal oxide. This enhances the adhesion of the radical generation layer to the soft vinyl chloride resin sheet and the adhesion of the photocatalytic metal oxide bearing in the radical generation layer, and at the same time causes stains due to bleeding and blocking problems in which the film materials adhere to each other. It is possible to obtain a radical film material.

本発明の帯電防止性抗菌防黴膜材は、前記軟質塩化ビニル樹脂シートが織物を芯材として含み、この織物が、１）経糸及び緯糸からなる織物、または２）経糸及び左上バイアス糸／右上バイアス糸からなる三軸織物、または３）経糸、緯糸及び左上バイアス糸／右上バイアス糸からなる四軸織物、の何れかであることが好ましい。このような織物を芯材として含むターポリン、メッシュシート、合成皮革、帆布などの形態で、天井膜、空間仕切り、巻上昇降式シートシャッター、クリーンルームカーテン、敷物、カバー、ブラインドなどの用途で使用することができる。 In the antistatic antibacterial anti-mold film material of the present invention, the soft vinyl chloride resin sheet contains a woven fabric as a core material, and the woven fabric is 1) a woven fabric consisting of warps and wefts, or 2) warps and upper left bias yarns / upper right. It is preferably either a triaxial woven fabric consisting of a bias yarn, or 3) a quaternary fabric consisting of a warp, a weft and an upper left bias yarn / upper right bias yarn. In the form of tarpaulins, mesh sheets, synthetic leather, canvas, etc. containing such woven fabrics as core materials, they are used in applications such as ceiling membranes, space partitions, hoisting elevating sheet shutters, clean room curtains, floor coverings, covers, and blinds. be able to.

本発明によれば、帯電防止性が安定持続的に発揮され、アレルゲン性（黴、ダニダスト、花粉）物質の静電吸着が抑止可能、かつ抗菌防黴性、抗ウイルス性、抗アレルゲン性（黴、ダニダスト、花粉）を兼備する軟質塩化ビニル樹脂製の膜材で、ブリードによる汚れ、膜材同士が癒着するブロッキング問題を生じることのない膜材が得られるので、これらの膜材は、フィルム、シート、テープの形態、織物、ターポリン、メッシュシート、合成皮革、帆布などの形態で、これらのパーツを熱融着法で縫製し、天井膜、空間仕切り、巻上昇降式シートシャッター、クリーンルームカーテン、壁紙、敷物、カバー、ブラインド、防護衣、フェイスガード、など加工されて、工場、オフィス、学校、商業施設、病院、介護施設、式場、ごみ集積場、公衆トイレ、動物園などに広く使用される。特にターポリン、帆布などは、医療検査用パーティション、空気注入式仮設膜構造による医療検査用陰圧テントシェルターに適して用いることができ、（透明）フィルムはウイルス感染に対する、パーソナル空間構築用、対人カウンターの間仕切り構築用、フェイスガード（シールド）などの用途に適している。
※本発明において、数多くある菌種、黴種、ウイルス種のうちの代表的一部に対しての有効性を確認したことでの、抗菌防黴効果、抗ウイルス効果の応用の可能性を提案するのもで、未知を含めたあらゆる菌種、黴種、ウイルス種に対する有効性を示唆するものではない。 According to the present invention, antistatic properties are stably and continuously exhibited, electrostatic adsorption of allergenic substances (blinds, mite dust, pollen) can be suppressed, and antibacterial antifungal properties, antiviral properties, and anti-allergenic properties (blinds). , Tick dust, pollen), and a film material made of soft vinyl chloride resin that does not cause stains due to bleeding or blocking problems in which the film materials adhere to each other can be obtained. These parts are sewn by heat fusion method in the form of sheets, tapes, textiles, tarpaulins, mesh sheets, synthetic leather, canvas, etc., and ceiling membranes, space partitions, hoisting lift sheet shutters, clean room curtains, etc. It is processed into wallpapers, rugs, covers, blinds, protective clothing, face guards, etc., and is widely used in factories, offices, schools, commercial facilities, hospitals, nursing homes, ceremonies, garbage collection areas, public toilets, zoos, etc. In particular, tarpaulins and canvas can be used as suitable for medical examination partitions and negative pressure tent shelters for medical examinations with an inflatable temporary membrane structure, and (transparent) films are used for building personal spaces and interpersonal counters against virus infection. Suitable for partition construction, face guard (shield), etc.
* In the present invention, we propose the possibility of applying antibacterial and antifungal effects and antiviral effects by confirming the effectiveness against a representative part of many fungal species, fungal species, and virus species. However, it does not suggest efficacy against all fungal, fungal, and viral species, including unknown ones.

本発明の帯電防止性抗菌防黴膜材は、少なくともイオン液体化合物、及び可塑剤を含有する軟質塩化ビニル樹脂シートであって、前記イオン液体化合物が、特定のカチオン及びアニオンのイオン対で形成され、可塑剤が液状エステル化合物（アルキル鎖中に１個以上のエーテル結合を有する可塑剤）を３０質量％以上含み、イオン液体化合物、及び可塑剤との併用質量比が、１：１００～１：５の態様を包含し、特に軟質塩化ビニル樹脂シートの一面上に特定の光触媒性金属酸化物によるラジカル発生層が設けられた態様を包含し、またラジカル発生層にゾルゲル縮合体を含み、このゾルゲル縮合体が光触媒性金属酸化物を担持する態様を包含し、さらに軟質塩化ビニル樹脂シートが特定の織物を芯材として含む態様を包含する。 The antistatic antibacterial and anti-mold film material of the present invention is a soft vinyl chloride resin sheet containing at least an ionic liquid compound and a plasticizer, in which the ionic liquid compound is formed of an ion pair of a specific cation and anion. , The plasticizer contains 30% by mass or more of a liquid ester compound (a plasticizer having one or more ether bonds in an alkyl chain), and the combined mass ratio with the ionic liquid compound and the plasticizer is 1: 100 to 1: 1. 5. The embodiment is included, in particular, an embodiment in which a radical generation layer made of a specific photocatalytic metal oxide is provided on one surface of a soft vinyl chloride resin sheet, and the radical generation layer contains a solgel condensate, and the solgel is contained. The embodiment in which the condensate carries a photocatalytic metal oxide is included, and the embodiment in which the soft vinyl chloride resin sheet contains a specific woven fabric as a core material is included.

本発明の帯電防止性抗菌防黴膜材の実体は、少なくともイオン液体化合物、及び可塑剤を含有する軟質塩化ビニル樹脂シート（塗膜、フィルム、シート、ターポリン、帆布、合成皮革など）であって、その主構成は、塩化ビニル系樹脂（懸濁重合ＰＶＣ、乳化重合ＰＶＣ、塩ビ－酢ビ共重合体樹脂、ポリ塩化ビニリデン、塩素化塩化ビニル樹脂など）、分子量３９０以上の可塑剤（アジピン酸エステル系、フタル酸エステル系、シクロヘキサンエステル系、トリメリット酸エステル系、ピロメリット酸エステル系、ポリエステル系、エポキシ化大豆油系、芳香族リン酸エステル系、エチレンＣＯ酢酸ビニルエステル系高分子可塑剤など）、イオン液体化合物（後述）で、特に塩化ビニル系樹脂はＫ値６５～８５（JIS K7367-2）、１０００～２５００の平均重合度（旧JIS K6721）の塩化ビニル樹脂を用い、分子量３９０以上の可塑剤を併用することが好ましい。Ｋ値が６５を下回る塩化ビニル樹脂を用いることで、得られる軟質塩化ビニル樹脂シート同士のブロッキング現象を引き起こし易くなることがあり、また可塑剤がシート表面に移行するブリード現象を促進することでよりブロッキング現象を過酷なものとすることがある。イオン液体化合物と可塑剤との併用質量比は１：１００～１：５、特に３：１００～１：１０が好ましい。そして副成分には、耐熱安定剤（カルシウム亜鉛複合系、バリウム亜鉛複合系、有機錫ラウレート、有機錫メルカプタイト、エポキシ系など）、難燃剤（リン含有化合物、窒素含有化合物、無機系化合物、ハロゲン置換有機化合物）、耐光安定剤（ＨＡＬＳ）、紫外線吸収剤（ベンゾトリアゾール系、ベンゾフェノン系など）、酸化防止剤（フェノール系）、蛍光増白剤、帯電防止剤、硬化剤（イソシアネート系など）、防虫剤（ピレスロイド系など）、消臭剤（酸化珪素・金属酸化物複合系など）、遮熱フィラー（中空粒子、粗粒酸化チタンなど）、芳香剤、蓄光顔料（アルミン酸ストロンチウム系など）、アルミフレーク顔料、パール顔料、有機系顔料、無機系顔料、無機充填剤（炭酸カルシウム、硫酸バリウムなど）などの公知の添加剤を必要に応じて任意量配合した組成である。 The substance of the antistatic antibacterial antifungal film material of the present invention is a soft vinyl chloride resin sheet (coating film, film, sheet, tarpaulin, canvas, synthetic leather, etc.) containing at least an ionic liquid compound and a plasticizer. , Its main composition is vinyl chloride resin (suspended polymerized PVC, emulsified polymerized PVC, vinyl chloride-vinegar vinyl copolymer resin, polyvinyl chloride, chlorinated vinyl chloride resin, etc.), plasticizer with a molecular weight of 390 or more (adipic acid). Ester-based, phthalic acid ester-based, cyclohexane ester-based, trimellitic acid ester-based, pyromellitic acid ester-based, polyester-based, epoxidized soybean oil-based, aromatic phosphate ester-based, ethylene CO vinyl chloride ester-based polymer plasticizer Etc.), ionic liquid compounds (described later), especially vinyl chloride-based resins with a K value of 65 to 85 (JIS K7367-2) and an average polymerization degree of 1000 to 2500 (formerly JIS K6721) vinyl chloride resin with a molecular weight of 390. It is preferable to use the above plastic agents together. By using a vinyl chloride resin having a K value of less than 65, it may be easier to cause a blocking phenomenon between the obtained soft vinyl chloride resin sheets, and by promoting a bleeding phenomenon in which the plasticizer is transferred to the sheet surface, it is more likely to occur. The blocking phenomenon may be severe. The combined mass ratio of the ionic liquid compound and the plasticizer is preferably 1: 100 to 1: 5, particularly preferably 3: 100 to 1:10. As sub-ingredients, heat-resistant stabilizers (calcium-zinc composite system, barium-zinc composite system, organic tin laurate, organic tin mercaptite, epoxy system, etc.), flame retardant (phosphorus-containing compound, nitrogen-containing compound, inorganic compound, halogen substitution) Organic compounds), light-resistant stabilizers (HALS), ultraviolet absorbers (benzotriazole-based, benzophenone-based, etc.), antioxidants (phenol-based), fluorescent whitening agents, antistatic agents, curing agents (isocyanate-based, etc.), insect repellent Agents (pyresroids, etc.), deodorants (silicon oxide / metal oxide composites, etc.), heat-shielding fillers (hollow particles, coarse-grained titanium oxide, etc.), fragrances, phosphorescent pigments (strontium aluminate, etc.), aluminum It is a composition in which an arbitrary amount of known additives such as flake pigments, pearl pigments, organic pigments, inorganic pigments, and inorganic fillers (calcium carbonate, barium sulfate, etc.) is blended as necessary.

分子量３９０以上の可塑剤としては、例えば、フタル酸ジ（２－エチルヘキシル）（Ｃ８：ＭＷ３９０）、フタル酸ジノニル（Ｃ９：ＭＷ４１８）、フタル酸ジイソノニル（Ｃ９：ＭＷ４１８）、フタル酸ジイソデシル（Ｃ１０：ＭＷ４４７）、フタル酸ジデシル（Ｃ１０：ＭＷ４４７）などのフタル酸ジアルキルエステル系可塑剤などのフタル酸系可塑剤が例示できる。またフタル酸系可塑剤の位置異性体である、ベンゼン環に対するＣ８以上のジカルボン酸ジアルキルエステルの結合位置が、メタ位（１，３位）のイソフタル酸系可塑剤、パラ位（１，４位）のテレフタル酸系可塑剤などであってもよい。また例えば、１，２－シクロヘキサンジカルボン酸ジオクチル（Ｃ８：ＭＷ３９３）、１，２－シクロヘキサンジカルボン酸ジノニル（Ｃ９：ＭＷ４２１）、１，２－シクロヘキサンジカルボン酸ジイソノニル（Ｃ９：ＭＷ４２１）、１，２－シクロヘキサンジカルボン酸ジイソデシル（Ｃ１０：ＭＷ４５０）、１，２－シクロヘキサンジカルボン酸ジデシル（Ｃ１０：ＭＷ４５０）などのシクロヘキサンジカルボン酸ジアルキルエステル系可塑剤が例示される。シクロヘキサンジカルボン酸ジアルキルエステル系可塑剤は、シクロヘキサン環に対するＣ８以上のジカルボン酸ジアルキルエステルの結合位置が、メタ位（１，３位）、パラ位（１，４位）の位置異性体であってもよい。また４-シクロヘキセン-１，２-ジカルボン酸ビス（２-エチルヘキシル）（Ｃ８：ＭＷ３９５）、４-シクロヘキセン-１，２-ジカルボン酸ジノニル（Ｃ９：ＭＷ４２３）、４-シクロヘキセン-１，２-ジカルボン酸ジイソノニル（Ｃ９：ＭＷ４２３）、４-シクロヘキセン-１，２-ジカルボン酸ジイソデシル（Ｃ１０：ＭＷ４５２）、４-シクロヘキセン-１，２-ジカルボン酸ジデシル（Ｃ１０：ＭＷ４５２）などのシクロヘキセンジカルボン酸ジアルキルエステル系可塑剤が例示される。シクロヘキセンジカルボン酸ジアルキルエステル系可塑剤は、シクロヘキセン環に対するＣ８以上のジカルボン酸ジアルキルエステルの結合位置が、メタ位（１，３位）、パラ位（１，４位）の位置異性体であってもよい。 Examples of the plasticizer having a molecular weight of 390 or more include di (2-ethylhexyl) phthalate (C8: MW390), dinonyl phthalate (C9: MW418), diisononyl phthalate (C9: MW418), and diisodecyl phthalate (C10: MW447). ), A phthalic acid-based plasticizer such as a phthalic acid dialkyl ester-based plasticizer such as didecyl phthalate (C10: MW447) can be exemplified. Further, the bond position of the dicarboxylic acid dialkyl ester of C8 or higher with respect to the benzene ring, which is a position isomer of the phthalic acid plasticizer, is at the meta position (1,3 position) of the isophthalic acid plasticizer and the para position (1,4 position). ) May be a terephthalic acid-based plasticizer or the like. Further, for example, dioctyl 1,2-cyclohexanedicarboxylic acid (C8: MW393), dinonyl 1,2-cyclohexanedicarboxylic acid (C9: MW421), diisononyl 1,2-cyclohexanedicarboxylic acid (C9: MW421), 1,2-cyclohexane. Examples thereof include cyclohexanedicarboxylic acid dialkyl ester-based plasticizers such as diisodecyl dicarboxylic acid (C10: MW450) and didecyl 1,2-cyclohexanedicarboxylic acid (C10: MW450). In the cyclohexane dicarboxylic acid dialkyl ester-based plasticizer, even if the bond position of the dicarboxylic acid dialkyl ester of C8 or higher with respect to the cyclohexane ring is a position isomer at the meta position (1,3 position) or the para position (1,4 position). good. In addition, 4-cyclohexene-1,2-dicarboxylic acid bis (2-ethylhexyl) (C8: MW395), 4-cyclohexene-1,2-dicarboxylic acid dinonyl (C9: MW423), 4-cyclohexene-1,2-dicarboxylic acid. Cyclohexene dicarboxylic acid dialkyl ester-based plasticizers such as diisononyl (C9: MW423), 4-cyclohexene-1,2-dicarboxylic acid diisodecyl (C10: MW452), 4-cyclohexene-1,2-dicarboxylic acid didecyl (C10: MW452). Is exemplified. In the cyclohexene dicarboxylic acid dialkyl ester-based plasticizer, even if the bond position of the dicarboxylic acid dialkyl ester of C8 or higher with respect to the cyclohexene ring is a position isomer at the meta position (1,3 position) or the para position (1,4 position). good.

またアジピン酸、セバシン酸、アゼライン酸、フタル酸などのジカルボン酸とエチレングリコール、１，２－ブタンジオール、１，６－ヘキサンジオールなどのグリコール類との反応によって得られる分子量６００～２５００のオリゴマー、またはトリマーであるポリエステル系可塑剤を用いることができ、段落〔００１６〕に記載の可塑剤と併用することができる。またトリキシレニルホスフェート（ＭＷ４１０）、ビス-(t-ブチルフェニル)フェニルホスフェート（ＭＷ４３８）、トリス-(t-ブチルフェニル)ホスフェート（ＭＷ４９４）などの芳香族リン酸エステルを用いることができ、段落〔００１６〕に記載の可塑剤、及び上記ポリエステル系可塑剤と併用することができる。また分子末端または側鎖に（メタ）アクリロイル基を２個以上有する反応性アクリル系化合物、アリル基を２個以上有するアリルフタレート系化合物などを段落〔００１６〕に記載の可塑剤、及び上記ポリエステル系可塑剤などと併用することができる。分子量３９０を下回る可塑剤を主体に使用することで可塑剤がシート表面に移行するブリード現象を促進し、シート同士のブロッキング現象を過酷なものとすることがある。 Further, an oligomer having a molecular weight of 600 to 2500 obtained by reacting a dicarboxylic acid such as adipic acid, sebacic acid, azelaic acid, and phthalic acid with glycols such as ethylene glycol, 1,2-butanediol, and 1,6-hexanediol. Alternatively, a polyester-based plasticizer which is a trimmer can be used, and can be used in combination with the plasticizer described in paragraph [0016]. In addition, aromatic phosphate esters such as trixylenyl phosphate (MW410), bis- (t-butylphenyl) phenyl phosphate (MW438), and tris- (t-butylphenyl) phosphate (MW494) can be used. 0016] can be used in combination with the plasticizer described above and the polyester-based plasticizer described above. Further, the plasticizers described in paragraph [0016], such as a reactive acrylic compound having two or more (meth) acryloyl groups at the molecular end or a side chain, an allyl phthalate compound having two or more allyl groups, and the above polyester-based compound. It can be used in combination with a plasticizer or the like. By mainly using a plasticizer having a molecular weight of less than 390, the bleeding phenomenon in which the plasticizer migrates to the sheet surface is promoted, and the blocking phenomenon between the sheets may become severe.

また特に全可塑剤量に対し、液状エステル化合物（アルキル鎖中に１個以上のエーテル結合を有する分子量３９０以上の可塑剤）を３０質量％以上含むことが好ましい。アルキル鎖中に１個以上のエーテル結合を有する液状エステル化合物を含むことで得られる軟質塩化ビニル樹脂シートに帯電防止性を向上させる。このような帯電防止性を向上させる可塑剤としても作用する液状エステル化合物は、〔化１〕、〔化２〕から選ばれた１種以上である。軟質塩化ビニル樹脂シートに含む可塑剤量は、塩化ビニル系樹脂１００質量部に対し３５～９０質量部、特に４５～７５質量部が好ましく、この可塑剤量の３０質量％以上を〔化１〕、〔化２〕から選ばれた１種以上の液状エステル化合物とすることが好ましく、全可塑剤量に対する液状エステル化合物の占有率は１００質量％であってもよい。全可塑剤量が９０質量部を超えると得られる軟質塩化ビニル樹脂シートの風合いがラバー化してブロッキング現象を引き起こし易くなる。特に可塑剤量はデュロメータＡ硬度（JIS K6253：10秒後）がＡ６０～８５の範囲に軟質塩化ビニル樹脂シートの硬度を調整することが好ましい。硬度がＡ６０を下回ると、得られる軟質塩化ビニル樹脂シートの風合いがラバー化してブロッキング現象を引き起こし易くなる。
〔化１〕
Ｒ（ＡＯ）_ｎＯＯＣ－Ｘ－ＣＯＯ（ＡＯ）_ｍＲ
（式中、Ｘは：Ｃ_６Ｈ_４、Ｃ_６Ｈ_８、Ｃ_６Ｈ_１０、Ｃ_２Ｈ_４～Ｃ_８Ｈ_１６、Ｒは：Ｃ_３～１５の直鎖または分岐鎖のアルキル基(Ｒは互いに同一または異なる)、Ａは：Ｃ_２～４のアルキレン基、ｍとｎは１～１０の整数(互いに同一または異なる)で表される化合物）
〔化２〕
Ｒ_１ＣＯ（ＯＣＨ_２ＣＨ-Ｒ_２）_ｎＣＯＯＲ_３
（式中、Ｒ_１及びＲ_３は：Ｃ_３～１５の直鎖または分岐鎖のアルキル基、またはアルケニル基、Ｒ_２は：Ｈ、ＣＨ_３、Ｃ_２Ｈ_５、ｎは３～２０の整数で表される化合物） Further, it is particularly preferable to contain 30% by mass or more of a liquid ester compound (a plasticizer having a molecular weight of 390 or more having one or more ether bonds in the alkyl chain) with respect to the total amount of the plasticizer. The soft vinyl chloride resin sheet obtained by containing a liquid ester compound having one or more ether bonds in the alkyl chain has improved antistatic properties. The liquid ester compound that also acts as a plasticizer that improves such antistatic properties is one or more selected from [Chemical formula 1] and [Chemical formula 2]. The amount of the plasticizer contained in the soft vinyl chloride resin sheet is preferably 35 to 90 parts by mass, particularly 45 to 75 parts by mass with respect to 100 parts by mass of the vinyl chloride resin, and 30% by mass or more of this plasticizer amount is [Chemical formula 1]. , It is preferable to use one or more liquid ester compounds selected from [Chemical formula 2], and the occupancy ratio of the liquid ester compound with respect to the total amount of the plasticizer may be 100% by mass. When the total amount of the plasticizer exceeds 90 parts by mass, the texture of the obtained soft vinyl chloride resin sheet becomes rubber and easily causes a blocking phenomenon. In particular, it is preferable to adjust the hardness of the soft vinyl chloride resin sheet so that the amount of the plasticizer is in the range of Durometer A hardness (JIS K6253: after 10 seconds) of A60 to 85. When the hardness is lower than A60, the texture of the obtained soft vinyl chloride resin sheet becomes rubber and easily causes a blocking phenomenon.
[Chemical 1]
R (AO) _n OOC-X-COO (AO) _m R
(In the formula, X is: C ₆ H ₄ , C ₆ H ₈ , C ₆ H ₁₀ , C ₂ H ₄ to C ₈ H ₁₆ , R is: C _{3 to 15} linear or branched alkyl group (R). Are the same or different from each other), A is: an alkylene group of C2-4, m and n are integers of _1-10 (same or different from each other).
[Chemical 2]
R ₁ CO (OCH ₂ CH-R ₂ ) _n COOR ₃
(In the formula, R ₁ and R ₃ are: C _{3 to 15} linear or branched alkyl or alkenyl groups, R ₂ is: H, CH ₃ , C ₂ H ₅ , n is an integer of 3 to 20. Compound represented by)

上記〔化１〕式の液状エステル化合物の製造に用いられるジカルボン酸としては、アジピン酸、アゼライン酸、セバシン酸、コハク酸、ブラシル酸、テトラヒドロフタル酸、フタル酸などのジカルボン酸が好ましく、上記〔化２〕式の液状エステル化合物の製造に用いられるカルボン酸としては、モノカルボン酸、三価以上の多価カルボン酸、またはエポキシシクロヘキサン環を有する二価カルボン酸である。これらのカルボン酸はメチル基、エチル基などのアルキル基、水酸基、酸素、ケイ素、ハロゲンなどのヘテロ原子を含む置換基を有していてもよい。モノカルボン酸としては炭素数２～２２の脂肪族モノカルボン酸が好ましく、更に炭素数３～８のカルボン酸残基からなる脂肪族、脂環式若しくは芳香族の多塩基酸で、具体的には、クエン酸、アコニット酸、ブタントリカルボン酸、ブタンテトラカルボン酸などの脂肪族多価カルボン酸、エポキシヘキサヒドロフタル酸などの脂環式カルボン酸、トリメリット酸、ピロメリット酸などの芳香族多価カルボン酸、並びにこれらのカルボン酸の酸無水物などを用いることができる。上記〔化１〕式、及び上記〔化２〕式の液状エステル化合物は上記カルボン酸を単独で用いたもの、あるいは２種以上の混合物を用いたものである。 As the dicarboxylic acid used for producing the liquid ester compound of the above [Chemical formula 1], dicarboxylic acids such as adipic acid, azelaic acid, sebacic acid, succinic acid, brassic acid, tetrahydrophthalic acid and phthalic acid are preferable. The carboxylic acid used for producing the liquid ester compound of the formula 2] is a monocarboxylic acid, a trivalent or higher polyvalent carboxylic acid, or a divalent carboxylic acid having an epoxycyclohexane ring. These carboxylic acids may have an alkyl group such as a methyl group or an ethyl group, and a substituent containing a heteroatom such as a hydroxyl group, oxygen, silicon or halogen. As the monocarboxylic acid, an aliphatic monocarboxylic acid having 2 to 22 carbon atoms is preferable, and an aliphatic, alicyclic or aromatic polybasic acid composed of carboxylic acid residues having 3 to 8 carbon atoms is specifically used. Is an aliphatic polyvalent carboxylic acid such as citric acid, aconitic acid, butane tricarboxylic acid, butane tetracarboxylic acid, an alicyclic carboxylic acid such as epoxyhexahydrophthalic acid, and aromas such as trimellitic acid and pyromellitic acid. Valuable carboxylic acids and acid anhydrides of these carboxylic acids can be used. The liquid ester compounds of the above formula [Chemical formula 1] and the above formula [Chemical formula 2] are those using the above carboxylic acid alone or those using a mixture of two or more kinds.

このような液状エステル化合物〔化１〕は具体的に、フタル酸ジエチルセロソルブ、フタル酸ジブチルセロソルブ、アジピン酸ジエチルセロソルブ、アジピン酸ジブチルセロソルブ、アゼライン酸ジエチルセロソルブ、アゼライン酸ジブチルセロソルブ、セバシン酸ジエチルセロソルブ、セバシン酸ジブチルセロソルブ、などのジカルボン酸アルキルセロソルブ系エステル化合物、及びアジピン酸、フタル酸などのジカルボン酸と、モノ－及びポリ－アルキレングリコールモノアルキルエーテルとの反応物が挙けられる。モノ－及びポリ－アルキレングリコールモノアルキルエーテルは、プロパノール、ブタノール、ヘキサノール、ヘプタノール、オクタノール、ノナノールなどのアルコールとエチレンオキシドとの付加化合物、アルコールとプロピレンオキシドとの付加化合物、アルコールとブチレンオキシドとの付加化合物、あるいは、アルコールと、エチレンオキシド、プロピレンオキシド、ブチレンオキシドなどアルキレンオキシドから選ばれた２種以上のアルキレンオキシドとの付加化合物であり、これらは具体的に、エチレングリコールモノオクチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノブチルエーテル、ジエチレングリコールモノヘプチルエーテル、トリエチレングリコールモノメチルエーテル、トリエチレングリコールモノプロピルエーテル、テトラエチレングリコールモノエチルエーテル、プロピレングリコールモノエチルエーテル、プロピレングリコールモノオクチルエーテル、ジプロピレングリコールモノブチルエーテル、ブチレングリコールモノエチルエーテルなどの（モノ～ポリ）アルキレングリコールモノアルキルエーテルなど、その他、ジエチレングリコールジ－２－エチルヘキソネート、テトラエチレングリコールジ－２－エチルヘキソネート、ヘキサエチレングリコールジ－２－エチルヘキソネート、トリエチレングリコールジエチルブチレート、ポリエチレングリコールジエチルブチレート、ポリプロピレングリコールジエチルヘキソネート、トリエチレングリコールジベンゾエート、テトラエチレングリコールジベンゾエート、ポリエチレングリコールジベンゾエート、ポリプロピレングリコールジベンゾエート、またはポリエチレングリコール－２－エチルヘキソネートベンゾエートなどである。また液状エステル化合物〔化２〕は、トリエチレングリコールのカプリル酸エステル、テトラエチレングリコールのオクチル酸エステル、ポリエチレングリコールと２－エチル酢酸とのジエステル、ポリエステルグリコールと２－エチルヘキ酸とのジエステルなどが挙げられる。 Specific examples of such a liquid ester compound [Chemical formula 1] include diethyl cellosolve phthalate, dibutyl cellosolve phthalate, diethyl cellosolve adipate, dibutyl cello adipate, diethyl cellosolve azelaine, dibutyl cellosolve azelaline, diethyl cellosebacate, and the like. Examples thereof include a reaction product of a dicarboxylic acid alkyl cellosolve-based ester compound such as dibutyl cellosolve sebacic acid, a dicarboxylic acid such as adipic acid and phthalic acid, and a mono- and poly-alkylene glycol monoalkyl ether. Mono- and poly-alkylene glycol monoalkyl ethers are addition compounds of alcohol and ethylene oxide such as propanol, butanol, hexanol, heptanol, octanol and nonanol, addition compounds of alcohol and propylene oxide, and addition compounds of alcohol and butylene oxide. Alternatively, it is an addition compound of alcohol and two or more alkylene oxides selected from alkylene oxides such as ethylene oxide, propylene oxide and butylene oxide, and these are specifically ethylene glycol monooctyl ether, diethylene glycol monomethyl ether and diethylene glycol. Monobutyl Ether, Diethylene Glycol Monoheptyl Ether, Triethylene Glycol Monomethyl Ether, Triethylene Glycol Monopropyl Ether, Tetraethylene Glycol Monoethyl Ether, Propylene Glycol Monoethyl Ether, Propylene Glycol Monooctyl Ether, Dipropylene Glycol Monobutyl Ether, Butylene Glycol Monoethyl Others such as (mono-poly) alkylene glycol monoalkyl ethers such as ethers, diethylene glycol di-2-ethylhexonate, tetraethylene glycol di-2-ethylhexonate, hexaethylene glycol di-2-ethylhexonate , Triethylene glycol diethylbutyrate, polyethylene glycol diethylbutyrate, polypropylene glycol diethylhexonate, triethylene glycol dibenzoate, tetraethylene glycol dibenzoate, polyethylene glycol dibenzoate, polypropylene glycol dibenzoate, or polyethylene glycol-2-ethyl. Hexonate benzoate and the like. Examples of the liquid ester compound [Chemical Formula 2] include caprylic acid ester of triethylene glycol, octylate ester of tetraethylene glycol, diester of polyethylene glycol and 2-ethylacetic acid, and diester of polyester glycol and 2-ethylhexic acid. Be done.

本発明の帯電防止性抗菌防黴膜材に用いるイオン液体化合物は、有機系カチオンと、無機系アニオン、及び／または有機系アニオンとの対イオンを成して形成される常温液体の塩である。有機系カチオンは、イミダゾリウム系、イミダゾリニウム系、ピリジニウム系、ピラゾリウム系、ピロリジニウム系、ピペリジニウム系、アンモニウム系、ホスホニウム系、スルホニウム系、から選ばれた１種以上である。具体的に、１）イミダゾリウム系イオン液体化合物として、１－（Ｒ_１）－３－（Ｒ_２）イミダゾリウム／テトラフルオロボレート（ＢＦ₄ ^-）、１－（Ｒ_１）－３－（Ｒ_２）イミダゾリウム／トリフルオロメタンスルホネート（ＣＦ₃ＳＯ_３ ^-）、１－（Ｒ_１）－３－（Ｒ_２）イミダゾリウム／ビス（トリフルオロメタンスルホニル）イミド（〔ＣＦ₃ＳＯ₂〕₂Ｎ^-）、１－（Ｒ_１）－３－（Ｒ_２）イミダゾリウム／ヘキサフルオロホスフェート（ＰＦ₆ ^-）、１－（Ｒ_１）－３－（Ｒ_２）イミダゾリウム／ブロマイド（Ｂｒ^-）またはクロライド（Ｃｒ^-）、などのイミダゾリニウム塩：ここでＲ_１：メチル基、エチル基、ブチル基、プロピル基、イソプロピル基などのＣ_１～Ｃ_１２直鎖アルキル基、または分岐アルキル基、Ｒ_２：メチル基、エチル基、ブチル基、プロピル基、イソプロピル基などのＣ_１～Ｃ_１２直鎖アルキル基、または分岐アルキル基、でＲ_１とＲ_２は互いに同一、あるいは互いに異なるアルキル基である。Ｒ_１とＲ_２は以下、２）～７）に記載のイオン液体化合物においても同様の定義である。２）イミダゾリニウム系イオン液体化合物として、１－（Ｒ_１）－３－（Ｒ_２）イミダゾリニウム／テトラフルオロボレート、１－（Ｒ_１）－３－（Ｒ_２）イミダゾリニウム／トリフルオロメタンスルホネート、１－（Ｒ_１）－３－（Ｒ_２）イミダゾリニウム／ビス（トリフルオロメタンスルホニル）イミド、１－（Ｒ_１）－３－（Ｒ_２）イミダゾリニウム／ヘキサフルオロホスフェート、１－（Ｒ_１）－３－（Ｒ_２）イミダゾリニウム／ブロマイドまたはクロライド、などのイミダゾリニウム塩、３）ピリジニウム系イオン液体化合物として、１－（Ｒ_１）－３－（Ｒ_２）ピリジニウム／テトラフルオロボレート、１－（Ｒ_１）－３－（Ｒ_２）ピリジニウム／トリフルオロメタンスルホネート、１－（Ｒ_１）－３－（Ｒ_２）ピリジニウム／ビス（トリフルオロメタンスルホニル）イミド、１－（Ｒ_１）－３－（Ｒ_２）ピリジニウム／ヘキサフルオロホスフェート、１－（Ｒ_１）－３－（Ｒ_２）ピリジニウム／ブロマイドまたはクロライド、などのピリジニウム塩；４）ピラゾリウム系イオン液体化合物として、Ｎ－（Ｒ_１）－Ｎ－（Ｒ_２）ピラゾリウム／テトラフルオロボレート、Ｎ－（Ｒ_１）－Ｎ－（Ｒ_２）ピラゾリウム／トリフルオロメタンスルホネート、Ｎ－（Ｒ_１）－Ｎ－（Ｒ_２）ピラゾリウム／ビス（トリフルオロメタンスルホニル）イミド、Ｎ－（Ｒ_１）－Ｎ－（Ｒ_２）ピラゾリウム／ヘキサフルオロホスフェート、Ｎ－（Ｒ_１）－Ｎ－（Ｒ_２）ピラゾリウム／ブロマイドまたはクロライド、などのピラゾリウム塩；５）ピロリジニウム系イオン液体化合物として、Ｎ－（Ｒ_１）－Ｎ－（Ｒ_２）ピロリジニウム／テトラフルオロボレート、Ｎ－（Ｒ_１）－Ｎ－（Ｒ_２）ピロリジニウム／トリフルオロメタンスルホネート、Ｎ－（Ｒ_１）－Ｎ－（Ｒ_２）ピロリジニウム／ビス（トリフルオロメタンスルホニル）イミド、Ｎ－（Ｒ_１）－Ｎ－（Ｒ_２）ピロリジニウム／ヘキサフルオロホスフェート、Ｎ－（Ｒ_１）－Ｎ－（Ｒ_２）ピロリジニウム／ブロマイドまたはクロライド、などのピロリジニウム塩；６）ピペリジニウム系イオン液体化合物として、Ｎ－（Ｒ_１）－Ｎ－（Ｒ_２）ピペリジニウム／テトラフルオロボレート、Ｎ－（Ｒ_１）－Ｎ－（Ｒ_２）ピペリジニウム／トリフルオロメタンスルホネート、Ｎ－（Ｒ_１）－Ｎ－（Ｒ_２）ピペリジニウム／ビス（トリフルオロメタンスルホニル）イミド、Ｎ－（Ｒ_１）－Ｎ－（Ｒ_２）ピペリジニウム／ヘキサフルオロホスフェート、Ｎ－（Ｒ_１）－Ｎ－（Ｒ_２）ピペリジニウム／ブロマイドまたはクロライド、などのピペリジニウム塩；７）アンモニウム系イオン液体化合物として、Ｎ，Ｎ，Ｎ－トリ（Ｒ_１）－Ｎ－（Ｒ_２）アンモニウム／ブロマイドまたはクロライド、Ｎ，Ｎ，Ｎ－トリ（Ｒ_１）－Ｎ－（Ｒ_２）アンモニウム／テトラフルオロボレート、Ｎ，Ｎ，Ｎ－トリ（Ｒ_１）－Ｎ－（Ｒ_２）アンモニウム／ヘキサフルオロホスフェート、Ｎ，Ｎ，Ｎ－トリ（Ｒ_１）－Ｎ－（Ｒ_２）アンモニウム／ビス（トリフルオロメタンスルホニル）イミド、アミルトリエチルアンモニウム／ビス（トリフルオロメタンスルホニル）イミド、メチルトリ－ｎ－オクチルアンモニウム／ビス（トリフルオロメタンスルホニル）イミド、２－プロペン－１－アミニウム－Ｎ，Ｎ－ジメチル－１－Ｎ－２－プロペン－１－イル塩などのアンモニウム塩などが挙げられ、これらは１種のみを使用してもよいし、２種以上を併用してもよい。 The ionic liquid compound used in the antistatic antibacterial antifungal film material of the present invention is a normal temperature liquid salt formed by forming a counterion between an organic cation and an inorganic anion and / or an organic anion. .. The organic cation is one or more selected from imidazolium-based, imidazolinium-based, pyridinium-based, pyrizolium-based, pyrrolidinium-based, piperidinium-based, ammonium-based, phosphonium-based, and sulfonium-based. Specifically, 1) as imidazolium-based ion liquid compounds, 1- (R ₁ ) -3- (R ₂ ) imidazolium / tetrafluoroborate (BF _4- ), ^1- (R ₁ ) -3- (R). ₂ ) Imidazolium / trifluoromethanesulfonate (CF ₃ SO _3- ), ^1- (R ₁ ) -3- (R ₂ ) Imidazolium / bis (trifluoromethanesulfonyl) imide ([CF ₃ SO ₂ ] ₂ N- ⁾ , 1- (R ₁ ) -3- (R ₂ ) imidazolium / hexafluorophosphate (PF _6- ), ^1- (R ₁ ) -3- (R ₂ ) imidazolium / bromide (Br- ⁾ or chloride (Br-) Imidazolinium salts such as Cr- ⁾ , etc .: where R ₁ : methyl group, ethyl group, butyl group, propyl group, isopropyl group and other C ₁ to C ₁₂ linear alkyl groups, or branched alkyl groups, R ₂ : C ₁ to C ₁₂ linear alkyl groups such as methyl group, ethyl group, butyl group, propyl group and isopropyl group, or branched alkyl groups, and R ₁ and R ₂ are alkyl groups that are the same as or different from each other. R ₁ and R ₂ have the same definitions in the ionic liquid compounds described in 2) to 7) below. 2) As imidazolinium-based ionic liquid compounds, 1- (R ₁ ) -3- (R ₂ ) imidazolinium / tetrafluoroborate, 1- (R ₁ ) -3- (R ₂ ) imidazolinium / trifluo Lomethanesulfonate, 1- (R ₁ ) -3- (R ₂ ) imidazolinium / bis (trifluoromethanesulfonyl) imide, 1- (R ₁ ) -3- (R ₂ ) imidazolinium / hexafluorophosphate, 1 -(R ₁ ) -3- (R ₂ ) imidazolinium salt such as imidazolinium / bromide or chloride, 3) 1- (R ₁ ) -3- (R ₂ ) pyridinium as a pyridinium-based ionic liquid compound / Tetrafluoroborate, 1- (R ₁ ) -3- (R ₂ ) pyridinium / trifluoromethanesulfonate, 1- (R ₁ ) -3- (R ₂ ) pyridinium / bis (trifluoromethanesulfonyl) imide, 1-( Pyridinium salts such as R ₁ ) -3- (R ₂ ) pyridinium / hexafluorophosphate, 1- (R ₁ ) -3- (R ₂ ) pyridinium / bromide or chloride; 4) N as a pyrazolium-based ionic liquid compound. -(R ₁ ) -N- (R ₂ ) pyrazolium / tetrafluoroborate, N- (R ₁ ) -N- (R ₂ ) pyrazolium / trifluoromethanesulfonate, N- (R ₁ ) -N- (R ₂ ) Pyrazolium / bis (trifluoromethanesulfonyl) imide, N- (R ₁ ) -N- (R ₂ ) pyrazolium / hexafluorophosphate, N- (R ₁ ) -N- (R ₂ ) pyrazolium / bromide or chloride, etc. Pyrazolium salt; 5) N- (R ₁ ) -N- (R ₂ ) pyrrolidinium / tetrafluoroborate, N- (R ₁ ) -N- (R ₂ ) pyrrolidinium / trifluoromethanesulfonate, as pyrrolidinium-based ionic liquid compounds. N- (R ₁ ) -N- (R ₂ ) pyrrolidinium / bis (trifluoromethanesulfonyl) imide, N- (R ₁ ) -N- (R ₂ ) pyrrolidinium / hexafluorophosphate, N- (R ₁ ) -N -(R ₂ ) Pyrrolidinium salts such as pyrrolidinium / bromide or chloride; 6) As a piperidinium-based ionic liquid compound, N- (R ₁ ) -N- (R ₂ ) piperidinium / tetrafluoroborate, N- (R ₁ ) -N- (R ₂ ) piperidinium / trifluoromethanesulfonate, N- (R ₁ ) -N- (R ₂ ) piperidinium / bis (trifluoromethanesulfonyl) imide, N- (R ₁ ) -N -Piperidinium salts such as (R ₂ ) piperidinium / hexafluorophosphate, N- (R ₁ ) -N- (R ₂ ) piperidinium / bromide or chloride; 7) N, N, N- as ammonium-based ion liquid compounds. Tri (R ₁ ) -N- (R ₂ ) Ammonium / Bromide or Chloride, N, N, N-Tri (R ₁ ) -N- (R ₂ ) Ammonium / Tetrafluoroborate, N, N, N-Tri ( R ₁ ) -N- (R ₂ ) ammonium / hexafluorophosphate, N, N, N-tri (R ₁ ) -N- (R ₂ ) ammonium / bis (trifluoromethanesulfonyl) imide, amyltriethylammonium / bis (R 1) -N- (R 2) ammonium / hexafluorophosphate Ammonium such as trifluoromethanesulfonyl) imide, methyltri-n-octylammonium / bis (trifluoromethanesulfonyl) imide, 2-propen-1-aminonium-N, N-dimethyl-1-N-2-propen-1-yl salt Examples thereof include salts, and these may be used alone or in combination of two or more.

上記段落〔００２１〕記載の有機系カチオンと対となるカウンターイオン（アニオン）は、ＢＦ₄ ^-、ＰＦ₆ ^-、ＴａＦ₆ ^-、ＮｂＦ₆ ^-、ＳｉＦ₆ ^-、ＡｌＦ₄ ^-、ＡｌＣｌ₄ ^-、ＮＯ₂ ^-、ＮＯ₃ ^-、Ｆ^-、Ｃｌ^-、Ｂｒ^-、Ｉ^-、ＣＮ^-、ＡｓＦ₆ ^-、ＳｂＦ₆ ^-、ＮｂＦ₆ ^-、ＴａＦ₆ ^-の無機系アニオン、及びＣＦ₃ＳＯ₂ ^-、（ＣＦ₃ＳＯ₂）₂Ｎ^-、ｐ－ＣＨ₃ＰｈＳＯ₃ ^-、ＣＨ₃ＣＯ₂ ^-、ＣＨ₃ＳＯ₃ ^-、ＣＦ₃ＳＯ₃ ^-、（ＣＦ₃ＳＯ₂）₃Ｃ^-、Ｃ₃Ｆ₇ＣＯ₂ ^-、Ｃ₄Ｆ₉ＳＯ₃ ^-、（Ｃ₂Ｆ₅ＳＯ₂）₂Ｎ^-、（ＣＦ₃ＳＯ₂）（ＣＦ₃ＣＯ）Ｎ^-、（ＣＮ）₂Ｎ^-の有機系アニオンから選ばれた１種以上のアニオンで、上記段落〔００２１〕記載の有機系カチオンと対となって帯電防止性及び抗菌・防黴性・抗ウイルス性を発現する。これによって、帯電防止性が安定持続的に発揮され、アレルゲン性（黴、ダニダスト、花粉）物質の静電吸着が抑止可能となり、かつ抗菌防黴性、抗ウイルス性、抗アレルゲン性（黴、ダニダスト、花粉）を兼備する軟質塩化ビニル樹脂製の膜材で、ブリードによる汚れ、膜材同士が癒着するブロッキング問題を生じることのない膜材を得ることができる。抗菌性は、黄色ブドウ球菌、大腸菌、肺炎桿菌、緑膿菌、メチシリン耐性黄色ブドウ球菌、および腸管出血性大腸菌など、防黴性は、黒黴（クラドスポリウム）、青黴（ペニシリウム）、緑黴（トリコデルマ）、赤黴（フザリウム）、黄黴（カワキコウジカビ）など、抗ウイルス性は、インフルエンザウイルス、ノルウイルス、ヘルペスウイルスなど、それらの増殖を抑止する効果を発現し得る。抗菌・防黴効果はイオン液体化合物による細胞膜の破壊によるもので、細胞膜破壊には、イオン液体の有機系カチオンの正電荷とそのカチオンのアルキル鎖長が関与する。静電相互作用によって、イオン液体化合物の有機系カチオンが菌・黴の細胞膜のリン脂質のアニオン部位に引き寄せられた後、有機系カチオンのアルキル鎖が細胞膜のリン脂質の疎水部と疎水性相互作用することによって膜に入り込み、カチオン部が細胞膜に蓄積することで菌・黴の細胞膜を破壊するメカニズムのため、有機系カチオンのアルキル鎖が長いほど細胞膜の破壊に効果的となる。ウイルスに対しては核酸のＤＮＡ、またはＲＮＡの塩基にイオン液体化合物（カチオン、またはアニオン）が配位することで、ＤＮＡ、ＲＮＡの複製を阻害する作用でウイルスを抑制する。イオン液体化合物と上述の可塑剤との併用質量比は１：１００～１：５、特に３：１００～１：１０が好ましい。イオン液体化合物の含有量が１：１００未満だと帯電防止性、及び抗菌・防黴性、抗ウイルス性が不十分となることがあり、またイオン液体化合物の含有量が１：５を超えるとイオン液体化合物の膜材表面へのブリード現象が顕著となることがある。このようなイオン液体化合物と可塑剤の併用によって、帯電防止性が安定持続的に発揮され、アレルゲン性（黴、ダニダスト、花粉）物質の静電吸着が抑止可能、かつ抗菌防黴性、抗ウイルス性、抗アレルゲン性（黴、ダニダスト、花粉）を兼備する軟質塩化ビニル樹脂製の膜材で、ブリードによる汚れ、膜材同士が癒着するブロッキング問題を生じることのない膜材を得ることができる。また黴に対しては、イミダゾリウム系、イミダゾリニウム系、ピリジニウム系、ピラゾリウム系、ピロリジニウム系、ピペリジニウム系、アンモニウム系、ホスホニウム系、スルホニウム系などの有機系カチオンが効果的である。 The counter ions (anions) paired with the organic cations described in the above paragraph [0021] are BF _4- ^, PF _6- ^, TaF _6- ^, NbF _6- ^, SiF _6- ^, AlF _4- ^, AlCl _4- ^, NO. _2- ^, NO _3- , F- ^{, Cl- ,} Br- ^, I- ^, CN- ^, AsF _6- ^, SbF _6- ^, NbF _6- , TaF ₆ ^- inorganic anions, ^and CF ₃ SO _2- ^, ( CF ₃ SO ₂ ) ₂ N- ^, p-CH _{3 PhSO 3-} , CH ₃ CO ^{2- ,} CH ₃ SO _3- ^, CF ₃ SO _3- ^, (CF ₃ SO ₂ ) ₃ C- ^, C ₃ F ₇ CO Selected from _2- ^, C ₄ F ₉ SO _3- ^, (C ₂ F ₅ SO ₂ ) ₂ N- ^, (CF ₃ SO ₂ ) (CF ₃ CO) N- ^, (CN) ₂ N ^- organic anions Only one or more anions are paired with the organic cations described in the above paragraph [0021] to exhibit antistatic, antibacterial, antifungal, and antiviral properties. As a result, antistatic properties are stably and continuously exhibited, electrostatic adsorption of allergenic substances (mold, mite dust, pollen) can be suppressed, and antibacterial antifungal, antiviral, and antiallergenic properties (mold, mite dust). , Pollen), and it is possible to obtain a film material that does not cause stains due to bleeding or blocking problems in which the film materials adhere to each other. Antibacterial properties include yellow staphylococcus, Escherichia coli, pneumoniae, pyogenic, methicillin-resistant yellow bacillus, and intestinal hemorrhagic Escherichia coli. Antiviral properties such as (Trichoderma), red mold (Fuzalium), yellow mold (Kawakikouji mold) can exert the effect of suppressing the growth of influenza virus, norvirus, herpes virus and the like. The antibacterial and antifungal effects are due to the destruction of the cell membrane by the ionic liquid compound, and the positive charge of the organic cation of the ionic liquid and the alkyl chain length of the cation are involved in the cell membrane destruction. After the organic cation of the ionic liquid compound is attracted to the phospholipid anion site of the cell membrane of the fungus / mold by electrostatic interaction, the alkyl chain of the organic cation interacts hydrophobically with the hydrophobic part of the phospholipid of the cell membrane. As a result, the longer the alkyl chain of the organic cation is, the more effective it is in the destruction of the cell membrane because of the mechanism of entering the membrane and accumulating the cation part in the cell membrane to destroy the cell membrane of fungi and mold. For viruses, ionic liquid compounds (cations or anions) are coordinated with nucleic acid DNA or RNA bases to suppress the virus by inhibiting the replication of DNA and RNA. The combined mass ratio of the ionic liquid compound and the above-mentioned plasticizer is preferably 1: 100 to 1: 5, particularly preferably 3: 100 to 1:10. If the content of the ionic liquid compound is less than 1: 100, the antistatic property, antibacterial / antifungal property, and antiviral property may be insufficient, and if the content of the ionic liquid compound exceeds 1: 5. The bleeding phenomenon of the ionic liquid compound on the surface of the film material may be remarkable. By using such an ionic liquid compound and a plasticizer in combination, antistatic properties can be stably and sustainably exhibited, electrostatic adsorption of allergenic (mold, tick dust, pollen) substances can be suppressed, and antibacterial antifungal properties and antiviruses can be suppressed. It is a film material made of a soft vinyl chloride resin that has both properties and anti-allergenic properties (mold, mite dust, pollen), and it is possible to obtain a film material that does not cause stains due to bleeding or blocking problems in which the film materials adhere to each other. For mold, organic cations such as imidazolium-based, imidazolinium-based, pyridinium-based, pyrazolium-based, pyrrolidinium-based, piperidinium-based, ammonium-based, phosphonium-based, and sulfonium-based cations are effective.

軟質塩化ビニル樹脂シート（帯電防止性抗菌防黴膜材）の一面上に、紫外線（２００ｎｍ～３９９ｎｍ）励起または可視光線（４００ｎｍ～７８０ｎｍ）励起が可能なラジカル発生層が設けられていることが好ましく、このラジカル発生層は紫外線励起、または可視光線励起によって、有機物に対するラジカル酸化攻撃を行い、この作用によって菌・黴の細胞膜を破壊し死滅させ、菌・黴の増殖を抑止するもので、この作用はイオン液体化合物によるイオン配位との相乗でより効果的、かつ即効的に作用する。ウイルスに対しては核酸のＤＮＡ、またはＲＮＡの二重螺旋をラジカル酸化攻撃してＤＮＡ、ＲＮＡを破壊する作用でウイルスを抑制するもので、この作用はイオン液体化合物によるイオン配位との相乗でより効果的、かつ即効的に作用する。このラジカル発生層は、酸化チタン、過酸化チタン、酸化亜鉛、酸化錫、チタン酸ストロンチウム、酸化タングステン、酸化ビスマス、及び酸化鉄、から選ばれた１種以上の光触媒性金属酸化物により構成される。特に可視光線励起可能なラジカル発生層は、１）上記の光触媒性金属酸化物に、銀、プラチナ、金、銅、ロジウム、パラジウム、ルテニウム、イリジウムなどの金属およびそれらの金属の化合物を助触媒として添加（担持）した助触媒添加（担持）型光触媒、２）上記の光触媒性金属酸化物に、窒素、炭素、硫黄、リン、ホウ素、フッ素などをドープしたアニオンドープ型光触媒、３）上記の光触媒性金属酸化物に、クロム、ニオブ、マンガン、コバルト、バナジウム、鉄、ニッケルなどの遷移金属イオンをドープしたカチオンドープ型光触媒、４）上記の光触媒性金属酸化物に、アニオンとカチオンの両方をドープした共ドープ型光触媒、５）上記の光触媒性金属酸化物に、白金、パラジウム、ロジウムなど貴金属のハロゲン化物を担持させた金属ハロゲン化物担持型光触媒、６）上記の光触媒性金属酸化物から部分的に酸素を引き抜いた酸素欠損型光触媒、などが例示できる。光触媒性金属酸化物は、上記より１種、または２種以上を併用して用いることができ、特に紫外線励起可能な光触媒性金属酸化物と、可視光線励起可能な光触媒性金属酸化物との併用によるラジカル発生層により、屋内外の光源の種類を問わず光触媒活性によるラジカル酸化作用を発現し、抗菌防黴、及び抗ウイルス性などを常時持続的なものとする。 It is preferable that a radical generation layer capable of being excited by ultraviolet rays (200 nm to 399 nm) or visible light (400 nm to 780 nm) is provided on one surface of a soft vinyl chloride resin sheet (antistatic antibacterial antimold film material). , This radical generation layer performs radical oxidative attack on organic matter by ultraviolet excitation or visible light excitation, and this action destroys and kills the cell membrane of bacteria and mold, and suppresses the growth of bacteria and mold. Acts more effectively and immediately in synergy with the ionic coordination by the ionic liquid compound. For viruses, it suppresses viruses by radically oxidatively attacking the DNA of nucleic acids or the double helix of RNA to destroy DNA and RNA, and this action is synergistic with ion coordination by ionic liquid compounds. It works more effectively and immediately. This radical generation layer is composed of one or more photocatalytic metal oxides selected from titanium oxide, titanium peroxide, zinc oxide, tin oxide, strontium titanate, tungsten oxide, bismuth oxide, and iron oxide. .. In particular, the radical generation layer that can be excited by visible light is 1) using the above photocatalytic metal oxide as an auxiliary catalyst for metals such as silver, platinum, gold, copper, rhodium, palladium, ruthenium, and iridium, and compounds of those metals. Addition (supporting) co-catalyst Addition (supporting) type photocatalyst 2) Anion-doped photocatalyst in which nitrogen, carbon, sulfur, phosphorus, boron, fluorine, etc. are doped into the above photocatalytic metal oxide, 3) The above photocatalyst Cationic-doped photocatalyst in which a sex metal oxide is doped with transition metal ions such as chromium, niobium, manganese, cobalt, vanadium, iron, nickel, etc. 4) The above photocatalytic metal oxide is doped with both anions and cations. 5) Metal halide-supporting photocatalyst in which a halide of a noble metal such as platinum, palladium, or rhodium is supported on the above-mentioned photocatalytic metal oxide, 6) Partial from the above-mentioned photocatalytic metal oxide. An example is an oxygen-deficient photocatalyst that extracts oxygen. The photocatalytic metal oxide can be used alone or in combination of two or more from the above, and in particular, a photocatalytic metal oxide that can be excited by ultraviolet rays and a photocatalytic metal oxide that can be excited by visible rays can be used in combination. The radical oxidative action by photocatalytic activity is exhibited by the radical generation layer due to the photocatalytic activity regardless of the type of light source indoors and outdoors, and the antibacterial and antibacterial properties and the antiviral property are always sustained.

ラジカル発生層にはゾルゲル縮合体を含み、このゾルゲル縮合体は、シラノール基含有有機シラン化合物のゾルゲル縮合、またはチタノール基含有有機チタン化合物のゾルゲル縮合によって形成されたもので、ゾルゲル縮合体によって光触媒性金属酸化物が担持された態様が好ましい。このゾルゲル縮合体の存在によって、軟質塩化ビニル樹脂シートに対するラジカル発生層の密着性、及びラジカル発生層内での光触媒性金属酸化物担持の密着性を高めると同時に、ブリードによる汚れ、膜材同士が癒着するブロッキング問題を生じることのない膜材を得ることができる。光触媒性金属酸化物は、シラノール基含有有機シラン化合物、チタノール基含有有機チタン化合物、などのゾルゲル縮合体を生成可能な成分と共に使用し、ゾルゲル縮合体中に光触媒性金属酸化物が密集した態様のラジカル発生層が好ましい。光触媒性金属酸化物は、ゾルゲル縮合体中の結合の一部に何らかの形で取り込まれた塗膜層となり、基材との密着強さ、表面摩耗強さを向上させる。ラジカル発生層は、光触媒性金属酸化物を含む塗料組成物の塗布、乾燥（熱処理）によるゾルゲル縮合反応により形成される。 The radical generation layer contains a sol-gel condensate, which is formed by sol-gel condensation of a silanol group-containing organic silane compound or sol-gel condensation of a titanol group-containing organic titanium compound, and is photocatalytic by the sol-gel condensate. An embodiment in which a metal oxide is supported is preferable. The presence of this sol-gel condensate enhances the adhesion of the radical generation layer to the soft vinyl chloride resin sheet and the adhesion of the photocatalytic metal oxide carrier in the radical generation layer, and at the same time, stains due to bleeding and the film materials are prevented from becoming dirty. It is possible to obtain a membrane material that does not cause the blocking problem of adhesion. The photocatalytic metal oxide is used in combination with a component capable of producing a sol-gel condensate such as a silanol group-containing organic silane compound and a titanol group-containing organic titanium compound, and the photocatalytic metal oxide is densely packed in the sol-gel condensate. A radical generation layer is preferable. The photocatalytic metal oxide becomes a coating film layer that is somehow incorporated into a part of the bonds in the sol-gel condensate, and improves the adhesion strength with the substrate and the surface abrasion strength. The radical generation layer is formed by a sol-gel condensation reaction by coating a coating composition containing a photocatalytic metal oxide and drying (heat treatment).

シラノール基含有有機シラン化合物は、化学式：ＳｉＯ(ＯＲ)_４で表される４官能加水分解性シラン化合物であり、式中、Ｒは炭素原子数１～１０のアルキル基（特に炭素数１～３の低級アルキル基）、またはアリール基（特にフェニル基）で具体的に、テトラメトキシシラン（Ｓｉ(ＯＣＨ_３)_４：別名テトラメチルシリケート）、テトラエトキシシラン（Ｓｉ(ＯＣ_２Ｈ_５)_４：別名テトラエチルシリケート）、テトラプロポキシシラン（Ｓｉ(ＯＣ_３Ｈ_７)_４：別名テトラプロピルシリケート）、テトラブトキシシラン（Ｓｉ(ＯＣ_４Ｈ_９)_４：別名テトラブチルシリケート）、テトラフェノキシシラン（Ｓｉ(ＯＣ_６Ｈ_６)_４：別名テトラフェニルシリケート）、ジメトキシジエトキシシラン（Ｓｉ(ＯＣＨ_３)_２(ＯＣ_２Ｈ_５)_２：別名ジメチルジエチルシリケート）などである。シラノール基含有有機シラン化合物の多量体は、化学式：Ｓｉ_ｎＯ_ｎ－１(ＯＲ)_{２（ｎ＋１）}で表される縮合体であり、式中、Ｒは炭素原子数１～１０のアルキル基（特に炭素数１～３の低級アルキル基）、またはアリール基（特にフェニル基）、ｎは４官能加水分解性シラン化合物の縮合分子数を表す多量化度（所謂ｎ量体）で、ｎが２以上のシラノール基含有有機シラン化合物多量体は、４官能加水分解性シラン化合物が加水分解して生成するシラノール基同士の反応で２分子以上が縮合して生成する多量体であり、ｎの表す多量化度は多量体１分子中に含有するＳｉ原子数を意味する。本発明においては多量化度２～１０、好ましくは４～６のシラノール基含有有機シラン化合物多量体（Ｓｉ_ｎＯ_ｎ－１(ＯＲ)_{２（ｎ＋１）}）によるゾルゲル縮合体によるラジカル発生層であることが好ましい。このゾルゲル縮合体の原子配列はヨコ軸とタテ軸からなる四角格子網目をモデルとすれば、ヨコ軸とタテ軸の交点にＳｉ原子が配置され、上下左右に隣接するＳｉ－Ｓｉ原子間にＯ原子が配置されたイメージである。 The silanol group-containing organic silane compound is a tetrafunctional hydrolyzable silane compound represented by the chemical formula: SiO (OR) ₄ , in which R is an alkyl group having 1 to 10 carbon atoms (particularly 1 to 3 carbon atoms). (Lower alkyl group), or aryl group (particularly phenyl group), specifically tetramethoxysilane (Si (OCH ₃ ) ₄ : also known as tetramethylsilicate), tetraethoxysilane (Si (OC ₂ H ₅ ) ₄ : alias. Tetraethyl silicate), tetrapropoxysilane (Si (OC ₃ H ₇ ) ₄ : also known as tetrapropyl silicate), tetrabutoxysilane (Si (OC ₄ H ₉ ) ₄ : also known as tetrabutyl silicate), tetraphenoxysilane (Si (OC ₆ )). H ₆ ) ₄ : Also known as tetraphenyl silicate), dimethoxydiethoxysilane (Si (OCH ₃ ) ₂ (OC ₂ H ₅ ) ₂ : also known as dimethyl diethyl silicate), and the like. The multimer of the silanol group-containing organic silane compound is a condensate represented by the chemical formula: Syn On _-1 (OR) 2 ( _{n + 1)} , in which R is an alkyl group having 1 to 10 carbon atoms (1 to 10 carbon atoms). In particular, a lower alkyl group having 1 to 3 carbon atoms), an aryl group (particularly a phenyl group), or n is a degree of mulnation (so-called n-mer) representing the number of condensed molecules of a tetrafunctional hydrolyzable silane compound, and n is 2. The above silanol group-containing organic silane compound multimer is a multimer formed by condensing two or more molecules by the reaction between silanol groups produced by hydrolysis of a tetrafunctional hydrolyzable silane compound, and is represented by n. The degree of quantification means the number of Si atoms contained in one molecule of the multimer. In the present invention, it is a radical generation layer by a sol-gel condensate made of a silanol group-containing organic silane compound multimer (Si _{nOn -1} (OR) _{2 (n + 1)} ) having a degree of mass increase of 2 to 10, preferably 4 to 6. Is preferable. If the atomic arrangement of this solgel condensate is modeled on a square lattice network consisting of horizontal and vertical axes, Si atoms are arranged at the intersections of the horizontal and vertical axes, and O is placed between the Si-Si atoms adjacent to the top, bottom, left, and right. It is an image in which atoms are arranged.

チタノール基含有有機チタン化合物は、化学式：ＴｉＯ(ＯＲ)_４で表される４官能加水分解性チタン化合物であり、式中、Ｒは炭素原子数１～１０のアルキル基（特に炭素数１～３の低級アルキル基）、またはアリール基（特にフェニル基）で具体的に、テトラメトキシチタン（Ｔｉ(ＯＣＨ_３)_４：別名テトラメチルチタネート）、テトラエトキシチタン（Ｔｉ(ＯＣ_２Ｈ_５)_４：別名テトラエチルチタネート）、テトラプロポキシチタン（Ｔｉ(ＯＣ_３Ｈ_７)_４：別名テトラプロピルチタネート）、テトラブトキシチタン（Ｔｉ(ＯＣ_４Ｈ_９)_４：別名テトラブチルチタネート）、テトラフェノキシチタン（Ｔｉ(ＯＣ_６Ｈ_６)_４：別名テトラフェニルチタネート）、ジメトキシジエトキシチタン（Ｔｉ(ＯＣＨ_３)_２(ＯＣ_２Ｈ_５)_２：別名ジメチルジエチルチタネート）などのチタニウムアルコキシド化合物、さらにはトリブトキシチタンステアレート、イソプロポキシチタントリステアレートなどのチタニウムアシレート化合物：Ｔｉ（ＯＯＣＲ）_ｎ、またさらにジイソプロポキシチタンビスアセチルアセトナト、ジイソプロポキシチタンビスエチルアセトアセテートなどのチタニウムキレート化合物：（ＲＯＯ）_２Ｔｉ（ＯＲ）_２錯体、その他、イソプロポキシチタントリイソステアレート、イソプロポキシチタンジメタクリレートイソステアレート、イソプロポキシチタントリスジオクチルホスフェート、ビスジオクチルホスフェートエチレングリコラートチタン、ジブトキシビストリエタノールアミナトチタンなどが例示できる。チタノール基含有有機チタン化合物の多量体は、化学式：Ｔｉ_ｎＯ_ｎ－１(ＯＲ)_{２（ｎ＋１）}で表される縮合体であり、式中Ｒは炭素原子数１～１０のアルキル基（特に炭素数１～３の低級アルキル基）、またはアリール基（特にフェニル基）、ｎは４官能加水分解性チタン化合物の縮合分子数を表す多量化度（所謂ｎ量体）で、ｎが２以上のチタノール基含有有機チタン化合物多量体は、４官能加水分解性チタン化合物が加水分解して生成するチタノール基同士の反応で２分子以上が縮合して生成する多量体であり、ｎの表す多量化度は多量体１分子中に含有するＴｉ原子数を意味する。本発明においては多量化度２～１０、好ましくは４～６のチタノール基含有有機チタン化合物多量体（Ｔｉ_ｎＯ_ｎ－１(ＯＲ)_{２（ｎ＋１）}）によるゾルゲル縮合体によるラジカル発生層が好ましい。このゾルゲル縮合体の原子配列はヨコ軸とタテ軸からなる四角格子網目をモデルとすれば、ヨコ軸とタテ軸の交点にＴｉ原子が配置され、上下左右に隣接するＴｉ－Ｔｉ原子間にＯ原子が配置されたイメージである。 The titanium group-containing organic titanium compound is a tetrafunctional hydrolyzable titanium compound represented by the chemical formula: TiO (OR) ₄ , in which R is an alkyl group having 1 to 10 carbon atoms (particularly 1 to 3 carbon atoms). (Lower alkyl group), or aryl group (particularly phenyl group), specifically tetramethoxytitanium (Ti (OCH ₃ ) ₄ : also known as tetramethyltitanate), tetraethoxytitanium (Ti (OC ₂ H ₅ ) ₄ : alias. Tetraethyl Titanium), Tetrapropoxytitanium (Ti (OC ₃ H ₇ ) ₄ : Also known as Tetrapropyl Titanate), Tetrabutoxytitanium (Ti (OC ₄ H ₉ ) ₄ : Also known as Tetrabutyl Titanium), Tetraphenoxytitanium (Ti (OC ₆ ) H ₆ ) ₄ : Titanium alkoxide compounds such as (also known as tetraphenyl titanate), dimethoxydiethoxytitanium (Ti (OCH ₃ ) ₂ (OC ₂ H ₅ ) ₂ : also known as dimethyldiethyl titanate), as well as tributoxytitanium stearate, iso. Titanium acylate compounds such as propoxytitanium tristearate: Ti (OOCR) _n , and further titanium chelate compounds such as diisopropoxytitanium bisacetylacetonato and diisopropoxytitanium bisethylacetoacetate: (ROO) ₂ Ti (OR) ₂ . Examples of the complex and others include isopropoxytitanium triisostearate, isopropoxytitanium dimethacrylate isostearate, isopropoxytitanium trisdioctyl phosphate, bisdioctyl phosphate ethylene glycolate titanium, and dibutoxybistriethanol aminatotitanium. The multimer of the titanol group-containing organic titanium compound is a condensed product represented by the chemical formula: Tin On _-1 (OR) 2 ( _{n + 1)} , in which R is an alkyl group having 1 to 10 carbon atoms (particularly). A lower alkyl group having 1 to 3 carbon atoms), an aryl group (particularly a phenyl group), or n is a degree of mulchification (so-called n-mer) representing the number of condensed molecules of a tetrafunctional hydrolyzable titanium compound, and n is 2 or more. The titanol group-containing organic titanium compound multimer is a multimer produced by condensing two or more molecules by the reaction between titanol groups produced by hydrolysis of a tetrafunctional hydrolyzable titanium compound, and is represented by n. Degree means the number of Ti atoms contained in one molecule of the multimer. In the present invention, a radical generation layer made of a solgel condensate made of a _titanol group-containing organic titanium compound multimer (Tin On _-1 (OR) _{2 (n + 1)} ) having a degree of mass increase of 2 to 10, preferably 4 to 6, is preferable. .. If the atomic arrangement of this solgel condensate is modeled on a square lattice network consisting of horizontal and vertical axes, Ti atoms are arranged at the intersections of the horizontal and vertical axes, and O between the Ti-Ti atoms adjacent to the top, bottom, left, and right. It is an image in which atoms are arranged.

本発明の帯電防止性抗菌防黴膜材は、軟質塩化ビニル樹脂シート（またはフィルム、塗膜）の態様であると同時に、軟質塩化ビニル樹脂シートが織物を芯材として含み、この織物が、１）経糸及び緯糸からなる織物、または２）経糸及び左上バイアス糸／右上バイアス糸からなる三軸織物、または３）経糸、緯糸及び左上バイアス糸／右上バイアス糸からなる四軸織物、の何れかの態様でもある。上記織物は、平織物（二軸織物、三軸織物、四軸織物）、斜子織物（２×２、３×３、４×４などの正則斜子織、３×２、４×２、４×３、５×３、２×３、２×４、３×４、３×５などの不規則斜子織）、綾織物（経糸、緯糸とも最少３本ずつ用いた最小構成単位を有する：３枚斜文、４枚斜文、５枚斜文、６枚斜文など）、朱子織物（経糸、緯糸とも最少５本ずつ用いた最小構成単位を有する：２飛び、３飛び、４飛び、５飛びなどの正則朱子）、及び変化平織物、変化綾織物、変化朱子織物など、さらに蜂巣織物、梨子地織物、破れ斜文織物、昼夜朱子織物、もじり織物（紗織物、絽織物）、縫取織物、二重織物などの織物が使用できる。織物の目付量は１００～５００ｇ／ｍ^２、空隙率は０～２５％、が適している。これらの織物には精練、漂白、染色、柔軟化、撥水、防黴、防炎、カレンダー、などの公知の染色整理加工を施したものを使用することもできる。 The antistatic antibacterial antifungal film material of the present invention is an embodiment of a soft vinyl chloride resin sheet (or film, coating film), and at the same time, the soft vinyl chloride resin sheet contains a woven fabric as a core material, and this woven fabric is 1 ) A woven fabric consisting of warps and wefts, or a triaxial woven fabric consisting of warps and upper left bias yarns / upper right bias yarns, or 3) a quadrilateral fabric consisting of warps, wefts and upper left bias yarns / upper right bias yarns. It is also an aspect. The above-mentioned woven fabrics include plain woven fabrics (biaxial woven fabrics, triaxial woven fabrics, quaternary woven fabrics), slanted woven fabrics (regular slanted weaves such as 2x2, 3x3, 4x4, 3x2, 4x2, etc. It has a minimum structural unit using at least 3 warp and weft fabrics such as 4x3, 5x3, 2x3, 2x4, 3x4, 3x5, etc. : 3 woven fabrics, 4 woven fabrics, 5 woven fabrics, 6 woven fabrics, etc.), Akiko woven fabric (with a minimum of 5 warp and weft yarns): 2 jumps, 3 jumps, 4 jumps , 5 jumps and other regular woven fabrics), and changed plain woven fabrics, changed woven fabrics, changed woven fabrics, etc. Woven fabrics such as sewn fabrics and double woven fabrics can be used. A basis weight of the woven fabric is 100 to 500 g / m ² , and a porosity of 0 to 25% is suitable. As these woven fabrics, those that have undergone known dyeing arrangement processing such as scouring, bleaching, dyeing, softening, water repellency, mold proofing, flame proofing, and calendar can also be used.

織物を構成する糸条は、合成繊維、天然繊維（綿、ケナフ）、半合成繊維（レーヨン）、無機繊維（ガラス、シリカ、アルミナ）及びこれらの２種以上から成る混合繊維など、何れの繊維も使用できるが、ポリプロピレン繊維、ポリエチレン繊維、ポリビニルアルコール繊維、ポリエステル（ポリエチレンテレフタレート：ＰＥＴ、ポリブチレンテレフタレート：ＰＢＴ、ポリナフタレンテレフタレート：ＰＮＴなど）繊維、ナイロン繊維、アラミド繊維及び、これらの混用繊維（混撚・合撚）などの合成繊維による、１）マルチフィラメント糸条、２）短繊維紡績糸条、３）及びカバリング糸条、から選ばれた１種以上の糸条態様にて使用できる。マルチフィラメント糸条は、ナイロン、ポリエステルなどの熱可塑性樹脂を溶融紡糸した長繊維紡原糸を３～５倍に延伸した長繊維紡糸束（５０～５００本のフィラメント束）のまま無撚、または１～２００回／ｍ撚りを掛けた、繊度１２５～２０００デニール（１３９～２２２２dtex）の糸条が使用できる。これらのマルチフィラメント糸条には、タスラン糸条、ウーリー糸条などの嵩高加工糸条を包含する。短繊維紡績糸条は、ナイロン、ポリエステルなどの熱可塑性樹脂を溶融紡糸した長繊維紡糸束（延伸していてもよい）を３．８～５．８ｍｍ長程度に切断したステープルを開繊練条したスライバを引き伸ばしたロービング（粗糸）とし、これに所定の番手太さにドラフトと撚りを掛けてトウ紡績したものが使用できる。撚糸は単糸または単糸２本を引き揃えてＳ（右）撚りもしくはＺ（左）撚りしたもの、また単糸または単糸２本を引き揃えて下撚りした加撚糸を２本引き揃えて上撚りを掛けてなる双糸が挙げられる。これらの撚糸の撚り回数は２００～２０００回／ｍ程度である。またカバリング糸条は、上記マルチフィラメント糸束の外周に上記短繊維を巻き付けたカバリング糸条が挙げられ、芯鞘複合糸条もカバリング糸条に包含するものとする。 The threads that make up the fabric are any fiber, such as synthetic fibers, natural fibers (cotton, kenaf), semi-synthetic fibers (rayon), inorganic fibers (glass, silica, alumina) and mixed fibers consisting of two or more of these. Polypropylene fiber, polyethylene fiber, polyvinyl alcohol fiber, polyester (polyethylene terephthalate: PET, polybutylene terephthalate: PBT, polynaphthalene terephthalate: PNT, etc.) fiber, nylon fiber, aramid fiber, and mixed fiber (blended twist) thereof can also be used. -It can be used in one or more types of yarns selected from 1) multifilament yarns, 2) short fiber spun yarns, 3) and covering yarns made of synthetic fibers such as synthetic fibers. The multifilament yarn is untwisted or untwisted as a long fiber spun bundle (50 to 500 filament bundles) in which long fiber spun yarn obtained by melt-spinning a thermoplastic resin such as nylon or polyester is stretched 3 to 5 times. A yarn having a fineness of 125 to 2000 denier (139 to 2222 dtex) and twisted from 1 to 200 times / m can be used. These multifilament yarns include bulky processed yarns such as Taslan yarns and Woolly yarns. The short fiber spun yarn is a staple made by cutting a long fiber spun bundle (which may be stretched) obtained by melt-spinning a thermoplastic resin such as nylon or polyester to a length of about 3.8 to 5.8 mm. A roving (coarse yarn) made by stretching a sliver can be used, which is tow-spun by applying a draft and a twist to a predetermined count thickness. The twisted yarn is a single yarn or two single yarns aligned and S (right) twisted or Z (left) twisted, and a single yarn or two single yarns aligned and two under-twisted twisted yarns aligned. A twin yarn made by applying an upper twist can be mentioned. The number of twists of these twisted yarns is about 200 to 2000 times / m. Further, the covering yarn includes a covering yarn in which the short fibers are wound around the outer circumference of the multifilament yarn bundle, and the core-sheath composite yarn is also included in the covering yarn.

本発明の帯電防止性抗菌防黴膜材において、軟質塩化ビニル樹脂シートは、厚さ０．１ｍｍ～０．２９ｍｍのフィルム、または厚さ０．３ｍｍ～２．５ｍｍのシートであることが好ましい。軟質塩化ビニル樹脂シートに織物を芯材として含む態様の製造方法は、軟質塩化ビニル樹脂組成物を熱混練し、カレンダー法、またはＴダイス押出法で溶融圧延したフィルム、またはシートを使用し、これを織物の表裏に熱ラミネートで積層することで得られる。この熱ラミネートは例えば、熱ロール／ゴムロールの連続圧着ユニットを１～２と、冷却ロールユニット、及び巻取ユニットを有するラミネーターを用い、ラミネーターの１回通しまたは２回通しの工程により熱溶融圧着する方法が挙げられる。また、シート基材に織物を芯材として含む態様として、織物の表裏に軟質塩化ビニル樹脂組成物ゾルをナイフコート、クリアランスコート、グラビアコートなどのコーティング法により塗工し、これを熱乾燥、または加熱ゲル化によって、樹脂被覆層を形成したもの、または軟質塩化ビニル樹脂組成物ゾルを充填した液浴中に織物を浸漬し、これを引き上げると同時に１対のゴムロール間で圧搾し、直後に熱乾燥、または加熱ゲル化させるディッピング法によって、織物の表裏に樹脂被覆層を形成したものが挙げられる。 In the antistatic antibacterial antibacterial film material of the present invention, the soft vinyl chloride resin sheet is preferably a film having a thickness of 0.1 mm to 0.29 mm or a sheet having a thickness of 0.3 mm to 2.5 mm. As a method for producing a soft vinyl chloride resin sheet containing a woven fabric as a core material, a film or sheet obtained by hot-kneading a soft vinyl chloride resin composition and melt-rolling it by a calender method or a T-die extrusion method is used. Is obtained by laminating the front and back of the woven fabric with a thermal laminate. For this thermal laminating, for example, a continuous crimping unit of a hot roll / rubber roll is used, and a laminator having a cooling roll unit and a winding unit is used, and heat melt crimping is performed by a one-time or two-time process of the laminator. The method can be mentioned. In addition, as a mode in which the woven fabric is included in the sheet base material as the core material, the soft vinyl chloride resin composition sol is applied to the front and back of the woven fabric by a coating method such as knife coat, clearance coat, gravure coat, etc., and this is heat-dried or heat-dried. The woven fabric is immersed in a liquid bath in which a resin coating layer is formed by heat gelation or filled with a soft vinyl chloride resin composition sol, and the woven fabric is pulled up and simultaneously squeezed between a pair of rubber rolls, and immediately after that, heat is applied. Examples thereof include a woven fabric in which a resin coating layer is formed on the front and back surfaces of the woven fabric by a dipping method of drying or heat gelling.

また軟質塩化ビニル樹脂シート（帯電防止性抗菌防黴膜材）には、アルキルアミン類、第４級アンモニウム塩類などのカチオン性帯電防止剤；脂肪酸塩類、アルキル硫酸エステル塩類、アルキルベンゼンスルホン酸塩類、アルキルナフタレンスルホン酸類、アルキルスルホコハク酸塩類、アルキルジフェニルエーテルジスルホン酸塩類、アルキルリン酸塩類、ポリオキシエチレンアルキル硫酸エステル塩類、ポリオキシエチレンアルキルアリル硫酸エステル塩類、ナフタレンスルホン酸ホルマリン縮合物、カルボン酸型高分子界面活性剤類などのアニオン性帯電防止剤；及びアルキルベタイン類、アミンオキサイド類などの両性イオン性帯電防止剤、及び上記帯電防止剤を高分子量化した高分子型帯電防止剤などを軟質塩化ビニル樹脂シートに対して０．０５～２質量％程度併用することができる。無機導電性材料としては、カーボンブラック、黒鉛、フラーレン、カーボンナノチューブなどの炭素系材料や、酸化インジウム、酸化亜鉛、酸化スズ、チタン酸カリウム、酸化チタン、スズ－アンチモン系酸化物、インジウム－スズ系酸化物、アンチモン－スズ系酸化物などの金属系材料を軟質塩化ビニル樹脂シートに対して０．０５～２質量％程度併用することができる。 In addition, the soft vinyl chloride resin sheet (antistatic antibacterial antistatic film material) is a cationic antistatic agent such as alkylamines and quaternary ammonium salts; fatty acid salts, alkyl sulfate ester salts, alkylbenzene sulfonates, alkyl. Naphthalene sulfonic acids, alkyl sulfosuccinates, alkyl diphenyl ether disulfonates, alkyl phosphates, polyoxyethylene alkyl sulfate esters, polyoxyethylene alkyl allyl sulfate esters, naphthalene sulfonic acid formalin condensates, carboxylic acid type polymer surfactants. Anionic antistatic agents such as activators; and amphoteric ionic antistatic agents such as alkylbetaines and amine oxides, and high molecular weight antistatic agents obtained by increasing the amount of the above antistatic agents, etc., are soft vinyl chloride resins. It can be used in combination with the sheet in an amount of about 0.05 to 2% by mass. Inorganic conductive materials include carbon-based materials such as carbon black, graphite, fullerene, and carbon nanotubes, indium oxide, zinc oxide, tin oxide, potassium titanate, titanium oxide, tin-antimon oxide, and indium-tin oxide. A metal-based material such as an oxide or an antimon-tin oxide can be used in combination with a soft vinyl chloride resin sheet in an amount of about 0.05 to 2% by mass.

また軟質塩化ビニル樹脂シート（帯電防止性抗菌防黴膜材）には、黴、細菌（グラム陽性、グラム陰性）、真菌などの細胞壁、細胞膜、細胞質、及び細胞核などに対して、酸化的リン酸化阻害、電子伝達系阻害、－ＳＨ基阻害、ＤＮＡ合成阻害、細胞表皮機能阻害、脂質代謝阻害、キレート形成などの作用を及ぼす有機化合物を含むことが好ましく、このような有機化合物としては、イミダゾール系化合物、チアゾール系化合物、イソチアゾリン系化合物、ピリジン系化合物、トリアジン系化合物、トリアゾール系化合物、Ｎ－ハロアルキルチオ系化合物、四級アンモニウム塩系化合物、フェノキシアルシン化合物など、具体的に、１０，１０^′－オキシビスフェノキシアルシン、２－（４－チアゾリル）－ベンズイミダゾールが特に好ましい。これら有機化合物は、メソポーラスシリカ、（合成）ゼオライト、チタンゼオライト、リン酸ジルコニウム、リン酸カルシウム、リン酸亜鉛カルシウム、ハイドロタルサイト、ヒドロキシアパタイト、シリカアルミナ、ケイ酸カルシウム、ケイ酸アルミン酸マグネシウム、ケイソウ土などの粒子、及びこれら粒子のシランカップリング剤処理物、から選ばれた１種以上の多孔質粒子に担持されていることが徐放効果の観点において好ましい。有機化合物または多孔質粒子担持物は、軟質塩化ビニル樹脂シートに対して０．０５～１質量％程度併用することができる。 In addition, the soft vinyl chloride resin sheet (antistatic antibacterial anti-mold film material) oxidatively phosphorylates the cell walls of molds, bacteria (gram-positive, gram-negative), fungi, etc., cell membranes, cytoplasm, and cell nuclei. It is preferable to contain an organic compound that exerts actions such as inhibition, electron transfer system inhibition, -SH group inhibition, DNA synthesis inhibition, cell epidermal function inhibition, lipid metabolism inhibition, chelate formation, etc., and examples of such an organic compound include imidazole compounds. Specific examples include compounds, thiazole-based compounds, isothiazoline ^- based compounds, pyridine-based compounds, triazine-based compounds, triazole-based compounds, N-haloalkylthio-based compounds, quaternary ammonium salt-based compounds, and phenoxyarcin compounds. Oxybisphenoxyarcin, 2- (4-thiazolyl) -benzimidazole is particularly preferred. These organic compounds include mesoporous silica, (synthetic) zeolite, titanium zeolite, zirconium phosphate, calcium phosphate, zinc calcium phosphate, hydrotalcite, hydroxyapatite, silica alumina, calcium silicate, magnesium silicate aluminate, silicate soil, etc. It is preferable that the particles are supported on one or more kinds of porous particles selected from the particles of the above and the silane coupling agent-treated product of these particles from the viewpoint of the sustained release effect. The organic compound or the porous particle carrier can be used in combination with the soft vinyl chloride resin sheet in an amount of about 0.05 to 1% by mass.

本発明の帯電防止性抗菌防黴膜材は、フィルム、シート、テープの形態、織物、ターポリン、メッシュシート、合成皮革、帆布などの形態で、これらのパーツを熱融着法で縫製し、天井膜、空間仕切り、巻上昇降式シートシャッター、クリーンルームカーテン、壁紙、敷物、カバー、ブラインド、防護衣、フェイスガード、など加工されて、工場、オフィス、学校、商業施設、病院、介護施設、式場、ごみ集積場、公衆トイレ、動物園などに広く使用される。特にターポリン、帆布などは、医療検査用パーティション、空気注入式仮設膜構造による医療検査用陰圧テントシェルターに適して用いることができる。膜材同士の接合（同じ面に向き揃えての端部重ね合わせ接着）は、高周波ウエルダー機を用いて高周波振動によって接合を行うことができる。具体的に、２ヶ所の電極（一方の電極は、ウエルドバー）間に膜材を置き、ウエルドバーで加圧しながら高周波（１～２００ＭＨｚ）で発振する電位差を印加することで膜材を分子摩擦熱で溶融軟化状態とすることで融合し、その状態で冷却固化して接合体を得る。また、超音波振動子から発生する超音波エネルギー（１６～３０ＫＨｚ）の振幅を増幅させ、膜材の境界面に発生する摩擦熱を利用して融合を行う超音波融着法、またはヒーターの電気制御によって、１００～７００℃に無段階設定された熱風を、ノズルを通じて膜材間に吹き込み、膜材の表面を溶融軟化させ、ノズル通過直後膜材を圧着して融合を行う熱風融着法、膜材の溶融温度以上にヒーター内蔵加熱した金型（こて）を用いて被着体を圧着し融合を行う熱板融着法などによって接合可能である。これらの融着接合方法において、ラジカル発生層の存在が融着接合の阻害となって融着接合部の耐久強度が得られないことがあるので、ラジカル発生層を付帯する態様においては、グラインダーなどによるラジカル発生層の切削、研削除去を行うことが好ましい。 The antistatic antibacterial anti-mold film material of the present invention is in the form of a film, sheet, tape, woven fabric, tarpaulin, mesh sheet, synthetic leather, canvas, etc., and these parts are sewn by heat fusion method to the ceiling. Membranes, space dividers, hoisting lift sheet shutters, clean room curtains, wallpaper, rugs, covers, blinds, protective clothing, face guards, etc. are processed into factories, offices, schools, commercial facilities, hospitals, nursing homes, ceremonial halls, etc. Widely used in garbage collection areas, public toilets, zoos, etc. In particular, tarpaulins, canvas and the like can be suitable for medical examination partitions and negative pressure tent shelters for medical examinations due to an inflatable temporary membrane structure. The bonding between the film materials (the end overlapping and bonding with the same surface facing each other) can be performed by high-frequency vibration using a high-frequency welder machine. Specifically, a film material is placed between two electrodes (one electrode is a weld bar), and the film material is subjected to molecular friction by applying a potential difference oscillating at a high frequency (1 to 200 MHz) while pressurizing with the weld bar. It is fused by being melted and softened by heat, and then cooled and solidified in that state to obtain a bonded body. In addition, an ultrasonic fusion method that amplifies the amplitude of ultrasonic energy (16 to 30 KHz) generated from an ultrasonic transducer and fuses using the frictional heat generated at the interface of the membrane material, or the electric heater. A hot air fusion method in which hot air set steplessly at 100 to 700 ° C. is blown between the membrane materials through a nozzle to melt and soften the surface of the membrane material, and the membrane material is crimped and fused immediately after passing through the nozzle. It can be joined by a hot plate fusion method in which the adherend is crimped and fused using a mold (iron) that has a built-in heater and is heated above the melting temperature of the membrane material. In these fusion-bonding methods, the presence of the radical-generating layer may hinder the fusion-bonding and the durable strength of the fusion-bonded portion may not be obtained. It is preferable to perform cutting and grinding removal of the radical generation layer by the above method.

次ぎに実施例、比較例を挙げて本発明を具体的に説明するが、本発明はこれらの例の範囲に限定されるものではない。下記実施例及び比較例において、帯電防止性抗菌防黴膜材の効果は以下の測定方法によって評価した。
（１）表面抵抗率測定（JIS K7194準拠）
２３℃、相対湿度５０％ＲＨで膜材片を２４時間静置後、下記の抵抗率計（JIS K7194準拠）を用い表面抵抗率を３回測定し、その平均値を表面抵抗率とした。帯電防止性の基準は表面抵抗率１０⁹Ω/□以下とし、１０⁹Ω/□以下であれば、アレルゲン性（黴、ダニダスト、花粉）物質の静電吸着が抑止可能、アレルゲン性物質を寄せ付け難いものとした。
１）高抵抗・抵抗率計
株式会社三菱化学アナリテック製「ハイレスタUP MCP-HT800（レンジ１０³～１０¹⁴Ω）
２）低抵抗・抵抗率計
株式会社三菱化学アナリテック製「ロレスタGX MCP-T700（レンジ１０^-4～１０⁷Ω）」
（２）抗菌性（JIS Z2801：2010年準拠）
シート状物試験片（ラジカル発生層のある試験片はラジカル発生層）の表面に菌液を滴下して植菌し（植菌数１０^４）、試験片が菌液に接するように、菌液と試験片シート状物を密着させ、３５℃、相対湿度９０％以上の環境下、ブラックライト（ピーク３６５ｎｍ）照射（ラジカル発生層形成のある試験片のみ：照射距離２．５ｃｍ）条件下で２４時間培養した。培養後、試験片シートを洗い流し１ｃｍ^２あたりの生菌数を測定し、抗菌活性値（対象区における菌数対数値から実施例または比較例の試験片シート状物における菌数対数値を差し引いた値）を算出した。
また実施例のシート状物試験片にブラックライトの照射、または蛍光灯の照射を行わず、ブラックライトもしくは蛍光灯の有無による抗菌効果の対比試験を行った結果を参考例の扱いとした。
表中の数値は試験片１ｃｍ^２当たりの生菌数であり、「ＮＤ」は生菌の不検出（Not Detected）とする。菌液調整溶液は１／２００ＮＢ培地を用いた。使用した菌種を以下に示す。
黄色ぶどう球菌「Staphylococcus aureus subsp. aureus 12732」
大腸菌「Escherichia coli NBRC 3972」
※ブラックライト 機種ＳＬ－Ｂ０１Ａ５（オーム電機株式会社）実施例９～１２
Ｗ５５ｍｍ×Ｈ１６０ｍｍ×Ｄ２５ｍｍ
※直管蛍光灯 ４Ｗ（ＦＬ４Ｄ）×２本（パナソニック株式会社）実施例１３～１６
（３）防黴性（JIS Z2911培養試験）
幅３cm×長さ３cmのシート状物（ラジカル発生層のある試験片はラジカル発生層）に、下記試験用黴の胞子を接種し、ポテト・デキストロース寒天培地上に置き、ブラックライト（ピーク３６５ｎｍ）照射、または蛍光灯照射（ラジカル発生層形成のある試験片のみ：照射距離２．５ｃｍ）条件下、２８℃×７日間、及び１４日間、黴の発生状況を観察し、以下の判定基準で評価した。
また実施例のシート状物試験片にブラックライトの照射、または蛍光灯の照射を行わず、ブラックライトもしくは蛍光灯の有無による防黴効果の対比試験を行った結果を参考例の扱いとした。
１：接種部分に菌糸の発育が認められない
２：接種部分に認められる菌糸の発育部分の面積が全面積の１/３を超えない
３：接種部分に認められる菌糸の発育部分の面積が全面積の１/３を超える
〈試験用黴〉（Ａ）＋（Ｂ）＋（Ｃ）の混合黴
（Ａ）Aspergillus niger NBRC 105649（黒黴）
（Ｂ）Penicillium citrinum NBRC 6352（青黴）
（Ｃ）Cladosporium cladosporioides NBRC 6348（クロカワ黴）
※ブラックライト 機種ＳＬ－Ｂ０１Ａ５（オーム電機株式会社）実施例９～１２
Ｗ５５ｍｍ×Ｈ１６０ｍｍ×Ｄ２５ｍｍ
※直管蛍光灯 ４Ｗ（ＦＬ４Ｄ）×２本（パナソニック株式会社）実施例１３～１６
（４）抗ウイルス性（ISO 21720）
※プラスチック製品向け抗菌試験方法：ISO 22196（JIS Z2801）準拠
試験方法：一般財団法人カケンテストセンター法
５ｃｍ×５ｃｍの試験片（ラジカル発生層のある試験片はラジカル発生層）に０．４ｍｌのネコカリシウイルス（feline calicivirus）液を滴下し、４ｃｍ×４ｃｍのフィルムで被覆し、２５℃×２４Ｈｒ静置（ブラックライト：ピーク３６５ｎｍ照射、または蛍光灯照射（ラジカル発生層形成のある試験片のみ：照射距離２．５ｃｍ条件下）した後、抗ウイルス活性値を測定。
抗ウイルス活性値は、抗ウイルス未加工の試験片の２４時間静置後のウイルス感染価（ＰＦＵ/ｃｍ^２）の常用対数の平均値から、抗ウイルス加工品の24時間静置後のウイルス感染価（ＰＦＵ/ｃｍ^２）の常用対数の平均値を差し引いた値で、抗ウイルス活性値２．０以上（ウイルスの減少率１/１００以上、抗ウイルス活性値３．０以上はウイルスの減少率１／１０００）を効果ありと判断する。
また実施例のシート状物試験片にブラックライトの照射、または蛍光灯の照射を行わず、ブラックライトもしくは蛍光灯の有無による抗ウイルス性の効果の対比試験を行った結果を参考例とした。
（５）ブロッキング抑止効果（積重法）
１０ｃｍ×１０ｃｍサイズの正方形試料２枚を位置ズレのないよう（一方の試料の表面に、もう一方の試料の裏面が重なる状態）に重ね、２枚のガラス板（１０ｃｍ×１０ｃｍサイズ×５ｍｍ厚）で挟み、５ｋｇ荷重×３５℃×２４０時間静置後、取り出した積重試料の一角を２ｃｍ（対角を結ぶ線上の距離）剥がしてスタンドにクリップ止めで固定し、もう一方の一角２ｃｍ（対角を結ぶ線上の距離）部を重り（１００ｇ）を装備したクリップで掴み、重りから手を離した瞬間から２枚の試料が分離するまでの時間（荷重した試料が落下するまでの時間）を計測した。この試験試料の密着面積は９２ｃｍ^２である。
※シート巻回体を横に倒して長期間床置した状態を想定した試験
１（極めて良好）：分離して即時落下
２（良好）：３秒以内
３（やや不良）：３秒超１０秒以内
４（不良）：１０秒を超えても分離しない
５（劣悪）：癒着して樹脂層が剥がれる Next, the present invention will be specifically described with reference to Examples and Comparative Examples, but the present invention is not limited to the scope of these examples. In the following Examples and Comparative Examples, the effect of the antistatic antibacterial antifungal film material was evaluated by the following measurement method.
(1) Surface resistivity measurement (JIS K7194 compliant)
After allowing the film material piece to stand at 23 ° C. and a relative humidity of 50% RH for 24 hours, the surface resistivity was measured three times using the following resistivity meter (JIS K7194 compliant), and the average value was taken as the surface resistivity. The standard of antistatic property is a surface resistivity of 10 ⁹ Ω / □ or less, and if it is 10 ⁹ Ω / □ or less, electrostatic adsorption of allergenic substances (mold, tick dust, pollen) can be suppressed, and allergenic substances are attracted. I made it difficult.
1) High resistivity / resistivity meter Mitsubishi Chemical Analytech Co., Ltd. "High Resta UP MCP-HT800 (range 10 ³ to 10 ¹⁴ Ω)"
2) Low resistivity / resistivity meter "Loresta GX MCP-T700 (range 10 ^-4 to 10 ⁷ Ω)" manufactured by Mitsubishi Chemical Analytech Co., Ltd.
(2) Antibacterial property (JIS Z2801: 2010 compliant)
A bacterial solution is dropped on the surface of a sheet-shaped test piece (a test piece having a radical generation layer is a radical generation layer) and inoculated ⁽ inoculation number 104) so that the test piece is in contact with the bacterial solution. And the test piece sheet-like material are brought into close contact with each other, and under the conditions of black light (peak 365 nm) irradiation (only test piece with radical generation layer formation: irradiation distance 2.5 cm) at 35 ° C. and relative humidity of 90% or more, 24 It was cultured for hours. After culturing, the test piece sheet was washed away, the viable cell count per 1 cm ² was measured, and the antibacterial activity value (the bacterial count log value in the test piece sheet form of the Example or Comparative Example was subtracted from the bacterial count logarithmic value in the target group). Value) was calculated.
In addition, the result of a comparison test of the antibacterial effect with and without black light or fluorescent lamp without irradiating the sheet-shaped test piece of the example with black light or fluorescent lamp was treated as a reference example.
The numerical value in the table is the number of viable bacteria per 1 cm ² of the test piece, and "ND" is defined as "Not Detected". A 1/200 NB medium was used as the bacterial solution adjusting solution. The bacterial species used are shown below.
Staphylococcus aureus subsp. Aures 12732 "Staphylococcus aureus subsp.
Escherichia coli NBRC 3972
* Black light model SL-B01A5 (Ohm Electric Co., Ltd.) Examples 9-12
W55mm x H160mm x D25mm
* Straight tube fluorescent lamp 4W (FL4D) x 2 (Panasonic Corporation) Examples 13 to 16
(3) Mold resistance (JIS Z2911 culture test)
A sheet-like material having a width of 3 cm and a length of 3 cm (a test piece having a radical generation layer is a radical generation layer) is inoculated with the following test mold spores, placed on a potato / dextrose agar medium, and black light (peak 365 nm). Under the conditions of irradiation or fluorescent light irradiation (only test pieces with radical generation layer formation: irradiation distance 2.5 cm), observe the mold generation status at 28 ° C for 7 days and 14 days, and evaluate according to the following criteria. did.
In addition, the result of a comparison test of the antifungal effect with and without black light or fluorescent lamp without irradiating the sheet-shaped test piece of the example with black light or fluorescent lamp was treated as a reference example.
1: No hyphal growth is observed in the inoculated area 2: The area of the hyphal growth area observed in the inoculated area does not exceed 1/3 of the total area 3: The area of the hyphal growth area observed in the inoculated area is the entire area <Test mold> (A) + (B) + (C) mixed mold that exceeds 1/3 of the area (A) Aspergillus niger NBRC 105649 (black mold)
(B) Penicillium citrinum NBRC 6352 (Penicillium)
(C) Cladosporium cladosporioides NBRC 6348 (Kurokawa mold)
* Black light model SL-B01A5 (Ohm Electric Co., Ltd.) Examples 9-12
W55mm x H160mm x D25mm
* Straight tube fluorescent lamp 4W (FL4D) x 2 (Panasonic Corporation) Examples 13 to 16
(4) Antiviral (ISO 21720)
* Antibacterial test method for plastic products: ISO 22196 (JIS Z2801) compliant test method: Kaken Test Center Method 5 cm x 5 cm test piece (test piece with radical generation layer is a radical generation layer) and 0.4 ml cat A feline calicivirus solution is dropped, covered with a 4 cm x 4 cm film, and allowed to stand at 25 ° C. x 24 hours (black light: peak 365 nm irradiation, or fluorescent lamp irradiation (test piece with radical generation layer formation only: irradiation). After (under the condition of a distance of 2.5 cm), the anti-virus activity value was measured.
The anti-virus activity value is determined from the average value of the common logarithm of the virus infection titer (PFU / cm ² ) after 24 hours of standing of the anti-virus processed test piece, and the virus infection of the anti-virus processed product after 24 hours of standing. The value obtained by subtracting the average value of the common logarithm of the value (PFU / cm ² ), the anti-virus activity value is 2.0 or more (virus reduction rate of 1/100 or more, anti-virus activity value of 3.0 or more is the virus reduction rate). 1/1000) is judged to be effective.
Further, the result of a comparison test of the antiviral effect depending on the presence or absence of the black light or the fluorescent lamp without irradiating the sheet-shaped test piece of the example with the black light or the fluorescent lamp was used as a reference example.
(5) Blocking deterrent effect (product method)
Two 10 cm x 10 cm square samples are stacked on top of each other so that there is no misalignment (the front surface of one sample overlaps the back surface of the other sample), and two glass plates (10 cm x 10 cm size x 5 mm thickness). After sandwiching with 5 kg load x 35 ° C x 240 hours, peel off one corner of the stacked sample taken out by 2 cm (distance on the line connecting the diagonals), fix it to the stand with a clip, and fix the other corner to 2 cm (pair). Grasp the (distance on the line connecting the corners) part with a clip equipped with a weight (100 g), and the time from the moment you release your hand from the weight until the two samples separate (the time until the loaded sample falls). I measured it. The contact area of this test sample is 92 cm ² .
* Test assuming that the sheet winding body is laid on its side for a long period of time 1 (extremely good): separated and immediately dropped 2 (good): within 3 seconds 3 (slightly poor): over 3 seconds 10 seconds Within 4 (poor): Does not separate even after 10 seconds 5 (poor): Adhesion and peeling of resin layer

［実施例１］
ポリエステル繊維平織基布（経糸１１１１dtexマルチフィラメント糸条：糸密度２２本／２．５４ｃｍ×緯糸１１１１dtexマルチフィラメント糸条：糸密度２４本／２．５４ｃｍ：空隙率２１％：質量１６５ｇ／ｍ^２）を基材として、その両面に下記〔配合１〕軟質塩化ビニル樹脂組成物からなる厚さ０．２ｍｍのカレンダー成型フィルムを表層、及び裏層として熱圧着ブリッジ溶融ラミネートにより「表フィルム層／織物／裏フィルム層」とする、厚さ０．７５ｍｍ、質量７８５ｇ／ｍ^２のターポリン（１）を得た。
〔配合１〕軟質塩化ビニル樹脂組成物
塩化ビニル樹脂（重合度１３００） １００質量部
液状エステル化合物（１） ３０質量部
※ｎオクタノールにエチレンオキシドを付加したアルコールとアジピン酸との反応によ
るアジピン酸ジエステル：(エーテル結合２個〔化１〕に相当：分子量４９０の可塑剤)
４－シクロヘキセン－１，２－ジカルボン酸ビス（２－エチルヘキシル）３０質量部
※分子量３９４の可塑剤
エポキシ化大豆油（安定剤） ５質量部
バリウム／亜鉛複合安定剤 ２質量部
三酸化アンチモン（難燃剤） １０質量部
ルチル型酸化チタン（白顔料） ５質量部
ベンゾトリアゾール骨格化合物（紫外線吸収剤） ０．３質量部
１－エチル－３－メチルイミダゾリウム／ビス（トリフルオロメタンスルホニル）イミド（〔ＣＦ₃ＳＯ₂〕₂Ｎ^-）：イオン液体化合物（１） ３質量部
※イオン液体化合物（１）と液状エステル化合物（１）との併用質量比は１：１０、イオン液体化合物（１）と可塑剤との併用質量比は１：２０ [Example 1]
Polyester fiber plain weave base fabric (warp 1111dtex multifilament yarn: yarn density 22 / 2.54 cm × weft 1111dtex multifilament yarn: yarn density 24 / 2.54 cm: void ratio 21%: mass 165 g / m ² ) As a base material, a calendar-molded film having a thickness of 0.2 mm made of the following [formulation 1] soft vinyl chloride resin composition is used as a front layer on both sides thereof, and a heat-bonded bridge melt-laminated as a back layer to "front film layer / fabric / back". A tarpaulin (1) having a thickness of 0.75 mm and a mass of 785 g / m ² was obtained as a “film layer”.
[Formulation 1] Soft vinyl chloride resin composition Vinyl chloride resin (degree of polymerization 1300) 100 parts by mass Liquid ester compound (1) 30 parts by mass * n Adipic acid by reaction between alcohol with ethylene oxide added to octanol and adipic acid Diester: (corresponds to 2 ether bonds [Chemical formula 1]: plasticizer with a molecular weight of 490)
4-Cyclohexene-1,2-dicarboxylic acid bis (2-ethylhexyl) 30 parts by mass * Plasticizer with a molecular weight of 394
Eoxidized soybean oil (stabilizer) 5 parts by mass barium / zinc composite stabilizer 2 parts by mass Antimon trioxide (flame retardant) 10 parts by mass rutile type titanium oxide (white pigment) 5 parts by mass benzotriazole skeleton compound (ultraviolet absorber) 0.3 parts by mass 1-ethyl-3-methylimidazolium / bis (trifluoromethanesulfonyl) imide ([CF ₃ SO ₂ ] ₂ N- ⁾ : ionic liquid compound (1) 3 parts by mass * ionic liquid compound (1) The combined mass ratio of the liquid ester compound (1) and the liquid ester compound (1) is 1:10, and the combined mass ratio of the ionic liquid compound (1) and the plasticizing agent is 1:20.

［実施例２］
実施例１のターポリン（１）において〔配合１〕の液状エステル化合物（１）３０質量部を、ｎ－オクタノールにエチレンオキシドを付加したアルコールと無水フタル酸の反応によるフタル酸ジエステル：液状エステル化合物（２）：（エーテル結合２個〔化１〕に相当：分子量５１０の可塑剤）、３０質量部に置換えた〔配合２〕とした以外は実施例１と同様にして厚さ０．７５ｍｍ、質量７８５ｇ／ｍ^２のターポリン（２）を得た。 [Example 2]
In the tarpaulin (1) of Example 1, a phthalic acid diester: a liquid ester compound (2) obtained by reacting 30 parts by mass of the liquid ester compound (1) of [Formulation 1] with an alcohol obtained by adding ethylene oxide to n-octanol and phthalic anhydride. ): (Equivalent to 2 ether bonds [Chemical formula 1]: Plasticizer having a molecular weight of 510), with the exception of [Formulation 2] replaced with 30 parts by mass, the thickness is 0.75 mm and the mass is 785 g in the same manner as in Example 1. A tarpaulin (2) of / m ² was obtained.

［実施例３］
実施例１のターポリン（１）において〔配合１〕の液状エステル化合物（１）３０質量部を、ｎオクタノールにプロピレンオキシドを付加したアルコールとセバシン酸との反応によるセバシン酸ジエステル：液状エステル化合物（３）：（エーテル結合２個〔化１〕に相当：分子量５７４の可塑剤）、３０質量部に置換えた〔配合３〕とした以外は実施例１と同様にして厚さ０．７５ｍｍ、質量７８５ｇ／ｍ^２のターポリン（３）を得た。 [Example 3]
In the tarpaulin (1) of Example 1, a sebacic acid diester: a liquid ester compound (3) is obtained by reacting 30 parts by mass of the liquid ester compound (1) of [Formulation 1] with an alcohol obtained by adding propylene oxide to n-octanol and sebacic acid. ): (Equivalent to 2 ether bonds [Chemical formula 1]: plasticizer having a molecular weight of 574), and the thickness was 0.75 mm and the mass was 785 g in the same manner as in Example 1 except that it was replaced with 30 parts by mass [Formulation 3]. A tarpaulin (3) of / m ² was obtained.

［実施例４］
実施例１のターポリン（１）において〔配合１〕の液状エステル化合物（１）３０質量部を、テトラエチレングリコールのオクチル酸エステル：液状エステル化合物（４）：（エーテル結合３個〔化２〕に相当：分子量４７８の可塑剤）、３０質量部に置換えた〔配合４〕とした以外は実施例１と同様にして厚さ０．７５ｍｍ、質量７８５ｇ／ｍ^２のターポリン（４）を得た。 [Example 4]
In the tarpaulin (1) of Example 1, 30 parts by mass of the liquid ester compound (1) of [Formulation 1] was converted into an octylate ester of tetraethylene glycol: a liquid ester compound (4): (three ether bonds [formation 2]. Esters (4) having a thickness of 0.75 mm and a mass of 785 g / m ² were obtained in the same manner as in Example 1 except that the plasticizer had a molecular weight of 478 and was replaced with 30 parts by mass [Compound 4].

［実施例５］
実施例１のターポリン（１）において〔配合１〕の１－エチル－３－メチルイミダゾリウム／ビス（トリフルオロメタンスルホニル）イミド：イオン液体化合物（１）３質量部を、１－エチル－３－メチルイミダゾリウム／テトラフルオロボレート（ＢＦ₄ ^-）：イオン液体化合物（２）３質量部に置換えた〔配合５〕とした以外は実施例１と同様にして厚さ０．７５ｍｍ、質量７８５ｇ／ｍ^２のターポリン（５）を得た。 [Example 5]
In the tarpaulin (1) of Example 1, 1-ethyl-3-methylimidazolium / bis (trifluoromethanesulfonyl) imide of [Formulation 1]: 3 parts by mass of the ionic liquid compound (1) was added to 1-ethyl-3-methyl. Imidazole / tetrafluoroborate (BF _4- ⁾ : Ionic liquid compound (2) Thickness 0.75 mm, mass 785 g / m ² in the same manner as in Example 1 except that it was replaced with 3 parts by mass [Formulation 5]. Tarpaulin (5) was obtained.

［実施例６］
実施例１のターポリン（１）において〔配合ｑ〕の１－エチル－３－メチルイミダゾリウム／ビス（トリフルオロメタンスルホニル）イミド：イオン液体化合物（１）３質量部を、１－ブチル－３－メチルピリジニウム／ビス（トリフルオロメチルスルホニル）イミド（〔ＣＦ₃ＳＯ₂〕₂Ｎ^-）：イオン液体化合物（３）３質量部に置換えた〔配合６〕とした以外は実施例１と同様にして厚さ０．７５ｍｍ、質量７８５ｇ／ｍ^２のターポリン（６）を得た。 [Example 6]
In the tarpaulin (1) of Example 1, 1-ethyl-3-methylimidazolium / bis (trifluoromethanesulfonyl) imide of [formulation q]: 3 parts by mass of the ionic liquid compound (1) was added to 1-butyl-3-methyl. Pyridinium / bis (trifluoromethylsulfonyl) imide ([CF ₃ SO ₂ ] ₂ N- ⁾ : Ionic liquid compound (3) Thickness as in Example 1 except that it was replaced with 3 parts by mass [Formulation 6]. A tarpaulin (6) having a size of 0.75 mm and a mass of 785 g / m ² was obtained.

［実施例７］
実施例１のターポリン（１）において〔配合１〕の１－エチル－３－メチルイミダゾリウム／ビス（トリフルオロメタンスルホニル）イミド：イオン液体化合物（１）３質量部を、１－ブチル－３－メチルピリジニウム／トリフルオロメタンスルホネート（ＣＦ₃ＳＯ_３ ^-）：イオン液体化合物（４）３質量部に置換えた〔配合７〕とした以外は実施例１と同様にして厚さ０．７５ｍｍ、質量７８５ｇ／ｍ^２のターポリン（７）を得た。 [Example 7]
In the tarpaulin (1) of Example 1, 1-ethyl-3-methylimidazolium / bis (trifluoromethanesulfonyl) imide of [Formulation 1]: 3 parts by mass of the ionic liquid compound (1) was added to 1-butyl-3-methyl. Pyridinium / trifluoromethanesulfonate (CF ₃ SO _3- ⁾ : Ionic liquid compound (4) Thickness 0.75 mm, mass 785 g / m in the same manner as in Example 1 except that it was replaced with 3 parts by mass [Formulation 7]. ^Two tarpaulins (7) were obtained.

［実施例８］
実施例１のターポリン（１）において〔配合１〕の１－エチル－３－メチルイミダゾリウム／ビス（トリフルオロメタンスルホニル）イミド：イオン液体化合物（１）３質量部を、Ｎ，Ｎ，Ｎ－トリメチル－Ｎ－ブチルアンモニウム／クロライド（Ｃｌ^-）：イオン液体化合物（５）３質量部に置換えた〔配合８〕とした以外は実施例１と同様にして厚さ０．７５ｍｍ、質量７８５ｇ／ｍ^２のターポリン（８）を得た。 [Example 8]
In the tarpaulin (1) of Example 1, 1-ethyl-3-methylimidazolium / bis (trifluoromethanesulfonyl) imide of [Formulation 1]: 3 parts by mass of the ionic liquid compound (1) was added to N, N, N-trimethyl. -N-butylammonium / chloride ( ^Cl- ): Ionic liquid compound (5) Thickness 0.75 mm, mass 785 g / m ² in the same manner as in Example 1 except that it was replaced with 3 parts by mass [Formulation 8]. Tarpaulin (8) was obtained.

［実施例９－１２］
実施例１のターポリン（１）、実施例２のターポリン（２）、実施例５のターポリン（５）、実施例６のターポリン（６）、各々のターポリンの表面上に、下記〔配合９〕の塗工液を用い、１００メッシュのグラビアロール塗工を行い、１２０℃の熱風炉で２分間加熱乾燥してゾルゲル硬化を完結させ、紫外線（２００ｎｍ～３９９ｎｍ）励起型の光触媒性金属酸化物粒子を担持するラジカル発生層（１）を付帯する、質量７８７ｇ／ｍ^２のターポリン（９－１２）を得た。
〔配合９〕ラジカル発生層用溶液
エチルシリケート（Ｓｉ(ＯＣ_２Ｈ_５)_４：ＳｉＯ_２換算４０質量％）５質量％、及び
[Ｓｉ_５Ｏ_４(ＯＣ_２Ｈ_５)_１２]のテトラエトキシシラン５量体が９５質量％の混合体
２５質量部
加水分解触媒：２％塩酸 １質量部
光触媒性酸化チタンゾル（１次粒子径５ｎｍ：紫外線励起型） ５質量部
水（５０質量％）／エタノール（５０質量％） １００質量部 [Example 9-12]
The tarpaulin (1) of Example 1, the tarpaulin (2) of Example 2, the tarpaulin (5) of Example 5, the tarpaulin (6) of Example 6, and the following [formulation 9] on the surface of each tarpaulin. Using the coating liquid, apply 100 mesh gravure rolls, heat and dry in a hot air furnace at 120 ° C for 2 minutes to complete the sol-gel curing, and obtain ultraviolet (200 nm to 399 nm) -excited photocatalytic metal oxide particles. A tarpaulin (9-12) having a mass of 787 g / m ² was obtained, which was accompanied by the radical generation layer (1) to be carried.
[Formulation 9] Solution for radical generation layer Ethyl silicate (Si (OC ₂ H ₅ ) ₄ : SiO ₂ equivalent 40% by mass) 5% by mass, and
A mixture of 95% by mass of the tetraethoxysilane pentamer of [Si ₅ O ₄ (OC ₂ H ₅ ) ₁₂ ].
25 parts by mass Hydrolysis catalyst: 2% hydrochloric acid 1 part by mass Photocatalytic titanium oxide sol (primary particle diameter 5 nm: ultraviolet excitation type) 5 parts by mass Water (50% by mass) / Ethanol (50% by mass) 100 parts by mass

［実施例１３－１６］
実施例３のターポリン（３）、実施例４のターポリン（４）、実施例７のターポリン（７）、実施例８のターポリン（８）、各々のターポリンの表面上に、下記〔配合１０〕の塗工液を用い、１００メッシュのグラビアロール塗工を行い、１２０℃の熱風炉で２分間加熱乾燥してゾルゲル硬化を完結させ、可視光線（４００ｎｍ～７８０ｎｍ）励起型の光触媒性金属酸化物粒子を担持するラジカル発生層（２）を付帯する、質量７８７ｇ／ｍ^２のターポリン（１３－１６）を得た。
〔配合１０〕ラジカル発生層用溶液
エチルシリケート（Ｓｉ(ＯＣ_２Ｈ_５)_４：ＳｉＯ_２換算４０質量％）５質量％、及び
[Ｓｉ_５Ｏ_４(ＯＣ_２Ｈ_５)_１２]のテトラエトキシシラン５量体が９５質量％の混合体
２５質量部
加水分解触媒：２％塩酸 １質量部
光触媒性酸化タングステンゾル（１次粒子径５ｎｍ：Ｓｉ／Ｎ共ドープ：
Ｆｅイオン助触媒の可視光線励起型） ５質量部
水（５０質量％）／エタノール（５０質量％） １００質量部 [Example 13-16]
The tarpaulin (3) of Example 3, the tarpaulin (4) of Example 4, the tarpaulin (7) of Example 7, the tarpaulin (8) of Example 8, and the following [formulation 10] on the surface of each tarpaulin. 100 mesh gravure roll coating is performed using the coating liquid, and the mixture is heated and dried in a hot air furnace at 120 ° C. for 2 minutes to complete the sol-gel curing. Visible light (400 nm to 780 nm) excitation type photocatalytic metal oxide particles A tarpaulin (13-16) having a mass of 787 g / m ² was obtained, which was accompanied by the radical generation layer (2) carrying the above.
[Formulation 10] Solution for radical generation layer Ethyl silicate (Si (OC ₂ H ₅ ) ₄ : SiO ₂ equivalent 40% by mass) 5% by mass, and
A mixture of 95% by mass of the tetraethoxysilane pentamer of [Si ₅ O ₄ (OC ₂ H ₅ ) ₁₂ ].
25 parts by mass Hydrolysis catalyst: 2% hydrochloric acid 1 part by mass Photocatalytic tungsten oxide sol (primary particle diameter 5 nm: Si / N co-doping:
Visible light excitation type of Fe ion co-catalyst) 5 parts by mass Water (50% by mass) / Ethanol (50% by mass) 100 parts by mass

［実施例１７］
〔配合１〕軟質塩化ビニル樹脂組成物からなる厚さ０．２ｍｍ、質量３１０ｇ／ｍ^２のカレンダー成型フィルム（１）を得た。 [Example 17]
[Formulation 1] A calendar molded film (1) having a thickness of 0.2 mm and a mass of 310 g / m ² made of a soft vinyl chloride resin composition was obtained.

［実施例１８］
〔配合２〕軟質塩化ビニル樹脂組成物からなる厚さ０．２ｍｍ、質量３１０ｇ／ｍ^２のカレンダー成型フィルム（２）を得た。 [Example 18]
[Formulation 2] A calendar molded film (2) having a thickness of 0.2 mm and a mass of 310 g / m ² made of a soft vinyl chloride resin composition was obtained.

［実施例１９］
〔配合３〕軟質塩化ビニル樹脂組成物からなる厚さ０．２ｍｍ、質量３１０ｇ／ｍ^２のカレンダー成型フィルム（３）を得た。 [Example 19]
[Formulation 3] A calendar molded film (3) having a thickness of 0.2 mm and a mass of 310 g / m ² made of a soft vinyl chloride resin composition was obtained.

［実施例２０］
〔配合４〕軟質塩化ビニル樹脂組成物からなる厚さ０．２ｍｍ、質量３１０ｇ／ｍ^２のカレンダー成型フィルム（４）を得た。 [Example 20]
[Formulation 4] A calendar molded film (4) having a thickness of 0.2 mm and a mass of 310 g / m ² made of a soft vinyl chloride resin composition was obtained.

［実施例２１］
〔配合５〕軟質塩化ビニル樹脂組成物からなる厚さ０．２ｍｍ、質量３１０ｇ／ｍ^２のカレンダー成型フィルム（５）を得た。 [Example 21]
[Formulation 5] A calendar molded film (5) having a thickness of 0.2 mm and a mass of 310 g / m ² made of a soft vinyl chloride resin composition was obtained.

［実施例２２］
〔配合６〕軟質塩化ビニル樹脂組成物からなる厚さ０．２ｍｍ、質量３１０ｇ／ｍ^２のカレンダー成型フィルム（６）を得た。 [Example 22]
[Formulation 6] A calendar molded film (6) having a thickness of 0.2 mm and a mass of 310 g / m ² made of a soft vinyl chloride resin composition was obtained.

［実施例２３］
〔配合７〕軟質塩化ビニル樹脂組成物からなる厚さ０．２ｍｍ、質量３１０ｇ／ｍ^２のカレンダー成型フィルム（７）を得た。 [Example 23]
[Formulation 7] A calendar molded film (7) having a thickness of 0.2 mm and a mass of 310 g / m ² made of a soft vinyl chloride resin composition was obtained.

［実施例２４］
〔配合８〕軟質塩化ビニル樹脂組成物からなる厚さ０．２ｍｍ、質量３１０ｇ／ｍ^２のカレンダー成型フィルム（８）を得た。 [Example 24]
[Formulation 8] A calendar molded film (8) having a thickness of 0.2 mm and a mass of 310 g / m ² made of a soft vinyl chloride resin composition was obtained.

［実施例２５－２８］
実施例１７のフィルム（１）、実施例１８のフィルム（２）、実施例２１のフィルム（５）、実施例２２のフィルム（６）、各々のフィルムの表面上に、〔配合９〕の塗工液を用い、１００メッシュのグラビアロール塗工を行い、１２０℃の熱風炉で２分間加熱乾燥してゾルゲル硬化を完結させ、紫外線（２００ｎｍ～３９９ｎｍ）励起型の光触媒性金属酸化物粒子を担持するラジカル発生層（１）を付帯する、質量３１２ｇ／ｍ^２のフィルム（９－１２）を得た。 [Example 25-28]
The film (1) of Example 17, the film (2) of Example 18, the film (5) of Example 21, the film (6) of Example 22, and the coating of [Formulation 9] on the surface of each film. A 100-mesh gravure roll coating is performed using a working solution, and the mixture is heated and dried in a hot air furnace at 120 ° C. for 2 minutes to complete sol-gel curing, and carries ultraviolet (200 nm to 399 nm) -excited photocatalytic metal oxide particles. A film (9-12) having a mass of 312 g / m ² was obtained, which was accompanied by the radical generation layer (1).

［実施例２９－３２］
実施例１９のフィルム（３）、実施例２０のフィルム（４）、実施例２３のフィルム（７）、実施例２４のフィルム（８）、各々のフィルムの表面上に、〔配合１０〕の塗工液を用い、１００メッシュのグラビアロール塗工を行い、１２０℃の熱風炉で２分間加熱乾燥してゾルゲル硬化を完結させ、可視光線（４００ｎｍ～７８０ｎｍ）励起型の光触媒性金属酸化物粒子を担持するラジカル発生層（２）を付帯する、質量３１２ｇ／ｍ^２のフィルム（１３－１６）を得た。 [Example 29-32]
The film (3) of Example 19, the film (4) of Example 20, the film (7) of Example 23, the film (8) of Example 24, and the coating of [Formulation 10] on the surface of each film. A 100-mesh gravure roll coating was performed using the working liquid, and the sol-gel curing was completed by heating and drying in a hot air furnace at 120 ° C. for 2 minutes to obtain visible light (400 nm to 780 nm) -excited photocatalytic metal oxide particles. A film (13-16) having a mass of 312 g / m ² was obtained, which was accompanied by the carrying radical generation layer (2).

［実施例１～８の効果］
イオン液体化合物、及び分子量３９０以上の可塑剤を併用質量比１：２０で含有する軟質塩化ビニル樹脂組成物からなるターポリン１～８は、何れも表面抵抗率１０^９Ω/□程度か、それよりも優れた帯電防止性を有することで、黴、ダニダスト（死骸、糞塵）、花粉などのアレルゲン物質を静電吸着する心配のないもので、さらに抗菌性・防黴性・抗ウイルス性を有し、しかもターポリン同士のブロッキングの心配のない使い勝手のよい態様であった。イオン液体化合物の有機系カチオンが菌・黴の細胞膜のリン脂質のアニオン部位に引き寄せられた後、イオン液体化合物の有機系カチオンのアルキル鎖が細胞膜のリン脂質の疎水部と疎水性相互作用することによって膜に入り込み、カチオン部が細胞膜に蓄積することで菌・黴の細胞膜を破壊し、死滅させた。ウイルスに対しては核酸のＤＮＡ、またはＲＮＡの塩基にイオン液体化合物（カチオン、またはアニオン）が配位して、ＤＮＡ、ＲＮＡの複製を阻害する作用でウイルスの増殖を抑制した。
［実施例９～１６の効果］
ターポリン１，２，５，６に紫外線励起型のラジカル発生層（１）を付帯するターポリン９～１２は、ブラックライト（紫外線）照射によって、照射３０分経過後から抗菌性・防黴性・抗ウイルス性の効果を即効的に発現するなど、ターポリン１～８よりも短時間で抗菌性・防黴性・抗ウイルス性を発現し、しかもこれらの効果をさらに増強した。またターポリン３，４，７，８に可視光線励起型のラジカル発生層（２）を付帯するターポリン１３～１６は、可視光照射によって、照射３０分経過後から抗菌性・防黴性・抗ウイルス性の効果を即効的に発現するなど、ターポリン１～８よりも短時間で抗菌性・防黴性・抗ウイルス性を発現し、しかもこれらの効果をさらに増強した。ラジカル発生層は紫外線励起、または可視光線励起によって、菌・黴の細胞膜へのラジカル酸化攻撃を行って細胞膜を破壊し死滅させ、菌・黴の増殖を抑止した。この作用はイオン液体化合物の作用（実施例１～８：前述の菌・黴の細胞膜を破壊、ウイルスのＤＮＡ、ＲＮＡの複製を阻害）と相乗的となった。ウイルスに対しては核酸のＤＮＡ、またはＲＮＡの二重螺旋をラジカル酸化攻撃して破壊する作用でＤＮＡ、ＲＮＡの複製を阻害してウイルスの増殖を抑制した。この作用はイオン液体化合物の作用（実施例１～８：前述の菌・黴の細胞膜を破壊、ウイルスのＤＮＡ、ＲＮＡの複製を阻害）と相乗的となった。そしてターポリン９～１６は、ラジカル発生層（１）,（２）に含むゾルゲル縮合体の存在によって、ターポリン同士のブロッキング性がターポリン１～８よりも格段優れたものとなった。紫外線励起型、または可視光線励起型のラジカル発生層を片面に付帯するターポリン９～１６は、紫外線及び可視光線の照射の無い環境下における抗菌性・防黴性・抗ウイルス性などの性能は、各々の基材であるターポリン１～８と同等で、夜間、暗闇でも抗菌性・防黴性・抗ウイルス性などの効果発現可能なものであった。
［実施例１７～３２の効果］
カレンダー成型フィルム１～８は、各々ターポリン１～８で用いたフィルムと同一、カレンダー成型フィルム９～１６は、各々ターポリン９～１６で用いたフィルムと同一（紫外線励起型、または可視光線励起型のラジカル活性層付帯）であるため、これらのフィルムの帯電防止効果、抗菌性・防黴性・抗ウイルス性、及びブロッキング防止効果などは、各々ターポリン１～１６と同機構、同等性能である。カレンダー成型フィルム１～１６は、ウイルス感染に対する防御空間構築用、間仕切り構築用などに用いることができ、特に〔配合１〕の軟質塩化ビニル樹脂組成物から、三酸化アンチモン（難燃剤）１０質量部、及びルチル型酸化チタン（白顔料）５質量部を省略した組成物からカレンダー成型された透明フィルムは、ウイルス感染に対する、パーソナル空間構築用、対人カウンターの間仕切り構築用、フェイスガード（シールド）などの用途に適している。 [Effects of Examples 1 to 8]
Tarpaulins 1 to 8 composed of a soft vinyl chloride resin composition containing an ionic liquid compound and a plasticizer having a molecular weight of 390 or more in a combined mass ratio of 1:20 have a surface resistance of about ¹⁰⁹ Ω / □ or more. Also has excellent antistatic properties, so there is no need to worry about electrostatically adsorbing allergen substances such as mold, mite dust (dead body, manure dust), and pollen, and it also has antibacterial, antifungal, and antiviral properties. Moreover, it was an easy-to-use mode without worrying about blocking between tarpaulins. After the organic cation of the ionic liquid compound is attracted to the phospholipid anion site of the cell membrane of the fungus / mold, the alkyl chain of the organic cation of the ionic liquid compound interacts hydrophobically with the hydrophobic part of the phospholipid of the cell membrane. The cation part accumulated in the cell membrane, destroying the cell membrane of the fungus and the mold and killing it. For the virus, an ionic liquid compound (cation or anion) was coordinated with the DNA of the nucleic acid or the base of RNA, and the growth of the virus was suppressed by the action of inhibiting the replication of DNA and RNA.
[Effects of Examples 9 to 16]
Tarpaulins 9 to 12, which are attached to tarpaulins 1, 2, 5, and 6 with an ultraviolet-excited radical generation layer (1), are exposed to black light (ultraviolet rays) to have antibacterial, antibacterial, and antibacterial properties 30 minutes after irradiation. Antibacterial, antibacterial, and antiviral properties were exhibited in a shorter time than tarpaulins 1 to 8, such as immediate viral effects, and these effects were further enhanced. In addition, tarpaulins 13 to 16 in which visible light-excited radical generation layer (2) is attached to tarpaulins 3, 4, 7, and 8 are antibacterial, antibacterial, and antiviral after 30 minutes of irradiation by visible light irradiation. Antibacterial, antibacterial, and antiviral properties were exhibited in a shorter time than tarpaulins 1 to 8, such as immediate expression of sexual effects, and these effects were further enhanced. The radical generation layer was excited by ultraviolet rays or visible light to perform a radical oxidative attack on the cell membrane of fungi and molds to destroy and kill the cell membranes and suppress the growth of fungi and molds. This action was synergistic with the action of the ionic liquid compound (Examples 1 to 8: destroying the cell membranes of the above-mentioned fungi and molds and inhibiting the replication of viral DNA and RNA). For viruses, the replication of DNA and RNA was inhibited by radical oxidative attack to destroy the double helix of nucleic acid DNA or RNA, and the growth of the virus was suppressed. This action was synergistic with the action of the ionic liquid compound (Examples 1 to 8: destroying the cell membranes of the above-mentioned fungi and molds and inhibiting the replication of viral DNA and RNA). The blocking properties of the tarpaulins 9 to 16 were significantly superior to those of the tarpaulins 1 to 8 due to the presence of the sol-gel condensate contained in the radical generation layers (1) and (2). Tarpaulins 9 to 16 having an ultraviolet-excited or visible-light-excited radical generation layer on one side have antibacterial, antibacterial, and antiviral performance in an environment without irradiation with ultraviolet rays and visible light. It was equivalent to tarpaulins 1 to 8 as the respective base materials, and was capable of exhibiting antibacterial, antibacterial, and antiviral effects even at night and in the dark.
[Effects of Examples 17 to 32]
The calender molded films 1 to 8 are the same as the films used for the tarpaulins 1 to 8, and the calender molded films 9 to 16 are the same as the films used for the tarpaulins 9 to 16, respectively (ultraviolet excitation type or visible light excitation type). Since it is accompanied by a radical active layer), these films have the same mechanism and performance as tarpaulins 1 to 16 in terms of antistatic effect, antibacterial property, anticorrosion property, antiviral property, and blocking prevention effect, respectively. The calender molded films 1 to 16 can be used for constructing a protective space against virus infection, for constructing a partition, and in particular, from the soft vinyl chloride resin composition of [Formulation 1], 10 parts by mass of antimony trioxide (flame retardant). , And a transparent film calender-molded from a composition omitting 5 parts by mass of rutile-type titanium oxide (white pigment), for building a personal space against virus infection, for building a partition for an interpersonal counter, a face guard (shield), etc. Suitable for applications.

［比較例１］
実施例１のターポリン（１）において、軟質塩化ビニル樹脂組成物（配合１）の液状エステル化合物（１）３０質量部を、４－シクロヘキセン－１，２－ジカルボン酸ビス（２－エチルヘキシル）３０質量部に置換し、軟質塩化ビニル樹脂組成物中の可塑剤を４－シクロヘキセン－１，２－ジカルボン酸ビス（２－エチルヘキシル）６０質量部とし、分子中にエーテル結合を有する可塑剤を含有しないこと以外は実施例１と同様として、質量７８５ｇ／ｍ^２のターポリン（１７）を得た。得られたターポリンの帯電防止性は実施例１のターポリン（１）よりも劣る７．３×１０¹⁰Ω/□であったが、抗菌性・防黴性は同等であった。 [Comparative Example 1]
In the tarpaulin (1) of Example 1, 30 parts by mass of the liquid ester compound (1) of the soft vinyl chloride resin composition (formulation 1) was added to 30 parts by mass of 4-cyclohexene-1,2-dicarboxylate bis (2-ethylhexyl). The plasticizer in the soft vinyl chloride resin composition shall be 60 parts by mass of 4-cyclohexene-1,2-dicarboxylate bis (2-ethylhexyl), and the plasticizer having an ether bond in the molecule shall not be contained. A tarpaulin (17) having a mass of 785 g / m ² was obtained in the same manner as in Example 1 except for the above. The antistatic property of the obtained tarpaulin was 7.3 × 10 ¹⁰ Ω / □, which was inferior to that of the tarpaulin (1) of Example 1, but the antibacterial and antifungal properties were the same.

［比較例２］
実施例１のターポリン（１）において、軟質塩化ビニル樹脂組成物（配合１）のイオン液体化合物（１）、３質量部を省略した以外は実施例１と同様として質量７８５ｇ／ｍ^２のターポリン（１８）を得た。得られたターポリンの帯電防止性は実施例１のターポリン（１）よりも劣る８．５×１０¹¹Ω/□で、抗菌性・防黴性も劣るものであった。 [Comparative Example 2]
In the tarpaulin (1) of Example 1, the ionic liquid compound (1) of the soft vinyl chloride resin composition (formulation 1) is the same as in Example 1 except that 3 parts by mass is omitted, and the tarpaulin having a mass of 785 g / m ² ( 18) was obtained. The antistatic property of the obtained tarpaulin was 8.5 × 10 ¹¹ Ω / □, which was inferior to that of the tarpaulin (1) of Example 1, and the antibacterial and antifungal properties were also inferior.

［比較例３］
実施例１のターポリン（１）において、軟質塩化ビニル樹脂組成物（配合１）のイオン液体化合物（１）、３質量部を１８質量部に増量した以外は実施例１と同様として質量７８５ｇ／ｍ^２のターポリン（１９）を得た。得られたターポリンの帯電防止性は実施例１のターポリン（１）よりもやや優れた２．２×１０^９Ω/□で、抗菌性・防黴性もやや優れていたが、イオン液体化合物（１）のブリードが顕著となり、ブロッキングを引き起こしていた。 [Comparative Example 3]
In the tarpaulin (1) of Example 1, the mass was 785 g / m as in Example 1 except that the amount of the ionic liquid compound (1) of the soft vinyl chloride resin composition (formulation 1) was increased from 3 parts by mass to 18 parts by mass. ^Two tarpaulins (19) were obtained. The antistatic property of the obtained tarpaulin was 2.2 × 10 ⁹ Ω / □, which was slightly superior to that of the tarpaulin (1) of Example 1, and the antibacterial and antifungal properties were also slightly excellent, but the ionic liquid compound ( The bleeding of 1) became remarkable, causing blocking.

［比較例４］
実施例１のターポリン（１）において、軟質塩化ビニル樹脂組成物（配合１）の４－シクロヘキセン－１，２－ジカルボン酸ビス（２－エチルヘキシル）３０質量部を、フタル酸ジブチル（分子量２７８）３０質量部に変更し、また液状エステル化合物（１）３０質量部を、ｎブタノールにエチレンオキシドを付加したアルコールとアジピン酸との反応によるアジピン酸ジエステル：（エーテル結合２個〔化１〕に相当：分子量３７８の可塑剤）である液状エステル化合物（５）３０質量部に変更した以外は実施例１と同様として質量７８５ｇ／ｍ^２のターポリン（２０）を得た。得られたターポリンの帯電防止性は実施例１のターポリン（１）と同等の６．８×１０^９Ω/□で、抗菌性・防黴性・抗ウイルス性も同等であったが、経時的に可塑剤（フタル酸ジブチル）、及び液状エステル化合物（５）のブリードが顕著となり、ブロッキングを引き起こしていた。 [Comparative Example 4]
In the tarpaulin (1) of Example 1, 30 parts by mass of bis (2-ethylhexyl) 4-cyclohexene-1,2-dicarboxylate (2-ethylhexyl) of the soft vinyl chloride resin composition (Compound 1) was added to 30 parts of dibutyl phthalate (molecular weight 278) 30. The amount of the liquid ester compound (1) was changed to parts by mass, and 30 parts by mass of the liquid ester compound (1) was changed to an adipic acid diester by a reaction between an alcohol obtained by adding ethylene oxide to nbutanol and adipic acid: (corresponding to 2 ether bonds [formation 1]: molecular weight. A tarpaulin (20) having a mass of 785 g / m ² was obtained in the same manner as in Example 1 except that the liquid ester compound (5) was changed to 30 parts by mass. The antistatic property of the obtained tarpaulin was 6.8 × 10 ⁹ Ω / □, which was the same as that of the tarpaulin (1) of Example 1, and the antibacterial, antimicrobial, and antiviral properties were also the same, but over time. The bleeding of the plasticizer (dibutyl phthalate) and the liquid ester compound (5) became prominent and caused blocking.

上記、実施例、及び比較例から明らかな様に、本発明によれば、帯電防止性が安定持続的に発揮され、アレルゲン性（黴、ダニダスト、花粉）物質の静電吸着が抑止可能、かつ抗菌防黴性、抗ウイルス性、抗アレルゲン性（黴、ダニダスト、花粉）を兼備する軟質塩化ビニル樹脂製の膜材で、ブリードによる汚れ、膜材同士が癒着するブロッキング問題を生じることのない膜材が得られるので、これらの膜材は、フィルム、シート、テープの形態、織物、ターポリン、メッシュシート、合成皮革、帆布などの形態で、これらのパーツを熱融着法で縫製し、天井膜、空間仕切り、巻上昇降式シートシャッター、クリーンルームカーテン、壁紙、敷物、カバー、ブラインド、防護衣、フェイスガード、など加工されて、工場、オフィス、学校、商業施設、病院、介護施設、式場、ごみ集積場、公衆トイレ、動物園などに広く使用される。特にターポリン、帆布などは、医療検査用パーティション、空気注入式仮設膜構造による医療検査用陰圧テントシェルターに適して用いることができ、（透明）フィルムはウイルス感染に対する、パーソナル空間構築用、対人カウンターの間仕切り構築用、フェイスガード（シールド）などの用途に適している。
※本発明において、数多くある菌種、黴種、ウイルス種のうちの代表的一部に対しての有効性を確認したことでの、抗菌防黴効果、抗ウイルス効果の応用の可能性を提案するのもで、未知を含めたあらゆる菌種、黴種、ウイルス種に対する有効性を示唆するものではない。 As is clear from the above Examples and Comparative Examples, according to the present invention, the antistatic property is stably and continuously exhibited, the electrostatic adsorption of allergenic (mold, mite dust, pollen) substances can be suppressed, and the electrostatic adsorption is possible. A film made of soft vinyl chloride resin that has antibacterial, antiviral, and anti-allergenic properties (mold, mite dust, pollen), and does not cause stains due to bleeding or blocking problems where the film materials adhere to each other. Since the materials are obtained, these membranes are in the form of films, sheets, tapes, woven fabrics, tarpaulins, mesh sheets, synthetic leathers, canvas, etc., and these parts are sewn by heat fusion method to make ceiling membranes. , Space partition, hoisting lift sheet shutter, clean room curtain, wallpaper, rug, cover, blind, protective clothing, face guard, etc., processed into factories, offices, schools, commercial facilities, hospitals, nursing homes, ceremonies, garbage Widely used in collection areas, public toilets, zoos, etc. In particular, tarpaulins and canvas can be used as suitable for medical examination partitions and negative pressure tent shelters for medical examinations with an inflatable temporary membrane structure, and (transparent) films are used for building personal spaces and interpersonal counters against virus infection. Suitable for partition construction, face guard (shield), etc.
* In the present invention, we propose the possibility of applying antibacterial and antifungal effects and antiviral effects by confirming the effectiveness against a representative part of many fungal species, fungal species, and virus species. However, it does not suggest efficacy against all fungal, fungal, and viral species, including unknown ones.

Claims (6)

少なくともイオン液体化合物、及び分子量３９０以上の可塑剤を含有する軟質塩化ビニル樹脂シートであって、前記イオン液体化合物が、有機系カチオンと、無機系アニオン、及び／または有機系アニオンとの対イオンで形成され、前記有機系カチオンが、イミダゾリウム系、イミダゾリニウム系、ピリジニウム系、ピラゾリウム系、ピロリジニウム系、ピペリジニウム系、アンモニウム系、ホスホニウム系、スルホニウム系、から選ばれた１種以上、かつ前記アニオンが、ＢＦ₄ ^-、ＰＦ₆ ^-、ＴａＦ₆ ^-、ＮｂＦ₆ ^-、ＳｉＦ₆ ^-、ＡｌＦ₄ ^-、ＡｌＣｌ₄ ^-、ＮＯ₂ ^-、ＮＯ₃ ^-、Ｆ^-、Ｃｌ^-、Ｂｒ^-、Ｉ^-、ＣＮ^-、ＡｓＦ₆ ^-、ＳｂＦ₆ ^-、ＮｂＦ₆ ^-、ＴａＦ₆ ^-、ＣＦ₃ＳＯ₂ ^-、（ＣＦ₃ＳＯ₂）₂Ｎ^-、ｐ－ＣＨ₃ＰｈＳＯ₃ ^-、ＣＨ₃ＣＯ₂ ^-、ＣＨ₃ＳＯ₃ ^-、ＣＦ₃ＳＯ₃ ^-、（ＣＦ₃ＳＯ₂）₃Ｃ^-、Ｃ₃Ｆ₇ＣＯ₂ ^-、Ｃ₄Ｆ₉ＳＯ₃ ^-、（Ｃ₂Ｆ₅ＳＯ₂）₂Ｎ^-、（ＣＦ₃ＳＯ₂）（ＣＦ₃ＣＯ）Ｎ^-、（ＣＮ）₂Ｎ^-から選ばれた１種以上、であることを特徴とする帯電防止性抗菌防黴膜材。 A soft vinyl chloride resin sheet containing at least an ionic liquid compound and a plasticizer having a molecular weight of 390 or more, wherein the ionic liquid compound is a counterion of an organic cation and an inorganic anion and / or an organic anion. The organic cation formed is one or more selected from imidazolium-based, imidazolinium-based, pyridinium-based, pyrazolium-based, pyrrolidinium-based, piperidinium-based, ammonium-based, phosphonium-based, and sulfonium-based, and the anion. BF _4- ^, PF _6- ^, TaF _6- ^, NbF _6- ^, SiF _6- ^, AlF _4- ^, AlCl _4- , NO ^{2- ,} NO _3- ^, F- _, ^{Cl- ,} Br- ^, I- ^, CN- ^, AsF _6- ^, SbF _6- ^, NbF _6- ^, TaF _6- , CF ₃ SO ^{2- ,} (CF ₃ SO ₂ ) ₂ N- ^, p-CH _{3 PhSO 3-} ^, CH ₃ CO _2- ^, CH ₃ SO _3- ^, CF ₃ SO _3- ^, (CF ₃ SO ₂ ) ₃ C- ^, C ₃ F ₇ CO _2- ^, C ₄ F ₉ SO _3- ^, (C ₂ F ₅ SO ₂ ) ₂ N- ^, ( An antistatic antibacterial antifungal film material characterized by being one or more selected from CF ₃ SO ₂ ) (CF ₃ CO) N- ^and (CN ⁾ ₂ N-. 前記可塑剤が、〔化１〕、〔化２〕から選ばれた１種以上の液状エステル化合物（アルキル鎖中に１個以上のエーテル結合を有する分子量３９０以上の可塑剤）を３０質量％以上含んでいる請求項１に記載の帯電防止性抗菌防黴膜材。
〔化１〕
Ｒ（ＡＯ）_ｎＯＯＣ－Ｘ－ＣＯＯ（ＡＯ）_ｍＲ
（式中、Ｘは：Ｃ_６Ｈ_４、Ｃ_６Ｈ_８、Ｃ_６Ｈ_１０、Ｃ_２Ｈ_４～Ｃ_８Ｈ_１６、Ｒは：Ｃ_３～１５の直鎖または分岐鎖のアルキル基(Ｒは互いに同一または異なる)、Ａは：Ｃ_２～４のアルキレン基、ｍとｎは１～１０の整数(互いに同一または異なる)で表される化合物）

〔化２〕
Ｒ_１ＣＯ（ＯＣＨ_２ＣＨ-Ｒ_２）_ｎＣＯＯＲ_３
（式中、Ｒ_１及びＲ_３は：Ｃ_３～１５の直鎖または分岐鎖のアルキル基、またはアルケニル基、Ｒ_２は：Ｈ、ＣＨ_３、Ｃ_２Ｈ_５、ｎは３～２０の整数で表される化合物） The plasticizer is 30% by mass or more of one or more liquid ester compounds (plasticizer having one or more ether bonds in the alkyl chain and having a molecular weight of 390 or more) selected from [Chemical formula 1] and [Chemical formula 2]. The antistatic antibacterial anti-mold film material according to claim 1, which is included.
[Chemical 1]
R (AO) _n OOC-X-COO (AO) _m R
(In the formula, X is: C ₆ H ₄ , C ₆ H ₈ , C ₆ H ₁₀ , C ₂ H ₄ to C ₈ H ₁₆ , R is: C _{3 to 15} linear or branched alkyl group (R). Are the same or different from each other), A is: an alkylene group of C2-4, m and n are integers of _1-10 (same or different from each other).

[Chemical 2]
R ₁ CO (OCH ₂ CH-R ₂ ) _n COOR ₃
(In the formula, R ₁ and R ₃ are: C _{3 to 15} linear or branched alkyl or alkenyl groups, R ₂ is: H, CH ₃ , C ₂ H ₅ , n is an integer of 3 to 20. Compound represented by) 前記イオン液体化合物、及び前記可塑剤との併用質量比が、１：１００～１：５である請求項１または２に記載の帯電防止性抗菌防黴膜材。 The antistatic antibacterial antimold film material according to claim 1 or 2, wherein the combined mass ratio of the ionic liquid compound and the plasticizer is 1: 100 to 1: 5. 前記軟質塩化ビニル樹脂シートの一面上に、紫外線（２００ｎｍ～３９９ｎｍ）励起または可視光線（４００ｎｍ～７８０ｎｍ）励起が可能なラジカル発生層が設けられ、このラジカル発生層が、酸化チタン、過酸化チタン、酸化亜鉛、酸化錫、チタン酸ストロンチウム、酸化タングステン、酸化ビスマス、及び酸化鉄、から選ばれた１種以上の光触媒性金属酸化物である請求項１～３の何れか１項に記載の帯電防止性抗菌防黴膜材。 A radical generation layer capable of being excited by ultraviolet rays (200 nm to 399 nm) or visible light (400 nm to 780 nm) is provided on one surface of the soft vinyl chloride resin sheet, and the radical generation layers are titanium oxide, titanium peroxide, and the like. The antistatic agent according to any one of claims 1 to 3, which is one or more photocatalytic metal oxides selected from zinc oxide, tin oxide, strontium titanate, tungsten oxide, bismuth oxide, and iron oxide. Antibacterial and antifungal film material. 前記ラジカル発生層にゾルゲル縮合体を含み、このゾルゲル縮合体が、シラノール基含有有機シラン化合物のゾルゲル縮合、またはチタノール基含有有機チタン化合物のゾルゲル縮合によって形成されたもので、前記光触媒性金属酸化物を担持している請求項４に記載の帯電防止性抗菌防黴膜材。 The radical generation layer contains a sol-gel condensate, and the sol-gel condensate is formed by sol-gel condensation of a silanol group-containing organic silane compound or sol-gel condensation of a titanol group-containing organic titanium compound, and is the photocatalytic metal oxide. The antistatic antibacterial antifungal film material according to claim 4, which carries the above-mentioned. 前記軟質塩化ビニル樹脂シートが織物を芯材として含み、この織物が、１）経糸及び緯糸からなる織物、または２）経糸及び左上バイアス糸／右上バイアス糸からなる三軸織物、または３）経糸、緯糸及び左上バイアス糸／右上バイアス糸からなる四軸織物、の何れかである請求項１~５の何れか１項に記載の帯電防止性抗菌防黴膜材。 The soft vinyl chloride resin sheet contains a woven fabric as a core material, and the woven fabric is 1) a woven fabric consisting of warps and wefts, or 2) a triaxial woven fabric consisting of warps and upper left bias yarns / upper right bias yarns, or 3) warps. The antistatic antibacterial antimold film material according to any one of claims 1 to 5, which is a woven fabric composed of a warp and an upper left bias yarn / an upper right bias yarn.