JP2021096964A - インターコネクタ部材、および、インターコネクタ部材の製造方法 - Google Patents
インターコネクタ部材、および、インターコネクタ部材の製造方法 Download PDFInfo
- Publication number
- JP2021096964A JP2021096964A JP2019227820A JP2019227820A JP2021096964A JP 2021096964 A JP2021096964 A JP 2021096964A JP 2019227820 A JP2019227820 A JP 2019227820A JP 2019227820 A JP2019227820 A JP 2019227820A JP 2021096964 A JP2021096964 A JP 2021096964A
- Authority
- JP
- Japan
- Prior art keywords
- coating layer
- interconnector
- layer
- metal member
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
A−1.燃料電池スタック100の構成:
(燃料電池スタック100の構成)
図1は、本実施形態における燃料電池スタック100の外観構成を示す斜視図であり、図2は、図1(および後述する図6,7)のII−IIの位置における燃料電池スタック100のXZ断面構成を示す説明図であり、図3は、図1(および後述する図6,7)のIII−IIIの位置における燃料電池スタック100のYZ断面構成を示す説明図である。各図には、方向を特定するための互いに直交するXYZ軸が示されている。本明細書では、便宜的に、Z軸正方向を上方向と呼び、Z軸負方向を下方向と呼ぶものとするが、燃料電池スタック100は実際にはそのような向きとは異なる向きで設置されてもよい。図4以降についても同様である。
一対のエンドプレート104,106は、略矩形の平板形状の導電性部材であり、例えばステンレスにより形成されている。一方のエンドプレート104は、最も上に位置する発電単位102の上側に配置され、他方のエンドプレート106は、最も下に位置する発電単位102の下側に配置されている。一対のエンドプレート104,106によって複数の発電単位102が押圧された状態で挟持されている。上側のエンドプレート104は、燃料電池スタック100のプラス側の出力端子として機能し、下側のエンドプレート106は、燃料電池スタック100のマイナス側の出力端子として機能する。
図4は、図2に示す断面と同一の位置における互いに隣接する2つの発電単位102のXZ断面構成を示す説明図であり、図5は、図3に示す断面と同一の位置における互いに隣接する2つの発電単位102のYZ断面構成を示す説明図である。図5の上部には、発電単位102の一部分のYZ断面構成が拡大して示されている。また、図6は、図4のVI−VIの位置における発電単位102のXY断面構成を示す説明図であり、図7は、図4のVII−VIIの位置における発電単位102のXY断面構成を示す説明図である。
図2および図4に示すように、酸化剤ガス導入マニホールド161の位置に設けられたガス通路部材27の分岐部29に接続されたガス配管(図示せず)を介して酸化剤ガスOGが供給されると、酸化剤ガスOGは、ガス通路部材27の分岐部29および本体部28の孔を介して酸化剤ガス導入マニホールド161に供給され、酸化剤ガス導入マニホールド161から各発電単位102の酸化剤ガス供給連通孔132を介して、空気室166に供給される。また、図3および図5に示すように、燃料ガス導入マニホールド171の位置に設けられたガス通路部材27の分岐部29に接続されたガス配管(図示せず)を介して燃料ガスFGが供給されると、燃料ガスFGは、ガス通路部材27の分岐部29および本体部28の孔を介して燃料ガス導入マニホールド171に供給され、燃料ガス導入マニホールド171から各発電単位102の燃料ガス供給連通孔142を介して、燃料室176に供給される。
図8は、本実施形態におけるインターコネクタ複合体200(の空気極側集電体134されている部分)の詳細構成を示す説明図である。図8には、図5のX1部の断面構成が拡大して示されている。図9は、本実施形態におけるインターコネクタ複合体200(のうち、空気極側集電体134が形成されていない部分)の詳細構成を示す説明図である。図8には、図5のX2部の断面構成が拡大して示されている。上述したように、インターコネクタ複合体200は、金属部材190(空気極側集電体134とインターコネクタ150との一体部材)と、金属部材190の表面上に配置された酸化被膜層194と、酸化被膜層194における金属部材190とは反対側の表面上に配置されたMn−Co被膜層196とを備える。
次に、インターコネクタ複合体200の製造方法について説明する。図10は、本実施形態におけるインターコネクタ複合体200の製造方法の一例を示すフローチャートである。また、図11および図12は、本実施形態におけるインターコネクタ複合体200の製造方法の一例を概略的に示す説明図である。
以上説明したように、本実施形態におけるインターコネクタ複合体200は、FeとCrとを含有する金属部材190と、金属部材190におけるZ軸負方向側(Z軸方向の一方側)に配置され、Cr酸化物を含有する酸化被膜層194と、酸化被膜層194におけるZ軸負方向側に配置され、MnとCoとを含有するスピネル型の酸化物を含有するMn−Co被膜層196とを備えている。Mn−Co被膜層196におけるMnの濃度(atm%)とCoの濃度(atm%)との比は、1:1〜2である。Z軸方向に平行な任意の断面(例えば、図8に示す断面、および図9に示す断面)において、Mn−Co被膜層196の外側部分197(Mn−Co被膜層196におけるZ軸負方向側の部分)における気孔率S1(%)は、内側部分198(Mn−Co被膜層196のうちの外側部分197と酸化被膜層194との間に位置する部分)における気孔率S2(%)よりも大きい。
インターコネクタ複合体200のサンプルを作製し、該サンプルを用いて性能評価を行った。図13は、本実施形態における性能評価結果を示す説明図である。なお、図13の「気孔率の勾配」とは、外側部分197における気孔率S1(%)が内側部分198における気孔率S2(%)よりも大きいことを意味し、「外側部分197におけるMnの物質量の割合」とは、外側部分197に存在する酸素元素を除いた残りの元素の物質量に対するMnの物質量の割合を意味する。
図13に示すように、本性能評価には、4つのサンプル(サンプルSp1、Sp2、Sp3)を用いた。
大気雰囲気で、室温および900℃の各温度における1時間の保持について、100℃/時間の昇温速度及び100℃/時間の降温速度で、繰り返し熱サイクル試験を10回行った。その後、上記の各サンプル(サンプルSp1、Sp2、Sp3)に対して900℃大気中において、一定の電流(例えば、0.5A/cm2)を流し、電気抵抗(接触抵抗)(Ωcm2)を測定した。10回の熱サイクル試験後の900℃大気雰囲気における電気抵抗値が小さいほど、高い評価である(Mn−Co被膜層196の剥離が抑制された)と判定した。具体的には、電気抵抗値が2.0Ωcm2以下であれば「◎」、電気抵抗値が2.0Ωcm2より大きく、かつ3.0Ωcm2以下であれば「○」、電気抵抗値の上昇値が3.0Ωcm2より大きければ「×」と判定した。「◎」か「○」である場合は「合格」と判定し、「×」である場合は「不合格」と判定した。
本明細書で開示される技術は、上述の実施形態に限られるものではなく、その要旨を逸脱しない範囲において種々の形態に変形することができ、例えば次のような変形も可能である。
Claims (5)
- FeとCrとを含有する金属部材と、
前記金属部材における第1の方向の一方側に配置され、Cr酸化物を含有する第1の被膜層と、
前記第1の被膜層における前記一方側に配置され、MnとCoとを含有するスピネル型の酸化物を含有する第2の被膜層と、を備えるインターコネクタ部材であって、
前記第2の被膜層におけるMnの濃度(atm%)とCoの濃度(atm%)との比は、1:1〜2であり、
前記第2の被膜層における前記一方側の部分を外側部分とし、前記第2の被膜層のうちの前記外側部分と前記第1の被膜層との間に位置する部分を内側部分としたとき、
前記第1の方向に平行な少なくとも1つの断面において、前記外側部分における気孔率S1(%)は、前記内側部分における気孔率S2(%)よりも大きい、
ことを特徴とするインターコネクタ部材。 - 請求項1に記載のインターコネクタ部材であって、
前記第2の被膜層の前記外側部分に存在する酸素元素を除いた残りの元素の物質量に対するMnの物質量の割合は、60(atm%)以上である、
ことを特徴とするインターコネクタ部材。 - 請求項1または請求項2に記載のインターコネクタ部材において、
前記インターコネクタ部材は、電解質層と前記電解質層を挟んで前記第1の方向に互いに対向する空気極および燃料極とを含み、前記空気極および前記燃料極の少なくとも一方である特定電極の表面に面するガス室が形成された電気化学反応単セルを備える複数の電気化学反応単位を備える電気化学反応セルスタックにおいて、前記金属部材に、前記第1の方向の前記一方に突出する複数の凸部が形成され、前記複数の凸部が前記第1の被膜層および前記第2の被膜層によって覆われており、前記複数の凸部が前記特定電極に接続されることにより前記特定電極に電気的に接続される導電性部材であり、
前記第1の方向における前記一方とは反対の方向を他方とし、前記第1の方向に直交する方向を第2の方向とし、前記第2の被膜層のうち、前記第1の方向における前記金属部材の前記一方側の先端を通る前記第2の方向の仮想直線よりも前記一方に位置する部分を第1の部分とし、前記仮想直線よりも前記他方に位置し、少なくとも一部が前記ガス室に面する部分を第2の部分としたとき、
前記第2の被膜層の前記第1の部分の気孔率Saは、前記第2の被膜層の前記第2の部分の気孔率Sbよりも少ない、
ことを特徴とするインターコネクタ部材。 - 請求項1から請求項3までのいずれか1項に記載のインターコネクタ部材の製造方法であって、
前記金属部材を準備する第1の工程と、
前記金属部材に、泳動電析によりMn酸化物層を形成する第2の工程と、
前記Mn酸化物層に、メッキによりCoを含有するCoメッキ層を形成する第3の工程と、
前記第1の工程、前記第2の工程、および前記第3の工程を経た前記金属部材を焼成することにより、前記金属部材に前記第1の被膜層および前記第2の被膜層を形成する第4の工程と、を備える、
ことを特徴とするインターコネクタ部材の製造方法。 - 請求項4に記載のインターコネクタ部材の製造方法であって、
前記第2の工程において、前記金属部材を浸す溶剤として、ケトン類の溶剤を用いる、
ことを特徴とするインターコネクタ部材の製造方法。