JP2020200371A - ハロゲン含有ポリマーとその製造法 - Google Patents
ハロゲン含有ポリマーとその製造法 Download PDFInfo
- Publication number
- JP2020200371A JP2020200371A JP2019106798A JP2019106798A JP2020200371A JP 2020200371 A JP2020200371 A JP 2020200371A JP 2019106798 A JP2019106798 A JP 2019106798A JP 2019106798 A JP2019106798 A JP 2019106798A JP 2020200371 A JP2020200371 A JP 2020200371A
- Authority
- JP
- Japan
- Prior art keywords
- halogen
- containing polymer
- general formula
- formula
- alkali metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
[1] 下記一般式(1m)で示される繰り返し単位を少なくとも1つ以上有するハロゲン含有ポリマーであって、アルカリ金属イオン含有量が0.1〜300ppmであるハロゲン含有ポリマー。
[2] アルカリ金属イオン含有量が0.5〜200ppmである、[1]に記載のハロゲン含有ポリマー。
[3] 標準ポリスチレン換算における重量平均分子量が7,500以上である、[1]又は[2]に記載のハロゲン含有ポリマー。
[4] 下記一般式(1m)
で示される繰り返し単位を少なくとも1つ以上有するハロゲン含有ポリマーを酸で洗浄することを特徴とする[1]に記載のハロゲン含有ポリマーの製造法。
[5] 下記一般式(2)で示される化合物
と、一般式(3)で示される化合物
を反応させて下記一般式(1m)
で示される繰り返し単位を少なくとも1つ以上有するハロゲン含有ポリマーを得、次いで、当該ハロゲン含有ポリマーを酸で洗浄することを特徴とする[1]に記載のハロゲン含有ポリマーの製造法。
で示されるハロゲン含有ポリマーを好ましい例として挙げることができる。
で示される繰り返し単位を1つ以有するハロゲン含有ポリマーを酸で洗浄することを特徴とする。
と、一般式(3)で示される化合物
を反応させて下記一般式(1m)
で示される繰り返し単位を1つ以上有するハロゲン含有ポリマーを得、次いで、当該ハロゲン含有ポリマーを酸で洗浄するものであることが好ましい。
8Lのガラス製ナス型フラスコに、テトラブロモビスフェノールA 550g(1.01mol)、炭酸水素ナトリウム 200g(2.38mol)、二塩化エタン800g(8.08mol)、ジメチルホルムアミド 3.1Lを、この順序にて室温中加えてから混合下に90℃まで昇温させた。同温にて3時間撹拌後、130℃まで昇温させ、未反応の二塩化エタンを留去した。次いで、室温まで放冷させた後、テトラブロモビスフェノールA 550g(1.01mol)、炭酸水素ナトリウム 170g(2.02mol)、ジメチルホルムアミド 3.1Lを加えた。その後、130℃にて17時間撹拌後、室温まで放冷させた。水を加えた後、析出した固体をろ過し、水で洗浄した。
合成例1で得られた固体をpH3の塩酸水溶液中で20分撹拌後、再度固体をろ過し、水で洗浄し、さらに乾燥させて、重量平均分子量10,000の白色固体(ポリマー)を収率98%で得た。このポリマーを以下、ハロゲン含有ポリマー(B−1)と記す。このハロゲン含有ポリマー(B−1)を硫酸および硝酸にて湿式分解後、ICP−AESにてナトリウムイオン量を定量したところ、90ppmであった。
合成例1で得られた固体を乾燥させて、重量平均分子量10,000の白色固体(ポリマー)を収率97%で得た。このポリマーを以下、ハロゲン含有ポリマー(B−2)と記す。このハロゲン含有ポリマー(B−2)を硫酸および硝酸にて湿式分解後、ICP−AESにてナトリウムイオン量を定量したところ、2,000ppmであった。
<難燃性および耐トラッキング性の測定>
以下、難燃性および耐電気特性の測定に用いた材料を以下に示す。
<ポリアミド樹脂(A)>
ポリアミド66:東レ(株)製、(商標名)アミラン。
<難燃剤>
難燃剤B−1:上記のハロゲン含有ポリマー(B−1)。
<無機強化剤(C)>
ガラス繊維:日東紡(株)製チョップドストランド、(商標名)CSF3PE−455S。
<アンチモン系難燃助剤(D)>
三酸化アンチモン:(株)鈴裕化学製、(商標名)AT3CN。
<滴下防止剤(E)>
ポリテトラフルオロエチレン:三菱ケミカル(株)製、(商標名)メタンブレン。
まず、コンパウンディングによってポリアミド樹脂組成物を調製した。この目的のために、表1に記載の個々の成分(難燃剤(B−1)、ポリアミド6,6、ガラス繊維、三酸化アンチモン、及びテトラフルオロエチレン)を、二軸押出機(ZSK−26、Coperion製)の中で230〜325の温度で混合し、ポリアミド樹脂組成物をストランドとして排出し、次いでペレット化した。得られたポリアミド樹脂組成物のペレットを270〜330℃の温度で成形加工して、難燃性試験および耐トラッキング性試験のための標準試験片を作成した。
難燃剤(B−1)の代わりに難燃剤(B−2)を用いた以外は、実施例1と同様の操作を行って難燃性を評価した。結果を表1に示した。
難燃剤(B−1)の代わりに難燃剤(B−3)を用いた以外は、実施例1と同様の操作を行って難燃性を評価した。結果を表1に示した。
Claims (5)
- 下記一般式(1m)で示される繰り返し単位を少なくとも1つ以上有するハロゲン含有ポリマーであって、アルカリ金属イオン含有量が0.1〜300ppmであるハロゲン含有ポリマー。
- アルカリ金属イオン含有量が0.5〜200ppmである、請求項1に記載のハロゲン含有ポリマー。
- 標準ポリスチレン換算における重量平均分子量が7,500以上である、請求項1又は2に記載のハロゲン含有ポリマー。
- 下記一般式(1m)
で示される繰り返し単位を少なくとも1つ以上有するハロゲン含有ポリマーを酸で洗浄することを特徴とする請求項1に記載のハロゲン含有ポリマーの製造法。 - 下記一般式(2)で示される化合物
と、一般式(3)で示される化合物
を反応させて下記一般式(1m)
で示される繰り返し単位を少なくとも1つ以上有するハロゲン含有ポリマーを得、次いで、当該ハロゲン含有ポリマーを酸で洗浄することを特徴とする請求項1に記載のハロゲン含有ポリマーの製造法。