JP2019099876A - 金属粉末分散剤および金属粉末スラリー - Google Patents
金属粉末分散剤および金属粉末スラリー Download PDFInfo
- Publication number
- JP2019099876A JP2019099876A JP2017233057A JP2017233057A JP2019099876A JP 2019099876 A JP2019099876 A JP 2019099876A JP 2017233057 A JP2017233057 A JP 2017233057A JP 2017233057 A JP2017233057 A JP 2017233057A JP 2019099876 A JP2019099876 A JP 2019099876A
- Authority
- JP
- Japan
- Prior art keywords
- metal powder
- slurry
- dispersant
- metal
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
(1) 炭素数12以上、24以下のアシル基を有するN−アシルメチルアラニンからなることを特徴とする、金属粉末分散剤。
本発明に用いる金属粉末分散剤は、未中和の界面活性剤である、炭素数12以上、24以下の不飽和脂肪酸由来のアシル基を有するN−アシルメチルアラニンである。
金属粉末を構成する金属としては、導電性に優れたものが好ましいが、10族あるいは11族の金属が特に好ましい。具体的にはニッケル、銅等が特に好ましい。また金属は一種でもよく、また二種類以上の金属粉末を併用してもよい。
本発明に用いる有機溶媒は、インキ、塗料や導電性ペースト等の分野で用いられている溶剤を用いることができる。例えば、トルエンやキシレンなどの芳香族炭化水素系溶媒:シクロヘキサンなどの炭化水素系溶媒:アセトン、メチルエチルケトン、メチルイソブチルケトン、およびシクロヘキサノンなどのケトン系溶媒:酢酸エチル、酢酸n−プロピル、酢酸イソプロピル、酢酸n−ブチル、およびγ−ブチロラクトンなどのエステル系溶媒:エチレングリコールモノエチルエーテル、エチレングリコールモノイソプロピルエーテル、エチレングリコールモノブチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノn − ブチルエーテル、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、プロピレングリコールモノn−プロピルエーテル、プロピレングリコールモノn−ブチルエーテル、ジプロピレングリコールモノメチルエーテル、ジプロピレングリコールモノエチルエーテル、ジプロピレングリコールモノn−プロピルエーテル、およびジプロピレングリコールモノn−ブチルエーテルなどのグリコールエーテル系溶媒:エチレングリコールモノエチルエーテルアセテート、エチレングリコールモノイソプロピルエーテルアセテート、エチレングリコールモノブチルエーテルアセテート、ジエチレングリコールモノエチルエーテルアセテート、ジエチレングリコールモノn−ブチルエーテルアセテート、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート、プロピレングリコールモノn−プロピルエーテルアセテート、プロピレングリコールモノn−ブチルエーテルアセテート、ジプロピレングリコールモノメチルエーテルアセテート、ジプロピレングリコールモノエチルエーテルアセテート、ジプロピレングリコールモノn−プロピルエーテルアセテート、およびジプロピレングリコールモノn−ブチルエーテルアセテートなどのグリコールエーテルエステル系溶媒:ターピネオール、ジヒドロターピネオール、ターピニルアセテート、およびジヒドロターピニルアセテートなどのテルペン系溶媒:メタノール、エタノール、n−プロパノール、イソプロパノール、n−ブタノール、イソブタノール、およびt−ブタノールなどのアルコール系溶媒が挙げられる。これらの溶剤のうち、テルペン系溶媒及びアルコール系溶媒が好ましく、テルペン系溶媒がより好ましく、ターピネオールが特に好ましい。これらの溶剤は1種単独で用いてもよく、2種以上を併用してもよい。
まず、有機溶媒に金属粉末分散剤としてN−オレオイル−N−メチルアラニンを、金属粉末100質量部に対して、表1に示す所定量添加して溶解させた。前記の溶解液に金属粉末を所定量添加して、自転・公転ミキサー等を用いた分散処理を所定時間実施することで、スラリーを作製した。
つぎに、25℃におけるスラリーのせん断粘度(せん断速度:1、10、100(1/s))をレオメーター(アントンパール社製MCR301)により測定し、初期の分散性がオレオイルサルコシンと同等であることを確認した。
分散剤として、N−オレオイル−N−メチルアラニンの代わりにオレオイルサルコシンを選択し、実施例1と同配合比率、同方法にてスラリーを作製した。
分散剤として、N−オレオイル−N−メチルアラニンの代わりにオレオイルサルコシンを選択し、実施例2と同配合比率、同方法にてスラリーを作製した。
分散剤として、N−オレオイル−N−メチルアラニンの代わりにオレオイルサルコシンを選択し、実施例3と同配合比率、同方法にてスラリーを作製した。
分散剤として、N−オレオイル−N−メチルアラニンの代わりにオレオイルサルコシンを選択し、実施例4と同配合比率、同方法にてスラリーを作製した。
スラリー作成後、常温で18時間経過したものについて、下記に示す条件で後方散乱光強度を測定し、分散液の経時安定性を評価した。表1に各例のスラリーの組成を示し、表2に分散液の経時安定性の評価結果を示す。
・ 測定装置:溶液安定性評価装置(英弘精機(株)製 タービスキャンMA2000型)
・ 測定波長:850nm
・ 試料質量:15g
◎: 初期値と比較して後方散乱光強度の変化率が1%未満
○: 初期値と比較して後方散乱光強度の変化率が1%以上、
10%未満
△: 初期値と比較して後方散乱光強度の変化率が10%以上、
15%未満
×: 初期値と比較して後方散乱光強度の変化率が15%以上
(測定条件)
・ 測定装置:示差熱熱重量同時測定装置((株)日立ハイテクサイエンス製 STA 7200型)
・ 窒素流量:75mL/min
・ 温度範囲:30℃〜350℃
・ 昇温速度:10℃/min、
・ 試料質量:約10mg
すなわち、表2および表3の結果より、オレオイルサルコシンよりもN−オレオイル−N−メチルアラニンの方が、幅広い金属含有量において良好な分散安定性を有し、かつ良好な熱分解性を有するという結果が得られた。
Claims (2)
- 炭素数12以上、24以下のアシル基を有するN−アシルメチルアラニンからなることを特徴とする、金属粉末分散剤。
- 金属粉末、請求項1記載の金属粉末分散剤および有機溶媒を含有する金属粉末スラリーであって、前記金属粉末の含有量が30〜80質量%であり、前記金属粉末100質量部に対して前記金属粉末分散剤を0.2〜2.0質量部含有することを特徴とする、金属粉末スラリー。