JP2018193620A - 表面調整剤、並びに、皮膜付きマグネシウム材又はマグネシウム合金材、及びそれらの製造方法 - Google Patents
表面調整剤、並びに、皮膜付きマグネシウム材又はマグネシウム合金材、及びそれらの製造方法 Download PDFInfo
- Publication number
- JP2018193620A JP2018193620A JP2018173277A JP2018173277A JP2018193620A JP 2018193620 A JP2018193620 A JP 2018193620A JP 2018173277 A JP2018173277 A JP 2018173277A JP 2018173277 A JP2018173277 A JP 2018173277A JP 2018193620 A JP2018193620 A JP 2018193620A
- Authority
- JP
- Japan
- Prior art keywords
- magnesium
- dicalcium phosphate
- film
- less
- magnesium alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
また、特許文献2には、所定のエッチング処理を施した、アルミニウム含有量が7.5質量%以下であるマグネシウム合金の表面を、カルシウムイオン、マンガンイオン及びリン酸イオンを含有する溶液を用いて化成処理する工程を含む、マグネシウム合金の化成処理皮膜の形成方法が開示されている。
本発明は上記課題を解決するものであり、マグネシウム含有金属材に対して、優れた密着性及び耐食性を有する化成皮膜を形成することを可能とする技術及びその技術の利用を提供するものである。
(1)第二リン酸カルシウム粒子を含有し、
前記第二リン酸カルシウム粒子のD50が0.1μm以上0.8μm以下であり、
前記第二リン酸カルシウムがモネタイト及び/又はブルシャイトである、表面調整剤;(2)マグネシウム材又はマグネシウム合金材に、上記(1)に記載の表面調整剤を接触させる工程と、
前記表面調整剤を接触させたマグネシウム材又はマグネシウム合金材に、リン酸イオン及びカルシウムイオンを含む表面処理剤を接触させる工程と、
を含む、皮膜付きマグネシウム材又はマグネシウム合金材の製造方法;
(3)マグネシウム材又はマグネシウム合金材の表面上に、第二リン酸カルシウムの結晶性粒子を含有する皮膜を有し、
前記第二リン酸カルシウムの結晶性粒子の平均粒子径が0.7μm以上25μm以下であり、かつ、粒度分布の標準偏差が5以下であり、
前記第二リン酸カルシウムがモネタイト及び/又はブルシャイトである、皮膜付きマグネシウム材又はマグネシウム合金材;
などである。
本発明の実施形態に係る表面調整剤は、マグネシウム含有金属材に対してリン酸カルシウムを含む化成皮膜を効率よく形成させるための前処理剤である。表面調整剤は、特定の粒子径を有する第二リン酸カルシウム粒子を含有する。このような表面調整剤を用いて、リン酸イオンとカルシウムイオンを含む表面処理剤による化成処理前に、表面調整処理を行うことで、優れた密着性及び耐食性を有する上記化成皮膜を形成することができる。
本実施形態に係る表面調整剤は、本発明の効果を奏する限り、第二リン酸カルシウム粒子以外の成分を含んでいてもよいが、溶媒及び第二リン酸カルシウム粒子のみからなるものであってもよい。
第二リン酸カルシウムは、リン酸一水素カルシウムとも呼ばれる。第二リン酸カルシウムには、無水和物(CaHPO4)と二水和物(CaHPO4・2H2O)が存在し、無水和物はモネタイト、二水和物はブルシャイトとそれぞれ呼ばれている。
本実施形態に係る表面調整剤は、モネタイト又はブルシャイトの少なくとも一方を含んでいればよく、双方を含んでいてもよい。また、双方を含む場合において、その含有比率は特に限定されるものではない。
また、第二リン酸カルシウムは市販のものを用いてもよく、リン酸原料とカルシウム原料から製造してもよい。第二リン酸カルシウムの製造方法は、例えば、リン酸水溶液に炭酸カルシウムや水酸化カルシウムなどのカルシウム原料を反応させ、pHを4〜5に調整することで得ることができる。この際、反応温度を少なくとも80℃以上とすることでモネタイトが得られ、反応温度を少なくとも60℃以下とすることでブルシャイトが得られ
る。なお、80℃未満であってもモネタイトが得られることがあり、60℃より高くてもブルシャイトが得られることがある。
また、第二リン酸カルシウム粒子は、そのD90が通常0.15μm以上であり、0.2μm以上であってもよく、0.3μm以上であってもよい。また上限は通常1.5μm以下であり、1.2μm以下であってもよく、1.0μm以下であってもよい。D90がこの範囲内である第二リン酸カルシウム粒子を含有する表面調整剤を用いて表面調整処理を行うことにより、その後の上記化成処理を行うことにより均一性が高い皮膜を形成することができる。
分散剤としては、例えば、単糖類若しくは多糖類又はそれらの誘導体;正りん酸、ポリりん酸若しくはその塩、又は有機ホスホン酸化合物若しくはその塩;酢酸ビニルの重合体若しくはその誘導体又は酢酸ビニルと共重合可能な単量体と酢酸ビニルとの共重合体からなる水溶性高分子化合物;式:H2C=C(R1)−COOR2(式中R1はHまたはCH3、R2はH、Cが1〜5のアルキル基またはCが1〜5のヒドロキシアルキル基)に示される単量体もしくはα,β不飽和カルボン酸単量体の中から選ばれる少なくとも1種以上と、該単量体と共重合可能な単量体50重量%以下とを重合して得られる重合体又は共重合体;等を挙げることができる。
た、前記単量体の何種類かを組み合わせて重合して得られた共重合体を使用してもよい。
溶媒としては、第二リン酸カルシウムを好適に分散できる限り特に限定されないが、通常水が用いられる。水に対し有機溶媒を加えてもよいが、その場合、溶媒全量に対する有機溶媒の含有量は通常10重量%以下であり、5重量%以下であってもよく、3重量%以下であってもよい。
有機溶媒の種類は特に限定されず、アルコール系の有機溶媒、炭化水素系の有機溶媒、ケトン系の有機溶媒、アミド系の有機溶媒などがあげられる。
表面調整剤は、必要に応じて増粘剤、分散安定性向上剤、pH調整剤などを含んでいてもよい。
増粘剤は、表面調整剤における第二リン酸カルシウム粒子の分散性を確保し、第二リン酸カルシウム粒子の沈降によるケーキングを防止することができる。増粘剤の種類は特に制限されるものではなく、例えば、タンパク質類、天然ゴム類、糖類(糖誘導体を含む)、アルギン酸類、セルロース類などの天然高分子;アミン系樹脂、カルボン酸系樹脂、オレフィン系樹脂、エステル系樹脂、ウレタン系樹脂、PVA、アクリル(メタクリル)系樹脂等、又はこれらの樹脂のうち2種以上を組み合わせて共重合させた共重合体等の合成高分子;ノニオン系界面活性剤、カチオン系界面活性剤、アニオン系界面活性剤、両性界面活性剤などの各種界面活性剤;シランカップリング剤、チタンカップリング剤などの各種カップリング剤;などが例示される。
表面調整剤のpHは通常6以上、11以下に調整される。下限は7以上であってもよく、上限は10以下であってもよく、9以下であってもよい。ここで、本明細書におけるpHは、25℃の表面調整剤を市販のpHメーターにて測定した値を示す。
本実施形態に係る表面調整剤は、例えば、溶媒に第二リン酸カルシウム粒子と、必要に応じて分散剤とを混合した混合物のpHをpH調整剤で所定のpHに調整し、続いて、p
H調整した混合物を湿式粉砕した後、撹拌して第二リン酸カルシウム粒子を分散させることで製造することができる。その他、溶媒に、所定粒径に予め調整された第二リン酸カルシウム粒子と、必要に応じて分散剤とを混合した混合物のpHを、pH調整剤で所定のpHに調整することで製造することができる。なお、上述においては、湿式粉砕する前に分散剤とpH調整剤を予め第二リン酸カルシウム粒子と混合しているが、いずれか一方を湿式粉砕する前に第二リン酸カルシウム粒子と混合し、湿式粉砕した後に他方を第二リン酸カルシウム粒子と混合してもよい。また、湿式粉砕した後に分散剤とpH調整剤を第二リン酸カルシウム粒子と混合してもよい。
溶媒への原料の添加の順序は特段限定されるものではなく、第二リン酸カルシウム、分散剤及びpH調整剤を一度に添加してもよく、分散剤のみ添加した溶媒に第二リン酸カルシウムを添加し、必要に応じてpH調整剤を添加してもよい。
本発明の別の実施形態は、皮膜付きマグネシウム含有金属材であり、該皮膜は化成皮膜である。この化成皮膜は、第二リン酸カルシウムの結晶性粒子を有する。化成皮膜を有するマグネシウム含有金属材の製造方法は、マグネシウム含有金属材の表面に上記表面調整剤を接触させる第1の接触工程と、表面処理剤を接触させたマグネシウム含有金属材に、リン酸イオン及びカルシウムイオンを含む表面処理剤を接触させる第2の接触工程とを含む。なお、第1の接触工程は、以下、表面調整処理工程という。また、第2の接触工程は、以下、化成処理工程という。
上記化成処理工程の前に表面調整処理工程を行うことで、優れた密着性及び耐食性を有する化成皮膜を、マグネシウム含有金属材の表面に形成することが可能となる。なお、表面調整処理工程前に、マグネシウム含有金属材の表面に対して、脱脂、酸洗、エッチング、スマット除去、ペーパー研磨等の前処理工程を行ってもよい。これらの前処理工程により、マグネシウム含有金属材が有する酸化膜、マグネシウム含有金属材に付着している油分や汚れ等を除去し、表面を清浄化することができる。これらの前処理工程後に、溶剤洗浄、水蒸気処理(「水熱処理」、「水酸化マグネシウム皮膜形成処理」等とも称する。)等の処理も行ってよい。これらの処理により、マグネシウム含有金属材と化成皮膜との密着性を向上し、優れた耐食性を有する皮膜付きマグネシウム含有金属材を得ることができる。なお、上記水蒸気処理方法としては、公知の方法を用いることができる。また、各種前処理工程、表面調整処理工程、化成処理工程等の後に、水洗等の洗浄、乾燥、塗装等の後処理工程を適宜行ってもよい。これらの前処理工程及び後処理工程は、公知の方法により行うことができる。
表面調整処理工程は、上記表面調整剤をマグネシウム含有金属材に接触させてその表面を処理する方法である。表面調整剤の接触方法としては、例えば、スプレーコート法、ディップコート法、ロールコート法、カーテンコート法、スピンコート法、又はこれらを適宜組み合せた方法などがあげられる。
表面調整処理工程における表面処理剤、あるいはマグネシウム含有金属材の温度は、通常0℃以上であり、10℃以上であってよく、また通常40℃以下であり、30℃以下であってよい。
表面調整剤とマグネシウム含有金属材との接触時間は、通常1秒以上であり、5秒以上であってよく、10秒以上であってもよい。また、通常10分以下であり、5分以下であってよく、3分以下であってよく、1分以下であってよい。
化成処理工程は、表面調整剤を接触させたマグネシウム含有金属材に、表面処理剤(化成処理剤)を接触させて、その表面を化成処理する方法である。
化成処理剤は、リン酸イオンとカルシウムイオンを含むものであれば特に制限されるものではない。
リン酸イオンの供給源は、例えば、リン酸又は水溶性リン酸塩等があげられる。また、カルシウムイオンの供給源は、例えば、水酸化カルシウム、炭酸カルシウム、硝酸カルシウムなどがあげられる。
化成処理剤のpHは、通常2.0以上であり、3.0以上であってよく、4.0以上であってよく、また通常5.0以下であり、4.5以下であってよい。化成処理剤のpHを調整するためのpH調整剤は特に限定されず、硝酸、リン酸、硫酸などの酸成分、又は水酸化ナトリウム、炭酸ナトリウム、アンモニア水、炭酸水素アンモニウムなどのアルカリ成分を用いることができる。
化成処理における、マグネシウム含有金属材と表面処理剤との接触時間は、通常1分以上であり、3分以上であってよく、5分以上であってよく、また通常60分以下であり、30分以下であってよく、15分以下であってよい。
上記表面調整処理及び化成処理の対象であるマグネシウム含有金属材は、マグネシウム材、マグネシウム合金材等のマグネシウムを主成分とする金属材である。マグネシウム合金材が2つの金属成分からなる場合には、マグネシウムを50重量%以上含有するものであればよく、80重量%以上含有するものが好ましい。また、マグネシウム合金材が3つ以上の金属成分からなる場合には、マグネシウムが1番多く含有するものであればよい。マグネシウム合金材の種類としては、例えば、AZ91、AM60、ZK51、ZK61、AZ31、AZ61、ZK60などがあげられる。
本発明の別の実施形態は、マグネシウム含有金属材の表面上に、第二リン酸カルシウム粒子を含有する皮膜を有する、皮膜付きマグネシウム含有金属材である。なお、皮膜付きマグネシウム含有金属材は、第二リン酸カルシウム粒子を含有する皮膜に防錆油やシーリング剤が付着したものであってもよいし、第二リン酸カルシウム粒子を含有する皮膜上に塗膜をさらに有するものであってもよい。
皮膜に含まれる第二リン酸カルシウム粒子は、結晶性の粒子である。第二リン酸カルシウム粒子は、モネタイト又はブルシャイトであってもよいし、双方を含んでいてもよい。また、双方を含む場合は、それらの含有比率は特に限定されるものではない。
また、結晶性の第二リン酸カルシウム粒子を含有する皮膜は、均一かつ緻密な構造を有する。そのため、該皮膜は、優れた密着性及び耐食性を有する。なお、第二リン酸カルシウム粒子が結晶性粒子であることは、X線回折(XRD)により確認することができる。
また、皮膜中の第二リン酸カルシウム粒子は、粒度分布の標準偏差が5以下であり、3以下であってよく、1.5以下であってよく、1以下であってよい。標準偏差がこの範囲内である結晶性第二リン酸カルシウム粒子を含む皮膜は、より均一で緻密な構造を有する。
皮膜中の第二リン酸カルシウム粒子を上記径及び標準偏差に調整する手段としては、上記表面調整処理工程及び化成処理工程を行うことがあげられる。
結晶性第二リン酸カルシウム粒子を含有する皮膜の量は、蛍光X線分光分析によりカルシウムの量及びリンの量を定量し、CaHPO4に換算することで算出できる。
被覆率を高める方法、及び皮膜量を増加させる方法としては、化成処理工程前に表面調整剤による表面調整処理工程を行う方法の他、化成処理工程における処理時間を調整する方法があげられる。
塗膜の厚さは、特に制限されるものではないが、平均で5〜30μmであり、8〜25μmであってよい。
<マグネシウム合金材>
マグネシウム合金材として、ASTM(American Society for Testing and Materiarls)−AZ31の板材を用いた。なお、板材に対して、後述の表面調整処理を行う前に、
以下の前処理を施した。具体的には、板材の表面に、65℃に加温したアルカリ脱脂剤(日本パーカライジング株式会社製;ファインクリーナーMG110E)を120秒間スプレーした後、水洗した。続いて、研磨面に脱イオン水をかけながらサンドペーパーにて板材表面を物理研磨した後、脱イオン水で水洗し、熱風乾燥した。
脱イオン水55重量部にカルボキシメチルセルロース1重量部を溶解させた。その溶解物に、モネタイトまたはブルシャイト24重量部を添加した混合物を撹拌した後、ダイノーミル粉砕機(φ1mmアルカリガラスビーズ)を用いて湿式粉砕した。粉砕した混合物(固形分濃度30%の懸濁液)における固形分の粒度分布を、日機装株式会社製マイクロトラック計UPA−EX150で測定し、D50及びD90を求めた。その結果、D50が0.45μm、D90が0.9μmであった。
更に上記懸濁液に、最終濃度で250ppm及び200ppmとなるように、ピロリン酸ナトリウム及びリン酸三ナトリウムをそれぞれ添加し、実施例1〜8の表面調整剤を調製した。なお、表1に、各表面調整剤の調製に用いた第二リン酸カルシウム粒子の種類とその濃度を示す。
研磨した板材を25℃の表面調整剤に30秒間浸漬し、表面調整処理を行った。その後、板材を化成処理剤に15分間浸漬し、化成処理を行った。続いて、板材を脱イオン水で
水洗して熱風乾燥することにより、皮膜付きマグネシウム合金材を作製した。なお、化成処理に用いた各化成処理剤の温度を表2に示す。
マグネシウム合金材上に形成した皮膜の表面を走査型電子顕微鏡により観察し、マグネシウム合金材に対して皮膜が占める面積割合を被覆率として求めた。結果を表2に示す。
マグネシウム合金材上に形成した皮膜をX線回折法により測定し、その結晶系を同定した。結果を表2に示す。
蛍光X線分光分析装置により、マグネシウム合金材上に形成した皮膜におけるリンの含有量(リン付着量)を測定し、皮膜量に換算した。皮膜量への換算は、X線回折法による結晶系の同定結果に基づいて行った。例えば、皮膜が100%ブルシャイトと同定された場合、リン付着量Pから皮膜量Wへの換算は、リンの原子量31.0とブルシャイトの分子量172.1を用いて、式:W=P×172.1/31.0により算出した。結果を表2に示す。
マグネシウム合金材上に形成した皮膜の表面を走査型電子顕微鏡により観察し、無作為に選択した100個の結晶粒子サンプルの粒子径を測定し、平均粒子径とその分布の標準偏差を算出した。結果を表2に示す。なお、個々のサンプルの粒子径は、測定したサンプルの最大径と最小径の平均値とした。また、粒子径分布の標準偏差はいずれも5以下であった。
皮膜付きマグネシウム合金材を40℃の5%塩化ナトリウム水溶液に24時間浸漬した後、水洗及び風乾を行い、以下の判定基準に従って外観を評価した。結果を表2に示す。(判定基準)
5点:錆発生無し
4点:数点の点錆有り
3点:点錆多数または面積率20%未満で錆が発生
2点:面積率20%以上で錆が発生しているが、全面が錆に覆われていない
1点:全面が錆に覆われている
皮膜付きマグネシウム合金材を電着塗装し、マグネシウム合金材に対する塗膜の密着性を評価した。関西ペイント社製カチオン電着塗料「GT−10LF」を用い、塗料温度28℃、電圧200Vの条件下で塗膜を形成させた。その後、水洗し、150℃で20分間焼き付けて、乾燥膜厚20μmの塗膜を有するマグネシウム合金材を得た。
塗膜を有するマグネシウム合金材を、40℃の脱イオン水に浸漬し、240時間後にペーパーカッターで碁盤目状にクロスカットを施し、セロハンテープをクロスカット部に貼り付け、テープ剥離試験を行った。なお、碁盤目状のクロスカットは、1mm間隔の平行線11本を直角に交差することにより100個のマス目とした。テープ剥離後に剥離したマス目の数を計測し、以下の判定基準に従って密着性を評価した。結果を表2に示す。
(判定基準)
5点:剥離無し
4点:マス目のエッジ部のみ剥離し、マス目全体の剥離は無かった
3点:1〜20個の剥離が生じた
2点:21〜50個の剥離が生じた
1点:51個以上の剥離が生じた
研磨した板材を用い、上記表面調整処理及び化成処理を行わないで、上記耐食性評価及び上記密着性評価を実施したところ、それぞれ1点の評価結果が得られた。
Claims (3)
- 第二リン酸カルシウム粒子を含有し、
前記第二リン酸カルシウム粒子のD50が0.1μm以上0.8μm以下であり、
前記第二リン酸カルシウムがモネタイト及び/又はブルシャイトである、表面調整剤。 - マグネシウム材又はマグネシウム合金材に、請求項1に記載の表面調整剤を接触させる工程と、
前記表面調整剤を接触させたマグネシウム材又はマグネシウム合金材に、リン酸イオン及びカルシウムイオンを含む表面処理剤を接触させる工程と、
を含む、皮膜付きマグネシウム材又はマグネシウム合金材の製造方法。 - マグネシウム材又はマグネシウム合金材の表面上に、第二リン酸カルシウムの結晶性粒子を含有する皮膜を有し、
前記第二リン酸カルシウムの結晶性粒子の平均粒子径が0.7μm以上25μm以下であり、かつ、粒度分布の標準偏差が5以下であり、
前記第二リン酸カルシウムがモネタイト及び/又はブルシャイトである、皮膜付きマグネシウム材又はマグネシウム合金材。