JP2018067399A - Sheet-like air electrode, acid battery, and power generation system - Google Patents
Sheet-like air electrode, acid battery, and power generation system Download PDFInfo
- Publication number
- JP2018067399A JP2018067399A JP2016203891A JP2016203891A JP2018067399A JP 2018067399 A JP2018067399 A JP 2018067399A JP 2016203891 A JP2016203891 A JP 2016203891A JP 2016203891 A JP2016203891 A JP 2016203891A JP 2018067399 A JP2018067399 A JP 2018067399A
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- electrolyte
- negative electrode
- power generation
- electrode
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、酸性電解質を用いた電池（酸電池）の正極に用いるシート状空気電極、酸電池及びそれを比較的大規模で実現する発電システムに関する。
とりわけ、カーボンナノチューブを含む膜状物を表面に有する炭素繊維シートにより構成されるシート状空気電極、酸電池及び発電システムに関する。
The present invention relates to a sheet-like air electrode used for a positive electrode of a battery (acid battery) using an acidic electrolyte, an acid battery, and a power generation system that realizes the same on a relatively large scale.
In particular, the present invention relates to a sheet-like air electrode composed of a carbon fiber sheet having a film-like material containing carbon nanotubes on its surface, an acid battery, and a power generation system.
電池には、物理電池（光電池、太陽電池）と化学電池がある。化学電池には、自ら発電して放電する一次電池と、外から与えた電力を蓄えて放電する二次電池とがあり、さらに、燃料電池がある。
二次電池は、充電と放電を繰り返すことが可能であるので、繰り返し使用することができる。それに対し、一次電池は、充電できないといわれることが多いが、使用によって減少した物質を機械的に取り替えること（メカニカルチャージ）によって繰り返し使用することができる。
The battery includes a physical battery (photo battery, solar battery) and a chemical battery. Chemical batteries include a primary battery that generates and discharges itself, a secondary battery that stores and discharges electric power applied from the outside, and a fuel cell.
Since the secondary battery can be repeatedly charged and discharged, it can be used repeatedly. On the other hand, the primary battery is often said to be unable to be charged, but can be repeatedly used by mechanically replacing the material reduced by use (mechanical charge).
繰り返し使用することが可能な一次電池の例として、マグネシウム又はアルミニウムを負極として用い、酸性電解質を用いるものが提案されている（特許文献１）。
特許文献１には、マグネシウム又はアルミニウムを負極として、導電部材（カーボンシート）を正極として、当該正極に空気を供給し、この負極と正極間に過塩素酸からなる酸性電解質を配設してなり、前記負極の金属が溶滅したら、新しい金属と取り替えるだけで引き続き使用することが可能である酸電池が開示されている。
さらに、この酸電池では、負極と電解質との接触を断つことにより、化学反応を完全に停止させることができる。
特許文献１における正極は、カーボン等の炭素系導電部材と記載されている。
As an example of a primary battery that can be used repeatedly, one using magnesium or aluminum as a negative electrode and using an acidic electrolyte has been proposed (Patent Document 1).
In Patent Document 1, magnesium or aluminum is used as a negative electrode, a conductive member (carbon sheet) is used as a positive electrode, air is supplied to the positive electrode, and an acidic electrolyte made of perchloric acid is disposed between the negative electrode and the positive electrode. In addition, an acid battery is disclosed that can be used continuously by replacing the metal of the negative electrode with a new metal after it has been melted.
Furthermore, in this acid battery, the chemical reaction can be completely stopped by breaking the contact between the negative electrode and the electrolyte.
The positive electrode in Patent Document 1 is described as a carbon-based conductive member such as carbon.
一方、炭素は、グラファイト、ダイヤモンド、無定形炭素など、性質が大きく異なる複数の同素体が存在する。１９８０年代以降次々と新発見されたナノメートルサイズの炭素の同素体は、従来知られていた炭素同素体とは全く異なる原子構造や物性を有することが確かめられ、その工業的利用価値の高さが注目されている。本明細書ではそれらを「ナノ炭素材料」と称し、カーボンナノチューブ、カーボンナノファイバー、ナノグラフェン、フラーレン、カーボンナノホーン、カーボンマイクロコイル、カーボンブラック、ダイヤモンドライクカーボン、カーボンナノクリスタル、活性炭などであって、数ｎｍ〜１０μｍ程度のサイズのものを含むものとする。 On the other hand, carbon has a plurality of allotropes having greatly different properties such as graphite, diamond, and amorphous carbon. Nanometer-sized carbon allotropes that have been newly discovered since the 1980s have been confirmed to have completely different atomic structures and physical properties from the conventionally known carbon allotropes. Has been. In the present specification, these are referred to as “nanocarbon materials”, and are carbon nanotubes, carbon nanofibers, nanographene, fullerenes, carbon nanohorns, carbon microcoils, carbon black, diamond-like carbon, carbon nanocrystals, activated carbon, etc. The one having a size of about 10 nm to 10 μm is included.
ナノ炭素材料は炭素のみから構成されるため、極めて軽量で、高強度で、導電性を有する高分子材料である。その導電性は銅よりも優れ、強度は鋼よりも優れ、耐熱性が高く、多くの薬品に対しても反応せず、大気中で安定である。
ナノ炭素材料の中でも、カーボンナノチューブは、特に優れた電気特性、力学特性、熱特性などを示すものであり、様々な材料への応用が期待され、広く研究開発が行われている。例えば、カーボンナノチューブと樹脂とを混合した複合材とし、あるいはカーボンナノチューブ分散液をバインダーとを混合して乾燥させたものから、様々な用途の材料が得られる。
Since the nanocarbon material is composed only of carbon, it is a polymer material that is extremely lightweight, high in strength, and conductive. Its conductivity is superior to copper, strength is superior to steel, heat resistance is high, it does not react to many chemicals, and is stable in the atmosphere.
Among nanocarbon materials, carbon nanotubes exhibit particularly excellent electrical properties, mechanical properties, thermal properties, etc., and are expected to be applied to various materials, and are widely researched and developed. For example, a material for various uses can be obtained from a composite material in which carbon nanotubes and a resin are mixed, or a carbon nanotube dispersion mixed with a binder and dried.
カーボンナノチューブは、ファンデルワールス力により凝集する性質があり、溶液中ではバンドル構造体を形成するため、そのままでは良好なカーボンナノチューブ複合材料を製造することができず、カーボンナノチューブを溶液中に分散（あるいは可溶化）させる工程が必要となる。カーボンナノチューブが良好に分散された溶液（分散液）を用いることが、カーボンナノチューブ複合材料の特性向上に大きく寄与することから、カーボンナノチューブを溶液中に安定的に分散させる技術に関して多くの提案がなされている。 Carbon nanotubes have the property of agglomerating due to van der Waals forces and form a bundle structure in the solution. Therefore, it is impossible to produce a good carbon nanotube composite as it is, and the carbon nanotubes are dispersed in the solution ( Alternatively, a step of solubilization is required. Since the use of a solution (dispersion) in which carbon nanotubes are well dispersed greatly contributes to the improvement of the characteristics of the carbon nanotube composite material, many proposals have been made regarding techniques for stably dispersing carbon nanotubes in a solution. ing.
溶液中のカーボンナノチューブの分散方法としては、有機溶媒（例えば、Ｎ−メチルピロリドン；ＮＭＰ）を用いる方法、酸処理によりカーボンナノチューブを化学修飾する方法、界面活性剤（例えば、ドデシル硫酸ナトリウム；ＳＤＳ）によりミセル化する方法などがあり、さらに超音波処理やビーズミル処理などが併用されることも多い。 As a method for dispersing carbon nanotubes in a solution, a method using an organic solvent (for example, N-methylpyrrolidone; NMP), a method for chemically modifying carbon nanotubes by acid treatment, a surfactant (for example, sodium dodecyl sulfate; SDS) There is a method of forming micelles, and ultrasonic treatment and bead mill treatment are often used together.
特許文献２には、アルキルエステル基、ビニリデン基及びアニオン性基を有する界面活性剤、カーボンナノチューブ、水性溶媒を含むカーボンナノチューブ分散液が提案されている（請求項１等）。この分散技術では、界面活性剤のビニリデン基が有する炭素二重結合がカーボンナノチューブと相互作用することによりカーボンナノチューブの分散が促進されるものとされており、従来のドデシル硫酸ナトリウム（ＳＤＳ）等の分散剤を用いた場合に比べて分散度が高く（[００５５]〜[００６２]等）、さらにはｐＨ変化に対する安定性が高い（[００６３]〜[００６９]等）カーボンナノチューブ分散液が得られるとの結果が報告されている。 Patent Document 2 proposes a carbon nanotube dispersion containing a surfactant having an alkyl ester group, a vinylidene group and an anionic group, carbon nanotubes, and an aqueous solvent (claim 1 and the like). In this dispersion technique, the carbon double bond possessed by the vinylidene group of the surfactant interacts with the carbon nanotubes to promote the dispersion of the carbon nanotubes, such as conventional sodium dodecyl sulfate (SDS). Compared with the case where a dispersant is used, the degree of dispersion is high ([0055] to [0062], etc.) and the stability against pH change ([0063] to [0069] etc.) is also obtained. Results have been reported.
特許文献３には、カーボンナノチューブと活性炭との複合材料を提案している。 Patent Document 3 proposes a composite material of carbon nanotubes and activated carbon.
ＮＭＰ等の有機溶媒やＳＤＳ等の界面活性剤を用いたカーボンナノチューブ分散液は、時間経過により再びカーボンナノチューブが凝集してしまうという問題点や作製したナノ炭素材料に有機溶媒や界面活性剤が不純物として残留してしまうという問題点が解消されていない。
酸処理によりカーボンナノチューブを化学修飾する方法は、溶媒に親和性を有する官能基を共有結合的にカーボンナノチューブ表面に導入するものであるが、これによりカーボンナノチューブが本来有する性質が失われたり、切断されてしまったりするという問題点が解消されていない。
The carbon nanotube dispersion using an organic solvent such as NMP or a surfactant such as SDS is problematic in that the carbon nanotubes agglomerate again over time and the organic solvent and surfactant are impurities in the produced nanocarbon material. The problem of remaining as is not solved.
The method of chemically modifying carbon nanotubes by acid treatment is to covalently introduce functional groups having an affinity for the solvent to the surface of the carbon nanotubes. The problem of being done is not solved.
本発明は、カーボンナノチューブのすぐれた特性を生かす上で、分散の課題があること、その課題を乗り越えることができれば、酸電池の正極としてのカーボンシートに有効であると思われることに鑑みてなされたものであり、カーボンナノチューブが本来有する性質を損なうことなく、かつ、時間経過しても良好な分散状態を保つことができるナノ炭素材料の分散方法及びナノ炭素材料の分散液、並びにそれらによって得られるナノ炭素材料複合体を提供し、さらに、その炭素材料複合体を膜状にして、炭素繊維シートの表面を覆うものを酸電池の正極として提案する。
さらに、必要な電力量を、電力の需要に合わせて発電する計画発電を実現可能な発電システムを提案する。
The present invention has been made in view of the fact that there is a problem of dispersion in taking advantage of the excellent characteristics of carbon nanotubes, and that it is considered effective for a carbon sheet as a positive electrode of an acid battery if the problem can be overcome. Nanocarbon material dispersion method and nanocarbon material dispersion liquid that can maintain a good dispersion state over time without impairing the inherent properties of carbon nanotubes, and obtained by them The nanocarbon material composite is provided, and the carbon material composite is formed into a film and covering the surface of the carbon fiber sheet as a positive electrode of an acid battery.
Furthermore, we propose a power generation system that can realize planned power generation that generates the required amount of power according to the demand for power.
上記解決課題に鑑みて鋭意研究の結果、本発明者は、
（１）低級アルコールを１０重量％以上含む水溶液に対し、０．０１〜１０％の陰イオン性界面活性剤又は非イオン性界面活性剤を添加した溶媒中に、カーボンナノチューブ、及び当該カーボンナノチューブに対し１〜３０重量％の他の種類のナノ炭素材料であるグラフェン、カーボンブラック、活性炭のうち１種類又は２種類以上を含むものを凝集阻止剤として加えて、得た溶液（スラリー）に超音波照射することで、分散処理を行う。
（２）好適な界面活性剤を含む水溶液に上記（１）のスラリーを加え、原材料水溶液（カーボンナノチューブ１重量部に対して、カルボキシメチルセルロースアンモニウム１〜５重量部、炭酸水素アンモニウム１〜５重量部、ポリオールを含む）とし、超音波処理を行うことにより、極めて優れた分散性を有するナノ炭素材料の分散液を得られることを見出した。
さらに、炭素繊維シートの表面に、前記カーボンナノチューブを含有する膜状物を設けて、ファイバー結合した３Ｄメッシュとし、酸電池の正極とすることに思い至り、本発明を成すに至った。
As a result of earnest research in view of the above-mentioned problem, the present inventors
(1) In an aqueous solution containing 10% by weight or more of a lower alcohol, in a solvent to which 0.01 to 10% of an anionic surfactant or a nonionic surfactant is added, In contrast, 1 to 30% by weight of other types of nanocarbon materials, such as graphene, carbon black, and activated carbon, containing one or more kinds are added as an aggregation inhibitor, and ultrasonic waves are added to the obtained solution (slurry). Dispersion processing is performed by irradiation.
(2) The slurry of (1) above is added to an aqueous solution containing a suitable surfactant, and the raw material aqueous solution (1 to 5 parts by weight of carboxymethyl cellulose ammonium and 1 to 5 parts by weight of ammonium hydrogen carbonate with respect to 1 part by weight of carbon nanotubes) It was found that a dispersion of a nanocarbon material having extremely excellent dispersibility can be obtained by ultrasonic treatment.
Furthermore, the present inventors have conceived that a film-like material containing the carbon nanotube is provided on the surface of the carbon fiber sheet to form a fiber-bonded 3D mesh to be a positive electrode of an acid battery.
本発明に係るシート状空気電極は、カーボンナノチューブを含有する膜状物をその表面に有する炭素繊維シートからなる。
これにより、カーボンナノチューブのイオン透過性、導電性、酸素透過性などの特性を生かした空気電極を構成することができる。
The sheet-like air electrode according to the present invention comprises a carbon fiber sheet having a film-like material containing carbon nanotubes on its surface.
As a result, an air electrode that makes use of the characteristics of carbon nanotubes such as ion permeability, conductivity, and oxygen permeability can be configured.
また、配置する場所の空間形状に合わせて、前記炭素繊維シートの面積、寸法、形状、立体的な変形加工が変更可能とすることができる。これにより、電池形状をカスタマイズ可能となり、大きさ、形などを自在に選ぶことができる。 Moreover, according to the space shape of the place to arrange | position, the area of the said carbon fiber sheet, a dimension, a shape, and a three-dimensional deformation process can be changed. As a result, the battery shape can be customized, and the size and shape can be freely selected.
特に、酸電池の正極として用いられる。これにより、電流密度などの点で有利な酸電池を構成可能となる。 In particular, it is used as a positive electrode for acid batteries. Thereby, an acid battery advantageous in terms of current density and the like can be configured.
また、前記酸電池の負極はマグネシウム、アルミニウム、亜鉛、鉄または銅のうちの一つ又は二つ以上を含む金属からなり、前記正極と前記負極とが近接する空間に酸性電解質が配される。これにより、酸により負極の金属が溶ける（腐食する）ことで電池が構成される。 The negative electrode of the acid battery is made of a metal containing one or more of magnesium, aluminum, zinc, iron or copper, and an acidic electrolyte is disposed in a space where the positive electrode and the negative electrode are close to each other. Thereby, a battery is comprised because the metal of a negative electrode melt | dissolves (corrodes) with an acid.
前記酸性電解質は、溶液であり、前記炭素繊維シートを当該溶液の電解質が透過して前記負極に接触するようにすることができる。これにより電解質及び溶液中の溶存酸素が溶液中を移動して機能することができる。 The acidic electrolyte is a solution, and the electrolyte of the solution can pass through the carbon fiber sheet and contact the negative electrode. Thereby, the dissolved oxygen in the electrolyte and the solution can move and function in the solution.
前記溶液を循環させる循環装置により、前記電解質及び前記溶液中の溶存酸素が前記炭素繊維シートを透過して循環することができる。これにより、化学反応による生成物を排除するとともに、必要な電解質及び溶存酸素を必要なところに運ぶことが可能となる。 The electrolyte and the dissolved oxygen in the solution can be circulated through the carbon fiber sheet by the circulation device that circulates the solution. As a result, it is possible to eliminate a product due to a chemical reaction and to carry a necessary electrolyte and dissolved oxygen to a necessary place.
前記循環装置による循環を、制御可能とし、それにより前記電解質が前記炭素シートを透過して循環することを停止し、又は前記溶液中の溶存酸素の供給を減らすことができる。これにより、化学反応を停止または緩慢にすることが可能となる。 Circulation by the circulation device can be controlled, thereby stopping the electrolyte from circulating through the carbon sheet, or reducing the supply of dissolved oxygen in the solution. This makes it possible to stop or slow down the chemical reaction.
前記酸性電解質は、ジェルであり、シートに含浸させたジェルシートとして設けられるようにすることができる。これにより、液垂れを防止し、置く向きを気にせずに用いることができる。 The acidic electrolyte is a gel and can be provided as a gel sheet impregnated in the sheet. Thereby, dripping can be prevented and it can be used without worrying about the orientation.
前記ジェルは、電解質が透過せず抜き差し可能な遮断シートを介して前記負極と接触し、遮断シートを抜いた状態で発電し、遮断シートを差した状態で発電停止することができる。これにより不使用時の無駄な放電を避けることができる。 The gel is in contact with the negative electrode through a blocking sheet that can be inserted and removed without allowing the electrolyte to pass through, and can generate power with the blocking sheet removed and stop generating power with the blocking sheet inserted. Thereby, useless discharge when not in use can be avoided.
前記ジェルシートは、抜き差し可能であり、抜くことにより前記酸性電解質と前記負極との接触を断ち、差すことにより前記電解質と前記負極との接触を実現する。これにより、電池の放電を停止又は緩慢にし、必要あるときに再び電池使用をすることができる。 The gel sheet can be inserted and removed, and by disconnecting, the contact between the acidic electrolyte and the negative electrode is cut off, and by connecting, the contact between the electrolyte and the negative electrode is realized. Thereby, the discharge of the battery can be stopped or slowed down, and the battery can be used again when necessary.
前記負極は、交換可能であり、溶滅した際に、新たな負極と交換することができる。これにより、繰り返し使用が可能な一次電池を実現できる。 The negative electrode is replaceable and can be replaced with a new negative electrode when it is melted. Thereby, the primary battery which can be used repeatedly is realizable.
本発明に係る酸電池は、カーボンナノチューブを含有する膜状物をその表面に有する炭素繊維シートからなるシート状空気電極を正極とし、マグネシウム、アルミニウム、亜鉛、鉄または銅を含む金属を負極とし、前記正極と前記負極との間に酸性電解質が配される。これにより、カーボンナノチューブの特性を生かした酸電池を構成することができる。 The acid battery according to the present invention uses a sheet-like air electrode made of a carbon fiber sheet having a film-like material containing carbon nanotubes on its surface as a positive electrode, and a metal containing magnesium, aluminum, zinc, iron or copper as a negative electrode, An acidic electrolyte is disposed between the positive electrode and the negative electrode. As a result, an acid battery utilizing the characteristics of the carbon nanotube can be configured.
前記正極を構成する前記炭素繊維シート配置する場所の空間形状に合わせて、前記炭素繊維シートの面積、寸法、形状を変更可能であり、前記負極を前記正極の面積、寸法、形状の変更に合わせて変形する。これにより、狭い場所や、湾曲形状の場所などでも設置可能な酸電池を提供できる。 The area, size, and shape of the carbon fiber sheet can be changed in accordance with the space shape of the place where the carbon fiber sheet constituting the positive electrode is arranged, and the negative electrode is adjusted to change in the area, size, and shape of the positive electrode. And deform. Thereby, the acid battery which can be installed in a narrow place or a curved place can be provided.
前記酸性電解質は、溶液とすることができる。これにより、反応後の生成物を除去すること、電解質及び溶液中の溶存酸素を必要なところに移動することにおいて、有利な電池を構成できる。 The acidic electrolyte can be a solution. Thereby, an advantageous battery can be constituted in removing the product after the reaction and moving the dissolved oxygen in the electrolyte and the solution to a necessary place.
前記溶液を循環させる循環装置をさらに有し、前記電解質及び前記溶液中の溶存酸素が循環するようにすることができる。これにより、化学反応を効率的に行える電池を提供できる。 The apparatus may further include a circulation device for circulating the solution, and the electrolyte and the dissolved oxygen in the solution may be circulated. Thereby, the battery which can perform a chemical reaction efficiently can be provided.
前記循環装置による循環を、制御可能とし、電解質の循環を停止し、又は前記溶液中の溶存酸素の供給を減らすことができる。これにより、化学反応を停止すること、または緩慢にすることが可能となる。 The circulation by the circulation device can be controlled, the circulation of the electrolyte can be stopped, or the supply of dissolved oxygen in the solution can be reduced. This makes it possible to stop or slow down the chemical reaction.
前記酸性電解質は、ジェル状であり、シートに含浸させたジェルシートとして設けることができる。これにより、液垂れを防ぐことができる。また、電池を置く向きを限定されない。 The acidic electrolyte is in a gel form and can be provided as a gel sheet impregnated in the sheet. Thereby, dripping can be prevented. Further, the direction in which the battery is placed is not limited.
前記ジェルシートは、電解質が透過せず抜き差し可能な遮断シートを介して前記負極と接触し、遮断シートを抜いた状態で発電し、遮断シートを差した状態で発電停止することができる。これにより、不使用時の無駄な放電を避けることができる。 The gel sheet is in contact with the negative electrode through a non-permeable blocking sheet that does not allow electrolyte to pass through, and can generate power with the blocking sheet removed, and can stop power generation with the blocking sheet inserted. Thereby, useless discharge when not in use can be avoided.
前記ジェルシートは、抜き差し可能であり、抜くことにより前記電解質と前記負極との接触を断ち、差すことにより前記電解質と前記負極との接触を実現する。これにより、電池を使わないときの無駄な放電を防止することができる。 The gel sheet can be inserted and removed, and by disconnecting, the contact between the electrolyte and the negative electrode is cut off, and by connecting, the contact between the electrolyte and the negative electrode is realized. Thereby, useless discharge when not using a battery can be prevented.
前記負極は、交換可能であり、溶滅した際に、新たな負極と交換する。これにより、繰り返して使用可能な酸電池を提供することができる。 The negative electrode is replaceable and is replaced with a new negative electrode when melted. Thereby, the acid battery which can be used repeatedly can be provided.
本発明に係る発電システムは、カーボンナノチューブを含有する膜状物をその表面に有するシート状空気電極を正極とし、マグネシウム、アルミニウム、亜鉛、鉄または銅のうちの一つ又は二つ以上を含む金属を負極とし、前記正極と前記負極との間に酸性電解質が配されてなる酸電池を複数積層配置し、電気接続してなる。 A power generation system according to the present invention uses a sheet-like air electrode having a film-like material containing carbon nanotubes on its surface as a positive electrode, and a metal containing one or more of magnesium, aluminum, zinc, iron or copper And a plurality of acid batteries in which an acidic electrolyte is arranged between the positive electrode and the negative electrode are stacked and electrically connected.
前記正極をなす前記空気電極の基材として、炭素繊維シートを用いる。これにより、表面積を大きくすることができ、反応を促進する上で有利である。 A carbon fiber sheet is used as a base material of the air electrode forming the positive electrode. Thereby, the surface area can be increased, which is advantageous in promoting the reaction.
前記正極を構成する前記炭素繊維シートは、配置する場所の空間形状に合わせて面積、寸法、形状を変更可能であり、前記負極を前記正極の面積、寸法、形状の変更に合わせて変形するる。これにより、酸電池の形状をカスタマイズ可能となる。 The carbon fiber sheet constituting the positive electrode can be changed in area, size, and shape in accordance with the spatial shape of the place where the positive electrode is disposed, and the negative electrode is deformed in accordance with the change in area, size, and shape of the positive electrode. . Thereby, the shape of the acid battery can be customized.
前記酸性電解質は、溶液とする。これにより、反応性生物の除去、電解質及び溶液中の溶存酸素の移動に有利である。 The acidic electrolyte is a solution. This is advantageous for removal of reactive organisms, transfer of electrolytes and dissolved oxygen in the solution.
前記溶液を循環させる循環装置をさらに有し、前記電解質及び前記溶液中の溶存酸素が循環するようにする。これにより、化学反応を促進できる。 A circulation device that circulates the solution is further provided to circulate the electrolyte and dissolved oxygen in the solution. Thereby, a chemical reaction can be promoted.
前記循環装置による循環を、制御可能とし、電解質の循環を停止し、又は前記溶液中の溶存酸素の供給を減らすことができる。これにより、化学反応を停止すること、又は緩慢にすることができる。 The circulation by the circulation device can be controlled, the circulation of the electrolyte can be stopped, or the supply of dissolved oxygen in the solution can be reduced. This can stop or slow down the chemical reaction.
前記酸性電解質は、ジェル状であり、シートに含浸させたジェルシートとして設けられる。これにより液垂れを防止し、発電システムの置く向きの制限をなくす。 The acidic electrolyte is in a gel form and is provided as a gel sheet impregnated in the sheet. This prevents dripping and eliminates the restrictions on the orientation of the power generation system.
前記ジェルシートは、電解質が透過せず抜き差し可能な遮断シートを介して前記負極と接触し、遮断シートを抜いた状態で発電し、遮断シートを差した状態で発電停止する。これにより、不使用時の無駄な放電を避ける。 The gel sheet is in contact with the negative electrode through a blocking sheet that does not allow electrolyte to pass through and can be inserted and removed, and generates power with the blocking sheet removed, and stops power generation with the blocking sheet inserted. This avoids wasteful discharge when not in use.
前記ジェルシートは、抜き差し可能であり、当該ジェルシートを抜くことにより前記電解質と前記負極との接触を断ち、差すことにより前記電解質と前記負極との接触を実現する。これにより、電気を使わないときの無駄な放電を防止する。 The gel sheet can be inserted and removed, and the contact between the electrolyte and the negative electrode is cut off by pulling out the gel sheet, and the contact between the electrolyte and the negative electrode is realized by inserting the gel sheet. This prevents wasteful discharge when electricity is not used.
前記負極と、前記酸性電解質との接触を断つ、又は前記正極と酸素との接触を断つ反応停止装置を有する。これにより、電気を使わないときの無駄な放電を防止し、計画発電を可能にする。 There is provided a reaction stopping device that cuts off contact between the negative electrode and the acidic electrolyte, or cuts off contact between the positive electrode and oxygen. This prevents wasteful discharge when electricity is not used and enables planned power generation.
前記反応停止装置は、当該反応停止状態を解除して、再び発電を開始可能である。これにより、電気の使用、不使用を自在に管理できる。 The reaction stop device can release the reaction stop state and start power generation again. Thereby, use or non-use of electricity can be managed freely.
カーボンナノチューブを含有する膜状物をその表面に有するシート状空気電極を正極とし、マグネシウム、アルミニウム、亜鉛、鉄または銅のうちの一つ又は二つ以上を含む金属を、溶滅の際には新しい物と交換可能に設けて、負極とし、前記正極と前記負極との間に、電気絶縁性を有し、電解質を透過するセパレータを設け、前記正極、前記セパレータ、前記負極を積層配置した積層物に対して、前記正極の側から、発電に必要な量の酸性電解質を滴下又は噴霧して負極に到達させる酸性電解質供給装置とを有する発電システムとすることができる。これにより、たきぎを燃やすのに必要かつ十分な火を準備するように、無駄のない酸性電解質供給をすることができる。 When a sheet-like air electrode having a film-like material containing carbon nanotubes on its surface is used as a positive electrode, a metal containing one or more of magnesium, aluminum, zinc, iron, or copper is used in the case of melting. A laminate that is provided in a replaceable manner as a negative electrode, and is provided with a separator having electrical insulation and permeation of electrolyte between the positive electrode and the negative electrode, and the positive electrode, the separator, and the negative electrode are stacked. It is possible to provide a power generation system having an acidic electrolyte supply device that drops or sprays an amount of an acidic electrolyte necessary for power generation from the positive electrode side to reach the negative electrode. Thereby, it is possible to supply an acidic electrolyte without waste so as to prepare a necessary and sufficient fire for burning the firewood.
前記酸性電解質供給装置による酸性電解質の供給量を制御する酸性電解質供給制御装置をさらに有し、計画発電を実現する。これにより、停電や、真夏の電力不足に対応することが可能となる。 It further has an acidic electrolyte supply control device that controls the supply amount of the acidic electrolyte by the acidic electrolyte supply device, and realizes planned power generation. As a result, it becomes possible to cope with power outages and power shortages in midsummer.
本発明に係るカーボンナノチューブを含有する膜状物をその表面に有する炭素繊維シートからなるシート状空気電極の製造方法は、カーボンナノチューブと、カルボキシメチルセルロースアンモニウムと炭酸水素アンモニウムとグリセリンとを水に溶解させて原材料水溶液とする原材料水溶液生成ステップと、前記原材料水溶液に超音波ホモジナイザーにより超音波を照射して分散水溶液を得る超音波照射ステップと、炭素繊維シートを前記超音波照射後の前記分散水溶液に含浸させる含浸ステップと、含浸後の炭素繊維シートを乾燥させる乾燥ステップとを有する。これにより、カーボンナノチューブ本来の性質を引き出すことが可能となる。 A method for producing a sheet-like air electrode comprising a carbon fiber sheet having a film-like material containing carbon nanotubes on the surface according to the present invention comprises dissolving carbon nanotubes, carboxymethyl cellulose ammonium, ammonium hydrogen carbonate and glycerin in water. A raw material aqueous solution generating step to make a raw material aqueous solution, an ultrasonic irradiation step of irradiating the raw material aqueous solution with ultrasonic waves by an ultrasonic homogenizer to obtain a dispersed aqueous solution, and impregnating the dispersed aqueous solution after the ultrasonic irradiation with a carbon fiber sheet And an impregnation step for drying, and a drying step for drying the carbon fiber sheet after the impregnation. Thereby, it is possible to draw out the original properties of the carbon nanotube.
前記含浸ステップと乾燥ステップとを繰り返し（たとえば３度）行う。これにより、炭素繊維シートの表面にカーボンナノチューブの被覆（膜状物）を有効に設けることができる。 The impregnation step and the drying step are repeated (for example, three times). Thereby, it is possible to effectively provide a carbon nanotube coating (film-like material) on the surface of the carbon fiber sheet.
以上、説明したように、本発明によれば、カーボンナノチューブが本来有する性質を生かした、電極、電池、発電システムを構成することが可能になる。 As described above, according to the present invention, it is possible to configure an electrode, a battery, and a power generation system that take advantage of the properties inherent to carbon nanotubes.
以下、添付図面を参照しながら、本発明のナノ炭素材料の分散方法、ナノ炭素材料の分散液、ナノ炭素材料複合体を実現し、空気電極、酸電池、発電システムを実現するための最良の形態を詳細に説明する。
説明の順序を、そのタイトルを挙げて、目次とする。
≪カーボンナノチューブの分散、塗布、含浸、乾燥によるシート状空気電極の製造方法≫
≪シート状空気電極及びその変形加工≫
≪酸電池の正極及び正極活物質≫
≪酸電池の負極及び負極活物質≫
≪酸性電解質≫
≪酸性電解質溶液を循環させ、それを制御する≫
≪ジェル状の電解質及び発電停止、発電再開≫
≪積層によるスケーラビリティ≫
≪酸性電解質溶液を滴下又は噴霧することによる計画発電≫
BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, with reference to the attached drawings, the nanocarbon material dispersion method, the nanocarbon material dispersion, and the nanocarbon material composite of the present invention are realized. A form is demonstrated in detail.
The order of explanation is the table of contents, with the titles.
≪Method for producing sheet-like air electrode by dispersion, coating, impregnation and drying of carbon nanotube≫
≪Sheet air electrode and its deformation process≫
≪Acid battery positive electrode and positive electrode active material≫
≪Negative electrode and negative electrode active material of acid battery≫
≪Acid electrolyte≫
≪Circulate an acidic electrolyte solution and control it≫
≪Gel electrolyte and power generation stop, power generation resumed≫
≪Scalability by stacking≫
≪Planned power generation by dropping or spraying acidic electrolyte solution≫
≪カーボンナノチューブの分散、塗布、含浸、乾燥によるシート状空気電極の製造方法≫
本発明のナノ炭素材料の分散方法、ナノ炭素材料の分散液及びナノ炭素材料複合体の実施例として、ナノ炭素材料分散液及びナノ炭素材料複合体の具体的な製造方法とそれらが示す物性の試験結果について説明する。
≪Method for producing sheet-like air electrode by dispersion, coating, impregnation and drying of carbon nanotube≫
Examples of the nanocarbon material dispersion method, nanocarbon material dispersion, and nanocarbon material composite of the present invention include specific methods for producing the nanocarbon material dispersion and nanocarbon material composite and the physical properties thereof. The test results will be described.
＜分散液１、ＣＮＴ被覆炭素繊維１の調整＞
原材料水溶液の調製
カーボンナノチューブは、多層カーボンナノチューブ（Ｎａｎｏｃｙｌ社製、ＮＣ７０００（平均直径９．５ｎｍ、平均長さ１．５μｍ、比表面積２５０〜３００ｍ2／ｇ、炭素純度９０％））を用いた。
カルボキシメチルセルロースアンモニウムは、株式会社ファインクレイ製の製品名「ＣＭＣＡ２５」（カルボキシメチルセルロースアンモニウム２５％水和物）を用いた。
炭酸水素アンモニウムは、宇部興産株式会社製品（製品コード：ＩＯ−Ｂ１４−００１６）、純度９５．０％以上）を用いた。
３００ｍｌの水に、カーボンナノチューブ２ｇ、カルボキシメチルセルロースアンモニウム１０ｇ、炭酸水素アンモニウム１０ｇ、ポリオール（グリセリン）２ｇを溶解して原材料水溶液を得た。
ポリオール（多価アルコール）は、２個以上のヒドロキシ基−ＯＨをもった脂肪族化合物であり、エチレングリコール、プロピレングリコール、テトラメチレングリコール、ジエチレングリコール、ジプロピレングリコール、ポリエチレングリコール、グリセリン、ペンタエリスリトールなどであり、これらのうちのいずれでもよい。ここでは、グリセリンを用いた。
<Preparation of dispersion 1, CNT-coated carbon fiber 1>
Preparation of Raw Material Aqueous Solution Multi-walled carbon nanotubes (manufactured by Nanocyl, NC7000 (average diameter 9.5 nm, average length 1.5 μm, specific surface area 250-300 m 2 / g, carbon purity 90%)) were used.
As the carboxymethyl cellulose ammonium, a product name “CMCA25” (
As the ammonium hydrogen carbonate, Ube Industries, Ltd. product (product code: IO-B14-0016), purity 95.0% or more) was used.
In 300 ml of water, 2 g of carbon nanotubes, 10 g of carboxymethyl cellulose ammonium, 10 g of ammonium hydrogen carbonate, and 2 g of polyol (glycerin) were dissolved to obtain an aqueous raw material solution.
Polyol (polyhydric alcohol) is an aliphatic compound having two or more hydroxy groups —OH, such as ethylene glycol, propylene glycol, tetramethylene glycol, diethylene glycol, dipropylene glycol, polyethylene glycol, glycerin, pentaerythritol, etc. Yes, any of these may be used. Here, glycerin was used.
分散処理
この原材料水溶液に、超音波ホモジナイザー（三井電気精機株式会社製、型式：ＵＸ−６００、発振周波数２０±１ＫＨｚ、最大出力６００Ｗ）により２０分間超音波を照射して、カーボンナノチューブの分散水溶液を得た。
Dispersion treatment This raw material aqueous solution was irradiated with ultrasonic waves for 20 minutes by an ultrasonic homogenizer (Mitsui Denki Seiki Co., Ltd., model: UX-600,
炭素繊維への塗布・含浸及び乾燥処理
炭素繊維は、東レ株式会社の製品を用いた。
この炭素繊維を分散水溶液に含浸した後、１４０℃で３０分間焼付け処理を行い、分散水溶液の水分及びアンモニア成分を蒸発させて炭素繊維の表面を乾燥させた。この含浸及び焼付け処理を３回繰り返した。
以上の手順により、カーボンナノチューブを含有する薄膜を被覆された炭素繊維を得た。
Application / impregnation to carbon fiber and drying treatment The product of Toray Industries, Inc. was used for the carbon fiber.
After impregnating the carbon fiber with the aqueous dispersion, baking treatment was performed at 140 ° C. for 30 minutes to evaporate the water and ammonia components of the aqueous dispersion, thereby drying the surface of the carbon fiber. This impregnation and baking process was repeated three times.
By the above procedure, carbon fibers coated with a thin film containing carbon nanotubes were obtained.
電極としての比較例
以上の分散液１に対する比較例として、カーボンナノチューブの分散水溶液を塗布・含浸されていない炭素繊維（ＣＮＴ被覆炭素繊維１に用いたのと同じ製品）を用いて評価実験を行った。
Comparative Example as an Electrode As a comparative example for the dispersion 1 described above, an evaluation experiment was performed using a carbon fiber (the same product used for the CNT-coated carbon fiber 1) not coated / impregnated with a carbon nanotube dispersion aqueous solution. It was.
空気マグネシウム電池の電極として用いる。
実施例１と比較例の炭素繊維について、空気マグネシウム電池の空気極（正極）として用いて、幅２センチメートル、長さ５センチメートルのマグネシウム板を負極として用い、それと同等の大きさの炭素繊維を正極とし、塩化第二鉄を電解液として、炭素繊維に垂らす。そのときに開放電圧２ボルトで、どれだけのイニシャル電流が流れるかをテスターにより測定した。
マグネシウムは、権田金属工業株式会社の製品の「難燃性マグネシウム」を用いた。テスターは、共立電気計器社のAC/DCクランプ付デジタルマルチメーターを用いた。
比較例では、６６．４ミリアンペアのイニシャル電流を得られた。ＣＮＴ被覆炭素繊維１では、５３８．３ミリアンペアのイニシャル電流を得ることができた。
Used as an electrode for an air magnesium battery.
About the carbon fiber of Example 1 and a comparative example, it uses as an air electrode (positive electrode) of an air magnesium battery, uses a magnesium plate of width 2cm and length 5cm as a negative electrode, and carbon fiber of the magnitude | size equivalent to it Is used as a positive electrode, and ferric chloride is used as an electrolytic solution and hung on a carbon fiber. At that time, how much initial current flows with an open-circuit voltage of 2 volts was measured by a tester.
As the magnesium, “Flame-resistant magnesium” manufactured by Gonda Metal Industry Co., Ltd. was used. The tester used was a digital multimeter with an AC / DC clamp manufactured by Kyoritsu Electric Instruments.
In the comparative example, an initial current of 66.4 milliamperes was obtained. With the CNT-coated carbon fiber 1, an initial current of 538.3 milliamps could be obtained.
このように、ＣＮＴ被覆炭素繊維１は、比較例の炭素繊維に比べて、電流値が顕著に大きく、８倍以上の電流密度を達成できたことが明らかとなった。 Thus, it became clear that the CNT-coated carbon fiber 1 has a remarkably large current value as compared with the carbon fiber of the comparative example, and has achieved a current density of 8 times or more.
分散についての比較例
上記分散液１に対する比較例として、下記４通りの方法でカーボンナノチューブ分散液を作製した。
（Ａ）多層カーボンナノチューブ（上記同様）０．１ｇを水２０ｍｌに添加し、上記同様の超音波処理を行って得たカーボンナノチューブ分散液
（Ｂ）多層カーボンナノチューブ（上記同様）０．１ｇとカーボンブラック粉末（上記同様）０．０５ｇとを混合した粉体を、エタノール１６ｍｌと水４ｍｌとからなる溶媒に添加し、上記同様の超音波処理を行って得たカーボンナノチューブ分散液
（Ｃ）多層カーボンナノチューブ（上記同様）０．１ｇとグラファイト・ナノプレートレット（上記同様）０．０５ｇとを混合した粉体を、エタノール１６ｍｌと水４ｍｌとからなる溶媒に添加し、上記同様の超音波処理を行って得たカーボンナノチューブ分散液
（Ｄ）多層カーボンナノチューブ（上記同様）０．１ｇとカーボンブラック粉末（上記同様）０．０５ｇとグラファイト・ナノプレートレット（上記同様）０．０５ｇとを混合した粉体を、エタノール１６ｍｌと水４ｍｌとからなる溶媒に添加し、上記同様の超音波処理を行って得たカーボンナノチューブ分散液
Comparative Example for Dispersion As a comparative example for the dispersion liquid 1, a carbon nanotube dispersion liquid was prepared by the following four methods.
(A) Carbon nanotube dispersion obtained by adding 0.1 g of multi-walled carbon nanotubes (same as above) to 20 ml of water and subjecting to ultrasonic treatment similar to the above (B) 0.1 g of multi-walled carbon nanotubes (same as above) and carbon Carbon nanotube dispersion (C) multi-layer carbon obtained by adding 0.05 g of black powder (same as above) to a solvent consisting of 16 ml of ethanol and 4 ml of water and subjecting to ultrasonic treatment as described above Powder obtained by mixing 0.1 g of nanotubes (same as above) and 0.05 g of graphite nanoplatelets (same as above) is added to a solvent composed of 16 ml of ethanol and 4 ml of water, and subjected to the same ultrasonic treatment as above. Carbon nanotube dispersion (D) obtained in this way (0.1) multi-walled carbon nanotubes (same as above) and carbon black powder (top (Similar) A powder obtained by mixing 0.05 g and 0.05 g of graphite nanoplatelet (same as above) was added to a solvent composed of 16 ml of ethanol and 4 ml of water and subjected to the same ultrasonic treatment as above. Carbon nanotube dispersion
分散性の試験結果
上記の比較例によるカーボンナノチューブ分散液（Ａ）〜（Ｄ）と、本発明の分散液１よるカーボンナノチューブ分散液（Ｅ）とをほぼ同時に作製し、保存容器に密封保存して常温下で静置し、５日間の経過を観察した。
超音波処理直後の時点では、分散液（Ｂ）〜（Ｅ）は程よく分散されているが、特に分散液（Ｅ）の分散性が優れていることが確認される。
超音波処理直後２４時間経過した時点では、分散液（Ｂ）〜（Ｄ）の分散性が失われ、カーボンナノチューブの沈殿が見られる。一方、分散液（Ｅ）の分散性は保たれている。
超音波処理直後５日間経過した時点においても、分散液（Ｅ）は超音波処理直後と同等の分散性が保たれている。
Dispersibility test results The carbon nanotube dispersion liquids (A) to (D) according to the above comparative examples and the carbon nanotube dispersion liquid (E) according to the dispersion liquid 1 of the present invention were prepared almost simultaneously, and sealed in a storage container. The mixture was allowed to stand at room temperature and observed for 5 days.
At the time immediately after the ultrasonic treatment, the dispersions (B) to (E) are moderately dispersed, but it is confirmed that the dispersibility of the dispersion (E) is particularly excellent.
When 24 hours have passed immediately after the ultrasonic treatment, the dispersibility of the dispersions (B) to (D) is lost, and precipitation of carbon nanotubes is observed. On the other hand, the dispersibility of the dispersion liquid (E) is maintained.
Even when 5 days have passed immediately after the ultrasonic treatment, the dispersion (E) maintains the same dispersibility as that immediately after the ultrasonic treatment.
ナノ炭素材料複合体の作製
上記分散液１から乾燥処理して得られた粉体をＰＴＦＥ（ポリテトラフルオロエチレン）等のバインダーと混合し、熱プレス処理（２００℃、１０トン）して成形体を得た。この成形体は、電気抵抗率が０．３〜０．７Ω・ｃｍと顕著に優れた電気特性を示すものであった。
Production of nano-carbon material composite Powder obtained by drying from dispersion 1 is mixed with a binder such as PTFE (polytetrafluoroethylene) and subjected to hot press treatment (200 ° C., 10 tons) to form a molded body. Got. This molded article exhibited remarkably excellent electrical characteristics with an electrical resistivity of 0.3 to 0.7 Ω · cm.
この成形体の表面を走査型電子顕微鏡（株式会社日立ハイテクノロジーズ製、Ｓ−３０００Ｈ）で撮影した。倍率１５０００倍、倍率６０００倍で撮影したところ、成形体中でカーボンナノチューブが凝集せず分散しており、所々に空孔が形成された構造となっていることが分かった。 The surface of this molded body was photographed with a scanning electron microscope (manufactured by Hitachi High-Technologies Corporation, S-3000H). When the images were taken at a magnification of 15000 times and a magnification of 6000 times, it was found that the carbon nanotubes were not aggregated and dispersed in the molded body, and pores were formed in places.
以上、ナノ炭素材料の分散方法、ナノ炭素材料の分散液及びナノ炭素材料複合体について、具体的な実施の形態を示して説明したが、本発明はこれらに限定されるものではない。当業者であれば、本発明の要旨を逸脱しない範囲内において、原材料、試薬、処理条件、処理手順、測定条件、測定方法について様々な変更・改良を加えることが可能である。
たとえば、溶媒を、エタノール１６ｍｌ、水４ｍｌにドデシル硫酸ナトリウム（０．０５ｇ）を溶解して溶媒としたが、エタノール１５ｍｌ、水５ｍｌ、ドデシル硫酸ナトリウム０．０４〜０．０６ｇとしてもよい。
また、超音波照射時間を２０分としたが、１５分〜３０分としてもよい。
乾燥処理については、１４０℃で３０分間の焼付処理を３回繰り返したが、１２０℃〜１５０℃で、２０〜４０分間の焼付処理を２〜４回繰り返すこととしてもよい。
As mentioned above, although the specific embodiment was shown and demonstrated about the dispersion method of a nano carbon material, the dispersion liquid of a nano carbon material, and a nano carbon material composite_body | complex, this invention is not limited to these. A person skilled in the art can make various changes and improvements to the raw materials, reagents, processing conditions, processing procedures, measurement conditions, and measurement methods without departing from the scope of the present invention.
For example, although 16 ml of ethanol and 4 ml of water were dissolved in sodium dodecyl sulfate (0.05 g) as a solvent, the solvent was 15 ml of ethanol, 5 ml of water, and 0.04 to 0.06 g of sodium dodecyl sulfate.
Moreover, although the ultrasonic irradiation time is 20 minutes, it may be 15 minutes to 30 minutes.
About the drying process, although the baking process for 30 minutes at 140 degreeC was repeated 3 times, it is good also as repeating the baking process for 20 to 40 minutes at 120 to 150 degreeC 2-4 times.
≪シート状空気電極及びその変形加工≫
図１は、空気電極の基材となる炭素繊維シートの例を示す図である。図１(a)は、炭素繊維シートの一例について、斜視図で示したものであり、図１（b)は、炭素繊維シートの他の例について平面図を示したものである。
炭素繊維シートは、ポリアクリロニトリル繊維、ピッチ繊維、レーヨンなどの有機繊維を不活性雰囲気中で加熱して炭素以外の元素を脱離させることで製造される。９０％以上が炭素成分の繊維である。
本発明で上に述べたＣＮＴ被覆炭素繊維１では、東レ株式会社の製品を用いている。東レ株式会社の製品では、図１に示すものに比べて、さらに密に縦糸と横糸を整然と織り上げて、布状にしたものとなっている。
図１(a)で挙げた例のように、何本かをスキップして、織っているものでもよい。また、図１（b）で挙げた例のように、ゆるい織り方をしたものでもよい。
さらに、織物としていないもの、たとえば、不織布であってもかまわない。
≪Sheet air electrode and its deformation process≫
FIG. 1 is a diagram illustrating an example of a carbon fiber sheet serving as a base material for an air electrode. FIG. 1A is a perspective view of an example of a carbon fiber sheet, and FIG. 1B is a plan view of another example of the carbon fiber sheet.
The carbon fiber sheet is produced by heating organic fibers such as polyacrylonitrile fiber, pitch fiber, and rayon in an inert atmosphere to desorb elements other than carbon. 90% or more is a carbon component fiber.
In the CNT-coated carbon fiber 1 described above in the present invention, a product of Toray Industries, Inc. is used. The products of Toray Industries, Inc. are made by weaving warp yarns and weft yarns more densely than the one shown in FIG.
As in the example shown in FIG. 1 (a), some may be skipped and woven. Further, as shown in the example shown in FIG.
Further, it may be a non-woven fabric, for example, a non-woven fabric.
上述の分散液の調整をしたものに、超音波照射した後、図１に示すような炭素繊維シートを、その液に含浸し、焼付処理（乾燥）して、上述のＣＮＴ被覆炭素繊維を構成する。そして、これが、シート状空気電極１１となる。シート状空気電極１１のすくなくとも表面には、ＣＮＴ（カーボンナノチューブ）が、凝集阻止剤により、凝集が阻止された状態で、安定して分散された状態で、被覆膜を形成していると考えられる。
図２は、シート状空気電極（正極）１１がセパレータシート１２を介して負極１４と重なって、積層される様子を示す図である。セパレータシート１２は、たとえば不織布のような絶縁物からなり、正極と負極とが電気的にショートしないように設けられる。セパレータシート１２を介して、負極に電解質を供給する必要があるので、セパレータシート１２は、電解質を透過するものである。電池としての性能を高めるためには、正極と負極とは、できるだけ近づけることが望ましい。そのためには、セパレータシート１２は、薄いものであることが望ましい。
After irradiating the above-mentioned dispersion prepared with ultrasonic waves, a carbon fiber sheet as shown in FIG. 1 is impregnated in the liquid and baked (dried) to form the above-described CNT-coated carbon fiber. To do. This becomes the sheet-
FIG. 2 is a diagram illustrating a state in which the sheet-like air electrode (positive electrode) 11 is stacked so as to overlap the
シート状空気電極（正極）１１の基材は、炭素繊維シートであるので、その面積、寸法、形状の自由度が高い。また、セパレータシート１２もまた、不織布などで構成されるので、面積、寸法、形状の自由度が高い。一方、重ね合せる負極１４は、後述するように、金属であるので、炭素繊維シートや、不織布ほどではないが、折り曲げ加工や、変形がある程度可能である。したがって、負極の加工ができる範囲内で、正極１１、セパレータシート１２、正極１４を重ね合せた全体の面積、寸法、形状の自由度が決まる。
その自由度の範囲内で、変形加工が可能であるという特徴をこのシート状空気電極は有している。図３は、パイプに巻き付けて配置する酸電池を形成する場合の変形加工を示す図である。図３(a)は、パイプ15に巻き付けて、同心円状（同軸円筒状）に内側から、シート状空気電極１１、セパレータシート１２、負極１４と設けた例であり、図３(b)は、外側から、シート状空気電極１１、セパレータシート１２、負極１４と設けた例である。負極１４が溶滅したのちに、負極を新しいものと取り替える便宜のためには、負極１４が外側となることが望ましい。シート状空気電極に空気（酸素）を供給する便宜のためには、正極であるシート状空気電極１４を外側にするのが望ましい。この酸電池が置かれる環境の風通しのよさなどを配慮して、どちらを外側にするかが設計されることとなる。
シート状空気電極１１、セパレータシート１２、負極１４の形状は、円筒状としてもよいし、Ｃ字型の形状としてもよい。
パイプ１５を包み込む形状の酸電池を構成するのは、一例であって、酸電池を配置したい場所の空間形状の都合に合わせて、さまざまな形の酸電池をカスタマイズすることが可能である。たとえば、自動車の内部に電池を設けるにあたって、ボディー内のわずかのスペースに合うように電池を設計することができる。ウェアラブルコンピュータの電源として、人の身体に沿ってフィットする形の電池を設計することも可能となる。さらにいえば、救命胴衣などの衣服に合わせた電池設計も可能である。
Since the base material of the sheet-like air electrode (positive electrode) 11 is a carbon fiber sheet, the degree of freedom of its area, size, and shape is high. Moreover, since the
This sheet-like air electrode has a feature that deformation is possible within the range of the degree of freedom. FIG. 3 is a diagram showing a deformation process in the case of forming an acid battery wound around a pipe and arranged. FIG. 3 (a) is an example in which a sheet-
The shape of the sheet-
The configuration of the acid battery that encloses the
≪酸電池の正極及び正極活物質≫
本発明に係る酸電池の正極として機能するのが、シート状空気電極１１である。そして、正極活物質は、酸素である。さらに言えば、シート状空気電極１１が大気に触れている状態では、大気中の酸素が活物質であり、シート状空気電極１１が溶液（電解質溶液）中に浸っている状態では、当該溶液中の溶存酸素である。
酸電池は、酸により負極の金属を溶かす際に発電するという現象であるが、見方を変えれば、金属が燃える（腐食する、酸化する）という現象でもあり、正極から正極活物質である酸素を取り込んで金属酸化物を生成する際に発電する現象であるとみることもできる。
正極における反応は、
２Ｈ＋Ｏ2＋２ｅ-→２ＯＨ-
または
４Ｈ+Ｏ2＋４e-→２Ｈ2Ｏ
と表せる。
≪Acid battery positive electrode and positive electrode active material≫
The sheet-
The acid battery is a phenomenon in which electricity is generated when the metal of the negative electrode is dissolved by acid, but from a different perspective, it is also a phenomenon that the metal burns (corrodes and oxidizes), and oxygen that is the positive electrode active material is removed from the positive electrode. It can also be considered that this is a phenomenon of generating electricity when taking in and producing a metal oxide.
The reaction at the positive electrode is
2H + O 2 + 2e − → 2OH −
Or 4H + O 2 + 4e − → 2H 2 O
It can be expressed.
≪酸電池の負極及び負極活物質≫
負極は、マグネシウム、アルミニウム、亜鉛、鉄又は銅のうちの一つ又は二つ以上を含む金属からなる。純粋なマグネシウムは、燃えやすい（酸化しやすい）ので、激しい化学反応を起こしてしまい、扱いに不便である。したがって、難燃性マグネシウムが用いられる。権田金属工業株式会社が提供する「難燃性マグネシウム」を用いることができる。マグネシウムを主体として、カルシウム、アルミニウム、マンガン、珪素、亜鉛、銅、鉄などを含む合金として難燃性を実現したものである。負極として難燃性マグネシウムを用いる場合には、負極活物質は、主にマグネシウムであると考えられる。
負極における反応は、
２ＨＣｌ＋Ｍｇ→ＭｇＣｌ2＋Ｈ2＋２ｅ-
である。ここで、ＭｇＣｌ2は、水に溶けるので、流れていく。
≪Negative electrode and negative electrode active material of acid battery≫
The negative electrode is made of a metal containing one or more of magnesium, aluminum, zinc, iron or copper. Pure magnesium is flammable (it is easy to oxidize), which causes a violent chemical reaction and is inconvenient to handle. Therefore, flame retardant magnesium is used. “Flame retardant magnesium” provided by Gonda Metal Industry Co., Ltd. can be used. Flame retardant is realized as an alloy containing magnesium, calcium, aluminum, manganese, silicon, zinc, copper, iron and the like. When flame retardant magnesium is used as the negative electrode, the negative electrode active material is considered to be mainly magnesium.
The reaction at the negative electrode is
2HCl + Mg → MgCl 2 + H 2 + 2e −
It is. Here, MgCl 2 dissolves in water and flows.
≪酸性電解質≫
酸性電解質は、塩酸、硫酸などの酸の水溶液でもよいが、塩の水溶液で酸性となるものであってもよい。マグネシウムが負極活物質である場合に、塩化第二鉄水溶液を用いることができる。
酸性電解質を、負極に接触させることで、金属の腐食（酸化、エッチング）が生じて、発電がなされる。電解質を負極に接触させる方法は、大別すると、３つが考えられる。第一に、シート状空気電極１１、セパレータシート１２、負極１４を重ね合せたもの全体を電解質溶液に浸すことである。第二に、電解質溶液をジェル状にしたものをシートに含浸させて接触させることである。第三に、電解質溶液を、正極側（シート状空気電極側）から、滴下又は噴霧することである。
以下、これらの三つの場合のそれぞれについて、発電の開始、停止、再開をどのように制御するかを中心に説明する。
≪Acid electrolyte≫
The acidic electrolyte may be an aqueous solution of an acid such as hydrochloric acid or sulfuric acid, or may be acidic with an aqueous salt solution. When magnesium is the negative electrode active material, an aqueous ferric chloride solution can be used.
By bringing the acidic electrolyte into contact with the negative electrode, metal corrosion (oxidation and etching) occurs, and power is generated. There are three methods for bringing the electrolyte into contact with the negative electrode. The first is to immerse the entire sheet-
Hereinafter, each of these three cases will be described focusing on how to control the start, stop, and restart of power generation.
≪酸性電解質溶液を循環させ、それを制御する≫
セパレータシート１２が電解質を透過する。さらに、シート状空気電極１１を構成する炭素繊維シート、カーボンナノチューブ、ＣＭＣＡ（カルボキシメチルセルロースアンモニウム）などは、電解質透過性を有する。したがって、酸性電解質をシート状空気電極１１を介して、負極に到達せしめることが可能である。
このとき、電解質溶液が停滞しないように、ポンプなどで強制的に水流を作って循環させることが望ましい。第一に、生成した酸化物が化学反応を阻害しないように排除するためである。第二に、正極、セパレータ、負極という組合せを複数セット、積層する場合には、シート状空気電極の周辺部でのみ電解質や、酸化物の出入がなされることになるので、淀みなく流れることが有利だからである。第三に、正極活物質である溶存酸素が適切に動く必要があるためでもある。
≪Circulate an acidic electrolyte solution and control it≫
At this time, it is desirable to forcibly create a water flow with a pump or the like so that the electrolyte solution does not stagnate. First, the generated oxide is excluded so as not to inhibit the chemical reaction. Second, when multiple sets of positive electrodes, separators, and negative electrodes are stacked and stacked, electrolytes and oxides can flow in and out only at the periphery of the sheet-like air electrode, so it can flow without stagnation. Because it is advantageous. Third, it is because the dissolved oxygen which is a positive electrode active material needs to move appropriately.
図４は、電解質を循環させ、発電の開始、停止、再開を制御するシステムを示す図である。図４(a)に示す構成では、酸電池（発電システム）３０は、正極、セパレータシート、負極の組合せを５セット有するものである。隣り合うセットとの正極、負極間では、化学反応が起こらないように、絶縁される。
第１の電解質タンク３１の中に蓄えられた電解質溶液は、ポンプ４１によって酸電池（発電システム）３０内に流れ込む。また、酸電池（発電システム）３０内の電解質溶液は、ポンプ４２によって吸い上げられて第１の電解質タンク３１に戻る。これにより電解質の循環が実現する。循環することによって、電解質、反応生成物、溶存酸素は、酸電池（発電システム）３０内の正極と負極間の空間を淀みなく流れて、効率のよい発電を継続させることができる。
また、酸素曝気装置３３は、大気中の空気又は酸素を第一の電解質タンクに送り込んで、当該電解質溶液を空気又は酸素に曝（さら）す。これにより、電解質溶液内の溶存酸素が低下するのを防ぐ。
発電を停止したいときには、ポンプ４１を停止して酸電池（発電システム）３０への電解質溶液の供給を停止するとともに、ポンプ４２により電解質溶液をすべて吸い上げて回収する。これにより、電解質が負極に接触しなくなるので、発電が停止する。
FIG. 4 is a diagram showing a system that controls the start, stop, and restart of power generation by circulating an electrolyte. In the configuration shown in FIG. 4 (a), the acid battery (power generation system) 30 has five sets of combinations of a positive electrode, a separator sheet, and a negative electrode. Insulation is performed so that no chemical reaction occurs between the positive electrode and the negative electrode of the adjacent set.
The electrolyte solution stored in the
Further, the
When it is desired to stop the power generation, the
図４（a）の構成で、さらに早く発電を停止する方法としては、酸電池（発電システム）３０の底に栓（不図示）を設けて、その栓を開くとともに、上部に設けたガス抜き栓（不図示）を開くことで、一度に抜いてしまうこともできる。 In the configuration of FIG. 4 (a), as a method of stopping power generation even earlier, a plug (not shown) is provided at the bottom of the acid battery (power generation system) 30, the plug is opened, and the gas vent provided at the top is removed. By opening a stopper (not shown), it can be removed at once.
図４（b）の構成は、発電プラントと呼べるほどの大きな設備の場合に比較的適したシステムである。図４(b)では、図4(a)の構成に加えて、第２の電解質タンク３２、ポンプ４３，４４、窒素曝気装置３４を備えている。第２の電解質タンク３２内の電解質溶液は、窒素曝気装置３４の働きにより、たえず窒素にさらされており、溶存酸素がゼロに近い状態に保たれる。第２の電解質タンク３２の上部には、ガス抜き栓（不図示）が設けられており、溶液中から窒素により追い出された酸素、過剰に送り込まれた窒素が外に出ることができるように構成されている。
発電している際には、図４(a)と同様に、ポンプ４１、４２が働いて、溶存酸素が豊富な電解質溶液が第１の電解質タンクと酸電池（発電システム）３０との間を循環する。発電を停止する際には、ポンプ４１，４２を停止し、ポンプ４３，４４とを働かせて、第２の電解質タンク内の電解質溶液を酸電池（発電システム）３０内の電解質との間で循環させる。そして、それとともに窒素曝気措置３４を稼動させる。これにより、酸電池（発電システム）３０内の電解質溶液の溶存酸素は、徐々にゼロに近づき、やがて発電が停止する。
The configuration of FIG. 4B is a system that is relatively suitable for a large facility that can be called a power plant. In FIG. 4B, in addition to the configuration of FIG. 4A, a
During power generation, as in FIG. 4A, the
そのほかの方法としては、電解質溶液を回収して、水を送り込むことで、発電を停止するやりかたも考えられる。 As another method, it is conceivable to stop the power generation by collecting the electrolyte solution and feeding water.
≪ジェル状の電解質及び発電停止、発電再開≫
図５は、ジェルシートを用いて電解質を供給する場合に遮断シートを用いて、発電の開始、停止、再開を制御することを示す図である。
図５(a)においては、負極１４、セパレータシート１２、シート状空気電極１１、遮断シート２５、電解質ジェルシート２０と順に積層した例を示す。電解質ジェルシート２０は、ジェルを含むのに適した基材、たとえば不織布に電解質、ここでは塩化第二鉄をジェル状にしたものを含ませてなるシートである。遮断シート２５は、電解質を透過しないシートである。
図５(a)のように、遮断シート２５が配置されている状態では、電解質ジェルシート２０に含まれる電解質は、遮断シート２５を透過しないので、負極１４に到達しない。したがって、負極活物質の腐食（燃焼、酸化）は起こらないので、発電は開始しない。
遮断シート２５を取り除く（引き抜く、引き剥がす）こと、そして、電解質ジェルシート２０の電解質がシート状空気電極１１、セパレータシート１２を介して、負極１４に到達できるようにすることで、発電を開始する。電解質は、シート状空気電極１１、セパレータシート１２のいずれをも透過するからである。このとき、電解質ジェルシート２０と負極１４との距離が近づくように、押し付ける力を加えてもよい。
発電を停止するときには、遮断シート２５を電解質ジェルシート２０と負極１４との間のいずれかの位置に配置する。それにより、電解質が負極に供給されなくなって、負極活物質の腐食（燃焼、酸化）が停止する。
≪Gel electrolyte and power generation stop, power generation resumed≫
FIG. 5 is a diagram illustrating that the start, stop, and restart of power generation are controlled using a blocking sheet when an electrolyte is supplied using a gel sheet.
5A shows an example in which the
As shown in FIG. 5A, in the state where the blocking
Power generation is started by removing the blocking sheet 25 (withdrawing and peeling) and allowing the electrolyte of the
When power generation is stopped, the blocking
図５（b）は、負極１４、セパレータシート１２、遮断シート２５、電解質ジェルシート２０、シート状空気電極１１の順に配置した例である。電池の性能の見地からは、負極１４とシート状空気電極１１との間の距離は短いほうが望ましい。したがって、電解質ジェルシート２０を薄くすることが望ましいと考えられる。電解質ジェルシート２０が含浸する電解質が減るために発電が出来なくなる場合には、電解質ジェルシート２０を新しいものに取り替える。または、シート状空気電極１１を介して電解質ジェルシート２０に電解質を供給する。
発電開始、発電停止、発電再開についての遮断シート２５の機能は、図５(a)の場合と同様である。
FIG. 5B is an example in which the
The functions of the blocking
図６は、電解質ジェルシートを用いる場合に、ジェルシート自体を抜き差しすることで、発電の開始、停止、再開を制御することを示す図である。
図６(a)においては、負極１４、セパレータシート１２、シート状空気電極１１、電解質ジェルシート２０の順に積層配置しており、電解質ジェルシート２０の電解質は、この状態では、シート状空気電極１１、セパレータシート１２を介して負極１４に到達する。したがって、発電がなされる。
発電を停止するときには、電解質ジェルシート２０を引き抜く、または引き剥がす。
発電を再開するには、再度、電解質ジェルシート２０を図６(a)の位置に戻す。
FIG. 6 is a diagram showing that the start, stop, and restart of power generation are controlled by inserting and removing the gel sheet itself when the electrolyte gel sheet is used.
In FIG. 6A, the
When power generation is stopped, the
To resume power generation, the
図６(b)においては、負極１４、セパレータシート１２、電解質ジェルシート２０、シート状空気電極１１の順に積層配置している。
発電停止のために、電解質ジェルシート２０を引き抜く、あるいは引き剥がす。このとき、電解質ジェルシート２０を単独で引き剥がすかわりに、シート状空気電極１１と電解質ジェルシート２０とをいっしょに引き剥がしてもよい。
発電を再開するには、図６(b)の配置に戻す。
In FIG. 6B, the
In order to stop power generation, the
To resume power generation, the arrangement shown in FIG. 6B is restored.
≪積層によるスケーラビリティ≫
図４に示したように、負極１４、セパレータシート１２、シート状空気電極１１からなる組み合わせのセットを、複数組積層することが可能である。このとき、電気的に直列接続するようにすれば、電圧を高めることができる。並列接続すれば電流を高めることができる。
≪Scalability by stacking≫
As shown in FIG. 4, it is possible to stack a plurality of sets of combinations including the
≪酸性電解質溶液を滴下又は噴霧することによる計画発電≫
図７は、酸性電解質を正極側から滴下又は噴霧する場合の構成を示す図である。
図７(a)は、負極１４、セパレータ１２、シート状空気電極１１がこの順番で水平に積層配置されたものに対して、上から、すなわちシート状空気電極１１の側から電解質溶液滴下装置５０により、滴下する様子を示す。電解質溶液の滴下は、一定量の滴下を続けることができる。あるいは間欠的に所定時間、所定量の滴下をした後に、所定時間停止し、また再開するやりかたでもよい。この滴下により、電力の需要に見合う分だけの必要かつ十分な電解質溶液の供給が可能となる。
本発明に係る酸電池では、酸性電解質が、酸として機能して負極活物質を酸化させるので、供給した電解質溶液が尽きれば、発電は停止する。したがって、必要以上に電解質を供給せず、無駄な発電をしないですむというメリットがある。
≪Planned power generation by dropping or spraying acidic electrolyte solution≫
FIG. 7 is a diagram showing a configuration in the case where an acidic electrolyte is dropped or sprayed from the positive electrode side.
FIG. 7A shows an electrolyte
In the acid battery according to the present invention, since the acidic electrolyte functions as an acid to oxidize the negative electrode active material, power generation is stopped when the supplied electrolyte solution is exhausted. Therefore, there is an advantage that it is not necessary to supply unnecessary electrolyte and unnecessary power generation.
この電解質供給を計画的に制御するために制御装置６０を設ける。一日のうちの電力需要、一週間のうちの電力需要、一年のうちの電力需要などのピークがいつであるかを過去の統計データから割り出して計画的に発電する。
In order to systematically control the electrolyte supply, a
図７（b）は、電解質用益滴下装置５０の代わりに電解質溶液噴霧装置５５を設けた例である。滴下と噴霧とはほぼ同様の効果がある。噴霧の場合には、電解質とともに酸素（正極活物質）を同時に供給できるメリットがある。
また、噴霧の場合には、図７(c)に示すように、負極１４、セパレータ１２、シート状空気電極１１が、直立している場合にも利用可能である。
FIG. 7B shows an example in which an electrolyte
In the case of spraying, as shown in FIG. 7 (c), the
本発明に係る酸電池（発電システム）にあっては、負極活物質（たとえば、マグネシウム）、電解質（たとえば、塩化第二鉄）、正極活物質（酸素）の３つのうちのいずれかを制御することで、発電の開始、停止、再開のコントロールが可能である。したがって、制御装置による計画発電に適したシステム、プラントなどの設備を構築するのに適している。 In the acid battery (power generation system) according to the present invention, one of three of a negative electrode active material (for example, magnesium), an electrolyte (for example, ferric chloride), and a positive electrode active material (oxygen) is controlled. Therefore, it is possible to control the start, stop and restart of power generation. Therefore, it is suitable for constructing equipment such as a system and a plant suitable for planned power generation by the control device.
本発明の空気電極、酸電池、発電システムは、発電所における補助発電システム、製造設備、病院、船舶、など、さまざまな場所での非常用電源、または常用の電源として利用することができる。 The air electrode, acid battery, and power generation system of the present invention can be used as an emergency power source or a regular power source in various places such as an auxiliary power generation system in a power plant, a manufacturing facility, a hospital, and a ship.
１１ シート状空気電極
１２ セパレータシート
１４ 負極
１５ パイプ
２０ 電解質ジェルシート
２５ 遮断シート
３０ 酸電池（発電システム）
３１ 第１の電解質タンク
３２ 第２の電解質タンク
３３ 酸素曝気装置
３４ 窒素曝気装置
４１，４２，４３，４４ ポンプ
５０ 電解質溶液滴下装置
５５ 電解質溶液噴霧装置
６０ 制御装置
11 Sheet-
31
Claims (35)
マグネシウム、アルミニウム、亜鉛、鉄または銅を含む金属を負極とし、
前記正極と前記負極との間に酸性電解質が配されることを特徴とする酸電池。 A sheet-like air electrode made of a carbon fiber sheet having a film-like material containing carbon nanotubes on its surface is used as a positive electrode.
A metal containing magnesium, aluminum, zinc, iron or copper is used as the negative electrode,
An acid battery, wherein an acidic electrolyte is disposed between the positive electrode and the negative electrode.
前記負極を前記正極の面積、寸法、形状の変更に合わせて変形することを特徴とする請求項１２記載の酸電池。 The carbon fiber constituting the positive electrode can be changed in area, size, and shape in accordance with the spatial shape of the place to be arranged,
The acid battery according to claim 12, wherein the negative electrode is deformed in accordance with a change in the area, size, and shape of the positive electrode.
マグネシウム、アルミニウム、亜鉛、鉄または銅のうちの一つ又は二つ以上を含む金属を負極とし、
前記正極と前記負極との間に酸性電解質が配されてなる酸電池を
複数積層配置し、電気接続してなる発電システム。 A sheet-like air electrode having a film-like material containing carbon nanotubes on its surface is used as a positive electrode,
A metal containing one or more of magnesium, aluminum, zinc, iron or copper is used as the negative electrode,
A power generation system in which a plurality of acid batteries each having an acidic electrolyte disposed between the positive electrode and the negative electrode are stacked and electrically connected.
前記負極を前記正極の面積、寸法、形状の変更に合わせて変形することを特徴とする請求項２２記載の発電システム。 The carbon fiber sheet constituting the positive electrode can be changed in area, size, and shape according to the spatial shape of the place to be arranged,
23. The power generation system according to claim 22, wherein the negative electrode is deformed in accordance with a change in the area, size, and shape of the positive electrode.
マグネシウム、アルミニウム、亜鉛、鉄または銅のうちの一つ又は二つ以上を含む金属を、溶滅の際には新しい物と交換可能に設けて、負極とし、
前記正極と前記負極との間に、電気絶縁性を有し、電解質を透過するセパレータを設け、
前記正極、前記セパレータ、前記負極を積層配置した積層物に対して、前記正極の側から、発電に必要な量の酸性電解質を滴下又は噴霧して負極に到達させる酸性電解質供給装置と
を有する発電システム。 A sheet-like air electrode having a film-like material containing carbon nanotubes on its surface is used as a positive electrode,
A metal containing one or more of magnesium, aluminum, zinc, iron or copper is provided to be exchangeable with a new one at the time of melting, and is used as a negative electrode.
Between the positive electrode and the negative electrode is provided a separator having electrical insulation and permeating the electrolyte,
Power generation having an acidic electrolyte supply device that drops or sprays an amount of an acidic electrolyte necessary for power generation from the positive electrode side to the negative electrode with respect to a laminate in which the positive electrode, the separator, and the negative electrode are stacked. system.
カーボンナノチューブと、カルボキシメチルセルロースアンモニウムと炭酸水素アンモニウムとグリセリンとを水に溶解させて原材料水溶液とする原材料水溶液生成ステップと、
前記原材料水溶液に超音波ホモジナイザーにより超音波を照射して分散水溶液を得る超音波照射ステップと、
炭素繊維シートを前記超音波照射後の前記分散水溶液に含浸させる含浸ステップと、
含浸後の炭素繊維シートを乾燥させる乾燥ステップと
を有するシート状空気電極の製造方法。 A method for producing a sheet-like air electrode comprising a carbon fiber sheet having a film-like material containing carbon nanotubes on its surface,
A raw material aqueous solution generation step in which carbon nanotubes, carboxymethylcellulose ammonium, ammonium hydrogen carbonate, and glycerin are dissolved in water to form a raw material aqueous solution,
An ultrasonic irradiation step of irradiating the raw material aqueous solution with ultrasonic waves using an ultrasonic homogenizer to obtain a dispersed aqueous solution;
An impregnation step of impregnating the dispersed aqueous solution after the ultrasonic irradiation with a carbon fiber sheet;
The manufacturing method of a sheet-like air electrode which has a drying step which dries the carbon fiber sheet after an impregnation.