JP2018016902A - 紙用撥水剤、および、紙の製造方法 - Google Patents
紙用撥水剤、および、紙の製造方法 Download PDFInfo
- Publication number
- JP2018016902A JP2018016902A JP2016147795A JP2016147795A JP2018016902A JP 2018016902 A JP2018016902 A JP 2018016902A JP 2016147795 A JP2016147795 A JP 2016147795A JP 2016147795 A JP2016147795 A JP 2016147795A JP 2018016902 A JP2018016902 A JP 2018016902A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- water
- repellent
- water repellent
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
つぎに、本発明の紙用撥水剤の成分等の例について説明する。
本発明の紙用撥水剤は、前述のとおり、長鎖アルキル基を有するビニル系単量体を重合成分として含み、かつ、前記長鎖アルキル基を有するビニル系単量体のアルキル基の炭素数が14以上であるポリマー(以下「撥水ポリマー」という場合がある。)を含有することを特徴とする。前記ビニル単量体は、前記撥水ポリマーの主要重合成分であることが好ましい。本発明において、ポリマーの「重合成分」は、前記ポリマーの単量体単位であって、「主要重合成分」は、前記ポリマーを構成する単量体単位の全量に対して、例えば、50重量%以上、60重量%以上、70重量%以上、80重量%以上、または90重量%以上である単量体単位をいう。前記長鎖アルキル基を有するビニル系単量体としては、例えば、下記化学式(1)または(2)で表されるビニル系単量体が挙げられる。
本発明の紙用撥水剤は、前記撥水ポリマー以外の他の成分を適宜含んでいても良いし、含んでいなくても良い。前記他の成分は、特に限定されないが、例えば、以下のとおりである。
本発明の紙の製造方法は、前述のとおり、紙の表面に、前記本発明の紙用撥水剤により撥水加工処理することを特徴とする。これによって、前記本発明の紙用撥水剤により表面に撥水加工処理をした、本発明の紙を製造できる。また、本発明の紙の製造方法は、前述のとおり、例えば、前記撥水加工処理後の表面に印刷をしても良い。これによって、さらに、前記撥水加工処理後の表面に印刷をした紙を製造できる。
(1)撥水ポリマーの重合方法(溶液重合)
・合成例1
撹拌機、冷却管、窒素導入管および温度計を備えたフラスコに、ベヘニルアクリレート 100重量部、トルエン 100重量部を仕込んだ。反応系内の酸素を窒素で十分に置換し、次いで、前記混合物を70℃まで昇温した後、反応容器に少量のトルエンに溶解させたラジカル重合開始剤AIBN 0.3重量部を投入した。次いで75〜80℃の温度範囲で8時間重合反応を進行させた。反応終了後、室温まで冷却し、撥水ポリマーであるポリマーAを得た。
使用するモノマーを、下記表1に示すモノマー種類・比率に変更した以外は合成例1と同様の方法で調製し、重合物として、撥水ポリマーであるポリマーB〜Jをそれぞれ得た。
合成例1〜10で得られたポリマーA〜Jについて、重量平均分子量はウォーターズ社製の分析モジュールWaters e2695、検出器Waters 2414、データ処理Empower2 ソフトウェア(商品名)を用いて測定した。
・実施例1
加熱によって溶剤成分を除去した前記ポリマーAを9重量部、パラフィンワックス(商品名「パーバン1320」、エクソンモービル有限会社製)2重量部、石油樹脂(商品名「クイントンD−200」、日本ゼオン株式会社製13重量部、商品名「ハリタック4740」、ハリマ化成株式会社製6重量部)19重量部、混合脂肪酸(商品名「糠脂肪酸」、築野食品工業株式会社製)0.6部、乳化剤(商品名「ブラウノンSR−706」POEステアリルエーテル(EO=6モル)、青木油脂工業株式会社製)2.0部、48%水酸化カリウム水溶液1.3重量部、トリエタノールアミン1.3重量部を混合して90〜95℃に加温し均一に混合した。次に、あらかじめ沸騰させた温水64.8重量部を3g/minの流速で徐々に加えて転相乳化を20分間行なった後、室温まで冷却し、撥水剤(撥水剤組成物)を得た。
前記ポリマーAに代えて前記ポリマーB〜Hをそれぞれ用いた以外は、実施例1と同様の方法で乳化し撥水剤組成物を得た。
ポリマーAとパラフィンワックスを使用しない代わりに、ポリマーCを11重量部使用した以外は、実施例1と同様の方法で乳化し撥水剤組成物を得た。
ポリマーを使用せず、パラフィンワックスを11重量部使用した以外は、実施例1と同様の方法で乳化し撥水剤組成物を得た。
前記ポリマーAに代えて前記ポリマーJを用いた以外は、実施例1と同様の方法で乳化し撥水剤組成物を得た。
ポリマーDおよびパラフィンの配合量を変更した以外は、実施例4と同様の方法で乳化し撥水剤組成物を得た。
ポリマーD、パラフィンおよび石油樹脂の配合量を変更した以外は、実施例4と同様の方法で乳化し撥水剤組成物を得た。
(1)撥水剤を処理した試験片の作製方法
撥水剤処理量が0.2g/m2(=ライナー単位面積当たりの撥水剤固形分の重量)となるように、撥水剤を坪量280g/m2のライナー(段ボール)にガラス棒で塗工した後、循環乾燥器にて120℃で1分間乾燥し撥水ライナー(本発明の紙)を得た。
上記撥水処理試験片に黒色の水性フレキソインキ(商品名「FK−Flemio DF−260 黒」、サカタインクス株式会社製)の87.5%水溶液をマイヤーバーNo.12で塗工し、10秒後のインク塗工面に白色塗工紙を貼り合せ5kgの荷重で圧着し、試験片から剥がしたときの白色塗工紙面のインク汚れを目視で確認した。評価結果は、下記のとおり、○△×の三段階評価とした。
○:撥水加工処理していない試験片でのインク汚れ状態と同等(インク汚れが、ほとんどない)
△:撥水加工処理していない試験片でのインク汚れ状態よりも汚れている
×:撥水加工処理していない試験片でのインク汚れ状態よりも著しく汚れている
(1)撥水紙の製造方法
撥水剤処理量が0.2g/m2となるように、撥水剤を坪量280g/m2のライナーにガラス棒で塗工した後、循環乾燥器にて120℃、1分間で乾燥し撥水紙を得た。
上記方法で製造した撥水紙を、160℃に設定した循環乾燥器内で30分加熱処理し、その後、撥水性の評価試験に供した。これは、撥水加工処理した撥水ライナーを工業的に大量生産する場合、巻き取られて保管される際にロール内部に熱がこもりやすいので、その状態を再現するためである。前記加熱処理後、JAPAN TAPPI 紙パルプ試験方法 No.68:2000に規定される方法に準じて撥水度を測定した。具体的には、上記方法で作成した撥水紙を45°に傾斜させ、垂直方向に10mm離したところからイオン交換水を滴下し(1滴:約0.1ml)、流下の跡を観察した。撥水性は、下記表2の評価基準に従ってR0〜R10で評価した。R以降の数字が最も小さい撥水度(例;R0)が、最も撥水性が低く、R以降の数字が最も大きい撥水度(例;R10)が、最も撥水性が高い。R7以上を撥水性良好とする。
Claims (6)
- 長鎖アルキル基を有するビニル系単量体を重合成分として含むポリマーを含有し、かつ、前記ビニル系単量体の前記長鎖アルキル基の炭素数が14以上であることを特徴とする紙用撥水剤。
- 前記ポリマーにおける前記ビニル系単量体の構成割合が、前記ポリマーを構成する単量体単位の全量に対して80〜100重量%である、請求項1記載の紙用撥水剤。
- 前記ビニル系単量体が、アクリレートおよびメタクリレートの少なくとも一方を含む、請求項1または2記載の紙用撥水剤。
- 紙の表面に、請求項1から3のいずれか一項に記載の紙用撥水剤により撥水加工処理することを特徴とする、撥水加工処理された紙の製造方法。
- さらに、前記撥水加工処理後の表面に印刷をすることを特徴とする請求項4記載の製造方法。
- 前記紙が、板紙である請求項4または5記載の製造方法。