JP2017121779A - Thermal-insulating and moisture-permeable waterproof sheet and method for producing the same - Google Patents

Thermal-insulating and moisture-permeable waterproof sheet and method for producing the same Download PDF

Info

Publication number
JP2017121779A
JP2017121779A JP2016002700A JP2016002700A JP2017121779A JP 2017121779 A JP2017121779 A JP 2017121779A JP 2016002700 A JP2016002700 A JP 2016002700A JP 2016002700 A JP2016002700 A JP 2016002700A JP 2017121779 A JP2017121779 A JP 2017121779A
Authority
JP
Japan
Prior art keywords
moisture
layer
heat
permeable waterproof
permeable
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2016002700A
Other languages
Japanese (ja)
Inventor
敦実 星野
Atsumi Hoshino
敦実 星野
一浩 中江
Kazuhiro Nakae
一浩 中江
田中　俊也
Toshiya Tanaka
俊也 田中
嘉徳 西川
Yoshinori Nishikawa
嘉徳 西川
英之 藤村
Hideyuki Fujimura
英之 藤村
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ROOTARII KK
Fukuvi Chemical Industry Co Ltd
Chori Co Ltd
Original Assignee
ROOTARII KK
Fukuvi Chemical Industry Co Ltd
Chori Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ROOTARII KK, Fukuvi Chemical Industry Co Ltd, Chori Co Ltd filed Critical ROOTARII KK
Priority to JP2016002700A priority Critical patent/JP2017121779A/en
Publication of JP2017121779A publication Critical patent/JP2017121779A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide a thermal-insulating and moisture-permeable waterproof sheet which has thermal insulating property, moisture permeability and waterproofness, and also has weather resistance.SOLUTION: There is provided a thermal-insulating and moisture-permeable waterproof sheet 1 which includes a moisture-permeable waterproof laminate 10 having a non-woven fabric layer 11 and a porous polyolefin film layer 12, a thermal-insulating layer 20 formed on one surface of the moisture-permeable waterproof laminate 10, and a surface protective layer 30 that covers and protects the thermal-insulating layer 20, the thermal-insulating layer 20 contains a thermal-insulating agent and a binder resin, and is formed at such an area ratio that a coverage factor is 70-95% with respect to one surface of the moisture-permeable waterproof laminate 10.SELECTED DRAWING: Figure 1

Description

本発明は、遮熱性、透湿性及び防水性を有する遮熱透湿防水シート及びその製造方法に関する。   The present invention relates to a heat-insulating and moisture-permeable waterproof sheet having heat-insulating properties, moisture permeability, and waterproof properties and a method for producing the same.

住宅等の建築物においては、屋外からの熱線の透過と屋内への雨水の侵入を抑制しつつ、室内の湿気を屋外に透過させるために、遮熱性、透湿性及び防水性を備えた遮熱透湿防水シートを屋根下地及び外壁下地に設置することがある。
遮熱透湿防水シートとしては、例えば、透湿防水シートの一方の面に、金属粒子を含む遮熱層が部分的に設けられたシートが知られている（特許文献１）。 In buildings such as houses, heat insulation with heat insulation, moisture permeability and waterproofing is required to allow indoor moisture to permeate outdoors while suppressing the penetration of heat rays from the outside and the penetration of rainwater into the indoors. A moisture permeable waterproof sheet may be installed on the roof base and the outer wall base.
As a heat-insulating and moisture-permeable waterproof sheet, for example, a sheet in which a heat-insulating layer containing metal particles is partially provided on one surface of a moisture-permeable and waterproof sheet is known (Patent Document 1).

特開２０１１−８４９７０号公報JP 2011-84970 A

しかし、特許文献１に記載の遮熱透湿防水シートは、耐候性が低く、遮熱層が劣化する傾向にあった。
そこで、本発明は、遮熱性、透湿性及び防水性を有し、しかも耐候性が高い遮熱透湿防水シート及びその製造方法を提供することを目的とする。 However, the heat-insulating and moisture-permeable waterproof sheet described in Patent Document 1 has low weather resistance and the heat-insulating layer tends to deteriorate.
Then, an object of this invention is to provide the heat insulation moisture permeability waterproof sheet which has heat insulation, moisture permeability, and waterproofness, and also has high weather resistance, and its manufacturing method.

本発明の遮熱透湿防水シートは、不織布層及び多孔性ポリオレフィンフィルム層を有する透湿防水性積層体と、該透湿防水性積層体の一方の面に形成された遮熱層と、該遮熱層を被覆して保護する表面保護層とを備え、前記遮熱層は、遮熱剤及びバインダ樹脂を含有し、前記透湿防水性積層体の一方の面に対して被覆率７０〜９５％の面積割合で形成されており、波長２〜１４μｍにおける赤外線反射率の平均値が５０％以上、ＪＩＳ Ａ６１１１に従って測定した透湿抵抗値が０．１９ｍ２・ｓ・Ｐａ／μｇ以下である。
本発明の遮熱透湿防水シートにおいては、前記表面保護層が、アクリル樹脂又はウレタン樹脂を含有することが好ましい。
本発明の遮熱透湿防水シートの製造方法は、不織布層及び多孔性ポリオレフィンフィルム層を積層して透湿防水性積層体を作製する透湿防水性積層体作製工程と、前記透湿防水性積層体の一方の面に、遮熱剤及びバインダ樹脂を含有する遮熱層形成用インクを、前記透湿防水性積層体の一方の面に対して被覆率７０〜９５％の面積割合で印刷して遮熱層を形成する遮熱層形成工程と、前記遮熱層を、表面保護層形成用樹脂を含有する表面保護層により被覆する表面保護層被覆工程とを有する。
本発明の遮熱透湿防水シートの製造方法においては、前記表面保護層形成用樹脂が、アクリル樹脂又はウレタン樹脂を含有することが好ましい。 The heat-insulating and moisture-permeable waterproof sheet of the present invention includes a moisture-permeable and waterproof laminate having a nonwoven fabric layer and a porous polyolefin film layer, a heat-insulating layer formed on one surface of the moisture-permeable and waterproof laminate, And a surface protective layer that covers and protects the heat shield layer, the heat shield layer contains a heat shield and a binder resin, and has a coverage of 70 to one surface of the moisture-permeable waterproof laminate. It is formed with an area ratio of 95%, the average value of infrared reflectance at a wavelength of 2 to 14 μm is 50% or more, and the moisture permeability resistance value measured according to JIS A6111 is 0.19 m 2 · s · Pa / μg or less. .
In the heat insulation moisture-permeable waterproof sheet of this invention, it is preferable that the said surface protective layer contains an acrylic resin or a urethane resin.
The method for producing a heat-insulating and moisture-permeable waterproof sheet according to the present invention includes a moisture-permeable and waterproof laminate-producing process for producing a moisture-permeable and waterproof laminate by laminating a nonwoven fabric layer and a porous polyolefin film layer, and the moisture-permeable and waterproof property. On one surface of the laminate, a heat shielding layer forming ink containing a heat shield and a binder resin is printed at an area ratio of 70 to 95% with respect to one surface of the moisture-permeable and waterproof laminate. A thermal barrier layer forming step for forming a thermal barrier layer, and a surface protective layer coating step for coating the thermal barrier layer with a surface protective layer containing a surface protective layer forming resin.
In the manufacturing method of the heat-insulation moisture-permeable waterproof sheet of this invention, it is preferable that the said resin for surface protection layer contains an acrylic resin or a urethane resin.

本発明の遮熱透湿防水シートは、遮熱性、透湿性及び防水性を有し、しかも耐候性が高い。
本発明の遮熱透湿防水シートの製造方法によれば、遮熱性、透湿性及び防水性を有し、しかも耐候性が高い遮熱透湿防水シートを容易に製造できる。 The heat-insulating and moisture-permeable waterproof sheet of the present invention has heat-insulating properties, moisture-permeable properties and waterproof properties, and has high weather resistance.
According to the method for producing a heat-insulating and moisture-permeable waterproof sheet of the present invention, it is possible to easily produce a heat-insulating and moisture-permeable waterproof sheet having heat shielding properties, moisture permeability, and waterproof properties and high weather resistance.

実施形態の遮熱透湿防水シートを示す断面図である。It is sectional drawing which shows the heat insulation moisture-permeable waterproof sheet of embodiment.

本発明の遮熱透湿防水シートの一実施形態について説明する。
図１に示すように、本実施形態の遮熱透湿防水シート１は、不織布層１１及び多孔性ポリオレフィンフィルム層１２を有する透湿防水性積層体１０と、遮熱層２０と、表面保護層３０とを備える。
本実施形態では、多孔性ポリオレフィンフィルム層１２の露出面に遮熱層２０が形成され、その遮熱層２０を覆うように表面保護層３０が形成されている。
本実施形態の遮熱透湿防水シート１は、屋根や外壁に取り付けられる際、不織布層１１が屋内側に配置され、表面保護層３０が屋外側に配置される。 An embodiment of the heat-insulating and moisture-permeable waterproof sheet of the present invention will be described.
As shown in FIG. 1, a heat-permeable and moisture-permeable waterproof sheet 1 according to this embodiment includes a moisture-permeable and waterproof laminate 10 having a nonwoven fabric layer 11 and a porous polyolefin film layer 12, a heat-shielding layer 20, and a surface protective layer. 30.
In the present embodiment, the heat shield layer 20 is formed on the exposed surface of the porous polyolefin film layer 12, and the surface protective layer 30 is formed so as to cover the heat shield layer 20.
When the heat-insulating and moisture-permeable waterproof sheet 1 of the present embodiment is attached to a roof or an outer wall, the nonwoven fabric layer 11 is disposed on the indoor side, and the surface protective layer 30 is disposed on the outdoor side.

透湿防水性積層体１０を構成する不織布層１１は、遮熱透湿防水シート１の剛性及び破断強度を補強する補強材として機能するものである。
不織布層１１を構成する不織布の種類としては、特に制限はなく、例えば、スパンボンド不織布、メルトブロー不織布、ニードルパンチ不織布などが挙げられる。これらのなかでも、防水性がより高まることから、スパンボンド不織布またはメルトブロー不織布が好ましい。
不織布層１１を構成する繊維の材質としては特に制限はないが、価格と強度の点から、ポリエチレンテレフタレート、ポリエチレン、ポリプロピレン、ポリアミドが好ましい。
不織布層１１の目付量は１０〜８０ｇ／ｍ２であることが好ましく、２０〜５０ｇ／ｍ２であることがより好ましい。不織布層１１の目付量が前記下限値以上であれば、充分な補強効果が得られ、前記上限値以下であれば、より軽量化できる。 The nonwoven fabric layer 11 constituting the moisture-permeable and waterproof laminate 10 functions as a reinforcing material that reinforces the rigidity and breaking strength of the heat-insulating and moisture-permeable waterproof sheet 1.
There is no restriction | limiting in particular as a kind of nonwoven fabric which comprises the nonwoven fabric layer 11, For example, a spun bond nonwoven fabric, a melt blown nonwoven fabric, a needle punch nonwoven fabric, etc. are mentioned. Among these, a spunbond nonwoven fabric or a melt blown nonwoven fabric is preferable because the waterproofness is further improved.
Although there is no restriction | limiting in particular as a material of the fiber which comprises the nonwoven fabric layer 11, From the point of a price and intensity | strength, a polyethylene terephthalate, polyethylene, a polypropylene, and polyamide are preferable.
Preferably the basis weight of the nonwoven fabric layer 11 is 10 to 80 g / m 2, and more preferably 20 to 50 g / m 2. If the fabric weight of the nonwoven fabric layer 11 is more than the said lower limit, sufficient reinforcement effect will be acquired, and if it is below the said upper limit, it can be reduced in weight.

透湿防水性積層体１０を構成する多孔性ポリオレフィンフィルム層１２は、遮熱透湿防水シート１において防水性及び透湿性を発現させるために主要な役割を果たす層である。
多孔性ポリオレフィンフィルム層１２としては特に限定されないが、多孔性ポリエチレンフィルム又は多孔性ポリプロピレンフィルムから構成されるのが好ましい。さらには、透湿性をより高める点では、多孔性ポリオレフィンフィルム層１２は多孔性ポリエチレンフィルムにより構成することがより好ましい。
多孔性ポリオレフィンフィルム層１２の多孔性は、例えば無機粒子（炭酸カルシウム等）を含有することにより付与される。すなわち、例えば、多孔性ポリオレフィンフィルムを作製する際に、延伸性がないため破断点になりやすい無機粒子（炭酸カルシウム等）を含有させたフィルムを延伸させ、無機粒子の存在位置で微小な亀裂を生させることにより微小孔を形成することができる。このような微小孔の形成により防水性を有しつつ透湿性を付与することができる。レーザ回折・散乱法により測定した無機粒子の体積平均粒子は５μｍ以下であることが好ましい。
また、多孔性ポリオレフィンフィルム層１２に多孔性を付与する方法として、一軸延伸したポリオレフィンフィルムに、延伸方向に沿って多数の切り込みを入れた後、延伸方向に対して直交方向に延伸することにより、ポリオレフィンフィルムを、破断しない程度に裂けさせて開口させる方法が挙げられる。 The porous polyolefin film layer 12 constituting the moisture-permeable and waterproof laminate 10 is a layer that plays a major role in developing waterproofness and moisture permeability in the heat-insulating and moisture-permeable waterproof sheet 1.
Although it does not specifically limit as the porous polyolefin film layer 12, It is preferable to comprise from a porous polyethylene film or a porous polypropylene film. Furthermore, it is more preferable that the porous polyolefin film layer 12 is composed of a porous polyethylene film in terms of further improving moisture permeability.
The porosity of the porous polyolefin film layer 12 is imparted, for example, by containing inorganic particles (such as calcium carbonate). That is, for example, when a porous polyolefin film is produced, a film containing inorganic particles (calcium carbonate or the like) that tends to be a break point due to lack of stretchability is stretched, and minute cracks are formed at the positions where the inorganic particles are present. By making it grow, micropores can be formed. By forming such micropores, moisture permeability can be imparted while having waterproofness. It is preferable that the volume average particle of the inorganic particles measured by a laser diffraction / scattering method is 5 μm or less.
Further, as a method of imparting porosity to the porous polyolefin film layer 12, by making a number of cuts along the stretching direction in the uniaxially stretched polyolefin film, by stretching in a direction perpendicular to the stretching direction, A method of opening the polyolefin film by tearing it to such an extent that it does not break is mentioned.

多孔性ポリオレフィンフィルム層１２の目付量は１〜５０ｇ／ｍ２であることが好ましく、１０〜３０ｇ／ｍ２であることがより好ましい。多孔性ポリオレフィンフィルム層１２の目付量が前記下限値以上であれば、充分に高い防水性を確保でき、前記上限値以下であれば、充分に高い透湿性を確保できる。 Basis weight of the porous polyolefin film layer 12 is preferably from 1 to 50 g / m 2, and more preferably 10 to 30 g / m 2. If the basis weight of the porous polyolefin film layer 12 is not less than the above lower limit value, a sufficiently high waterproof property can be secured, and if it is not more than the above upper limit value, a sufficiently high moisture permeability can be secured.

多孔性ポリオレフィンフィルム層１２の透湿度は、３０００ｇ／（ｍ２・２４ｈｒ）以上であることが好ましい。ここで透湿度は、ＪＩＳ Ｌ１０９９の４．１のＡ法（繊維製品の透湿度試験方法）に準拠して測定される値である。多孔性ポリオレフィンフィルム層１２の透湿度が前記下限値以上であれば、遮熱透湿防水シート１の透湿性をより高めることができる。しかし、透湿度が高すぎると、防水性が低下するおそれがあるため、多孔性ポリオレフィンフィルム層１２の透湿度は１２０００ｇ／（ｍ２・２４ｈｒ）以下であることが好ましい。 The moisture permeability of the porous polyolefin film layer 12 is preferably 3000 g / (m 2 · 24 hr) or more. Here, the moisture permeability is a value measured in accordance with JIS L1099, 4.1, Method A (moisture permeability test method for textiles). If the water vapor transmission rate of the porous polyolefin film layer 12 is more than the said lower limit, the water vapor transmission property of the heat-insulation moisture-permeable waterproof sheet 1 can be improved more. However, if the moisture permeability is too high, the waterproof property may be lowered. Therefore, the moisture permeability of the porous polyolefin film layer 12 is preferably 12000 g / (m 2 · 24 hr) or less.

遮熱層２０は、赤外線を反射して遮熱する層であり、遮熱剤及びバインダ樹脂を含有する。
遮熱剤としては、アルミニウム粉等の金属粉、赤外線（波長２〜１４μｍ）の反射率が２０％以上の顔料が挙げられる。遮熱剤の含有量は、目的の遮熱性（波長２〜１４μｍにおける赤外線反射率の平均値が５０％以上、好ましくは５５％以上となる遮熱性）が得られるように適宜調整される。
アルミニウム粉は、遮熱性を高くできることから、鱗片状のアルミニウム粉が好ましい。鱗片状のアルミニウム粉としては、層の表面に偏在しやすいリーフィングタイプのものと、層中に均一に分散しやすいノンリーフィングタイプのものが挙げられる。遮熱性がより高くなる点では、リーフィングタイプのアルミニウム粉が好ましい。
また、アルミニウム粉は、レーザ回折・散乱法により測定した体積平均粒子径が１〜２０μｍであることが好ましく、５〜１５μｍであることがより好ましい。
また、アルミニウム粉は、遮熱性がより高くなることから、純度が９０質量％以上であることが好ましく、９５質量％以上であることがより好ましく、９９質量％以上であることがさらに好ましい。
バインダ樹脂としては、例えば、アクリル樹脂、ポリスチレン、ポリウレタン、ポリエステル、ポリ塩化ビニル等が挙げられる。遮熱性がより高くなる点では、バインダ樹脂の透明性が低いことが好ましい。
遮熱層２０に含まれる遮熱剤がアルミニウム粉、バインダ樹脂がアクリル樹脂である場合には、遮熱性を容易に確保しながら、遮熱層２０の材料費を低く抑えることできる。
アルミニウム粉とアクリル樹脂との質量比率（アルミニウム粉：アクリル樹脂）は２０：８０〜６０：４０であることが好ましく、３０：７０〜５０：５０であることがより好ましい。この範囲であると、充分に高い遮熱性を確保できると共に遮熱層２０におけるアルミニウム粉の脱落を防止できる。 The heat shield layer 20 is a layer that reflects infrared rays and shields heat, and contains a heat shield and a binder resin.
Examples of the heat shield include metal powders such as aluminum powder, and pigments having infrared (wavelength 2 to 14 μm) reflectance of 20% or more. The content of the heat-shielding agent is appropriately adjusted so as to obtain the desired heat-shielding property (the heat-shielding property that the average value of infrared reflectance at a wavelength of 2 to 14 μm is 50% or more, preferably 55% or more).
The aluminum powder is preferably a scaly aluminum powder because the heat shielding property can be increased. Examples of the scaly aluminum powder include a leafing type that tends to be unevenly distributed on the surface of the layer and a non-leafing type that tends to be uniformly dispersed in the layer. Leafing type aluminum powder is preferred from the viewpoint of higher heat shielding properties.
The aluminum powder preferably has a volume average particle diameter of 1 to 20 μm, more preferably 5 to 15 μm, measured by a laser diffraction / scattering method.
In addition, since the aluminum powder has higher heat shielding properties, the purity is preferably 90% by mass or more, more preferably 95% by mass or more, and further preferably 99% by mass or more.
Examples of the binder resin include acrylic resin, polystyrene, polyurethane, polyester, and polyvinyl chloride. It is preferable that the transparency of the binder resin is low in terms of higher heat shielding properties.
When the heat shield contained in the heat shield layer 20 is aluminum powder and the binder resin is an acrylic resin, the material cost of the heat shield layer 20 can be kept low while easily ensuring the heat shield.
The mass ratio of aluminum powder to acrylic resin (aluminum powder: acrylic resin) is preferably 20:80 to 60:40, and more preferably 30:70 to 50:50. Within this range, it is possible to ensure a sufficiently high heat shielding property and prevent the aluminum powder from falling off in the heat shielding layer 20.

遮熱層２０は、透湿防水性積層体１０の一方の面の面積を１００％とした際、被覆率７０〜９５％の面積割合で形成されている（すなわち、透湿防水性積層体１０の一方の面のうち５〜３０％には遮熱層２０が形成されていない。）。遮熱層２０の被覆率が前記下限値未満であると、遮熱性を確保できないことがあり、前記上限値を超えると、透湿性を確保できないことがある。前記被覆率は、８０〜９０％であることが好ましい。
透湿防水性積層体１０の表面において、遮熱層２０は均一に形成されていることが好ましい。例えば、透湿防水性積層体１０の表面を５ｃｍ四方の領域に分割した際、各領域において、遮熱層２０が被覆率７０〜９５％の面積割合で形成されていることが好ましく、被覆率８０〜９０％の面積割合で形成されていることが好ましい。 The heat shielding layer 20 is formed with an area ratio of 70 to 95% when the area of one surface of the moisture permeable waterproof laminate 10 is 100% (that is, the moisture permeable waterproof laminate 10). The thermal barrier layer 20 is not formed on 5% to 30% of the one surface. When the coverage of the heat-insulating layer 20 is less than the lower limit value, heat shielding properties may not be ensured, and when the upper limit value is exceeded, moisture permeability may not be ensured. The coverage is preferably 80 to 90%.
It is preferable that the heat shielding layer 20 is formed uniformly on the surface of the moisture permeable waterproof laminate 10. For example, when the surface of the moisture-permeable and waterproof laminate 10 is divided into 5 cm square regions, the heat shielding layer 20 is preferably formed in an area ratio of 70 to 95% in each region. It is preferable to be formed with an area ratio of 80 to 90%.

表面保護層３０は、遮熱層２０を被覆して保護することにより耐候性を向上させる層である。表面保護層３０は、図１のように、遮熱層２０だけでなく、遮熱層２０が形成されていない部分も被覆してもよいし、遮熱層２０のみを選択的に被覆してもよい。
また、表面保護層３０は、表面保護層形成用樹脂から形成される。表面保護層形成用樹脂としては、アクリル樹脂、ウレタン樹脂、ポリエステル、ポリエチレン、ポリプロピレン、ポリスチレン等の各種熱可塑性樹脂を用いることができる。これら熱可塑性樹脂は１種を単独で使用してもよいし、２種以上を併用してもよい。前記表面保護層形成用樹脂のなかでも、耐候性をより向上させやすいことから、アクリル樹脂又はウレタン樹脂を含有することが好ましい。
表面保護層３０の目付量は、０．０５〜１．０ｇ／ｍ２であることが好ましい。表面保護層３０の目付量が前記下限値以上であれば、遮熱層２０を充分に保護でき、前記上限値以下であれば、透湿性を充分に確保できる。
表面保護層３０の厚さは、１０〜１０００ｎｍであることが好ましい。表面保護層３０の厚さが前記下限値以上であれば、遮熱層２０を充分に保護でき、前記上限値以下であれば、透湿性を充分に確保できる。 The surface protective layer 30 is a layer that improves the weather resistance by covering and protecting the thermal barrier layer 20. As shown in FIG. 1, the surface protective layer 30 may cover not only the heat shield layer 20 but also a portion where the heat shield layer 20 is not formed, or selectively coat only the heat shield layer 20. Also good.
The surface protective layer 30 is formed from a resin for forming a surface protective layer. As the resin for forming the surface protective layer, various thermoplastic resins such as acrylic resin, urethane resin, polyester, polyethylene, polypropylene, and polystyrene can be used. These thermoplastic resins may be used individually by 1 type, and may use 2 or more types together. Among the resins for forming the surface protective layer, it is preferable to contain an acrylic resin or a urethane resin because weather resistance is easily improved.
The basis weight of the surface protective layer 30 is preferably 0.05 to 1.0 g / m 2 . When the basis weight of the surface protective layer 30 is equal to or greater than the lower limit, the heat shield layer 20 can be sufficiently protected, and when it is equal to or smaller than the upper limit, moisture permeability can be sufficiently secured.
The thickness of the surface protective layer 30 is preferably 10 to 1000 nm. If the thickness of the surface protective layer 30 is equal to or greater than the lower limit value, the heat shield layer 20 can be sufficiently protected, and if the thickness is equal to or smaller than the upper limit value, moisture permeability can be sufficiently secured.

上記遮熱透湿防水シート１は、透湿防水性積層体作製工程と遮熱層形成工程と表面保護層被覆工程とを有する製造方法により製造される。   The said heat-permeable moisture-permeable waterproof sheet 1 is manufactured with the manufacturing method which has a moisture-permeable waterproof laminated body preparation process, a heat-shielding layer formation process, and a surface protective layer coating process.

透湿防水性積層体作製工程は、不織布層１１及び多孔性ポリオレフィンフィルム層１２を積層して透湿防水性積層体１０を作製する工程である。
不織布層１１及び多孔性ポリオレフィンフィルム層１２との積層では、接着剤を用いてもよい。
接着剤として用いられるものとしては、例えば、ポリエチレン樹脂等のオレフィン樹脂、エチレン−酢酸ビニル共重合体樹脂、ポリウレタン樹脂、ポリアミド樹脂のホットメルト系接着剤、アクリル樹脂、酢酸ビニル樹脂、又は、ポリビニルアルコールのエマルジョン系接着剤等が挙げられる。
接着剤の塗工は、スプレーを用いてもよいし、コーターを用いてもよい。 The moisture permeable waterproof laminate manufacturing step is a step of manufacturing the moisture permeable waterproof laminate 10 by laminating the nonwoven fabric layer 11 and the porous polyolefin film layer 12.
An adhesive may be used in the lamination with the nonwoven fabric layer 11 and the porous polyolefin film layer 12.
Examples of the adhesive used include olefin resin such as polyethylene resin, ethylene-vinyl acetate copolymer resin, polyurethane resin, polyamide resin hot melt adhesive, acrylic resin, vinyl acetate resin, or polyvinyl alcohol. And emulsion type adhesives.
The adhesive may be applied using a spray or a coater.

遮熱層形成工程は、前記透湿防水性積層体の一方の面に、遮熱剤及びバインダ樹脂を含有する遮熱層形成用インクを印刷して遮熱層２０を形成する工程である。本実施形態では、多孔性ポリオレフィンフィルム層１２の露出面に遮熱層２０を形成する。
遮熱層形成用インクを印刷する方法としては、グラビア印刷、オフセット印刷、フレキソ印刷、スクリーン印刷等を適用することができ、簡便に遮熱層２０を形成できる点では、グラビア印刷又はオフセット印刷が好ましい。
グラビア印刷又はオフセット印刷を適用する場合に、遮熱層２０の被覆率を調整する方法としては、例えば、グラビア印刷版の凹部面積率を調整する方法、オフセット印刷版の網点面積率を調整する方法等が挙げられる。 The thermal barrier layer forming step is a step of forming the thermal barrier layer 20 by printing the thermal barrier layer forming ink containing the thermal barrier agent and the binder resin on one surface of the moisture permeable waterproof laminate. In the present embodiment, the heat shield layer 20 is formed on the exposed surface of the porous polyolefin film layer 12.
As a method for printing the heat shielding layer forming ink, gravure printing, offset printing, flexographic printing, screen printing, etc. can be applied, and gravure printing or offset printing is used in that the heat shielding layer 20 can be easily formed. preferable.
In the case of applying gravure printing or offset printing, as a method for adjusting the coverage of the thermal barrier layer 20, for example, a method of adjusting the concave area ratio of the gravure printing plate, or adjusting the dot area ratio of the offset printing plate Methods and the like.

表面保護層被覆工程は、遮熱層２０を表面保護層３０により被覆する工程である。
遮熱層２０を表面保護層３０により被覆する方法としては、例えば、表面保護層形成用樹脂を含む表面保護層形成用塗料を、透湿防水性積層体１０の、遮熱層２０が形成された側の面に塗布して表面保護層３０を形成する方法が挙げられる。
また、遮熱層２０を表面保護層３０により被覆する他の方法としては、例えば、表面保護層形成用樹脂を含む表面保護層形成用塗料を、離型フィルムの片面に塗布して表面保護層３０を形成し、該表面保護層３０を離型フィルムから剥離し、透湿防水性積層体１０の、遮熱層２０が形成された側の面に貼合する方法が挙げられる。 The surface protective layer coating step is a step of covering the heat shield layer 20 with the surface protective layer 30.
As a method of covering the heat shield layer 20 with the surface protective layer 30, for example, the heat shield layer 20 of the moisture permeable waterproof laminate 10 is formed by using a surface protective layer forming paint containing a resin for forming the surface protective layer. The method of apply | coating to the surface of the other side and forming the surface protective layer 30 is mentioned.
Further, as another method of coating the heat shield layer 20 with the surface protective layer 30, for example, a surface protective layer-forming coating material containing a surface protective layer-forming resin is applied to one surface of the release film to form the surface protective layer. 30 is formed, and the surface protective layer 30 is peeled from the release film and bonded to the surface of the moisture permeable waterproof laminate 10 on the side where the heat shielding layer 20 is formed.

以上説明した遮熱透湿防水シート１では、アルミニウム層の代わりに、遮熱剤及びバインダ樹脂を含む遮熱層２０によって遮熱性を発揮している。例えば、分光光度計等の反射率測定装置を用いて測定した、波長２〜１４μｍの赤外線の反射率を５０％以上、特に５５％以上にできる。なお、反射率が高すぎると、他の性能が低下するおそれがあるから、反射率の平均値の上限値は、７０％とすることが好ましい。
アルミニウム層の代わりに遮熱層２０によって遮熱性を得ることにより、コストを低めに抑えることができる。
また、遮熱透湿防水シート１では、多孔性ポリオレフィンフィルム層１２を備えるため、防水性及び透湿性の両方を向上させることができる。具体的には、ＪＩＳ Ａ６１１１：２００４で示される透湿防水シートの透湿性及び防水性を容易に満足させることができる。例えば、ＪＩＳ Ａ６１１１における遮熱透湿防水シート１全体の透湿抵抗値を容易に０．１９ｍ２・ｓ・Ｐａ／μｇ以下となる。この透湿抵抗にするためには、遮熱層２０が設けられている部分の透湿抵抗が０．２６〜０．３０ｍ２・ｓ・Ｐａ／μｇであることが好ましく、遮熱層２０が設けられていない部分の透湿抵抗が０．０５〜０．１２ｍ２・ｓ・Ｐａ／μｇであることが好ましい。 In the heat-insulating and moisture-permeable waterproof sheet 1 described above, the heat-insulating property is exhibited by the heat-insulating layer 20 containing a heat-insulating agent and a binder resin instead of the aluminum layer. For example, the reflectance of infrared rays having a wavelength of 2 to 14 μm, measured using a reflectance measuring device such as a spectrophotometer, can be 50% or more, particularly 55% or more. If the reflectance is too high, other performance may be deteriorated, so the upper limit of the average value of the reflectance is preferably 70%.
By obtaining a heat shielding property by the heat shielding layer 20 instead of the aluminum layer, the cost can be kept low.
Moreover, since the heat-insulating and moisture-permeable waterproof sheet 1 includes the porous polyolefin film layer 12, both waterproofness and moisture permeability can be improved. Specifically, the moisture permeability and waterproofness of the moisture permeable waterproof sheet shown in JIS A6111: 2004 can be easily satisfied. For example, the moisture permeability resistance value of the entire heat-insulating and moisture-permeable waterproof sheet 1 in JIS A6111 is easily 0.19 m 2 · s · Pa / μg or less. In order to achieve this moisture resistance, the moisture permeability resistance of the portion where the heat shielding layer 20 is provided is preferably 0.26 to 0.30 m 2 · s · Pa / μg, It is preferable that the moisture permeability resistance of the portion not provided is 0.05 to 0.12 m 2 · s · Pa / μg.

なお、本発明の遮熱透湿防水シートは、上記実施形態のものに限定されない。
例えば、上記実施形態では、多孔性ポリオレフィンフィルム層の露出面に遮熱層が形成されていたが、不織布層の露出面に遮熱層が形成されてもよい。 In addition, the heat insulation moisture-permeable waterproof sheet of this invention is not limited to the thing of the said embodiment.
For example, in the above embodiment, the heat shielding layer is formed on the exposed surface of the porous polyolefin film layer, but the heat shielding layer may be formed on the exposed surface of the nonwoven fabric layer.

（比較例１）
不織布層と多孔性ポリオレフィンフィルム層とを、接着剤を用いて貼合して、透湿防水性積層体を得た。ここで、不織布層としては、ポリエチレンテレフタレート繊維の不織布であって、目付量が４５ｇ／ｍ２のものを用いた。多孔性ポリオレフィンフィルム層としては、目付量２７ｇ／ｍ２で、ＪＩＳ Ｌ１０９９の４．１のＡ法（繊維製品の透湿度試験方法）に準拠して測定される値が１００００ｇ／（ｍ２・２４ｈｒ）のものを用いた。
透湿防水性積層体を構成する多孔性ポリオレフィンフィルム層の露出面に、アルミニウム粉及びアクリル樹脂を含む遮熱層形成用インク（リーフィングタイプアルミニウム粉（体積平均粒子径１３μｍ、純度９９質量％以上）とアクリル酸アルキルエステル共重合体とを含む。）を、被覆率９５％になるようにグラビア印刷して、遮熱層を形成した。これにより、遮熱透湿防水シートを得た。 (Comparative Example 1)
The nonwoven fabric layer and the porous polyolefin film layer were bonded using an adhesive to obtain a moisture-permeable and waterproof laminate. Here, as the nonwoven fabric layer, a nonwoven fabric of polyethylene terephthalate fiber having a basis weight of 45 g / m 2 was used. The porous polyolefin film layer has a basis weight of 27 g / m 2 and a value measured according to JIS L1099 4.1 method A (moisture permeability test method for textiles) of 10,000 g / (m 2 · 24 hr. ) Was used.
Heat-shielding layer forming ink containing aluminum powder and acrylic resin on the exposed surface of the porous polyolefin film layer constituting the moisture-permeable waterproof laminate (leafing type aluminum powder (volume average particle diameter 13 μm, purity 99% by mass or more) And an acrylic acid alkyl ester copolymer) were subjected to gravure printing so that the coverage was 95%, thereby forming a heat shielding layer. This obtained the heat-insulation moisture-permeable waterproof sheet.

（比較例２〜４）
遮熱層形成用インクを、表１に示す被覆率になるようにグラビア印刷した以外は実施例１と同様にして遮熱透湿防水シートを得た。 (Comparative Examples 2 to 4)
A heat and moisture permeable waterproof sheet was obtained in the same manner as in Example 1 except that the heat shielding layer forming ink was subjected to gravure printing so as to have the coverage shown in Table 1.

（比較例５）
遮熱層形成用インクを、被覆率９８％になるようにグラビア印刷して遮熱層を形成し、アクリル系の表面保護層形成用塗料（アクリル酸アルキルエステル共重合体を含む。）を目付量０．１０ｇ／ｍ２となるように塗布して表面保護層を形成した以外は比較例１と同様にして遮熱透湿防水シートを得た。 (Comparative Example 5)
A thermal barrier layer is formed by gravure printing the thermal barrier layer forming ink so that the coverage is 98%, and an acrylic surface protective layer-forming coating material (including an alkyl acrylate copolymer) is used. A heat-insulating and moisture-permeable waterproof sheet was obtained in the same manner as in Comparative Example 1 except that the surface protective layer was formed by coating so that the amount was 0.10 g / m 2 .

（比較例６）
遮熱層形成用インクを、被覆率６５％になるようにグラビア印刷して遮熱層を形成し、比較例５と同様のアクリル系の表面保護層形成用塗料を目付量０．１５ｇ／ｍ２となるように塗布して表面保護層を形成した以外は比較例５と同様にして遮熱透湿防水シートを得た。 (Comparative Example 6)
A thermal barrier layer is formed by gravure printing the thermal barrier layer forming ink so that the coverage is 65%, and an acrylic surface protective layer forming coating material similar to Comparative Example 5 has a basis weight of 0.15 g / m. A heat-permeable and moisture-permeable waterproof sheet was obtained in the same manner as in Comparative Example 5 except that the surface protective layer was formed by coating so as to be 2 .

（実施例１）
比較例３における遮熱透湿防水シートの、遮熱層が形成された側の面に、ウレタン系の表面保護層形成用塗料（日本曹達株式会社チタボンドＴ−１２５、ウレタンプレポリマーと２，４−トリレンジイソシアネートと４，４’−ジフェニルメタンジイソシアネートを含む。）を、目付量０．１５ｇ／ｍ２となるように塗布し、乾燥させて、表面保護層を形成した。これにより、表面保護層付きの遮熱透湿防水シートを得た。 Example 1
On the surface of the heat-insulating and moisture-permeable waterproof sheet in Comparative Example 3 on which the heat-insulating layer was formed, a urethane-based surface protective layer-forming paint (Nippon Soda Co., Ltd., Chitabond T-125, urethane prepolymer and 2,4 -Tolylene diisocyanate and 4,4′-diphenylmethane diisocyanate) were applied so as to have a basis weight of 0.15 g / m 2 and dried to form a surface protective layer. This obtained the heat-insulation moisture-permeable waterproof sheet with a surface protective layer.

（実施例２）
比較例３における遮熱透湿防水シートの、遮熱層が形成された側の面に、実施例１と同様のウレタン系の表面保護層形成用塗料を、目付量０．０７５ｇ／ｍ２となるように塗布し、乾燥させて、表面保護層を形成した。これにより、表面保護層付きの遮熱透湿防水シートを得た。 (Example 2)
On the surface of the heat-insulating and moisture-permeable waterproof sheet in Comparative Example 3 on which the heat-insulating layer is formed, the same urethane-based surface protective layer-forming coating material as in Example 1 has a basis weight of 0.075 g / m 2 . This was applied and dried to form a surface protective layer. This obtained the heat-insulation moisture-permeable waterproof sheet with a surface protective layer.

（実施例３）
比較例４における遮熱透湿防水シートの、遮熱層が形成された側の面に、実施例１と同様のウレタン系の表面保護層形成用塗料を、目付量０．１５ｇ／ｍ２となるように塗布し、乾燥させて、表面保護層を形成した。これにより、表面保護層付きの遮熱透湿防水シートを得た。 (Example 3)
On the surface of the heat-insulating and moisture-permeable waterproof sheet in Comparative Example 4 on the side where the heat-insulating layer was formed, the same urethane-based surface protective layer-forming coating material as in Example 1 had a basis weight of 0.15 g / m 2 . This was applied and dried to form a surface protective layer. This obtained the heat-insulation moisture-permeable waterproof sheet with a surface protective layer.

（実施例４）
比較例３における遮熱透湿防水シートの、遮熱層が形成された側の面に、比較例５と同様のアクリル系の表面保護層形成用塗料を、目付量０．１５ｇ／ｍ２となるように塗布し、乾燥させて、表面保護層を形成した。これにより、表面保護層付きの遮熱透湿防水シートを得た。 Example 4
On the surface of the heat-insulating and moisture-permeable waterproof sheet in Comparative Example 3 on which the heat-insulating layer is formed, an acrylic surface protective layer-forming coating material similar to that in Comparative Example 5 has a basis weight of 0.15 g / m 2 . This was applied and dried to form a surface protective layer. This obtained the heat-insulation moisture-permeable waterproof sheet with a surface protective layer.

（実施例５）
比較例３における遮熱透湿防水シートの、遮熱層が形成された側の面に、比較例５と同様のアクリル系の表面保護層形成用塗料を、目付量０．０７５ｇ／ｍ２となるように塗布し、乾燥させて、表面保護層を形成した。これにより、表面保護層付きの遮熱透湿防水シートを得た。 (Example 5)
On the surface of the heat-insulating and moisture-permeable waterproof sheet in Comparative Example 3 on which the heat-insulating layer is formed, an acrylic surface protective layer-forming coating material similar to that in Comparative Example 5 is applied with a basis weight of 0.075 g / m 2 . This was applied and dried to form a surface protective layer. This obtained the heat-insulation moisture-permeable waterproof sheet with a surface protective layer.

（実施例６）
比較例４における遮熱透湿防水シートの、遮熱層が形成された側の面に、比較例５と同様のアクリル系の表面保護層形成用塗料を、目付量０．１５ｇ／ｍ２となるように塗布し、乾燥させて、表面保護層を形成した。これにより、表面保護層付きの遮熱透湿防水シートを得た。 (Example 6)
On the surface of the heat-insulating and moisture-permeable waterproof sheet in Comparative Example 4 on the side on which the heat-insulating layer was formed, an acrylic surface protective layer-forming coating material similar to that in Comparative Example 5 was applied with a basis weight of 0.15 g / m 2 . This was applied and dried to form a surface protective layer. This obtained the heat-insulation moisture-permeable waterproof sheet with a surface protective layer.

（実施例７〜９）
遮熱層形成用インクを、表１に示す被覆率になるようにグラビア印刷して遮熱層を形成し、比較例５と同様のアクリル系の表面保護層形成用塗料を表１に示す目付量で塗布して表面保護層を形成した以外は実施例１と同様にして遮熱透湿防水シートを得た。 (Examples 7 to 9)
A thermal barrier layer is formed by gravure printing the thermal barrier layer forming ink so as to have the coverage shown in Table 1, and an acrylic surface protective layer-forming paint similar to Comparative Example 5 is shown in Table 1. A heat-permeable and moisture-permeable waterproof sheet was obtained in the same manner as in Example 1 except that the surface protective layer was formed by coating in an amount.

Figure 2017121779
Figure 2017121779

＜評価＞
［遮熱性］
各例の遮熱透湿防水シートについて、波長２〜２０μｍの光線の反射率を、反射率測定装置（株式会社島津製作所製ＵＶ−３１０１ＰＣ型自記分光光度計）を用いて測定し、その平均値を求めた。その結果を表１に示す。反射率の平均値が大きい程、遮熱性が高い。
［透湿抵抗］
各例の遮熱透湿防水シートについて、ＪＩＳ Ａ６１１１：２００４に規定の透湿性試験方法に基づいて透湿抵抗を測定した。その結果を表１に示す。透湿抵抗の値が小さい程、透湿性が高い。
［耐候性］
各例の遮熱透湿防水シートについて、ＪＩＳ Ｚ ２３７１：１９９４に記載の塩水噴霧試験法に準拠した試験を行い、遮熱層の剥落（遮熱層の外観）を評価した。評価結果を表１に示す。
○：ほぼ（９０％以上）剥落なし。
△：剥落が６０〜９０％有り。
×：剥落が６０％以上有り。 <Evaluation>
[Heat insulation]
About the heat-insulation moisture-permeable waterproof sheet of each example, the reflectance of the light ray with a wavelength of 2-20 micrometers is measured using a reflectance measuring apparatus (Shimadzu Corporation UV-3101PC type self-recording spectrophotometer), The average value Asked. The results are shown in Table 1. The higher the average reflectance, the higher the heat shielding property.
[Moisture permeability resistance]
About the heat-insulation moisture-permeable waterproof sheet of each example, moisture-permeable resistance was measured based on the moisture-permeable test method prescribed | regulated to JISA6111: 2004. The results are shown in Table 1. The smaller the value of moisture permeability resistance, the higher the moisture permeability.
[Weatherability]
About the heat-insulation moisture-permeable waterproof sheet of each example, the test based on the salt spray test method of JISZ2371: 1994 was done, and peeling of a heat-shielding layer (appearance of a heat-shielding layer) was evaluated. The evaluation results are shown in Table 1.
A: Almost (90% or more) no peeling off.
Δ: There is 60 to 90% peeling.
X: Exfoliation is 60% or more.

各実施例の遮熱透湿防水シートは、波長２〜１４μｍの赤外線の反射率が５０％以上であり、遮熱性が高かった。
また、各実施例の遮熱透湿防水シートの透湿抵抗は、０．１９ｍ２・ｓ・Ｐａ／μｇ以下の範囲にあり、高い透湿性を有していた。
表面保護層が形成された各実施例の遮熱透湿防水シートは、耐候性に優れていた。一方、表面保護層が形成されていない比較例１〜４の遮熱透湿防水シートは、耐候性が低かった。
比較例５の遮熱透湿防水シートは、透湿抵抗が０．２０ｍ２・ｓ・Ｐａ／μｇであり、透湿性が低かった。
比較例６の遮熱透湿防水シートは、反射率が４６％と低かった。
なお、防水性については評価していないが、各実施例の遮熱透湿防水シートは、多孔性ポリオレフィンフィルム層を備えるため、防水性は得られている。 The heat-insulating and moisture-permeable waterproof sheet of each example had a reflectance of 50% or more of infrared rays having a wavelength of 2 to 14 μm and high heat shielding properties.
Moreover, the moisture permeability resistance of the heat-insulating moisture-permeable waterproof sheet of each example was in a range of 0.19 m 2 · s · Pa / μg or less, and had high moisture permeability.
The heat-insulating and moisture-permeable waterproof sheet of each example in which the surface protective layer was formed was excellent in weather resistance. On the other hand, the heat-insulating and moisture-permeable waterproof sheets of Comparative Examples 1 to 4 in which the surface protective layer was not formed had low weather resistance.
The heat-insulating and moisture-permeable waterproof sheet of Comparative Example 5 had a moisture permeability resistance of 0.20 m 2 · s · Pa / μg and a low moisture permeability.
The heat insulating and moisture permeable waterproof sheet of Comparative Example 6 had a low reflectance of 46%.
In addition, although waterproof property is not evaluated, since the heat-insulation moisture-permeable waterproof sheet of each Example is equipped with the porous polyolefin film layer, waterproofness is acquired.

１ 遮熱透湿防水シート
１０ 透湿防水性積層体
１１ 不織布層
１２ 多孔性ポリオレフィンフィルム層
２０ 遮熱層
３０ 表面保護層 DESCRIPTION OF SYMBOLS 1 Thermal insulation moisture permeable waterproof sheet 10 Moisture permeable waterproof laminated body 11 Nonwoven fabric layer 12 Porous polyolefin film layer 20 Thermal insulation layer 30 Surface protective layer

Claims (4)

不織布層及び多孔性ポリオレフィンフィルム層を有する透湿防水性積層体と、該透湿防水性積層体の一方の面に形成された遮熱層と、該遮熱層を被覆して保護する表面保護層とを備え、
前記遮熱層は、遮熱剤及びバインダ樹脂を含有し、前記透湿防水性積層体の一方の面に対して被覆率７０〜９５％の面積割合で形成されており、
波長２〜１４μｍにおける赤外線反射率の平均値が５０％以上、ＪＩＳ Ａ６１１１に従って測定した透湿抵抗値が０．１９ｍ２・ｓ・Ｐａ／μｇ以下である、遮熱透湿防水シート。 A moisture permeable waterproof laminate having a nonwoven fabric layer and a porous polyolefin film layer, a heat shielding layer formed on one surface of the moisture permeable waterproof laminate, and surface protection that covers and protects the heat shielding layer With layers,
The heat shield layer contains a heat shield and a binder resin, and is formed at an area ratio of 70 to 95% coverage with respect to one surface of the moisture-permeable and waterproof laminate.
A heat-permeable and moisture-permeable waterproof sheet having an average value of infrared reflectance at a wavelength of 2 to 14 μm of 50% or more and a moisture permeability resistance value measured according to JIS A6111 of 0.19 m 2 · s · Pa / μg or less. 前記表面保護層が、アクリル樹脂又はウレタン樹脂を含有する、請求項１に記載の遮熱透湿防水シート。   The heat-insulating and moisture-permeable waterproof sheet according to claim 1, wherein the surface protective layer contains an acrylic resin or a urethane resin. 不織布層及び多孔性ポリオレフィンフィルム層を積層して透湿防水性積層体を作製する透湿防水性積層体作製工程と、
前記透湿防水性積層体の一方の面に、遮熱剤及びバインダ樹脂を含有する遮熱層形成用インクを、前記透湿防水性積層体の一方の面に対して被覆率７０〜９５％の面積割合で印刷して遮熱層を形成する遮熱層形成工程と、
前記遮熱層を、表面保護層形成用樹脂を含有する表面保護層により被覆する表面保護層被覆工程とを有する、遮熱透湿防水シートの製造方法。 Moisture permeable waterproof laminate production process for producing a moisture permeable waterproof laminate by laminating a nonwoven fabric layer and a porous polyolefin film layer;
On one surface of the moisture permeable and waterproof laminate, a heat shielding layer forming ink containing a heat shielding agent and a binder resin is coated on the one surface of the moisture permeable and waterproof laminate with a coverage of 70 to 95%. A thermal barrier layer forming step of forming a thermal barrier layer by printing at an area ratio of
The manufacturing method of the heat-insulation moisture-permeable waterproof sheet which has the surface protection layer coating process which coat | covers the said heat insulation layer with the surface protection layer containing resin for surface protection layer formation. 前記表面保護層形成用樹脂が、アクリル樹脂又はウレタン樹脂を含有する、請求項３に記載の遮熱透湿防水シートの製造方法。   The manufacturing method of the heat-insulation moisture-permeable waterproof sheet of Claim 3 with which the said resin for surface protection layer formation contains an acrylic resin or a urethane resin.
JP2016002700A 2016-01-08 2016-01-08 Thermal-insulating and moisture-permeable waterproof sheet and method for producing the same Pending JP2017121779A (en)