JP2009509816A - Synthetic membrane - Google Patents

Synthetic membrane Download PDF

Info

Publication number
JP2009509816A
JP2009509816A JP2008533811A JP2008533811A JP2009509816A JP 2009509816 A JP2009509816 A JP 2009509816A JP 2008533811 A JP2008533811 A JP 2008533811A JP 2008533811 A JP2008533811 A JP 2008533811A JP 2009509816 A JP2009509816 A JP 2009509816A
Authority
JP
Japan
Prior art keywords
layer
use according
synthetic
glass
synthetic membrane
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2008533811A
Other languages
Japanese (ja)
Inventor
ピヒラー，ヘルマン
ユングヴィルト，ラインホールト
アイヒホルツァー，シュテファン
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lenzing Plastics GmbH
Original Assignee
Lenzing Plastics GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lenzing Plastics GmbH filed Critical Lenzing Plastics GmbH
Publication of JP2009509816A publication Critical patent/JP2009509816A/en
Pending legal-status Critical Current

Abstract

本発明は、少なくとも、合成膜の外側を形成する軽くて耐候性を有する樹脂の層ａ）、支持層ｂ）、並びに層ａ）及び層ｂ）の間に配置された金属層ｃ）及び／又は水蒸気耐性を有する金属処理された樹脂の層、からなる複数のシート材料（ａ，ｂ，ｃ）から構成された合成膜（１）の使用に関するものである。The present invention comprises at least a light and weather resistant resin layer a) forming the outside of the synthetic membrane, a support layer b), and a metal layer c) and / or a layer disposed between the layers a) and b). Alternatively, the present invention relates to the use of a synthetic film (1) composed of a plurality of sheet materials (a, b, c) made of a metal-treated resin layer having water vapor resistance.

Description

発明の詳細な説明Detailed Description of the Invention

本発明は、複数の層状構造を有する材料から構成された合成膜の使用に関するものである。   The present invention relates to the use of a synthetic membrane composed of a material having a plurality of layered structures.

特に本発明は、断熱材、特に、備え付けチューブの断熱材、様々な性質を有する保護容器の断熱材、及び被覆板の断熱材のそれぞれに、積層及び被覆するのに適した合成膜の使用に関するものである。   In particular, the present invention relates to the use of a synthetic membrane suitable for laminating and coating each of a heat insulating material, in particular a heat insulating material for an installed tube, a heat insulating material for a protective container having various properties, and a heat insulating material for a covering plate. Is.

現在そのような断熱材は、例えば約０．６から１．００ｍｍの厚さのアルミニウム、又は亜鉛メッキ剛板により被覆されている。そのような厚い金属薄板の欠点は柔軟性に乏しいことである。例えばへこみなどの力学的なダメージは、金属薄板などの材料に永久に残ってしまう。上記の材料は比較的コスト高であるし、特に重量の大きさを原因としてそのような材料の処理工程においても問題が生じる。さらに欠点として言及しなければいけないことは、金属薄板は、常に工場での製造後に例えば現場においてしか、断熱材の上に取り付けることができないことである。   Currently, such insulation is covered by, for example, aluminum having a thickness of about 0.6 to 1.00 mm, or a galvanized rigid plate. The disadvantage of such thick sheet metal is that it is not flexible. For example, mechanical damage such as dents is left permanently in a material such as a thin metal plate. The above materials are relatively expensive, and problems arise in the processing of such materials, especially due to their large weight. It must also be mentioned as a disadvantage that the sheet metal can always be mounted on the insulation only after factory production, for example only in the field.

硬質塩化ビニル樹脂膜の被膜も同様に知られている。しかしながら、それは耐候性を有していない。同様に周知のアルミニウム膜の被膜は耐候性が乏しいという欠点を示す。   A hard vinyl chloride resin film is also known. However, it does not have weather resistance. Similarly, the well-known aluminum film has the disadvantage of poor weather resistance.

さらに、断熱材を外部と遮断するための外膜として使用されるテレフタル酸ポリエチレン（ＰＥＴ）膜、ポリプロピレン素材（ＰＰ）の内膜、及び内膜と外膜との間に配置されるアルミニウム膜、を備えた合成膜は既に提供されている。この合成膜も耐候性が乏しいという欠点を有する。   Furthermore, a polyethylene terephthalate (PET) film used as an outer film for shielding the heat insulating material from the outside, an inner film of a polypropylene material (PP), and an aluminum film disposed between the inner film and the outer film, Synthetic membranes with have already been provided. This synthetic film also has the disadvantage of poor weather resistance.

オーストリア実用新案AT7931Uには、少なくとも、
合成膜の外側を形成する遮光性及び耐候性を有する樹脂の層ａ）、
熱可塑性高分子の主要層ｂ）、
並びに層ａ）及び層ｂ）の間に配置された水蒸気障壁の特性を有する層ｃ）、
からなる複数の層状材料から構成された合成膜が記載されている。 Austrian utility model AT7931U, at least,
A resin layer a) having a light-shielding property and weather resistance to form the outside of the synthetic film;
A main layer b) of a thermoplastic polymer;
And a layer c) having the characteristics of a water vapor barrier arranged between layers a) and b),
A synthetic membrane composed of a plurality of layered materials consisting of is described.

上記文献によれば、上記主要層、又は支持層ｂ）は、基本的に硬質ポリ塩化ビニル（ＰＶＣ）膜により構成されることが好ましい。   According to the above document, the main layer or the support layer b) is preferably basically composed of a hard polyvinyl chloride (PVC) membrane.

EP1344875A2、DE29801546U1、DE1927377U及びDE1944317Uの文献に、屋根用の水蒸気障壁膜の分野における種々の材料の使用が記載されている。   The documents EP1344875A2, DE29801546U1, DE1927377U and DE1944317U describe the use of various materials in the field of water vapor barrier membranes for roofs.

WO2004/098879A1には、自動車の内側部における繊維フリース合成成分の使用が記載されている。   WO2004 / 098879A1 describes the use of a fiber fleece synthetic component in the inner part of an automobile.

EP0167956A2に、複合格子膜、及びその包装材料としての使用が記載されている。   EP0167956A2 describes a composite lattice film and its use as a packaging material.

DE202005007653Uに、その層状組織として設計された繊維マット及び金属フォイルを含んでいる絶縁素子が記載されている。   DE202005007653U describes an insulating element comprising a fiber mat and a metal foil designed as its layered structure.

WO97/22838によって、太陽熱収集器の吸収膜が周知である。   From WO97 / 22838, absorption films for solar collectors are known.

本発明の目的は上記技術の不都合を解決することであり、周知の断熱材の上部に取り付けるのに、より適した物質を提供することにある。   An object of the present invention is to solve the disadvantages of the above-described technology, and to provide a material that is more suitable for being mounted on top of a known heat insulating material.

上記目的は、断熱材の上部に請求項１から１４に従った合成膜を適用することにより達成される。   The object is achieved by applying a synthetic membrane according to claims 1 to 14 on top of the heat insulating material.

請求項１から１４に定義された合成膜が、断熱材の上部に取り付けるのに優れた方法として適していることが示された。例えば、断熱材、特に、備え付けチューブの断熱材、異なる性質の保護容器の断熱材、及び被覆板の断熱材のそれぞれに積層及び被覆するのに適している。   It has been shown that the synthetic membrane defined in claims 1 to 14 is suitable as an excellent method for attaching to the top of the insulation. For example, it is suitable for laminating and covering each of the heat insulating material, in particular, the heat insulating material of the installed tube, the heat insulating material of the protective container of different properties, and the heat insulating material of the covering plate.

それに関して、例えばAT7931Uに記載されている合成膜と対比して、ガラス織物又はガラス合成繊維が支持層ｂ）に素晴らしく適していることが偶然にも発見された。   In that regard, it has been discovered by chance that glass fabrics or glass synthetic fibers are excellently suitable for the support layer b), for example in contrast to the synthetic membranes described in AT7931U.

ガラス織物又はガラス合成繊維は、今まで支持層ｂ）として使用されてきた合成物質と比較して非常に優れている。なぜなら、それらは実際に燃えにくいので、その結果、合成膜の可燃性が低くなる。ガラス織物又はガラス合成繊維からなる物質は、耐熱安定性によっても特徴づけられる。もし燃焼しても、皆無か合成物質と比較してごく少量の有毒ガスしか発生しない。   Glass fabrics or glass synthetic fibers are very good compared to the synthetic materials that have heretofore been used as the support layer b). Because they are actually less flammable, the result is a lower flammability of the synthetic membrane. Substances made of glass fabric or glass synthetic fibers are also characterized by their heat resistance stability. If it burns, it produces little or no toxic gas compared to synthetics.

本発明の好ましい実施形態において、ガラス織物又はガラス合成繊維は４０ｇ/ｍ２〜６００ｇ/ｍ２、好ましくは１５０ｇ/ｍ２〜２５０ｇ/ｍ２、特に好ましくは２００ｇ/ｍ２前後の単位面積質量を有する。 In a preferred embodiment of the present invention, the glass fabric or glass synthetic fiber has a unit area mass of 40 g / m 2 to 600 g / m 2 , preferably 150 g / m 2 to 250 g / m 2 , particularly preferably around 200 g / m 2. Have.

支持層ｂ）の厚さは２０〜５００μｍまで可能であり、１００〜３００μｍであることが好ましく、２００μｍ前後であることが特に好ましい。   The thickness of the support layer b) can be from 20 to 500 μm, preferably from 100 to 300 μm, particularly preferably around 200 μm.

ガラス織物又はガラス合成繊維のそれぞれを形成するガラスフィラメントは、１１〜２４００ｔｅｘの番手を有し得る。   The glass filaments forming each of the glass fabric or glass synthetic fiber may have a count of 11 to 2400 tex.

特別に好ましいことは、ＥＣ９−６８型（６８ｔｅｘの番手を有するＤＩＮ１２４９ＰＡＲＴ１に準じたＥガラス）のガラスフィラメントから構成されたガラス織物が支持層ｂ）として使用されることである。   Particular preference is given to using as the support layer b) a glass fabric composed of glass filaments of the EC9-68 type (E glass according to DIN 1249 PART 1 with 68 tex count).

上記ガラス織物の上記ガラスフィラメントは平織に織り合わされるのが好ましい。綾織のガラス織物を使用することも可能である。   The glass filaments of the glass fabric are preferably woven into a plain weave. It is also possible to use a twilled glass fabric.

上記ガラス織物は伝統的な仕上げ、特にいわゆる「ロック織り仕上げ（ｗｅａｖｅ ｌｏｃｋ ｆｉｎｉｓｈ）」により提供され得る。   The glass fabric can be provided with a traditional finish, in particular with a so-called “weave lock finish”.

支持層ｂ）として使用される上記ガラス織物又はガラス合成繊維は着色され得る。使用されるガラス織物又はガラス合成繊維は、好ましくは白色である。   The glass fabric or glass synthetic fiber used as support layer b) can be colored. The glass fabric or glass synthetic fiber used is preferably white.

本発明の実施形態は支持層ｂ）として、おおよそ２００ｇ/ｍ２の単位面積質量を有する７６２８型のガラス織物であり、平織のＥＣ９−６８型のガラスフィラメントからなるおおよそ２００μｍの厚さであり、かつ「ロック織り（ｗｅａｖｅ ｌｏｃｋ）」仕上げにより提供されることが特に好ましい。 An embodiment of the present invention is a 7628 type glass fabric having a unit area mass of approximately 200 g / m 2 as the support layer b), and is approximately 200 μm thick consisting of plain weave EC9-68 type glass filaments, And it is particularly preferred to be provided with a “weave lock” finish.

オーストリア実用新案AT7931Uによってその分野に周知のように、本発明に従って使用される合成膜はいくつかの層の組み合わせなので複数の有利点がある。外側の層ａ）によって上記合成膜は光にさらされても安定しており、かつ耐候性を有する。したがって、上記外側の層ａ）は層ｃ）の腐食防止の役目も果たす。   As is well known in the art by the Austrian utility model AT7931U, the synthetic membrane used according to the invention has several advantages since it is a combination of several layers. Due to the outer layer a), the synthetic film is stable even when exposed to light and has weather resistance. Thus, the outer layer a) also serves to prevent corrosion of the layer c).

層ａ）は被膜、ラッカー被膜又は薄膜であることが好ましい。また、任意に着色され得る。特に層ａ）は、シリコーンを主成分とする被膜、アクリルラッカー、ニトロセルロースラッカー、並びに紫外線抵抗性を有するように仕上げられた、テレフタル酸ポリエチレン及び低密度ポリエチレンにより構成された膜よりなる群から選択された１つの材料、又はそれらのそれぞれの混合物から基本的に構成され得る。   Layer a) is preferably a coating, a lacquer coating or a thin film. It can also be arbitrarily colored. In particular, layer a) is selected from the group consisting of silicone-based coatings, acrylic lacquers, nitrocellulose lacquers, and membranes composed of polyethylene terephthalate and low-density polyethylene finished to be UV resistant. Can basically consist of a single material, or their respective mixtures.

層ｃ）は水蒸気障壁として機能する。それゆえ、断熱材のさらなる保護として合成膜がその上部に取り付けられる。層ｃ）は金属層及び／又は金属処理された樹脂の層、特に蒸着により付けられたアルミニウム膜又はアルミニウム層のそれぞれであることが好ましい。   Layer c) functions as a water vapor barrier. Therefore, a synthetic membrane is attached on top of it as a further protection of the insulation. Layer c) is preferably a metal layer and / or a metal-treated resin layer, in particular an aluminum film or an aluminum layer applied by evaporation.

層ｂ）は、特に、所要の、力学的影響に対する耐性を合成膜に与える。   Layer b) gives the synthetic membrane in particular the required resistance to mechanical influences.

本発明に準じて使用される合成膜の好ましい実施形態は、支持層ｂ）の厚さが合成膜全体の厚さの４０〜９５％であり、７０％以上であることが好ましく、８０％以上であることが特に好ましい。特にへこみ、剛性、引裂強度、耐穿刺性及び伸張反発力に対して必要とされる外形の安定性は、特に適した方法において上記の厚さにより保証され得る。   A preferred embodiment of the synthetic membrane used according to the invention is that the thickness of the support layer b) is 40-95% of the total thickness of the synthetic membrane, preferably 70% or more, preferably 80% or more. It is particularly preferred that In particular, the stability of the profile required for dents, stiffness, tear strength, puncture resistance and stretch repulsion can be ensured by the above thicknesses in a particularly suitable manner.

層ｃ）の厚さは、５〜５０μｍの範囲が好ましく、特に２０μｍまでが好ましく、９〜１２μｍであることが特に好ましい。   The thickness of layer c) is preferably in the range of 5 to 50 μm, particularly preferably up to 20 μm, particularly preferably 9 to 12 μm.

層ａ）の厚さは、好ましくは１０〜３５μｍの範囲であってもよいし、５〜３０ｇ/ｍ２の範囲であることのそれぞれが好ましい。 The thickness of layer a) may preferably be in the range of 10 to 35 μm, each preferably in the range of 5 to 30 g / m 2 .

合成膜は、層ａ）、ｂ）及びｃ）から基本的に構成されるのが好ましい。これが意味するところは、必要とされ得る粘着性の膜を別とすれば、合成膜は層ａ）、ｂ）及びｃ）の間にさらに構成要素となる層を持たない。   The synthetic membrane is preferably basically composed of layers a), b) and c). This means that, apart from the sticky membrane that may be required, the synthetic membrane does not have a further constituent layer between layers a), b) and c).

層ａ）、ｂ）及びｃ）からなる合成膜の全体の厚さは５０〜８００μｍの範囲であることが好ましい。   The total thickness of the synthetic membrane consisting of layers a), b) and c) is preferably in the range of 50 to 800 μm.

しかしながら、本発明において使用される合成膜はさらに膜を含んでもよい。例えば付加的な密封層、又は断熱材の上面である層ｂ）の底面において粘着物質の層が設けられ得る。断熱材の上部に本発明に準じて使用される合成膜を取り付け可能にするために、取り外し可能な合成膜が任意に備えられ得る。さらに、断熱材の上面である層ｂ）の底面にアルミニウム層を備えることもできる。   However, the synthetic membrane used in the present invention may further include a membrane. For example, an additional sealing layer or a layer of adhesive substance can be provided on the bottom surface of layer b) which is the top surface of the insulation. In order to be able to attach the synthetic membrane used according to the invention on top of the thermal insulation, a removable synthetic membrane can optionally be provided. Furthermore, an aluminum layer can be provided on the bottom surface of the layer b) which is the top surface of the heat insulating material.

さらなる実施形態において、本発明において使用される合成膜が、少なくとも１つの熱可塑性高分子のさらなる層ｅ）を含むことが好ましい。上記熱可塑性高分子は、特にポリプロピレン、ポリ塩化ビニル、低密度ポリプロピレン、テレフタル酸ポリエチレン及びポリスチレンからなる群より選択された物質、又はそれらのそれぞれの混合物からなる。   In a further embodiment, it is preferred that the synthetic membrane used in the present invention comprises at least one further layer e) of thermoplastic polymer. Said thermoplastic polymer consists in particular of a material selected from the group consisting of polypropylene, polyvinyl chloride, low density polypropylene, polyethylene terephthalate and polystyrene, or a respective mixture thereof.

オーストリア実用新案AT7931Uによって、熱可塑性高分子からなる層を提供することは周知である。このような層を、ガラス織物又はガラス繊維フリースから構成された層に、本発明に準じた組み入れ方で組み合わせた合成膜は十分な復元力を持つ。このため、例えば合成膜又は断熱材の形成中においてそれぞれに起こり得るへこみ及びこれに類する形状は復元される。   It is well known that the Austrian utility model AT7931U provides a layer of thermoplastic polymer. A synthetic membrane in which such a layer is combined with a layer composed of a glass fabric or glass fiber fleece according to the incorporation method according to the present invention has a sufficient restoring force. For this reason, for example, dents and similar shapes that can occur in the formation of the synthetic film or the heat insulating material are restored.

層ｅ）は、層ｂ）と層ｃ）との間に配置されるのが好ましい。   Layer e) is preferably arranged between layer b) and layer c).

特に、２つの層ｃ´）とｃ´´）との間に層ｅ）が配置され得る。これにより、層ｂ）は断熱材の上面、及び第二の層ｃ´´）の下面に配置される。   In particular, a layer e) can be arranged between the two layers c ′) and c ″). Thereby, the layer b) is arranged on the upper surface of the insulation and on the lower surface of the second layer c ″).

本発明に係る合成膜の個々の層は、従来の接着層例えばホットメルト接着層により互いに接着されてもよい。紫外線抵抗性、耐候性、及び耐水性を有する目的のため、添加物の添加により仕上げられたポリウレタンを主成分とする二液形接着剤が特に適している。これにより個々の層の層間剥離を防ぐことができる。   The individual layers of the synthetic membrane according to the present invention may be bonded together by a conventional adhesive layer, for example a hot melt adhesive layer. For the purpose of having ultraviolet resistance, weather resistance, and water resistance, a two-part adhesive mainly composed of polyurethane finished by addition of additives is particularly suitable. Thereby, delamination of individual layers can be prevented.

本発明に係る合成膜は、例えば支持層ｂ）に、予め合成した層ａ）及び層ｃ）の合成物を被膜することにより同様に加工され得る。   The synthetic membrane according to the invention can be processed in the same way, for example, by coating the support layer b) with a pre-synthesized composite of layers a) and c).

本発明に係る合成膜が断熱材の上面に取り付けられた場合、又は本発明に係る合成膜と共に供給される断熱材がチューブの上に取り付けられた場合のそれぞれの場合には、合成膜の個々の部分又は断熱材のそれぞれが、その分野に周知の方法により互いに接着され得る。例えば、空間を埋めるように重ねる方法、及び、それらを一体にくっつけるか、溶接する方法のそれぞれにおいて互いに接着され得る。   In each case where the synthetic membrane according to the present invention is attached to the top surface of the heat insulating material or when the heat insulating material supplied together with the synthetic membrane according to the present invention is attached onto the tube, the individual of the synthetic membrane Each of these parts or insulation can be glued together by methods well known in the art. For example, they can be glued together in each of a method of overlapping to fill the space and a method of attaching them together or welding.

本発明に係る合成膜は工場での製造過程においても断熱材の上部に接着され得るし、現場において後で断熱材に取り付けられ得る。   The synthetic membrane according to the present invention can be adhered to the upper portion of the heat insulating material even in the manufacturing process at the factory, or can be attached to the heat insulating material later on site.

以下に本発明を、図、及び典型的な実施形態を用いてより詳細に説明する。   In the following, the invention will be described in more detail with the aid of figures and exemplary embodiments.

図１は、本発明において用いられる合成膜を概略的に示す。   FIG. 1 schematically shows a synthetic membrane used in the present invention.

図２は、接着層をさらに備えた図１に係る実施形態を概略的に示す。   FIG. 2 schematically shows the embodiment according to FIG. 1 further comprising an adhesive layer.

図３は、樹脂膜ｅ）をさらに備えた実施形態を示す。   FIG. 3 shows an embodiment further comprising a resin film e).

図４は、本発明において用いられる合成膜の、断熱材の上面への取り付けを概略的に示す。   FIG. 4 schematically shows the attachment of the synthetic membrane used in the present invention to the top surface of the heat insulating material.

〔実施例１〕
図１に、本発明において用いられる合成膜の実施形態を大きく拡大したものを概略的に示す。ここに、基本的に耐候性の外膜ａ、支持層ｂ及び水蒸気障壁層ｃからなる合成膜１が示されている。 [Example 1]
FIG. 1 schematically shows a greatly enlarged embodiment of a synthetic membrane used in the present invention. Here, a synthetic membrane 1 basically composed of a weather-resistant outer membrane a, a support layer b and a water vapor barrier layer c is shown.

図２に、接着層ｄ´、及びｄ´´がよりはっきりと示されている（極めて拡大された尺度において）。   FIG. 2 shows the adhesive layers d ′ and d ″ more clearly (on a very enlarged scale).

外層ａ）は、紫外線抵抗性を有するようにテレフタル酸ポリエチレンにて仕上げられることで構成されており、厚さは１９μｍである。層ｃ）は厚さ１２μｍのアルミニウム膜である。層ｂ）は、単位面積当たりの質量が約２００ｇ/ｍ２の７６２８型のガラス織物であり、厚さは約２００μｍであり、平織のＥＣ９−６８型のガラスフィラメントからなり、かつ、「ロック織り（ｗｅａｖｅ ｌｏｃｋ）」の仕上げにより構成されている。 The outer layer a) is constituted by finishing with polyethylene terephthalate so as to have ultraviolet resistance, and its thickness is 19 μm. Layer c) is a 12 μm thick aluminum film. Layer b) is a 7628 type glass fabric with a mass per unit area of about 200 g / m 2 , a thickness of about 200 μm, consisting of plain weave EC9-68 type glass filaments and “rock weave” (Weave lock) "finish.

上記層は、ポリウレタンを主成分とする二液形接着剤により、その分野に周知の方法で互いに接着される。上記層は、紫外線抵抗性、並びに天気及び大気条件に対する耐性のそれぞれを有するように仕上げられる（接着層ｄ´及びｄ´´）。   The above layers are bonded to each other by a well-known method in the field using a two-component adhesive mainly composed of polyurethane. The layers are finished to have UV resistance and resistance to weather and atmospheric conditions, respectively (adhesive layers d ′ and d ″).

〔実施例２〕
図３に、２つのアルミニウム膜ｃ´と、ｃ´´との間に配置された熱可塑性高分子の付加的な層ｅを備えた、本発明において用いられる合成膜のさらなる実施形態の構成を示す（接着層はこの図には図示されていない）。 [Example 2]
FIG. 3 shows the configuration of a further embodiment of the synthetic membrane used in the present invention with two aluminum membranes c ′ and an additional layer e of thermoplastic polymer arranged between c ″. Shown (adhesive layer not shown in this figure).

実施例１に記載の層ｂ）がガラス織物であり約２００μｍの厚さなのに対して、層ｅはポリ塩化ビニルからなり厚さは１４０μｍである。２つのアルミニウム層ｃ´及びｃ´´はそれぞれが厚さ９μｍである。   Layer b) described in Example 1 is a glass fabric and is approximately 200 μm thick, whereas layer e is made of polyvinyl chloride and has a thickness of 140 μm. Each of the two aluminum layers c ′ and c ″ has a thickness of 9 μm.

〔実施例３〕
図４に、チューブ２を覆っている断熱材３の上面に、本発明において用いられる合成膜１の、取り付けられ得る構造を概略的に示す。合成膜１は断熱材３の周囲に配置されている。膜層の重複点において、上記膜は例えばリベット４によって密封される。 Example 3
FIG. 4 schematically shows a structure that can be attached to the synthetic membrane 1 used in the present invention on the upper surface of the heat insulating material 3 covering the tube 2. The synthetic film 1 is disposed around the heat insulating material 3. At the overlapping points of the membrane layers, the membrane is sealed, for example by rivets 4.

本発明に係る合成膜を概略的に示す。1 schematically shows a synthetic membrane according to the present invention. 接着層をさらに備えた図１に示した合成膜を概略的に示す。2 schematically shows the synthetic membrane shown in FIG. 1 further comprising an adhesive layer. 樹脂膜（ｅ）をさらに備えた実施形態を示す。An embodiment further comprising a resin film (e) is shown. 本発明において用いられる合成膜の、断熱材の上面への取り付けを概略的に示す。The attachment to the upper surface of a heat insulating material of the synthetic membrane used in this invention is shown schematically.

Claims (15)

少なくとも複数の層状材料（ａ、ｂ、ｃ）より構成される合成膜（１）の使用：
ａ）フィルムの外側を形成する、遮光性及び耐候性を有する樹脂の層、
ｂ）支持層、並びに、
ｃ）層ａ）及び層ｂ）の間に配置された、水蒸気障壁としての特性を有する金属層、及び／又は金属処理された樹脂の層、
上記支持層ｂ）は、断熱材の上に取り付けるためのガラス織物又はガラス合成繊維である。 Use of synthetic membrane (1) composed of at least a plurality of layered materials (a, b, c):
a) a resin layer having a light-shielding property and weather resistance, which forms the outside of the film;
b) a support layer, and
c) a metal layer having properties as a water vapor barrier and / or a layer of metal-treated resin arranged between layers a) and b)
The support layer b) is a glass fabric or glass synthetic fiber for mounting on a heat insulating material. 上記ガラス織物又は上記ガラス合成繊維は、４０〜６００ｇ/ｍ２、好ましくは１５０〜２５０ｇ/ｍ２、特に好ましくは２００ｇ/ｍ２前後の単位面積質量を有することを特徴とする請求項１に記載の使用。 The glass fabric or the glass synthetic fibers, 40~600g / m 2, preferably 150 to 250 g / m 2, particularly preferably according to claim 1, characterized in that it has a mass per unit area of 200 g / m 2 before and after Use of. 上記支持層ｂ）の厚さは、２０〜５００μｍ、好ましくは１００〜３００μｍ、特に好ましくは２００μｍ前後であることを特徴とする請求項１又は２に記載の使用。   3. Use according to claim 1 or 2, characterized in that the thickness of the support layer b) is 20 to 500 [mu] m, preferably 100 to 300 [mu] m, particularly preferably around 200 [mu] m. ＥＣ９６−８型のガラスフィラメントから構成されたガラス織物が上記支持層ｂ）として用いられることを特徴とする請求項１から３のいずれか１項に記載の使用。   4. Use according to any one of claims 1 to 3, characterized in that a glass fabric composed of EC96-8 type glass filaments is used as the support layer b). 平織により織り合わされたガラスフィラメントを有するガラス織物が、上記支持層ｂ）として用いられることを特徴とする請求項１から４のいずれか１項に記載の使用。   5. Use according to any one of claims 1 to 4, characterized in that a glass fabric having glass filaments interwoven with plain weave is used as the support layer b). 仕上げ、特にロック織り仕上げ（ｗｅａｖｅ ｌｏｃｋ ｆｉｎｉｓｈ）により得られたガラス織物が、上記支持層ｂ）として用いられることを特徴とする請求項１から５のいずれか１項に記載の使用。   6. Use according to any one of the preceding claims, characterized in that a glass fabric obtained by finishing, in particular a weave lock finish, is used as the support layer b). 上記層ａ）は、被膜、ラッカー被膜又は薄膜であることを特徴とする請求項１から６のいずれか１項に記載の使用。   7. Use according to any one of claims 1 to 6, characterized in that the layer a) is a coating, a lacquer coating or a thin film. 上記層ａ）は、シリコーンを主成分とする被膜、アクリルラッカー、ニトロセルロースラッカー、並びに紫外線抵抗性を有するように仕上げられ、テレフタル酸ポリエチレン及び低密度ポリエチレンにより構成された膜よりなる群から選択された１つの材料、又はそれらのそれぞれの混合物から基本的に構成されていることを特徴とする請求項１から７のいずれか１項に記載の使用。   The layer a) is selected from the group consisting of a silicone-based coating, an acrylic lacquer, a nitrocellulose lacquer, and a membrane composed of polyethylene terephthalate and low density polyethylene, finished to have UV resistance. 8. Use according to any one of claims 1 to 7, characterized in that it consists essentially of a single material or a respective mixture thereof. 上記層ｃ）は、アルミニウム膜又は蒸着により付けられたアルミニウム層であることを特徴とする請求項１から８のいずれか１項に記載の使用。   Use according to any one of claims 1 to 8, characterized in that the layer c) is an aluminum film or an aluminum layer applied by vapor deposition. 上記支持層ｂ）の厚さは、合成膜全体の４０〜９５％、好ましくは７０％以上であり、特に好ましくは８０％以上であることを特徴とする請求項１から９のいずれか１項に記載の使用。   10. The thickness of the support layer b) is 40 to 95% of the total synthetic membrane, preferably 70% or more, particularly preferably 80% or more. Use as described in. 上記合成膜は、基本的に上記層ａ）、ｂ）、及びｃ）からなる、請求項１から１０のいずれか１項に記載の使用。   Use according to any one of claims 1 to 10, wherein the synthetic membrane consists essentially of the layers a), b) and c). 上記合成膜は、熱可塑性高分子、特にポリプロピレン、ポリ塩化ビニル、低密度ポリプロピレン、テレフタル酸ポリエチレン及びポリスチレンからなる群より選択された１つの材料、又はそれらのそれぞれの混合物である層ｅ）を少なくとも１つさらに備えていることを特徴とする請求項１から１０のいずれか１項に記載の使用。   The synthetic membrane comprises at least a layer e) which is a thermoplastic polymer, in particular one material selected from the group consisting of polypropylene, polyvinyl chloride, low density polypropylene, polyethylene terephthalate and polystyrene, or a respective mixture thereof. 11. Use according to any one of the preceding claims, further comprising one. 上記層ｅ）は、層ｂ）と層ｃ）との間に配置されていることを特徴とする請求項１２に記載の使用。   Use according to claim 12, characterized in that the layer e) is arranged between the layers b) and c). 層ｅ）は、２つの層ｃ´）とｃ´´）の間に配置されていることを特徴とする請求項１３に記載の使用。   Use according to claim 13, characterized in that layer e) is arranged between two layers c ') and c "). 請求項１〜１４のいずれか１項に記載の合成膜を外部に備えた断熱材。   The heat insulating material which equips the exterior with the synthetic film of any one of Claims 1-14.
JP2008533811A 2005-10-05 2006-09-28 Synthetic membrane Pending JP2009509816A (en)