JP2017082109A - 日射センサーカバー用ポリカーボネート樹脂組成物 - Google Patents
日射センサーカバー用ポリカーボネート樹脂組成物 Download PDFInfo
- Publication number
- JP2017082109A JP2017082109A JP2015212479A JP2015212479A JP2017082109A JP 2017082109 A JP2017082109 A JP 2017082109A JP 2015212479 A JP2015212479 A JP 2015212479A JP 2015212479 A JP2015212479 A JP 2015212479A JP 2017082109 A JP2017082109 A JP 2017082109A
- Authority
- JP
- Japan
- Prior art keywords
- polycarbonate resin
- resin composition
- solar radiation
- radiation sensor
- sensor cover
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
械、自動車、医療用途等に幅広く使用されている。例えば、光学情報記録媒体、光学レン
ズ、建築物・車輌用グレージング材料などの用途を挙げることができる。
囲気もしくは還元性ガス雰囲気中で熱処理して得ることができる。当該熱処理を経て得ら
れた複合タングステン酸化物微粒子は、十分な可視光選択透過性を有している。
剤としてはポリカーボネート、ポリサルホン、ポリアクリロニトリル、ポリアリレート、
ポリエチレン、ポリ塩化ビニル、ポリ塩化ビニリデン、フッ素樹脂、ポリビニルブチラー
ル、ポリビニルアルコール、ポリスチレン、シリコーン系樹脂やこれらの誘導体等が挙げ
られ、これらで被覆されることにより樹脂へ添加したときの分散性が向上し、更に機械物
性の低下を防ぐ効果がある。なお、分散剤による被覆方法としては複合タングステン酸化
微粒子と分散剤をトルエン等の溶媒に溶解、攪拌し分散液を調製した後、真空乾燥等の処
理で溶媒を除去することにより複合タングステン酸化微粒子を被覆する方法等が挙げられ
る。
一般式1:
一般式4:
1.ポリカーボネート樹脂(A):
ビスフェノールAと塩化カルボニルとから合成されたポリカーボネート樹脂
(商品名カリバー200−20、住化スタイロンポリカーボネート(株)製、「カリバー」はトリンゼオ ユーロップ ゲーエムベーハーの登録商標、粘度平均分子量:19000、(以下、「PC」と略記)
YMDS874(住友金属工業社製、平均粒子径5nm)
酸化セシウムタングステン微粒子、Cs0.33WO3(23wt%)および分散剤からなる。(以下、「化合物B」と略記)
3−1.クラリアントジャパン社製ホスタノックスP−EPQ(以下「AO1」と略記)
3−2.旭電化社製 アデカスタブ AO−50(以下「AO2」と略記)
4−1.ADEKA社製 アデカスタブ LA-31(以下「UVA1」と略記)
4−2.BASF社製 TINUVIN329(以下「UVA2」と略記)
得られたペレットをそれぞれ120℃×4時間の条件にて乾燥を行った後、射出成形機(日本製鋼所製J100E2P)を用いて、シリンダー設定温度280℃の条件にて平板試験片(縦50mm、横50mm、厚み1mm)を作成後、分光光度計(日立ハイテクサイエンス社製 UH−4150形分光光度計)により、紫外領域300nm、可視光領域550nm及び近赤外領域900nmにおける透過率を測定し、300nmと900nmにおける透過率は5%以下、550nmにおける透過率は40%以上を良好(○)とし、それを満足出来ない場合には不良(×)とした。
得られた各種ペレットをそれぞれ120℃×4時間の条件にて乾燥を行った後、射出成形機(日本製鋼所製J100E2P)を用いて、シリンダー設定温度300℃の条件にて15分間滞留前後の平板試験片(縦50mm、横50mm、厚み1mm)を作成後、スペクトロフォトメーター(村上色彩研究所社製CMS−35SP)により、YIの変化(△YI)を測定した。△YIとは、滞留前後の黄味の程度の差を表し、△YIが小さい程、変色は小さく熱安定性に優れている。△YIの評価の基準としては、△YIの値が5未満であるものを良好(○)、5以上であるものを不良(×)とした。
得られた各種ペレットを120℃×4時間の条件にて乾燥を行った後に、射出成形機(日本製鋼所製J100E2P)を用いてシリンダー設定温度280℃にて耐候性評価用試験片(縦50mm、横50mm、厚み1mm)を作成した。得られた試験片を、キセノンウェザーメーター(スガ試験機社製スーパーキセノンウェザーメーターSX75)に装着し、放射照度180W/m2、湿度50%RH、ブラックパネル温度63℃の設定で、1時間42分照射に引き続き18分降雨のサイクルにて600時間照射試験を行い、スペクトロフォトメーター(村上色彩研究所社製CMS−35SP)により、YIの変化(△YI)を測定した。△YIとは、照射試験前後の黄味の程度の差を表し、△YIが小さい程、変色は小さく耐候性に優れている。△YIの評価の基準としては、△YIの値が10未満であるものを良好(○)、10以上であるものを不良(×)とした。
比較例1は、化合物Bの配合量が規定量より少ない場合で、可視光選択透過性および耐候性に劣っていた。
比較例2は、化合物Bの配合量が規定量より多い場合で、可視光選択透過性および熱安定性に劣っていた。
比較例3は、AO1の配合量が規定量より少ない場合で、熱安定性に劣っていた。
比較例4は、AO1の配合量が規定量より多い場合で、熱安定性に劣っていた。
比較例5は、UVA1の配合量が規定量より多い場合で、熱安定性に劣っていた。
Claims (5)
- ポリカーボネート樹脂(A)100重量部、無機酸化物(B)0.1〜1重量部、リン系酸化防止剤およびフェノール系酸化防止剤から選択される1もしくは2種以上の酸化防止剤(C) 0.05〜1重量部、及び紫外線吸収剤(D)0〜2重量部を含有することを特徴とする、日射センサーカバー用ポリカーボネート樹脂組成物。
- 前記無機酸化物(B)が、複合タングステン酸化物である、請求項1記載の日射センサーカバー用ポリカーボネート樹脂組成物。
- 前記複合タングステン酸化物が、酸化セシウムタングステン微粒子である、請求項2記載の日射センサーカバー用ポリカーボネート樹脂組成物。
- 前記酸化セシウムタングステン微粒子の粒子径が1nm〜800nmである、請求項3記載の日射センサーカバー用ポリカーボネート樹脂組成物。
- 前記紫外線吸収剤(D)が、ベンゾトリアゾール系、トリアジン系およびベンゾフェノン系の化合物から選択される1種もしくは2種以上の紫外線吸収剤である、請求項1記載の日射センサーカバー用ポリカーボネート樹脂組成物。