JP2016029142A - Thermally conductive polycarbonate resin composition and molding - Google Patents
Thermally conductive polycarbonate resin composition and molding Download PDFInfo
- Publication number
- JP2016029142A JP2016029142A JP2015076808A JP2015076808A JP2016029142A JP 2016029142 A JP2016029142 A JP 2016029142A JP 2015076808 A JP2015076808 A JP 2015076808A JP 2015076808 A JP2015076808 A JP 2015076808A JP 2016029142 A JP2016029142 A JP 2016029142A
- Authority
- JP
- Japan
- Prior art keywords
- polycarbonate resin
- mass
- parts
- resin composition
- bis
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、熱伝導性ポリカーボネート樹脂組成物及び成形品に関し、詳しくは、優れた熱伝導性と高度の耐熱性を有しながら、特に優れた耐衝撃性を示す熱伝導性ポリカーボネート樹脂組成物及び成形品に関する。 The present invention relates to a thermally conductive polycarbonate resin composition and a molded article, and more specifically, a thermally conductive polycarbonate resin composition exhibiting particularly excellent impact resistance while having excellent thermal conductivity and high heat resistance, and It relates to molded products.
ポリカーボネート樹脂は、耐衝撃性、耐熱性、電気絶縁性、寸法安定性等に優れ、これらの特性のバランスも良好であることから、電気電子機器部品、OA機器部品、精密機械部品、車輌用部品などの分野で広く使用されている。 Polycarbonate resin is excellent in impact resistance, heat resistance, electrical insulation, dimensional stability, etc., and has a good balance of these characteristics. Therefore, electrical and electronic equipment parts, OA equipment parts, precision machine parts, vehicle parts Widely used in such fields.
しかしながら、ポリカーボネート樹脂は、電気抵抗率が高く帯電し易いために、静電気に起因する様々な障害を引き起こす可能性がある。また、上記の分野においては、殆どの機器が発熱する部品を搭載しているが、近年、機器の高性能化に伴い、部品当たりの消費電力量が増え、部品からの発熱量が増大する傾向にあり、より高い熱伝導率を示すポリカーボネート樹脂材料が求められている。 However, since the polycarbonate resin has a high electric resistivity and is easily charged, it may cause various troubles due to static electricity. In the above fields, most devices are equipped with components that generate heat. However, in recent years, as the performance of devices increases, the amount of power consumed per component increases and the amount of heat generated from components tends to increase. Therefore, there is a need for a polycarbonate resin material that exhibits higher thermal conductivity.
ポリカーボネート樹脂材料に熱伝導性を付与する方法として、種々の熱伝導性フィラーを配合する方法が知られており、特許文献1〜6には、熱伝導度の良好なポリカーボネート樹脂組成物が開示されている。しかし、これらのポリカーボネート樹脂組成物は、それなりの良好な熱伝導性を示すことができるが耐衝撃性が悪化してしまうという欠点を有しており、熱伝導性が優れ、かつ耐衝撃性にも優れたポリカーボネート樹脂組成物が望まれている。 As a method for imparting thermal conductivity to a polycarbonate resin material, a method of blending various heat conductive fillers is known, and Patent Documents 1 to 6 disclose polycarbonate resin compositions having good thermal conductivity. ing. However, these polycarbonate resin compositions can exhibit good thermal conductivity, but have the disadvantage that the impact resistance is deteriorated, the thermal conductivity is excellent, and the impact resistance is improved. In addition, an excellent polycarbonate resin composition is desired.
近年、携帯端末に代表されるような各種の電気電子機器等の部品(筺体やカバー等)の分野においては、熱伝導性と耐衝撃性についての要求スペックは、ますます高度なものになり、また耐熱性にも優れることが必須となっている。しかし、今日まで、熱伝導性と耐衝撃性と耐熱性を全てバランス良く改良した高レベルのポリカーボネート樹脂材料は提案されていないというのが実情であった。
本発明の目的(課題)は、高い熱伝導性と高度の耐熱性を有しながら、特に優れた耐衝撃性を有する熱伝導性ポリカーボネート樹脂組成物を提供することにある。
In recent years, in the field of parts such as various electric and electronic devices represented by mobile terminals (such as housings and covers), the required specifications for thermal conductivity and impact resistance have become increasingly sophisticated. It is also essential to have excellent heat resistance. However, to date, there has been no actual proposal of a high-level polycarbonate resin material that has improved thermal conductivity, impact resistance, and heat resistance in a well-balanced manner.
An object (issue) of the present invention is to provide a heat conductive polycarbonate resin composition having particularly high impact resistance while having high heat conductivity and high heat resistance.
本発明者らは、上記課題を達成すべく、鋭意検討を重ねた結果、ポリカーボネート樹脂に、窒化硼素及び平均粒径が10μm以上であるタルクをそれぞれ特定の量で含有するものが、上記課題を解決し、特に耐衝撃性をより向上させることを見出し、本発明を完成させるに至った。
本発明は、以下のとおりである。
As a result of intensive investigations to achieve the above-mentioned problems, the inventors of the present invention have the polycarbonate resin containing boron nitride and talc having an average particle size of 10 μm or more in specific amounts, respectively. In particular, the inventors have found that the impact resistance is further improved and have completed the present invention.
The present invention is as follows.
[1]ポリカーボネート樹脂100質量部に対し、窒化硼素10〜50質量部および平均粒径が10μm以上であるタルク15〜80質量部を含有することを特徴とする熱伝導性ポリカーボネート樹脂組成物。
[2]さらに、ホスファゼン化合物を、ポリカーボネート樹脂100質量部に対し、2〜20質量部含有する上記[1]に記載の熱伝導性ポリカーボネート樹脂組成物。
[3]さらに、シロキサン系エラストマーを、ポリカーボネート樹脂100質量部に対し、5〜20質量部含有する上記[1]または[2]に記載の熱伝導性ポリカーボネート樹脂組成物。
[4]ノッチなしシャルピー衝撃強度が105kJ/m2以上である上記[1]〜[3]のいずれかに記載の熱伝導性ポリカーボネート樹脂組成物。
[5]上記[1]〜[4]のいずれかに記載の熱伝導性ポリカーボネート樹脂組成物を成形してなる成形品。
[1] A thermally conductive polycarbonate resin composition comprising 10 to 50 parts by mass of boron nitride and 15 to 80 parts by mass of talc having an average particle size of 10 μm or more with respect to 100 parts by mass of the polycarbonate resin.
[2] The thermally conductive polycarbonate resin composition according to [1], further containing 2 to 20 parts by mass of a phosphazene compound with respect to 100 parts by mass of the polycarbonate resin.
[3] The thermally conductive polycarbonate resin composition according to the above [1] or [2], further comprising 5 to 20 parts by mass of a siloxane elastomer with respect to 100 parts by mass of the polycarbonate resin.
[4] The thermally conductive polycarbonate resin composition according to any one of [1] to [3], wherein the Charpy impact strength without notch is 105 kJ / m 2 or more.
[5] A molded product obtained by molding the thermally conductive polycarbonate resin composition according to any one of [1] to [4].
本発明のポリカーボネート樹脂組成物によれば、優れた熱伝導性と高度の耐熱性を有しながら、特に優れた耐衝撃性を示す熱伝導性ポリカーボネート樹脂組成物を提供することができる。 According to the polycarbonate resin composition of the present invention, it is possible to provide a heat conductive polycarbonate resin composition exhibiting particularly excellent impact resistance while having excellent heat conductivity and high heat resistance.
以下、本発明について実施形態及び例示物等を示して詳細に説明するが、本発明は、以下に示す実施形態及び例示物等に限定されるものではなく、本発明の要旨を逸脱しない範囲において任意に変更して実施できる。 Hereinafter, the present invention will be described in detail with reference to embodiments and examples, but the present invention is not limited to the following embodiments and examples and the like, and is within the scope of the present invention. Any change can be made.
本発明の熱伝導性ポリカーボネート樹脂組成物は、ポリカーボネート樹脂100質量部に対し、窒化硼素10〜50質量部および平均粒径が10μm以上であるタルク15〜80質量部を含有することを特徴とする。 The heat conductive polycarbonate resin composition of the present invention contains 10 to 50 parts by mass of boron nitride and 15 to 80 parts by mass of talc having an average particle size of 10 μm or more with respect to 100 parts by mass of the polycarbonate resin. .
[ポリカーボネート樹脂]
本発明において使用するポリカーボネート樹脂の種類に制限はなく、ポリカーボネート樹脂は、1種類を用いてもよく、2種類以上を任意の組み合わせ及び任意の比率で併用してもよい。
[Polycarbonate resin]
There is no restriction | limiting in the kind of polycarbonate resin used in this invention, A polycarbonate resin may use 1 type and may use 2 or more types together by arbitrary combinations and arbitrary ratios.
ポリカーボネート樹脂は、[−O−X−O−CO−]で表される炭酸結合を有する基本構造の重合体であり、Xは一般には炭化水素であるが、種々の特性付与のためヘテロ原子、ヘテロ結合の導入されたXを用いてもよい。 The polycarbonate resin is a polymer having a basic structure having a carbonic acid bond represented by [—O—X—O—CO—], and X is generally a hydrocarbon, but a hetero atom for imparting various properties, X introduced with a hetero bond may be used.
また、ポリカーボネート樹脂は、炭酸結合に直接結合する炭素がそれぞれ芳香族炭素である芳香族ポリカーボネート樹脂、及び脂肪族炭素である脂肪族ポリカーボネート樹脂に分類できるが、いずれを用いることもできる。なかでも、耐熱性、機械的物性、電気的特性等の観点から、芳香族ポリカーボネート樹脂が好ましい。 The polycarbonate resin can be classified into an aromatic polycarbonate resin in which carbon directly bonded to a carbonic acid bond is aromatic carbon and an aliphatic polycarbonate resin in which aliphatic carbon is aliphatic carbon, either of which can be used. Of these, aromatic polycarbonate resins are preferred from the viewpoints of heat resistance, mechanical properties, electrical characteristics, and the like.
ポリカーボネート樹脂の具体的な種類に制限はないが、例えば、ジヒドロキシ化合物とカーボネート前駆体とを反応させてなるポリカーボネート重合体が挙げられる。この際、ジヒドロキシ化合物及びカーボネート前駆体に加えて、ポリヒドロキシ化合物等を反応させるようにしてもよい。また、二酸化炭素をカーボネート前駆体として、環状エーテルと反応させる方法も用いてもよい。またポリカーボネート重合体は、直鎖状でもよく、分岐鎖状でもよい。さらに、ポリカーボネート重合体は1種の繰り返し単位からなる単重合体であってもよく、2種以上の繰り返し単位を有する共重合体であってもよい。このとき共重合体は、ランダム共重合体、ブロック共重合体等、種々の共重合形態を選択することができる。なお、通常、このようなポリカーボネート重合体は、熱可塑性の樹脂となる。 Although there is no restriction | limiting in the specific kind of polycarbonate resin, For example, the polycarbonate polymer formed by making a dihydroxy compound and a carbonate precursor react is mentioned. At this time, in addition to the dihydroxy compound and the carbonate precursor, a polyhydroxy compound or the like may be reacted. Further, a method of reacting carbon dioxide with a cyclic ether using a carbonate precursor may be used. The polycarbonate polymer may be linear or branched. Further, the polycarbonate polymer may be a homopolymer composed of one type of repeating unit or a copolymer having two or more types of repeating units. At this time, the copolymer can be selected from various copolymerization forms such as a random copolymer and a block copolymer. In general, such a polycarbonate polymer is a thermoplastic resin.
芳香族ポリカーボネート樹脂の原料となるモノマーのうち、芳香族ジヒドロキシ化合物の例を挙げると、 Among monomers used as raw materials for aromatic polycarbonate resins, examples of aromatic dihydroxy compounds include:
1,2−ジヒドロキシベンゼン、1,3−ジヒドロキシベンゼン(即ち、レゾルシノール)、1,4−ジヒドロキシベンゼン等のジヒドロキシベンゼン類;
2,5−ジヒドロキシビフェニル、2,2’−ジヒドロキシビフェニル、4,4’−ジヒドロキシビフェニル等のジヒドロキシビフェニル類;
Dihydroxybenzenes such as 1,2-dihydroxybenzene, 1,3-dihydroxybenzene (ie, resorcinol), 1,4-dihydroxybenzene;
Dihydroxybiphenyls such as 2,5-dihydroxybiphenyl, 2,2′-dihydroxybiphenyl, 4,4′-dihydroxybiphenyl;
2,2’−ジヒドロキシ−1,1’−ビナフチル、1,2−ジヒドロキシナフタレン、1,3−ジヒドロキシナフタレン、2,3−ジヒドロキシナフタレン、1,6−ジヒドロキシナフタレン、2,6−ジヒドロキシナフタレン、1,7−ジヒドロキシナフタレン、2,7−ジヒドロキシナフタレン等のジヒドロキシナフタレン類; 2,2′-dihydroxy-1,1′-binaphthyl, 1,2-dihydroxynaphthalene, 1,3-dihydroxynaphthalene, 2,3-dihydroxynaphthalene, 1,6-dihydroxynaphthalene, 2,6-dihydroxynaphthalene, , 7-dihydroxynaphthalene, dihydroxynaphthalene such as 2,7-dihydroxynaphthalene;
2,2’−ジヒドロキシジフェニルエーテル、3,3’−ジヒドロキシジフェニルエーテル、4,4’−ジヒドロキシジフェニルエーテル、4,4’−ジヒドロキシ−3,3’−ジメチルジフェニルエーテル、1,4−ビス(3−ヒドロキシフェノキシ)ベンゼン、1,3−ビス(4−ヒドロキシフェノキシ)ベンゼン等のジヒドロキシジアリールエーテル類; 2,2′-dihydroxydiphenyl ether, 3,3′-dihydroxydiphenyl ether, 4,4′-dihydroxydiphenyl ether, 4,4′-dihydroxy-3,3′-dimethyldiphenyl ether, 1,4-bis (3-hydroxyphenoxy) Dihydroxy diaryl ethers such as benzene and 1,3-bis (4-hydroxyphenoxy) benzene;
2,2−ビス(4−ヒドロキシフェニル)プロパン(即ち、ビスフェノールA)、
1,1−ビス(4−ヒドロキシフェニル)プロパン、
2,2−ビス(3−メチル−4−ヒドロキシフェニル)プロパン、
2,2−ビス(3−メトキシ−4−ヒドロキシフェニル)プロパン、
2−(4−ヒドロキシフェニル)−2−(3−メトキシ−4−ヒドロキシフェニル)プロパン、
1,1−ビス(3−tert−ブチル−4−ヒドロキシフェニル)プロパン、
2,2−ビス(3,5−ジメチル−4−ヒドロキシフェニル)プロパン、
2,2−ビス(3−シクロヘキシル−4−ヒドロキシフェニル)プロパン、
2−(4−ヒドロキシフェニル)−2−(3−シクロヘキシル−4−ヒドロキシフェニル)プロパン、
α,α’−ビス(4−ヒドロキシフェニル)−1,4−ジイソプロピルベンゼン、
1,3−ビス[2−(4−ヒドロキシフェニル)−2−プロピル]ベンゼン、
ビス(4−ヒドロキシフェニル)メタン、
ビス(4−ヒドロキシフェニル)シクロヘキシルメタン、
ビス(4−ヒドロキシフェニル)フェニルメタン、
ビス(4−ヒドロキシフェニル)(4−プロペニルフェニル)メタン、
ビス(4−ヒドロキシフェニル)ジフェニルメタン、
ビス(4−ヒドロキシフェニル)ナフチルメタン、
1,1−ビス(4−ヒドロキシフェニル)エタン、
1,1−ビス(4−ヒドロキシフェニル)−1−フェニルエタン、
1,1−ビス(4−ヒドロキシフェニル)−1−ナフチルエタン、
1,1−ビス(4−ヒドロキシフェニル)ブタン、
2,2−ビス(4−ヒドロキシフェニル)ブタン、
2,2−ビス(4−ヒドロキシフェニル)ペンタン、
1,1−ビス(4−ヒドロキシフェニル)ヘキサン、
2,2−ビス(4−ヒドロキシフェニル)ヘキサン、
1,1−ビス(4−ヒドロキシフェニル)オクタン、
2,2−ビス(4−ヒドロキシフェニル)オクタン、
1,1−ビス(4−ヒドロキシフェニル)ヘキサン、
2,2−ビス(4−ヒドロキシフェニル)ヘキサン、
4,4−ビス(4−ヒドロキシフェニル)ヘプタン、
2,2−ビス(4−ヒドロキシフェニル)ノナン、
1,1−ビス(4−ヒドロキシフェニル)デカン、
1,1−ビス(4−ヒドロキシフェニル)ドデカン、
等のビス(ヒドロキシアリール)アルカン類;
2,2-bis (4-hydroxyphenyl) propane (ie, bisphenol A),
1,1-bis (4-hydroxyphenyl) propane,
2,2-bis (3-methyl-4-hydroxyphenyl) propane,
2,2-bis (3-methoxy-4-hydroxyphenyl) propane,
2- (4-hydroxyphenyl) -2- (3-methoxy-4-hydroxyphenyl) propane,
1,1-bis (3-tert-butyl-4-hydroxyphenyl) propane,
2,2-bis (3,5-dimethyl-4-hydroxyphenyl) propane,
2,2-bis (3-cyclohexyl-4-hydroxyphenyl) propane,
2- (4-hydroxyphenyl) -2- (3-cyclohexyl-4-hydroxyphenyl) propane,
α, α′-bis (4-hydroxyphenyl) -1,4-diisopropylbenzene,
1,3-bis [2- (4-hydroxyphenyl) -2-propyl] benzene,
Bis (4-hydroxyphenyl) methane,
Bis (4-hydroxyphenyl) cyclohexylmethane,
Bis (4-hydroxyphenyl) phenylmethane,
Bis (4-hydroxyphenyl) (4-propenylphenyl) methane,
Bis (4-hydroxyphenyl) diphenylmethane,
Bis (4-hydroxyphenyl) naphthylmethane,
1,1-bis (4-hydroxyphenyl) ethane,
1,1-bis (4-hydroxyphenyl) -1-phenylethane,
1,1-bis (4-hydroxyphenyl) -1-naphthylethane,
1,1-bis (4-hydroxyphenyl) butane,
2,2-bis (4-hydroxyphenyl) butane,
2,2-bis (4-hydroxyphenyl) pentane,
1,1-bis (4-hydroxyphenyl) hexane,
2,2-bis (4-hydroxyphenyl) hexane,
1,1-bis (4-hydroxyphenyl) octane,
2,2-bis (4-hydroxyphenyl) octane,
1,1-bis (4-hydroxyphenyl) hexane,
2,2-bis (4-hydroxyphenyl) hexane,
4,4-bis (4-hydroxyphenyl) heptane,
2,2-bis (4-hydroxyphenyl) nonane,
1,1-bis (4-hydroxyphenyl) decane,
1,1-bis (4-hydroxyphenyl) dodecane,
Bis (hydroxyaryl) alkanes such as;
1,1−ビス(4−ヒドロキシフェニル)シクロペンタン、
1,1−ビス(4−ヒドロキシフェニル)シクロヘキサン、
1,1−ビス(4−ヒドロキシフェニル)−3,3−ジメチルシクロヘキサン、
1,1−ビス(4−ヒドロキシフェニル)−3,4−ジメチルシクロヘキサン、
1,1−ビス(4−ヒドロキシフェニル)−3,5−ジメチルシクロヘキサン、
1,1−ビス(4−ヒドロキシフェニル)−3,3,5−トリメチルシクロヘキサン、
1,1−ビス(4−ヒドロキシ−3,5−ジメチルフェニル)−3,3,5−トリメチルシクロヘキサン、
1,1−ビス(4−ヒドロキシフェニル)−3−プロピル−5−メチルシクロヘキサン、
1,1−ビス(4−ヒドロキシフェニル)−3−tert−ブチル−シクロヘキサン、
1,1−ビス(4−ヒドロキシフェニル)−4−tert−ブチル−シクロヘキサン、
1,1−ビス(4−ヒドロキシフェニル)−3−フェニルシクロヘキサン、
1,1−ビス(4−ヒドロキシフェニル)−4−フェニルシクロヘキサン、
等のビス(ヒドロキシアリール)シクロアルカン類;
1,1-bis (4-hydroxyphenyl) cyclopentane,
1,1-bis (4-hydroxyphenyl) cyclohexane,
1,1-bis (4-hydroxyphenyl) -3,3-dimethylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3,4-dimethylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3,5-dimethylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3,3,5-trimethylcyclohexane,
1,1-bis (4-hydroxy-3,5-dimethylphenyl) -3,3,5-trimethylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3-propyl-5-methylcyclohexane,
1,1-bis (4-hydroxyphenyl) -3-tert-butyl-cyclohexane,
1,1-bis (4-hydroxyphenyl) -4-tert-butyl-cyclohexane,
1,1-bis (4-hydroxyphenyl) -3-phenylcyclohexane,
1,1-bis (4-hydroxyphenyl) -4-phenylcyclohexane,
Bis (hydroxyaryl) cycloalkanes such as;
9,9−ビス(4−ヒドロキシフェニル)フルオレン、
9,9−ビス(4−ヒドロキシ−3−メチルフェニル)フルオレン等のカルド構造含有ビスフェノール類;
9,9-bis (4-hydroxyphenyl) fluorene,
Cardio structure-containing bisphenols such as 9,9-bis (4-hydroxy-3-methylphenyl) fluorene;
4,4’−ジヒドロキシジフェニルスルフィド、
4,4’−ジヒドロキシ−3,3’−ジメチルジフェニルスルフィド等のジヒドロキシジアリールスルフィド類;
4,4′-dihydroxydiphenyl sulfide,
Dihydroxydiaryl sulfides such as 4,4′-dihydroxy-3,3′-dimethyldiphenyl sulfide;
4,4’−ジヒドロキシジフェニルスルホキシド、4,4’−ジヒドロキシ−3,3’−ジメチルジフェニルスルホキシド等のジヒドロキシジアリールスルホキシド類; Dihydroxydiaryl sulfoxides such as 4,4'-dihydroxydiphenyl sulfoxide, 4,4'-dihydroxy-3,3'-dimethyldiphenyl sulfoxide;
4,4’−ジヒドロキシジフェニルスルホン、
4,4’−ジヒドロキシ−3,3’−ジメチルジフェニルスルホン等のジヒドロキシジアリールスルホン類;
等が挙げられる。
4,4′-dihydroxydiphenyl sulfone,
Dihydroxydiaryl sulfones such as 4,4′-dihydroxy-3,3′-dimethyldiphenyl sulfone;
Etc.
これらの中ではビス(ヒドロキシアリール)アルカン類が好ましく、中でもビス(4−ヒドロキシフェニル)アルカン類が好ましく、特に耐衝撃性、耐熱性の点から2,2−ビス(4−ヒドロキシフェニル)プロパン(即ち、ビスフェノールA)が好ましい。
なお、芳香族ジヒドロキシ化合物は、1種を用いてもよく、2種以上を任意の組み合わせ及び比率で併用してもよい。
Among these, bis (hydroxyaryl) alkanes are preferable, and bis (4-hydroxyphenyl) alkanes are particularly preferable, and 2,2-bis (4-hydroxyphenyl) propane (especially from the viewpoint of impact resistance and heat resistance). That is, bisphenol A) is preferred.
In addition, 1 type may be used for an aromatic dihydroxy compound and it may use 2 or more types together by arbitrary combinations and a ratio.
また、脂肪族ポリカーボネート樹脂の原料となるモノマーの例を挙げると、
エタン−1,2−ジオール、プロパン−1,2−ジオール、プロパン−1,3−ジオール、2,2−ジメチルプロパン−1,3−ジオール、2−メチル−2−プロピルプロパン−1,3−ジオール、ブタン−1,4−ジオール、ペンタン−1,5−ジオール、ヘキサン−1,6−ジオール、デカン−1,10−ジオール等のアルカンジオール類;
In addition, when an example of a monomer that is a raw material of the aliphatic polycarbonate resin is given,
Ethane-1,2-diol, propane-1,2-diol, propane-1,3-diol, 2,2-dimethylpropane-1,3-diol, 2-methyl-2-propylpropane-1,3- Alkanediols such as diol, butane-1,4-diol, pentane-1,5-diol, hexane-1,6-diol, decane-1,10-diol;
シクロペンタン−1,2−ジオール、シクロヘキサン−1,2−ジオール、シクロヘキサン−1,4−ジオール、1,4−シクロヘキサンジメタノール、4−(2−ヒドロキシエチル)シクロヘキサノール、2,2,4,4−テトラメチル−シクロブタン−1,3−ジオール等のシクロアルカンジオール類; Cyclopentane-1,2-diol, cyclohexane-1,2-diol, cyclohexane-1,4-diol, 1,4-cyclohexanedimethanol, 4- (2-hydroxyethyl) cyclohexanol, 2,2,4, Cycloalkanediols such as 4-tetramethyl-cyclobutane-1,3-diol;
エチレングリコール、2,2’−オキシジエタノール(即ち、ジエチレングリコール)、トリエチレングリコール、プロピレングリコール、スピログリコール等のグリコール類; Glycols such as ethylene glycol, 2,2'-oxydiethanol (ie, diethylene glycol), triethylene glycol, propylene glycol, spiro glycol and the like;
1,2−ベンゼンジメタノール、1,3−ベンゼンジメタノール、1,4−ベンゼンジメタノール、1,4−ベンゼンジエタノール、1,3−ビス(2−ヒドロキシエトキシ)ベンゼン、1,4−ビス(2−ヒドロキシエトキシ)ベンゼン、2,3−ビス(ヒドロキシメチル)ナフタレン、1,6−ビス(ヒドロキシエトキシ)ナフタレン、4,4’−ビフェニルジメタノール、4,4’−ビフェニルジエタノール、1,4−ビス(2−ヒドロキシエトキシ)ビフェニル、ビスフェノールAビス(2−ヒドロキシエチル)エーテル、ビスフェノールSビス(2−ヒドロキシエチル)エーテル等のアラルキルジオール類; 1,2-benzenedimethanol, 1,3-benzenedimethanol, 1,4-benzenedimethanol, 1,4-benzenediethanol, 1,3-bis (2-hydroxyethoxy) benzene, 1,4-bis ( 2-hydroxyethoxy) benzene, 2,3-bis (hydroxymethyl) naphthalene, 1,6-bis (hydroxyethoxy) naphthalene, 4,4′-biphenyldimethanol, 4,4′-biphenyldiethanol, 1,4- Aralkyl diols such as bis (2-hydroxyethoxy) biphenyl, bisphenol A bis (2-hydroxyethyl) ether, bisphenol S bis (2-hydroxyethyl) ether;
1,2−エポキシエタン(即ち、エチレンオキシド)、1,2−エポキシプロパン(即ち、プロピレンオキシド)、1,2−エポキシシクロペンタン、1,2−エポキシシクロヘキサン、1,4−エポキシシクロヘキサン、1−メチル−1,2−エポキシシクロヘキサン、2,3−エポキシノルボルナン、1,3−エポキシプロパン等の環状エーテル類;等が挙げられる。 1,2-epoxyethane (ie ethylene oxide), 1,2-epoxypropane (ie propylene oxide), 1,2-epoxycyclopentane, 1,2-epoxycyclohexane, 1,4-epoxycyclohexane, 1-methyl And cyclic ethers such as -1,2-epoxycyclohexane, 2,3-epoxynorbornane, and 1,3-epoxypropane;
ポリカーボネート樹脂の原料となるモノマーのうち、カーボネート前駆体の例を挙げると、カルボニルハライド、カーボネートエステル等が使用される。なお、カーボネート前駆体は、1種を用いてもよく、2種以上を任意の組み合わせ及び比率で併用してもよい。 Among the monomers used as the raw material for the polycarbonate resin, carbonyl halides, carbonate esters and the like are used as examples of the carbonate precursor. In addition, 1 type may be used for a carbonate precursor and it may use 2 or more types together by arbitrary combinations and a ratio.
カルボニルハライドとしては、具体的には例えば、ホスゲン;ジヒドロキシ化合物のビスクロロホルメート体、ジヒドロキシ化合物のモノクロロホルメート体等のハロホルメート等が挙げられる。 Specific examples of carbonyl halides include phosgene; haloformates such as bischloroformate of dihydroxy compounds and monochloroformate of dihydroxy compounds.
カーボネートエステルとしては、具体的には例えば、ジフェニルカーボネート、ジトリルカーボネート等のジアリールカーボネート類;ジメチルカーボネート、ジエチルカーボネート等のジアルキルカーボネート類;ジヒドロキシ化合物のビスカーボネート体、ジヒドロキシ化合物のモノカーボネート体、環状カーボネート等のジヒドロキシ化合物のカーボネート体等が挙げられる。 Specific examples of the carbonate ester include diaryl carbonates such as diphenyl carbonate and ditolyl carbonate; dialkyl carbonates such as dimethyl carbonate and diethyl carbonate; biscarbonate bodies of dihydroxy compounds, monocarbonate bodies of dihydroxy compounds, and cyclic carbonates. And carbonate bodies of dihydroxy compounds such as
・ポリカーボネート樹脂の製造方法
ポリカーボネート樹脂の製造方法は、特に限定されるものではなく、任意の方法を採用できる。その例を挙げると、界面重合法、溶融エステル交換法、ピリジン法、環状カーボネート化合物の開環重合法、プレポリマーの固相エステル交換法などを挙げることができる。
以下、これらの方法のうち、特に好適なものについて具体的に説明する。
-Manufacturing method of polycarbonate resin The manufacturing method of polycarbonate resin is not specifically limited, Arbitrary methods are employable. Examples thereof include an interfacial polymerization method, a melt transesterification method, a pyridine method, a ring-opening polymerization method of a cyclic carbonate compound, and a solid phase transesterification method of a prepolymer.
Hereinafter, a particularly preferable one of these methods will be described in detail.
・・界面重合法
まず、ポリカーボネート樹脂を界面重合法で製造する場合について説明する。
界面重合法では、反応に不活性な有機溶媒及びアルカリ水溶液の存在下で、通常pHを9以上に保ち、ジヒドロキシ化合物とカーボネート前駆体(好ましくは、ホスゲン)とを反応させた後、重合触媒の存在下で界面重合を行うことによってポリカーボネート樹脂を得る。なお、反応系には、必要に応じて分子量調整剤(末端停止剤)を存在させるようにしてもよく、ジヒドロキシ化合物の酸化防止のために酸化防止剤を存在させるようにしてもよい。
.. Interfacial polymerization method First, the case where a polycarbonate resin is produced by the interfacial polymerization method will be described.
In the interfacial polymerization method, a dihydroxy compound and a carbonate precursor (preferably phosgene) are reacted in the presence of an organic solvent inert to the reaction and an aqueous alkaline solution, usually at a pH of 9 or higher. Polycarbonate resin is obtained by interfacial polymerization in the presence. In the reaction system, a molecular weight adjusting agent (terminal terminator) may be present as necessary, or an antioxidant may be present to prevent the oxidation of the dihydroxy compound.
ジヒドロキシ化合物及びカーボネート前駆体は、前述のとおりである。なお、カーボネート前駆体の中でもホスゲンを用いることが好ましく、ホスゲンを用いた場合の方法は特にホスゲン法と呼ばれる。 The dihydroxy compound and the carbonate precursor are as described above. Of the carbonate precursors, phosgene is preferably used, and a method using phosgene is particularly called a phosgene method.
反応に不活性な有機溶媒としては、例えば、ジクロロメタン、1,2−ジクロロエタン、クロロホルム、モノクロロベンゼン、ジクロロベンゼン等の塩素化炭化水素等;ベンゼン、トルエン、キシレン等の芳香族炭化水素;などが挙げられる。なお、有機溶媒は、1種を用いてもよく、2種以上を任意の組み合わせ及び比率で併用してもよい。 Examples of the organic solvent inert to the reaction include chlorinated hydrocarbons such as dichloromethane, 1,2-dichloroethane, chloroform, monochlorobenzene and dichlorobenzene; aromatic hydrocarbons such as benzene, toluene and xylene; It is done. In addition, 1 type may be used for an organic solvent and it may use 2 or more types together by arbitrary combinations and a ratio.
アルカリ水溶液に含有されるアルカリ化合物としては、例えば、水酸化ナトリウム、水酸化カリウム、水酸化リチウム、炭酸水素ナトリウム等のアルカリ金属化合物やアルカリ土類金属化合物が挙げられるが、中でも水酸化ナトリウム及び水酸化カリウムが好ましい。なお、アルカリ化合物は、1種を用いてもよく、2種以上を任意の組み合わせ及び比率で併用してもよい。 Examples of the alkali compound contained in the alkaline aqueous solution include alkali metal compounds and alkaline earth metal compounds such as sodium hydroxide, potassium hydroxide, lithium hydroxide, and sodium hydrogen carbonate, among which sodium hydroxide and water Potassium oxide is preferred. In addition, 1 type may be used for an alkali compound and it may use 2 or more types together by arbitrary combinations and a ratio.
アルカリ水溶液中のアルカリ化合物の濃度に制限はないが、通常、反応のアルカリ水溶液中のpHを10〜12にコントロールするために、5〜10質量%で使用される。また、例えばホスゲンを吹き込むに際しては、水相のpHが10〜12、好ましくは10〜11になる様にコントロールするために、ビスフェノール化合物とアルカリ化合物とのモル比を、通常1:1.9以上、中でも1:2.0以上、また、通常1:3.2以下、中でも1:2.5以下とすることが好ましい。 Although there is no restriction | limiting in the density | concentration of the alkali compound in alkaline aqueous solution, Usually, in order to control pH in the alkaline aqueous solution of reaction to 10-12, it is used at 5-10 mass%. For example, when phosgene is blown, the molar ratio of the bisphenol compound and the alkali compound is usually 1: 1.9 or more in order to control the pH of the aqueous phase to be 10 to 12, preferably 10 to 11. Among these, it is preferable that the ratio is 1: 2.0 or more, usually 1: 3.2 or less, and more preferably 1: 2.5 or less.
重合触媒としては、例えば、トリメチルアミン、トリエチルアミン、トリブチルアミン、トリプロピルアミン、トリヘキシルアミン等の脂肪族三級アミン;N,N’−ジメチルシクロヘキシルアミン、N,N’−ジエチルシクロヘキシルアミン等の脂環式三級アミン;N,N’−ジメチルアニリン、N,N’−ジエチルアニリン等の芳香族三級アミン;トリメチルベンジルアンモニウムクロライド、テトラメチルアンモニウムクロライド、トリエチルベンジルアンモニウムクロライド等の第四級アンモニウム塩等;ピリジン;グアニジンの塩;等が挙げられる。なお、重合触媒は、1種を用いてもよく、2種以上を任意の組み合わせ及び比率で併用してもよい。 Examples of the polymerization catalyst include aliphatic tertiary amines such as trimethylamine, triethylamine, tributylamine, tripropylamine, and trihexylamine; alicyclic rings such as N, N′-dimethylcyclohexylamine and N, N′-diethylcyclohexylamine. Formula tertiary amines; aromatic tertiary amines such as N, N′-dimethylaniline and N, N′-diethylaniline; quaternary ammonium salts such as trimethylbenzylammonium chloride, tetramethylammonium chloride, triethylbenzylammonium chloride, etc. Pyridine; guanidine salt; and the like. In addition, 1 type may be used for a polymerization catalyst and it may use 2 or more types together by arbitrary combinations and a ratio.
分子量調節剤としては、例えば、一価のフェノール性水酸基を有する芳香族フェノール;メタノール、ブタノールなどの脂肪族アルコール;メルカプタン;フタル酸イミド等が挙げられるが、中でも芳香族フェノールが好ましい。このような芳香族フェノールとしては、具体的に、m−メチルフェノール、p−メチルフェノール、m−プロピルフェノール、p−プロピルフェノール、p−tert−ブチルフェノール、p−長鎖アルキル置換フェノール等のアルキル基置換フェノール;イソプロぺニルフェノール等のビニル基含有フェノール;エポキシ基含有フェノール;o−ヒドロキシ安息香酸、2−メチル−6−ヒドロキシフェニル酢酸等のカルボキシル基含有フェノール;等が挙げられる。なお、分子量調整剤は、1種を用いてもよく、2種以上を任意の組み合わせ及び比率で併用してもよい。 Examples of the molecular weight regulator include aromatic phenols having a monohydric phenolic hydroxyl group; aliphatic alcohols such as methanol and butanol; mercaptans; phthalimides and the like. Of these, aromatic phenols are preferred. Specific examples of such aromatic phenols include alkyl groups such as m-methylphenol, p-methylphenol, m-propylphenol, p-propylphenol, p-tert-butylphenol, and p-long chain alkyl-substituted phenol. Examples thereof include substituted phenols; vinyl group-containing phenols such as isopropenyl phenol; epoxy group-containing phenols; carboxyl group-containing phenols such as o-hydroxybenzoic acid and 2-methyl-6-hydroxyphenylacetic acid; In addition, a molecular weight regulator may use 1 type and may use 2 or more types together by arbitrary combinations and a ratio.
分子量調節剤の使用量は、ジヒドロキシ化合物100モルに対して、通常0.5モル以上、好ましくは1モル以上であり、また、通常50モル以下、好ましくは30モル以下である。分子量調整剤の使用量をこのような範囲とすることで、樹脂組成物の熱安定性及び耐加水分解性を向上させることができる。 The usage-amount of a molecular weight regulator is 0.5 mol or more normally with respect to 100 mol of dihydroxy compounds, Preferably it is 1 mol or more, and is 50 mol or less normally, Preferably it is 30 mol or less. By making the usage-amount of a molecular weight modifier into such a range, the thermal stability and hydrolysis resistance of a resin composition can be improved.
反応の際に、反応基質、反応媒、触媒、添加剤等を混合する順番は、所望のポリカーボネート樹脂が得られる限り任意であり、適切な順番を任意に設定すればよい。例えば、カーボネート前駆体としてホスゲンを用いた場合には、分子量調節剤はジヒドロキシ化合物とホスゲンとの反応(ホスゲン化)の時から重合反応開始時までの間であれば任意の時期に混合できる。
なお、反応温度は通常0〜40℃であり、反応時間は通常は数分(例えば、10分)〜数時間(例えば、6時間)である。
In the reaction, the order of mixing the reaction substrate, reaction medium, catalyst, additive and the like is arbitrary as long as a desired polycarbonate resin is obtained, and an appropriate order may be arbitrarily set. For example, when phosgene is used as the carbonate precursor, the molecular weight regulator can be mixed at any time as long as it is between the reaction (phosgenation) of the dihydroxy compound and phosgene and the start of the polymerization reaction.
In addition, reaction temperature is 0-40 degreeC normally, and reaction time is normally several minutes (for example, 10 minutes)-several hours (for example, 6 hours).
・・溶融エステル交換法
次に、ポリカーボネート樹脂を溶融エステル交換法で製造する場合について説明する。
溶融エステル交換法では、例えば、炭酸ジエステルとジヒドロキシ化合物とのエステル交換反応を行う。
-Melt transesterification method Next, the case where a polycarbonate resin is manufactured by the melt transesterification method is demonstrated.
In the melt transesterification method, for example, a transesterification reaction between a carbonic acid diester and a dihydroxy compound is performed.
ジヒドロキシ化合物は、前述の通りである。
一方、炭酸ジエステルとしては、例えば、ジメチルカーボネート、ジエチルカーボネート、ジ−tert−ブチルカーボネート等の炭酸ジアルキル化合物;ジフェニルカーボネート;ジトリルカーボネート等の置換ジフェニルカーボネートなどが挙げられる。中でも、ジフェニルカーボネート及び置換ジフェニルカーボネートが好ましく、特にジフェニルカーボネートがより好ましい。なお、炭酸ジエステルは1種を用いてもよく、2種以上を任意の組み合わせ及び比率で併用してもよい。
The dihydroxy compound is as described above.
On the other hand, examples of the carbonic acid diester include dialkyl carbonate compounds such as dimethyl carbonate, diethyl carbonate, and di-tert-butyl carbonate; diphenyl carbonate; substituted diphenyl carbonate such as ditolyl carbonate, and the like. Among these, diphenyl carbonate and substituted diphenyl carbonate are preferable, and diphenyl carbonate is more preferable. In addition, carbonic acid diester may use 1 type and may use 2 or more types together by arbitrary combinations and a ratio.
ジヒドロキシ化合物と炭酸ジエステルとの比率は、所望のポリカーボネート樹脂が得られる限り任意であるが、ジヒドロキシ化合物1モルに対して、炭酸ジエステルを等モル量以上用いることが好ましく、中でも1.01モル以上用いることがより好ましい。なお、上限は通常1.30モル以下である。このような範囲にすることで、末端水酸基量を好適な範囲に調整できる。 The ratio of the dihydroxy compound and the carbonic acid diester is arbitrary as long as the desired polycarbonate resin is obtained, but it is preferable to use an equimolar amount or more of the carbonic acid diester with respect to 1 mol of the dihydroxy compound, and above all, 1.01 mol or more is used. It is more preferable. The upper limit is usually 1.30 mol or less. By setting it as such a range, the amount of terminal hydroxyl groups can be adjusted to a suitable range.
ポリカーボネート樹脂では、その末端水酸基量が熱安定性、加水分解安定性、色調等に大きな影響を及ぼす傾向がある。このため、公知の任意の方法によって末端水酸基量を必要に応じて調整してもよい。エステル交換反応においては、通常、炭酸ジエステルと芳香族ジヒドロキシ化合物との混合比率;エステル交換反応時の減圧度などを調整することにより、末端水酸基量を調整したポリカーボネート樹脂を得ることができる。なお、この操作により、通常は得られるポリカーボネート樹脂の分子量を調整することもできる。 In the polycarbonate resin, the amount of terminal hydroxyl groups tends to have a great influence on thermal stability, hydrolysis stability, color tone and the like. For this reason, you may adjust the amount of terminal hydroxyl groups as needed by a well-known arbitrary method. In the transesterification reaction, a polycarbonate resin in which the amount of terminal hydroxyl groups is adjusted can be usually obtained by adjusting the mixing ratio of the carbonic diester and the aromatic dihydroxy compound; the degree of vacuum during the transesterification reaction, and the like. In addition, the molecular weight of the polycarbonate resin usually obtained can also be adjusted by this operation.
炭酸ジエステルとジヒドロキシ化合物との混合比率を調整して末端水酸基量を調整する場合、その混合比率は前記の通りである。
また、より積極的な調整方法としては、反応時に別途、末端停止剤を混合する方法が挙げられる。この際の末端停止剤としては、例えば、一価フェノール類、一価カルボン酸類、炭酸ジエステル類などが挙げられる。なお、末端停止剤は、1種を用いてもよく、2種以上を任意の組み合わせ及び比率で併用してもよい。
When adjusting the amount of terminal hydroxyl groups by adjusting the mixing ratio of the carbonic acid diester and the dihydroxy compound, the mixing ratio is as described above.
Further, as a more aggressive adjustment method, there may be mentioned a method in which a terminal terminator is mixed separately during the reaction. Examples of the terminal terminator at this time include monohydric phenols, monovalent carboxylic acids, carbonic acid diesters, and the like. In addition, 1 type may be used for a terminal terminator and it may use 2 or more types together by arbitrary combinations and a ratio.
溶融エステル交換法によりポリカーボネート樹脂を製造する際には、通常、エステル交換触媒が使用される。エステル交換触媒は任意のものを使用できる。なかでも、例えばアルカリ金属化合物及び/又はアルカリ土類金属化合物を用いることが好ましい。また補助的に、例えば塩基性硼素化合物、塩基性リン化合物、塩基性アンモニウム化合物、アミン系化合物などの塩基性化合物を併用してもよい。なお、エステル交換触媒は、1種を用いてもよく、2種以上を任意の組み合わせ及び比率で併用してもよい。 When producing a polycarbonate resin by the melt transesterification method, a transesterification catalyst is usually used. Any transesterification catalyst can be used. Among them, it is preferable to use, for example, an alkali metal compound and / or an alkaline earth metal compound. In addition, for example, basic compounds such as basic boron compounds, basic phosphorus compounds, basic ammonium compounds, and amine compounds may be used in combination. In addition, 1 type may be used for a transesterification catalyst and it may use 2 or more types together by arbitrary combinations and a ratio.
溶融エステル交換法において、反応温度は通常100〜320℃である。また、反応時の圧力は通常2mmHg以下の減圧条件である。具体的操作としては、前記の条件で、芳香族ヒドロキシ化合物等の副生成物を除去しながら、溶融重縮合反応を行えばよい。 In the melt transesterification method, the reaction temperature is usually 100 to 320 ° C. The pressure during the reaction is usually a reduced pressure condition of 2 mmHg or less. As a specific operation, a melt polycondensation reaction may be performed under the above-mentioned conditions while removing a by-product such as an aromatic hydroxy compound.
溶融重縮合反応は、バッチ式、連続式の何れの方法でも行うことができる。バッチ式で行う場合、反応基質、反応媒、触媒、添加剤等を混合する順番は、所望の芳香族ポリカーボネート樹脂が得られる限り任意であり、適切な順番を任意に設定すればよい。ただし中でも、ポリカーボネート樹脂の安定性等を考慮すると、溶融重縮合反応は連続式で行うことが好ましい。 The melt polycondensation reaction can be performed by either a batch method or a continuous method. When performing by a batch type, the order which mixes a reaction substrate, a reaction medium, a catalyst, an additive, etc. is arbitrary as long as a desired aromatic polycarbonate resin is obtained, What is necessary is just to set an appropriate order arbitrarily. However, considering the stability of the polycarbonate resin and the like, the melt polycondensation reaction is preferably carried out continuously.
溶融エステル交換法においては、必要に応じて、触媒失活剤を用いてもよい。触媒失活剤としてはエステル交換触媒を中和する化合物を任意に用いることができる。その例を挙げると、イオウ含有酸性化合物及びその誘導体などが挙げられる。なお、触媒失活剤は、1種を用いてもよく、2種以上を任意の組み合わせ及び比率で併用してもよい。 In the melt transesterification method, a catalyst deactivator may be used as necessary. As the catalyst deactivator, any compound that neutralizes the transesterification catalyst can be used. Examples thereof include sulfur-containing acidic compounds and derivatives thereof. In addition, 1 type may be used for a catalyst deactivator and it may use 2 or more types together by arbitrary combinations and a ratio.
触媒失活剤の使用量は、前記のエステル交換触媒が含有するアルカリ金属又はアルカリ土類金属に対して、通常0.5当量以上、好ましくは1当量以上であり、また、通常10当量以下、好ましくは5当量以下である。更には、ポリカーボネート樹脂に対して、通常1ppm以上であり、また、通常100ppm以下、好ましくは20ppm以下である。 The amount of the catalyst deactivator used is usually 0.5 equivalents or more, preferably 1 equivalent or more, and usually 10 equivalents or less, relative to the alkali metal or alkaline earth metal contained in the transesterification catalyst. Preferably it is 5 equivalents or less. Furthermore, it is 1 ppm or more normally with respect to polycarbonate resin, and is 100 ppm or less normally, Preferably it is 20 ppm or less.
・ポリカーボネート樹脂に関するその他の事項
ポリカーボネート樹脂の分子量は、適宜選択して決定すればよいが、粘度平均分子量[Mv]で通常10000以上、好ましくは16000以上、より好ましくは17000以上、より好ましくは18000以上であり、また、通常40000以下、好ましくは30000以下である。
-Other matters concerning polycarbonate resin The molecular weight of the polycarbonate resin may be appropriately selected and determined, but is usually 10,000 or more, preferably 16000 or more, more preferably 17000 or more, more preferably 18000 or more in terms of viscosity average molecular weight [Mv]. Moreover, it is 40000 or less normally, Preferably it is 30000 or less.
なお、粘度平均分子量[Mv]とは、溶媒としてメチレンクロライドを使用し、ウベローデ粘度計を用いて温度20℃での極限粘度[η](単位dl/g)を求め、Schnellの粘度式、すなわち、η=1.23×10−4Mv0.83 から算出される値を意味する。また、極限粘度[η]とは、各溶液濃度[C](g/dl)での比粘度[ηsp]を測定し、下記式により算出した値である。
ポリカーボネート樹脂の末端水酸基濃度は任意であり、適宜選択して決定すればよいが、通常1000ppm以下、好ましくは800ppm以下、より好ましくは600ppm以下である。これによりポリカーボネート樹脂の滞留熱安定性及び色調をより向上させることができる。また、その下限は、特に溶融エステル交換法で製造されたポリカーボネート樹脂では、通常10ppm以上、好ましくは30ppm以上、より好ましくは40ppm以上である。これにより、分子量の低下を抑制し、樹脂組成物の機械的特性をより向上させることができる。 The terminal hydroxyl group concentration of the polycarbonate resin is arbitrary and may be appropriately selected and determined, but is usually 1000 ppm or less, preferably 800 ppm or less, more preferably 600 ppm or less. Thereby, the residence heat stability and color tone of polycarbonate resin can be improved more. In addition, the lower limit is usually 10 ppm or more, preferably 30 ppm or more, more preferably 40 ppm or more, particularly for polycarbonate resins produced by the melt transesterification method. Thereby, the fall of molecular weight can be suppressed and the mechanical characteristic of a resin composition can be improved more.
なお、末端水酸基濃度の単位は、ポリカーボネート樹脂の質量に対する、末端水酸基の質量をppmで表示したものである。その測定方法は、四塩化チタン/酢酸法による比色定量(Macromol.Chem.88 215(1965)に記載の方法)である。 In addition, the unit of a terminal hydroxyl group density | concentration represents the mass of the terminal hydroxyl group with respect to the mass of polycarbonate resin in ppm. The measurement method is colorimetric determination (method described in Macromol. Chem. 88 215 (1965)) by the titanium tetrachloride / acetic acid method.
ポリカーボネート樹脂は、ポリカーボネート樹脂単独(ポリカーボネート樹脂単独とは、ポリカーボネート樹脂の1種のみを含む態様に限定されず、例えば、モノマー組成や分子量が互いに異なる複数種のポリカーボネート樹脂を含む態様を含む意味で用いる。)で用いてもよく、ポリカーボネート樹脂と他の熱可塑性樹脂とのアロイ(混合物)とを組み合わせて用いてもよい。さらに、例えば、難燃性や耐衝撃性をさらに高める目的で、ポリカーボネート樹脂を、シロキサン構造を有するオリゴマーまたはポリマーとの共重合体;熱酸化安定性や難燃性をさらに向上させる目的でリン原子を有するモノマー、オリゴマーまたはポリマーとの共重合体;熱酸化安定性を向上させる目的で、ジヒドロキシアントラキノン構造を有するモノマー、オリゴマーまたはポリマーとの共重合体;光学的性質を改良するためにポリスチレン等のオレフィン系構造を有するオリゴマーまたはポリマーとの共重合体;耐薬品性を向上させる目的でポリエステル樹脂オリゴマーまたはポリマーとの共重合体;等の、ポリカーボネート樹脂を主体とする共重合体として構成してもよい。 The polycarbonate resin is a polycarbonate resin alone (the polycarbonate resin alone is not limited to an embodiment containing only one type of polycarbonate resin, and is used in a sense including an embodiment containing a plurality of types of polycarbonate resins having different monomer compositions and molecular weights, for example. .), Or an alloy (mixture) of a polycarbonate resin and another thermoplastic resin may be used in combination. Further, for example, for the purpose of further improving flame retardancy and impact resistance, a polycarbonate resin is copolymerized with an oligomer or polymer having a siloxane structure; for the purpose of further improving thermal oxidation stability and flame retardancy A monomer, oligomer or polymer having a copolymer; a monomer, oligomer or polymer having a dihydroxyanthraquinone structure for the purpose of improving thermal oxidation stability; A copolymer with an oligomer or polymer having an olefin structure; a copolymer with a polyester resin oligomer or polymer for the purpose of improving chemical resistance; Good.
また、成形品の外観の向上や流動性の向上を図るため、ポリカーボネート樹脂は、ポリカーボネートオリゴマーを含有していてもよい。このポリカーボネートオリゴマーの粘度平均分子量[Mv]は、通常1500以上、好ましくは2000以上であり、また、通常9500以下、好ましくは9000以下である。さらに、含有されるポリカーボネートリゴマーは、ポリカーボネート樹脂(ポリカーボネートオリゴマーを含む)の30質量%以下とすることが好ましい。 Further, in order to improve the appearance of the molded product and improve the fluidity, the polycarbonate resin may contain a polycarbonate oligomer. The viscosity average molecular weight [Mv] of this polycarbonate oligomer is usually 1500 or more, preferably 2000 or more, and is usually 9500 or less, preferably 9000 or less. Furthermore, the polycarbonate ligomer contained is preferably 30% by mass or less of the polycarbonate resin (including the polycarbonate oligomer).
さらにポリカーボネート樹脂は、バージン原料だけでなく、使用済みの製品から再生されたポリカーボネート樹脂(いわゆるマテリアルリサイクルされたポリカーボネート樹脂)であってもよい。前記の使用済みの製品としては、例えば、光学ディスク等の光記録媒体;導光板;自動車窓ガラス、自動車ヘッドランプレンズ、風防等の車両透明部材;水ボトル等の容器;メガネレンズ;防音壁、ガラス窓、波板等の建築部材などが挙げられる。また、製品の不適合品、スプルー、ランナー等から得られた粉砕品またはそれらを溶融して得たペレット等も使用可能である。
ただし、再生されたポリカーボネート樹脂は、ポリカーボネート樹脂のうち、80質量%以下であることが好ましく、中でも50質量%以下であることがより好ましい。再生されたポリカーボネート樹脂は、熱劣化や経年劣化等の劣化を受けている可能性が高いため、このようなポリカーボネート樹脂を前記の範囲よりも多く用いた場合、色相や機械的物性を低下させる可能性があるためである。
Further, the polycarbonate resin may be not only a virgin raw material but also a polycarbonate resin regenerated from a used product (so-called material-recycled polycarbonate resin). Examples of the used products include: optical recording media such as optical disks; light guide plates; vehicle window glass, vehicle headlamp lenses, windshields and other vehicle transparent members; water bottles and other containers; eyeglass lenses; Examples include architectural members such as glass windows and corrugated sheets. Also, non-conforming products, pulverized products obtained from sprues, runners, etc., or pellets obtained by melting them can be used.
However, the regenerated polycarbonate resin is preferably 80% by mass or less of the polycarbonate resin, and more preferably 50% by mass or less. Recycled polycarbonate resin is likely to have undergone deterioration such as heat deterioration and aging deterioration, so when such polycarbonate resin is used more than the above range, hue and mechanical properties can be reduced. It is because there is sex.
[窒化硼素]
本発明のポリカーボネート樹脂組成物は、窒化硼素を含有する。窒化硼素を、ポリカーボネート樹脂100質量部に対し、10〜50質量部の割合で含有することによって、得られるポリカーボネート樹脂組成物の熱伝導性を大きく向上させることができ、また、平均粒径が10μm以上であるタルクの15〜80質量部という特定量と併せて含有することにより、優れた熱伝導性と高度の耐熱性を有しながら、優れた耐衝撃性を示す熱伝導性ポリカーボネート樹脂組成物とすることができる。
[Boron nitride]
The polycarbonate resin composition of the present invention contains boron nitride. By containing boron nitride at a ratio of 10 to 50 parts by mass with respect to 100 parts by mass of the polycarbonate resin, the thermal conductivity of the obtained polycarbonate resin composition can be greatly improved, and the average particle size is 10 μm. The heat conductive polycarbonate resin composition showing excellent impact resistance while having excellent heat conductivity and high heat resistance by containing together with the specific amount of 15 to 80 parts by mass of talc as described above. It can be.
本発明に用いる窒化硼素は、その形状は特に限定されず、任意のものを使用できる。具体的には、球状、線状(繊維状)、平板状(鱗片状)、曲板状、針状等が挙げられる。そして単粒体として、または顆粒状(単粒の凝集体)として用いてもよい。本発明では鱗片状のものを用いると、熱伝導性に優れた樹脂組成物が得られるとともに、機械的特性が良好となるので好ましい。 The shape of the boron nitride used in the present invention is not particularly limited, and an arbitrary one can be used. Specific examples include a spherical shape, a linear shape (fiber shape), a flat plate shape (scale shape), a curved plate shape, and a needle shape. Then, it may be used as a single particle or as a granule (single particle aggregate). In the present invention, it is preferable to use a scale-like material because a resin composition excellent in thermal conductivity can be obtained and the mechanical properties become good.
窒化硼素には、c−BN(閃亜鉛鉱構造)、w−BN(ウルツ鉱構造)、h−BN(六方晶構造)、r−BN(菱面体晶構造)など、複数の安定構造が知られている。本発明では、いずれの窒化硼素を用いてもよいが、なかでも、六方晶構造の窒化硼素を用いるのが熱伝導性が充分となりかつ樹脂成形体を得る際に用いる成形機や金型の摩耗が低減できるので、好ましい。 Boron nitride has several stable structures such as c-BN (zinc blende structure), w-BN (wurtzite structure), h-BN (hexagonal crystal structure), and r-BN (rhombohedral crystal structure). It has been. In the present invention, any boron nitride may be used. Among them, the use of hexagonal structure boron nitride provides sufficient thermal conductivity and wear of a molding machine or a mold used for obtaining a resin molded body. Is preferable.
窒化硼素の平均粒子径には制限はないが、好ましくは1〜300μmであり、より好ましくは2〜200μm、中でも5〜100μmであることが好ましい。 The average particle diameter of boron nitride is not limited, but is preferably 1 to 300 μm, more preferably 2 to 200 μm, and particularly preferably 5 to 100 μm.
窒化硼素としては、25℃における熱伝導率が30W/(m・K)以上であることが好ましく、中でも50W/(m・K)以上であるものが好ましい。 As boron nitride, the thermal conductivity at 25 ° C. is preferably 30 W / (m · K) or more, and more preferably 50 W / (m · K) or more.
本発明の熱伝導性ポリカーボネート樹脂組成物における窒化硼素の含有量は、ポリカーボネート樹脂100質量部に対して、10〜50質量部である。窒化硼素の含有量が10質量部未満では熱伝導性が不十分となり、また耐衝撃性の改良効果が不十分であり、逆に50質量部を超えると耐衝撃性が不十分となりやすい。窒化硼素の含有量は、好ましくは13質量部以上、より好ましくは15質量部以上、中でも20質量部以上であり、また好ましくは45質量部以下、より好ましくは40質量部以下である。 Content of boron nitride in the heat conductive polycarbonate resin composition of this invention is 10-50 mass parts with respect to 100 mass parts of polycarbonate resin. If the boron nitride content is less than 10 parts by mass, the thermal conductivity is insufficient, and the effect of improving the impact resistance is insufficient. Conversely, if it exceeds 50 parts by mass, the impact resistance tends to be insufficient. The content of boron nitride is preferably 13 parts by mass or more, more preferably 15 parts by mass or more, especially 20 parts by mass or more, and preferably 45 parts by mass or less, more preferably 40 parts by mass or less.
[タルク]
本発明のポリカーボネート樹脂組成物は、平均粒径が10μm以上であるタルクを、ポリカーボネート樹脂100質量部に対し、15〜80質量部含有する。
タルクとしては、天然物であっても合成されたものであってもよい。また、焼成物であっても未焼成物であってもよく、さらに、水和物であっても無水和物であってもよい。
[talc]
The polycarbonate resin composition of this invention contains 15-80 mass parts of talc whose average particle diameter is 10 micrometers or more with respect to 100 mass parts of polycarbonate resin.
The talc may be a natural product or a synthesized talc. Further, it may be a fired product or an unfired product, and may be a hydrate or an anhydrous product.
タルクの平均粒径が10μm以上であることで、これを窒化硼素と併せて含有することでシャルピー衝撃値が極めて優れることとなり、本発明のポリカーボネート樹脂組成物はノッチなしシャルピー衝撃強度が好ましくは105kJ/m2以上もの高い耐衝撃性を達成することができる。タルクの平均粒径は好ましくは13μm以上、さらには15μm以上であることが好ましく、その上限としては好ましくは100μm以下、より好ましくは50μm以下、中でも40μm以下、とりわけ30μm以下が好ましい。タルクの粒径が100μmを超えると樹脂組成物の流動性が悪化し、薄肉での成形が困難となりやすく、また異物となって耐衝撃性や他の機械物性が低下する傾向がある。 When the average particle diameter of talc is 10 μm or more, the Charpy impact value is extremely excellent by containing this together with boron nitride, and the polycarbonate resin composition of the present invention preferably has an unnotched Charpy impact strength of 105 kJ. High impact resistance as high as / m 2 can be achieved. The average particle size of talc is preferably 13 μm or more, more preferably 15 μm or more, and the upper limit thereof is preferably 100 μm or less, more preferably 50 μm or less, especially 40 μm or less, especially 30 μm or less. When the particle size of talc exceeds 100 μm, the fluidity of the resin composition is deteriorated and molding with a thin wall tends to be difficult, and it becomes a foreign substance and impact resistance and other mechanical properties tend to decrease.
タルクは、ポリカーボネート樹脂との接着性を高めるため、シラン処理剤等の各種表面処理剤で表面処理がなされたものであってもよい。表面処理剤としては特に限定されず、従来公知のものを使用することができるが、メチル水素シロキサン等のハイドロジェンシロキサン化合物やエポキシシラン等のエポキシ基含有シランカップリング剤、及び、アミノシラン等のアミノ基含有シランカップリング剤が、ポリカーボネート樹脂の物性を低下させることが少ないため好ましい。その他にもポリオキシエチレンシラン等を用いることができる。 Talc may be surface-treated with various surface treatment agents such as a silane treatment agent in order to enhance the adhesion to the polycarbonate resin. The surface treatment agent is not particularly limited, and a conventionally known one can be used, but a hydrogen siloxane compound such as methylhydrogen siloxane, an epoxy group-containing silane coupling agent such as epoxy silane, and an amino such as amino silane. A group-containing silane coupling agent is preferable because it hardly reduces the physical properties of the polycarbonate resin. In addition, polyoxyethylene silane or the like can be used.
タルクを表面処理剤で処理する方法には特に限定はなく、通常の方法で実施しうる。たとえば、タルクに表面処理剤を添加し、溶液中であるいは加熱しながら撹拌あるいは混合することで行なうことができる。 There is no particular limitation on the method for treating talc with the surface treatment agent, and it can be carried out by a usual method. For example, it can be carried out by adding a surface treatment agent to talc and stirring or mixing in solution or with heating.
上記したタルクは、1種類のみを単独で用いてもよいし、平均粒子径、種類、表面処理剤等が異なる2種以上を併用してもよい。 As for the talc described above, only one type may be used alone, or two or more types having different average particle diameters, types, surface treatment agents, and the like may be used in combination.
タルクの含有量は、前述のとおり、ポリカーボネート樹脂100質量部に対し、10〜80質量部である。含有量が10質量部に満たないと得られる耐衝撃性改善効果に乏しいうえ、耐熱性、機械的強度の改良効果も乏しくなる。また80質量部を超えると得られる成形品の耐衝撃性、熱安定性、表面性が低下する上、溶融混練時の樹脂との混練が困難となるなど作業性が低下する。タルクの含有量は、好ましくは15質量部以上、中でも20質量部以上であり、好ましくは60質量部以下、さらに好ましくは50質量部以下、特に好ましくは40質量部以下、中でも35質量部以下であることが好ましい。 As described above, the content of talc is 10 to 80 parts by mass with respect to 100 parts by mass of the polycarbonate resin. When the content is less than 10 parts by mass, the impact resistance improving effect obtained is poor, and the heat resistance and mechanical strength improving effects are also poor. On the other hand, when the amount exceeds 80 parts by mass, the impact resistance, thermal stability, and surface properties of the obtained molded product are lowered, and workability is lowered such that kneading with a resin during melt kneading becomes difficult. The content of talc is preferably 15 parts by mass or more, more preferably 20 parts by mass or more, preferably 60 parts by mass or less, more preferably 50 parts by mass or less, particularly preferably 40 parts by mass or less, especially 35 parts by mass or less. Preferably there is.
[難燃剤]
本発明のポリカーボネート樹脂組成物は、難燃剤を含有することが好ましく、難燃剤としてはリン系難燃剤、特にはホスファゼン化合物が好ましい。
[Flame retardants]
The polycarbonate resin composition of the present invention preferably contains a flame retardant, and the flame retardant is preferably a phosphorus-based flame retardant, particularly a phosphazene compound.
ホスファゼン化合物としては、下記一般式(1)および(2)で表されるホスファゼン化合物が特に好ましい。 As the phosphazene compound, phosphazene compounds represented by the following general formulas (1) and (2) are particularly preferable.
上記一般式(1)及び(2)で表されるホスファゼン化合物としては、例えば、フェノキシホスファゼン、(ポリ)トリルオキシホスファゼン(例えば、o−トリルオキシホスファゼン、m−トリルオキシホスファゼン、p−トリルオキシホスファゼン、o,m−トリルオキシホスファゼン、o,p−トリルオキシホスファゼン、m,p−トリルオキシホスファゼン、o,m,p−トリルオキシホスファゼン等)、(ポリ)キシリルオキシホスファゼン等の環状及び/又は鎖状C1−6アルキルC6−20アリールオキシホスファゼンや、(ポリ)フェノキシトリルオキシホスファゼン(例えば、フェノキシo−トリルオキシホスファゼン、フェノキシm−トリルオキシホスファゼン、フェノキシp−トリルオキシホスファゼン、フェノキシo,m−トリルオキシホスファゼン、フェノキシo,p−トリルオキシホスファゼン、フェノキシm,p−トリルオキシホスファゼン、フェノキシo,m,p−トリルオキシホスファゼン等)、(ポリ)フェノキシキシリルオキシホスファゼン、(ポリ)フェノキシトリルオキシキシリルオキシホスファゼン等の環状及び/又は鎖状C6−20アリールC1−10アルキルC6−20アリールオキシホスファゼン等が例示できる。
これらのうち、好ましくは、環状及び/又は鎖状フェノキシホスファゼン、環状及び/又は鎖状C1−3アルキルC6−20アリールオキシホスファゼン、C6−20アリールオキシC1−3アルキルC6−20アリールオキシホスファゼン(例えば、環状及び/又は鎖状トリルオキシホスファゼン、環状及び/又は鎖状フェノキシトリルフェノキシホスファゼン等)である。
Examples of the phosphazene compounds represented by the general formulas (1) and (2) include phenoxyphosphazene, (poly) tolyloxyphosphazene (for example, o-tolyloxyphosphazene, m-tolyloxyphosphazene, p-tolyloxyphosphazene). O, m-tolyloxyphosphazene, o, p-tolyloxyphosphazene, m, p-tolyloxyphosphazene, o, m, p-tolyloxyphosphazene, etc.), (poly) xylyloxyphosphazene and / or cyclic and chain C 1-6 alkyl C 6-20 aryloxy phosphazene, (poly) phenoxy tolyloxy phosphazene (e.g., phenoxy o- tolyloxy phosphazene, a phenoxy m- tolyloxyethyl phosphazene, a phenoxy p- tolyloxy phosphazene, phenoxy o, m-tolyloxyphosphazene, phenoxy o, p-tolyloxyphosphazene, phenoxy m, p-tolyloxyphosphazene, phenoxy o, m, p-tolyloxyphosphazene, etc.), (poly) phenoxysilyloxyphosphazene, (poly ) Cyclic and / or chain C 6-20 aryl C 1-10 alkyl C 6-20 aryloxy phosphazene such as phenoxytolyloxyxyloxyphosphazene .
Of these, cyclic and / or chain phenoxyphosphazene, cyclic and / or chain C 1-3 alkyl C 6-20 aryloxyphosphazene, C 6-20 aryloxy C 1-3 alkyl C 6-20 Aryloxyphosphazenes (eg, cyclic and / or chain tolyloxyphosphazenes, cyclic and / or chain phenoxytolylphenoxyphosphazenes, etc.).
一般式(1)で表される環状ホスファゼン化合物としては、R1及びR2は、同一又は異なっていてもよく、アリール基又はアルキルアリール基を示す。このようなアリール基又はアルキルアリール基としては、フェニル基、ナフチル基、メチルフェニル基、ベンジル基等が挙げられるが、なかでもR1及びR2がフェニル基である環状フェノキシホスファゼンが特に好ましい。
このような環状フェノキシホスファゼン化合物としては、例えば、塩化アンモニウムと五塩化リンとを120〜130℃の温度で反応させて得られる環状及び直鎖状のクロロホスファゼン混合物から、ヘキサクロロシクロトリホスファゼン、オクタクロロシクロテトラホスファゼン、デカクロロシクロペンタホスファゼン等の環状のクロルホスファゼンを取り出した後にフェノキシ基で置換して得られる、フェノキシシクロトリホスファゼン、オクタフェノキシシクロテトラホスファゼン、デカフェノキシシクロペンタホスファゼン等の化合物が挙げられる。
In the cyclic phosphazene compound represented by the general formula (1), R 1 and R 2 may be the same or different and each represents an aryl group or an alkylaryl group. Examples of such an aryl group or alkylaryl group include a phenyl group, a naphthyl group, a methylphenyl group, and a benzyl group. Among them, cyclic phenoxyphosphazene in which R 1 and R 2 are phenyl groups is particularly preferable.
Examples of such a cyclic phenoxyphosphazene compound include hexachlorocyclotriphosphazene, octachlorocyclohexane, and a mixture of cyclic and linear chlorophosphazene obtained by reacting ammonium chloride and phosphorus pentachloride at a temperature of 120 to 130 ° C. Examples include compounds such as phenoxycyclotriphosphazene, octaphenoxycyclotetraphosphazene, and decaffenoxycyclopentaphosphazene obtained by removing a cyclic chlorophosphazene such as cyclotetraphosphazene and decachlorocyclopentaphosphazene and then substituting with a phenoxy group. .
また、一般式(1)中、aは3〜25の整数を表すが、なかでもaが3〜8の整数である化合物が好ましく、aの異なる化合物の混合物であってもよい。なかでも、a=3のものが50質量%以上、a=4のものが10〜40質量%、a=5以上のものが合わせて30質量%以下である化合物の混合物が好ましい。 Moreover, in general formula (1), although a represents the integer of 3-25, the compound whose a is an integer of 3-8 is preferable especially, and the mixture of the compound from which a differs may be sufficient. Among them, a mixture of compounds in which a = 3 is 50% by mass or more, a = 4 is 10 to 40% by mass, and a = 5 or more is 30% by mass or less is preferable.
一般式(2)中、R3及びR4は、同一又は異なっていてもよく、アリール基又はアルキルアリール基を示す。このようなアリール基又はアルキルアリール基としては、フェニル基、ナフチル基、メチルフェニル基、ベンジル基等が挙げられるが、R3及びR4がフェニル基である鎖状フェノキシホスファゼンが特に好ましい。
このような鎖状フェノキシホスファゼン化合物は、例えば、上記の方法で得られるヘキサクロロシクロトリホスファゼンを220〜250℃の温度で開還重合し、得られた重合度3〜10,000の直鎖状ジクロロホスファゼンをフェノキシ基で置換することにより得られる化合物が挙げられる。
In General Formula (2), R 3 and R 4 may be the same or different and each represents an aryl group or an alkylaryl group. Examples of such an aryl group or alkylaryl group include a phenyl group, a naphthyl group, a methylphenyl group, a benzyl group, and the like, and a chain phenoxyphosphazene in which R 3 and R 4 are phenyl groups is particularly preferable.
Such a chain phenoxyphosphazene compound is obtained by, for example, subjecting hexachlorocyclotriphosphazene obtained by the above-described method to reverse polymerization at a temperature of 220 to 250 ° C., and the obtained linear dichloromethane having a polymerization degree of 3 to 10,000. Examples thereof include compounds obtained by substituting phosphazene with a phenoxy group.
また、R5は、−N=P(OR3)3基、−N=P(OR4)3基、−N=P(O)OR3基、−N=P(O)OR4基から選ばれる少なくとも1種を示し、R6は、−P(OR3)4基、−P(OR4)4基、−P(O)(OR3)2基、−P(O)(OR4)2基から選ばれる少なくとも1種を示す。 In addition, R 5 is represented by -N = P (OR 3 ) 3 groups, -N = P (OR 4 ) 3 groups, -N = P (O) OR 3 groups, and -N = P (O) OR 4 groups. represents at least one selected, R 6 is, -P (OR 3) 4 group, -P (OR 4) 4 group, -P (O) (OR 3 ) 2 group, -P (O) (OR 4 ) At least one selected from two groups.
また、一般式(2)中、bは3〜10,000の整数を示し、好ましくは3〜1,000、より好ましくは3〜100、さらに好ましくは3〜25である。 Moreover, in general formula (2), b shows the integer of 3-10,000, Preferably it is 3-1,000, More preferably, it is 3-100, More preferably, it is 3-25.
また、ホスファゼン化合物は、その一部が架橋された架橋ホスファゼン化合物であってもよい。このような架橋構造を有することで耐熱性が向上する傾向にある。
このような架橋ホスファゼン化合物としては、下記一般式(3)に示す架橋構造、例えば、4,4’−スルホニルジフェニレン(すなわち、ビスフェノールS残基)の架橋構造を有する化合物、2,2−(4,4’−ジフェニレン)イソプロピリデン基の架橋構造を有する化合物、4,4’−オキシジフェニレン基の架橋構造を有する化合物、4,4’−チオジフェニレン基の架橋構造を有する化合物等の、4,4’−ジフェニレン基の架橋構造を有する化合物等が挙げられる。
Further, the phosphazene compound may be a crosslinked phosphazene compound partially crosslinked. By having such a crosslinked structure, the heat resistance tends to be improved.
Examples of such a crosslinked phosphazene compound include a crosslinked structure represented by the following general formula (3), for example, a compound having a crosslinked structure of 4,4′-sulfonyldiphenylene (that is, bisphenol S residue), 2,2- ( 4,4′-diphenylene) isopropylidene group-crosslinked structure, 4,4′-oxydiphenylene group-crosslinked structure, 4,4′-thiodiphenylene group-crosslinked structure, etc. And compounds having a crosslinked structure of 4,4′-diphenylene group.
また、架橋ホスファゼン化合物としては、一般式(1)においてR1及びR2がフェニル基である環状フェノキシホスファゼン化合物が上記一般式(3)で表される架橋基によって架橋されてなる架橋フェノキシホスファゼン化合物又は、前記一般式(2)においてR3及びR4がフェニル基である鎖状フェノキシホスファゼン化合物が上記一般式(3)で表される架橋基によって架橋されてなる架橋フェノキシホスファゼン化合物が難燃性の点から好ましく、環状フェノキシホスファゼン化合物が上記一般式(3)で表される架橋基によって架橋されてなる架橋フェノキシホスファゼン化合物がより好ましい。 In addition, as the crosslinked phosphazene compound, a crosslinked phenoxyphosphazene compound obtained by crosslinking a cyclic phenoxyphosphazene compound in which R 1 and R 2 are phenyl groups in the general formula (1) with a crosslinking group represented by the general formula (3). Alternatively, a crosslinked phenoxyphosphazene compound obtained by crosslinking a chain phenoxyphosphazene compound in which R 3 and R 4 are phenyl groups in the general formula (2) with a crosslinking group represented by the general formula (3) is flame retardant. From the above point, a crosslinked phenoxyphosphazene compound obtained by crosslinking a cyclic phenoxyphosphazene compound with a crosslinking group represented by the general formula (3) is more preferable.
また、架橋フェノキシホスファゼン化合物中のフェニレン基の含有量は、一般式(1)で表される環状ホスファゼン化合物及び/又は一般式(2)で表される鎖状フェノキシホスファゼン化合物中の全フェニル基及びフェニレン基数を基準として、通常50〜99.9%、好ましくは70〜90%である。また、該架橋フェノキシホスファゼン化合物は、その分子内にフリーの水酸基を有しない化合物であることが特に好ましい。 The content of the phenylene group in the crosslinked phenoxyphosphazene compound is such that the cyclic phosphazene compound represented by the general formula (1) and / or the all phenyl groups in the chain phenoxyphosphazene compound represented by the general formula (2) and Based on the number of phenylene groups, it is usually 50 to 99.9%, preferably 70 to 90%. The crosslinked phenoxyphosphazene compound is particularly preferably a compound having no free hydroxyl group in the molecule.
本発明においては、ホスファゼン化合物は、前記一般式(1)で表される環状フェノキシホスファゼン化合物、及び、上記一般式(2)で表される環状フェノキシホスファゼン化合物が架橋基によって架橋されてなる架橋フェノキシホスファゼン化合物よる成る群から選択される少なくとも1種であることが、難燃性及び機械的特性の点から好ましい。 In the present invention, the phosphazene compound is a crosslinked phenoxy obtained by crosslinking the cyclic phenoxyphosphazene compound represented by the general formula (1) and the cyclic phenoxyphosphazene compound represented by the general formula (2) with a crosslinking group. In view of flame retardancy and mechanical properties, at least one selected from the group consisting of phosphazene compounds is preferable.
ホスファゼン化合物の含有量は、ポリカーボネート樹脂100質量部に対し、好ましくは2〜20質量部であるが、2.5質量部以上がより好ましく、さらに好ましくは3質量部以上であり、15質量部以下がより好ましく、さらに好ましくは10量部以下、中でも7質量部以下、特に好ましくは5質量部以下である。 The content of the phosphazene compound is preferably 2 to 20 parts by mass with respect to 100 parts by mass of the polycarbonate resin, more preferably 2.5 parts by mass or more, still more preferably 3 parts by mass or more, and 15 parts by mass or less. Is more preferably 10 parts by weight or less, especially 7 parts by weight or less, and particularly preferably 5 parts by weight or less.
[シロキサン系エラストマー]
本発明のポリカーボネート樹脂組成物は、エラストマーを含有することが好ましく、中でもシロキサン系エラストマーを含有することが好ましい。
シロキサン系エラストマーとしては、ポリオルガノシロキサンゴムなどのシリコーン系ゴムがあるが、特には、ポリシロキサンゴム成分にこれと共重合可能な単量体成分をグラフト共重合したグラフト共重合体が好ましい。グラフト共重合体の製造方法としては、塊状重合、溶液重合、懸濁重合、乳化重合などのいずれの製造方法であってもよく、共重合の方式は一段グラフトでも多段グラフトであってもよい。
[Siloxane elastomer]
The polycarbonate resin composition of the present invention preferably contains an elastomer, and particularly preferably contains a siloxane elastomer.
Examples of the siloxane elastomer include silicone rubbers such as polyorganosiloxane rubber. In particular, a graft copolymer obtained by graft copolymerizing a polysiloxane rubber component with a monomer component copolymerizable therewith is preferable. The production method of the graft copolymer may be any production method such as bulk polymerization, solution polymerization, suspension polymerization, and emulsion polymerization, and the copolymerization method may be single-stage graft or multi-stage graft.
ポリオルガノシロキサンゴム成分とグラフト共重合可能な単量体成分の具体例としては、芳香族ビニル化合物、シアン化ビニル化合物、(メタ)アクリル酸エステル化合物、(メタ)アクリル酸化合物、グリシジル(メタ)アクリレート等のエポキシ基含有(メタ)アクリル酸エステル化合物;マレイミド、N−メチルマレイミド、N−フェニルマレイミド等のマレイミド化合物;マレイン酸、フタル酸、イタコン酸等のα,β−不飽和カルボン酸化合物やそれらの無水物(例えば無水マレイン酸等)などが挙げられる。これらの単量体成分は1種を単独で用いても2種以上を併用してもよい。これらの中でも、機械的特性や表面外観の面から、芳香族ビニル化合物、シアン化ビニル化合物、(メタ)アクリル酸エステル化合物、(メタ)アクリル酸化合物が好ましく、より好ましくは(メタ)アクリル酸エステル化合物である。(メタ)アクリル酸エステル化合物の具体例としては、(メタ)アクリル酸メチル、(メタ)アクリル酸エチル、(メタ)アクリル酸ブチル、(メタ)アクリル酸シクロヘキシル、(メタ)アクリル酸オクチル等を挙げることができる。 Specific examples of monomer components that can be graft copolymerized with the polyorganosiloxane rubber component include aromatic vinyl compounds, vinyl cyanide compounds, (meth) acrylic acid ester compounds, (meth) acrylic acid compounds, glycidyl (meth). Epoxy group-containing (meth) acrylic acid ester compounds such as acrylate; maleimide compounds such as maleimide, N-methylmaleimide and N-phenylmaleimide; α, β-unsaturated carboxylic acid compounds such as maleic acid, phthalic acid and itaconic acid These anhydrides (for example, maleic anhydride etc.) etc. are mentioned. These monomer components may be used alone or in combination of two or more. Among these, aromatic vinyl compounds, vinyl cyanide compounds, (meth) acrylic acid ester compounds, and (meth) acrylic acid compounds are preferable from the viewpoint of mechanical properties and surface appearance, and (meth) acrylic acid esters are more preferable. A compound. Specific examples of the (meth) acrylate compound include methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, cyclohexyl (meth) acrylate, octyl (meth) acrylate, and the like. be able to.
ポリオルガノシロキサンゴム成分を共重合したグラフト共重合体は、耐衝撃性や表面外観の点からコア/シェル型グラフト共重合体タイプのものが好ましい。なかでも、ポリオルガノシロキサンゴムとポリアルキルアクリレートゴムとからなるIPN型複合ゴムから選ばれる少なくとも1種のゴム成分をコア層とし、その周囲に(メタ)アクリル酸エステルを共重合して形成されたシェル層からなる、コア/シェル型グラフト共重合体が特に好ましい。上記コア/シェル型グラフト共重合体において、ポリオルガノシロキサンゴム成分を40〜80質量%含有するものが好ましく、50〜70質量%含有するものがさらに好ましい。 The graft copolymer obtained by copolymerizing the polyorganosiloxane rubber component is preferably a core / shell type graft copolymer type from the viewpoint of impact resistance and surface appearance. Among them, it was formed by using at least one rubber component selected from IPN type composite rubber composed of polyorganosiloxane rubber and polyalkyl acrylate rubber as a core layer and copolymerizing (meth) acrylate around it. A core / shell type graft copolymer comprising a shell layer is particularly preferred. The core / shell type graft copolymer preferably contains 40-80% by mass of the polyorganosiloxane rubber component, more preferably 50-70% by mass.
シロキサン系エラストマーの含有量は、ポリカーボネート樹脂100質量部に対して、好ましくは5〜20質量部である。このように、シロキサン系エラストマーを含有することで、ポリカーボネート樹脂組成物の耐衝撃性をさらに向上させることができる。シロキサン系エラストマーの含有量が5質量部より少ないと、シロキサン系エラストマーによる耐衝撃性のさらなる向上効果が不十分となりやすく、20質量部を超えると、成形品の外観不良や耐熱性の低下が生じやすい。含有量の下限は、より好ましくは7質量部以上であり、また、含有量の上限は、より好ましくは15質量部以下、中でも13質量部以下が特に好ましい。 The content of the siloxane elastomer is preferably 5 to 20 parts by mass with respect to 100 parts by mass of the polycarbonate resin. Thus, the impact resistance of a polycarbonate resin composition can further be improved by containing a siloxane-based elastomer. If the content of the siloxane elastomer is less than 5 parts by mass, the effect of further improving the impact resistance due to the siloxane elastomer tends to be insufficient, and if it exceeds 20 parts by mass, the appearance of the molded product is poor and the heat resistance is reduced. Cheap. The lower limit of the content is more preferably 7 parts by mass or more, and the upper limit of the content is more preferably 15 parts by mass or less, and particularly preferably 13 parts by mass or less.
[フルオロポリマー]
本発明のポリカーボネート樹脂組成物は、滴下防止剤としてフルオロポリマーを含有することが好ましい。
フルオロポリマーとしては、例えば、フルオロオレフィン樹脂が挙げられる。フルオロオレフィン樹脂は、通常フルオロエチレン構造を含む重合体あるいは共重合体である。具体例としては、ジフルオロエチレン樹脂、テトラフルオロエチレン樹脂、テトラフルオロエチレン/ヘキサフルオロプロピレン共重合樹脂、テトラフルオロエチレン/パーフルアルキルビニルエーテル共重合樹脂等が挙げられる。なかでも好ましくはテトラフルオロエチレン樹脂等が挙げられる。このフルオロエチレン樹脂としては、フィブリル形成能を有するフルオロエチレン樹脂が挙げられる。
[Fluoropolymer]
The polycarbonate resin composition of the present invention preferably contains a fluoropolymer as an anti-dripping agent.
An example of the fluoropolymer is a fluoroolefin resin. The fluoroolefin resin is usually a polymer or copolymer containing a fluoroethylene structure. Specific examples include difluoroethylene resin, tetrafluoroethylene resin, tetrafluoroethylene / hexafluoropropylene copolymer resin, tetrafluoroethylene / perfluoroalkyl vinyl ether copolymer resin, and the like. Of these, tetrafluoroethylene resin and the like are preferable. Examples of the fluoroethylene resin include a fluoroethylene resin having a fibril forming ability.
フィブリル形成能を有するフルオロエチレン樹脂としては、例えば、三井・デュポンフロロケミカル社製「テフロン(登録商標)6J」、「テフロン(登録商標)640J」、「テフロン(登録商標)6C」、ダイキン工業社製「ポリフロンF201L」、「ポリフロンF103」、「ポリフロンFA500H」などが挙げられる。さらに、フルオロエチレン樹脂の水性分散液の市販品として、例えば、三井・デュポンフロロケミカル社製「テフロン(登録商標)30J」、「テフロン(登録商標)31−JR」、ダイキン工業社製「フルオンD−1」等が挙げられる。 Examples of the fluoroethylene resin having a fibril-forming ability include “Teflon (registered trademark) 6J”, “Teflon (registered trademark) 640J”, “Teflon (registered trademark) 6C”, and Daikin Industries, Ltd. “Polyflon F201L”, “Polyflon F103”, “Polyflon FA500H”, and the like are available. Furthermore, as commercially available products of aqueous dispersions of fluoroethylene resin, for example, “Teflon (registered trademark) 30J”, “Teflon (registered trademark) 31-JR” manufactured by Mitsui DuPont Fluorochemical Co., Ltd., “Fluon D” manufactured by Daikin Industries, Ltd. -1 "and the like.
さらに、ビニル系単量体を重合してなる多層構造を有するフルオロエチレン重合体も使用することができ、このようなフルオロエチレン重合体としては、ポリスチレン−フルオロエチレン複合体、ポリスチレン−アクリロニトリル−フルオロエチレン複合体、ポリメタクリル酸メチル−フルオロエチレン複合体、ポリメタクリル酸ブチル−フルオロエチレン複合体等が挙げられ、具体例としては三菱レイヨン社製「メタブレンA−3800」、GEスペシャリティケミカル社製「ブレンデックス449」等が挙げられる。
なお、フルオロポリマーは、1種が含有されていてもよく、2種以上が任意の組み合わせ及び比率で含有されていてもよい。
Furthermore, a fluoroethylene polymer having a multilayer structure obtained by polymerizing vinyl monomers can also be used. Examples of such a fluoroethylene polymer include polystyrene-fluoroethylene composites, polystyrene-acrylonitrile-fluoroethylene. Examples include composites, polymethyl methacrylate-fluoroethylene composites, polybutyl methacrylate-fluoroethylene composites, etc. Specific examples include “Metablene A-3800” manufactured by Mitsubishi Rayon Co., Ltd., “Blendex” manufactured by GE Specialty Chemical Co., Ltd. 449 "and the like.
In addition, 1 type may contain fluoropolymer and 2 or more types may contain it by arbitrary combinations and a ratio.
フルオロポリマーの含有量は、ポリカーボネート樹脂100質量部に対して、好ましくは0.001質量部以上であり、より好ましくは0.01質量部以上、さらに好ましくは0.05質量部以上、特に好ましくは0.1質量部以上であり、また、好ましくは10質量部以下であり、より好ましくは8質量部以下、さらに好ましくは7質量部以下である。フルオロポリマーの含有量が前記範囲の下限値未満の場合は、フルオロポリマーによる難燃性改良の効果が不十分となりやすく、フルオロポリマーの含有量が前記範囲の上限値を超える場合は、ポリカーボネート樹脂組成物を成形した成形品の外観不良や機械的強度の低下が生じやすい。 The content of the fluoropolymer is preferably 0.001 part by mass or more, more preferably 0.01 part by mass or more, further preferably 0.05 part by mass or more, particularly preferably 100 parts by mass of the polycarbonate resin. It is 0.1 mass part or more, Preferably it is 10 mass parts or less, More preferably, it is 8 mass parts or less, More preferably, it is 7 mass parts or less. When the fluoropolymer content is less than the lower limit of the above range, the effect of improving the flame retardancy by the fluoropolymer tends to be insufficient, and when the fluoropolymer content exceeds the upper limit of the above range, the polycarbonate resin composition Deterioration in appearance and mechanical strength of the molded product formed from the product are likely to occur.
[有機ホスフェート化合物]
本発明のポリカーボネート樹脂組成物は、更に安定剤として、下記一般式(4)で表される有機ホスフェート化合物を含有することが好ましい。
O=P(OH)m(OR)3−m ・・・(4)
(一般式(4)中、Rはアルキル基またはアリール基であり、それぞれ同一であっても異なっていてもよい。mは0〜2の整数である。)
上記有機ホスフェート化合物は、1種を単独で用いてもよく、2種以上を混合して用いてもよい。
[Organic phosphate compounds]
The polycarbonate resin composition of the present invention preferably further contains an organic phosphate compound represented by the following general formula (4) as a stabilizer.
O = P (OH) m (OR) 3-m (4)
(In general formula (4), R is an alkyl group or an aryl group, and may be the same or different. M is an integer of 0-2.)
The said organic phosphate compound may be used individually by 1 type, and may mix and use 2 or more types.
上記一般式(4)中、Rは、好ましくは、炭素原子数1〜30のアルキル基または炭素原子数6〜30のアリール基であり、より好ましくは、炭素原子数1〜30のアルキル基である。また、mは好ましくは1又は2である。 In the general formula (4), R is preferably an alkyl group having 1 to 30 carbon atoms or an aryl group having 6 to 30 carbon atoms, more preferably an alkyl group having 1 to 30 carbon atoms. is there. M is preferably 1 or 2.
上記一般式(4)において、Rは炭素原子数1〜30のアルキル基が好ましいが、中でも炭素原子数8〜30のアルキル基であることが好ましい。具体的には例えば、n−オクチル基、2−エチルヘキシル基、イソオクチル基、ノニル基、イソノニル基、デシル基、イソデシル基、ドデシル基、トリデシル基、イソトリデシル基、テトラデシル基、ヘキサデシル基、オクタデシル基、エイコシル基、トリアンコチル基等であることが好ましい。 In the general formula (4), R is preferably an alkyl group having 1 to 30 carbon atoms, and more preferably an alkyl group having 8 to 30 carbon atoms. Specifically, for example, n-octyl group, 2-ethylhexyl group, isooctyl group, nonyl group, isononyl group, decyl group, isodecyl group, dodecyl group, tridecyl group, isotridecyl group, tetradecyl group, hexadecyl group, octadecyl group, eicosyl group Group, triancotyl group and the like are preferable.
また上記一般式(4)において、mが2であるモノアルキルアシッドホスフェートや、mが1であるジアルキルアシッドホスフェート、或いはそれらの混合物も本発明に好ましく使用できる。このようなホスフェート化合物の具体的商品としては、例えばADEKA社製、商品名「AX−71」として、オクタデシルアシッドホスフェート(モノアルキル体とジアルキル体の混合物)が挙げられる。 Moreover, in the said General formula (4), the monoalkyl acid phosphate whose m is 2 and the dialkyl acid phosphate whose m is 1 or those mixtures can be used preferably for this invention. Specific products of such a phosphate compound include, for example, octadecyl acid phosphate (mixture of monoalkyl and dialkyl) as trade name “AX-71” manufactured by ADEKA.
[離型剤]
本発明のポリカーボネート樹脂組成物は、離型剤を含有することが好ましい。
離型剤としては、例えば、脂肪族カルボン酸、脂肪族カルボン酸とアルコールとのエステル、脂肪族炭化水素化合物、ポリシロキサン系シリコーンオイルなどが挙げられる。
[Release agent]
The polycarbonate resin composition of the present invention preferably contains a release agent.
Examples of the release agent include aliphatic carboxylic acids, esters of aliphatic carboxylic acids and alcohols, aliphatic hydrocarbon compounds, polysiloxane silicone oils, and the like.
脂肪族カルボン酸としては、例えば、飽和または不飽和の脂肪族一価、二価または三価カルボン酸を挙げることができる。ここで脂肪族カルボン酸とは、脂環式のカルボン酸も包含する。これらの中で好ましい脂肪族カルボン酸は炭素数6〜36の一価または二価カルボン酸であり、炭素数6〜36の脂肪族飽和一価カルボン酸がさらに好ましい。かかる脂肪族カルボン酸の具体例としては、パルミチン酸、ステアリン酸、カプロン酸、カプリン酸、ラウリン酸、アラキン酸、ベヘン酸、リグノセリン酸、セロチン酸、メリシン酸、テトラリアコンタン酸、モンタン酸、アジピン酸、アゼライン酸などが挙げられる。 Examples of the aliphatic carboxylic acid include saturated or unsaturated aliphatic monovalent, divalent or trivalent carboxylic acid. Here, the aliphatic carboxylic acid includes alicyclic carboxylic acid. Among these, preferable aliphatic carboxylic acids are monovalent or divalent carboxylic acids having 6 to 36 carbon atoms, and aliphatic saturated monovalent carboxylic acids having 6 to 36 carbon atoms are more preferable. Specific examples of such aliphatic carboxylic acids include palmitic acid, stearic acid, caproic acid, capric acid, lauric acid, arachidic acid, behenic acid, lignoceric acid, serotic acid, mellicic acid, tetrariacontanoic acid, montanic acid, adipine Examples include acids and azelaic acid.
脂肪族カルボン酸とアルコールとのエステルにおける脂肪族カルボン酸としては、例えば、前記脂肪族カルボン酸と同じものが使用できる。一方、アルコールとしては、例えば、飽和または不飽和の一価または多価アルコールが挙げられる。これらのアルコールは、フッ素原子、アリール基などの置換基を有していてもよい。これらの中では、炭素数30以下の一価または多価の飽和アルコールが好ましく、炭素数30以下の脂肪族飽和一価アルコールまたは脂肪族飽和多価アルコールがさらに好ましい。なお、ここで脂肪族とは、脂環式化合物も含有する。 As aliphatic carboxylic acid in ester of aliphatic carboxylic acid and alcohol, the same thing as the said aliphatic carboxylic acid can be used, for example. On the other hand, examples of the alcohol include saturated or unsaturated monohydric or polyhydric alcohols. These alcohols may have a substituent such as a fluorine atom or an aryl group. Among these, monovalent or polyvalent saturated alcohols having 30 or less carbon atoms are preferable, and aliphatic saturated monohydric alcohols or aliphatic saturated polyhydric alcohols having 30 or less carbon atoms are more preferable. In addition, an aliphatic includes an alicyclic compound here.
かかるアルコールの具体例としては、オクタノール、デカノール、ドデカノール、ステアリルアルコール、ベヘニルアルコール、エチレングリコール、ジエチレングリコール、グリセリン、ペンタエリスリトール、2,2−ジヒドロキシペルフルオロプロパノール、ネオペンチレングリコール、ジトリメチロールプロパン、ジペンタエリスリトール等が好ましく挙げられる。 Specific examples of such alcohols include octanol, decanol, dodecanol, stearyl alcohol, behenyl alcohol, ethylene glycol, diethylene glycol, glycerin, pentaerythritol, 2,2-dihydroxyperfluoropropanol, neopentylene glycol, ditrimethylolpropane, dipentaerythritol, and the like. Is preferred.
なお、上記のエステルは、不純物として脂肪族カルボン酸及び/またはアルコールを含有していてもよい。また、上記のエステルは、純物質であってもよいが、複数の化合物の混合物であってもよい。さらに、結合して一つのエステルを構成する脂肪族カルボン酸及びアルコールは、それぞれ、1種を用いてもよく、2種以上を任意の組み合わせ及び比率で併用しても良い。 In addition, said ester may contain aliphatic carboxylic acid and / or alcohol as an impurity. Moreover, although said ester may be a pure substance, it may be a mixture of a plurality of compounds. Furthermore, the aliphatic carboxylic acid and alcohol which combine to form one ester may be used alone or in combination of two or more in any combination and ratio.
脂肪族カルボン酸とアルコールとのエステルの具体例としては、蜜ロウ(ミリシルパルミテートを主成分とする混合物)、ステアリン酸ステアリル、ベヘン酸ベヘニル、ベヘン酸ステアリル、グリセリンモノパルミテート、グリセリンモノステアレート、グリセリンジステアレート、グリセリントリステアレート、ペンタエリスリトールモノパルミテート、ペンタエリスリトールモノステアレート、ペンタエリスリトールジステアレート、ペンタエリスリトールトリステアレート、ペンタエリスリトールテトラステアレート等が好ましく挙げられる。 Specific examples of esters of aliphatic carboxylic acids and alcohols include beeswax (a mixture based on myricyl palmitate), stearyl stearate, behenyl behenate, stearyl behenate, glycerin monopalmitate, glycerin monostearate Preferred examples include rate, glycerol distearate, glycerol tristearate, pentaerythritol monopalmitate, pentaerythritol monostearate, pentaerythritol distearate, pentaerythritol tristearate, pentaerythritol tetrastearate and the like.
脂肪族炭化水素化合物としては、例えば、流動パラフィン、パラフィンワックス、マイクロワックス、ポリエチレンワックス、フィッシャ−トロプシュワックス、炭素数3〜12のα−オレフィンオリゴマー等が挙げられる。なお、ここで脂肪族炭化水素としては、脂環式炭化水素も含まれる。また、これらの炭化水素は部分酸化されていてもよい。また、脂肪族炭化水素化合物の数平均分子量は、好ましくは数平均分子量200〜15,000であり、より好ましくは5,000以下である。 Examples of the aliphatic hydrocarbon compound include liquid paraffin, paraffin wax, micro wax, polyethylene wax, Fischer-Tropsch wax, α-olefin oligomer having 3 to 12 carbon atoms, and the like. Here, the aliphatic hydrocarbon includes alicyclic hydrocarbons. Further, these hydrocarbons may be partially oxidized. Moreover, the number average molecular weight of the aliphatic hydrocarbon compound is preferably a number average molecular weight of 200 to 15,000, more preferably 5,000 or less.
これらの中では、パラフィンワックス、ポリエチレンワックスまたはポリエチレンワックスの部分酸化物が好ましく、パラフィンワックス、ポリエチレンワックスがさらに好ましく、ポリエチレンワックスが特に好ましい。 Among these, paraffin wax, polyethylene wax, or a partial oxide of polyethylene wax is preferable, paraffin wax and polyethylene wax are more preferable, and polyethylene wax is particularly preferable.
なお、離型剤は、1種が含有されていてもよく、2種以上が任意の組み合わせ及び比率で含有されていても良い。
離型剤の含有量は、ポリカーボネート樹脂100質量部に対して、通常0.001質量部以上、好ましくは0.01質量部以上であり、また、通常2質量部以下、好ましくは1質量部以下である。離型剤の含有量が上記範囲の下限値未満の場合は、離型性の効果が十分でない場合があり、離型剤の含有量が上記範囲の上限値を超える場合は、耐加水分解性の低下、射出成形時の金型汚染などが生じる可能性がある。
In addition, 1 type may contain the mold release agent and 2 or more types may contain it by arbitrary combinations and a ratio.
The content of the release agent is usually 0.001 part by mass or more, preferably 0.01 part by mass or more, and usually 2 parts by mass or less, preferably 1 part by mass or less with respect to 100 parts by mass of the polycarbonate resin. It is. When the content of the release agent is less than the lower limit of the above range, the effect of releasability may not be sufficient, and when the content of the release agent exceeds the upper limit of the above range, hydrolysis resistance And mold contamination during injection molding may occur.
[その他の成分]
本発明の熱伝導性ポリカーボネート樹脂組成物は、所望の諸物性を著しく損なわない限り、必要に応じて、上記以外のその他成分を含有していてもよい。その他の成分の例を挙げると、ポリカーボネート樹脂以外の樹脂、上記した以外の各種樹脂添加剤などが挙げられる。なお、その他の成分は、1種が含有されていてもよく、2種以上が任意の組み合わせ及び比率で含有されていても良い。
[Other ingredients]
The heat conductive polycarbonate resin composition of the present invention may contain other components other than those described above as necessary, as long as desired physical properties are not significantly impaired. Examples of other components include resins other than polycarbonate resins and various resin additives other than those described above. In addition, 1 type may contain other components and 2 or more types may contain them by arbitrary combinations and ratios.
・その他の樹脂
その他の樹脂としては、例えば、ポリエチレンテレフタレート樹脂、ポリトリメチレンテレフタレート、ポリブチレンテレフタレート樹脂などの熱可塑性ポリエステル樹脂;ポリスチレン樹脂、高衝撃ポリスチレン樹脂(HIPS)、アクリロニトリル−スチレン共重合体(AS樹脂)、アクリロニトリル−スチレン−アクリルゴム共重合体(ASA樹脂)、アクリロニトリル−エチレンプロピレン系ゴム−スチレン共重合体(AES樹脂)、アクリロニトリル−ブタジエン−スチレン共重合体(ABS樹脂)などのスチレン系樹脂;ポリエチレン樹脂、ポリプロピレン樹脂等のポリオレフィン樹脂;ポリアミド樹脂;ポリイミド樹脂;ポリエーテルイミド樹脂;ポリウレタン樹脂;ポリフェニレンエーテル樹脂;ポリフェニレンサルファイド樹脂;ポリスルホン樹脂等が挙げられる。
Other resins Examples of other resins include thermoplastic polyester resins such as polyethylene terephthalate resin, polytrimethylene terephthalate, and polybutylene terephthalate resin; polystyrene resin, high impact polystyrene resin (HIPS), acrylonitrile-styrene copolymer ( AS resin), acrylonitrile-styrene-acrylic rubber copolymer (ASA resin), acrylonitrile-ethylenepropylene rubber-styrene copolymer (AES resin), styrene-based acrylonitrile-butadiene-styrene copolymer (ABS resin), etc. Resins; Polyolefin resins such as polyethylene resins and polypropylene resins; Polyamide resins; Polyimide resins; Polyetherimide resins; Polyurethane resins; Polyphenylene ether resins; Rensulfide resin; polysulfone resin and the like.
なお、その他の樹脂は、1種が含有されていてもよく、2種以上が任意の組み合わせ及び比率で含有されていても良い。
その他の樹脂を含有する場合は、ポリカーボネート樹脂及びその他の樹脂の合計100質量部中の、40質量部以下であることが好ましく、30質量部以下であることがより好ましく、20質量部以下であることがさらに好ましい。
In addition, 1 type may contain other resin and 2 or more types may contain it by arbitrary combinations and ratios.
When other resins are contained, it is preferably 40 parts by mass or less, more preferably 30 parts by mass or less, and more preferably 20 parts by mass or less, in a total of 100 parts by mass of the polycarbonate resin and other resins. More preferably.
・樹脂添加剤
樹脂添加剤としては、例えば、上記した以外の熱安定剤、酸化防止剤、ガラス繊維、紫外線吸収剤、染顔料(カーボンブラックを含む)、帯電防止剤、防曇剤、滑剤、アンチブロッキング剤、流動性改良剤、可塑剤、分散剤、抗菌剤などが挙げられる。なお、樹脂添加剤は1種が含有されていてもよく、2種以上が任意の組み合わせ及び比率で含有されていても良い。
以下、本発明のポリカーボネート樹脂組成物に好適な添加剤の例について具体的に説明する。
Resin additives Examples of resin additives include heat stabilizers other than those described above, antioxidants, glass fibers, ultraviolet absorbers, dyes and pigments (including carbon black), antistatic agents, antifogging agents, lubricants, Antiblocking agents, fluidity improvers, plasticizers, dispersants, antibacterial agents and the like can be mentioned. In addition, 1 type may contain resin additive and 2 or more types may contain it by arbitrary combinations and a ratio.
Hereinafter, the example of an additive suitable for the polycarbonate resin composition of this invention is demonstrated concretely.
・・熱安定剤
熱安定剤としては、例えばリン系化合物が挙げられ、リン酸、ホスホン酸、亜燐酸、ホスフィン酸、ポリリン酸などのリンのオキソ酸;酸性ピロリン酸ナトリウム、酸性ピロリン酸カリウム、酸性ピロリン酸カルシウムなどの酸性ピロリン酸金属塩;リン酸カリウム、リン酸ナトリウム、リン酸セシウム、リン酸亜鉛など第1族または第2B族金属のリン酸塩;有機ホスファイト化合物、有機ホスホナイト化合物などが挙げられるが、有機ホスファイト化合物が特に好ましい。
.. Thermal stabilizer As the thermal stabilizer, for example, phosphorus compounds, phosphorous oxo acids such as phosphoric acid, phosphonic acid, phosphorous acid, phosphinic acid, polyphosphoric acid; acidic sodium pyrophosphate, acidic potassium pyrophosphate, Acid pyrophosphate metal salts such as calcium acid pyrophosphate; Group 1 or Group 2B metal phosphates such as potassium phosphate, sodium phosphate, cesium phosphate, zinc phosphate; organic phosphite compounds, organic phosphonite compounds, etc. Of these, organic phosphite compounds are particularly preferred.
有機ホスファイト化合物としては、トリフェニルホスファイト、トリス(モノノニルフェニル)ホスファイト、トリス(モノノニル/ジノニル・フェニル)ホスファイト、トリス(2,4−ジ−tert−ブチルフェニル)ホスファイト、モノオクチルジフェニルホスファイト、ジオクチルモノフェニルホスファイト、モノデシルジフェニルホスファイト、ジデシルモノフェニルホスファイト、トリデシルホスファイト、トリラウリルホスファイト、トリステアリルホスファイト、2,2−メチレンビス(4,6−ジ−tert−ブチルフェニル)オクチルホスファイト等が挙げられる。
なお、熱安定剤は、1種が含有されていてもよく、2種以上が任意の組み合わせ及び比率で含有されていても良い。
Organic phosphite compounds include triphenyl phosphite, tris (monononylphenyl) phosphite, tris (monononyl / dinonyl phenyl) phosphite, tris (2,4-di-tert-butylphenyl) phosphite, monooctyl Diphenyl phosphite, dioctyl monophenyl phosphite, monodecyl diphenyl phosphite, didecyl monophenyl phosphite, tridecyl phosphite, trilauryl phosphite, tristearyl phosphite, 2,2-methylenebis (4,6-di- tert-butylphenyl) octyl phosphite and the like.
In addition, 1 type may contain the heat stabilizer and 2 or more types may contain it by arbitrary combinations and a ratio.
熱安定剤の含有量は、ポリカーボネート樹脂100質量部に対して、通常0.001質量部以上、好ましくは0.01質量部以上、より好ましくは0.03質量部以上であり、また、通常1質量部以下、好ましくは0.7質量部以下、より好ましくは0.5質量部以下である。熱安定剤の含有量が上記範囲の下限値未満の場合は、熱安定効果が不十分となる可能性があり、熱安定剤の含有量が上記範囲の上限値を超える場合は、効果が頭打ちとなり経済的でなくなる可能性がある。 The content of the heat stabilizer is usually 0.001 part by mass or more, preferably 0.01 part by mass or more, more preferably 0.03 part by mass or more, based on 100 parts by mass of the polycarbonate resin. It is not more than part by mass, preferably not more than 0.7 part by mass, more preferably not more than 0.5 part by mass. If the content of the heat stabilizer is less than the lower limit of the above range, the heat stability effect may be insufficient, and if the content of the heat stabilizer exceeds the upper limit of the above range, the effect will reach its peak. And may become less economical.
・・酸化防止剤
酸化防止剤としては、例えばヒンダードフェノール系酸化防止剤が挙げられる。その具体例としては、ペンタエリスリトールテトラキス[3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオネート]、オクタデシル−3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオネート、チオジエチレンビス[3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオネート]、N,N’−ヘキサン−1,6−ジイルビス[3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオナミド]、2,4−ジメチル−6−(1−メチルペンタデシル)フェノール、ジエチル[[3,5−ビス(1,1−ジメチルエチル)−4−ヒドロキシフェニル]メチル]ホスフォエート、3,3’,3”,5,5’,5”−ヘキサ−tert−ブチル−a,a’,a”−(メシチレン−2,4,6−トリイル)トリ−p−クレゾール、4,6−ビス(オクチルチオメチル)−o−クレゾール、エチレンビス(オキシエチレン)ビス[3−(5−tert−ブチル−4−ヒドロキシ−m−トリイル)プロピオネート]、ヘキサメチレンビス[3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオネート]、1,3,5−トリス(3,5−ジ−tert−ブチル−4−ヒドロキシベンジル)−1,3,5−トリアジン−2,4,6(1H,3H,5H)−トリオン、2,6−ジ−tert−ブチル−4−(4,6−ビス(オクチルチオ)−1,3,5−トリアジン−2−イルアミノ)フェノール、2−[1−(2−ヒドロキシ−3,5−ジ−tert−ペンチルフェニル)エチル]−4,6−ジ−tert−ペンチルフェニルアクリレート等が挙げられる。
.. Antioxidants Examples of antioxidants include hindered phenol antioxidants. Specific examples thereof include pentaerythritol tetrakis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], octadecyl-3- (3,5-di-tert-butyl-4-hydroxyphenyl). ) Propionate, thiodiethylenebis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], N, N′-hexane-1,6-diylbis [3- (3,5-di-) tert-butyl-4-hydroxyphenyl) propionamide], 2,4-dimethyl-6- (1-methylpentadecyl) phenol, diethyl [[3,5-bis (1,1-dimethylethyl) -4-hydroxyphenyl] ] Methyl] phosphoate, 3,3 ′, 3 ″, 5,5 ′, 5 ″ -hexa-tert-butyl-a, a ′, a ″-( Mesitylene-2,4,6-triyl) tri-p-cresol, 4,6-bis (octylthiomethyl) -o-cresol, ethylenebis (oxyethylene) bis [3- (5-tert-butyl-4- Hydroxy-m-triyl) propionate], hexamethylenebis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], 1,3,5-tris (3,5-di-tert- Butyl-4-hydroxybenzyl) -1,3,5-triazine-2,4,6 (1H, 3H, 5H) -trione, 2,6-di-tert-butyl-4- (4,6-bis ( Octylthio) -1,3,5-triazin-2-ylamino) phenol, 2- [1- (2-hydroxy-3,5-di-tert-pentylphenyl) ethyl] -4,6-di tert- pentylphenyl acrylate.
なかでも、ペンタエリスリトールテトラキス[3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオネート]、オクタデシル−3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオネートが好ましい。
なお、酸化防止剤は、1種が含有されていてもよく、2種以上が任意の組み合わせ及び比率で含有されていても良い。
Among them, pentaerythritol tetrakis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], octadecyl-3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate preferable.
In addition, 1 type may contain antioxidant and 2 or more types may contain it by arbitrary combinations and a ratio.
酸化防止剤の含有量は、ポリカーボネート樹脂100質量部に対して、通常0.001質量部以上、好ましくは0.01質量部以上であり、また、通常1質量部以下、好ましくは0.5質量部以下である。酸化防止剤の含有量が上記範囲の下限値未満の場合は、酸化防止剤としての効果が不十分となる可能性があり、酸化防止剤の含有量が上記範囲の上限値を超える場合は、効果が頭打ちとなり経済的でなくなる可能性がある。 The content of the antioxidant is usually 0.001 part by mass or more, preferably 0.01 part by mass or more, and usually 1 part by mass or less, preferably 0.5 part by mass with respect to 100 parts by mass of the polycarbonate resin. Or less. When the content of the antioxidant is less than the lower limit of the above range, the effect as an antioxidant may be insufficient, and when the content of the antioxidant exceeds the upper limit of the above range, There is a possibility that the effect reaches its peak and is not economical.
・・酸化チタン
酸化チタンは、ポリカーボネート樹脂組成物から得られる成形品の遮光性、白度、光線反射特性などを向上させる様に機能する。酸化チタンは、その製造方法、結晶形態および平均粒子径などは、特に限定されるものではない。
.. Titanium oxide Titanium oxide functions to improve the light shielding properties, whiteness, light reflection characteristics, etc. of molded products obtained from the polycarbonate resin composition. The production method, crystal form and average particle size of titanium oxide are not particularly limited.
酸化チタンの製造方法には、硫酸法および塩素法があるが、いずれであってもよい。
また、その結晶形態には、ルチル型とアナターゼ型があるが、耐光性の観点からルチル型の結晶形態のものが好適である。酸化チタン系添加剤の平均粒子径は、通常0.1〜0.7μm、好ましくは0.1〜0.4μmである。
There are two methods for producing titanium oxide, the sulfuric acid method and the chlorine method.
The crystal form includes a rutile type and an anatase type, but a rutile type crystal form is preferred from the viewpoint of light resistance. The average particle size of the titanium oxide-based additive is usually 0.1 to 0.7 μm, preferably 0.1 to 0.4 μm.
なお、酸化チタンは、後記するオルガノシロキサン系の表面処理剤で表面処理する前に、アルミナ系表面処理剤で前処理するのが好ましい。アルミナ系表面処理剤としてはアルミナ水和物が好適に用いられる。さらにアルミナ水和物とともに珪酸水和物で前処理しても良い。前処理の方法は特に限定されるものではなく、任意の方法によることが出来る。アルミナ水和物、さらに必要に応じて珪酸水和物による前処理は、酸化チタンに対して1〜15質量%の範囲で行なうのが好ましい。 Titanium oxide is preferably pretreated with an alumina surface treatment agent before being surface treated with an organosiloxane surface treatment agent described later. Alumina hydrate is preferably used as the alumina-based surface treatment agent. Furthermore, it may be pretreated with silicic acid hydrate together with alumina hydrate. The pretreatment method is not particularly limited, and any method can be used. Pretreatment with alumina hydrate and, if necessary, silicic acid hydrate is preferably carried out in the range of 1 to 15% by mass with respect to titanium oxide.
アルミナ水和物、さらに必要に応じて珪酸水和物で前処理された酸化チタンは、更にその表面をオルガノシロキサン系の表面処理剤で表面処理することによって、熱安定性を大幅に改善することが出来る他、ポリカーボネート樹脂組成物中での均一分散性および分散状態の安定性を向上させる。オルガノシロキサン系の表面処理剤としては、ポリオルガノハイドロジェンシロキサン化合物が好ましい。 Titanium oxide pretreated with alumina hydrate and, if necessary, silicic acid hydrate, can be further improved in thermal stability by surface treatment with organosiloxane surface treatment agent. In addition, the uniform dispersibility in the polycarbonate resin composition and the stability of the dispersed state are improved. As the organosiloxane-based surface treatment agent, a polyorganohydrogensiloxane compound is preferable.
酸化チタンのオルガノシロキサン系の表面処理剤による表面処理法には湿式法と乾式法とがある。湿式法は、オルガノシロキサン系の表面処理剤と溶剤との混合物に、アルミナ水和物、さらに必要に応じて珪酸水和物で前処理された酸化チタンを加え、撹拌した後に脱溶媒を行い、更にその後100〜300℃で熱処理する方法である。乾式法は、上記と同様に前処理された酸化チタンとポリオルガノハイドロジェンシロキサン類とをヘンシェルミキサーなどで混合する方法、前処理された酸化チタンにポリオルガノハイドロジェンシロキサン類の有機溶液を噴霧して付着させ、100〜300℃で熱処理する方法などが挙げられる。シロキサン系の表面処理剤の量は、特に制限されるものではないが、酸化チタンの反射性、樹脂組成物の成形性などを勘案すると、酸化チタンに対し、通常1〜5質量%の範囲である。 Surface treatment methods using an organosiloxane-based surface treatment agent of titanium oxide include a wet method and a dry method. In the wet method, a mixture of an organosiloxane-based surface treatment agent and a solvent is added with alumina hydrate, and if necessary, titanium oxide pretreated with silicic acid hydrate. Furthermore, it is a method of heat-processing at 100-300 degreeC after that. In the dry method, pretreated titanium oxide and polyorganohydrogensiloxane are mixed with a Henschel mixer in the same manner as described above, and an organic solution of polyorganohydrogensiloxane is sprayed on the pretreated titanium oxide. And a method of heat-treating at 100 to 300 ° C. The amount of the siloxane-based surface treatment agent is not particularly limited, but in consideration of the reflectivity of titanium oxide, the moldability of the resin composition, etc., it is usually in the range of 1 to 5% by mass with respect to titanium oxide. is there.
酸化チタンの含有量は、ポリカーボネート樹脂100質量部に対し、3〜30質量部の範囲であることが好ましい。ここで、酸化チタンの質量は、アルミナ水和物、珪酸水和物、オルガノシロキサン系の表面処理剤によって表面処理されている場合は、これらの処理剤も含めた全質量を意味する。 The content of titanium oxide is preferably in the range of 3 to 30 parts by mass with respect to 100 parts by mass of the polycarbonate resin. Here, the mass of titanium oxide means the total mass including these treatment agents when surface treatment is performed with an alumina hydrate, silicic acid hydrate, or an organosiloxane surface treatment agent.
・・ガラス繊維
ガラス繊維としては、通常熱可塑性樹脂に使用されているものであれば、Aガラス、Eガラス、ジルコニア成分含有の耐アルカリガラス組成や、チョツプドストラント、ロービングガラス、熱可塑性樹脂とガラス繊維の(長繊維)マスターバッチ等の配合時のガラス繊維の形態を問わず、公知のいかなるガラス繊維も使用可能である。なかでも本発明に用いるガラス繊維としては、本発明のポリカーボネート樹脂組成物の熱安定性を向上させる目的から無アルカリガラス(Eガラス)が好ましい。
..Glass fiber As long as glass fiber is usually used for thermoplastic resin, A glass, E glass, alkali-resistant glass composition containing zirconia component, chopped strand, roving glass, thermoplastic resin Any known glass fiber can be used regardless of the form of the glass fiber at the time of blending the (long fiber) masterbatch and the like. Especially, as a glass fiber used for this invention, an alkali free glass (E glass) is preferable from the objective of improving the thermal stability of the polycarbonate resin composition of this invention.
ガラス繊維の数平均繊維長は1mm以上10mm以下であることが好ましく、1.5〜6mmであることがより好ましく、2〜5mmであることがさらに好ましい。数平均繊維長が10mmを超えると成形品表面からのガラス繊維の脱落が発生しやすく、生産性が低下しやすい。数平均繊維長が1mm未満では、ガラス繊維のアスペクト比が小さいため、機械的強度の改良が不十分となりやすい。 The number average fiber length of the glass fibers is preferably 1 mm or more and 10 mm or less, more preferably 1.5 to 6 mm, and further preferably 2 to 5 mm. When the number average fiber length exceeds 10 mm, the glass fibers are likely to fall off from the surface of the molded product, and the productivity tends to be lowered. If the number average fiber length is less than 1 mm, the glass fiber has a small aspect ratio, and therefore mechanical strength is likely to be insufficiently improved.
ガラス繊維の直径は3μm以上20μm以下であることが好ましい。これらは、従来公知の任意の方法に従い、ガラス繊維のストランドを、具体的には例えばハンマーミルやボールミルで粉砕することにより製造できる。ガラス繊維の直径が3μm未満の場合は、同様に機械的強度の改良が不十分で、20μmを超えると外観が低下しやすい。ガラス繊維の直径は、より好ましくは5μm以上15μm以下、さらに好ましくは6μm以上14μm以下である。 The diameter of the glass fiber is preferably 3 μm or more and 20 μm or less. These can be produced by pulverizing glass fiber strands using, for example, a hammer mill or a ball mill according to any conventionally known method. When the diameter of the glass fiber is less than 3 μm, the improvement of the mechanical strength is similarly insufficient, and when it exceeds 20 μm, the appearance tends to deteriorate. The diameter of the glass fiber is more preferably 5 μm or more and 15 μm or less, and further preferably 6 μm or more and 14 μm or less.
本発明で使用するガラス繊維は、ポリカーボネート樹脂との密着性を向上させる目的で、アミノシラン、エポキシシラン等のシランカップリング剤などにより表面処理を行うことができる。 The glass fiber used in the present invention can be subjected to surface treatment with a silane coupling agent such as aminosilane or epoxysilane for the purpose of improving the adhesion to the polycarbonate resin.
また、ガラス繊維は、通常はこれらの繊維を多数本集束したものを、所定の長さに切断したチョップドストランド(チョップドガラス繊維)として用いることが好ましく、このときガラス繊維は収束剤を配合することが好ましい。収束剤を配合することで本発明のポリカーボネート樹脂組成物の生産安定性が高まる利点に加え、良好な機械物性を得ることができる。
収束剤としては、特に制限はないが、例えばウレタン系、エポキシ系、アクリル系等の収束剤が挙げられる。なかでも本発明に使用するガラス繊維の収束剤としては、ウレタン系、エポキシ系収束剤がより好ましく、エポキシ系収束剤がさらに好ましい。
Moreover, it is preferable to use a glass fiber that is usually a bundle of many of these fibers as a chopped strand (chopped glass fiber) cut into a predetermined length. At this time, the glass fiber should contain a sizing agent. Is preferred. In addition to the advantage of increasing the production stability of the polycarbonate resin composition of the present invention by blending the sizing agent, good mechanical properties can be obtained.
The sizing agent is not particularly limited, and examples thereof include urethane-based, epoxy-based, acrylic-based sizing agents. Among them, as the glass fiber sizing agent used in the present invention, urethane-based and epoxy-based sizing agents are more preferable, and epoxy-based sizing agents are more preferable.
チョップドストランド(チョップドガラス繊維)のカット長についても特に制限はないが、通常1〜10mm、好ましくは1.5〜6mm、より好ましくは2〜5mmである。 Although there is no restriction | limiting in particular also about the cut length of a chopped strand (chopped glass fiber), Usually, 1-10 mm, Preferably it is 1.5-6 mm, More preferably, it is 2-5 mm.
ガラス繊維の好ましい含有量としては、ポリカーボネート樹脂100質量に対し、10〜100質量部である。ガラス繊維の含有量が10質量部未満では弾性率向上効果が不十分であり、逆に100質量部を超えると耐衝撃性や流動性が不十分となりやすい。ガラス繊維の含有量は、より好ましくは20質量部以上、さらに好ましくは25質量部以上であり、またより好ましくは80質量部以下、さらに好ましくは65質量部以下である。 As preferable content of glass fiber, it is 10-100 mass parts with respect to 100 mass of polycarbonate resin. If the glass fiber content is less than 10 parts by mass, the effect of improving the elastic modulus is insufficient. Conversely, if the glass fiber content exceeds 100 parts by mass, the impact resistance and fluidity tend to be insufficient. The content of the glass fiber is more preferably 20 parts by mass or more, further preferably 25 parts by mass or more, more preferably 80 parts by mass or less, and further preferably 65 parts by mass or less.
[ポリカーボネート樹脂組成物の製造方法]
本発明の熱伝導性ポリカーボネート樹脂組成物の製造方法に制限はなく、公知のポリカーボネート樹脂組成物の製造方法を広く採用でき、ポリカーボネート樹脂、窒化硼素及びタルク、並びに、必要に応じて配合されるその他の成分を、例えばタンブラーやヘンシェルミキサーなどの各種混合機を用い予め混合した後、バンバリーミキサー、ロール、ブラベンダー、単軸混練押出機、二軸混練押出機、ニーダーなどの混合機で溶融混練する方法が挙げられる。
なお、溶融混練の温度は特に制限されないが、通常240〜320℃の範囲である。
[Production Method of Polycarbonate Resin Composition]
There is no limitation on the production method of the heat conductive polycarbonate resin composition of the present invention, and a wide variety of production methods of known polycarbonate resin compositions can be adopted. Polycarbonate resin, boron nitride and talc, and other blended as necessary Are mixed in advance using various mixers such as a tumbler and a Henschel mixer, and then melt-kneaded with a mixer such as a Banbury mixer, roll, brabender, single-screw kneading extruder, twin-screw kneading extruder, kneader or the like. A method is mentioned.
The temperature for melt kneading is not particularly limited, but is usually in the range of 240 to 320 ° C.
本発明の熱伝導性ポリカーボネート樹脂組成物は、耐衝撃性が向上しており、具体的には、ノッチなしシャルピー衝撃強度が105kJ/m2以上の値を示すことが可能である。ノッチなしシャルピー衝撃強度は、より好ましくは110kJ/m2以上であり、上限としては好ましくは150kJ/m2以下、より好ましくは145kJ/m2以下、さらに好ましくは140kJ/m2以下である。 The heat conductive polycarbonate resin composition of the present invention has improved impact resistance. Specifically, the notch-free Charpy impact strength can exhibit a value of 105 kJ / m 2 or more. The notch-free Charpy impact strength is more preferably 110 kJ / m 2 or more, and the upper limit is preferably 150 kJ / m 2 or less, more preferably 145 kJ / m 2 or less, and further preferably 140 kJ / m 2 or less.
[成形品]
上記したポリカーボネート樹脂組成物をペレタイズしたペレットは、各種の成形法で成形して成形品とされる。またペレットを経由せずに、押出機で溶融混練された樹脂を直接、成形して成形品にすることもできる。
成形品の形状としては、特に制限はなく、成形品の用途、目的に応じて適宜選択することができ、例えば、板状、プレート状、ロッド状、シート状、フィルム状、円筒状、環状、円形状、楕円形状、多角形形状、異形品、中空品、枠状、箱状、パネル状のもの等が挙げられる。
[Molding]
The pellets obtained by pelletizing the above-described polycarbonate resin composition are molded into various molded products by various molding methods. Further, the resin melt-kneaded by an extruder can be directly molded into a molded product without going through the pellets.
The shape of the molded product is not particularly limited and can be appropriately selected according to the use and purpose of the molded product. For example, a plate shape, a plate shape, a rod shape, a sheet shape, a film shape, a cylindrical shape, an annular shape, Examples include a circular shape, an elliptical shape, a polygonal shape, an irregular shape, a hollow shape, a frame shape, a box shape, and a panel shape.
成形体を成形する方法としては、特に制限されず、従来公知の成形法を採用でき、例えば、射出成形法、射出圧縮成形法、押出成形法、異形押出法、トランスファー成形法、中空成形法、ガスアシスト中空成形法、ブロー成形法、押出ブロー成形、IMC(インモールドコ−ティング成形)成形法、回転成形法、多層成形法、2色成形法、インサート成形法、サンドイッチ成形法、発泡成形法、加圧成形法等が挙げられる。 The method for molding the molded body is not particularly limited, and a conventionally known molding method can be employed.For example, an injection molding method, an injection compression molding method, an extrusion molding method, a profile extrusion method, a transfer molding method, a hollow molding method, Gas assisted hollow molding method, blow molding method, extrusion blow molding, IMC (in-mold coating molding) molding method, rotational molding method, multilayer molding method, two-color molding method, insert molding method, sandwich molding method, foam molding method And a pressure molding method.
本発明のポリカーボネート樹脂組成物は、熱伝導性(放熱性)と耐熱性と耐衝撃性に優れた高熱伝導性の樹脂材料であるので、これを成形した成形品は、パーソナルコンピューター、デジタルカメラ或いは各種携帯端末等の部品や筺体、LED照明におけるLED実装用基板又はヒートシンク部材並びに部品類、バッテリー充電用機器部品、バッテリーカバー等に特に好適である。 Since the polycarbonate resin composition of the present invention is a highly heat conductive resin material excellent in heat conductivity (heat dissipation), heat resistance and impact resistance, a molded product obtained by molding it can be a personal computer, digital camera or It is particularly suitable for parts and casings of various portable terminals, LED mounting substrates or heat sink members and parts in LED lighting, battery charging equipment parts, battery covers, and the like.
以下、実施例を示して本発明について更に具体的に説明する。ただし、本発明は以下の実施例に限定されるものではなく、本発明の要旨を逸脱しない範囲において任意に変更して実施できる。
以下の実施例及び比較例に使用した各原料成分は、以下の表1のとおりである。
Hereinafter, the present invention will be described more specifically with reference to examples. However, the present invention is not limited to the following examples, and can be arbitrarily modified and implemented without departing from the gist of the present invention.
Each raw material component used in the following Examples and Comparative Examples is as shown in Table 1 below.
(実施例1〜13、比較例1〜2)
上記表1に記載した各成分を、下記の表3〜表5に示す割合(全て質量部にて表示)にて配合し、タンブラーミキサーにて均一に混合した後、二軸押出機(日本製鋼所製TEX30HSST)を用いて、シリンダー温度280℃、スクリュー回転数200rpm、吐出量20kg/hrにて押出機上流部のバレルより押出機にフィードし、溶融混練させてポリカーボネート樹脂組成物のペレットを得た。
(Examples 1-13, Comparative Examples 1-2)
Each component described in Table 1 above was blended in the proportions shown in Tables 3 to 5 below (all expressed in parts by mass) and uniformly mixed with a tumbler mixer, and then a twin screw extruder (Nippon Steel). Using TEX30HSST (manufactured by TEPCO), the cylinder temperature is 280 ° C., the screw rotation speed is 200 rpm, and the discharge rate is 20 kg / hr. It was.
[耐衝撃性の評価:シャルピー衝撃値(単位:kJ/m2)]
上記の方法で得られた樹脂組成物ペレットを100℃で5時間乾燥した後、射出成形機(日本製鋼所社製「J55−60H」)を用い、シリンダー設定温度270〜290℃、金型温度100℃、射出時間2秒、成形サイクル40秒の条件で射出成形を行い、ISO多目的試験片(4mm厚)を射出成形した。
得られたISO多目的試験片を使用し、切削加工にてノッチ有の試験片も準備した。
ISO179に準拠し、23℃の条件で、ノッチ有とノッチ無シャルピー耐衝撃強度(単位:kJ/m2)をそれぞれ測定した。
[Evaluation of impact resistance: Charpy impact value (unit: kJ / m 2 )]
After drying the resin composition pellet obtained by the above method at 100 ° C. for 5 hours, using an injection molding machine (“J55-60H” manufactured by Nippon Steel Co., Ltd.), a cylinder set temperature of 270 to 290 ° C., a mold temperature Injection molding was performed under the conditions of 100 ° C., injection time of 2 seconds, and molding cycle of 40 seconds, and an ISO multipurpose test piece (4 mm thick) was injection molded.
Using the obtained ISO multipurpose test piece, a test piece with a notch was also prepared by cutting.
In accordance with ISO 179, the notched and notched Charpy impact strength (unit: kJ / m 2 ) was measured under the condition of 23 ° C., respectively.
[耐熱性の評価:DTUL(荷重たわみ温度、単位:℃)]
上記で得られたISO多目的試験片を用い、ISO75−1&2に従い、荷重1.80MPaの条件(A法)にて測定を行った。なお、表中、「DTUL」と表記する。
[Evaluation of heat resistance: DTUL (deflection temperature under load, unit: ° C)]
Using the ISO multipurpose test piece obtained above, the measurement was performed under the condition (Method A) under a load of 1.80 MPa according to ISO 75-1 & 2. In the table, “DTUL” is used.
[熱伝導率の測定(単位:W/m・K)]
上記で得られたISO多目的試験片を0.15〜0.5mm厚のスライス状に切削し、これを試料として、(株)アイフェイズ製温度波熱分析装置「ai−Phase Mobile1」を使用し、MD方向(成形時の樹脂流れ方向)及び厚み方向について、測定した。
[Measurement of thermal conductivity (unit: W / m · K)]
The ISO multipurpose test piece obtained above was cut into a slice of 0.15 to 0.5 mm thickness, and this was used as a sample using a temperature wave thermal analyzer “ai-Phase Mobile1” manufactured by I-Phase Co., Ltd. The MD direction (resin flow direction during molding) and the thickness direction were measured.
[燃焼性の評価:UL94試験]
上記ペレットを100℃、5時間乾燥後、射出成形機(日本製鋼所製「J55−60H」)にて、シリンダー設定温度290℃、金型温度120℃、成形サイクル30秒の条件で射出成形し、長さ125mm×幅13mmで、厚さが1.5mmのUL試験用試験片を成形した。
得られた試験片を、温度23℃、湿度50%の恒温室の中で48時間調湿し、米国アンダーライターズ・ラボラトリーズ(UL)が定めているUL94試験(機器の部品用プラスチック材料の燃焼試験)に準拠して行なった。UL94Vとは、鉛直に保持した所定の大きさの試験片にバーナーの炎を10秒間接炎した後の残炎時間やドリップ性から燃焼性を評価する方法であり、V−0、V−1及びV−2の燃焼性を有するためには、以下の表2に示す基準を満たすことが必要となる。
[Evaluation of flammability: UL94 test]
The pellets were dried at 100 ° C. for 5 hours, and then injection-molded with an injection molding machine (“J55-60H” manufactured by Nippon Steel) under conditions of a cylinder set temperature of 290 ° C., a mold temperature of 120 ° C., and a molding cycle of 30 seconds. A test piece for UL test having a length of 125 mm × width of 13 mm and a thickness of 1.5 mm was molded.
The obtained specimens were conditioned for 48 hours in a temperature-controlled room at 23 ° C. and 50% humidity, and UL94 test (combustion of plastic materials for equipment parts) was established by US Underwriters Laboratories (UL). Test). UL94V is a method for evaluating the flammability from the afterflame time and the drip property after the flame of the burner is indirectly fired for 10 seconds on a test piece of a predetermined size held vertically. V-0, V-1 And in order to have V-2 flammability, it is necessary to satisfy the criteria shown in Table 2 below.
ここで残炎時間とは、着火源を遠ざけた後の、試験片の有炎燃焼を続ける時間の長さである。また、ドリップによる綿着火とは、試験片の下端から約300mm下にある標識用の綿が、試験片からの滴下(ドリップ)物によって着火されるかどうかによって決定される。さらに、5試料のうち、1つでも上記基準を満たさないものがある場合、V−2を満足しないとしてNR(not rated)と評価した。 Here, the after-flame time is the length of time for which the flammable combustion of the test piece is continued after the ignition source is moved away. The cotton ignition by the drip is determined by whether or not the labeling cotton, which is about 300 mm below the lower end of the test piece, is ignited by a drip from the test piece. Further, when any one of the five samples did not satisfy the above criteria, it was evaluated as NR (not rated) because V-2 was not satisfied.
[色相評価]
樹脂組成物のペレットを用いて、射出成形機(日本製鋼所製「J55−60H」)により、280℃の温度で成形したプレート(90mm×50mm×厚さ3mm、2mm、1mmの3段)の3mm厚部分について、分光式色彩計(日本電色工業社製「SE−2000型」)を使用して反射モードで、L*、a*、b*及びYI値を測定した。
以上の評価結果を、表3〜表5に示した。
[Hue evaluation]
Using the pellets of the resin composition, an injection molding machine (“J55-60H” manufactured by Nippon Steel Works) of a plate (three stages of 90 mm × 50 mm × thickness 3 mm, 2 mm, 1 mm) molded at a temperature of 280 ° C. About a 3 mm thickness part, L * , a * , b *, and YI value were measured in the reflection mode using the spectroscopic color meter (Nippon Denshoku Industries "SE-2000 type | mold").
The above evaluation results are shown in Tables 3 to 5.
本発明の熱伝導性ポリカーボネート樹脂組成物によれば、熱伝導性、耐熱性及び耐衝撃性に優れた熱伝導性熱可塑性樹脂材料が得られるので、パーソナルコンピューター、デジタルカメラ或いは各種携帯端末の部品や筺体、LED照明におけるLED実装用基板又はヒートシンク部材並びに部品類、バッテリー充電用機器部品、バッテリーカバー等などに特に好適に利用でき、産業上の利用性は非常に高いものがある。 According to the heat conductive polycarbonate resin composition of the present invention, a heat conductive thermoplastic resin material having excellent heat conductivity, heat resistance, and impact resistance can be obtained. Therefore, components for personal computers, digital cameras, and various portable terminals are used. It can be particularly preferably used for LED mounting substrates or heat sink members and parts, battery charging equipment parts, battery covers, etc. in LED lighting, and has very high industrial applicability.
Claims (5)