JP2015217608A - 軟質塩化ビニル樹脂製産業資材シート - Google Patents
軟質塩化ビニル樹脂製産業資材シート Download PDFInfo
- Publication number
- JP2015217608A JP2015217608A JP2014103091A JP2014103091A JP2015217608A JP 2015217608 A JP2015217608 A JP 2015217608A JP 2014103091 A JP2014103091 A JP 2014103091A JP 2014103091 A JP2014103091 A JP 2014103091A JP 2015217608 A JP2015217608 A JP 2015217608A
- Authority
- JP
- Japan
- Prior art keywords
- vinyl chloride
- chloride resin
- chemical formula
- triisocyanate
- soft vinyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】繊維織物を基材として、その少なくとも1面上に軟質塩化ビニル樹脂層を設けた可撓性積層体において、軟質塩化ビニル樹脂層が塩化ビニル系樹脂を主体に含み、さらにイソフタル酸ジアルキルエステル,テレフタル酸ジアルキルエステル、シクロヘキサンジカルボン酸ジアルキルエステル(オルト、メタ、パラの位置異性体を含む)から選ばれた1種以上の可塑剤、及びトリイソシアネート化合物とを質量比10:0.1〜10:1の範囲で含み、トリイソシアネート化合物が、少なくとも繊維織物の表面に対する結合を含む架橋構造を形成させる。
【選択図】なし
Description
〈耐熱性〉
〈接合体による耐熱クリープ特性による評価〉
2枚のシートの端部同士を4cm幅で直線状に平行に重ね合わせ、4cm幅×30
cm長のウエルドバー(平刃)を装着した高周波ウエルダー融着機(山本ビニター社
製YF−7000型:出力7KW)を用い、陽極電流1.0Aでシート同士の融着接
合を行い接合体シートを得た。これより融着接合部を重ね合わせ幅4cmを含む、
3cm幅×30cm長の試験片を9片採取し、クリープ試験機(東洋精機製作所社製:
100LDR型)により60℃×25kgf荷重(条件1)、65℃×25kgf荷
重(条件2)、70℃×25kgf荷重(条件3)の3条件で耐熱クリープ性を24
時間評価した。
評価の基準
1 :24時間経過後、接合部に異変や異常なく良好。
2 :24時間未満で接合部が破壊し、試験片が分断した。
〈破壊した時間を記録〉
3 :1時間以内に接合部が破壊し、試験片が分断した。
〈破壊した時間を記録〉
破壊状態の判断:接合部糸抜け破壊(糸の断裂なし),本体破壊等(糸の断裂あり)
〈耐光堅牢性〉
JIS K7350−3「プラスチック−実験室光源による暴露試験方法:紫外線蛍光ランプ」にて120時間、240時間、480時間の照射時間ごとにシート片の変色を色差ΔE(JIS Z8729)で評価した。(促進前のシート片を基準とする)
ΔE=0〜2.9 : 1=変色は極僅か (初期外観を維持)
ΔE=3〜5.9 : 2=やや変色を伴う(実用に支障なし)
ΔE=6〜11.9 : 3=薄い褐色に変化(実用に支障する)
ΔE=12〜 : 4=濃い褐色に変化(実用に支障する)
〈可塑剤ブリードの抑止効果:濡れ性評価〉
10cm×10cmサイズの試料を2枚のガラス板(10cm×10cmサイズ×5mm厚)で挟み、これを65℃に設定したギアーオーブン中に平置した状態で72時間静置し、取り出し直後のガラス板面の曇り(フォギング)や濡れ(ブリード)の有無の目視及び指触判断を以って可塑剤のブリードの抑止性(防止性)を判断した。
1(良好):ガラス板面にやや曇りを認めるレベル
2(やや不良):ガラス板面に曇りを認め、触ると滑るレベル
3(不良):ガラス板面に顕著な濡れを認め、試料表面にも濡れを認めるレベル
〈可塑剤ブリードの抑止効果:揮発減量評価〉
質量の明らかな10cm×10cmサイズの試料を85℃に設定したギアーオーブン中に吊した状態で72時間静置し、取り出し後の試料の質量より可塑剤の揮発量を求め、この揮発減量の「多い」「少ない」を以って可塑剤のブリードの抑止性(防止性)を判断した。
1:(ブリード防止効果を認める):50mg以下のレベル
2:(ブリード抑止効果を認める):50〜150mgのレベル
3:(ブリード防止効果が認めなれない):150mgを越えるレベル
ポリエステル(PET)短繊維紡績糸条からなる平織スパン布を基布1として用いた。
〈繊維織物:基布1〉
〔糸密度:経糸20番手双糸(590dtex)44本/インチ×緯糸20番手双糸(590dtex)40本/インチ:空隙率4.2%:質量228g/m2:両面にコロナ放電処理〕
下記〔配合1〕の軟質塩化ビニル樹脂ペーストゾル組成物を適度な粘度に調製し、この〔配合1〕のペーストゾル組成物を充填した液浴中に、基布1を浸漬し、基布1に完全に〔配合1〕のペーストゾル組成物を含浸し、基布1を引き上げると同時にゴムロールで圧搾して180℃の熱風炉で3分間、〔配合1〕のペーストゾル組成物のゲル化と、トリイソシアネート化合物の付加反応を進行させ、〔配合1〕のペーストゾル組成物で含浸し、かつ被覆されることで基布1の両面に軟質塩化ビニル樹脂層が形成された厚さ0.47mm、質量560g/m2の帆布を得た。
〔配合1〕軟質塩化ビニル樹脂ペーストゾル組成物
乳化重合ポリ塩化ビニル樹脂(重合度1700) 100質量部
イソフタル酸ジ(2−エチルヘキシル)(C8:MW390) 60質量部
※〔化1〕のRが2個とも炭素数9の分岐鎖状のアルキル基
エチレングリコール(ポリオール) 3.5質量部
エポキシ化大豆油(可塑剤) 10質量部
ステアリン酸亜鉛(安定剤) 2質量部
ステアリン酸バリウム(安定剤) 2質量部
表面水酸基修飾シリカ粒子(75nm) 5質量部
ルチル型酸化チタン(白色顔料) 5質量部
トリイソシアネート化合物 3質量部
※ヘキサメチレンジイソシアネート(HMDI)〔化12〕の3量体であるイソシアヌ
レート変性トリイソシアネート(〔化6〕−〔化9〕系)
※イソフタル酸ジ(2−エチルヘキシル)とトリイソシアネート化合物との質量比は
60:3(20:1)である。
実施例1において〔配合1〕に用いたイソフタル酸ジ(2−エチルヘキシル)(C8:MW390)60質量部を、テレフタル酸ジ(2−エチルヘキシル)(C8:MW390:〔化2〕のRが2個とも炭素数9の分岐鎖状のアルキル基)60質量部に置換し、さらにトリイソシアネート化合物:イソシアヌレート変性トリイソシアネート(〔化6〕−〔化9〕系)3質量部を、ヘキサメチレンジイソシアネート(HMDI)〔化12〕の3量体であるイソシアヌレート変性トリイソシアネート(〔化6〕−〔化10〕系)3質量部に置換した以外は実施例1と同様として、厚さ0.47mm、質量560g/m2の帆布を得た。
実施例1において〔配合1〕に用いたイソフタル酸ジ(2−エチルヘキシル)(C8:MW390)60質量部を、1,3−シクロヘキサンジカルボン酸ジ−2−エチルヘキシル(別名1,3−シクロヘキサンジカルボン酸ジオクチル)(C8:MW393:〔化3〕のRが2個とも炭素数9の分岐鎖状のアルキル基)60質量部に置換し、さらにトリイソシアネート化合物:イソシアヌレート変性トリイソシアネート(〔化6〕−〔化9〕系)3質量部を、ヘキサメチレンジイソシアネート(HMDI)〔化12〕の3量体であるイソシアヌレート変性トリイソシアネート(〔化6〕−〔化11〕系)3質量部に置換した以外は実施例1と同様として、厚さ0.47mm、質量560g/m2の帆布を得た。
実施例1において〔配合1〕に用いたイソフタル酸ジ(2−エチルヘキシル)(C8:MW390)60質量部を、1,4−シクロヘキサンジカルボン酸ジ−2−エチルヘキシル(別名1,4−シクロヘキサンジカルボン酸ジオクチル)(C8:MW393:〔化4〕のRが2個とも炭素数9の分岐鎖状のアルキル基)60質量部に置換し、さらにトリイソシアネート化合物:イソシアヌレート変性トリイソシアネート(〔化6〕−〔化9〕系)3質量部を、イソホロンジイソシアネート(IPDI)〔化13〕の3量体であるビュレット変性トリイソシアネート(〔化7〕−〔化9〕系)3質量部に置換した以外は実施例1と同様として、厚さ0.47mm、質量560g/m2の帆布を得た。
ポリエステル(PET)マルチフィラメント糸条からなる目抜け平織物を基布2として用いた。
〈繊維織物:基布2〉
〔糸密度:750d/3本模紗(833dtex/3本模紗)を経緯糸条として、経糸条11本/インチ、緯糸条11本/インチの打ち込みで製織した粗目模紗織物(質量225g/m2:空隙率11%:両面にコロナ放電処理)
実施例1において〔配合1〕に用いたトリイソシアネート化合物:イソシアヌレート変性トリイソシアネート(〔化6〕−〔化9〕系)3質量部を、イソホロンジイソシアネート(IPDI)〔化13〕の3量体であるビュレット変性トリイソシアネート(〔化7〕−〔化10〕系)3質量部に置換した〔配合2〕をペーストゾル組成物とした。
〔配合2〕の軟質塩化ビニル樹脂ペーストゾル組成物を適度な粘度に調製し、この〔配合2〕のペーストゾル組成物を充填した液浴中に、基布2を浸漬し、基布2に完全に〔配合2〕のペーストゾル組成物を含浸し、基布2を引き上げると同時にゴムロールで圧搾して180℃の熱風炉で3分間、〔配合2〕のペーストゾル組成物のゲル化と、トリイソシアネート化合物の付加反応を進行させ、〔配合2〕のペーストゾル組成物で含浸し、かつ被覆されることで基布2の両面に軟質塩化ビニル樹脂層が形成された厚さ0.36mm、質量470g/m2、空隙率10%のメッシュシートを得た。
実施例5において〔配合2〕に用いたイソフタル酸ジ(2−エチルヘキシル)(C8:MW390)60質量部を、テレフタル酸ジ(2−エチルヘキシル)(C8:MW390:〔化2〕のRが2個とも炭素数9の分岐鎖状のアルキル基)60質量部に置換し、さらにトリイソシアネート化合物:ビュレット変性トリイソシアネート(〔化7〕−〔化10〕系)3質量部を、イソホロンジイソシアネート(IPDI)〔化13〕の3量体であるビュレット変性トリイソシアネート(〔化7〕−〔化11〕系)3質量部に置換した以外は実施例5と同様として、厚さ0.36mm、質量470g/m2、空隙率10%のメッシュシートを得た。
実施例5において〔配合2〕に用いたイソフタル酸ジ(2−エチルヘキシル)(C8:MW390)60質量部を、1,2−シクロヘキサンジカルボン酸ジ−2−エチルヘキシル(別名1,2−シクロヘキサンジカルボン酸ジオクチル)(C8:MW393:〔化5〕のRが2個とも炭素数9の分岐鎖状のアルキル基)60質量部に置換し、さらにトリイソシアネート化合物:ビュレット変性トリイソシアネート(〔化7〕−〔化10〕系)3質量部を、水素添加キシリレンジイソシアネート(H6XDI)〔化14〕の3量体であるトリメチロールアルキル変性トリイソシアネート(〔化8〕−〔化9〕系)3質量部に置換した以外は実施例5と同様として、厚さ0.36mm、質量470g/m2、空隙率10%のメッシュシートを得た。
実施例5において〔配合2〕に用いたイソフタル酸ジ(2−エチルヘキシル)(C8:MW390)60質量部を、1,4−シクロヘキサンジカルボン酸ジ−2−エチルヘキシル(別名1,4−シクロヘキサンジカルボン酸ジオクチル)(C8:MW393:〔化4〕のRが2個とも炭素数9の分岐鎖状のアルキル基)60質量部に置換し、さらにトリイソシアネート化合物:ビュレット変性トリイソシアネート(〔化7〕−〔化10〕系)3質量部を、水素添加キシリレンジイソシアネート(H6XDI)〔化14〕の3量体であるトリメチロールアルキル変性トリイソシアネート(〔化8〕−〔化10〕系)3質量部に置換した以外は実施例5と同様として、厚さ0.36mm、質量470g/m2、空隙率10%のメッシュシートを得た。
ポリエステル(PET)マルチフィラメント糸条からなる目抜け平織物を基布3として用いた。
〈繊維織物:基布3〉
〔糸密度:1000d(1111dtex)を経緯糸条として、経糸条19本/インチ、緯糸条20本/インチの打ち込みで製織した粗目平織物(質量190g/m2:空隙率7%:両面にコロナ放電処理)
基布3の両面に〔配合3〕の軟質塩化ビニル樹脂コンパウンドから165℃〜180℃の熱条件でカレンダー成型された厚さが0.16mmのフィルムを、ラミネーターにより170℃の熱ロール条件でフィルムを軟化させた状態で積層し、厚さが0.75mm、質量が940g/m2のターポリンを得た。
〔配合3〕軟質塩化ビニル樹脂コンパウンド組成物
懸濁重合ポリ塩化ビニル樹脂(重合度1300) 100質量部
イソフタル酸ジ(2−エチルヘキシル)(C8:MW390) 60質量部
※〔化1〕のRが2個とも炭素数9の分岐鎖状のアルキル基
エチレングリコール(ポリオール) 3.5質量部
エポキシ化大豆油(可塑剤) 10質量部
ステアリン酸亜鉛(安定剤) 2質量部
ステアリン酸バリウム(安定剤) 2質量部
表面水酸基修飾シリカ粒子(75nm) 5質量部
ルチル型酸化チタン(白色顔料) 5質量部
トリイソシアネート化合物 3質量部
※水素添加キシリレンジイソシアネート(H6XDI)〔化14〕の3量体であるトリ
メチロールアルキル変性トリイソシアネート(〔化8〕−〔化11〕系)
※イソフタル酸ジ(2−エチルヘキシル)とトリイソシアネート化合物との質量比は
60:3(20:1)である。
実施例9において〔配合3〕に用いたイソフタル酸ジ(2−エチルヘキシル)(C8:MW390)60質量部を、テレフタル酸ジ(2−エチルヘキシル)(C8:MW390:〔化2〕のRが2個とも炭素数9の分岐鎖状のアルキル基)60質量部に置換し、さらにトリイソシアネート化合物:トリメチロールアルキル変性トリイソシアネート(〔化8〕−〔化11〕系)を、ヘキサメチレンジイソシアネート(HMDI)〔化12〕の3量体であるイソシアヌレート変性トリイソシアネート(〔化6〕−〔化9〕系)3質量部に置換した以外は実施例9と同様として、厚さが0.75mm、質量が940g/m2のターポリンを得た。
実施例9において〔配合3〕に用いたイソフタル酸ジ(2−エチルヘキシル)(C8:MW390)60質量部を、1,3−シクロヘキサンジカルボン酸ジ−2−エチルヘキシル(別名1,3−シクロヘキサンジカルボン酸ジオクチル)(C8:MW393:〔化3〕のRが2個とも炭素数9の分岐鎖状のアルキル基)60質量部に置換し、さらにトリイソシアネート化合物:トリメチロールアルキル変性トリイソシアネート(〔化8〕−〔化11〕系)を、イソホロンジイソシアネート(IPDI)〔化13〕の3量体であるビュレット変性トリイソシアネート(〔化7〕−〔化9〕系)3質量部に置換した以外は実施例9と同様として、厚さが0.75mm、質量が940g/m2のターポリンを得た。
実施例9において〔配合3〕に用いたイソフタル酸ジ(2−エチルヘキシル)(C8:MW390)60質量部を、1,2−シクロヘキサンジカルボン酸ジ−2−エチルヘキシル(別名1,2−シクロヘキサンジカルボン酸ジオクチル)(C8:MW393:〔化5〕のRが2個とも炭素数9の分岐鎖状のアルキル基)60質量部に置換し、さらにトリイソシアネート化合物:トリメチロールアルキル変性トリイソシアネート(〔化8〕−〔化11〕系)を、水素添加キシリレンジイソシアネート(H6XDI)〔化14〕の3量体であるトリメチロールアルキル変性トリイソシアネート(〔化8〕−〔化9〕系)3質量部に置換した以外は実施例9と同様として、厚さが0.75mm、質量が940g/m2のターポリンを得た。
実施例1〜4の帆布、実施例5〜8のメッシュシート、及び実施例9〜12のターポリンの表面に下記〔配合4〕による防汚層を形成し、各々、実施例13〜16の防汚層を片表面に設けた帆布、実施例17〜20の防汚層を両面に設けたメッシュシート、及び実施例21〜24の防汚層を片表面に設けたターポリンを得た。
〈防汚層〉
実施例1〜12の基材を100メッシュグラビアロール塗工条件の塗工機に掛け、軟質塩化ビニル樹脂層上に下記〔配合4〕の防汚組成物による表面処理を行い、120℃の熱風炉で3分間乾燥した。この防汚層は室温で約3日間養生した以降より効果を発現する。
〔配合4〕防汚組成物
シリカゾル(粒子径20〜30nm:固形分48質量%) 100質量部
ビニルトリエトキシシラン(シランカップリング剤) 50質量部
ベンゾトリアゾール化合物(紫外線吸収剤) 1質量部
ポリエチレングリコール型非イオン活性剤(帯電防止剤) 1質量部
希釈剤(水) 100質量部
実施例1において、〔配合1〕に用いたトリイソシアネート化合物:イソシアヌレート変性トリイソシアネート(〔化6〕−〔化9〕)3質量部を省略した以外は実施例1と同様として、厚さ0.47mm、質量560g/m2の帆布を得た。
実施例1において、〔配合1〕に用いたトリイソシアネート化合物:イソシアヌレート変性トリイソシアネート(〔化6〕−〔化9〕)3質量部を、トリレンジイソシアネート(TDI)〔化15〕の3量体であるイソシアヌレート変性芳香族トリイソシアネート〔化16〕3質量部に置換した以外は実施例1と同様として、厚さ0.47mm、質量560g/m2の帆布を得た。
実施例1において、〔配合1〕に用いたトリイソシアネート化合物:イソシアヌレート変性トリイソシアネート(〔化6〕−〔化9〕)3質量部を、トリレンジイソシアネート(TDI)〔化15〕の3量体であるビュレット変性芳香族トリイソシアネート〔化17〕3質量部に置換した以外は実施例1と同様として、厚さ0.47mm、質量560g/m2の帆布を得た。
実施例1において、〔配合1〕に用いたトリイソシアネート化合物:イソシアヌレート変性トリイソシアネート(〔化6〕−〔化9〕)3質量部を、トリレンジイソシアネート(TDI)〔化15〕の3量体であるトリメチロールプロパン変性芳香族トリイソシアネート〔化18〕3質量部に置換した以外は実施例1と同様として、厚さ0.47mm、質量560g/m2の帆布を得た。
実施例1において、〔配合1〕に用いた、イソフタル酸ジ(2−エチルヘキシル)(C8:MW390:〔化1〕)60質量部を、ジ−2−エチルヘキシル−フタレート(別名:フタル酸ジオクチル:DOP)60質量部に置換した以外は実施例1と同様として、厚さ0.47mm、質量560g/m2の帆布を得た。
実施例2の配合に用いた、テレフタル酸ジ(2−エチルヘキシル)(C8:MW390:〔化2〕)60質量部を、ジヘプチルフタレート(別名:フタル酸ジヘプチル:DHP)60質量部に置換した以外は実施例2と同様として、厚さ0.47mm、質量560g/m2の帆布を得た。
実施例3の配合に用いた、1,3−シクロヘキサンジカルボン酸ジ−2−エチルヘキシル(別名:1,3−シクロヘキサンジカルボン酸ジオクチル)(C8:MW393:〔化3〕)60質量部を、ジイソノニルフタレート(別名:フタル酸ジイソノニル:DINP)60質量部に置換した以外は実施例3と同様として、厚さ0.47mm、質量560g/m2の帆布を得た。
実施例4の配合に用いた、1,4−シクロヘキサンジカルボン酸ジ−2−エチルヘキシル(別名:1,4−シクロヘキサンジカルボン酸ジオクチル)(C8:MW393:〔化4〕)60質量部を、アジピン酸ジ−2−エチルヘキシル(別名:アジピン酸ジオクチル:DOA)60質量部に置換した以外は実施例4と同様として、厚さ0.47mm、質量560g/m2の帆布を得た。
Claims (6)
- 繊維織物を基材として、その少なくとも1面上に軟質塩化ビニル樹脂層が設けられた可撓性積層体であって、前記軟質塩化ビニル樹脂層が塩化ビニル系樹脂を主体に含み、さらにイソフタル酸ジアルキルエステル(〔化1〕の群),テレフタル酸ジアルキルエステル(〔化2〕の群)、1,3−シクロヘキサンジカルボン酸ジアルキルエステル(〔化3〕の群)、1,4−シクロヘキサンジカルボン酸ジアルキルエステル(〔化4〕の群)、及び1,2−シクロヘキサンジカルボン酸ジアルキルエステル(〔化5〕の群)から選ばれた1種以上の可塑剤、及びトリイソシアネート化合物とを質量比10:0.1〜10:1の範囲で含むことによって構成され、前記トリイソシアネート化合物が、イソシアヌレート変性トリイソシアネート〔化6〕の群(R=〔化9〕〜〔化11〕)、ビュレット変性トリイソシアネート〔化7〕の群(R=〔化9〕〜〔化11〕)、トリメチロールアルキル変性トリイソシアネート〔化8〕の群(R=〔化9〕〜〔化11〕)から選ばれた1種以上であることを特徴とする軟質塩化ビニル樹脂製産業資材シート。
- 前記トリイソシアネート化合物において、前記イソシアヌレート変性トリイソシアネート〔化6〕の群、前記ビュレット変性トリイソシアネート〔化7〕の群及び、前記トリメチロールアルキル変性トリイソシアネート〔化8〕の群が各々、ヘキサメチレンジイソシアネート(HMDI)〔化12〕、イソホロンジイソシアネート(IPDI)〔化13〕、水素添加キシリレンジイソシアネート(H6XDI)〔化14〕の3種から選ばれた何れか1種の化合物を基礎とする3量体であり、前記トリイソシアネート化合物が、これら9種類から選ばれた1種以上である、請求項1に記載の軟質塩化ビニル樹脂製産業資材シート。
- 前記可撓性積層体において前記トリイソシアネート化合物が、少なくとも前記繊維織物の表面に対する結合を含む架橋構造を軟質塩化ビニル樹脂層に形成している請求項1または2に記載の軟質塩化ビニル樹脂製産業資材シート。
- 前記軟質塩化ビニル樹脂層上に、1次粒子径3〜150nmの無機コロイド物質をバインダー成分に担持して含む防汚層が設けられている請求項1〜3の何れか1項に記載の軟質塩化ビニル樹脂製産業資材シート。
- 前記バインダー成分が、シランカップリング剤の加水分解縮合物を含む請求項4に記載の軟質塩化ビニル樹脂製産業資材シート。
- 前記無機コロイド物質が、酸化チタンゾル、酸化亜鉛ゾル、酸化錫ゾル、シリカ(酸化ケイ素)ゾル、アルミナ(酸化アルミニウム)ゾル、ジルコニア(酸化ジルコニウム)ゾル、セリア(酸化セリウム)ゾル、及び複合酸化物(酸化亜鉛−五酸化アンチモン複合または酸化スズ−五酸化アンチモン複合)ゾルから選ばれた1種以上である請求項4に記載の軟質塩化ビニル樹脂製産業資材シート。