JP2015110855A - 細片および偽造防止用紙 - Google Patents
細片および偽造防止用紙 Download PDFInfo
- Publication number
- JP2015110855A JP2015110855A JP2014220633A JP2014220633A JP2015110855A JP 2015110855 A JP2015110855 A JP 2015110855A JP 2014220633 A JP2014220633 A JP 2014220633A JP 2014220633 A JP2014220633 A JP 2014220633A JP 2015110855 A JP2015110855 A JP 2015110855A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- strip
- paper
- stress
- strip according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
(1)爪で引っ掻く、指で折り曲げる等により細片に外力を与えることで生じる発光を目視で確認することで、容易に真贋判定が可能となる。
(2)真珠光沢を有する細片は、可視光下で見る角度により色相が連続して変化するカラーシフト効果を有しており、目視により更に容易に真贋判定することができる。
(3)上記(1)と(2)の効果を同時に発揮することが可能であり、その効果の確認には特別な器具を要しないため、特に容易に真贋判定が可能である。
針葉樹晒クラフトパルプ40質量部、広葉樹晒クラフトパルプ60質量部を380mlC.S.F.に叩解し、これに紙力増強剤(商品名「ポリストロン117」、荒川化学工業(株)製)0.4質量部、サイズ剤(商品名「サイズパインG−F」、荒川化学工業(株)製)1.0質量部、硫酸バンド2.0質量部を加えて紙料を調製し、長網抄紙機を使用して坪量35g/m2の基材(基紙)を抄造した。この基紙の両面に応力発光材料を含む塗工層として、発光中心としてユウロピウムを添加したアルミン酸ストロンチウム(SrAl2O4 :Eu)の粉体をポリビニルアルコール(商品名「クラレポバール117」、クラレ(株)製)とともに水に分散させ、エアナイフコーターで基紙のそれぞれの面に8g/m2塗工した。さらに基紙の両面に接着剤層として、ポリビニルアルコール(商品名「クラレポバール117」、クラレ(株)製)の5質量部%水溶液を、エアナイフコーターで片面当たり2g/m2塗工した。これを打ち抜き機で5mm×6mmの長方形に打ち抜き、細片を得た。
応力発光材料を含む塗工層として発光中心としてユウロピウムを添加したアルミン酸ストロンチウム(SrAl2O4 :Eu)の粉体をポリエステル樹脂(商品名「バイロン、東洋紡(株)製」とともにトルエンに分散させて塗料を調製した。この塗料を実施例1の基紙の両面にグラビアコーターで片面当たり8g/m2塗工した。さらに基紙の両面に接着剤層として、ポリビニルアルコール(商品名「クラレポバール117」、クラレ(株)製)の5質量部%水溶液を、エアナイフコーターで片面当たり2g/m2塗工した。これを打ち抜き機で5mm×6mmの長方形に打ち抜き、細片を得た。
応力発光材料を含む塗工層として発光中心としてユウロピウムを添加したアルミン酸ストロンチウム(SrAl2O4 :Eu)の粉体をポリウレタン樹脂(商品名「サンプレンIB」三洋化成工業(株)製)及びイソシアネート系硬化剤(商品名「コロネート」日本ポリウレタン工業(株)製)と共にトルエンに分散させて塗料を調製した。この塗料を実施例1の基紙の両面にグラビアコーターで片面当たり8g/m2塗工した。さらに基紙の両面に接着剤層として、ポリビニルアルコール(商品名「クラレポバール117」、クラレ(株)製)の5質量部%水溶液を、エアナイフコーターで片面当たり2g/m2塗工した。これを打ち抜き機で5mm×6mmの長方形に打ち抜き、細片を得た。
応力発光材料を含む塗工層として発光中心としてユウロピウムを添加したアルミン酸ストロンチウム(SrAl2O4 :Eu)の粉体をポリウレタン樹脂(商品名「サンプレンIB」三洋化成工業(株)製)及びイソシアネート系硬化剤(商品名「コロネート」日本ポリウレタン工業(株)製)と共にトルエンに分散させて塗料を調製した。基材として厚さ16μmの透明PETフィルム(商品名「ルミラー16S28」、東レ(株)製)を用意し、前記塗料を基材の片面にグラビアコーターで8g/m2塗工した。さらに基紙の両面に接着剤層として、エチレン−酢酸ビニル系感熱接着剤を5μmの厚みで塗工した。これを打ち抜き機で5mm×6mmの長方形に打ち抜き、細片を得た。
ウレタン樹脂バインダー(商品名「ラミックF220」、大日精化工業(株)製)を固形分15%になるように希釈した。この溶液に真珠顔料(商品名「イリオジン225」、メルク(株)製)を総固形分が25%になるように添加、分散した塗料を作成した。この塗料を厚さ16μmの透明PETフィルム(商品名「ルミラー16S28」、東レ(株)製)の片面にグラビアコーターにて10g/m2塗工して真珠光沢層を有するフィルムを作成した。これを基材とする。
応力発光材料を含む塗工層として発光中心としてユウロピウムを添加したアルミン酸ストロンチウム(SrAl2O4 :Eu)の粉体をポリウレタン樹脂(商品名「サンプレンIB」三洋化成工業(株)製)及びイソシアネート系硬化剤(商品名「コロネート」日本ポリウレタン工業(株)製)と共にトルエンに分散させて塗料を調製した。基材として、厚さ16μmの透明多層膜(商品名「MLF16.5」、帝人デュポンフィルム(株)製)を用意し、この片面に前記塗料をグラビアコーターで8g/m2塗工した。さらに基材の両面に接着剤層として、エチレン−酢酸ビニル系感熱接着剤を5μmの厚みで塗工した。これを打ち抜き機で5mm×6mmの長方形に打ち抜き、細片を得た。
応力発光材料として発光中心としてスズを添加したアルミン酸ストロンチウム(SrAl2O4:Sn)の粉体を用いた以外は実施例1と同様にして、細片を得た。このようにして得られた細片を爪で外力を加えたところ、外力の加圧箇所に鮮明な発光が細片の両面で確認された。
応力発光材料として発光中心としてユーロピウムを添加したアルミン酸バリウム(BaAl2O4:Eu)の粉体を用いた以外は実施例1と同様にして、細片を得た。このようにして得られた細片を爪で外力を加えたところ、外力の加圧箇所に鮮明な発光が細片の両面で確認された。
実施例4で得られた細片の打ち抜き前に、応力発光層の上から、紫外線吸収性能を有した樹脂(商品名「ULS−1935」、一方社油脂工業(株)製)をグラビアコーターで1g/m2塗工した後、打ち抜き機で5mm×6mmの長方形に打ち抜いて、細片を得た。
応力発光材料を含む塗工層として発光中心としてユウロピウムを添加したアルミン酸ストロンチウム(SrAl2O4 :Eu)の粉体をアクリル樹脂とともにトルエンに分散させて塗料を調製した。この塗料を実施例1の基紙の両面にグラビアコーターで片面当たり8g/m2塗工した。さらに基紙の両面に接着剤層として、ポリビニルアルコール(商品名「クラレポバール117」、クラレ(株)製)の5質量部%水溶液を、エアナイフコーターで片面当たり2g/m2塗工した。これを打ち抜き機で5mm×6mmの長方形に打ち抜き、細片を得た。
応力発光材料を含む塗工層として発光中心としてユウロピウムを添加したアルミン酸ストロンチウム(SrAl2O4 :Eu)の粉体をポリスチレン樹脂とともにトルエンに分散させて塗料を調製した。この塗料を実施例1の基紙の両面にグラビアコーターで片面当たり8g/m2塗工した。さらに基紙の両面に接着剤層として、ポリビニルアルコール(商品名「クラレポバール117」、クラレ(株)製)の5質量部%水溶液を、エアナイフコーターで片面当たり2g/m2塗工した。これを打ち抜き機で5mm×6mmの長方形に打ち抜き、細片を得た。
<紙料の調整>
NBKP20質量部、LBKP80質量部を350mlC.S.F.に叩解し、これに白土10質量部、紙力増強剤(商品名「ポリストロン117」、荒川化学工業(株)製)0.4質量部、サイズ剤(商品名「サイズパインE50」、荒川化学工業(株)製)1.0質量部、さらに硫酸バンドを2.0質量部加え、紙料を調製した。
長網抄紙機を使用して坪量110g/m2の基紙を抄造時に実施例1〜9の各細片を抄紙網上の紙層形成前の湿紙に対し、特開平7−145600記載の装置を使用して均一に振りかけた。細片の分散密度は用紙100cm2当たり30〜40個となるように装置を調整した。後は常法に従い乾燥を行い、偽造防止用紙を得た。得られた各偽造防止用紙の細片は、抄紙工程における熱やこすれ等により応力発光機能は失われることはなく、実施例1〜9の各細片と同様の発光性能が確認された。
実施例1および実施例7の細片を同量混合し、用紙100cm2当たり30〜40個となるように調整した以外は実施例12と同様にして偽造防止用紙を作成した。得られた偽造防止用紙は実施例12と同様に応力発光機能が認められた。特に、各細片に含まれる応力発光材料由来の色である緑色と青色の2色が発光時に確認された。
Claims (13)
- 基材の少なくとも一部に、応力発光機能を有する細片。
- 少なくとも1種の応力発光材料の微粒子およびバインダー高分子を含む、請求項1記載の細片。
- バインダー高分子がポリウレタン樹脂、ポリエステル樹脂、ポリカーボネート樹脂、ポリオレフィン系樹脂、エチレン・酢酸ビニル共重合樹脂、スチレン・ブタジエン共重合体樹脂、ポリ塩化ビニル樹脂、ポリ塩化ビニリデン樹脂、ナイロン系樹脂、ポリアミド樹脂、ポリビニルアルコール、フッ素系樹脂からなる群から選択される少なくとも1種である、請求項2記載の細片。
- 前記バインダー高分子がポリウレタン樹脂および/またはポリエステル樹脂である、請求項2または3記載の細片。
- 前記ポリウレタン樹脂がポリエステル系ポリウレタンである、請求項4記載の細片。
- 可逆的に発光することを特徴とする、請求項1乃至5のいずれかに記載の細片。
- 基材が紙、布、フィルム、金属であることを特徴とする、請求項1乃至6のいずれかに記載の細片。
- 基材が透明多層膜である、請求項1乃至7のいずれかに記載の細片。
- 少なくとも一部に真珠光沢を有する、請求項1乃至8のいずれかに記載の細片。
- 基材に紫外線吸収層を設けた、請求項1乃至9のいずれかに記載の細片。
- 2種類以上の波長で発光する、請求項1乃至10のいずれかに記載の細片。
- 請求項1乃至11のいずれか1項に記載の細片が用いられている偽造防止用紙。
- 発光の波長が異なる2種類以上の細片が用いられている、請求項12に記載の偽造防止用紙。