JP2014136405A - Light shading paper - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide light shading paper in which light shading properties, adhesive properties between a paper base material and a light shading layer and the concealment properties of the light shading paper are excellent.SOLUTION: Provided is light shading paper obtained by laminating at least two paper base materials via a light shading layer, in which the light shading paper is provided with: a black layer including a black pigment and a thermoplastic resin; a white layer including a white pigment and a thermoplastic resin; and a resin layer including a thermoplastic resin in this order. Particularly, it is preferable that the ratio between the white pigment and the thermoplastic resin in the white layer satisfies the white pigment: the thermoplastic resin=15:85 to 50:50 (pts.wt).

Description

本発明は、少なくとも２枚の紙基材が遮光層を介して積層された遮光紙に関する。 The present invention relates to a light shielding paper in which at least two paper base materials are laminated via a light shielding layer.

従来から様々な遮光紙が提案されている。例えば、アルミ箔に代表される金属膜を基材表面に貼合あるいは金属粉末を基材表面に塗工した遮光紙などが挙げられる。しかしながら、アルミ箔を貼合した遮光紙などはアルミ箔自体が高価な上、更に貼合するための工程が必要で経済性に問題があるとともに、古紙回収が困難なため焼却処分した際にアルミ箔の残渣が残る問題がある。
このため、二酸化チタン粉末のような屈折率の大きな白色顔料や光を吸収するカーボンブラックのような黒色顔料を紙基材の内部に添加、あるいは表面に塗工した遮光紙が開発されている。特許文献１には、白色顔料と黒色顔料を組み合わせた遮光紙、具体的にはカップ内面から、各色顔料ポリエチレンラミネート層／紙基材／白ポリエチレン層（白色顔料を含有したポリエチレン層）／白印刷層／墨印刷層／ポリエチレンラミネート層／紙基材の構成の遮光性紙が開示されている。 Conventionally, various light shielding papers have been proposed. Examples thereof include light-shielding paper in which a metal film typified by aluminum foil is bonded to the surface of the base material or metal powder is applied to the surface of the base material. However, light-shielding paper with aluminum foil is expensive because the aluminum foil itself is expensive, and there is a problem in terms of economy because it requires a process for further bonding, and it is difficult to collect used paper. There is a problem that the residue of the foil remains.
For this reason, a light-shielding paper has been developed in which a white pigment having a large refractive index such as titanium dioxide powder or a black pigment such as carbon black that absorbs light is added to the inside of the paper substrate or coated on the surface. In Patent Document 1, a light-shielding paper combining a white pigment and a black pigment, specifically, each color pigment polyethylene laminate layer / paper substrate / white polyethylene layer (polyethylene layer containing a white pigment) / white printing from the inner surface of the cup. A light-shielding paper having the structure of layer / black printing layer / polyethylene laminate layer / paper substrate is disclosed.

特開２０１２−２２９０４６JP2012-229046

引用文献１に記載されている遮光紙は、この遮光紙は、十分な遮光性を有している。また、アイスクリーム、ヨーグルト等の容器に使用した場合、アイスクリームやヨーグルトなどに含まれる水分や脂肪分が、遮光紙を構成している紙基材の端部から浸透するため、紙基材が透明化するが、白ポリエチレン層／白印刷層の存在により、黒印刷層が透けて見えることも防止されている。   The light shielding paper described in the cited document 1 has sufficient light shielding properties. In addition, when used in containers such as ice cream and yogurt, the water and fat contained in the ice cream and yogurt permeate from the edge of the paper substrate that constitutes the shading paper. Although it is transparent, the presence of the white polyethylene layer / white printing layer prevents the black printing layer from being seen through.

しかしながら、引用文献１の遮光紙は、白ポリエチレン層と白印刷層の両方を必要としているため、工程が複雑になるといった問題が発生する。この問題に対しては、白色顔料を高配合した白ポリエチレンを用いることで白印刷層を省くことが可能であるが、白色顔料が高配合の白ポリエチレンはその流動性が大きく低下するため、押し出しラミネート法によって白ポリエチレン層を積層させる際に、ストリークの発生といった問題が発生する。さらに、白ポリエチレン層の紙基材への投錨性が悪化するため、白色ポリエチレン層と紙基材との界面で剥離するといった問題が発生する。   However, since the light shielding paper of the cited document 1 requires both a white polyethylene layer and a white print layer, there arises a problem that the process becomes complicated. To solve this problem, it is possible to omit the white printing layer by using white polyethylene with a high white pigment content. When the white polyethylene layer is laminated by the laminating method, a problem such as generation of streaks occurs. Furthermore, since the anchoring property of the white polyethylene layer to the paper base material is deteriorated, there arises a problem that peeling occurs at the interface between the white polyethylene layer and the paper base material.

そこで、本発明は、遮光性、紙基材と遮光層との接着性、遮光層の隠蔽性に優れた遮光紙を提供することを目的とする。   Therefore, an object of the present invention is to provide a light shielding paper excellent in light shielding properties, adhesiveness between a paper base material and a light shielding layer, and concealing properties of the light shielding layer.

本発明は以下の[１]〜[１０]を提供する。
[１] 少なくとも２枚の紙基材が遮光層を介して積層された遮光紙において、該遮光層が、黒色顔料と熱可塑性樹脂とを含有した黒色層、白色顔料と熱可塑性樹脂とを含有した白色層、熱可塑性樹脂を含有する樹脂層をこの順に設けていることを特徴とする遮光紙。
[２] 前記白色層の白色顔料と熱可塑性樹脂との比率が、白色顔料：熱可塑性樹脂＝１５：８５〜５０：５０（重量部）であることを特徴とす[１]に記載の遮光紙。
[３] 前記白色顔料が酸化チタンであることを特徴とする[１]〜[２]に記載の遮光紙。
[４] 前記白色顔料層が１０〜４０μmであることを特徴とする[１]〜[３]に記載
[５] 前記黒色層の黒色顔料と熱可塑性樹脂との比率が黒色顔料：熱可塑性樹脂＝０．５：９９．５〜１５：８５（重量部）であることを特徴とする[１]〜[４]に記載の遮光紙。
[６] 前記黒色顔料がカーボンブラックであることを特徴とする[１]〜[５]に記載の遮光紙。
[７] 前記黒色顔料層が５〜２５μmであることを特徴とする[１]〜[６]に記載の遮光紙。
[８] 前記熱可塑性樹脂がポリエチレン樹脂、ポリプロピレン樹脂、ポリメチルペンテン樹脂の少なくとも１種であることを特徴とする[１]〜[７]に記載の遮光紙。
[９] 前記遮光層が、溶融押し出しラミネート法によって、黒色層、白色層、樹脂層が積層されていることを特徴とする[１]〜[８]に記載の遮光紙。
[１０] [１]〜[９]に記載の遮光紙を用いることを特徴とする遮光性紙カップ。 The present invention provides the following [1] to [10].
[1] In a light shielding paper in which at least two paper base materials are laminated via a light shielding layer, the light shielding layer contains a black layer containing a black pigment and a thermoplastic resin, a white pigment and a thermoplastic resin. A light-shielding paper, wherein a white layer and a resin layer containing a thermoplastic resin are provided in this order.
[2] The light shielding material according to [1], wherein the ratio of the white pigment to the thermoplastic resin in the white layer is white pigment: thermoplastic resin = 15: 85 to 50:50 (parts by weight). paper.
[3] The light-shielding paper according to any one of [1] to [2], wherein the white pigment is titanium oxide.
[4] The [1] to [3], wherein the white pigment layer is 10 to 40 μm.
[5] The ratio of the black pigment and the thermoplastic resin in the black layer is black pigment: thermoplastic resin = 0.5: 99.5-15: 85 (parts by weight) [1]- The light-shielding paper according to [4].
[6] The light-shielding paper according to any one of [1] to [5], wherein the black pigment is carbon black.
[7] The light-shielding paper according to [1] to [6], wherein the black pigment layer is 5 to 25 μm.
[8] The light-shielding paper according to [1] to [7], wherein the thermoplastic resin is at least one of polyethylene resin, polypropylene resin, and polymethylpentene resin.
[9] The light-shielding paper according to any one of [1] to [8], wherein the light-shielding layer is formed by laminating a black layer, a white layer, and a resin layer by a melt extrusion lamination method.
[10] A light-shielding paper cup using the light-shielding paper according to any one of [1] to [9].

本発明によれば、、本発明は、遮光性、紙基材と遮光層（樹脂層）との接着性、遮光層の隠蔽性に優れた遮光紙を提供することができる。   ADVANTAGE OF THE INVENTION According to this invention, this invention can provide the light shielding paper excellent in light-shielding property, the adhesiveness of a paper base material and a light shielding layer (resin layer), and the concealment property of a light shielding layer.

以下、本発明の実施の形態について詳細に説明する。   Hereinafter, embodiments of the present invention will be described in detail.

本発明は、なくとも２枚の紙基材が遮光層を介して積層された遮光紙において、該遮光層が、黒色顔料と熱可塑性樹脂とを含有した黒色層、白色顔料と熱可塑性樹脂とを含有した白色層、熱可塑性樹脂を含有する樹脂層をこの順に設けていることを特徴とする遮光紙に関するもので、食品用途などに用いられる容器などの包装材料基材として好適に使用することができる。   The present invention provides a light-shielding paper in which at least two paper substrates are laminated via a light-shielding layer, wherein the light-shielding layer comprises a black layer containing a black pigment and a thermoplastic resin, a white pigment and a thermoplastic resin. It is related to light-shielding paper characterized by providing a white layer containing selenium and a resin layer containing a thermoplastic resin in this order, and should be suitably used as a packaging material substrate for containers used for food applications, etc. Can do.

（黒色層）
本発明の遮光層を構成する黒色層は黒色顔料と熱可塑性樹脂を必須成分とする。黒色顔料としては、カーボンブラック、油煙、植物黒、骨炭、黒鉛、酸化物系黒色顔料などを例示することができ、遮光性の点からカーボンブラックを用いることがより好ましい。また、熱可塑性樹脂としては、ポリエチレン樹脂、ポリプロピレン樹脂、ポリメチルペンテン樹脂、ポリエチレンテレフタレート樹脂、ポリビニルアルコール樹脂、エチレン酢酸ビニル樹脂などを例示することができ、これらの中では、上記顔料との相溶性、価格の点からポリエチレン樹脂、ポリプロピレン樹脂、ポリメチルペンテン樹脂を用いることが好ましい。 (Black layer)
The black layer constituting the light shielding layer of the present invention comprises black pigment and thermoplastic resin as essential components. Examples of the black pigment include carbon black, oil smoke, plant black, bone charcoal, graphite, and oxide black pigment, and it is more preferable to use carbon black from the viewpoint of light shielding properties. Examples of the thermoplastic resin include polyethylene resin, polypropylene resin, polymethylpentene resin, polyethylene terephthalate resin, polyvinyl alcohol resin, ethylene vinyl acetate resin, etc. Among these, compatibility with the above pigments From the viewpoint of cost, it is preferable to use polyethylene resin, polypropylene resin, or polymethylpentene resin.

黒色層中の黒色顔料と熱可塑性樹脂との比率は、黒色顔料：熱可塑性樹脂＝０．５：９９．５〜１５：８５（重量部）であることが好ましい。黒色顔料の配合量が少ないと十分な遮光性が得られない。一方、黒色顔料の配合量が多いと流動性が大きく低下するため、押し出しラミネート法によって黒色層を積層させる際に、ストリークの発生といった問題が発生する。さらに、黒色層の紙基材への投錨性（アンカー効果）が悪化するため、黒色層と紙基材との界面で剥離するといった問題が発生する。   The ratio of the black pigment to the thermoplastic resin in the black layer is preferably black pigment: thermoplastic resin = 0.5: 99.5 to 15:85 (parts by weight). If the amount of the black pigment is small, sufficient light shielding properties cannot be obtained. On the other hand, when the amount of the black pigment is large, the fluidity is greatly reduced, and thus a problem such as the occurrence of streak occurs when the black layer is laminated by the extrusion laminating method. Further, since the anchoring property (anchor effect) of the black layer to the paper base material is deteriorated, there arises a problem that peeling occurs at the interface between the black layer and the paper base material.

また、黒色層の厚さは、十分な遮光性を発現すれば特に限定されるものではないが、通常、を５〜２５μm程度であることが好ましい。   Further, the thickness of the black layer is not particularly limited as long as sufficient light-shielding properties are exhibited, but it is usually preferable that the thickness is about 5 to 25 μm.

（白色層）
本発明の遮光層を構成する白色層は白色顔料と熱可塑性樹脂を必須成分とする。白色顔料としては、カオリン、炭酸カルシウム、二酸化チタン、水酸化アルミニウムなどを例示することができるが、黒色層の可視光における外観不良の防止（隠蔽性）の点から、二酸化チタンを用いることが好ましい。また、熱可塑性樹脂としては、ポリエチレン樹脂、ポリプロピレン樹脂、ポリメチルペンテン樹脂、ポリエチレンテレフタレート樹脂、ポリビニルアルコール樹脂、エチレン酢酸ビニル樹脂などを例示することができ、これらの中では、上記顔料との相溶性、価格の点からポリエチレン樹脂、ポリプロピレン樹脂、ポリメチルペンテン樹脂を用いることが好ましい。 (White layer)
The white layer constituting the light shielding layer of the present invention contains a white pigment and a thermoplastic resin as essential components. Examples of white pigments include kaolin, calcium carbonate, titanium dioxide, and aluminum hydroxide, but it is preferable to use titanium dioxide from the viewpoint of preventing the appearance of the black layer from being poor (visible) in visible light. . Examples of the thermoplastic resin include polyethylene resin, polypropylene resin, polymethylpentene resin, polyethylene terephthalate resin, polyvinyl alcohol resin, ethylene vinyl acetate resin, etc. Among these, compatibility with the above pigments From the viewpoint of cost, it is preferable to use polyethylene resin, polypropylene resin, or polymethylpentene resin.

白色層中の白色顔料と熱可塑性樹脂との比率は、白色顔料：熱可塑性樹脂＝１５：８５〜５０：５０（重量部）であることが好ましく、より好ましくは白色顔料：熱可塑性樹脂＝２５：７５〜３５：６５（重量部）である。白色顔料の配合量が少ないと十分な隠蔽性が得られない。一方、白色顔料の配合量が多いと、白色顔料層と隣接する熱可塑性樹脂層の接着性が大幅に低下する問題を有する。なお、一般的な白ポリエチレンに含有されている白色顔料の配合量は、多きものでも、白色顔料：ポリエチレン＝１０：９０程度である。   The ratio of the white pigment to the thermoplastic resin in the white layer is preferably white pigment: thermoplastic resin = 15: 85 to 50:50 (parts by weight), more preferably white pigment: thermoplastic resin = 25. : 75 to 35: 65 (parts by weight). If the amount of the white pigment is small, sufficient concealing property cannot be obtained. On the other hand, when the amount of the white pigment is large, there is a problem that the adhesiveness of the thermoplastic resin layer adjacent to the white pigment layer is significantly lowered. In addition, even if there are many compounding quantities of the white pigment contained in general white polyethylene, it is about white pigment: polyethylene = 10: 90.

また、白色層の厚さは、十分な隠蔽性を発現すれば特に限定されるものではないが、通常、を１０〜４０μm程度であることが好ましい。   Further, the thickness of the white layer is not particularly limited as long as sufficient concealment is exhibited, but it is usually preferable that the thickness is about 10 to 40 μm.

（樹脂層）
本発明の遮光層を構成する樹脂層に用いられる熱可塑性樹脂としては、ポリエチレン樹脂、ポリプロピレン樹脂、ポリメチルペンテン樹脂、ポリエチレンテレフタレート樹脂、ポリビニルアルコール樹脂、エチレン酢酸ビニル樹脂などを例示することができるが、紙基材との接着性の点や安価汎用から、ポリエチレン樹脂、ポリプロピレン樹脂、ポリメチルペンテン樹脂、ポリビニルアルコール樹脂、エチレン酢酸ビニル樹脂であることがこの好ましく、さらに好ましくは、ポリビニルアルコール樹脂、エチレン酢酸ビニル樹脂である。 (Resin layer)
Examples of the thermoplastic resin used in the resin layer constituting the light shielding layer of the present invention include polyethylene resin, polypropylene resin, polymethylpentene resin, polyethylene terephthalate resin, polyvinyl alcohol resin, and ethylene vinyl acetate resin. From the viewpoint of adhesiveness with a paper base material and inexpensive general purpose, it is preferably a polyethylene resin, polypropylene resin, polymethylpentene resin, polyvinyl alcohol resin, ethylene vinyl acetate resin, more preferably polyvinyl alcohol resin, ethylene. Vinyl acetate resin.

本発明において、樹脂層は、白色層と紙基材との間に積層することに加えて、黒色層と紙基材の接着性を目的に、黒色層と紙基材との間に積層することができる。   In the present invention, the resin layer is laminated between the black layer and the paper substrate for the purpose of adhesion between the black layer and the paper substrate, in addition to being laminated between the white layer and the paper substrate. be able to.

本発明において、遮光層を構成する黒色層、白色層、樹脂層に使用する熱可塑性樹脂は同一あるいは類似の熱可塑性樹脂を使用することが好ましい。   In the present invention, it is preferable to use the same or similar thermoplastic resin as the thermoplastic resin used for the black layer, the white layer and the resin layer constituting the light shielding layer.

（紙基材）
本発明において、非塗工紙、塗工紙などを紙基材として使用することができ、特に限定されるものではない。 (Paper substrate)
In the present invention, non-coated paper, coated paper, and the like can be used as a paper substrate, and are not particularly limited.

非塗工紙としては、原料パルプとして針葉樹晒クラフトパルプ（ＮＢＫＰ）、広葉樹晒クラフトパルプ（ＬＢＫＰ）、針葉樹晒サルファイトパルプ（ＮＢＳＰ）、などの木材パルプを主体とし、これに必要に応じて、麻、竹、ワラ、ケナフ等の非木材パルプを併用することができる。これらの原料パルプに必要に応じてクレー、カオリン、タルク、二酸化チタン、炭酸カルシウム、水酸化アルミニウム粉末等の内添用填料を加え、さらにロジンサイズ剤等のサイズ剤、ポリアクリルアミド等の乾燥紙力増強剤、ポリアミド・ポリアミン・エピクロルヒドリンやメラミン樹脂等の湿潤紙力増強剤、硫酸バンド等の定着剤等の製紙用副資材を適宜添加して紙料を調製し、円網抄紙機、長網抄紙機、ツインワイヤー抄紙機等の抄紙機を使用して常法に従い非塗工紙を得ることができる。   As non-coated paper, wood pulp such as softwood bleached kraft pulp (NBKP), hardwood bleached kraft pulp (LBKP), softwood bleached sulfite pulp (NBSP) as a raw material pulp, mainly as needed, Non-wood pulp such as hemp, bamboo, straw and kenaf can be used in combination. Add internal fillers such as clay, kaolin, talc, titanium dioxide, calcium carbonate, aluminum hydroxide powder to these raw pulps as needed, and further sizing agents such as rosin sizing agent, dry paper strength such as polyacrylamide Paper stock is prepared by appropriately adding paper making auxiliary materials such as reinforcing agents, wet paper strength enhancers such as polyamide, polyamine, epichlorohydrin and melamine resin, and fixing agents such as sulfuric acid bands. A non-coated paper can be obtained according to a conventional method using a paper machine such as a machine or a twin wire paper machine.

また、非塗工紙の紙面強度を向上させるために、サイズプレス装置等によって、スチレン系樹脂、スチレン・アクリル系樹脂、スチレン・マレイン酸樹脂、アルキルケテンダイマー、澱粉、酸化澱粉、ヒドロキシエチル化澱粉、カルボキシメチル化セルロース、カルボキシメチル化グアーガム、リン酸化グアーガム、酸化グアーガム、ポリビニルアルコール、ポリアクリルアミド等の薬品を表面に塗工することが可能である。   In addition, in order to improve the paper surface strength of non-coated paper, a styrene resin, styrene / acrylic resin, styrene / maleic resin, alkyl ketene dimer, starch, oxidized starch, hydroxyethylated starch, etc., using a size press device, etc. It is possible to apply chemicals such as carboxymethylated cellulose, carboxymethylated guar gum, phosphorylated guar gum, oxidized guar gum, polyvinyl alcohol, and polyacrylamide to the surface.

塗工紙としては、カオリン、炭酸カルシウム、二酸化チタン、水酸化アルミニウムなどの顔料とスチレン・ブタジエンラテックス、メチルメタクリレート・ブタジエンラテックス、澱粉、ポリビニルアルコール等の周知の接着剤に分散剤、耐水化剤、防腐剤、防かび剤、等の塗工用の副資材を適宜併用して塗工液を調製し、エアナイフコーター、ブレードコーター、ロールコーター等の周知のコーターを使用して前記非塗工紙の表面に塗工することで得ることができる。   As coated paper, pigments such as kaolin, calcium carbonate, titanium dioxide, aluminum hydroxide, and well-known adhesives such as styrene / butadiene latex, methyl methacrylate / butadiene latex, starch, polyvinyl alcohol, dispersants, water resistance agents, Prepare coating liquid by appropriately using auxiliary materials for coating such as preservatives, fungicides, etc., and use a known coater such as an air knife coater, blade coater, roll coater, etc. It can be obtained by coating on the surface.

なお、本発明の遮光紙を食品用の容器に使用するに当たっては、紙基材にステキヒトサイズ度（ＪＩＳ Ｐ８１２２ ２００４）１秒以上、コッブ吸水（ＪＩＳ Ｐ８１４０ １９９８）５０ｇ／ｍ^２以下の耐水性や耐酸性を付与することが好ましい。耐水性、耐酸性を付与する方法は特に限定されるのではないが、紙製品のサイズに広く利用されているアルキルケテンダイマーとポリアミドエピクロロヒドリン系湿潤紙力剤を用いた既知の方法や、ロジンサイズ、アルケニル無水コハク酸（ＡＳＡ）を用いた方法によることができる。 In addition, when using the light-shielding paper of the present invention for a container for food, the paper substrate has a water resistance of not less than 1 second and a water absorption of Cobb water absorption (JIS P8140 1998) of 50 g / m ² or less. It is preferable to impart acid resistance. The method for imparting water resistance and acid resistance is not particularly limited, but a known method using an alkyl ketene dimer and a polyamide epichlorohydrin-based wet paper strength agent widely used for the size of paper products, Rosin size, alkenyl succinic anhydride (ASA).

なお、アルキルケテンダイマーとポリアミドエピクロロヒドリン系湿潤紙力剤を併用する場合、ポリアミドエピクロロヒドリン系湿潤紙力剤の配合量は、対絶乾パルプ重量に対して０．０５〜０．５重量％、より好ましくは対絶乾パルプ０．１〜０．４重量％とすることが望ましい。配合量が対絶乾パルプ重量に対して０．０５重量％より低いと十分な紙力、内部結合強さ、耐酸性が得られず、対絶乾パルプ重量に対して０．５重量％より高いと過剰添加となりコストアップとなる。湿潤紙力剤は、湿潤強度を上げて紙基材断面部への液体の浸透を防止するだけでなく、アルキルケテンダイマーのパルプへの定着を向上させる効果もある。   When the alkyl ketene dimer and the polyamide epichlorohydrin wet paper strength agent are used in combination, the blending amount of the polyamide epichlorohydrin wet paper strength agent is 0.05 to 0. 0 with respect to the dry pulp weight. It is desirable that the content be 5% by weight, more preferably 0.1 to 0.4% by weight against dry pulp. When the blending amount is lower than 0.05% by weight with respect to the dry pulp weight, sufficient paper strength, internal bond strength and acid resistance cannot be obtained, and from 0.5% by weight with respect to the dry pulp weight. If it is high, excessive addition will result in an increase in cost. The wet paper strength agent not only increases the wet strength and prevents the penetration of liquid into the cross section of the paper base material, but also has an effect of improving the fixation of the alkyl ketene dimer to the pulp.

また、アルキルケテンダイマーのサイズ度を発現するのに必要なｐＨ、アルカリ度を調整するために、炭酸カルシウムもしくは炭酸水素ナトリウム（重曹）を添加することが出来る。配合する炭酸カルシウムもしくは炭酸水素ナトリウムは対絶乾パルプ０．５〜２．０重量％の範囲、より好ましくは対絶乾パルプ０．８〜１．２重量％とすることが望ましい。対絶乾パルプ０．５重量％未満であると十分なサイズ効果は得られずかつ耐酸性も悪く、対絶乾パルプ２．０重量％より高いと高ｐＨによる黄変を招く懸念がある。   Moreover, in order to adjust pH and alkalinity required to express the sizing degree of the alkyl ketene dimer, calcium carbonate or sodium hydrogen carbonate (bicarbonate) can be added. It is desirable that the calcium carbonate or sodium hydrogen carbonate to be blended is in the range of 0.5 to 2.0% by weight of the dried pulp and more preferably 0.8 to 1.2% by weight of the dried pulp. When the amount is less than 0.5% by weight, the sufficient size effect cannot be obtained and the acid resistance is poor, and when the amount is more than 2.0% by weight, there is a concern of causing yellowing due to high pH.

内添サイズ剤としてロジンサイズを用いた場合、水溶液のｐＨが低い条件下ではサイズ性が低下するため、酸性水溶液に対してはサイズ効果が小さくなる。一方、アルキルケテンダイマー（AKD)は水溶液のｐＨが低い条件下でも十分な撥水性を示すため、酸性水溶液に対しても高度なサイズ性が期待できるため好ましいが、多量に配合した場合に原紙抄造時、プレスロール等のロールが汚れたり、サイズリバージョンと呼ばれる経時でサイズ性が低下していく現象が生じたりすることがある。また、アルケニル無水コハク酸（ASA）を用いた場合は、乳化安定性が低いために、多量に用いた場合はパルプ繊維に定着しなかったアルケニル無水コハク酸が分解を起こしてAKD同様に抄造マシンの汚れを引き起こすことがある。   When the rosin size is used as the internal sizing agent, the size effect is reduced under conditions where the pH of the aqueous solution is low. On the other hand, alkyl ketene dimer (AKD) is preferable because it exhibits sufficient water repellency even under conditions where the pH of the aqueous solution is low. Sometimes, a roll such as a press roll becomes dirty, or a phenomenon called size reversion in which the size property deteriorates with time may occur. Also, when alkenyl succinic anhydride (ASA) is used, the stability of emulsion is low. May cause dirt.

本発明において、紙基材の坪量は特に限定されるものではないが、３０〜３５０ｇ／ｍ^２であることが好ましい。また、遮光層を介して積層される２枚の紙基材の坪量は所望の遮光紙の坪量に応じて適宜選択できる。 In this invention, although the basic weight of a paper base material is not specifically limited, It is preferable that it is 30-350 g / m < ² >. Moreover, the basis weight of the two paper base materials laminated via the light shielding layer can be appropriately selected according to the basis weight of the desired light shielding paper.

本発明において、遮光紙の坪量が１００〜４５０ｇ／ｍ２であることが好ましい。   In this invention, it is preferable that the basic weight of light-shielding paper is 100-450 g / m <2>.

（遮光紙の製造）
本発明の遮光紙の製造方法は特に限定されるものではないが、遮光性および接着性、更には工程容易性の点から、溶融押出しラミネーターを使用して、紙基材と遮光層をサンドラミ方式で積層することが好ましい。 (Manufacture of shading paper)
The method for producing the light-shielding paper of the present invention is not particularly limited, but from the viewpoint of light-shielding properties and adhesiveness, and further process easiness, a melt-extruded laminator is used, and the paper base material and the light-shielding layer are sand laminated. Is preferably laminated.

具体的には、３層以上の層を同時に積層できる溶融押出ラミネーターを用いて、黒色層（黒色顔料、熱可塑性樹脂）、白色層（白色顔料、熱可塑性樹脂）、樹脂層（熱可塑性樹脂）を共押し出しされた遮光層と２枚の紙基材とを接着一体化させることで、白色顔料を高配合した白色層を押し出しラミネート法によって積層する場合でも、白色層に隣接する黒色層および／もしくは樹脂層によってストリークの発生といった問題が解決し、さらには隣接する黒色層および／もしくは樹脂層との接着性が大幅に低下するといった問題も同時に解決するため、良好な遮光紙を製造することができる。   Specifically, using a melt extrusion laminator that can laminate three or more layers simultaneously, a black layer (black pigment, thermoplastic resin), a white layer (white pigment, thermoplastic resin), a resin layer (thermoplastic resin) By adhering and integrating the light-shielding layer coextruded with two paper base materials, even when a white layer highly blended with a white pigment is laminated by the extrusion laminating method, the black layer adjacent to the white layer and / or Alternatively, the problem of streak generation is solved by the resin layer, and further, the problem that the adhesiveness to the adjacent black layer and / or resin layer is greatly reduced is solved at the same time. it can.

[実施例１]
押出ラミネーター機が３層の共押出機を用いて、第１層目にカーボンブラック８重量部、とポリエチレン樹脂９２重量部を混合した黒色層を９μｍ、第２層目にチタン３０重量部とポリエチレン樹脂７０重量部を混合した白色層を２５μｍ、第３層目にポリエチレン樹脂を２μｍとなるように調整して溶融押出して、２枚の紙基材のうち、紙基材Ａ（片面コート紙、日本製紙製、坪量１０４．７ｇ／ｍ^２）が第１層目に、紙基材Ｂ（上質紙、日本製紙製、坪量６４．０ｇ／ｍ^２、ステキヒトサイズ度：１４秒）が第３層目になるように接着一体化させ、遮光紙を得た。 [Example 1]
The extrusion laminator machine uses a three-layer co-extrusion machine. The first layer is 9 μm in black layer mixed with 8 parts by weight of carbon black and 92 parts by weight of polyethylene resin, and the second layer is 30 parts by weight of titanium and polyethylene. A white layer mixed with 70 parts by weight of resin was adjusted to 25 μm, and a polyethylene resin was adjusted to 2 μm in the third layer, melt extruded, and paper base A (single side coated paper, Nippon Paper Industries, basis weight 104.7 g / m ² ) is the first layer, and paper base B (fine paper, Nippon Paper Industries, basis weight 64.0 g / m ² , Steecht sizing degree: 14 seconds) Adhering and integrating so as to form the third layer, a light shielding paper was obtained.

[実施例２]
チタン１５重量部とポリエチレン樹脂８５重量部を混合した白色層を２５μｍとした以外は実施例１と同様にして遮光紙を得た。 [Example 2]
A light-shielding paper was obtained in the same manner as in Example 1 except that the white layer obtained by mixing 15 parts by weight of titanium and 85 parts by weight of polyethylene resin was changed to 25 μm.

[実施例３]
チタン１５重量部とポリエチレン樹脂８５重量部を混合した白色層を４０μｍとした以外は実施例１と同様にして遮光紙を得た。 [Example 3]
A light-shielding paper was obtained in the same manner as in Example 1 except that the white layer obtained by mixing 15 parts by weight of titanium and 85 parts by weight of polyethylene resin was changed to 40 μm.

[実施例４]
チタン５０重量部とポリエチレン樹脂５０重量部を混合した白色層を１０μｍとした以外は実施例１と同様にして遮光紙を得た。 [Example 4]
A light-shielding paper was obtained in the same manner as in Example 1 except that the white layer obtained by mixing 50 parts by weight of titanium and 50 parts by weight of polyethylene resin was changed to 10 μm.

[実施例５]
カーボンブラッ０．５重量部とポリエチレン樹脂９９．５重量部を混合した黒色層を２５μｍした以外は実施例１と同様にして遮光紙を得た。 [Example 5]
A light-shielding paper was obtained in the same manner as in Example 1 except that a black layer mixed with 0.5 parts by weight of carbon black and 99.5 parts by weight of polyethylene resin was changed to 25 μm.

[実施例６]
カーボンブラック１５重量部とポリエチレン樹脂８５重量部を混合した黒色層を５μｍした以外は実施例１と同様にして遮光紙を得た。 [Example 6]
A light-shielding paper was obtained in the same manner as in Example 1 except that 5 μm of a black layer obtained by mixing 15 parts by weight of carbon black and 85 parts by weight of polyethylene resin was used.

[比較例1]
第３層目のポリエチレン樹脂を除いた以外は実施例１と同様にして遮光紙を得た。 [Comparative Example 1]
A light-shielding paper was obtained in the same manner as in Example 1 except that the third layer of the polyethylene resin was omitted.

[比較例２]
チタン１２重量部とポリエチレン樹脂８８重量部を混合した白色層を２５μｍとした以外は比較例１と同様にして遮光紙を得た。 [Comparative Example 2]
A light-shielding paper was obtained in the same manner as in Comparative Example 1 except that the white layer obtained by mixing 12 parts by weight of titanium and 88 parts by weight of polyethylene resin was changed to 25 μm.

＜評価基準＞
（紙基材Ｂとの接着性）
得られた遮光紙の紙基材Ｂと隣接する遮光層（白色層あるいは樹脂層）との界面を剥離したときの剥離状態を下記の基準で評価した。
○：紙基材Ｂの層間が破壊されている。
×：紙基材Ｂと隣接する遮光層の界面で剥離している。 <Evaluation criteria>
(Adhesiveness with paper base B)
The peeled state when the interface between the paper base B of the obtained light shielding paper and the adjacent light shielding layer (white layer or resin layer) was peeled was evaluated according to the following criteria.
○: The interlayer of the paper base material B is broken.
X: Peeling at the interface between the paper base B and the adjacent light shielding layer.

（黒色層の隠蔽性）
得られた遮光紙の紙基材Ｂの面のＩＳＯ白色度（ＪＩＳ Ｐ８１４８）を測定し、下記の基準で評価した。
○：７２％以上
×：７２％未満 (Black layer concealment)
The ISO whiteness (JIS P8148) of the surface of the paper base B of the obtained light-shielding paper was measured and evaluated according to the following criteria.
○: 72% or more ×: less than 72%

（遮光性）
島津製作所製 自記分光光度計 UV−３１００PVを用いて、波長８００ｎｍにおける透過率を測定し、下記の基準で評価した。
○：０．６％未満
×：０．６％以上 (Light shielding)
Using a self-recording spectrophotometer UV-3100PV manufactured by Shimadzu Corporation, the transmittance at a wavelength of 800 nm was measured and evaluated according to the following criteria.
○: Less than 0.6% ×: 0.6% or more

Claims (10)

少なくとも２枚の紙基材が遮光層を介して積層された遮光紙において、該遮光層が、黒色顔料と熱可塑性樹脂とを含有した黒色層、白色顔料と熱可塑性樹脂とを含有した白色層、熱可塑性樹脂を含有する樹脂層をこの順に設けていることを特徴とする遮光紙。 In a light shielding paper in which at least two paper base materials are laminated via a light shielding layer, the light shielding layer includes a black layer containing a black pigment and a thermoplastic resin, and a white layer containing a white pigment and a thermoplastic resin. A light-shielding paper, wherein a resin layer containing a thermoplastic resin is provided in this order. 前記白色層の白色顔料と熱可塑性樹脂との比率が、白色顔料：熱可塑性樹脂＝１５：８５〜５０：５０（重量部）であることを特徴とする請求項１に記載の遮光紙。 2. The light-shielding paper according to claim 1, wherein a ratio of the white pigment to the thermoplastic resin in the white layer is white pigment: thermoplastic resin = 15: 85 to 50:50 (parts by weight). 前記白色顔料が酸化チタンであることを特徴とする請求項１〜２に記載の遮光紙。 The light-shielding paper according to claim 1, wherein the white pigment is titanium oxide. 前記白色顔料層が１０〜４０μmであることを特徴とする請求項１〜３に記載 The said white pigment layer is 10-40 micrometers, The Claims 1-3 characterized by the above-mentioned. 前記黒色層の黒色顔料と熱可塑性樹脂との比率が黒色顔料：熱可塑性樹脂＝０．５：９９．５〜１５：８５（重量部）であることを特徴とする請求項１〜４に記載の遮光紙。 The ratio between the black pigment and the thermoplastic resin in the black layer is black pigment: thermoplastic resin = 0.5: 99.5 to 15:85 (parts by weight). Shading paper. 前記黒色顔料がカーボンブラックであることを特徴とする請求項１〜５に記載の遮光紙。 The light-shielding paper according to claim 1, wherein the black pigment is carbon black. 前記黒色顔料層が５〜２５μmであることを特徴とする請求項１〜６に記載の遮光紙。 The light-shielding paper according to claim 1, wherein the black pigment layer is 5 to 25 μm. 前記熱可塑性樹脂がポリエチレン樹脂、ポリプロピレン樹脂、ポリメチルペンテン樹脂の少なくとも１種であることを特徴とする請求項１〜７に記載の遮光紙。 The light shielding paper according to claim 1, wherein the thermoplastic resin is at least one of a polyethylene resin, a polypropylene resin, and a polymethylpentene resin. 前記遮光層が、溶融押し出しラミネート法によって、黒色層、白色層、樹脂層が積層されていることを特徴とする請求項１〜８に記載の遮光紙。 The light shielding paper according to claim 1, wherein the light shielding layer is formed by laminating a black layer, a white layer, and a resin layer by a melt extrusion laminating method. 請求項１〜９に記載の遮光紙を用いることを特徴とする遮光性紙カップ。 A light-shielding paper cup using the light-shielding paper according to claim 1.