JP2014009387A - 母材靭性およびhaz靱性に優れた高張力鋼板 - Google Patents
母材靭性およびhaz靱性に優れた高張力鋼板 Download PDFInfo
- Publication number
- JP2014009387A JP2014009387A JP2012147891A JP2012147891A JP2014009387A JP 2014009387 A JP2014009387 A JP 2014009387A JP 2012147891 A JP2012147891 A JP 2012147891A JP 2012147891 A JP2012147891 A JP 2012147891A JP 2014009387 A JP2014009387 A JP 2014009387A
- Authority
- JP
- Japan
- Prior art keywords
- less
- toughness
- steel
- amount
- steel plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】本発明の高張力鋼板は、所定の鋼中成分を満足し、下記式で表わされるCeq(IIW)が0.40以上、0.45以下の範囲を満足し、鋼中に最大径2μm以下の酸化物が200個/mm2以上存在し、組織は、マルテンサイト組織を29体積%以上含有し、残部がベイナイト組織で構成されている。
Ceq(IIW)=[C]+{1/6×[Mn]}+{1/5×([Cr]+[Mo]+[V])}+{1/15×([Cu]+[Ni])}
式中、[ ]は、鋼中元素の含有量を意味する。
【選択図】なし
Description
Ceq(IIW)=[C]+{1/6×[Mn]}+{1/5×([Cr]+[Mo]+[V])}+{1/15×([Cu]+[Ni])}
式中、[ ]は、鋼中元素の含有量を意味する。
Cは、母材(鋼板)の強度および硬さを確保するために必要不可欠な元素である。このような作用を有効に発揮させるため、C量の下限を0.10%以上とする。C量の好ましい下限は0.12%以上である。但し、C量が過剰になるとHAZ靭性が劣化するため、C量の上限を0.16%以下とする。C量の好ましい上限は0.15%以下である。
Siは脱酸作用を有すると共に、母材の強度向上に有効な元素である。このような作用を有効に発揮させるため、Si量の下限を0.2%以上とする。Si量の好ましい下限は0.3%以上である。しかし、Si量が過剰になると溶接性が劣化するため、Si量の上限を0.5%以下とする。Si量の好ましい上限は0.40%以下である。
Mnは、母材の強度向上に有効な元素であり、このような作用を有効に発揮させるため、Mn量の下限を1%以上とする。Mn量の好ましい下限は1.10%以上である。しかし、Mn量が過剰になると溶接性が劣化するため、Mn量の上限を1.4%以下とする。Mn量の好ましい上限は1.3%以下である。
Pは、鋼材中に不可避的に含まれる元素であり、P量が0.03%を超えると母材靭性が劣化するため、P量の上限を0.03%とする。P量は出来るだけ少ない方が良く、P量の好ましい上限は0.020%以下である。
Sは、鋼材中に不可避的に含まれる元素であり、S量が多すぎるとMnSを多量に生成し,母材靭性が劣化するため、S量の上限を0.01%以下とする。S量は出来るだけ少ない方が良く、S量の好ましい上限は0.004%以下である。
Alは脱酸に用いられる元素であり、このような作用を有効に発揮させるため、Al量の好ましい下限を0.010%以上とする。しかし、Al量が0.08%を超えると,鋼板における清浄性が阻害されるため、Al量の上限を0.08%以下とする。Al量の好ましい上限は0.065%以下である。
Crは、母材の強度向上に有効な元素であり、このような作用を有効に発揮させるため、Cr量の下限を0.03%以上とする。Cr量の好ましい下限は0.05%以上である。一方、Cr量が0.25%を超えると溶接性が劣化するため、Cr量の上限を0.25%以下とする。Cr量の好ましい上限は0.20%以下である。
Moは、母材の強度および硬さ、特にt/2位置の内部硬さの向上に有効な元素である。このような作用を有効に発揮させるためには、Mo量の下限を0.25%以上とする。Mo量の好ましい下限は0.28%以上である。しかし、Mo量が0.4%を超えると溶接性が劣化するため、Mo量の上限を0.4%以下とする。Mo量の好ましい上限は0.35%以下である。
Nbは、母材の強度および靭性を高めるのに有効な元素である。このような作用を有効に発揮させるためには、Nb量の下限を0.01%以上とする。Nb量の好ましい下限は0.015%以上である。しかし、Nb量が0.03%を超えると、析出物が粗大化し,かえって母材靭性を劣化させるため、Nb量の上限を0.03%とする。Nb量の好ましい上限は0.025%以下である。
Bは焼入れ性を高め、母材および溶接部(HAZ部)の強度向上に有効な元素である。このような作用を有効に発揮させるためには、B量の下限を0.0003%以上とする。B量の好ましい下限は0.0005%以上である。しかし、B量が過剰になると溶接性が劣化するため、B量の上限を0.002%以下とする。B量の好ましい上限は0.0015%以下である。
Nは、鋼材中に不可避的に含まれる元素であり、N量が多すぎると固溶Nの存在により母材靭性が劣化するため、N量の上限を0.006%以下とする。N量は出来るだけ少ない方が良く、N量の好ましい上限は0.0050%以下である。
REM(希土類元素)は、酸化物を形成することによってHAZ靭性を向上させる元素である。このような作用を有効に発揮させるため、REM量の下限を0.0005%以上とする。REM量の好ましい下限は0.0010%以上であり、より好ましくは0.0015%以上である。一方、REM量が過剰になると粗大介在物が生成し,HAZ靭性が劣化するため、REM量の上限を0.0030%とする。REM量の好ましい上限は0.0025%以下である。
Zrは、酸化物を形成することによってHAZ靭性を向上させる元素である。このような作用を有効に発揮させるため、Zr量の下限を0.0003%以上とする。Zr量の好ましい下限は0.0005%以上である。一方、Zrを過剰に添加すると粗大介在物が生成し,HAZ靭性が劣化するため、Zr量の上限を0.0020%以下とする。Zr量の好ましい上限は0.015%以下である。
本発明では、上記のように鋼中成分の含有量を適切に制御することに加えて、上式で表される炭素当量Ceqを所定範囲に制御する必要がある。後記する実施例で実証したように、たとえ各鋼中成分が上記範囲を満足していたとしても、Ceq(IIW)が本発明で規定する範囲を外れると、所望とする特性を確保することができない。
Niは、母材の強度と靭性の向上に有効な元素である。このような作用を有効に発揮させるため、Ni量の下限を0.05%以上とすることが好ましく、0.10%以上とすることが、より好ましい。しかし、Ni量が過剰になると溶接性が劣化するため、Ni量の上限を0.25%以下とすることが好ましい。より好ましくは0.20%以下である。
温度、圧下率)に従って熱間圧延を行えば良い。
表1の成分組成(鋼種A〜R)を満足する溶鋼を用い、熱間圧延、焼入れ(一部の試料については、更に焼戻し)を行なって厚鋼板(厚さ20mm)を製造した。
加熱温度 :1100℃
仕上げ温後:900〜1000℃
冷却方法 :空冷
マルテンサイトおよびベイナイトの各分率は以下のようにして測定した。まず、上記の各スラブから、直径8mm、厚さ12mmの円柱状試験片を採取し、熱間加工再現試験装置を用いて、連続冷却変態特性(熱膨張曲線)を調べた。詳細には、上記試験片を、930℃に加熱し、26℃/秒の平均冷却速度で室温まで冷却し、試験片の熱膨張曲線を測定した。この平均冷却速度は、板厚20mmのt/2位置における平均冷却速度を模擬したものである。
Ms=550−361×[C]−39×[Mn]−20×[Cr]−17×[Ni]−5×[Mo]+30×[Al]
出展:日本金属学会、『講座・現代の金属学 材料編 第4巻 鉄鋼材料』、丸善,2006、p.45
上記のようにして得られた各鋼板から、JIS Z 2201に規定の5号試験片(全厚引張試験片)を採取し,JIS Z 2201に規定の方法で引張試験を行い、TS(引張強さ)およびYP(降伏応力)を測定した。本実施例では、TSが1100MPa以上のものを高強度に優れる(合格)とした。
上記のようにして得られた各鋼板のt/4位置(t:板厚)から,JIS Z 2242に規定の2mmVノッチ試験片をC方向にて採取し、JIS Z 2242に規定の方法でシャルピー衝撃試験を行い、−70℃での吸収エネルギー(vE-70)を測定した。本実施例では、vE-70が20J以上のものを母材靱性に優れる(合格)と評価した。
上記のようにして得られた各鋼板から熱サイクル用試験片を採取し、溶接時のHAZを模擬するため、所定の熱サイクル(1350℃に加熱して5sec保持した後、800〜500℃の温度範囲を7secかけて冷却する)を付与した。上記熱サイクル後の試験片から、JIS Z2242に規定の2mmVノッチ試験片を採取し,JIS Z2242に規定の方法でシャルピー衝撃試験を行い、0℃での吸収エネルギー(vE0)を測定した。本実施例では、vE0が100J以上のものをHAZ靱性に優れる(合格)と評価した。
上記のようにして得られた各鋼板について、板厚方向の任意の位置に存在する酸化物を測定するため、FE−SEM(Field Emission type Scanning Electron Microscope;電解放出型走査電子顕微鏡、観察倍率5000倍)を用い、40視野(計0.0172mm2)の調査を行った。各視野中に存在する個々の介在物粒子のうち、最大径2μm以下の各介在物粒子の中央部をFE−SEMに付属のEDSにて測定し、当該介在物粒子の構成元素に、REM、Zr、およびOが少なくとも含まれるものを酸化物と判定し、その個数密度(平均値)を測定した。
上記のようにして得られた各鋼板の表面および内部(t/2位置)におけるブリネル硬さ(いずれも、板厚方向と平行な方向での硬さ)を、JIS Z 2243に準拠して測定した。測定は3回行い、その平均値を算出した。本実施例では、このようにして得られたブリネル硬さ(平均値)が、表面および内部のいずれにおいても、360以上のものを耐摩耗性に優れる(合格)と評価した。
Claims (2)
- 鋼中成分は、
C:0.10〜0.16%(質量%の意味。化学成分について以下同じ)、
Si:0.2〜0.5%、
Mn:1〜1.4%、
P:0.03%以下(0%を含まない)、
S:0.01%以下(0%を含まない)、
Al:0.08%以下(0%を含まない)、
Cr:0.03〜0.25%、
Mo:0.25〜0.4%、
Nb:0.01〜0.03%、
B :0.0003〜0.002%、
N :0.006%以下(0%を含まない)、
REM:0.0005〜0.0030%、
Zr:0.0003〜0.0020%、
残部:鉄および不可避不純物であり、且つ、
下記式で表わされるCeq(IIW)が0.40以上、0.45以下の範囲を満足すると共に、
鋼中に最大径2μm以下の酸化物が200個/mm2以上存在し、
マルテンサイト組織を29体積%以上含有し、残部がベイナイト組織であることを特徴とする母材靱性およびHAZ靱性に優れた引張強さ1100MPa以上の高張力鋼板。
Ceq(IIW)=[C]+{1/6×[Mn]}+{1/5×([Cr]+[Mo]+[V])}+{1/15×([Cu]+[Ni])}
式中、[ ]は、鋼中元素の含有量を意味する。 - 更に他の元素として、Ni:0.25%以下(0%を含まない)を含有する請求項1に記載の高張力鋼板。