JP2013504514A - 防眩性を有するガラスおよびディスプレイ - Google Patents
防眩性を有するガラスおよびディスプレイ Download PDFInfo
- Publication number
- JP2013504514A JP2013504514A JP2012529868A JP2012529868A JP2013504514A JP 2013504514 A JP2013504514 A JP 2013504514A JP 2012529868 A JP2012529868 A JP 2012529868A JP 2012529868 A JP2012529868 A JP 2012529868A JP 2013504514 A JP2013504514 A JP 2013504514A
- Authority
- JP
- Japan
- Prior art keywords
- mol
- glass
- glass article
- less
- alkali aluminosilicate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
に従ってDOIを計算する。本明細書に記載される場合、とくに明記されていないかぎり、Rosは、正反射方向から0.2°〜0.4°の角度範囲にわたり反射率を平均することにより計算される。Rsは、正反射方向を中心として±0.05°の角度範囲にわたり反射率を平均することにより計算される。RsおよびRosは両方とも、ASTM手順D523およびD5767(その内容は参照によりその全体が組み入れられるものとする)に明記されるように、認証黒色ガラス標準で校正されたゴニオフォトメーター(Novo−gloss IQ、Rhopoint Instruments)を用いて測定した。Novo−gloss装置は、検出器アレイ中の最高値を正反射角の中心とする検出器アレイを使用する。また、片側法(ガラスの背面に黒色吸収体を結合させる)および両側法(ガラスに結合させずに両方のガラス表面から反射させる)を用いてDOIを評価した。片側測定では、ガラス物品の単一表面(たとえば、単一粗面化表面)の光沢、反射率、およびDOIの測定が可能であり、一方、両側測定では、ガラス物品全体の光沢、反射率、およびDOIの測定が可能である。比Ros/Rsは、上記のようにRsおよびRosに関して得られた平均値から計算される。本明細書で用いられる場合、「20°DOI」という用語は、とくに明記されていないかぎり、ASTM D5767に記載されるように光がガラス表面の法線から20°ずれてサンプルに入射するDOI測定を意味する。両側法を用いたDOIまたは通常の光沢の測定はいずれも、好ましくは、サンプルが存在しないときにこれらの性質の測定値がゼロになるように暗室内または包囲空間内で行われる。
6質量%のNH4HF2および10%のプロピレングリコールからなる静置溶液中にアルミノシリケートガラス板を5分間浸漬した。次に、ガラスサンプルを脱イオン(DI)水中で1分間洗浄し、続いて、1モルH2SO4中に5分間浸漬した。表面全体にわたり流体の移動が容易になるようにサンプルを垂直に保持し、そして垂直運動を用いてH2SO4浴中に浸漬しながら機械撹拌した。撹拌速度は約2Hzであり、移動距離は約2インチ(5.08センチメートル)であった。次に、サンプルをDI水中で再度1分間洗浄し、続いて、4質量%HF+4質量%HClの溶液中に10分間浸漬した。H2SO4浴で用いたのと同一の撹拌方法を用いてHF+HCl浴中で撹拌した。最終工程として、サンプルをDI水中で再度洗浄し、窒素空気流を用いて乾燥させた。サンプルで得られた光学測定および表面測定の結果を表1にまとめる。
10質量%のNH4HF2および10%のプロピレングリコールからなる静置溶液中にアルミノシリケートガラス板を10分間浸漬した。次に、ガラスサンプルをDI水中で洗浄し、垂直撹拌しながらH2SO4浴中に浸漬し、DI水中で再度洗浄し、垂直撹拌しながら4質量%HF+4質量%HClの溶液中に浸漬し、DI水中で再度洗浄し、そして実施例1に記載されるように窒素空気流を用いて乾燥させた。サンプルで得られた光学測定および表面測定の結果を表1にまとめる。
10質量%のNH4HF2および20%のプロピレングリコールからなる静置溶液中にアルミノシリケートガラス板を5分間浸漬した。次に、ガラスサンプルをDI水中で洗浄し、垂直撹拌しながらH2SO4浴中に浸漬し、DI水中で再度洗浄し、垂直撹拌しながら4質量%HF+4質量%HClの溶液中に浸漬し、DI水中で再度洗浄し、そして実施例1に記載されるように窒素空気流を用いて乾燥させた。サンプルで得られた光学測定および表面測定の結果を表1にまとめる。
10質量%のNH4HF2、2%のNaHF2、および20%のプロピレングリコールからなる静置溶液中にアルミノシリケートガラス板を5分間浸漬した。次に、ガラスサンプルをDI水中で洗浄し、垂直撹拌しながらH2SO4浴中に浸漬し、DI水中で再度洗浄し、垂直撹拌しながら4質量%HF+4質量%HClの溶液中に浸漬し、DI水中で再度洗浄し、そして実施例1に記載されるように窒素空気流を用いて乾燥させた。サンプルで得られた光学測定および表面測定の結果を表1にまとめる。
両側がエッチングされた実施例1〜4および6に記載のすべての他のサンプルとは対照的に、このガラスサンプルは、片側のみがエッチングされた。このサンプルは、エッチング前にANT(商標)フィルムを配設して片側がマスキングされた。8質量%のNH4HF2および20%のプロピレングリコールからなる静置溶液中にアルミノシリケートガラス板を10分間浸漬した。次に、ガラスサンプルをDI水中で洗浄し、垂直撹拌しながらH2SO4浴中に浸漬し、DI水中で再度洗浄し、垂直撹拌しながら4質量%HF+4質量%HClの溶液中に浸漬し、DI水中で再度洗浄し、そして実施例1に記載されるように窒素空気流を用いて乾燥させた。サンプルで得られた光学測定および表面測定の結果を表1にまとめる。
7質量%のNH4HF2および20%のプロピレングリコールからなる静置溶液中にアルミノシリケートガラス板を15分間浸漬した。次に、ガラスサンプルをDI水中で洗浄し、垂直撹拌しながらH2SO4浴中に浸漬し、DI水中で再度洗浄し、垂直撹拌しながら4質量%HF+4質量%HClの溶液中に浸漬し、DI水中で再度洗浄し、そして実施例1に記載されるように窒素空気流を用いて乾燥させた。サンプルで得られた光学測定および表面測定の結果を表1にまとめる。
実施例7〜9は、低いヘイズおよび低いDOIの両方を有するガラス表面を提供するのにとくに好適なプロセスを例示する。これらの実施例では、0.9Mのフッ化アンモニウム(NH4F)、2.4Mのプロピレングリコール、0.5MのHCl、および0.6MのHFからなる静置溶液中にアルミノシリケートガラス(Corning 2318)板を8〜12分間浸漬した。次に、ガラスサンプルを脱イオン水中で洗浄し、場合により、清浄化目的でH2SO4浴中に浸漬し、最後に、DI水で洗浄し、そして窒素空気流を用いて乾燥させた。場合により、(先行実施例のときのように、ガラスをHF含有浴中でさらにエッチングすることが可能である。実施例7では、ガラス板の両側表面をエッチング浴に暴露してサンプルの両側に防眩性表面を形成した。実施例8では、エッチング浴中に配置するときにガラスの一表面を犠牲ポリマーフィルムで保護して、ガラス板の片側に防眩性表面を形成した。実施例9では、低いヘイズおよび低いDOIの性質を保持した状態で、ポリマーのアンチスプリンターフィルムまたは反射防止フィルムをガラス板の一表面にラミネートした。実施例7〜9の光学的データを表2に列挙する。
Claims (10)
- 少なくとも1つの粗面化表面を有するガラス物品であって、前記少なくとも1つの粗面化表面が、約10nmから約800nmまでの範囲内の平均RMS粗さを有し、前記ガラス物品が、90未満の反射画像鮮明度および40%未満の透過へイズを有することを特徴とする、ガラス物品。
- 前記少なくとも1つの粗面化表面が、複数のトポグラフィーフィーチャーを含み、前記複数のトポグラフィーフィーチャーが、1μmから約50μmまでの範囲内の平均特性最大フィーチャーサイズを有することを特徴とする、請求項1に記載のガラス物品。
- 前記ガラス物品が、ディスプレイシステムおよびタッチセンサー入力デバイスのうちの一方の一部分を形成するガラスパネルであり、かつ前記ディスプレイシステムまたはタッチセンサー入力デバイスが、前記ガラス物品に隣接するピクセル型画像表示パネルを含み、前記画像表示パネルが、前記平均特性最大フィーチャーサイズよりも大きい最小固有ピクセルピッチ寸法を有することを特徴とする、請求項1に記載のガラス物品。
- 前記ガラス物品が4モル%未満のCaOを含むことを特徴とする、請求項1〜3のいずれか1項に記載のガラス物品。
- 前記ガラス物品が5モル%未満のNa2Oを含むことを特徴とする、請求項1〜3のいずれか1項に記載のガラス物品。
- 前記ガラス物品が少なくとも2モル%のB2O3を含むことを特徴とする、請求項1〜3のいずれか1項に記載のガラス物品。
- 前記ガラス物品が、アルカリアルミノシリケートガラスを含み、かつ前記アルカリアルミノシリケートガラスが、前記ガラス物品の少なくとも1つの表面上に圧縮応力層を形成すべくイオン交換され、かつ前記圧縮応力層が、少なくとも350MPaの圧縮応力および少なくとも15マイクロメートルの層の深さを有することを特徴とする、請求項1〜3のいずれか1項に記載のガラス物品。
- 前記ガラス物品が、アルカリアルミノシリケートガラスを含み、前記アルカリアルミノシリケートガラスが、60〜70モル%のSiO2、6〜14モル%のAl2O3、0〜15モル%のB2O3、0〜15モル%のLi2O、0〜20モル%のNa2O、0〜10モル%のK2O、0〜8モル%のMgO、0〜10モル%のCaO、0〜5モル%のZrO2、0〜1モル%のSnO2、0〜1モル%のCeO2、50ppm未満のAs2O3、および50ppm未満のSb2O3(ただし、12モル%≦Li2O+Na2O+K2O≦20モル%かつ0モル%≦MgO+CaO≦10モル%)を含むことを特徴とする、請求項1〜3のいずれか1項に記載のガラス物品。
- 前記ガラス物品が、アルカリアルミノシリケートガラスを含み、前記アルカリアルミノシリケートガラスが、60〜72モル%のSiO2、9〜16モル%のAl2O3、5〜12モル%のB2O3、8〜16モル%のNa2O、および0〜4モル%のK2O(ただし、比(Al2O3(モル%)+B2O3(モル%))/Σ(改質剤(モル%))>1、かつ前記改質剤は、アルカリ金属酸化物およびアルカリ土類金属酸化物からなる群から選択される)を含むことを特徴とする、請求項1〜3のいずれか1項に記載のガラス物品。
- 前記ガラス物品が、アルカリアルミノシリケートガラスを含み、前記アルカリアルミノシリケートガラスが、61〜75モル%のSiO2、7〜15モル%のAl2O3、0〜12モル%のB2O3、9〜21モル%のNa2O、0〜4モル%のK2O、0〜7モル%のMgO、および0〜3モル%のCaOを含むことを特徴とする、請求項1〜3のいずれか1項に記載のガラス物品。