JP2013185125A - タッチパネル部材貼付用粘着剤、タッチパネル部材貼付用粘着シート、及びタッチパネル装置 - Google Patents
タッチパネル部材貼付用粘着剤、タッチパネル部材貼付用粘着シート、及びタッチパネル装置 Download PDFInfo
- Publication number
- JP2013185125A JP2013185125A JP2012053220A JP2012053220A JP2013185125A JP 2013185125 A JP2013185125 A JP 2013185125A JP 2012053220 A JP2012053220 A JP 2012053220A JP 2012053220 A JP2012053220 A JP 2012053220A JP 2013185125 A JP2013185125 A JP 2013185125A
- Authority
- JP
- Japan
- Prior art keywords
- touch panel
- pressure
- meth
- sensitive adhesive
- sticking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】(メタ)アクリル酸エステル共重合体(A)と架橋剤(B)とを含有するタッチパネル部材貼付用粘着剤であって、(メタ)アクリル酸エステル共重合体(A)が、炭素数4〜20のアルキル基を有するアルキル(メタ)アクリレートモノマー(a1)由来の構成単位(a1)を19〜92質量%、特定構造を有するアルコキシアルキル(メタ)アクリレートモノマー(a2)由来の構成単位(a2)を7〜80質量%、及び官能基含有モノマー(a3)由来の構成単位(a3)を含む、タッチパネル部材貼付用粘着剤。
【選択図】なし
Description
このように静電容量方式タッチパネルの検出感度は、電界の変化の大きさに依存している。そのため、静電容量方式タッチパネルを構成する積層体材料としては、電界を形成し易い高静電容量の材料が求められている。
ここで、静電容量は、下記計算式(1)で表すことができる。計算式(1)からも分かるとおり、高い静電容量を得るためには、材料の薄膜化と、比誘電率の向上という2つの手段が考えられる。
そのため、タッチパネル部材の材料として、ガラスからプラスチックに代えた場合、比誘電率が下がり、静電容量の低下に伴う反応性や感度の低下が起こることが問題となる。
また、特許文献1に記載されたようなアクリル系粘着剤からなる粘着剤層の比誘電率は5程度であり、このような粘着剤からなる粘着剤層の存在も、静電容量低下の要因となる。
なお、タッチパネル部材の薄膜化によって静電容量を高めることも可能ではあるが、タッチパネルの設計上及び製造上の問題から、タッチパネル部材の厚みを適宜変更することは難しい。
すなわち、本発明は、次の〔1〕〜〔12〕を提供する。
〔1〕(メタ)アクリル酸エステル共重合体(A)と架橋剤(B)とを含有するタッチパネル部材貼付用粘着剤であって、
(メタ)アクリル酸エステル共重合体(A)が、炭素数4〜20のアルキル基を有するアルキル(メタ)アクリレートモノマー(a1)由来の構成単位(a1)を19〜92質量%、下記一般式(1)で表されるアルコキシアルキル(メタ)アクリレートモノマー(a2)由来の構成単位(a2)を7〜80質量%、及び官能基含有モノマー(a3)由来の構成単位(a3)を含む共重合体である、タッチパネル部材貼付用粘着剤。
〔2〕前記一般式(1)中のnの値が2〜12の整数である、上記〔1〕に記載のタッチパネル部材貼付用粘着剤。
〔3〕アルコキシアルキル(メタ)アクリレートモノマー(a2)が、エトキシジエチレングリコール(メタ)アクリレート又はメトキシトリエチレングリコール(メタ)アクリレートである、上記〔1〕又は〔2〕に記載のタッチパネル部材貼付用粘着剤。
〔4〕官能基含有モノマー(a3)由来に構成単位(a3)の含有量が、(メタ)アクリル酸エステル共重合体(A)の全構成単位に対して、0.01〜15質量%である、上記〔1〕〜〔3〕のいずれかに記載のタッチパネル部材貼付用粘着剤。
〔5〕架橋剤(B)の含有量が、(メタ)アクリル酸エステル共重合体(A)100質量部に対して、0.01〜15質量部である、上記〔1〕〜〔4〕のいずれかに記載のタッチパネル部材貼付用粘着剤。
〔6〕上記〔1〕〜〔5〕のいずれかに記載のタッチパネル部材貼付用粘着剤からなる粘着剤層を有する、タッチパネル部材貼付用粘着シート。
〔7〕基材上に、前記粘着剤層を有する、上記〔6〕に記載のタッチパネル部材貼付用粘着シート。
〔8〕前記基材が、プラスチック板又はプラスチックフィルムである、上記〔7〕に記載のタッチパネル部材貼付用粘着シート。
〔9〕前記粘着剤層の周波数1MHzでの比誘電率が、6.00以上である、上記〔6〕〜〔8〕のいずれかに記載のタッチパネル部材貼付用粘着シート。
〔10〕上記〔6〕〜〔9〕のいずれかに記載のタッチパネル部材貼付用粘着シートを用いた、タッチパネル装置。
〔11〕前記タッチパネル装置が、静電容量方式である、上記〔10〕に記載のタッチパネル装置。
本発明のタッチパネル部材貼付用粘着剤(以下、単に「粘着剤」ともいう)は、(メタ)アクリル酸エステル共重合体(A)と架橋剤(B)とを含有する。また、本発明の粘着剤は、(A)及び(B)成分以外のその他の添加剤を含有してもよい。以下、本発明の粘着剤に含まれる各成分について説明する。
なお、以下の記載において、例えば「(メタ)アクリル酸」とは、アクリル酸及びメタクリル酸の両方を意味し、他の類似用語も同様である。
本発明の粘着剤には、(A)成分として、炭素数4〜20のアルキル基を有するアルキル(メタ)アクリレートモノマー(a1)(以下、「モノマー(a1)」ともいう)由来の構成単位(a1)を19〜92質量%、一般式(1)で表されるアルコキシアルキル(メタ)アクリレートモノマー(a2)(以下、「モノマー(a2)」ともいう)由来の構成単位(a2)を7〜80質量%、及び官能基含有モノマー(a3)(以下、「モノマー(a3)」ともいう)由来の構成単位(a3)を含む(メタ)アクリル酸エステル共重合体を含む。
なお、本発明において、(A)成分は、単独で又は2種以上併用してもよい。
重量平均分子量が25万以上であれば、粘着剤の耐久性が向上し、浮きや剥がれが発生し難く、高温高湿の環境下においても発泡が生じ難い。一方、150万以下であれば、ポリマー合成時の重合を容易に行うことができる。
なお、本発明において、重量平均分子量(Mw)は、ゲルパーミエーションクロマトグラフィー(GPC)法で測定される標準ポリスチレン換算値である。
以下、(メタ)アクリル酸エステル共重合体(A)に含まれる各構成単位について説明する。
(メタ)アクリル酸エステル共重合体(A)は、構成単位として、炭素数4〜20のアルキル基を有するアルキル(メタ)アクリレートモノマー(a1)由来の構成単位(a1)を19〜92質量%含む。(A)成分の共重合体中に、特定量の構成単位(a1)を含むことで、粘着シートとして適度な粘着力が得られる。
アルキル基の炭素数が4未満であると、得られる粘着剤から比誘電率を十分に向上させた粘着剤層を形成することができず、静電容量の低下が問題となる。また、粘着剤の粘着力も十分に発現されないため好ましくない。
一方、アルキル基の炭素数が20を超えると、粘着剤から形成される粘着剤層の比誘電率を高くすることはできるが、該粘着剤層の誘電正接も上昇してしまい、該粘着剤層を有するタッチパネルは、コンデンサ性能が劣ることとなり好ましくない。
これらの中でも、比誘電率が高く、同時に誘電正接が低い粘着剤層を形成し得る粘着剤を得る観点から、ブチル(メタ)アクリレート、ペンチル(メタ)アクリレート、ヘキシル(メタ)アクリレートが好ましく、n−ブチル(メタ)アクリレートがより好ましい。
なお、これらのモノマー(a1)は、単独で又は2種以上併用して用いてもよい。
19質量%未満であると、粘着力の低下の要因となる。一方、92質量%を超えると、構成単位(a1)以外の構成単位(a2)等の含有量を十分に確保することができなくなり、特に粘着剤から形成される粘着剤層の比誘電率が低下するため好ましくない。
(メタ)アクリル酸エステル共重合体(A)は、構成単位として、下記一般式(1)で表されるアルコキシアルキル(メタ)アクリレートモノマー(a2)由来の構成単位(a2)を7〜80質量%含む。共重合体(A)中に、特定量の構成単位(a2)を含むことで、粘着剤から形成される粘着剤層の比誘電率を上昇させ、同時に誘電正接を低下させることができる。
また、R2は、炭素数1〜5の直鎖又は分岐鎖のアルキレン基を示し、好ましくは炭素数2〜5の直鎖又は分岐鎖のアルキレン基、より好ましくは炭素数2〜3の直鎖又は分岐鎖のアルキレン基、更に好ましくは炭素数2〜3の直鎖のアルキレン基である。
R2が示す炭素数1〜5の直鎖又は分岐鎖のアルキレン基としては、例えば、メチレン基、エチレン基、プロピレン基、イソプロピレン基、1,4−ブチレン基、1,3−ブチレン基、テトラメチレン基、1,5−ペンチレン基、1,4−ペンチレン基、1,3−ペンチレン基等が挙げられる。
R3が示す炭素数1〜8の直鎖又は分岐鎖のアルキル基としては、例えば、メチル基、エチル基、プロピル基、イソプロピル基、n−ブチル基、イソブチル基、t−ブチル基、ペンチル基、ヘキシル基、ヘプチル基、オクチル基等が挙げられる。
なお、上記一般式(1)で表される化合物において、R2で表される基一つあたりの炭素数がA個、R3で表される基の炭素数がB個である場合、「R2及びR3の炭素数の合計」は、A×n+B(個)と表すことができる。
例えば、エトキシジエチレングリコールアクリレートにおける当該炭素数の合計は6個(=2×2+2)となり、メトキシトリエチレングリコールアクリレートにおける当該炭素数の合計は7個(=2×3+1)となる。
なお、これらのモノマー(a2)は、単独で又は2種以上併用して用いてもよい。
7質量%未満であると、特に得られる粘着剤から形成される粘着剤層の比誘電率が低下するため好ましくない。一方、80質量%を超えると、構成単位(a2)以外の構成単位(a1)等の含有量を十分に確保することができなくなり、粘着力低下の要因となる。
(メタ)アクリル酸エステル共重合体(A)は、構成単位として、官能基含有モノマー(a3)を含む。共重合体(A)中に、構成単位(a3)を含むことで、凝集力が維持され、優れた粘着力を有する粘着剤層を形成することができる。
なお、ここでいう「官能基含有モノマー」の「官能基」とは、架橋剤(B)と反応し、架橋起点となり得る官能基又は架橋促進効果を有する官能基を意味する。
当該官能基としては、例えば、水酸基、カルボキシ基、アミド基、アミノ基、エポキシ基、シアノ基、ケト基、窒素元素含有環等が挙げられる。これらの中でも、架橋剤(B)との反応性の観点から、カルボキシ基、又は水酸基が好ましい。
なお、これらのモノマー(a3)は、単独で又は2種以上併用して用いてもよい。
その他のモノマー由来の構成単位の含有量は、(メタ)アクリル酸エステル共重合体(A)の全構成単位中、好ましくは0〜10質量%、より好ましくは0〜4質量%、更に好ましくは実質0質量%(実質含まない)である。
架橋剤(B)は、(メタ)アクリル酸エステル共重合体(A)を架橋するものである。
用いる架橋剤としては、例えば、有機多価イソシアネート化合物、有機多価エポキシ化合物、有機多価イミン化合物、金属キレート化合物等が挙げられる。これらの中でも、得られる粘着剤の凝集力を高めて粘着力を向上させる観点、及び、入手し易さ等の観点から、有機多価イソシアネート化合物、金属キレート化合物が好ましい。
なお、これらの有機多価イソシアネート化合物の三量体、並びに、これらの有機多価イソシアネート化合物とポリオール化合物とを反応して得られる末端イソシアネートウレタンプレポリマー等も使用することができる。
架橋剤(B)の含有量は、(メタ)アクリル酸エステル共重合体(A)100重量部に対して、好ましくは0.01〜15質量部(固形分比)、より好ましくは0.1〜8質量部(固形分比)、更に好ましくは0.2〜4質量部(固形分比)である。0.01質量部(固形分比)以上であれば、せん断方向の応力に対して形状を維持するのに十分な凝集力を得ることができる。一方、15質量部(固形分比)以下であれば、十分な粘着力が得られる。
また、本発明の粘着剤には、必要に応じ本発明の効果を損なわない程度で、他の添加剤を含有させてもよい。添加剤としては、従来から粘着剤に使用される、粘着付与剤、紫外線吸収剤、酸化防止剤、軟化剤(可塑剤)、充填剤、防錆剤、顔料、染料等が挙げられる。
水素化石油樹脂としては、例えば、水添テルペン系樹脂、水添ロジン及び水添ロジンエステル系樹脂、不均化ロジン、不均化ロジンエステル系樹脂、石油ナフサの熱分解で生成するペンテン、イソプレン、1.3−ペンタジエン等のC5留分を共重合して得られるC5系石油樹脂の水添加樹脂である水添ジシクロペンタジエン系樹脂、部分水添芳香族変性ジシクロペンタジエン系樹脂、石油ナフサの熱分解で生成するインデン、ビニルトルエン、α−又はβ−メチルスチレン等のC9留分を共重合して得られるC9系石油樹脂を水添した樹脂、上記したC5留分とC9留分の共重合石油樹脂を水添した樹脂等が挙げられる。
酸化防止剤としては、フェノール系酸化防止剤、リン系酸化防止剤、イオウ系酸化防止剤、ビタミン系酸化防止剤、ラクトン系酸化防止剤、アミン系酸化防止剤等が挙げられる。
軟化剤(可塑剤)としては、液状ポリエーテル、グリコールエステル、液状ポリテルペン、液状ポリアクリレート、フタル酸エステル、トリメリット酸エステル等が挙げられる。
有機溶媒としては、メチルエチルケトン、アセトン、酢酸エチル、テトラヒドロフラン、ジオキサン、シクロヘキサン、n−ヘキサン、トルエン、キシレン、n−プロパノール、イソプロパノール等が挙げられる。これらの有機溶媒は、(A)成分及び(B)成分の調製時に使用された有機溶媒をそのまま用いてもよいし、該粘着剤溶液を均一に塗布できるように、調製時に使用された有機溶媒以外の1種以上の有機溶媒を加えてもよい。
本発明のタッチパネル部材貼付用粘着シート(以下、単に「粘着シート」ともいう)は、上述の本発明のタッチパネル部材貼付用粘着剤からなる粘着剤層を有する。
本発明の粘着シートの構成は、特に限定されないが、例えば、図1、2の態様の粘着シートが挙げられる。
図1に示された粘着シート1は、粘着剤層11の両面に剥離シート12a、12bが積層されたものであり、基材無し両面粘着シートである。
剥離シートとしては、両面剥離処理を施した剥離シート、片面のみ剥離処理を施した剥離シートの双方とも用いられる。剥離シートは、剥離シート用基材の片面又は両面に剥離剤を塗布して得られる。
用いる剥離剤としては、例えば、シリコーン系樹脂、オレフィン系樹脂、長鎖アルキル系樹脂、アルキド系樹脂、フッ素系樹脂、イソプレン系樹脂やブタジエン系樹脂等のゴム系エラストマー等が挙げられる。
剥離シートの厚さは、特に制限は無いが、好ましくは5〜300μm、より好ましくは10〜200μmである。なお、剥離シート用基材としてポリエチレンテレフタレート系フィルムを用いる場合は、好ましくは10〜100μmである。
なお、基材付き両面粘着シートとした場合、両面ともに本発明の粘着剤を使うことが好ましいが、材質の異なる2種類の粘着剤を基材に積層するものであってもよい。この場合は、一方の粘着剤に本発明の粘着剤を適用することができる。また、両面粘着シートにある程度の厚みが必要な場合には、基材の厚みで適宜調節することで、基材付き両面粘着シートの総厚みを容易に調整できる。
基材付き片面粘着シートの場合、好ましくは1〜195μm、より好ましくは5〜100μm、更に好ましくは10〜60μmである。
基材付き両面粘着シートの場合、それぞれの粘着剤層の厚みが、好ましくは1〜195μm、より好ましくは5〜100μm、更に好ましくは10〜60μmである。
なお、粘着剤層の周波数1MHzでの比誘電率の値は、実施例に記載の方法により測定された値を意味する。
上述のとおり、本発明のタッチパネル部材貼付用粘着剤は、比誘電率が高く、且つ誘電正接が低い粘着剤層を形成し得る。
そのため、タッチパネルの各種部材の貼り付け用に、当該粘着剤からなる粘着剤層を有する本発明の粘着シートを用いたタッチパネル装置は、タッチパネル部材の材料としてガラスに代えてプラスチックを用いた場合でも、静電容量が高く、感度に優れ、コンデンサ性能に優れたタッチパネルとなり得る。特に、この効果は、タッチパネル装置が静電容量方式タッチパネルである場合に顕著である。
したがって、従来ガラスを用いていた部材をプラスチックに代えることができるため、軽量化されたタッチパネル装置を得ることができる。
[実施例1]
(A)成分として、n−ブチルアクリレート(BA)、エトキシジエチレングリコールアクリレート(EDG−A)、4−ヒドロキシブチルアクリレート(4HBA)からなるアクリル酸エステル共重合体(BA/EDG−A/4HBA=58.2/40.0/1.8(質量%)、Mw=80万、固形分濃度39.4質量%)100質量部(固形分)、及び(B)成分として、トリレンジイソシアネート系架橋剤(日本ポリウレタン工業社製、商品名「コロネートL」、固形分75%)1.71質量部(固形分比)を用いて、混合し、メチルエチルケトンで希釈して、固形分濃度25質量%の粘着剤溶液を調製した。
この調製した粘着剤溶液を、乾燥後の膜厚が25μmになるように、重剥離シート(リンテック社製、製品名「SP−PET382150」、厚み:38μm)の剥離処理面上に塗布して塗膜を形成し、該塗膜を120℃で2分間乾燥させて粘着剤層を形成した。そして、該粘着剤層の表面に、軽剥離シート(リンテック社製、製品名「SP−PET382120」、厚み:38μm)の剥離処理面を貼合し、2枚の剥離フィルムに挟持された基材無し両面粘着シートを得た。
(A)成分として、n−ブチルアクリレート(BA)、メトキシトリエチレングリコールアクリレート(MTG−A)、4−ヒドロキシブチルアクリレート(4HBA)からなるアクリル酸エステル共重合体(BA/MTG−A/4HBA=58.2/40.0/1.8(質量%)、Mw=80万、固形分濃度39.4質量%)を100質量部(固形分)用いた以外は、実施例1と同様にして、基材無し両面粘着シートを得た。
(A)成分として、n−ブチルアクリレート(BA)、メトキシエチルアクリレート(MEA)、4−ヒドロキシブチルアクリレート(4HBA)からなるアクリル酸エステル共重合体(BA/MEA/4HBA=58.2/40.0/1.8(質量%)、Mw=80万、固形分濃度37.2質量%)を100質量部(固形分)用い、(B)成分の配合量を1.81質量部(固形分比)とした以外は、実施例1と同様にして、基材無し両面粘着シートを得た。
(A)成分として、n−ブチルアクリレート(BA)、アクリル酸(AA)からなるアクリル酸エステル共重合体(BA/AA=90.0/10.0(質量%)、Mw=60万、固形分濃度33.6質量%)を100質量部(固形分)用い、(B)成分の配合量を2.23質量部(固形分比)とした以外は、実施例1と同様にして、基材無し両面粘着シートを得た。
(A)成分として、n−ブチルアクリレート(BA)、アクリル酸(AA)からなるアクリル酸エステル共重合体(BA/AA=95.0/5.0(質量%)、Mw=60万、固形分濃度34.5質量%)を100質量部(固形分)用い、(B)成分の配合量を1.96質量部(固形分比)とした以外は、実施例1と同様にして、基材無し両面粘着シートを得た。
(A)成分として、n−ブチルアクリレート(BA)、メチルアクリレート(MA)、2−ヒドロキシエチルアクリレート(HEA)からなるアクリル酸エステル共重合体(BA/MA/HEA=79.0/20.0/1.0(質量%)、Mw=80万、固形分濃度35.1質量%)を100質量部(固形分)用い、(B)成分の配合量を0.96質量部(固形分比)とした以外は、実施例1と同様にして、基材無し両面粘着シートを得た。
(A)成分として、n−ブチルアクリレート(BA)、メチルアクリレート(MA)、アクリル酸(AA)からなるアクリル酸エステル共重合体(BA/MA/AA=78.2/20.0/1.8(質量%)、Mw=80万、固形分濃度32.2質量%)を100質量部(固形分)用い、(B)成分の配合量を2.33質量部(固形分比)とした以外は、実施例1と同様にして、基材無し両面粘着シートを得た。
(A)成分として、n−ブチルアクリレート(BA)、メチルアクリレート(MA)、アクリル酸(AA)からなるアクリル酸エステル共重合体(BA/MA/AA=77.0/20.0/3.0(質量%)、Mw=80万、固形分濃度35.1質量%)を100質量部(固形分)用い、(B)成分として、トリレンジイソシアネート系架橋剤(日本ポリウレタン工業社製、商品名「コロネートL」、固形分濃度75質量%)2.34質量部(固形分比)とアルミキレート系架橋剤(綜研化学社製、商品名「M−5A」、固形分濃度4.95質量%)0.31質量部(固形分比)を用いて、混合し、メチルエチルケトンで希釈して調製した、固形分濃度25%の粘着剤溶液を用いた以外は、実施例1と同様にして、基材無し両面粘着シートを得た。
実施例及び比較例で作製した基材無し両面粘着シートの一方の剥離フィルムを剥がしたものを2枚用意し、粘着剤層同士をラミネートして、粘着剤層が2層積層された、2層からなる粘着剤層積層体付きシートを得た。さらに、この2層からなる粘着剤層積層体付きシートの一方の剥離フィルムを剥がしたものを2枚用意し、同様にラミネートして粘着剤層が4層積層された、4層からなる粘着剤層積層体付きシートを得た。
得られた4層からなる粘着剤層積層体付きシートの両方の剥離フィルムを剥がし、厚さ50μmのポリエチレンテレフタレートフィルム(東レ社製、商品名「ルミラーT−60」)を用い、図3に示すように、4層の粘着剤層11が積層された粘着剤層積層体11Aの両側を2枚の上記ポリエチレンテレフタレートフィルム51a、51bで挟持し、測定サンプルを作製した。なお、粘着剤層の厚みの測定には、定圧厚み計(テクロック社製、製品名「PG−02」)を使用した。
そして、LCR/レジスタンスメータ(アジレントテクノロジー社製、製品名「インピーダンス/ゲイン・フェーズ アナライザ4194A」)に、「Agilent16451B誘電体テスト・フィクスチャ」(製品名、アジレントテクノロジー社製)を接続して、周波数1MHzにおける測定サンプルの静電容量C1(単位:F)を測定した。
50μmのポリエチレンテレフタレートフィルム51a、51bの静電容量を別途測定し(その測定値をC2(単位:F)とする)、粘着剤層積層体11Aの静電容量C3(単位:F)を以下の計算式(2)から算出した。
A:比誘電率εrの値が7.00以上。
B:比誘電率εrの値が6.00以上7.00未満。
C:比誘電率εrの値が6.00未満。
上記の「比誘電率の測定」の際に作製した測定サンプルを用いて、LCR/レジスタンスメータ(アジレントテクノロジー社製、製品名「インピーダンス/ゲイン・フェーズ アナライザ4194A」)に、「Agilent16451B誘電体テスト・フィクスチャ」(製品名、アジレントテクノロジー社製)を接続して、周波数1MHzにおける測定サンプルの誘電正接を測定した。なお、当該測定値は、測定サンプルの積層体の誘電正接の値であり、粘着剤層単体の値ではない。
A:誘電正接の値が0.035未満。
B:誘電正接の値が0.035以上0.040未満。
C:誘電正接の値が0.040以上。
11、11a、11b 粘着剤層
11A 粘着剤層積層体
12a、12b 剥離シート
13 基材
51a、51b ポリエチレンテレフタレートフィルム
Claims (11)
- (メタ)アクリル酸エステル共重合体(A)と架橋剤(B)とを含有するタッチパネル部材貼付用粘着剤であって、
(メタ)アクリル酸エステル共重合体(A)が、炭素数4〜20のアルキル基を有するアルキル(メタ)アクリレートモノマー(a1)由来の構成単位(a1)を19〜92質量%、下記一般式(1)で表されるアルコキシアルキル(メタ)アクリレートモノマー(a2)由来の構成単位(a2)を7〜80質量%、及び官能基含有モノマー(a3)由来の構成単位(a3)を含む共重合体である、タッチパネル部材貼付用粘着剤。
- 前記一般式(1)中のnの値が2〜12の整数である、請求項1に記載のタッチパネル部材貼付用粘着剤。
- アルコキシアルキル(メタ)アクリレートモノマー(a2)が、エトキシジエチレングリコール(メタ)アクリレート又はメトキシトリエチレングリコール(メタ)アクリレートである、請求項1又は2に記載のタッチパネル部材貼付用粘着剤。
- 官能基含有モノマー(a3)由来に構成単位(a3)の含有量が、(メタ)アクリル酸エステル共重合体(A)の全構成単位に対して、0.01〜15質量%である、請求項1〜3のいずれかに記載のタッチパネル部材貼付用粘着剤。
- 架橋剤(B)の含有量が、(メタ)アクリル酸エステル共重合体(A)100質量部に対して、0.01〜15質量部である、請求項1〜4のいずれかに記載のタッチパネル部材貼付用粘着剤。
- 請求項1〜5のいずれかに記載のタッチパネル部材貼付用粘着剤からなる粘着剤層を有する、タッチパネル部材貼付用粘着シート。
- 基材上に、前記粘着剤層を有する、請求項6に記載のタッチパネル部材貼付用粘着シート。
- 前記基材が、プラスチック板又はプラスチックフィルムである、請求項7に記載のタッチパネル部材貼付用粘着シート。
- 前記粘着剤層の周波数1MHzでの比誘電率が、6.00以上である、請求項6〜8のいずれかに記載のタッチパネル部材貼付用粘着シート。
- 請求項6〜9のいずれかに記載のタッチパネル部材貼付用粘着シートを用いた、タッチパネル装置。
- 前記タッチパネル装置が、静電容量方式である、請求項10に記載のタッチパネル装置。