JP2012251017A - タイヤ用ゴム組成物 - Google Patents
タイヤ用ゴム組成物 Download PDFInfo
- Publication number
- JP2012251017A JP2012251017A JP2011122640A JP2011122640A JP2012251017A JP 2012251017 A JP2012251017 A JP 2012251017A JP 2011122640 A JP2011122640 A JP 2011122640A JP 2011122640 A JP2011122640 A JP 2011122640A JP 2012251017 A JP2012251017 A JP 2012251017A
- Authority
- JP
- Japan
- Prior art keywords
- tire
- rubber composition
- carbon black
- rubber
- dst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】 ジエン系ゴム100重量部に対し、ノボラック型フェノール樹脂及びメチレン供与体を配合しその合計が1〜50重量部、窒素吸着比表面積N2SAが55〜95m2/g、DBP吸収量が110〜160ml/100gのカーボンブラックを30〜100重量部を配合すると共に、前記カーボンブラックの凝集体のストークス径の質量分布曲線におけるモード径Dst(nm)と、前記N2SAとを、Dst=α(N2SA)-0.61の関係式で表わしたときの係数αが1979以上であることを特徴とする。
【選択図】図2
Description
Dst=α(N2SA)-0.61 (1)
(ただし、Dstは凝集体のストークス径の質量分布曲線におけるモード径(nm)、N2SAは窒素吸着比表面積(m2/g)、αは係数である。)
で表わしたとき、係数αが1979以上であることを特徴とする。
Dst=α(N2SA)-0.61 (1)
(ただし、Dstは凝集体のストークス径の質量分布曲線におけるモード径(nm)、N2SAは窒素吸着比表面積(m2/g)、αは係数である。)
Dst=1650×(N2SA)-0.61 (2)
(ただし、Dstは凝集体のストークス径の質量分布曲線におけるモード径(nm)、N2SAは窒素吸着比表面積(m2/g)を表わす。)
図2では、上記式(2)の関係を点線の曲線で表わした。
Dst=1979×(N2SA)-0.61 (3)
(ただし、Dstは凝集体のストークス径の質量分布曲線におけるモード径(nm)、N2SAは窒素吸着比表面積(m2/g)を表わす。)
・N2SA:JIS K6217−2に基づいて測定された窒素吸着比表面積
・IA:JIS K6217−1に基づいて測定されたよう素吸着量
・CTAB:JIS K6217−3に基づいて測定されたCTAB吸着比表面積
・DBP:JIS K6217−4(非圧縮試料)に基づいて測定されたDBP吸収量
・24M4:JIS K6217−4(圧縮試料)に基づいて測定された24M4−DBP吸収量
・TINT:JIS K6217−5に基づいて測定された比着色力
・Dst:JIS K6217−6に基づいて測定されたディスク遠心光沈降法による凝集体のストークス径の質量分布曲線の最大値であるモード径
・△D50:JIS K6217−6に基づいて測定されたディスク遠心光沈降法による凝集体のストークス径の質量分布曲線において、その質量頻度が最大点の半分の高さのときの分布の幅(半値幅)
・α:Dst及びN2SAを上述した式(1)の関係に当てはめたときの係数α
・CB1:東海カーボン社製シーストKHP
・CB2:東海カーボン社製シーストKH
・CB8:東海カーボン社製シースト300
・CB9:キャボットジャパン社製ショウブラック330T
・CB10:新日化カーボン社製ニテロン#10N
・CB11:東海カーボン社製シースト3
・CB12:東海カーボン社製シーストNH
・CB13:東海カーボン社製シースト6
円筒反応炉を使用して、表3に示すように全空気供給量、燃料油導入量、燃料油燃焼率、原料油導入量、反応時間を変えて、カーボンブラックCB3〜CB7を製造した。
上述した13種類のカーボンブラック(CB1〜CB13)を用いて、表4,5に示す配合からなる15種類のゴム組成物(実施例1〜6、比較例1〜9)を調製するに当たり、それぞれ硫黄及び加硫促進剤を除く成分を秤量し、55Lのニーダーで15分間混練した後、そのマスターバッチを放出し室温冷却した。このマスターバッチを55Lのニーダーに供し、硫黄及び加硫促進剤を加え、混合しタイヤ用ゴム組成物を得た。
得られたタイヤを標準リム(サイズ15×6Jのホイール)に組み付け、JIS D4230に準拠する室内ドラム試験機(ドラム径1707mm)に取り付け、JIS D4230の「6.4高速性能試験A」に記載される高速耐久性の試験に準拠して高速耐久性試験を実施し、試験荷重2.94kN、速度50km/時の抵抗力を測定し、転がり抵抗とした。得られた結果は、比較例1の値の逆数を100とする指数として表4,5の「転がり抵抗」の欄に示した。この指数が大きいほど転がり抵抗が小さく燃費性能が優れていることを意味する。
得られたタイヤを標準リム(サイズ15×6Jのホイール)に組み付け、国産2.0リットルクラスの試験車両に装着し、空気圧230kPaの条件で乾燥路面からなる1周2.6kmのテストコースを実車走行させ、そのときの操縦安定性を専門パネラー3名による感応評価により採点した。得られた結果は、比較例1の値を100とする指数として表4,5の「操縦安定性」の欄に示した。この指数が大きいほど操縦安定性能が優れていることを意味する。
NR:天然ゴム、RSS#3
SBR:スチレン−ブタジエンゴム、日本ゼオン社製Nipol 1502
フェノール樹脂1:カシュー変性ノボラック型フェノール樹脂、住友ベークライト社製スミライトレジンPR−YR−170
フェノール樹脂2:未変性のノボラック型フェノール樹脂、住友ベークライト社製PR7031A
メチレン供与体:ヘキサメチレンテトラミン、大内新興化学工業社製ノクセラーH−PO
CB1〜CB13:上述した表1,2に示したカーボンブラック
アロマオイル:ジャパンエナジー社製プロセスX−140
亜鉛華:正同化学工業社製酸化亜鉛3種
ステアリン酸:日油社製ビーズステアリン酸
老化防止剤:フレキシス社製SANTOFLEX6PPD
加硫促進剤:大内新興化学工業社製ノクセラーNS−P
硫黄:四国化成社製ミュークロンOT−20(硫黄分80重量%)
2 サイドウォール部
3 ビード部
4 ビードコア
5 ビードフィラー
6 カーカス
7 ベルト層
8 ゴム補強層
9 インナーライナー
Claims (5)
- ジエン系ゴム100重量部に対し、ノボラック型フェノール樹脂及びメチレン供与体を配合しその合計が1〜50重量部、窒素吸着比表面積N2SAが55〜95m2/g、DBP吸収量が110〜160ml/100gのカーボンブラックを30〜100重量部配合すると共に、前記カーボンブラックの凝集体のストークス径の質量分布曲線におけるモード径Dst(nm)と、前記N2SAとの関係を下記の式(1)
Dst=α(N2SA)-0.61 (1)
(ただし、Dstは凝集体のストークス径の質量分布曲線におけるモード径(nm)、N2SAは窒素吸着比表面積(m2/g)、αは係数である。)
で表わしたとき、係数αが1979以上であることを特徴とするタイヤ用ゴム組成物。 - 前記係数αが、1979≦α≦2450であることを特徴とする請求項1に記載のタイヤ用ゴム組成物。
- 前記ノボラック型フェノール樹脂がカシューオイルで変性された樹脂であることを特徴とする請求項1又は2に記載のタイヤ用ゴム組成物。
- 請求項1,2又は3に記載のタイヤ用ゴム組成物でビードフィラーを構成したことを特徴とする空気入りタイヤ。
- 請求項1,2又は3に記載のタイヤ用ゴム組成物で、ランフラットタイヤの左右のサイドウォール部の断面三日月形のゴム補強層を構成したことを特徴とする空気入りタイヤ。