JP2012154020A - サブミクロン繊維を生産するプロセスおよび装置、ならびに不織布およびその不織布を含む物品 - Google Patents
サブミクロン繊維を生産するプロセスおよび装置、ならびに不織布およびその不織布を含む物品 Download PDFInfo
- Publication number
- JP2012154020A JP2012154020A JP2012089937A JP2012089937A JP2012154020A JP 2012154020 A JP2012154020 A JP 2012154020A JP 2012089937 A JP2012089937 A JP 2012089937A JP 2012089937 A JP2012089937 A JP 2012089937A JP 2012154020 A JP2012154020 A JP 2012154020A
- Authority
- JP
- Japan
- Prior art keywords
- polymer
- nonwoven web
- gas
- fibers
- microns
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】本発明は、サブミクロン繊維を生産するプロセスおよび装置、より具体的には、ポリマーフィルムをフィブリル化することでサブミクロン繊維を形成するプロセスおよび装置、ならびにそのサブミクロン繊維を組み込んだ不織布素材および物品、を提供する。
【選択図】図1
Description
本発明は、概して、サブミクロンの繊維を生産することに関し、より具体的には、ポリマーフィルムをフィブリル化することによってサブミクロンの繊維を形成するプロセスおよび装置、および不織布材料、ならびにその不織布材料が入った物品に関するものである。
連続的および非連続なフィラメントスピニングテクノロジー(filament spinning technologies)が当該技術において既知であり、一般にスパンメルトテクノロジー(spunmelt technologies)と呼ばれている。スパンメルトテクノロジーとしては、メルトブロープロセスとスパンボンドプロセスの両方がある。スパンボンドプロセスでは、溶融ポリマーを供給し、次にこの溶融ポリマーに圧力をかけて、スピナレットまたは金型として知られているプレートにおける多数の開口部に押し通すことが必要である。結果として生じた連続フィラメントは、スロットドローシステム(slot draw system)、アッテネーターガン(attenuator guns)またはゴデットロール(Godet rolls)のようないくつかの方法のいずれかによって冷やされ、延伸される。連続フィラメントは、金網製のコンベヤベルトのような、動いている孔面の上に絡まっていないウェブとして集積される。多層の織物を形成するために、1つ以上のスピナレットを1列にして使用した場合、後続のウェブが先に形成されたウェブの1番上の面上に集積される。
本発明は、独自のシングルステップ、溶融体フィルムのフィブリル化、高生産量のプロセス、およびこの目的のために使用されるノズル装置において生成される、高品質で欠陥が少ないサブミクロン繊維およびそのサブミクロン繊維を組み込んだ不織布生産量に向けられている。ある一態様では、サブミクロン繊維の含有量が99%を超える高品質のマイクロファイバーを含む不織布製品が、商業規模の生産量で得られる。ポリマーのせん断変形が大きくなり、ノズル装置内でショットが発達するなど好ましくない繊維の欠陥につながるポリマーの逆流又は堆積という問題も本発明によって軽減する。本発明によれば、バリア特性、しなやかさ、吸収性、不透明度が改善されており、および/または表面積が大きな高品質のマイクロ繊維性不織布製品が提供されており、これらは、幅広い産業用および消費者用繊維性ケア製品に適している。
本発明はさまざまな形態での実施形態が可能であるが、本開示内容は発明の一例と見なすべきであり、かつ、説明する具体的な実施形態に発明を限定するものではないとの了解のもとで、本発明の現在のところ好ましい実施形態を図面に示し、以下に説明されるであろう。
押出機(直径63.5mm(2.5インチ)、シングルスクリュー押出機)および従来のメルトブロー金型本体(幅635mm(25インチ))を1800MFRポリプロピレンの供給源として用いた。押出機の温度は343℃(650°F)であった。だいたい図4の構成をしたノズルを従来の押出機金型本体に、ノズル装置の上部平坦面領域に取り付けられている従来のガスケット付ボルトを用いて取り付けた。圧縮空気源は、空気源からノズルの入口へ気密な接続部および密閉部を介して供給した。ノズルの形状の特徴は以下の通りであった(図4を非限定的な例として用いる)。のど状部分9における対向壁部5および6の間の最小距離は0.406mm(0.016インチ)であった。冷たい壁部5は、二等分面7に向かって−1.5度の角度θで近づいていた。熱い壁部は、二等分面7から2度の角度βで離れていた。ポリマー通路は、第2部分の第2下流側半部において第2部分に入っており、水力直径が約0.203mm(0.008インチ)であり、熱い壁部6に対して約32度の角度γに向いていた。ポリマー繊維化面の長さδはほぼゼロであった。収束部分8の縦方向長さは約2.286mm(0.090インチ)で、二等分角αは約30度であった。のど状部分9の縦方向の長さは約0.254mm(0.010インチ)であり、拡大部分10の縦方向長さは約5.080mm(0.200インチ)であった。加圧空気は、流量300scfm(standard cubic feet per minute)、空気温度27℃(80°F)でノズルの入口端部(収束部分)に導入した。不織ウェブ製品を集積、分析したところ、以下の製品特性を有することが分かった。スパンボンド層/サブミクロ繊維層/スパンボンド層構造全体の基本重量は17.2gsm。本発明のノズル装置で生産された繊維含有率は推定約15%(2.7gsm)。サブミクロ繊維層における繊維の平均直径は0.45ミクロン、標準偏差は0.15、サブミクロ繊維の直径分布の平均に対する標準偏差の比率は0.33、繊維径の範囲は0.1ミクロンから0.85ミクロン。
(1) 不織ウェブを作るプロセスにおいて、
加圧ガス流が、第1および第2の対向壁部の間に制限されているガス通路内を流れ、
これら対向壁部の少なくとも一方が、加熱されており、
前記ガス通路は、前記ガスが供給端部から流入する第1の上流側部分、移行領域、および前記ガスが出口端部へと流れる第2の下流側部分を備えており、
前記移行領域が、前記第1部分を前記第2部分に流体接続しており、
前記ガス通路は、前記第2部分の前記出口端部で終端しており、
前記ガス通路の前記第1部分は、前記供給端部から前記移行領域まで断面積が減少しており、前記ガス通路の前記第2部分は、前記移行領域から前記第2部分の前記出口端部まで断面積が増加しており、
少なくとも1つのポリマー流体流が、少なくとも1つの、境界が定められたポリマー通路を通って流れており、
前記ポリマー通路は、前記対向加熱壁部の少なくとも一方に設けられた少なくとも1つの開口部において終端しており、
各ポリマー流体流は、前記開口部の各々からフィルムの形態で押し出されており、
各押し出されたポリマーフィルムは、前記ガス流に加わり、前記ポリマーフィルムは、フィブリル化されて、直径がサブミクロンの繊維を含む、前記ガス通路の前記第2部分の前記出口端部から出ていく繊維を形成する、プロセス。
前記ガス流は、約150キログラム/時間/メーターから、約3500キログラム/時間/メーターまでの範囲の質量流量で前記ガス通路に導入される、プロセス。
(3) 実施態様1に記載のプロセスにおいて、
前記ガス流および前記ポリマー流体流は、約40:1より低いガス流/ポリマー流体流の質量流量比で導入される、プロセス。
(4) 実施態様1に記載のプロセスにおいて、
前記ガス通路の入口における前記ガス流は、温度が50℃より低い、プロセス。
(5) 実施態様1に記載のプロセスにおいて、
前記不織ウェブ材は、直径がサブミクロンの繊維を35%より多く含んでいる、プロセス。
(6) 実施態様1に記載の不織ウェブにおいて、
繊維径分布の標準偏差が約0.5ミクロンより小さい、不織ウェブ。
繊維径分布の標準偏差が約0.3ミクロンよりも小さい、不織ウェブ。
(8) 実施態様1に記載のプロセスにおいて、
前記繊維は、ポリオレフィン、ポリエステル、ポリアミド、生物分解性ポリマー、ポリウレタン、ポリスチレン、アルキド樹脂、ポリヒドロキシアルカン酸(polyhydroalkanoic acids)、およびこれらの組合せからなる群から選択されたポリマーからなる、プロセス。
加圧ガス流が、第1および第2の対向壁部の間に制限されているガス通路内を流れ、
これら対向壁部の少なくとも一方が、加熱されており、
前記ガス通路は、前記ガスが供給端部から流入する第1の上流側部分、移行領域、および前記ガスが出口端部へと流れる第2の下流側部分を備えており、
前記移行領域が、前記第1部分を前記第2部分に流体接続しており、
前記ガス通路は、前記第2部分の前記出口端部で終端しており、
前記ガス通路の前記第1部分は、前記供給端部から前記移行領域まで断面積が単調に減少しており、前記ガス通路の前記第2部分は、前記移行領域から前記第2部分の前記出口端部まで断面積が単調に増加しており、
少なくとも1つのポリマー流体流が、少なくとも1つの、境界が定められたポリマー通路を通って流れており、
前記ポリマー通路は、前記対向加熱壁部の少なくとも一方にある少なくとも1つの開口部において終端しており、
各ポリマー流体流は、前記開口部の各々からフィルムの形態で押し出されており、
各押し出されたポリマーフィルムは、前記ガス通路の前記第2部分において前記ガス流に加わり、前記ポリマーフィルムは、フィブリル化されて、サブミクロン繊維を含む、前記ガス通路の前記第2部分の前記出口端部から出ていく繊維を形成する、プロセス。
各ポリマー通路開口部は、スリットであり、
前記スリットの水力直径は、前記ポリマー通路開口部の断面積の4倍を前記ポリマー通路開口部の内周で割ったものと定義され、
各ポリマー通路開口部の前記水力直径は、約0.025mm(0.001インチ)から約2.540mm(0.100インチ)までの範囲である、プロセス。
(11) 実施態様10に記載のプロセスにおいて、
前記ポリマーフィルムは、前記ポリマー通路開口部の前記水力直径を超えないポリマーフィルムの厚さを有する、プロセス。
(12) 実施態様11に記載のプロセスにおいて、
前記第1および第2の壁部の間の角度を二等分するものとして定義される第1二等分面が、前記第1部分をほぼ等しい体積の二つの半部に幾何学的に分割し、前記第1および第2の壁部の間の角度を二等分するものとして定義される第2二等分面が前記第2部分をほぼ等しい体積の二つの半部に幾何学的に分割する、プロセス。
前記第1および第2の壁部の前記第1二等分面に対する前記二等分角は、前記第1部分において約15度から約40度までの範囲であり、
前記第1および第2の壁部の前記第2二等分面に対する前記二等分角は、前記ガス通路の前記第2部分において約2度から約20度までの範囲である、プロセス。
(14) 実施態様13に記載のプロセスにおいて、
前記ガス通路の前記第1および第2の壁部は、前記第1および第2の二等分面に対して対称な温度状態となるようにほぼ同一の温度に加熱される、プロセス。
(15) 実施態様14に記載のプロセスにおいて、
前記対向加熱壁部の少なくとも一方に、ポリマーフィルムが1つだけ形成され、
ポリマーフィルムが押し出されるポリマー通路開口部の各々が、前記移行領域と前記第2部分の前記出口端部との間に広がる、前記ポリマー通路を含んでいる前記加熱壁部の長さに対して定められた、第2部分の上側半部に配置されている、プロセス。
前記ガス通路の前記第1および第2の壁部は、滑らかに湾曲しており、前記ガス通路の前記移行領域において、前記第1部分における前記対向壁部の湾曲が、いかなる鋭利な角部もなく、前記第2部分における前記対向壁部の湾曲に滑らかに移行する、プロセス。
(17) 実施態様11に記載のプロセスにおいて、
前記対向壁部の一方が熱い壁部であり、他方の壁部が冷たい壁部であり、前記熱い壁部の温度は前記冷たい壁部より少なくとも50℃高く、前記熱い壁部のみが少なくとも1つのポリマー流体通路開口部を有する、プロセス。
(18) 実施態様17に記載のプロセスにおいて、
前記第1部分における前記第1の二等分面に対する前記第1および第2の壁部の前記二等分角は、約15度から約40度までの範囲である、プロセス。
前記第2部分における前記熱い壁部は、約1度から20度までの範囲の角度で前記第1の二等分面から離れ、前記第2部分における前記冷たい壁部は、約0.1度から約15度までの範囲の角度で前記第1の二等分面の方に近づく、プロセス。
(20) 実施態様19に記載のプロセスにおいて、
前記第1の二等分面に対する前記熱い壁部の広がり角と、前記第1の二等分面に対する前記冷たい壁部の収束角との比は、約1:1から約500:1までの範囲にある、プロセス。
(21) 実施態様9に記載のプロセスにおいて、
各ポリマー通路の中心線と、対応するポリマー通路開口部を含む前記壁部との間の角度は、約10度から約100度までの範囲にある、プロセス。
(22) 実施態様21に記載のプロセスにおいて、
各ポリマー通路開口部から押し出された前記ポリマーフィルムは、前記ガス流と共にポリマー繊維化面に沿って流れ、
前記ポリマー繊維化面の前記第1の二分割面に対する配向角度は、時計方向に測って約90度から、反時計方向に測って約45度までの範囲にある、プロセス。
各ポリマー通路開口部に対応する前記ポリマー繊維化面の長さは、前記対応するポリマー通路開口部の前記水力直径の約1000倍よりも小さい、プロセス。
(24) 実施態様23に記載のプロセスにおいて、
前記ガス通路の前記第1および第2の壁部は、滑らかに湾曲しており、前記ガス通路の前記移行領域において、前記第1部分における前記対向壁部の湾曲が、鋭利な角部が全くなく、前記第2部分における前記対向壁部の湾曲に滑らかに移行する、プロセス。
(25) 実施態様24に記載のプロセスにおいて、
前記ガス通路の前記第2部分における前記対向壁部は湾曲していて、前記ガス通路の前記第2部分の内部から見たときに、前記熱い壁部は、前記第2の二等分面から離れるように湾曲する凸形状をしており、前記冷たい壁部は、前記第2の二等分面の方に湾曲する凹形状をしている、プロセス。
前記ガス通路の前記第2部分における、前記熱い壁部の曲率半径の前記冷たい壁部の曲率半径に対する比は、約1:10000から約100:1までの範囲にある、プロセス。
(27) 実施態様11に記載のプロセスにおいて、
前記不織ウェブは、直径が約1ミクロンより小さい繊維を99%より多く含む、プロセス。
(28) 実施態様11に記載のプロセスにおいて、
前記ガス流は、約150キログラム/時間/メーターから約3500キログラム/時間/メーターまでの範囲の質量流量で前記ガス通路に導入される、プロセス。
(29) 実施態様11に記載のプロセスにおいて、
前記ガス流および前記ポリマー流体流は、約40:1よりも小さいガス流/ポリマー流体流の質量流量比で前記第2部分に導入される、プロセス。
(30) 実施態様11に記載のプロセスにおいて、
前記ガス通路の入口における前記ガス流は、温度が50℃より低い、プロセス。
前記不織ウェブ材は、サブミクロンの繊維を35%より多く含んでいる、プロセス。
(32) 実施態様11に記載のプロセスにおいて、
別個の、境界が定められたポリマー通路を通って流れる異なるポリマー流体流として、複数の異なるポリマー材料を提供すること、
をさらに含み、
前記別個の、境界が定められたポリマー通路は、前記対向加熱壁部の少なくとも一方に設けられた開口部において終端しており、
前記異なるポリマー流体流は、前記開口部の各々からフィルム形態で押し出され、前記不織ウェブ材は複数成分の繊維を含む、プロセス。
(33) 実施態様9に記載のプロセスの不織ウェブ製品。
(34) 実施態様9に記載のプロセスの不織ウェブ製品において、
繊維径分布の標準偏差が、約0.5ミクロンよりも小さい、不織ウェブ製品。
(35) 実施態様9に記載のプロセスの不織ウェブ製品において、
繊維径分布の標準偏差が、約0.3ミクロンよりも小さい、不織ウェブ製品。
前記繊維は、ポリオレフィン、ポリエステル、ポリアミド、生物分解性ポリマー、ポリウレタン、ポリスチレン、アルキド樹脂、ポリヒドロキシアルカン酸(polyhydroalkanoic acids)、およびこれらの組合せからなる群から選択されたポリマーからなる、不織ウェブ製品。
(37) 実施態様33に記載の不織ウェブ製品を含む物品。
(38) 実施態様37に記載の物品において、
前記物品は、フィルター、医療用衣服、医療用クリーニングワイプ(medical cleaning wipes)、ハウスラップ(housewrap)構築材、包帯、防護服、バッテリーセパレータ、触媒担体、おむつ、トレーニングパンツ、大人向け失禁パッド、婦人用ケアパッドおよびおりものシートのような月経製品、タンポン、個人用クリーニング用品、個人用ケア用品、および、ベビーワイプ(baby wipe)、顔用ワイプ(facial wipes)、ボディワイプ(body wipes)および婦人用ワイプ(feminine wipes)のような個人用ケアワイプ(personal care wipes)、ならびにこれらの組合せからなる群から選択される、物品
ガス通路を画定する第1および第2の対向壁部であって、
前記壁部の少なくとも一方が、加熱可能であり、
前記ガス通路は、加圧ガス源からの加圧ガスを受け入れ、前記加圧ガスをガス流としてノズル内部で上流から下流の方向に流すように作動することができ、
前記ガス通路は、供給端から前記ガスが流入する第1上流側部分、移行領域、および前記ガスが出口端へと流れる第2下側部分を備え、
前記移行領域が、前記第1部分を前記第2部分に流体接続しており、
前記ガス通路が、前記第2部分の出口端で終端しており、
前記ガス通路の前記第1部分は、前記供給端から前記移行領域へと減少する断面積を有し、前記ガス通路の前記第2部分は、前記移行領域から前記第2部分の前記出口端へ増大する断面積を有する、
第1および第2の対向壁部と、
少なくとも1つの、境界が定められたポリマー通路であって、
前記ポリマー通路は、ポリマー押出機から溶融ポリマーを受け入れ、前記溶融ポリマーを、少なくとも1つの流動可能なポリマー流体流として、前記ガス通路に設けられた前記加熱壁部の少なくとも一方まで流すように作動することができ、
前記ポリマー通路は、前記対向加熱可能壁部の少なくとも1つにおける少なくとも1つの開口部において終端しており、
前記開口部の各々は、加熱可能壁部に、ポリマー流体流をフィルム形態で押し出すように作動することができ、
前記フィルムは、前記ガス通路の前記ガス流に加わって、前記ポリマーフィルムをフィブリル化して、サブミクロンの繊維を含む、前記ガス通路の前記第2部分の前記出口端から出ていく繊維を形成することができる、
少なくとも1つの、境界が定められたポリマー通路と、
を備える、装置。
ポリマーフィルムが押し出される前記少なくとも1つのポリマー通路開口部は、前記ガス通路の前記第2部分に配置されている、装置。
(41) 実施態様39に記載の装置において、
ポリマーフィルムが押し出される前記少なくとも1つのポリマー通路開口部は、前記移行領域と前記第2部分の前記出口端との間に広がる、前記ポリマー通路を含む前記加熱壁部の長さに対して定められた、第2部分の下側下流半部に配置されている、装置。
Claims (19)
- 不織ウェブ製品において、
サブミクロン繊維を含む少なくとも1つの繊維性ウェブを含み、
前記サブミクロン繊維は、10kg/hr/m〜200kg/hr/mのポリマー生産量で得られるフィブリル化されたポリマー溶融フィルム製品を含み、0.5ミクロンより小さい繊維径分布の標準偏差を有しており、
前記繊維性ウェブは、1平方ミリメーター当りの平均粒子数が10ショット未満のショット量を有し、前記ショットは、最大の寸法が10ミクロン〜500ミクロンの範囲にある、球形、楕円形、またはこれらの組合せの形状となっている不連続なポリマーの塊を含み、
前記繊維性ウェブは、15ミクロン未満の平均孔径を有する、不織ウェブ製品。 - 請求項1に記載の不織ウェブ製品において、
前記繊維性ウェブの前記サブミクロン繊維は、0.3ミクロン未満の繊維径分布の標準偏差を有する、不織ウェブ製品。 - 請求項1に記載の不織ウェブ製品において、
前記サブミクロン繊維は、0.1ミクロン〜0.9ミクロンの平均繊維径を有する、不織ウェブ製品。 - 請求項1に記載の不織ウェブ製品において、
前記不織ウェブ製品の35%以上が、前記サブミクロン繊維で構成されている、不織ウェブ製品。 - 請求項1に記載の不織ウェブ製品において、
前記不織ウェブ製品の75%以上が、前記サブミクロン繊維で構成されている、不織ウェブ製品。 - 請求項1に記載の不織ウェブ製品において、
前記不織ウェブ製品の95%以上が、前記サブミクロン繊維で構成されている、不織ウェブ製品。 - 請求項1に記載の不織ウェブ製品において、
前記不織ウェブ製品は、0.01gsm〜200gsmの基本重量を有する、不織ウェブ製品。 - 請求項7に記載の不織ウェブ製品において、
前記不織ウェブ製品は、0.1gsm〜50gsmの基本重量を有する、不織ウェブ製品。 - 請求項1に記載の不織ウェブ製品において、
前記サブミクロン繊維は、ポリオレフィン、ポリエステル、ポリアミド、生物分解性ポリマー、ポリウレタン、ポリスチレン、アルキド樹脂、ポリヒドロキシアルカン酸、およびこれらの組合せからなる群から選択されたポリマーから構成される、不織ウェブ製品。 - 請求項1に記載の不織ウェブ製品において、
前記ポリマーの生産量は、25kg/hr/m〜70kg/hr/mである、不織ウェブ製品。 - 物品において、
請求項1に記載の不織ウェブ製品と、少なくとも1つの異なる層との組合せ、
を含む、物品。 - 請求項11に記載の物品において、
前記異なる層は、スパンボンド層を含む、物品。 - 請求項11に記載の物品において、
前記物品は、フィルター、医療用衣服、医療用クリーニングワイプ、ハウスラップ構築材、包帯、防護服、バッテリーセパレータ、触媒担体、おむつ、トレーニングパンツ、大人向け失禁パッド、月経製品、タンポン、個人用クリーニング用品、個人用ケア用品、および、個人用ケアワイプ、ならびにこれらの組合せからなる群から選択される、物品。 - 不織ウェブ製品を作るプロセスにおいて、
スロットの対向する第1および第2の壁部の少なくとも一方の加熱された壁部における少なくとも1つの開口部で終端している少なくとも1つの、境界が定められたポリマー通路を通して、少なくとも1つのポリマー流体流を流すことであって、
各ポリマー流体流は、各前記開口部からフィルムの形態で押し出されて、加熱された壁部表面上に押し出されたポリマーフィルムを提供し、
前記スロットの総ポリマー生産量は、10kg/hr/m〜200kg/hr/mである、
少なくとも1つのポリマー流体流を流すことと、
各押し出されたポリマーフィルムを前記対向する第1および第2の壁部の間で制限されたガス通路内部を流れる加圧ガス流と組合せて、前記ポリマーフィルムをフィブリル化して、前記ガス通路の出口端部から出るサブミクロン径繊維を含む繊維を形成し、前記サブミクロン繊維を含む繊維性ウェブを形成することと、
を含み、
前記繊維性ウェブの前記サブミクロン繊維は、0.5ミクロン未満の繊維径分布の標準偏差を有し、
前記繊維性ウェブは、1平方ミリメーター当りの平均粒子数が10ショット未満のショット量を有し、前記ショットは、最大の寸法が10ミクロン〜500ミクロンの範囲にある、球形、楕円形、またはこれらの組合せの形状となっている不連続なポリマーの塊を含み、
前記繊維性ウェブは、15ミクロン未満の平均孔径を有する、プロセス。 - 請求項14に記載のプロセスにおいて、
前記繊維性ウェブの前記サブミクロン繊維は、0.3ミクロン未満の繊維径分布の標準偏差を有する、プロセス。 - 請求項14に記載のプロセスにおいて、
前記不織ウェブの35%以上が、前記サブミクロン繊維で構成される、プロセス。 - 請求項14に記載のプロセスにおいて、
前記不織ウェブ製品は、0.1gsm〜50gsmの基本重量を有する、プロセス。 - 請求項14に記載のプロセスにおいて、
前記サブミクロン繊維は、ポリオレフィン、ポリエステル、ポリアミド、生物分解性ポリマー、ポリウレタン、ポリスチレン、アルキド樹脂、ポリヒドロキシアルカン酸、およびこれらの組合せからなる群から選択されたポリマーから構成される、プロセス。 - 不織ウェブ製品を作るプロセスにおいて、
スロットの対向する第1および第2の壁部の少なくとも一方の加熱された壁部における少なくとも1つの開口部で終端している少なくとも1つの、境界が定められたポリマー通路を通して、少なくとも1つのポリマー流体流を流すことであって、
各ポリマー流体流は、各前記開口部からフィルムの形態で押し出されて、加熱された壁部表面上に押し出されたポリマーフィルムを提供し、
前記スロットの総ポリマー生産量は、10kg/hr/m〜200kg/hr/mである、
少なくとも1つのポリマー流体流を流すことと、
各押し出されたポリマーフィルムを前記対向する第1および第2の壁部の間で制限されたガス通路内部を流れる加圧ガス流と組合せて、前記ポリマーフィルムをフィブリル化して、前記ガス通路の出口端部から出るサブミクロン径繊維を含む繊維を形成し、前記サブミクロン繊維を含む繊維性ウェブを形成することであって、
前記ガス通路は、前記ガスが供給端部から流入する第1の上流側部分、移行領域、および前記ガスが前記出口端部へと流れる第2の下流側部分を備えており、
前記移行領域が、前記第1部分を前記第2部分に流体接続しており、
前記ガス通路は、前記第2部分の前記出口端部で終端しており、
前記ガス通路の前記第1部分は、前記供給端部から前記移行領域まで断面積が減少しており、前記ガス通路の前記第2部分は、前記移行領域から前記第2部分の前記出口端部まで断面積が増加している、
繊維性ウェブを形成することと、
を含み、
前記繊維性ウェブの前記サブミクロン繊維は、0.5ミクロン未満の繊維径分布の標準偏差を有し、
前記繊維性ウェブは、1平方ミリメーター当りの平均粒子数が10ショット未満のショット量を有し、前記ショットは、最大の寸法が10ミクロン〜500ミクロンの範囲にある、球形、楕円形、またはこれらの組合せの形状となっている不連続なポリマーの塊を含み、
前記繊維性ウェブは、15ミクロン未満の平均孔径を有する、プロセス。