JP2012072347A - Surface protecting sheet - Google Patents

Surface protecting sheet Download PDF

Info

Publication number
JP2012072347A
JP2012072347A JP2011025606A JP2011025606A JP2012072347A JP 2012072347 A JP2012072347 A JP 2012072347A JP 2011025606 A JP2011025606 A JP 2011025606A JP 2011025606 A JP2011025606 A JP 2011025606A JP 2012072347 A JP2012072347 A JP 2012072347A
Authority
JP
Japan
Prior art keywords
sheet
hand
cut
film
shock
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2011025606A
Other languages
Japanese (ja)
Inventor
Naoki Kusakabe
直己 日下部
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nitoms Inc
Original Assignee
Nitoms Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nitoms Inc filed Critical Nitoms Inc
Priority to JP2011025606A priority Critical patent/JP2012072347A/en
Publication of JP2012072347A publication Critical patent/JP2012072347A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To inexpensively provide a surface protecting sheet which is easy in handling.SOLUTION: In a surface protecting sheet which is stuck onto an adherend to be protected and protects the adherend against external impact, the surface protecting sheet is specified by the followings. The surface protecting sheet is obtained by sandwiching both faces of a prescribed width of an impact-absorbing sheet having an impact-absorbing property, with hand-tearable films having a hand-tearing property. Either of the hand-tearable films has a self-adhesive face to be stuck onto the adherend, more particularly, both the faces of the impact-absorbing sheet 2 are sandwiched with the hand-tearable films 3, 4, where the self-adhesive face 41 to be stuck onto the adherend is formed on either hand-tearable film 4.

Description

本発明は、例えば引越などの際に家具や壁面などが傷つかないよう保護するための表面保護シートに関し、さらに詳しく言えば、より取り扱いが簡単な表面保護シートに関する。   The present invention relates to a surface protective sheet for protecting furniture and wall surfaces from being damaged, for example, when moving, and more particularly to a surface protective sheet that is easier to handle.

例えば特許文献１には、引越などの搬出入時に家具や家屋のサッシなどを傷つけないようにするための開口枠保護シート（いわゆる養生シート）が提案されている。この表面保護シートは、発泡ポリエチレン製のシート基材からなり、裏面の両端に沿って粘着剤層を設けることで、被貼着体に貼り付けることができるようになっている。   For example, Patent Document 1 proposes an opening frame protection sheet (so-called curing sheet) for preventing damage to furniture, a sash of a house, or the like during carry-in / out such as moving. The surface protective sheet is made of a foamed polyethylene sheet base material, and can be attached to an adherend by providing an adhesive layer along both ends of the back surface.

表面保護シートは、テープ幅が異なるバリエーションが用意されており、細幅タイプは窓枠サッシなどに用いられ、幅広タイプは、家具や柱全体を巻いて覆うことができるようになっている。   Variations with different tape widths are available for the surface protection sheet. The narrow type is used for window frame sashes and the like, and the wide type can cover and cover furniture and pillars as a whole.

しかしながら、従来の表面保護シートは、発泡シートのみで構成されおり、強度が弱いため、ちょっとした衝撃や引っ掛かりで、破れてしまうことがあった。さらには、発泡シートは、手切れ性を持たないため、手で切ろうとすると、斜め裂けしやすく、カッターやハサミなどの切断具を用いて切断する必要があった。   However, the conventional surface protection sheet is composed only of a foam sheet and has a low strength, and may be torn by a slight impact or catch. Furthermore, since the foam sheet does not have a hand cutting property, it is easy to tear diagonally when it is cut by hand, and it has been necessary to cut it using a cutting tool such as a cutter or scissors.

さらには、従来の表面保護シートは、粘着面を保護するために剥離紙が貼り付けられており、剥離紙を剥がし取りながら、被貼着体に貼り付けるため、その貼り付け作業が面倒になる。また、剥離紙を設ける分、コストが高くなるばかりでなく、使用後の剥離紙を処分しなければならない。   Furthermore, the conventional surface protection sheet has a release paper attached to protect the adhesive surface, and is attached to the adherend while removing the release paper, which makes the attaching operation troublesome. . In addition, since the release paper is provided, the cost is increased, and the used release paper must be disposed of.

特開２００１−２０７６４８号公報JP 2001-207648 A

そこで、本発明は上述した課題を解決するためになされたものであって、その目的は、より取り扱いが簡単な表面保護シートを安価に提供することにある。   Then, this invention was made | formed in order to solve the subject mentioned above, The objective is to provide the surface protection sheet which is easier to handle at low cost.

上述した目的を達成するため、本発明は以下に示すいくつかの特徴を備えている。請求項１に記載の発明は、保護対象となる被貼着体の表面に貼り付けられ、外部の衝撃から上記被貼着体を保護する表面保護シートにおいて、衝撃吸収性を有する所定幅の衝撃吸収シートの両面を、幅方向に手切れ性を有する手切れ性フィルムで挟み込むとともに、いずれか一方の上記手切れ性フィルムには、上記被貼着体に貼り付けるための粘着面が設けられていることを特徴としている。   In order to achieve the above-described object, the present invention has several features described below. The invention according to claim 1 is a surface protective sheet that is affixed to the surface of an adherend to be protected and protects the adherend from an external impact. While sandwiching both sides of the absorbent sheet with a hand-cut film having a hand-cut property in the width direction, either one of the hand-cut films is provided with an adhesive surface for sticking to the adherend. It is characterized by being.

請求項２に記載の発明は、上記請求項１において、上記衝撃吸収シートは、発泡体シートと、内部に空気層を有する緩衝材シートとを重ね合わせたものからなることを特徴としている。   A second aspect of the present invention is characterized in that, in the first aspect, the impact absorbing sheet is formed by superposing a foam sheet and a cushioning sheet having an air layer therein.

請求項３に記載の発明は、上記請求項１または２において、いずれか他方の上記手切れ性フィルムの表面には、上記粘着面に対する粘着力を弱める処理が施されており、上記他方の手切れ性フィルムの表面に上記一方の上記手切れ性フィルムの上記粘着面が接触するようにロール状に巻回することを特徴としている。   A third aspect of the present invention is the method according to the first or second aspect, wherein the surface of either one of the hand-cut films is subjected to a treatment for weakening the adhesive force to the adhesive surface. It rolls in the shape of a roll so that the said adhesive surface of said one said hand-cut film may contact the surface of a film.

請求項４に記載の発明は、上記請求項１，２または３において、上記粘着面は、再剥離可能な粘着剤からなることを特徴としている。   According to a fourth aspect of the present invention, in the first, second, or third aspect, the pressure-sensitive adhesive surface is made of a detachable pressure-sensitive adhesive.

請求項５に記載の発明は、上記請求項１ないし４のいずれか１項において、上記一方の手切れ性フィルムは、一方向に手切れ性を有する一軸延伸フィルムからなり、上記他方の手切れ性フィルムは、二方向に手切れ性を有する両面粘着テープからなることを特徴としている。   A fifth aspect of the present invention is the method according to any one of the first to fourth aspects, wherein the one hand-cut film is a uniaxially stretched film having a hand-cut property in one direction, and the other hand-cut film. The adhesive film is characterized by comprising a double-sided pressure-sensitive adhesive tape having hand cutting properties in two directions.

請求項６に記載の発明は、保護対象となる被貼着体の表面に貼り付けられ、外部の衝撃から上記被貼着体を保護する表面保護シートにおいて、衝撃吸収性を有する所定幅の衝撃吸収シートと、手切れ性を有する手切れ性フィルムとを有し、上記衝撃吸収シートの一部には、上記衝撃吸収シートの強度が弱められた脆弱部が所定方向に沿って筋状に形成されており、上記衝撃吸収シートの少なくとも一方の面に上記手切れ性フィルムが貼着されていることを特徴としている。   The invention according to claim 6 is a surface protective sheet that is affixed to the surface of an adherend to be protected and protects the adherend from an external impact. It has an absorbent sheet and a hand-cut film having a hand-cut property, and a weak part where the strength of the shock-absorbing sheet is weakened is formed in a streak shape along a predetermined direction in a part of the shock-absorbing sheet The hand-cut film is adhered to at least one surface of the shock absorbing sheet.

請求項７に記載の発明は、上記請求項６において、上記衝撃吸収シートは発泡体シートからなり、上記発泡体シートには、上記脆弱手段として格子状の凹凸加工が施されていることを特徴としている。   The invention according to claim 7 is characterized in that, in the above-mentioned claim 6, the shock absorbing sheet is made of a foam sheet, and the foam sheet is subjected to a grid-like unevenness process as the weakening means. It is said.

請求項８に記載の発明は、上記請求項６または７において、上記手切れ性フィルムは、縦方向および横方向の二方向に手切れ性を有する両面粘着テープからなることを特徴としている。   The invention described in claim 8 is characterized in that, in the above-mentioned claim 6 or 7, the hand-cut film is composed of a double-sided pressure-sensitive adhesive tape having hand-cut characteristics in two directions of the vertical direction and the horizontal direction.

請求項９に記載の発明は、請求項５または８において、上記衝撃吸収シートの上記両面粘着テープが貼着される面には、上記両面粘着テープとの密着性を高めるためのコロナ放電処理が施されていることを特徴としている。   The invention according to claim 9 is the corona discharge treatment for enhancing the adhesion with the double-sided pressure-sensitive adhesive tape on the surface of the shock-absorbing sheet to which the double-sided pressure-sensitive adhesive tape is attached, according to claim 9 or claim 8. It is characterized by being given.

本発明によれば、衝撃吸収シートの両面を手切れ性フィルムで挟む構造としたことにより、任意の位置で手で簡単に切り離すことが容易にできる。また、衝撃吸収シートを発泡体シートと緩衝材シートとを組み合わせたことで、より衝撃吸収性に富み、またシート自体の強度も向上する。さらには、他方の手切れ性フィルムの表面に粘着力を弱める処理が施されていることにより、従来のような剥離紙を必要とせず、ロール状に巻き取って保管することができ、より安価で貼り付け作業も簡単にできる。   According to the present invention, since both sides of the impact absorbing sheet are sandwiched by the hand-cut film, it can be easily separated by hand at an arbitrary position. Further, by combining the shock absorbing sheet with the foam sheet and the cushioning material sheet, the shock absorbing sheet is more excellent in shock absorbing property and the strength of the sheet itself is improved. Furthermore, because the surface of the other hand-cut film is treated to weaken the adhesive force, it can be rolled up and stored in a roll without the need for conventional release paper, making it cheaper. Easy pasting work.

また、衝撃吸収シートの一方の面に手切れ性フィルムを貼着するとともに、衝撃吸収シートに格子状の凹凸処理を施すことで、カッターなどを用いることなく、簡単に切断することがきる。さらには、衝撃吸収シートの両面粘着シートが貼着される面にコロナ放電処理を施すことで、微細な凹凸が形成され、衝撃吸収シートと手切れ性フィルムとの密着性を高めることができる。   In addition, by sticking a hand-cut film on one surface of the shock absorbing sheet and applying a lattice-shaped uneven treatment to the shock absorbing sheet, it can be easily cut without using a cutter or the like. Furthermore, by performing corona discharge treatment on the surface of the impact absorbing sheet to which the double-sided pressure-sensitive adhesive sheet is attached, fine irregularities are formed, and the adhesion between the impact absorbing sheet and the hand-cut film can be enhanced.

本発明の一実施形態に係る表面保護シートの模式的な斜視図。The typical perspective view of the surface protection sheet concerning one embodiment of the present invention. 上記表面保護シートの部分断面図。The fragmentary sectional view of the said surface protection sheet. 上記表面保護シートの第１変形例を示す部分断面図。The fragmentary sectional view which shows the 1st modification of the said surface protection sheet. 上記表面保護シートの第２変形例を示す部分断面図。The fragmentary sectional view which shows the 2nd modification of the said surface protection sheet.

次に、本発明の実施形態について図面を参照しながら説明する。図１および図２に示すように、この表面保護シート１は、衝撃吸収シート２と、衝撃吸収シート２の両面に沿って張り合わせられる手切れ性フィルム３，４とを備えており、手切れ性フィルム４の粘着面４１が手切れ性フィルム３の凹凸面３１に対して直に接触するようにロール状に巻回されている。   Next, embodiments of the present invention will be described with reference to the drawings. As shown in FIG. 1 and FIG. 2, the surface protection sheet 1 includes an impact absorbing sheet 2 and hand-cut films 3 and 4 that are bonded along both surfaces of the shock-absorbing sheet 2. The film 4 is wound in a roll shape so that the adhesive surface 41 of the film 4 is in direct contact with the uneven surface 31 of the hand-cut film 3.

衝撃吸収シート２は、発泡体樹脂をシート状に形成した発泡体シート２１と、内部に空気層２３を有する緩衝材シート２２とを重ね合わせたものからなる。発泡体シート２１は、ポリエチレン樹脂を所定倍率で発泡させた厚さ１．０ｍｍのシート体からなる。   The shock absorbing sheet 2 is formed by superposing a foam sheet 21 in which a foam resin is formed in a sheet shape and a cushioning sheet 22 having an air layer 23 inside. The foam sheet 21 is made of a 1.0 mm thick sheet body obtained by foaming a polyethylene resin at a predetermined magnification.

この例において、発泡体シート２１はポリエチレン製であるが、これ以外の材質であってもよい。また、シート厚さは１．０ｍｍであるが、好ましくは０．５ｍｍ超であることが好ましい。すなわち、厚さが０．５ｍｍ以下であると、発泡体シート２１と緩衝材シート２２とを熱融着によって一体化する際に発泡体シート２１が薄すぎて溶けてしまうため好ましくない。   In this example, the foam sheet 21 is made of polyethylene, but other materials may be used. The sheet thickness is 1.0 mm, preferably more than 0.5 mm. That is, when the thickness is 0.5 mm or less, the foam sheet 21 is too thin and melts when the foam sheet 21 and the buffer material sheet 22 are integrated by heat fusion, which is not preferable.

緩衝材シート２２は、凹凸ウエーブ状に形成されたキャップフィルム２２ａと、キャップフィルム２２ａの他方の面を塞ぐように一体的に貼り合わせられたバックフィルム２２ｂとを備えている。キャップフィルム２２ａとバックフィルム２２ｂは、ともにポリエチレン製である。   The cushioning material sheet 22 includes a cap film 22a formed in a concavo-convex wave shape, and a back film 22b bonded together so as to close the other surface of the cap film 22a. Both the cap film 22a and the back film 22b are made of polyethylene.

キャップフィルム２２ａとバックフィルム２２ｂとは、熱融着によって一体化されており、それらの間に空気層（気泡）２３が形成されている。空気層２３は、それぞれ独立した柱状に形成されており、緩衝材シート２２に所定の間隔で規則的、この例では、平面視で千鳥状に配置されている。   The cap film 22a and the back film 22b are integrated by heat fusion, and an air layer (bubble) 23 is formed between them. The air layers 23 are each formed in an independent columnar shape, and are regularly arranged at predetermined intervals on the cushioning material sheet 22, and in this example, are arranged in a staggered manner in a plan view.

この例において、緩衝材シート２２は、シート厚さが２．０〜４．０ｍｍであることが好ましい。すなわち、シート厚さが２．０ｍｍ未満だと、緩衝材としての衝撃吸収能力に劣るため好ましくない、逆にシート厚さが４．０ｍｍを越えると、強度が高くなりすぎ、形状に合わせて湾曲させたり、折り曲げたりしにくくなるため、好ましくない。   In this example, the cushioning material sheet 22 preferably has a sheet thickness of 2.0 to 4.0 mm. That is, if the sheet thickness is less than 2.0 mm, it is not preferable because the shock absorbing ability as a cushioning material is inferior. On the contrary, if the sheet thickness exceeds 4.0 mm, the strength becomes too high and curves according to the shape. This is not preferable because it is difficult to bend or bend.

この例において、発泡体シート２１と緩衝材シート２２とは、緩衝材シート２２のバックフィルム２２ｂ側で発泡体シート２１と熱融着によって一体化されている。これ以外に、例えば接着などによって一体化されてもよく、発泡体シート２１と緩衝材シート２２の貼り合わせ手段は仕様に応じて任意に選択されてよい。   In this example, the foam sheet 21 and the cushioning material sheet 22 are integrated with the foam sheet 21 on the back film 22b side of the cushioning material sheet 22 by heat fusion. In addition to this, for example, it may be integrated by adhesion or the like, and the means for bonding the foam sheet 21 and the cushioning material sheet 22 may be arbitrarily selected according to the specifications.

次に、一方の手切れ性フィルム３（以下、第１手切れ性フィルムとする）は、衝撃吸収シート２の一方の面（図２では上面）に沿って貼り付けられている。第１手切れ性フィルム３は、ポリエチレン製でフィルム厚さが１０〜２０μｍの樹脂フィルムからなり、幅方向（図１の矢印方向）に沿って手切れ性を有している。   Next, one hand-cut film 3 (hereinafter referred to as a first hand-cut film) is attached along one surface (the upper surface in FIG. 2) of the shock absorbing sheet 2. The first hand-cut film 3 is made of a resin film made of polyethylene and having a film thickness of 10 to 20 μm, and has hand-cut characteristics along the width direction (the arrow direction in FIG. 1).

この例において、第１手切れ性フィルム３は、表面保護シート１の幅方向に手切れ性を持たせるため、一軸方向に延伸された一軸延伸フィルムが用いられている。なお、一軸延伸フィルム以外にも手切れ性を備えることができれば、その他の態様も本発明に含まれる。   In this example, the first hand-cut film 3 is a uniaxially stretched film that is stretched in the uniaxial direction so as to have a hand-cut property in the width direction of the surface protective sheet 1. It should be noted that other aspects are also included in the present invention as long as they can have hand cutting properties other than the uniaxially stretched film.

第１手切れ性フィルム３の表面には、図１に示すように、表面保護シート３をロール状に巻いた際に、他方の手切れ性フィルム４（以下、第２手切れ性フィルム４とする）の粘着面４１に対する粘着力を弱める処理としての凹凸処理が施された凹凸面３１が設けられている。   On the surface of the first hand-cut film 3, as shown in FIG. 1, when the surface protective sheet 3 is wound into a roll, the other hand-cut film 4 (hereinafter referred to as the second hand-cut film 4 and The concave / convex surface 31 is provided with a concave / convex treatment as a processing for weakening the adhesive force to the adhesive surface 41.

この例において、弱粘着化する方法としては、フィルム表面に凹凸処理を施すことにより行っているが、これ以外にローレット処理やエンボス処理など、粘着面４１に対する接触面積を減らす処理などがある。また、表面に剥離剤層を設けて易剥離処理など施してもよい。   In this example, as a method for weakly adhering, the film surface is subjected to a concavo-convex process, but there are other processes such as a knurling process or an embossing process for reducing the contact area with the adhesive surface 41. Alternatively, a release agent layer may be provided on the surface and subjected to easy peeling treatment or the like.

第１手切れ性フィルム３は、下層の発泡体シート２１と熱融着によって一体的に貼り合わせられているが、これ以外に粘着剤によって貼り合わされていてもよく、その方法は仕様に応じて任意に選択されてよい。   The first hand-cut film 3 is integrally bonded to the lower foam sheet 21 by heat-sealing, but may be bonded by an adhesive other than this, and the method depends on the specification. It may be arbitrarily selected.

次に、第２手切れ性フィルム４は、ポリエチレン製のフラットヤーンを編み込んでシート状に形成した、いわゆるクロステープであり、縦方向と横方向のいずれにも手切れ性を備えている。この例において、第２手切れ性フィルム３は、フィルム厚さが２０μｍであるが、フィルム厚さは仕様に応じて任意に設定されてよい。   Next, the second hand-cut film 4 is a so-called cross tape formed by weaving a polyethylene flat yarn into a sheet shape, and has hand-cut characteristics in both the vertical direction and the horizontal direction. In this example, the second hand-cut film 3 has a film thickness of 20 μm, but the film thickness may be arbitrarily set according to specifications.

第２手切れ性フィルム４の一方の面（図２では下面）には、表面保護シート１を被貼着体に貼り付けるための第１粘着面４１が設けられている。第１粘着面４１は、再剥離性を有する再剥離粘着剤、この例ではアクリル系粘着剤が一様に塗布されている。   A first adhesive surface 41 for attaching the surface protection sheet 1 to an adherend is provided on one surface (lower surface in FIG. 2) of the second hand-cut film 4. The first pressure-sensitive adhesive surface 41 is uniformly coated with a re-peelable pressure-sensitive adhesive having removability, in this example, an acrylic pressure-sensitive adhesive.

再剥離性粘着剤は、貼って剥がしてを繰り返しできるように、その粘着力が３〜５Ｎ／２５ｍｍとなるように調整されていることが好ましい。すなわち、粘着力が３Ｎ／２５ｍｍ未満の場合、粘着力が弱すぎてしまい、自重で剥がれ落ちてしまうおそれがあるため、好ましくない。逆に、粘着力が５Ｎ／２５ｍｍ超の場合、粘着力が大きすぎ、白木などに貼り付けた場合、白木の表面を破壊してしまうおそれがあるため、好ましくない。   The re-peelable pressure-sensitive adhesive is preferably adjusted so that its adhesive strength is 3 to 5 N / 25 mm so that it can be repeatedly applied and peeled off. That is, when the adhesive strength is less than 3 N / 25 mm, the adhesive strength is too weak and may be peeled off by its own weight. On the contrary, when the adhesive strength is more than 5 N / 25 mm, the adhesive strength is too large, and when pasted on a white wood or the like, the surface of the white wood may be destroyed.

第２手切れ性フィルム４の一方の面（図２では下面）には、第２手切れ性フィルム４を衝撃吸収シート２に貼り付けるための第２粘着面４２が設けられている。第２粘着面４２は、第１粘着面４１と同様のアクリル系粘着剤からなり、粘着力が６Ｎ／２５ｍｍとなるように一様に塗布されている。第２粘着面４２についても仕様に応じて任意に変更可能である。   On one surface (the lower surface in FIG. 2) of the second hand-cut film 4, a second adhesive surface 42 for attaching the second hand-cut film 4 to the shock absorbing sheet 2 is provided. The second adhesive surface 42 is made of the same acrylic adhesive as the first adhesive surface 41, and is uniformly applied so that the adhesive force is 6 N / 25 mm. The second adhesive surface 42 can be arbitrarily changed according to the specifications.

次に、本発明の表面保護シートの第１変形例について説明する。図３に示すように、この表面保護シート１ａは、衝撃吸収シート２と、衝撃吸収シート２の両面に沿って張り合わせられる手切れ性フィルム３，４とを備えている。この表面保護シート１ａも、一方の手切れ性フィルム４の粘着面４１が他方の手切れ性フィルム３の凹凸面３１に重なるようにロール状に巻回される。   Next, the 1st modification of the surface protection sheet of this invention is demonstrated. As shown in FIG. 3, the surface protection sheet 1 a includes an impact absorbing sheet 2 and hand-cut films 3 and 4 that are bonded along both sides of the impact absorbing sheet 2. This surface protective sheet 1 a is also wound in a roll shape so that the adhesive surface 41 of one hand-cuttable film 4 overlaps the uneven surface 31 of the other hand-cuttable film 3.

この例において、衝撃吸収シート２は、ポリエチレン発泡体シート単体から構成されている。これによれば、衝撃吸収シート２を発泡体シートのみで構築したことにより、衝撃吸収シートの強度が下がるのに伴い、手切れ性がさらによくなる。また、材料コストを抑えることもできる。   In this example, the shock absorbing sheet 2 is composed of a single polyethylene foam sheet. According to this, by constructing the shock absorbing sheet 2 with only the foam sheet, hand cutting performance is further improved as the strength of the shock absorbing sheet is lowered. In addition, material costs can be reduced.

上述した実施例と同様に、第１手切れ性フィルム３の表面には、表面保護シート３をロール状に巻いた際に、他方の手切れ性フィルム４（以下、第２手切れ性フィルム４とする）の粘着面４１に対する粘着力を弱める処理としての凹凸面３１が設けられている。第１手切れ性フィルム３および凹凸面３１については、先の実施形態と同様である。また、第２手切れ性フィルム４の構成についても上記実施形態と同様であるため、その説明は省略する。   Similar to the above-described example, when the surface protective sheet 3 is wound in a roll shape on the surface of the first hand-cut film 3, the other hand-cut film 4 (hereinafter, the second hand-cut film 4). The uneven surface 31 is provided as a process for weakening the adhesive force to the adhesive surface 41. About the 1st hand-cut film 3 and the uneven surface 31, it is the same as that of previous embodiment. Moreover, since it is the same as that of the said embodiment also about the structure of the 2nd hand cutting film 4, the description is abbreviate | omitted.

次に、第２変形例として、図４に示すように、この表面保護シート１ｂは、衝撃吸収シート２と、衝撃吸収シート２の一方の面（図４では下面）に沿って張り合わせられる手切れ性フィルム４とを備えている。   Next, as a second modification, as shown in FIG. 4, the surface protection sheet 1 b is a hand-cut piece that is bonded to the impact-absorbing sheet 2 along one surface (the lower surface in FIG. 4) of the impact-absorbing sheet 2. The film 4 is provided.

衝撃吸収シート２は、ポリエチレン発泡体シート単体から構成されている。この衝撃吸収シート２は、それ自体が所定方向に手切れ性を有するように格子状に凹凸加工が施されている。格子状に凹凸加工が施された衝撃吸収シート２は、その凹部の強度が他の部分に比べて低下することで、はさみやカッターを用いることなく、表面保護シート１ｂを手で簡単に切ることができる。   The impact absorbing sheet 2 is composed of a single polyethylene foam sheet. The shock-absorbing sheet 2 is concavo-convexly processed in a lattice shape so that the shock-absorbing sheet 2 itself has a hand cutting property in a predetermined direction. The impact-absorbing sheet 2 having a concavo-convex process in a lattice shape can easily cut the surface protection sheet 1b by hand without using scissors or a cutter because the strength of the recesses is lower than other parts. Can do.

さらには、凹凸加工によって反発が少なくなり、表面保護シート１ｂ全体が柔軟となる。その結果、手切れ性フィルム４の粘着面４１の粘着力を弱めても、柱などの直角面に沿って剥がすこともできる。さらに、白木などの傷つきやすい面にも用いることができる。   Furthermore, repulsion is reduced by the uneven processing, and the entire surface protection sheet 1b becomes flexible. As a result, even if the adhesive force of the adhesive surface 41 of the hand-cut film 4 is weakened, it can be peeled off along a right angle surface such as a pillar. Furthermore, it can also be used on easily damaged surfaces such as Shiraki.

衝撃吸収シート２の手切れ性フィルム４が貼着される面には、コロナ放電処理が施されていることが好ましい。すなわち、衝撃吸収シート２の表面にコロナ放電処理することで、表面に微細な凹凸が形成されることで、ポリエチレン発泡体シートと手切れ性フィルム４の粘着面との密着性をより高めることができる。   It is preferable that the surface of the shock absorbing sheet 2 to which the hand-cut film 4 is attached is subjected to corona discharge treatment. That is, by performing corona discharge treatment on the surface of the shock absorbing sheet 2, fine irregularities are formed on the surface, thereby further improving the adhesion between the polyethylene foam sheet and the adhesive surface of the hand-cut film 4. it can.

この例において、手切れ性フィルム４は、上述した第２手切れ性フィルム４と同様に、縦方向と横方向の二方向に手切れ性を有するクロステープを基材として、その両面に粘着面が形成されら両面粘着テープが用いられているが、二方向に手切れ性を有する両面粘着テープであれば、その形態は仕様に応じて任意に選択されてよい。   In this example, the hand-cut film 4 is made of a cross tape having a hand-cut property in two directions, the vertical direction and the horizontal direction, as in the second hand-cut film 4 described above. However, as long as the double-sided pressure-sensitive adhesive tape is hand-cut in two directions, the form may be arbitrarily selected according to the specifications.

次に、本発明の表面保護テープについて、具体的な実施例を比較例とともに比較検討する。まず、以下の方法で表面保護シートのサンプルを作製した。空気層が設けられた緩衝材シートの一方の面に実施例と比較例の厚さの異なるポリエチレンの発泡体シートを貼り合わて衝撃吸収シートを作製した。   Next, specific examples of the surface protective tape of the present invention will be compared and examined together with comparative examples. First, a sample of the surface protection sheet was produced by the following method. An impact-absorbing sheet was prepared by bonding polyethylene foam sheets having different thicknesses in Examples and Comparative Examples to one surface of a cushioning material sheet provided with an air layer.

その各衝撃吸収シートの両面に上述した第１および第２手切れ性フィルムを貼り合わせたのち、以下の各評価試験を行った。   After the first and second hand-cut films described above were bonded to both surfaces of each impact absorbing sheet, the following evaluation tests were performed.

〔再剥離粘着力〕
まず、再剥離粘着力を測定するため、表面保護シートをステンレス板に貼り付けた後、ピーリング試験を行い、粘着力を測定した。
〔手切れ性フィルムとの密着力〕
次に、衝撃吸収シートと第１手切れ性シートとの熱融着による密着力を測定した。測定結果が、良好なものを○、不良なものを×として評価した。
〔シートの総合評価〕
また、表面保護シートの柔軟性および強度についても評価を行い、良好なものを○、不良なものを×として評価した。さらには、総合的な評価を行い、良好なものを○、不良なものを×として評価した。
以下に、その評価結果を示す。 [Re-peeling adhesive strength]
First, in order to measure the re-peeling adhesive strength, a surface protective sheet was attached to a stainless steel plate, and then a peeling test was performed to measure the adhesive strength.
[Adhesion with hand-cut film]
Next, the adhesive force by thermal fusion between the shock absorbing sheet and the first hand-cut sheet was measured. The measurement result was evaluated as “Good” when the measurement result was good, and “X” when the measurement result was poor.
[Comprehensive evaluation of sheet]
Further, the flexibility and strength of the surface protective sheet were also evaluated, and a good one was evaluated as “good” and a poor one as “poor”. Furthermore, comprehensive evaluation was performed, and a good one was evaluated as “◯” and a poor one as “×”.
The evaluation results are shown below.

《実施例１》
〔発泡体シート〕 １．０ｍｍ
〔再剥離粘着力〕 ３〜５Ｎ／２５ｍｍ
〔手切れ性フィルムとの密着力〕 ○
〔シート柔軟性〕 ○
〔シート強度〕 ○
〔総合判定〕 ○ Example 1
[Foam sheet] 1.0mm
[Re-peeling adhesive strength] 3-5N / 25mm
[Adhesion with hand-cut film] ○
[Sheet flexibility] ○
[Sheet strength] ○
[Comprehensive judgment] ○

〈比較例１〉
〔発泡体シート〕 なし
〔再剥離粘着力〕 ３〜５Ｎ／２５ｍｍ
〔手切れ性フィルムとの密着力〕 ×
〔シート柔軟性〕 ○
〔シート強度〕 ×
〔総合判定〕 × <Comparative example 1>
[Foam sheet] None [Re-peeling adhesive strength] 3 to 5 N / 25 mm
[Adhesion with hand-cut film] ×
[Sheet flexibility] ○
[Sheet strength] ×
[Comprehensive judgment] ×

〈比較例２〉
〔発泡体シート〕 ０．５ｍｍ
〔再剥離粘着力〕 ３〜５Ｎ／２５ｍｍ
〔手切れ性フィルムとの密着力〕 ×
〔シート柔軟性〕 ○
〔シート強度〕 ×
〔総合判定〕 × <Comparative example 2>
[Foam sheet] 0.5mm
[Re-peeling adhesive strength] 3-5N / 25mm
[Adhesion with hand-cut film] ×
[Sheet flexibility] ○
[Sheet strength] ×
[Comprehensive judgment] ×

〈比較例３〉
〔発泡体シート〕 ２．０ｍｍ
〔再剥離粘着力〕 ６〜８Ｎ／２５ｍｍ
〔手切れ性フィルムとの密着力〕 ○
〔シート柔軟性〕 ×
〔シート強度〕 ○
〔総合判定〕 × <Comparative Example 3>
[Foam sheet] 2.0mm
[Re-peeling adhesive strength] 6-8N / 25mm
[Adhesion with hand-cut film] ○
[Sheet flexibility] ×
[Sheet strength] ○
[Comprehensive judgment] ×

以下に、実施例１および比較例１〜３の結果のまとめを表１に示す。   A summary of the results of Example 1 and Comparative Examples 1 to 3 is shown in Table 1 below.

Figure 2012072347
Figure 2012072347

本発明によれば、以下の知見を得た。すなわち、発泡体シートの厚さが０．５ｍｍ以下とした場合、熱融着する際に発泡体シートが熱で溶けてしまうため、生産ができない。逆に、２．０ｍｍを越えると、シートの柔軟性がなくなり、再剥離性が乏しくなるが、粘着力を高めると、被貼着体を傷つけるおそれがあるため、好ましくない。   According to the present invention, the following knowledge was obtained. That is, when the thickness of the foam sheet is 0.5 mm or less, the foam sheet is melted by heat at the time of heat-sealing, and thus production cannot be performed. On the contrary, if the thickness exceeds 2.0 mm, the flexibility of the sheet is lost and the removability becomes poor. However, if the adhesive force is increased, the adherend may be damaged, which is not preferable.

この例において、表面保護シート１は、引越などの際に柱や家具などを傷から守る養生シートとして用いる点を例に説明したが、これ以外の用途として、幼児が家具や机などの尖った場所にぶつけて怪我をしないようにするための保護シートとしてもよい。また、自動車のボディの一部に貼り付けてもよい。   In this example, the surface protection sheet 1 has been described as an example of using as a curing sheet for protecting pillars and furniture from scratches when moving, etc. However, as an application other than this, an infant has a sharp point such as furniture or a desk It is good also as a protection sheet for hitting a place and preventing injury. Moreover, you may affix on a part of body of a motor vehicle.

さらには、衝撃吸収シート２は中間に空気層を備えているため、断熱効果がある。そこで、この表面保護シート１を窓ガラスやサッシ全体に貼り付けて、断熱シートとして用いてもよい。   Furthermore, since the shock absorbing sheet 2 has an air layer in the middle, it has a heat insulating effect. Therefore, the surface protective sheet 1 may be attached to the entire window glass or sash and used as a heat insulating sheet.

１，１ａ，１ｂ 表面保護シート
２ 衝撃吸収シート
２１ 発泡体シート
２２ 緩衝材シート
３ 第１手切れ性フィルム
４ 第２手切れ性フィルム 1, 1a, 1b Surface protective sheet 2 Impact absorbing sheet 21 Foam sheet 22 Buffer material sheet 3 First hand-cut film 4 Second hand-cut film

Claims (9)

保護対象となる被貼着体の表面に貼り付けられ、外部の衝撃から上記被貼着体を保護する表面保護シートにおいて、
衝撃吸収性を有する所定幅の衝撃吸収シートの両面を、手切れ性を有する手切れ性フィルムで挟み込むとともに、いずれか一方の上記手切れ性フィルムには、上記被貼着体に貼り付けるための粘着面が設けられていることを特徴とする表面保護シート。 In the surface protection sheet that is attached to the surface of the adherend to be protected and protects the adherend from external impacts,
While sandwiching both sides of a shock-absorbing sheet having a predetermined width having shock-absorbing properties with a hand-cutting film having hand-cutting properties, either one of the hand-cutting films is attached to the adherend. A surface protective sheet provided with an adhesive surface. 上記衝撃吸収シートは、発泡体シートと、内部に空気層を有する緩衝材シートとを重ね合わせたものからなることを特徴とする請求項１に記載の表面保護シート。   2. The surface protection sheet according to claim 1, wherein the impact absorbing sheet is composed of a foam sheet and a cushioning sheet having an air layer inside. いずれか他方の上記手切れ性フィルムの表面には、上記粘着面に対する粘着力を弱める処理が施されており、上記他方の手切れ性フィルムの表面に上記一方の上記手切れ性フィルムの上記粘着面が接触するようにロール状に巻回することを特徴とする請求項１または２に記載の表面保護シート。   The surface of any one of the above hand-cut films is subjected to a treatment for weakening the adhesive force to the above-mentioned adhesive surface, and the above-mentioned adhesive of the one above-mentioned hand-cut film on the surface of the other hand-cut film. The surface protective sheet according to claim 1 or 2, wherein the surface protective sheet is wound in a roll shape so that the surfaces come into contact with each other. 上記粘着面は、再剥離可能な粘着剤からなることを特徴とする請求項１，２または３項に記載の表面保護シート。   The surface protective sheet according to claim 1, 2 or 3, wherein the pressure-sensitive adhesive surface is made of a re-peelable pressure-sensitive adhesive. 上記一方の手切れ性フィルムは、一方向に手切れ性を有する一軸延伸フィルムからなり、上記他方の手切れ性フィルムは、二方向に手切れ性を有する両面粘着テープからなることを特徴とする請求項１ないし４のいずれか１項に記載の表面保護シート。   The one hand-cut film is composed of a uniaxially stretched film having hand-cut characteristics in one direction, and the other hand-cut film is composed of a double-sided pressure-sensitive adhesive tape having hand-cut characteristics in two directions. The surface protection sheet of any one of Claims 1 thru | or 4. 保護対象となる被貼着体の表面に貼り付けられ、外部の衝撃から上記被貼着体を保護する表面保護シートにおいて、
衝撃吸収性を有する所定幅の衝撃吸収シートと、手切れ性を有する手切れ性フィルムとを有し、上記衝撃吸収シートの一部には、上記衝撃吸収シートの強度が弱められた脆弱部が所定方向に沿って筋状に形成されており、上記衝撃吸収シートの少なくとも一方の面に上記手切れ性フィルムが貼着されていることを特徴とする表面保護シート。 In the surface protection sheet that is attached to the surface of the adherend to be protected and protects the adherend from external impacts,
A shock-absorbing sheet having a predetermined width having shock-absorbing properties, and a hand-cutting film having hand-cutting properties, and a weak portion where the strength of the shock-absorbing sheet is weakened is part of the shock-absorbing sheet. A surface protective sheet, which is formed in a streak shape along a predetermined direction, and wherein the hand-cut film is adhered to at least one surface of the shock absorbing sheet. 上記衝撃吸収シートは発泡体シートからなり、上記発泡体シートには、上記脆弱手段として格子状の凹凸加工が施されていることを特徴とする請求項６に記載の表面保護シート。   The surface protection sheet according to claim 6, wherein the impact absorbing sheet is made of a foam sheet, and the foam sheet is subjected to a grid-like unevenness process as the weakening means. 上記手切れ性フィルムは、縦方向および横方向の二方向に手切れ性を有する両面粘着テープからなることを特徴とする請求項６または７に記載の表面保護シート。   The surface protection sheet according to claim 6 or 7, wherein the hand-cut film comprises a double-sided pressure-sensitive adhesive tape having hand-cut characteristics in two directions, ie, a vertical direction and a horizontal direction. 上記衝撃吸収シートの上記両面粘着テープが貼着される面には、上記両面粘着テープとの密着性を高めるためのコロナ放電処理が施されていることを特徴とする請求項５または８に記載の表面保護シート。   The corona discharge treatment for improving the adhesiveness with the said double-sided adhesive tape is given to the surface to which the said double-sided adhesive tape of the said impact-absorbing sheet is affixed, The Claim 5 or 8 characterized by the above-mentioned. Surface protection sheet.
JP2011025606A 2010-09-03 2011-02-09 Surface protecting sheet Pending JP2012072347A (en)