JP2011156799A - 積層体 - Google Patents
積層体 Download PDFInfo
- Publication number
- JP2011156799A JP2011156799A JP2010021582A JP2010021582A JP2011156799A JP 2011156799 A JP2011156799 A JP 2011156799A JP 2010021582 A JP2010021582 A JP 2010021582A JP 2010021582 A JP2010021582 A JP 2010021582A JP 2011156799 A JP2011156799 A JP 2011156799A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- parts
- cement
- inorganic
- organic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】無機質基材及び有機質基材から選ばれる基材の少なくとも一方の面に、セメント100重量部に対し、発泡有機樹脂粒子を4〜40重量部、無機軽量粒子を5〜300重量部、及び吸熱物質を5〜800重量部含む組成物の硬化体からなる耐火断熱層を設ける。
【選択図】なし
Description
このように強度が低下したロックウール層では、衝撃、振動等の外力が加わると、層の剥離、脱落等が生じやすくなる。すなわち、ロックウール層において、断熱性と強度を両立することは難しいのが現状である。
セメント100重量部に対し、発泡有機樹脂粒子を4〜40重量部、無機軽量粒子を5〜300重量部、及び吸熱物質を5〜800重量部含む組成物の硬化体からなる耐火断熱層が設けられたことを特徴とする積層体。
2.無機質基材及び有機質基材から選ばれる基材の少なくとも一方の面に、
セメント100重量部に対し、発泡有機樹脂粒子を4〜40重量部、無機軽量粒子を5〜300重量部、及び吸熱物質を5〜800重量部含む組成物の硬化体からなる耐火断熱層、
厚さが0.05〜1mmである無機質薄層、
が順に設けられたことを特徴とする積層体。
3.無機質基材及び有機質基材から選ばれる基材の少なくとも一方の面に、
セメント100重量部に対し、発泡有機樹脂粒子を4〜40重量部、無機軽量粒子を5〜300重量部、吸熱物質を5〜800重量部、及び水を200〜1200重量部含む組成物を塗付し、硬化させることを特徴とする積層体の製造方法。
4.無機質基材及び有機質基材から選ばれる基材の少なくとも一方の面に、
セメント100重量部に対し、発泡有機樹脂粒子を4〜40重量部、無機軽量粒子を5〜300重量部、吸熱物質を5〜800重量部、水を200〜1200重量部、水溶性金属塩を0.5〜30重量部、及び水溶性高分子化合物を0.5〜30重量部含む組成物を塗付し、硬化させることを特徴とする積層体の製造方法。
発泡有機樹脂粒子としては、例えば、発泡スチロール、発泡ポリウレタン、発泡フェノール、発泡ポリエチレン、発泡ポリプロピレン、発泡ポリ塩化ビニル等の公知の発泡有機樹脂が挙げられ、これらの1種または2種以上が使用できる。本発明では、特に発泡スチロール粒子が好適である。
発泡有機樹脂粒子の平均粒子径は、通常1〜10mm程度である。また、発泡有機樹脂粉粒体のかさ密度は、通常0.08g/cm3以下であり、好ましくは0.03g/cm3以下、より好ましくは0.015g/cm3以下である。
このような難燃性に優れる有機樹脂を使用する場合において、さらに難燃剤を添加することもできる。
上記アルコキシシラン化合物としては限定的でなく、例えばテトラメトキシシラン、テトラエトキシシラン、メチルトリメトキシシラン、メチルトリエトキシシラン、エチルトリメトキシシラン、エチルトリエトキシシラン、ジメチルジメトキシシラン、ジメチルジエトキシシラン、ジエチルジメトキシシラン、ジエチルジエトキシシラン等が使用できる。
このような吸熱物質としては、例えば、
水酸化アルミニウム、水酸化マグネシウム、水酸化カルシウム、水酸化バリウム、水酸化ストロンチウム、水酸化スカンジウム等の金属水酸化物;
ホウ砂(四ホウ酸ナトリウム)、八ホウ酸二ナトリウム、ホウ酸亜鉛等の金属ホウ酸塩;
ゼオライト、ハロイサイト、アロフェン、エトリンジャイト等が挙げられ、これらの1種または2種以上が使用できる。吸熱物質としては、特に金属水酸化物が好適である。
このような水溶性金属塩としては、例えば、
硫酸アンモニウムアルミニウム、硫酸ナトリウムアルミニウム、硫酸アルミニウム、硫酸カリウムアルミニウム、硫酸鉄、硫酸カリウム鉄、硫酸マグネシウム、硫酸ニッケル、硫酸亜鉛、硫酸ベリリウム、硫酸ジルコニウム等の金属硫酸塩;
リン酸アルミニウム、リン酸コバルト、リン酸マグネシウム、リン酸マグネシウムアンモニウム、リン酸水素マグネシウム、リン酸亜鉛、リン酸二水素亜鉛等の金属リン酸塩;
硝酸アルミニウム、硝酸亜鉛、硝酸カルシウム、硝酸コバルト、硝酸ビスマス、硝酸ジルコニウム、硝酸セリウム、硝酸鉄、硝酸鉄、硝酸ニッケル、硝酸マグネシウム等の金属硝酸塩;
酢酸亜鉛、酢酸コバルト等の金属酢酸塩;
塩化カルシウム、塩化アルミニウム、塩化コバルト、塩化鉄等の金属塩化物塩、
が挙げられ、これらの1種または2種以上が使用できる。
このような水溶性高分子化合物としては、例えば、
ポリビニルアルコール、ポリ(メタ)アクリル酸、ポリアルキレンオキサイド、バイオガム、ガラクトマンナン誘導体、アルギン酸及びその誘導体、ゼラチン、カゼイン及びアルブメンならびにこれらの誘導体、セルロース誘導体等が挙げられる。水溶性高分子化合物は、高粘度品がより好ましく、具体的にはその水溶性高分子化合物の1%水溶液の粘度(B型粘度計を用いて20℃で測定した値を示す。以下同じ。)が通常8000mPa・s以上、好ましくは10000mPa・s以上、より好ましくは12000mPa・s以上となるような水溶性高分子化合物を使用することが好ましい。
無機質基材としては、例えば、モルタル、コンクリート、ケイ酸カルシウム板、石膏ボード、炭酸カルシウム発泡板、不燃火山性ガラス質複層板、繊維強化セメント板、軽量セメント板等が挙げられる。この他、無機質基材としては、無機繊維を含む繊維質シート等が挙げられる。無機繊維としては、例えばロックウール、ガラス繊維、シリカ繊維、シリカ−アルミナ繊維、カーボン繊維、炭化珪素繊維等が挙げられる。なお、本発明における無機質基材に、金属板は包含されない。
有機質基材としては、例えば、プラスチック、ゴム、紙等のほか、有機樹脂発泡体からなるもの、有機繊維を含む繊維質シート等が挙げられる。このうち、有機樹脂発泡体としては、例えば、ポリスチレンフォーム、ポリエチレンフォーム、ポリプロピレンフォーム、塩化ビニルフォーム、ビスコーススポンジ、ゴムフォーム、EVAフォーム、ABSフォーム、ポリアミドフォーム、アクリルフォーム、ウレタンフォーム、フェノールフォーム、ユリアフォーム、シリコンフォーム、エポキシフォーム等が挙げられる。
また、耐火断熱層は、各種下塗層を介して設けることもできる。
(1)基材の少なくとも一方の面に、
セメント100重量部に対し、発泡有機樹脂粒子を4〜40重量部、無機軽量粒子を5〜300重量部、吸熱物質を5〜800重量部、及び水を200〜1200重量部含む組成物を塗付し、硬化させる。
(2)基材の少なくとも一方の面に、
セメント100重量部に対し、発泡有機樹脂粒子を4〜40重量部、無機軽量粒子を5〜300重量部、吸熱物質を5〜800重量部、水を200〜1200重量部、水溶性金属塩を0.5〜30重量部、及び水溶性高分子化合物を0.5〜30重量部含む組成物を塗付し、硬化させる。
本発明では、特に上記(2)の方法が好ましい。このような方法によれば、基材上に、厚さ5〜100mmの耐火断熱層が設けられ、さらにその上に厚さ0.05〜1mmの無機質薄層が形成された積層体が得られやすい。耐火断熱層の厚さは、通常5〜100mm、好ましくは10〜50mmである。この範囲であれば、耐火性、断熱性等において優れた性能を有する。
・セメント:ポルトランドセメント、かさ比重1.2
・発泡有機樹脂粒子A:発泡スチロール粒子、平均粒子径3mm、かさ比重0.014
・発泡有機樹脂粒子B:発泡有機樹脂粒子A100重量部に対して珪酸リチウム溶液とアクリルスチレンエマルションとの混合物(珪酸リチウム溶液(固形分23重量%):アクリルスチレンエマルション(固形分50重量%)=9:1(重量比))60重量部を添加混合した後、50℃で24時間かけて乾燥したもの
・無機軽量粒子:ひる石、平均粒子径1mm、かさ比重0.12
・吸熱物質:水酸化アルミニウム、かさ比重1.2
・水溶性金属塩:硫酸アルミニウム
・水溶性高分子化合物:メチルセルロース(1%水溶液の粘度が15000mPa・s)
セメント100重量部に対し、発泡有機樹脂粒子A21重量部、無機軽量粒子140重量部、吸熱物質9重量部、水溶性高分子化合物5重量部を均一に混合した組成物に、水610重量部を加えて混練した。
上記混練物を、常温下で硬化させ、縦8cm×横14cm×厚み4cmに切り出し、硬化体の密度、及び熱伝導率を測定した。なお、熱伝導率は、熱伝導率計「Kemthrm QTM−D3」(京都電子工業製)を用いて測定した。
(加熱試験A)
試験体の繊維強化セメント板側に600℃のヒーターを設置して、10分間加熱した後、試験体の硬化体側の温度を測定した。試験結果を、表1に示す。評価は、最も低い温度領域であったものを「A」、最も高い温度領域であったものを「E」とする5段階にて行った。
表1〜2に示す配合にて、実施例1と同様に、硬化体と試験体を作製し、同様の試験を行った。結果を表1〜2に示す。
(加熱試験B)
試験体の硬化体側に対し、輻射電気ヒーターにより、50kW/m2の輻射熱を20分間照射した後の総発熱量を測定した。結果を表3に示す。
Claims (2)
- 無機質基材及び有機質基材から選ばれる基材の少なくとも一方の面に、
セメント100重量部に対し、発泡有機樹脂粒子を4〜40重量部、無機軽量粒子を5〜300重量部、及び吸熱物質を5〜800重量部含む組成物の硬化体からなる耐火断熱層が設けられたことを特徴とする積層体。 - 無機質基材及び有機質基材から選ばれる基材の少なくとも一方の面に、
セメント100重量部に対し、発泡有機樹脂粒子を4〜40重量部、無機軽量粒子を5〜300重量部、及び吸熱物質を5〜800重量部含む組成物の硬化体からなる耐火断熱層、
厚さが0.05〜1mmである無機質薄層、
が順に設けられたことを特徴とする積層体。