JP2011090859A - リチウムイオン二次電池正極活物質の製造方法 - Google Patents
リチウムイオン二次電池正極活物質の製造方法 Download PDFInfo
- Publication number
- JP2011090859A JP2011090859A JP2009242983A JP2009242983A JP2011090859A JP 2011090859 A JP2011090859 A JP 2011090859A JP 2009242983 A JP2009242983 A JP 2009242983A JP 2009242983 A JP2009242983 A JP 2009242983A JP 2011090859 A JP2011090859 A JP 2011090859A
- Authority
- JP
- Japan
- Prior art keywords
- lithium
- aluminum
- ion secondary
- active material
- secondary battery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】アルミニウムを含むマンガン酸リチウムによるリチウムイオン二次電池正極活物質の製造方法であって、マンガン化合物を含む溶液を生成する溶液生成工程と、溶液生成工程で生成されたマンガン化合物を含む溶液を加熱し、熱分解して酸化マンガン多孔体を生成する加熱工程と、加熱工程で生成された酸化マンガン多孔体に、リチウムおよびアルミニウムを含浸させる含浸工程と、含浸工程でリチウムおよびアルミニウムを含浸させた酸化マンガン多孔体を焼成し、表面にアルミニウムを含むマンガン酸リチウムを生成する焼成工程とを含むことを特徴とするリチウムイオン二次電池正極活物質の製造方法である。
【選択図】図1
Description
本実施形態の製造方法は、リチウムイオン二次電池正極活物質としてのマンガン酸リチウムを生成するものである。この製造方法は、溶液生成工程と加熱工程と含浸工程と焼成工程とを含む。第1番目の工程である溶液生成工程では、まず、酸化マンガンの原料である硝酸マンガン(Mn(NO3)3)1モルがビーカーなどに入れられ、水またはアルコールが添加され、撹拌されながら溶解される。硝酸マンガンを含む溶液(原料溶液)の濃度は、1リットル当たり0.1モル〜2モルの範囲に設定される。アルコールを使用する場合、アルコールの濃度は50%程度までが好適である。使用可能なアルコールは、エタノール以上の1級〜3級のアルコールであれば各種のアルコールを使用することができる。例えば、エタノールもしくはメタノール(1級)、イソプロピルアルコール(2級)または第3ブチルアルコール(3級)を使用することができる。硝酸マンガン以外に酢酸マンガン、硫酸マンガン、塩化マンガンを用いてもよい。または、炭酸マンガン、金属マンガン、マンガンアセチルアセトナートのいずれか1つを濃硝酸(全体の水溶液で10重量%)で溶解し、水で希釈したものを用いてもよい。
上述した本実施形態の製造方法によって生成された、酸化マンガン多孔体およびマンガン酸リチウムを対象として、所定の実験を行った。以下、この結果について説明する。
110 ミスト発生器
112 超音波振動子
120 石英管
130,140 電気炉
150 サイクロン
160 コンプレッサー
170 フローメータ
Claims (8)
- アルミニウムを含むマンガン酸リチウムによるリチウムイオン二次電池正極活物質の製造方法であって、
マンガン化合物を含む溶液を生成する溶液生成工程と、
前記溶液生成工程で生成された前記マンガン化合物を含む溶液を加熱し、熱分解して酸化マンガン多孔体を生成する加熱工程と、
前記加熱工程で生成された前記酸化マンガン多孔体に、リチウムおよびアルミニウムを含浸させる含浸工程と、
前記含浸工程でリチウムおよびアルミニウムを含浸させた前記酸化マンガン多孔体を焼成し、表面にアルミニウムを含むマンガン酸リチウムを生成する焼成工程とを含むことを特徴とするリチウムイオン二次電池正極活物質の製造方法。 - 前記含浸工程は、前記酸化マンガン多孔体に、リチウムおよびアルミニウムを含む溶液を含浸して行われることを特徴とする請求項1に記載のリチウムイオン二次電池正極活物質の製造方法。
- 前記焼成工程でリチウムおよびアルミニウムを含浸させた前記酸化マンガン多孔体の焼成は、500℃〜900℃の温度範囲で行われることを特徴とする請求項1または請求項2に記載のリチウムイオン二次電池正極活物質の製造方法。
- 前記焼成工程でリチウムおよびアルミニウムを含浸させた前記酸化マンガン多孔体の焼成は、1時間〜24時間の範囲で行われることを特徴とする請求項1から請求項3のいずれか1項に記載のリチウムイオン二次電池正極活物質の製造方法。
- 前記加熱工程は、前記マンガン化合物を含む溶液から発生させたミストを加熱し、熱分解して行われることを特徴とする請求項1から請求項4のいずれか1項に記載のリチウムイオン二次電池正極活物質の製造方法。
- 前記含浸工程で前記酸化マンガン多孔体へのリチウムの含浸は、リチウムが前記酸化マンガン多孔体に対してモル比で0.8〜1.2で混合され、かつアルミニウムが混合された溶液を生成して行われることを特徴とする請求項1から請求項5のいずれか1項に記載のリチウムイオン二次電池正極活物質の製造方法。
- 前記含浸工程では、前記酸化マンガン多孔体に含浸させるリチウムとして、リチウムの無機塩またはリチウムを含む有機金属化合物を用いることを特徴とする請求項1から請求項6のいずれか1項に記載のリチウムイオン二次電池正極活物質の製造方法。
- 前記含浸工程では、前記酸化マンガン多孔体に含浸させるアルミニウムとして、アルミニウムの無機塩またはアルミニウムを含む有機金属化合物を用いることを特徴とする請求項1から請求項7のいずれか1項に記載のリチウムイオン二次電池正極活物質の製造方法。