JP2011032167A - 焼結助剤を用いた耐環境コーティングの製造方法 - Google Patents
焼結助剤を用いた耐環境コーティングの製造方法 Download PDFInfo
- Publication number
- JP2011032167A JP2011032167A JP2010171253A JP2010171253A JP2011032167A JP 2011032167 A JP2011032167 A JP 2011032167A JP 2010171253 A JP2010171253 A JP 2010171253A JP 2010171253 A JP2010171253 A JP 2010171253A JP 2011032167 A JP2011032167 A JP 2011032167A
- Authority
- JP
- Japan
- Prior art keywords
- slurry
- layer
- rare earth
- transition
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】ボンドコート層14をセラミック部品10に塗布する工程、少なくとも有機溶剤と、希土類二ケイ酸塩又はドープ希土類二ケイ酸塩から選択される主要遷移材料と、少なくとも1つのスラリー焼結助剤とを混ぜ合わせた遷移層スラリー、少なくとも有機溶剤と、希土類一ケイ酸塩又はドープ希土類一ケイ酸塩から選択される主要外部材料とを混ぜ合わせた外層スラリー、少なくとも有機溶剤と、BSAS又は希土類ドープBSASからなる主要柔軟材料とを混ぜ合わせた柔軟層スラリー、遷移層スラリー、の少なくともいずれか1つ以上をセラミック部品10に塗布する工程、該セラミック部品10を焼結させて、ボンドコート層14、遷移層16、及び外層20又は柔軟層18のいずれか1つ以上を有する耐環境コーティングを製造する工程、を含む方法とする。
【選択図】図1
Description
イッテルビウム二ケイ酸塩(主要遷移材料)、鉄酸化物ナノ粒子(焼結助剤)、エタノール(溶剤)、及びポリエチレンイミン(分散剤)を混合することによって製造した。この混合物を15時間ローラーミルに配置した。ローラーミルから容器を取り除いた後、ジルコニア媒体を除去し、スラリーを325メッシュスクリーンによって濾過してあらゆる大径粒子の凝集体を除去した。
Claims (8)
- 焼結助剤を用いた耐環境コーティング(12)の製造方法であって、
ボンドコート層(14)をセラミック部品(10)に塗布するステップと、
少なくとも有機溶剤と、希土類二ケイ酸塩又はドープ希土類二ケイ酸塩からなる主要遷移材料とを混ぜ合わせて遷移層スラリーを製造するステップと、
少なくとも有機溶剤と、希土類一ケイ酸塩又はドープ希土類一ケイ酸塩からなる主要外部材料とを混ぜ合わせて外層スラリーを製造するステップと、
少なくとも有機溶剤と、BSAS又は希土類ドープBSASからなる主要柔軟材料とを混ぜ合わせて柔軟層スラリーを製造するステップと、
少なくとも前記遷移層スラリーと、前記外層スラリー及び前記柔軟層スラリーのいずれか1つ以上を前記部品に塗布するステップと、
前記部品を焼結させて、前記ボンドコート層(14)、遷移層(16)、及び外層(20)又は柔軟層(18)のいずれか1つ以上を少なくとも有する前記耐環境コーティングを製造するステップとからなっており、
前記遷移層、前記外層、又は前記柔軟層の少なくとも1つは少なくとも1つのスラリー焼結助剤を更に有しており、前記主要材料と前記スラリー焼結助剤の間の反応によって、その0〜約15容量%の多孔率を有する前記遷移層、その0〜約30容量%の多孔率を有する前記外層、及びその約0〜約30容量%の多孔率を有する前記柔軟層がもたらされる、方法。 - 前記外層スラリー又は前記柔軟層スラリーのいずれか1つ以上を塗布する前記ステップの前に、前記塗布された遷移層スラリーを焼結させて前記遷移層(16)を製造するステップを有する、請求項1に記載の方法。
- 前記溶剤は、メタノール、エタノール、プロパノール、ブタノール、ペンタノール、ヘキサノール、ヘプタノール、オクタノール、ノナノール、デカノール、ドデカノール、アセトン、メチルイソブチルケトン、メチルエチルケトン、トルエン、エチルベンゼン、プロピルベンゼン、メトキシベンゼン、ヘプタン、オクタン、ノナン、デカン、キシレン、ミネラルスピリット、ナフサ、テトラヒドロフラン、エーテル、及びそれらの混合物からなる群から選択される、請求項1又は2のいずれかに記載の方法。
- 前記遷移層(16)、前記外層(20)、及び前記柔軟層(18)の組み合わせを前記部品(10)に塗布するステップを有する、請求項1に記載の方法。
- 任意の追加層を塗布するステップの前に、各々の塗布された柔軟層スラリー、遷移層スラリー、及び外層スラリーを焼結させるステップを有する、請求項4に記載の方法。
- 前記部品(10)は、セラミックマトリックス複合体、即ち、燃焼器部品、タービンブレード、シュラウド、ノズル、ヒートシールド、及びベーンからなる群から選択されるモノリシックセラミックタービンエンジン部品である、請求項1、2、3、又は4のいずれかに記載の方法。
- 約6.8wt%〜約96.1wt%の溶剤と、約3.9wt%〜約93.2wt%の前記主要遷移材料と、選択的に任意の有機加工助剤とを混ぜ合わせて前記遷移層スラリーを製造するステップと、
約6.8wt%〜約96.1wt%の溶剤と、約3.9wt%〜約93.2wt%の前記主要外部材料と、選択的に任意の有機加工助剤とを混ぜ合わせて前記外層スラリーを製造するステップと、
約6.8wt%〜約96.1wt%の溶剤と、約3.9wt%〜約93.2wt%の前記主要柔軟材料と、選択的に任意の有機加工助剤とを混ぜ合わせて前記柔軟層スラリーを製造するステップとを有しており、
前記遷移層スラリー、前記外層スラリー、又は前記柔軟層スラリーのいずれか1つ以上は、約0.01wt%〜約20wt%のスラリー焼結助剤を有しており、前記遷移層スラリー及び前記外層スラリーで使用される前記スラリー焼結助剤は、鉄酸化物、酸化ガリウム、酸化アルミニウム、酸化ニッケル、酸化チタン、酸化ホウ素、アルカリ土類酸化物、カルボニル鉄、鉄金属、アルミニウム金属、ホウ素、ニッケル金属、水酸化鉄、水酸化ガリウム、水酸化アルミニウム、水酸化ニッケル、水酸化チタン、アルカリ土類水酸化物、炭酸鉄、炭酸ガリウム、炭酸アルミニウム、炭酸ニッケル、炭酸ホウ素、アルカリ土類炭酸塩、シュウ酸鉄、シュウ酸ガリウム、シュウ酸アルミニウム、シュウ酸ニッケル、シュウ酸チタン、溶剤可溶性鉄塩、溶剤可溶性ガリウム塩、溶剤可溶性アルミニウム塩、溶剤可溶性ニッケル塩、溶剤可溶性チタン塩、溶剤可溶性ホウ素塩、及び溶剤可溶性アルカリ土類塩からなる群から選択され、
前記柔軟層スラリーで使用される前記スラリー焼結助剤は、希土類硝酸塩、希土類酢酸塩、希土類塩化物、希土類酸化物、リン酸アンモニウム、リン酸、ポリビニルリン酸、及びそれらの組み合わせからなる群から選択される、請求項1、2、3、4、5、又は6のいずれかに記載の方法。 - 約6.8wt%〜約96.1wt%の溶剤と、約3.9wt%〜約93.2wt%の前記主要遷移材料と、選択的に任意の有機加工助剤とを混ぜ合わせて前記遷移層スラリーを製造するステップと、
約6.8wt%〜約96.1wt%の溶剤と、約3.9wt%〜約93.2wt%の前記主要外部材料と、選択的に任意の有機加工助剤とを混ぜ合わせて前記外層スラリーを製造するステップと、
約6.8wt%〜約96.1wt%の溶剤と、約3.9wt%〜約93.2wt%の前記主要柔軟材料と、選択的に任意の有機加工助剤とを混ぜ合わせて前記柔軟層スラリーを製造するステップとを有しており、
前記遷移層スラリー又は前記外層スラリーのいずれか1つ以上は、約0.01wt%〜約59.3wt%のLnb希土類金属スラリー焼結助剤及び約0.01wt%〜約20.6wt%のSiO2スラリー焼結助剤を有する、請求項1、2、3、4、5、又は6のいずれかに記載の方法。