JP2010249203A - 機械部品及び転がり軸受 - Google Patents
機械部品及び転がり軸受 Download PDFInfo
- Publication number
- JP2010249203A JP2010249203A JP2009098070A JP2009098070A JP2010249203A JP 2010249203 A JP2010249203 A JP 2010249203A JP 2009098070 A JP2009098070 A JP 2009098070A JP 2009098070 A JP2009098070 A JP 2009098070A JP 2010249203 A JP2010249203 A JP 2010249203A
- Authority
- JP
- Japan
- Prior art keywords
- rolling
- resin
- resin composition
- rolling element
- cage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
【解決手段】エチレン含有量が25〜40モル%のエチレン−ビニルアルコール共重合体をベース樹脂とし、強化繊維材を樹脂組成物全量の15〜40質量%の割合で含有する樹脂組成物からなる機械部品、並びに少なくとも保持器が前記樹脂組成物からなる転がり軸受。
【選択図】図1
Description
(1)エチレン含有量が25〜40モル%のエチレン−ビニルアルコール共重合体をベース樹脂とし、強化繊維材を樹脂組成物全量の15〜40質量%の割合で含有する樹脂組成物からなることを特徴とする機械部品。
(2)ベース樹脂が、ポリビニルアルコール樹脂を、エチレン−ビニルアルコール共重合体:ポリビニルアルコール樹脂=7:3〜9:1の割合で含有することを特徴とする上記(1)記載の機械部品。
(3)内輪と外輪との間に保持器を介して複数の転動体を転動自在に保持してなり、シール部材を備える転がり軸受であって、少なくとも保持器が上記(1)または(2)に記載の樹脂組成物からなることを特徴とする転がり軸受。
エチレン−ビニルアルコール共重合体(日本合成化学製「ソアライトG25H」;エチレン含有量29モル%、ガラス繊維(エポキシ系シランカップリング剤処理品)含有量25質量%)を用いた。尚、樹脂組成物のJIS K7113法による引張強度は173MPa、引張伸びは9.0%、融点は188℃であった。
エチレン−ビニルアルコール共重合体(日本合成化学製「ソアライトG25K」;エチレン含有量38モル%、ガラス繊維(エポキシ系シランカップリング剤処理品)含有量30質量%)を用いた。尚、樹脂組成物のJIS K7113法による引張強度は149MPa、引張伸びは10.0%、融点は173℃であった。
エチレン−ビニルアルコール共重合体(日本合成化学製「ソアライトG25H」のガラス繊維含有量を30質量%に増量;エチレン含有量29モル%)を70質量%、ポリビニルアルコール(日本合成化学製「エコマティAX−300」)にガラス繊維(エポキシ系シランカップリング剤処理品)を30質量%配合したものを30質量%混合したコンパウンドを用いた。
エチレン−ビニルアルコール共重合体(日本合成化学製「ソアライトG25H」のガラス繊維含有量を30質量%に増量;エチレン含有量29モル%)を90質量%、ポリビニルアルコール(日本合成化学製「エコマティAX−300」)にガラス繊維(エポキシ系シランカップリング剤処理品)を30質量%配合したものを10質量%にて混合した混合物を用いた。
ポリビニルアルコール(日本合成化学製「エコマティAX−300」)にガラス繊維(エポキシ系シランカップリング剤処理品)を30質量%配合したものを用いた。尚、樹脂組成物のJIS K7113法による引張強度は125MPa、引張伸びは3.0%、融点は200℃であった。
ディポン製生分解性プラスチック「Apexa ND201」(ポリエチレンテレフタレートの分子構造中に脂肪酸エステル構造を含有させたものに、ガラス繊維を30質量%配合)を用いた。尚、樹脂組成物のJIS K7113法による引張強度は95MPa、引張伸びは2.0%、融点は200℃であった。
保持器の円環強度を、室温(23℃)または120℃にて測定した。結果を表1に示すが、比較例1の測定値に対する相対値とした。
保持器を粉砕し、菱三商事社製微生物酸化分解測定装置「MODA」(JIS K6953、ISO14855対応)の反応筒部分(完熟堆肥+海砂)に投入し、生分解により発生した二酸化炭素を定量して生分解の進行度を測定した。結果を表1に示すが、比較例1が50%まで生分解するまでに要した日数を1とする相対値とした。
保持器を室温で1分間水中に放置し、形状を保持している場合を「○」、形状を保持していない場合を「×」とし、結果を表1に示す。
11 内輪
12 外輪
13 玉
14 保持器
15 シール部材
32B エンドキャップ
36 保持器
55 リターンガイド
61 保持器
101 仮軸
Claims (3)
- エチレン含有量が25〜40モル%のエチレン−ビニルアルコール共重合体をベース樹脂とし、強化繊維材を樹脂組成物全量の15〜40質量%の割合で含有する樹脂組成物からなることを特徴とする機械部品。
- ベース樹脂が、ポリビニルアルコール樹脂を、エチレン−ビニルアルコール共重合体:ポリビニルアルコール樹脂=7:3〜9:1の割合で含有することを特徴とする請求項1記載の機械部品。
- 内輪と外輪との間に保持器を介して複数の転動体を転動自在に保持してなり、シール部材を備える転がり軸受であって、
少なくとも保持器が請求項1または2に記載の樹脂組成物からなることを特徴とする転がり軸受。