JP2010229302A - オフセット用オーバープリントニス組成物および印刷物 - Google Patents
オフセット用オーバープリントニス組成物および印刷物 Download PDFInfo
- Publication number
- JP2010229302A JP2010229302A JP2009078798A JP2009078798A JP2010229302A JP 2010229302 A JP2010229302 A JP 2010229302A JP 2009078798 A JP2009078798 A JP 2009078798A JP 2009078798 A JP2009078798 A JP 2009078798A JP 2010229302 A JP2010229302 A JP 2010229302A
- Authority
- JP
- Japan
- Prior art keywords
- offset
- silica
- overprint varnish
- varnish composition
- metal organic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】シリカ、高反応性金属有機化合物、バインダー樹脂、植物油類および石油系溶剤を含有するオフセット用オーバープリントニス組成物において、シリカが、平均粒径0.05〜5μmおよびBET比表面積50〜400m2/gであり、高反応性金属有機化合物が、シリカ全量の3〜20重量%含有されてなることを特徴とするオフセット用オーバープリントニス組成物である。
【選択図】なし
Description
通常、ヒートセット型オフセット用オーバープリントニス組成物は、印刷インキ各色印刷後の表面に印刷され、カレンダー、ポスター、カタログ等の印刷物に対して、印刷面保護、印刷面の艶消しによる凹凸感、立体感、マット調、触感効果等を付与する際に使用されている。
一方、オフセットインキ業界は地球環境への負荷低減に取り組んできており、使用する材料は焼却の際、有害ガスの発生がないことが望ましいとされている。印刷物焼却の際、一般的にダイオキシンの発生量は塩素の量に比例するとの実験データもあり、ポリ塩化ビニル系樹脂をマット化剤として使用した印刷物は焼却時にダイオキシン等の有害ガスを発生させる懸念があり、環境負荷軽減の観点から好ましくない。
シリカが、平均粒径0.05〜5μm
および
BET比表面積50〜400m2/gであり、
高反応性金属有機化合物が、シリカ全量の3〜20重量%
含有されてなることを特徴とするオフセット用オーバープリントニス組成物に関するものである。
平均粒径が0.05μm未満であると、艶消し効果を得られず、平均粒径が5μmより大きいと耐摩擦性を向上させる効果に劣り、パイリング等の問題を生じ易い。
脂肪酸モノエステルは上記植物油とモノアルコールとをエステル交換したものや植物油の脂肪酸とモノアルコールを直接エステル反応させた脂肪酸モノエステルである。モノアルコールの代表的なものは、メタノール、エタノール、n−又はiso−プロパノール、n,sec又はte t−ブタノール、ヘプチノール、2−エチルヘキサノール、ヘキサノール、オクタノール、デカノール、ドデカノール等の飽和アルコール、オレイルアルコール、ドデセノール、フイセテリアルコール、ゾンマリルアルコール、ガドレイルアルコール、11−イコセノール、11−ドコセノール、15−テトラコセノール等の不飽和脂肪族系アルコールを挙げることができる。
本発明のインキに用いられる石油系溶剤は、芳香族炭化水素の含有率が1重量%以下でアニリン点が75〜95℃好ましくは80〜95℃及び、沸点が240℃〜350℃好ましくは280〜350℃の範囲にある石油系溶剤が好ましい。アニリン点が75℃未満の場合には、樹脂を溶解させる能力が高すぎる為、インキのセット性が遅くなり好ましくなく、また95℃を超える場合には樹脂の溶解性が乏しい為、着肉、保存安定性等が劣るため好ましくない。沸点が240℃未満の場合には、印刷機上でのニス溶剤の蒸発が多くなり、ニスの流動性の劣化により、ニスのローラー、ブランケット、版等への転移性の劣化、パイリング等を誘発する懸念があり好ましくない。また、350℃を超える場合には、ヒートセット型のインキの乾燥が劣る為、好ましくない。
無機顔料としては、黄鉛、亜鉛黄、紺青、硫酸バリウム、カドミウムレッド、酸化チタン、亜鉛華、弁柄、アルミナホワイト、炭酸カルシウム、群青、カーボンブラック、グラファイト、アルミニウム粉などがあげられ、有機顔料としては、アゾ系、フタロシアニン系、キナクリドン系、アントラキノン系、ジオキサジン系などオフセットインキに用いられる顔料が相当する。有機顔料に関しては、例えば、銅フタロシアニン系顔料(C.I.Pigment Blue 15、15:1、15:2、15:3、15:4、15:6、C.I.Pigment Green 7、36)、モノアゾ系顔料(C.I.Pigment Red 3、4、5、23、48:1、48:2、48:3、48:4、49:1、49:2、53:1、57:1)、ジスアゾ系顔料(C.I.Pigment Yellow 12、13、14、17、83)、アントラキノン系顔料(C.I.Pigment Red 177)、キナクリドン系顔料(C.I.Pigment Red 122、C.I.PigmentViolet 19)、ジオキサジン系顔料(C.I.Pigment Violet 23)などがあげられるが、これらに限定されるものではない。
さらに、本発明のオフセット用オーバープリントニス組成物およびオフセットインキには、必要に応じて ゲル化剤、顔料分散剤、金属ドライヤー、乾燥抑制剤、酸化防止剤、耐摩擦向上剤、裏移り防止剤、非イオン系海面活性剤、多価アルコール等の添加剤を便宜使用することができる
(1)本発明の平版印刷インキを印刷したもの、
(2)本発明のオーバープリント組成物を印刷したもの
または
(3)本発明の平版印刷インキもしくは他の印刷インキ(平版印刷インキ、グラビア 印刷インキあるいはスクリーン印刷インキ等)で印刷を行った印刷物の印刷面 上に本発明のオーバープリント組成物を印刷したもの
をさす。
撹拌機、冷却器、温度計をつけた4つ口フラスコにP−オクチルフェノール1000部、35%ホルマリン850部、93%水酸化ナトリウム60部、トルエン1000部を加えて、90℃で6時間反応させたる。その後6N塩酸125部、水道水1000部の塩酸溶液を添加し、撹拌、静置し、上層部を取り出し、不揮発分49%のレゾールタイプフェノール樹脂のトルエン溶液2000部を得て、これをレゾール液Xとした。
撹拌機、水分分離器付き冷却器、温度計をつけた4つ口フラスコに、ガムロジン1000部を仕込み、窒素ガスを吹き込みながら200℃で溶解し、レゾール液X1360部を添加し、トルエンを除去しながら230℃で4時間反応させた後、グリセリン110部を仕込み、250〜260℃で酸化20以下になるまでエステル化して、重量平均分子量40000のロジン変性フェノール樹脂A(以下、樹脂Aと称す)を得た。
攪拌機、リービッヒ冷却管、温度計付4つ口フラスコに樹脂A(重量平均分子量40000)43部、大豆油9部、AFソルベント7号(新日本石油(株)製)47部を仕込み、190℃に昇温、同温で30分間攪拌した後、放冷し、ゲル化剤としてエチルアセトアセテートアルミニウムジイソプロピレート1重量部(川研ファインケミカル(株)製ALCH、以下ALCHと称す)を仕込み、190℃で30分間攪拌してゲルワニス1(以下ワニス1と称す)を得た。
市販の湿式法シリカ1(平均粒径3.6μm、BET比表面積120m2/g)17部、ゲルワニス1を52部、AFソルベント7号(新日本石油(株)製)15部、大豆油5部、ALCH1.5部、計90.5部を3本ロール上に仕込み、60℃の3本ロールで2回練肉し、ヒートセット型のオフセット用オーバープリントニスベース1(以下ベース1)を得た。光散乱法式粒度分布計によりベース1の平均粒径を測定したところ、0.7μmであった。このベース1に、ゲルワニス1を3部、AFソルベント7号を6.5部を加えて実施例1のオフセット用オーバープリントニス組成物を約100部得た。
ヒートセット型オフセット墨インキ(東洋インキ製造(株)製、WDレオエックス墨M)をRIテスター(株式会社明製作所製)にてコート紙に展色し、光沢値を測定したところ(村上色彩研究所光沢計)、光沢値70の印刷面を得た。紙面乾燥後、実施例1〜5、比較例1〜3の各オフセット用オーバープリントニス組成物を上から展色し、自製コンベア式熱風乾燥試験機を通した後、光沢値を測定し、以下の評価基準に基づいて評価を行った。光沢値が低い程、艶消し効果が高いことを示す
(評価基準)
○:光沢値が20未満
△:光沢値が20以上、40未満
×:光沢値が40以上
上記のヒートセット型オフセット墨インキをRIテスター(株式会社明製作所製)にてマットコート紙に展色後、実施例1〜5、比較例1〜3の各オフセット用オーバープリントニス組成物を上から展色し、自製コンベア式熱風乾燥試験機を通した後、マットコート紙を展色面上に当て、学振型耐摩擦性試験機(重り1kg)にて5往復摩擦をかけ、目視により展色面上に当てたマットコート紙への墨インキの取られ度合いを観測し、以下の評価基準に基づいて評価を行った。
(評価基準)
○:展色面上に当てたマットコート紙へ墨インキがほとんど移らない
△:展色面上に当てたマットコート紙へ少し墨インキが移る
×:展色面上に当てたマットコート紙へ多く墨インキが移る
実施例1〜5、比較例1〜3の各ヒートセット型オフセット用オーバープリントニス組成物18gに蒸留水を2g添加し、強制乳化させ、乳化ニスを得る。乳化ニス2.1ccを半球状の容器にセットし、60°に傾けた傾斜板の上にインキを垂らし、10分間で流れた長さを測定し、以下の評価基準に基づいて評価を行った。値が高い程乳化したニスの流動性が良好であることを示す。
○:20mm以上
△:5mm以上、20mm未満
×:5mm未満
Claims (8)
- シリカ、高反応性金属有機化合物、バインダー樹脂、植物油類および石油系溶剤を含有するオフセット用オーバープリントニス組成物において、
シリカが、平均粒径0.05〜5μm
および
BET比表面積50〜400m2/gであり、
高反応性金属有機化合物が、シリカ全量の3〜20重量%
含有されてなることを特徴とするオフセット用オーバープリントニス組成物。 - シリカが、湿式シリカであり、ニス全量の5〜30重量%含有されてなることを特徴とする請求項1記載のオフセット用オーバープリントニス組成物。
- さらに、平均粒径0.05〜5μmであるポリテトラフルオロエチレンが、オフセット用オーバープリントニス組成物に、ニス全量の2〜15重量%含有されてなることを特徴とする請求項1〜3いずれか記載のオフセット用オーバープリントニス組成物。
- オフセット用オーバープリントニス組成物が、ヒートセット型であることを特徴とする
請求項1〜3いずれか記載のオフセット用オーバープリントニス組成物。 - 請求項1〜4いずれか記載のオフセット用オーバープリントニス組成物を、インキ全量の5〜30重量%含有してなることを特徴とするオフセットインキ。
- 請求項5記載のオフセットインキを基材に印刷してなることを特徴とする積層物。
- 請求項1〜4いずれか記載のオフセット用オーバープリントニス組成物を基材に印刷してなることを特徴とする積層物。
- 基材が、印刷物であることを特徴とする請求項6記載の積層物。