JP2010167332A

JP2010167332A - Asbestos detoxification treatment method

Info

Publication number: JP2010167332A
Application number: JP2009009893A
Authority: JP
Inventors: Motoyasu Sato; 元泰佐藤; Takashi Morita; 孝士守田; Kenichi Matsui; 健一松井; Masashi Koizumi; 昌士小泉; Nobuhisa Nakamori; 宣尚中森; Naoto Takeyama; 直人竹山; Akihiko Matsuyama; 昭彦松山
Original assignee: Kubota Matsushitadenko Exterior Works Ltd; National Institute of Natural Sciences
Current assignee: National Institute of Natural Sciences; KMEW Co Ltd
Priority date: 2009-01-20
Filing date: 2009-01-20
Publication date: 2010-08-05
Anticipated expiration: 2029-01-20
Also published as: JP5099561B2

Abstract

<P>PROBLEM TO BE SOLVED: To provide an asbestos detoxification treatment method for modifying asbestos contained in a cement hardened body by heating the body in a short time while preventing it from exploding. <P>SOLUTION: The cement hardened body is heated by using an external heating means for heating the cement hardened body from the outside and an internal heating means for heating it from the inside in combination and thereby, asbestos contained in the cement hardened body is modified and detoxified. Then, the cement hardened body is heat-treated stepwise in: a first heating process for heating to disperse crystal water in the cement hardened body; a second heating process for heating to increase the inside temperature of the cement hardened body to the surface temperature; and a third heating process for heating the cement hardened body at a temperature to modify the asbestos therein. <P>COPYRIGHT: (C)2010,JPO&INPIT

Description

本発明は、セメント硬化体に含有されるアスベストを無害化する処理法に関するものである。 The present invention relates to a treatment method for rendering asbestos contained in a hardened cement body harmless.

アスベスト（石綿）は、耐熱性、耐火性、耐薬品性、耐腐食性等において高い特性を有するために、建築資材や断熱材などにおいて古くから使用されている。建築資材としては、石綿スレート、石綿セメント板、石綿セメントサイディングなど、アスベスト含有セメント硬化体が代表的なものである。 Asbestos (asbestos) has long been used in building materials and heat insulating materials because it has high characteristics in heat resistance, fire resistance, chemical resistance, corrosion resistance, and the like. As building materials, asbestos-containing cement hardened bodies such as asbestos slate, asbestos cement board and asbestos cement siding are representative.

しかし、アスベストは、人体の呼吸器官に侵入すると中皮腫や肺ガン等を引き起こす原因物質と考えられるようになっており、被害者が多発していることが社会問題となっている。このため、アスベスト含有セメント硬化体を新規に製造することが規制されているのは勿論であるが、既存建築物に施工されているアスベスト含有セメント硬化体の廃棄が大きな問題になっている。すなわち、既存建築物から回収したアスベスト含有セメント硬化体を廃棄する際に、アスベストが飛散すると、この飛散したアスベストで二次的な被害が発生することになる。 However, asbestos is considered to be a causative substance that causes mesothelioma, lung cancer and the like when it enters the respiratory organs of the human body, and the frequent occurrence of victims has become a social problem. For this reason, as a matter of course, the production of a new hardened asbestos-containing cement is regulated, but the disposal of the hardened asbestos-containing cement applied to existing buildings has become a big problem. That is, when asbestos is scattered when the asbestos-containing hardened cement body recovered from the existing building is discarded, secondary damage is caused by the scattered asbestos.

そこで、アスベストを無害化処理することが種々検討されている。アスベストは針状結晶を有するものであり、このような針状結晶という性状によって、呼吸器官に中皮種や肺ガン等を引き起すものであるが、アスベストを高温に加熱すると、針状結晶が熱変性して分解され、アスベストを無害な状態にすることができることが知られている（特許文献１，２等参照）。 Therefore, various studies have been made to detoxify asbestos. Asbestos has needle-like crystals, and the nature of such needle-like crystals causes mesothelioma and lung cancer in the respiratory organs. However, when asbestos is heated to a high temperature, the needle-like crystals are formed. It is known that it can be decomposed by heat denaturation to make the asbestos harmless (see Patent Documents 1 and 2, etc.).

そして石綿スレートや石綿セメント板などのセメント硬化体の場合は、セメント硬化体を加熱して含有されるアスベストが熱変性する温度以上に昇温させることによって、セメント硬化体中のアスベストを無害化することができるものであり、アスベストを無害化したこのセメント硬化体は安全に処分することができるものである。 And in the case of hardened cement bodies such as asbestos slate and asbestos cement board, the asbestos in the hardened cement body is rendered harmless by heating the hardened cement body to a temperature higher than the temperature at which the asbestos contained is thermally denatured. This hardened cement made of asbestos detoxified can be safely disposed of.

ここで、上記の特許文献１や特許文献２では、アスベストを高温炉床や電気炉を用いて加熱することによって、無害化処理をするようにしており、セメント硬化体をこれらの加熱手段で加熱することによって、セメント硬化体に含有されるアスベストを無害化処理することが可能である。 Here, in patent document 1 and patent document 2 mentioned above, the asbestos is heated by using a high-temperature hearth or an electric furnace to be detoxified, and the hardened cement body is heated by these heating means. As a result, it is possible to detoxify the asbestos contained in the hardened cement body.

しかし、アスベスト含有セメント硬化体において、アスベスト自体が高い断熱性を有する他に、セメント硬化体中のセメントマトリクスや充填材も熱伝導が小さい材料である。例えばアスベスト含有セメント硬化体からなる屋根材の場合、熱伝導率は０．２〜０．３ｋｃａｌ/ｍｈ℃程度と小さい。このため、高温炉床や電気炉のようにセメント硬化体を外部から加熱する場合には、セメント硬化体の表面や端部の昇温速度は速いが、内部の昇温速度は遅く、外部と内部との間の温度差が大きくなって、セメント硬化体の内部まで高温に加熱するには長い加熱時間が必要になる。特に石綿スレートや石綿セメント板などのセメント硬化体の場合には、複数枚を積み重ねて加熱処理することによって、無害化処理の効率を高めるようにするのが一般的であるが、中央部に重ねたセメント硬化体にまで熱が伝わるのに時間がかかり、加熱時間がより長くなる。 However, in the asbestos-containing cement hardened body, asbestos itself has high heat insulation properties, and the cement matrix and filler in the cement hardened body are materials with low heat conduction. For example, in the case of a roof material made of a hardened asbestos-containing cement, the thermal conductivity is as small as about 0.2 to 0.3 kcal / mh ° C. For this reason, when heating a hardened cement body from the outside, such as a high-temperature hearth or electric furnace, the temperature rise rate at the surface and end of the hardened cement body is fast, but the internal temperature rise rate is slow, The difference in temperature between the two and the cement becomes large, and a long heating time is required to heat the inside of the cement hardened body to a high temperature. Particularly in the case of hardened cement bodies such as asbestos slate and asbestos cement board, it is common to increase the efficiency of detoxification treatment by stacking multiple sheets and heat-treating them. It takes time for heat to reach the hardened cement body, and the heating time becomes longer.

またこのようにセメント硬化体の外部と内部の間で温度ばらつきが生じると、セメント硬化体が変形して破損に繋がることがあり、この破損の際にセメント硬化体に含有されるアスベストが飛散するおそれがある。 Moreover, when temperature variation occurs between the outside and the inside of the hardened cement body in this way, the hardened cement body may be deformed and lead to breakage, and asbestos contained in the hardened cement body is scattered at the time of the breakage. There is a fear.

そこで、特許文献３では、アスベスト含有物にマイクロ波を照射して、内部から自己発熱させることによって、アスベストを短時間の加熱で変性して無害化処理をすることが提案されている。 Therefore, in Patent Document 3, it is proposed that the asbestos-containing material is irradiated with microwaves and self-heated from the inside, whereby the asbestos is denatured by heating in a short time and detoxified.

特開平３−６０７８９号公報Japanese Patent Laid-Open No. 3-60789 特開平７−１７１５３６号公報Japanese Patent Laid-Open No. 7-171536 ＷＯ２００７／０３４８１６WO2007 / 034816

従って、特許文献３の記載方法に従って、アスベスト含有セメント硬化体にマイクロ波を照射して、セメント硬化体を内部から加熱すると、セメント硬化体が熱伝導の小さい材料で形成されているにもかかわらず、セメント硬化体を短時間で加熱することができるものであり、またセメント硬化体の外部と内部との間での温度のばらつきが大きくなることを防ぐことができるものである。 Therefore, according to the method described in Patent Document 3, when the asbestos-containing cement cured body is irradiated with microwaves and the cement cured body is heated from the inside, the cement cured body is formed of a material having low heat conduction. The hardened cement body can be heated in a short time, and the temperature variation between the outside and the inside of the hardened cement body can be prevented from increasing.

しかし、セメント硬化体には結露、気中水分、雨水等外部から取り込まれた水や反応の余剰水をさす自由水や、セメント成分の化合物や骨材の化合物に結合された結晶水が含有されているものであり、マイクロ波照射のような内部から加熱する内部加熱手段を用いる場合、セメント硬化体が内部から加熱されると、セメント硬化体の内部に含まれる自由水及び結晶水が気化し、この気化した自由水及び結晶水がセメント硬化体の内部で膨張して、セメント硬化体が爆裂するおそれがある。そしてこのようにセメント硬化体が爆裂するとセメント硬化体に含有されているアスベストが飛散する危険がある。 However, hardened cement bodies contain water taken from outside, such as condensation, atmospheric moisture, and rainwater, free water that indicates excess water for reaction, and crystallization water that is bound to cement compounds and aggregate compounds. In the case of using an internal heating means such as microwave irradiation for heating from the inside, when the cement hardened body is heated from the inside, free water and crystal water contained in the cement hardened body are vaporized. The vaporized free water and crystal water may expand inside the hardened cement body, and the hardened cement body may explode. When the hardened cement body bursts in this way, there is a risk that asbestos contained in the hardened cement body will be scattered.

本発明は上記の点に鑑みてなされたものであり、セメント硬化体が爆裂することを防ぎつつ、セメント硬化体を短時間で加熱して含有されるアスベストを変性することができるアスベストの無害化処理方法を提供することを目的とするものである。 The present invention has been made in view of the above points, and detoxifies asbestos that can modify asbestos contained by heating the cement hardened body in a short time while preventing the cement hardened body from exploding. The object is to provide a processing method.

本発明に係るアスベストの無害化処理方法は、セメント硬化体を外部から加熱する外部加熱手段と、セメント硬化体を内部から加熱する内部加熱手段とを併用してセメント硬化体を加熱することによって、セメント硬化体中に含有されるアスベストを変性して無害化処理するにあたって、セメント硬化体中の自由水及び結晶水を飛散させる加熱を行なう第１加熱工程と、セメント硬化体の内部の温度を表面の温度にまで高めるように加熱を行なう第２加熱工程と、セメント硬化体中のアスベストを変性させる温度で加熱を行なう第３加熱工程により、セメント硬化体を段階的に加熱処理することを特徴とするものである。 The detoxification treatment method for asbestos according to the present invention is to heat the cement hardened body by using an external heating means for heating the cement hardened body from the outside and an internal heating means for heating the cement hardened body from the inside, In the detoxification treatment by modifying the asbestos contained in the hardened cement body, the first heating step for heating to disperse free water and crystal water in the hardened cement body and the temperature inside the hardened cement body to the surface Characterized in that the hardened cement body is heat-treated stepwise by a second heating step in which heating is performed to raise the temperature to a temperature of 3 and a third heating step in which heating is performed at a temperature that modifies asbestos in the hardened cement body. To do.

このように、外部加熱手段と内部加熱手段とを併用することによって、セメント硬化体を外部からと内部からと同時に加熱して、外部と内部との温度差が生じることなく迅速にセメント硬化体を加熱処理することができ、短時間の処理でセメント硬化体に含有されるアスベストを変性して無害化することができるものである。そしてまず第１加熱工程でセメント硬化体中の自由水及び結晶水を徐々に飛散させることによって、セメント硬化体に爆裂や大きな変形、破損が生じることを防ぐことができ、また第２加熱工程では自由水及び結晶水が除去されたセメント硬化体の内部を効率良く表面の温度まで迅速に温度上昇させることができ、さらに第３加熱工程でセメント硬化体の加熱温度を高温に維持して、含有されるアスベストを変性して無害化することができるものである。 In this way, by using the external heating means and the internal heating means in combination, the hardened cement body is heated from the outside and the inside at the same time, and the hardened cement body can be quickly removed without causing a temperature difference between the outside and the inside. It can be heat-treated and can be rendered harmless by modifying asbestos contained in the hardened cement body in a short time. First, in the first heating step, free water and crystallization water in the hardened cement body are gradually scattered to prevent the hardened cement body from undergoing explosion, large deformation, and damage. In the second heating step, The inside of the hardened cement body from which free water and crystallization water have been removed can be rapidly raised to the surface temperature efficiently, and the heating temperature of the hardened cement body is maintained at a high temperature in the third heating step. Asbestos can be denatured and detoxified.

また本発明において、上記の第１加熱工程では、セメント硬化体の温度が６５０〜７５０℃になるまで昇温させ、上記の第２加熱工程では、セメント硬化体の内部の温度を表面の温度にまで高めるように昇温させ、上記の第３加熱工程では、セメント硬化体の温度を８５０℃以上に保持するようにしたことを特徴とするものである。 In the present invention, in the first heating step, the temperature of the hardened cement body is increased to 650 to 750 ° C., and in the second heating step, the temperature inside the hardened cement body is set to the surface temperature. In the third heating step, the temperature of the hardened cement body is maintained at 850 ° C. or higher.

第１加熱工程でセメント硬化体を上記の温度になるまで昇温させることによって、セメント硬化体内の自由水及び結晶水をほぼ飛散させることができるものであり、また第２加熱工程では結晶水が除去されたセメント硬化体の内部を効率良く加熱してセメント硬化体を上記の温度にまで迅速に昇温させることができるものであり、さらに第３加熱工程でセメント硬化体の温度を８５０℃以上に保持することによって、セメント硬化体に含有されるアスベストを変性して無害化することができるものである。 By raising the temperature of the hardened cement body to the above temperature in the first heating step, free water and crystallization water in the hardened cement body can be almost scattered, and in the second heating step, crystallization water is The inside of the removed cement cured body can be efficiently heated to rapidly raise the cement cured body to the above temperature, and the temperature of the cement cured body is 850 ° C. or higher in the third heating step. Asbestos contained in the hardened cement body can be denatured and detoxified.

また本発明は、上記の第１加熱工程での内部加熱手段の出力を、第３加熱工程において設定される内部加熱手段の出力の２０％以下に設定すると共に、上記の第２加熱工程での内部加熱手段の出力を、第３加熱工程において設定される内部加熱手段の出力の２０％を超え８０％以下の範囲に設定することを特徴とするものである。 In the present invention, the output of the internal heating means in the first heating step is set to 20% or less of the output of the internal heating means set in the third heating step, and the output in the second heating step is set. The output of the internal heating means is set in a range exceeding 20% and 80% or less of the output of the internal heating means set in the third heating step.

このように内部加熱手段の出力を第１加熱工程、第２加熱工程、第３加熱工程の順に高めることによって、セメント硬化体内の自由水及び結晶水の急激な気化による爆裂を防ぎつつ、セメント硬化体の加熱温度を効率良く上昇させることができるものである。 In this way, the output of the internal heating means is increased in the order of the first heating step, the second heating step, and the third heating step, thereby preventing cement explosion while preventing explosion due to rapid vaporization of free water and crystal water in the hardened cement body. The heating temperature of the body can be increased efficiently.

また本発明は、上記外部加熱手段が電気ヒーターであり、上記内部加熱手段がマイクロ波発振器であることを特徴とするものである。 In the present invention, the external heating means is an electric heater, and the internal heating means is a microwave oscillator.

外部加熱手段として電気ヒーターを用いることによって、セメント硬化体を外部から効率良く加熱することができると共に、内部加熱手段としてマイクロ波発振器を用いることによって、マイクロ波（高周波）による誘電加熱でセメント硬化体を内部から効率良く加熱することができるものである。 By using an electric heater as an external heating means, the hardened cement body can be efficiently heated from the outside, and by using a microwave oscillator as an internal heating means, a hardened cement body by dielectric heating by microwave (high frequency). Can be efficiently heated from the inside.

また本発明は、セメント硬化体を外部から加熱する外部加熱手段と、セメント硬化体を内部から加熱する内部加熱手段とを備えた第１乃至第３の加熱ゾーンにこの順にセメント硬化体を通過させることによって、セメント硬化体を加熱するにあたって、上記第１加熱工程は第１加熱ゾーンで行なわれ、上記第２加熱工程は第２加熱ゾーンで行なわれ、上記第３加熱工程は第３加熱ゾーンで行なわれることを特徴とするものである。 In the present invention, the cement hardened body is passed in this order through first to third heating zones provided with external heating means for heating the cement hardened body from the outside and internal heating means for heating the cement hardened body from the inside. Accordingly, in heating the cement hardened body, the first heating step is performed in the first heating zone, the second heating step is performed in the second heating zone, and the third heating step is performed in the third heating zone. It is characterized by being performed.

この発明によれば、セメント硬化体を第１加熱ゾーン、第２加熱ゾーン、第３加熱ゾーンの順に連続して通過させることで、セメント硬化体に含有されるアスベストを無害化する処理を自動的に行なうことができるものであり、アスベストの無害化処理を効率良く行なうことができるものである。 According to this invention, the process of detoxifying the asbestos contained in the hardened cement body is automatically performed by passing the hardened cement body successively in the order of the first heating zone, the second heating zone, and the third heating zone. The asbestos detoxification process can be performed efficiently.

本発明によれば、外部加熱手段と内部加熱手段とを併用することによって、セメント硬化体を外部からと内部からと同時に加熱して、外部と内部との温度差が生じることなく迅速にセメント硬化体を加熱処理することができ、セメント硬化体に含有されるアスベストを変性して無害化することができるものである。そしてまず第１加熱工程でセメント硬化体中の自由水及び結晶水を徐々に飛散させることによって、セメント硬化体に爆裂や大きな変形、破損が生じることを防ぐことができ、また第２加熱工程では結晶水が除去されたセメント硬化体の内部を効率良く加熱して迅速に温度上昇させることができ、さらに第３加熱工程でセメント硬化体の加熱温度を高温に維持して、含有されるアスベストを変性して無害化することができるものである。このようにして、セメント硬化体が爆裂することを防ぎつつ、セメント硬化体を短時間で加熱処理して、セメント硬化体に含有されるアスベストを変性して無害化することができるものである。 According to the present invention, by using the external heating means and the internal heating means in combination, the cement hardening body is heated from the outside at the same time from the inside, and the cement hardening is quickly performed without causing a temperature difference between the outside and the inside. The body can be heat-treated, and asbestos contained in the hardened cement body can be modified and rendered harmless. First, in the first heating step, free water and crystallization water in the hardened cement body are gradually scattered to prevent the hardened cement body from undergoing explosion, large deformation, and damage. In the second heating step, The inside of the hardened cement body from which water of crystallization has been removed can be efficiently heated to quickly increase the temperature, and the heating temperature of the hardened cement body is maintained at a high temperature in the third heating step, and the contained asbestos It can be denatured and detoxified. In this way, while preventing the hardened cement body from exploding, the hardened cement body can be heat-treated in a short time to modify the asbestos contained in the hardened cement body and render it harmless.

本発明の実施の形態の一例を示す概略図である。It is the schematic which shows an example of embodiment of this invention.

以下、本発明の実施の形態を説明する。 Embodiments of the present invention will be described below.

図１は、アスベストを含有するセメント硬化体１を加熱してアスベストの無害化処理をするために用いる加熱炉２を概略的に示すものである。この加熱炉２は一端に入口２ａ、他端に出口２ｂを設けた細長いトンネル炉として形成してあり、入口２ａから加熱炉２内に導入されたセメント硬化体１はコンベアなどの搬送装置の上を一定速度で送られ、加熱炉２内を通過した後に、出口２ｂから送り出されるようになっている。 FIG. 1 schematically shows a heating furnace 2 used for heating a hardened cement body 1 containing asbestos to detoxify asbestos. The heating furnace 2 is formed as an elongated tunnel furnace having an inlet 2a at one end and an outlet 2b at the other end, and the cement hardened body 1 introduced into the heating furnace 2 from the inlet 2a is placed on a conveying device such as a conveyor. Is sent at a constant speed, and after passing through the heating furnace 2, is sent out from the outlet 2b.

加熱炉２内は入口２ａから出口２ｂへと複数のゾーンに分かれており、図の実施の形態では入口２ａから出口２ｂへと順に第１加熱ゾーン３、第２加熱ゾーン４、第３加熱ゾーン５、冷却ゾーン６から形成するようにしてある。各ゾーン３，４，５の境界部は、カーテンなどで仕切るようにしてもよいが、仕切りを設けないことも可能である。 The inside of the heating furnace 2 is divided into a plurality of zones from the inlet 2a to the outlet 2b. In the illustrated embodiment, the first heating zone 3, the second heating zone 4, and the third heating zone are sequentially arranged from the inlet 2a to the outlet 2b. 5. It is formed from the cooling zone 6. The boundary between the zones 3, 4 and 5 may be partitioned by a curtain or the like, but it is also possible not to provide a partition.

この第１乃至第３の加熱ゾーン３，４，５内にはそれぞれ、外部加熱手段と内部加熱手段が設けてある。外部加熱手段は、それ自体が熱を放出することによって、セメント硬化体１に外側から熱を加えて、セメント硬化体１を外部から加熱させるものであり、本発明では例えば電気ヒーターを用いることができる。また内部加熱手段は、それ自体が熱を放出することはなく、セメント硬化体１を内部から加熱させるものであり、本発明では例えばマイクロ波発振器を用いることができる。マイクロ波発振器から発振されるマイクロ波（高周波）によって、セメント硬化体１を高周波誘電加熱することができ、セメント硬化体１自体を発熱させて、セメント硬化体１を内部から加熱することができるものである。マイクロ波の周波数は特に限定されるものではないが、日本の電波法で許可されている９１５ＭＨｚ帯、２．４５ＧＨｚ帯が好ましい。 External heating means and internal heating means are provided in the first to third heating zones 3, 4 and 5, respectively. The external heating means, by itself releasing heat, applies heat to the cement hardened body 1 from the outside to heat the cement hardened body 1 from the outside. In the present invention, for example, an electric heater is used. it can. The internal heating means does not release heat by itself and heats the hardened cement body 1 from the inside. For example, a microwave oscillator can be used in the present invention. High-frequency dielectric heating of the hardened cement body 1 by microwaves (high frequency) oscillated from a microwave oscillator, heat generation of the hardened cement body 1 itself, and heating of the hardened cement body 1 from the inside It is. The frequency of the microwave is not particularly limited, but the 915 MHz band and 2.45 GHz band permitted by the Japanese Radio Law are preferable.

また、アスベストを含有するセメント硬化体１としては、特定のものに限定されるものではなく、任意のものを用いることができるものであり、例えば、建築資材の石綿スレート、石綿セメント板、石綿セメントサイディングなどを挙げることができる。これらの建築資材は、既存の建築物から回収されたものを主として用いることになるが、これに限定されるものではない。 Moreover, as the hardened cement body 1 containing asbestos, it is not limited to a specific thing, Arbitrary things can be used, for example, asbestos slate of a building material, asbestos cement board, asbestos cement Siding can be mentioned. Although these building materials will mainly use what was collect | recovered from the existing building, it is not limited to this.

アスベスト含有セメント硬化体１を加熱炉２で加熱処理するにあたっては、加熱炉２に入口２ａからセメント硬化体１を導入する。このとき、セメント硬化体１が板状など積み重ねることができる形態の場合は、複数枚のセメント硬化体１を積み上げて加熱炉２に導入し、多量のセメント硬化体１を同時に加熱処理するようにするのが好ましい。 When the asbestos-containing hardened cement body 1 is heat-treated in the heating furnace 2, the hardened cement body 1 is introduced into the heating furnace 2 from the inlet 2 a. At this time, in the case where the hardened cement body 1 can be stacked, such as a plate shape, a plurality of hardened cement bodies 1 are stacked and introduced into the heating furnace 2, and a large amount of the hardened cement body 1 is heat-treated at the same time. It is preferable to do this.

このように加熱炉２に導入されたセメント硬化体１はまず第１加熱ゾーン３を通過し、外部加熱手段と内部加熱手段とによって加熱される。このようにセメント硬化体１を外部加熱手段で外部からと、内部加熱手段で内部からとで加熱することによって、セメント硬化体１を内部と外部の温度差が大きくならないように均一に加熱することができるものである。 The cement hardened body 1 introduced into the heating furnace 2 first passes through the first heating zone 3 and is heated by the external heating means and the internal heating means. In this way, by heating the cement hardened body 1 from the outside by the external heating means and from the inside by the internal heating means, the cement hardened body 1 is uniformly heated so that the temperature difference between the inside and the outside does not increase. Is something that can be done.

そしてこの第１加熱ゾーン３で、セメント硬化体１中の自由水及び結晶水を飛散させる第１加熱工程が行なわれるものである。セメント硬化体１中には、結露、気中水分、雨水等外部から取り込まれた水や反応の余剰水をさす自由水や、セメント成分の化合物や骨材の化合物に結合された結晶水が含有されているものであり、内部加熱手段でセメント硬化体１を内部から加熱する際に、セメント硬化体１の内部の温度上昇が急激に過ぎると、セメント硬化体１の内部の自由水及び結晶水が急激に蒸発して内部に閉じ込められた状態で膨張し、セメント硬化体１に爆裂が発生するおそれがある。このため、第１加熱ゾーン３では内部加熱手段を小さい出力で作動させ、セメント硬化体１の内部での昇温速度を緩やかなものとすることによって、結晶水を徐々に蒸発させるようにするものであり、セメント硬化体１の内部での自由水及び結晶水の急激な蒸発を抑制して爆裂が発生することを防ぐようにしてある。 And in this 1st heating zone 3, the 1st heating process which disperses the free water and crystal water in the cement hardening body 1 is performed. The hardened cement body 1 includes water taken from outside such as condensation, atmospheric moisture, rainwater, free water that indicates excess water for reaction, and crystallization water combined with cement components and aggregate compounds. When the temperature of the cement hardened body 1 is excessively increased when the cement hardened body 1 is heated from the inside by the internal heating means, free water and crystal water inside the cement hardened body 1 May suddenly evaporate and expand in a state of being confined inside, and there is a risk that explosion will occur in the hardened cement body 1. For this reason, in the first heating zone 3, the internal heating means is operated with a small output, and the temperature rise rate inside the hardened cement body 1 is made slow so that the crystal water is gradually evaporated. In this case, the rapid evaporation of free water and crystal water inside the hardened cement body 1 is suppressed to prevent explosion.

後述のように第１加熱ゾーン３から、第２加熱ゾーン４、第３加熱ゾーン５の順に段階的に内部加熱手段の出力を高めて加熱を行なうが、第１加熱ゾーン３での内部加熱手段の出力は、第３加熱ゾーン５において設定される内部加熱手段の出力の２０％以下に設定するのが好ましい。ここで、内部加熱手段としてマイクロ波発振器を用いる場合、出力は消費電力で決まるので、第１加熱ゾーン３でのマイクロ波発振器の消費電力を、第３加熱ゾーン５でのマイクロ波発振器の消費電力の２０％以下に設定するものである。このように第１加熱ゾーン３の内部加熱手段の出力を第３加熱ゾーン５の内部加熱手段の出力の２０％以下に設定することによって、セメント硬化体１の内部の急激な温度上昇を抑えて、爆裂が発生することを確実に防ぐことができるものである。第１加熱ゾーン３の内部加熱手段の出力の下限は特に設定されないが、第１加熱ゾーン３の内部加熱手段の出力を零にして、外部加熱手段のみで第１加熱工程を行なうようにしてもよい。尚、各加熱ゾーン３，４，５に内部加熱手段が複数設けられる場合は、上記の出力の比率は、複数の平均値として設定されるものである（後述の第２加熱ゾーン４に於いても同じ）。 As will be described later, heating is performed by increasing the output of the internal heating means stepwise in the order of the first heating zone 3, the second heating zone 4, and the third heating zone 5, but the internal heating means in the first heating zone 3 Is preferably set to 20% or less of the output of the internal heating means set in the third heating zone 5. Here, when a microwave oscillator is used as the internal heating means, the output is determined by the power consumption, so the power consumption of the microwave oscillator in the first heating zone 3 is the power consumption of the microwave oscillator in the third heating zone 5. Is set to 20% or less. In this way, by setting the output of the internal heating means in the first heating zone 3 to 20% or less of the output of the internal heating means in the third heating zone 5, the rapid temperature rise inside the hardened cement body 1 is suppressed. It is possible to reliably prevent the explosion from occurring. The lower limit of the output of the internal heating means in the first heating zone 3 is not particularly set, but the output of the internal heating means in the first heating zone 3 is set to zero and the first heating process is performed only with the external heating means. Good. When a plurality of internal heating means are provided in each heating zone 3, 4 and 5, the above output ratio is set as a plurality of average values (in the second heating zone 4 described later). The same).

また、第１加熱ゾーン３において外部加熱手段と内部加熱手段を併用してセメント硬化体１を加熱するにあたって、外部加熱手段の出力と内部加熱手段の出力の比率は特に限定されるものではないが、外部加熱手段の出力を１００とすると、内部加熱手段の出力を２５以下に設定するのが好ましい。ここで、外部加熱手段として電気ヒーターを、内部加熱手段としてマイクロ波発振器を用いる場合、それぞれの消費電力をこの比率に設定するものである。尚、外部加熱手段や内部加熱手段が複数設けられる場合は、上記の出力の比率は、複数の平均値として設定されるものである（後述の第２加熱ゾーン４や第３加熱ゾーン５に於いても同じ）。 Further, in heating the cement hardened body 1 in the first heating zone 3 using both the external heating means and the internal heating means, the ratio of the output of the external heating means and the output of the internal heating means is not particularly limited. When the output of the external heating means is 100, the output of the internal heating means is preferably set to 25 or less. Here, when an electric heater is used as the external heating means and a microwave oscillator is used as the internal heating means, each power consumption is set to this ratio. When a plurality of external heating means and internal heating means are provided, the above output ratio is set as a plurality of average values (in the second heating zone 4 and the third heating zone 5 described later). The same).

第１加熱ゾーン３で行なわれる上記の第１加熱工程は、セメント硬化体１の表面温度が６５０〜７５０℃になるまで昇温させるように行なわれるものである。セメント硬化体１は７００℃程度の温度で結晶水がほぼ飛散するので、第１加熱ゾーン３での第１加熱工程が、セメント硬化体１の表面温度が上記の６５０〜７５０℃程度になる時点で終了するように、第１加熱ゾーン３の外部加熱手段の出力や内部加熱手段の出力を設定するものである。 Said 1st heating process performed in the 1st heating zone 3 is performed so that it may heat up until the surface temperature of the cement hardening body 1 becomes 650-750 degreeC. Since the crystallization water almost scatters at a temperature of about 700 ° C. in the hardened cement body 1, the first heating step in the first heating zone 3 is the time when the surface temperature of the hardened cement body 1 becomes about 650 to 750 ° C. The output of the external heating means in the first heating zone 3 and the output of the internal heating means are set so as to end in step S2.

そして第１加熱工程でセメント硬化体１の表面温度を上記のように６５０〜７５０℃になるまで昇温させるのに要する時間を、３０分以上に設定するのが好ましい。このように３０分以上を要して昇温させることによって、セメント硬化体の内部の自由水及び結晶水が急激に気化することによる爆裂を防ぎつつ、自由水及び結晶水を蒸発させてセメント硬化体から除去することができるものである。従って、第１加熱ゾーン３は３０分以上を要してセメント硬化体１を通過させるように形成されるものである。この時間の上限は特に設定されないが、処理時間を短くするという本発明の主旨から、４５分以下であることが好ましい。 In the first heating step, it is preferable to set the time required for raising the surface temperature of the cement hardened body 1 to 650 to 750 ° C. as described above to 30 minutes or more. By raising the temperature over 30 minutes in this way, the free water and the crystal water are evaporated and the free water and the crystal water are evaporated, while preventing the explosion due to the rapid vaporization of the free water and the crystal water. It can be removed from the body. Accordingly, the first heating zone 3 is formed so as to allow the hardened cement body 1 to pass for 30 minutes or longer. Although the upper limit of this time is not particularly set, it is preferably 45 minutes or less from the gist of the present invention to shorten the processing time.

上記のようにセメント硬化体１を第１加熱ゾーン３に通過させて第１加熱工程の処理を行ない、セメント硬化体１の自由水及び結晶水を飛散させて除去した後、セメント硬化体１を第２加熱ゾーン４に移動させて第２加熱工程の処理を行なう。上記の第１加熱工程では、内部加熱手段の出力を抑制しているため、セメント硬化体１は内部の温度が表面の温度よりも低い。そこで第２加熱工程では内部加熱手段の出力を高め、セメント硬化体１を内部から加熱する効率を高めて、セメント硬化体１の内部の温度を迅速に上昇させるものである。内部加熱手段による加熱はセメント硬化体１の全体が同時に温度上昇し、また外部加熱手段でも同時に加熱を行なっているので、セメント硬化体１は内部の温度と表面温度とが同じになる。そしてセメント硬化体１内の自由水及び結晶水は上記の第１加熱工程で除去されているので、このように内部加熱手段の出力を高めてセメント硬化体１の温度を急上昇させるようにしても、爆裂が発生するようなおそれはない。 As described above, the cement hardened body 1 is passed through the first heating zone 3 to perform the first heating process, and free water and crystal water of the cement hardened body 1 are scattered and removed. It moves to the 2nd heating zone 4, and the process of a 2nd heating process is performed. In said 1st heating process, since the output of an internal heating means is suppressed, the internal temperature of the cement hardening body 1 is lower than the surface temperature. Therefore, in the second heating step, the output of the internal heating means is increased, the efficiency of heating the hardened cement body 1 from the inside is increased, and the temperature inside the hardened cement body 1 is rapidly increased. In the heating by the internal heating means, the temperature of the entire cement hardened body 1 rises at the same time, and the external heating means also heats up simultaneously. Therefore, the internal temperature and the surface temperature of the hardened cement body 1 are the same. Since the free water and crystal water in the hardened cement body 1 are removed in the first heating step, the temperature of the hardened cement body 1 can be increased rapidly by increasing the output of the internal heating means. There is no risk of explosion.

第２加熱ゾーン４での内部加熱手段の出力は、第３加熱ゾーン５において設定される内部加熱手段の出力の２０％を超え、８０％以下の範囲に設定するのが好ましい。ここで、内部加熱手段としてマイクロ波発振器を用いる場合は、第２加熱ゾーン４でのマイクロ波発振器の消費電力を、第３加熱ゾーン５でのマイクロ波発振器の消費電力の２０％を超え、８０％以下の範囲に設定するものである。第２加熱ゾーン４の内部加熱手段の出力が第３加熱ゾーン５の内部加熱手段の出力の２０％以下であると、セメント硬化体１の温度上昇の速度を十分に得ることができず、加熱処理の時間を短くする効果が不十分になる。逆に第２加熱ゾーン４の内部加熱手段の出力が第３加熱ゾーン５の内部加熱手段の出力の８０％を超えると、セメント硬化体１の温度上昇が急激に過ぎ、セメント硬化体１の加熱温度が不均一になって変形や破損が発生するおそれがある。 The output of the internal heating means in the second heating zone 4 is preferably set in the range of more than 20% and 80% or less of the output of the internal heating means set in the third heating zone 5. Here, when a microwave oscillator is used as the internal heating means, the power consumption of the microwave oscillator in the second heating zone 4 exceeds 20% of the power consumption of the microwave oscillator in the third heating zone 5, % Is set within the range. If the output of the internal heating means in the second heating zone 4 is 20% or less of the output of the internal heating means in the third heating zone 5, the rate of temperature rise of the cement hardened body 1 cannot be sufficiently obtained, and heating is performed. The effect of shortening the processing time becomes insufficient. On the contrary, when the output of the internal heating means in the second heating zone 4 exceeds 80% of the output of the internal heating means in the third heating zone 5, the temperature rise of the hardened cement body 1 is too rapid and the heating of the hardened cement body 1 is performed. There is a possibility that the temperature becomes non-uniform and deformation or breakage occurs.

また、第２加熱ゾーン４において外部加熱手段と内部加熱手段を併用してセメント硬化体１を加熱するにあたって、外部加熱手段の出力と内部加熱手段の出力の比率は特に限定されるものではないが、外部加熱手段の出力を１００とすると、内部加熱手段の出力を２５〜４００の範囲に設定するのが好ましい。ここで、外部加熱手段として電気ヒーターを、内部加熱手段としてマイクロ波発振器を用いる場合、それぞれの消費電力をこの比率に設定するものである。 In addition, in heating the cement hardened body 1 using the external heating means and the internal heating means in combination in the second heating zone 4, the ratio between the output of the external heating means and the output of the internal heating means is not particularly limited. If the output of the external heating means is 100, the output of the internal heating means is preferably set in the range of 25-400. Here, when an electric heater is used as the external heating means and a microwave oscillator is used as the internal heating means, each power consumption is set to this ratio.

第２加熱ゾーン４で行なわれる上記の第２加熱工程は、セメント硬化体１の表面温度が８００〜８５０℃になるまで昇温させるように行なわれるものである。アスベストは８５０℃以上の温度で加熱することによって、変性して無害化することができるので、第２加熱ゾーン４での第２加熱工程が、セメント硬化体１の表面温度が上記の８００〜８５０℃の範囲になる時点で終了するように、第２加熱ゾーン４の外部加熱手段の出力や内部加熱手段の出力を設定するものである。 Said 2nd heating process performed in the 2nd heating zone 4 is performed so that it may heat up until the surface temperature of the cement hardening body 1 becomes 800-850 degreeC. Since asbestos can be denatured and detoxified by heating at a temperature of 850 ° C. or higher, the second heating step in the second heating zone 4 is performed at a surface temperature of the cement hardened body 1 of the above 800 to 850. The output of the external heating means and the output of the internal heating means in the second heating zone 4 are set so as to end when the temperature is in the range of ° C.

そして第２加熱工程でセメント硬化体１の表面温度を上記のように８００〜８５０℃になるまで昇温させるのに要する時間は、５〜１５分の範囲に設定するのが好ましい。この時間が５分未満であると、セメント硬化体１の温度上昇が急激に過ぎて変形や破損が発生するおそれがあり、逆に１５分を超えると、加熱処理の時間を短くする効果が不十分になる。従って、第２加熱ゾーン４は５〜１５分を要してセメント硬化体１を通過させるように形成されるものである。 And it is preferable to set the time required to raise the surface temperature of the cement hardening body 1 to 800-850 degreeC as mentioned above in the 2nd heating process in the range of 5-15 minutes. If this time is less than 5 minutes, the temperature rise of the cement hardened body 1 may be abrupt and deformation or breakage may occur. Conversely, if it exceeds 15 minutes, the effect of shortening the heat treatment time is ineffective. It will be enough. Therefore, the 2nd heating zone 4 is formed so that 5-15 minutes may be required and the cement hardening body 1 may be allowed to pass through.

上記のようにセメント硬化体１を第２加熱ゾーン４に通過させて第２加熱工程の処理を行ない、セメント硬化体１の内部の温度が表面温度と等しくなるように急速加熱をした後、セメント硬化体１を第３加熱ゾーン５に移動させて第３加熱工程の加熱処理を行なう。上記の第２加熱工程でセメント硬化体１の表面温度は８００〜８５０℃に上昇しており、第３加熱ゾーン５では内部加熱手段を第１加熱ゾーン３や第２加熱ゾーン４の内部加熱手段より高い出力で作動させることによって、セメント硬化体１の表面温度を８５０℃以上に維持するものである。アスベストは８５０℃以上の温度で加熱されることによって、結晶が変性し、無害化されるものである。このため、第３加熱ゾーン５での第３加熱工程でセメント硬化体１の温度を８５０℃以上に維持することによって、セメント硬化体１に含有されるアスベストを変性して無害化することができるものである。セメント硬化体１の加熱温度の上限は特に設定されるものではないが、エネルギーの効率の上から１０００℃以下の温度に設定するのが好ましい。なお、セメント硬化体の補強繊維として一般的に使用されていたアスベストの場合は一般に１０００℃以下の温度で結晶が変性し、無害化するが、アスベストの種類によっては、結晶が変性して無害化するのに１０００℃以上の温度を必要とする場合があり、その場合には、１０００℃以上に設定することは言うまでもない。 As described above, the cement hardened body 1 is passed through the second heating zone 4 to perform the second heating process, and after the rapid heating so that the temperature inside the cement hardened body 1 becomes equal to the surface temperature, the cement The cured body 1 is moved to the third heating zone 5 to perform the heat treatment in the third heating step. In the second heating step, the surface temperature of the cement hardened body 1 is increased to 800 to 850 ° C., and in the third heating zone 5, the internal heating means is used as the internal heating means in the first heating zone 3 and the second heating zone 4. By operating at a higher output, the surface temperature of the hardened cement body 1 is maintained at 850 ° C. or higher. Asbestos is denatured and detoxified by heating at a temperature of 850 ° C. or higher. For this reason, the asbestos contained in the hardened cement body 1 can be modified and rendered harmless by maintaining the temperature of the hardened cement body 1 at 850 ° C. or higher in the third heating step in the third heating zone 5. Is. The upper limit of the heating temperature of the cement hardened body 1 is not particularly set, but is preferably set to a temperature of 1000 ° C. or less in view of energy efficiency. In the case of asbestos, which is generally used as a reinforcing fiber for hardened cement, the crystals are generally denatured and detoxified at a temperature of 1000 ° C. or lower. However, depending on the type of asbestos, the crystals are denatured and detoxified. In order to do this, a temperature of 1000 ° C. or higher may be required. In this case, it goes without saying that the temperature is set to 1000 ° C. or higher.

ここで、第３加熱ゾーン５において外部加熱手段と内部加熱手段を併用してセメント硬化体１を加熱するにあたって、外部加熱手段の出力と内部加熱手段の出力の比率は特に限定されるものではないが、外部加熱手段の出力を１００とすると、内部加熱手段の出力を４００以上に設定するのが好ましい。外部加熱手段として電気ヒーターを、内部加熱手段としてマイクロ波発振器を用いる場合、それぞれの消費電力をこの比率に設定するものである。 Here, in heating the cement hardened body 1 in the third heating zone 5 by using both the external heating means and the internal heating means, the ratio between the output of the external heating means and the output of the internal heating means is not particularly limited. However, when the output of the external heating means is 100, the output of the internal heating means is preferably set to 400 or more. When an electric heater is used as the external heating means and a microwave oscillator is used as the internal heating means, each power consumption is set to this ratio.

第３加熱ゾーン５で行なわれる上記の第３加熱工程は、セメント硬化体１を８５０℃以上の温度に維持してアスベストを無害化するためのものであり、第３加熱工程における処理時間は、特に限定されるものではないが、１５〜３０分間の範囲が好ましい。１５分未満であると、セメント硬化体１内の温度バラツキやアスベストの分布バラツキなどが原因でアスベストの総てを完全に無害化できないことがある。また３０分を超えて加熱しても、セメント硬化体１内のアスベストは既に十二分に無害化されているので、これ以上に加熱することはエネルギーの無駄になる。従って、第３加熱ゾーン５は１５〜３０分を要してセメント硬化体１を通過させるように形成されるものである。 Said 3rd heating process performed in the 3rd heating zone 5 is for maintaining the cement hardening body 1 at the temperature of 850 degreeC or more, and detoxifying asbestos, The processing time in a 3rd heating process is as follows. Although not particularly limited, a range of 15 to 30 minutes is preferable. If it is less than 15 minutes, it may not be possible to completely detoxify all of asbestos due to temperature variation and asbestos distribution variation in the hardened cement body 1. Moreover, even if it heats exceeding 30 minutes, since the asbestos in the cement hardened body 1 has already been made harmless enough, heating more than this will waste energy. Accordingly, the third heating zone 5 is formed so as to pass through the cement hardened body 1 in 15 to 30 minutes.

上記のようにセメント硬化体１を加熱炉２の第１加熱ゾーン３、第２加熱ゾーン４、第３加熱ゾーン５の順に通して加熱処理することによって、セメント硬化体１に含有されるアスベストを無害化処理することができるものであり、このようにアスベストを無害化処理したセメント硬化体１は、加熱炉２の出口２ｂから送り出されるものである。 Asbestos contained in the cement hardened body 1 is obtained by heat-treating the cement hardened body 1 through the first heating zone 3, the second heating zone 4 and the third heating zone 5 of the heating furnace 2 in this order. The hardened cement body 1 that can be detoxified and thus detoxified asbestos is sent out from the outlet 2 b of the heating furnace 2.

次に、本発明を実施例１〜４及び比較例１〜５によって例証する。 The invention will now be illustrated by Examples 1-4 and Comparative Examples 1-5.

一端に入口２ａ、他端に出口２ｂを設けた細長いトンネル状の加熱炉２を用い、加熱炉２内に入口２ａから出口２ｂへと順に第１加熱ゾーン３、第２加熱ゾーン４、第３加熱ゾーン５、冷却ゾーン６を形成した。そして各ゾーン３，４，５内には、外部加熱手段である電気ヒーターと、内部加熱手段であるマイクロ波発振器（周波数２．４５ＧＨｚ）とを設けた。 An elongated tunnel-shaped heating furnace 2 having an inlet 2a at one end and an outlet 2b at the other end is used. In the heating furnace 2, the first heating zone 3, the second heating zone 4, and the third A heating zone 5 and a cooling zone 6 were formed. In each zone 3, 4 and 5, an electric heater as an external heating means and a microwave oscillator (frequency 2.45 GHz) as an internal heating means were provided.

一方、アスベスト含有セメント硬化体１として、屋根材（カラーベスト：厚み５ｍｍ、熱伝導率０．２〜０．２５ｋｃａｌ/ｍｈ℃）を用いた。 On the other hand, as the asbestos-containing cement cured body 1, a roof material (color vest: thickness 5 mm, thermal conductivity 0.2 to 0.25 kcal / mh ° C.) was used.

そして、このセメント硬化体１を上下に７枚重ねて入口２ａから加熱炉２に導入し、コンベアによってセメント硬化体１を第１加熱ゾーン３、第２加熱ゾーン４、第３加熱ゾーン５、冷却ゾーン６の順に通過させて加熱処理した後、出口２ｂから取り出した。このとき、第１加熱ゾーン３、第２加熱ゾーン４、第３加熱ゾーン５での電気ヒーターとマイクロ波発振器の出力を表１のように設定し、また第１加熱ゾーン３、第２加熱ゾーン４、第３加熱ゾーン５の各通過時間を表１のように設定した。 Then, the seven hardened cement bodies 1 are stacked one above the other and introduced into the heating furnace 2 through the inlet 2a, and the hardened cement body 1 is cooled by the conveyor by the first heating zone 3, the second heating zone 4, the third heating zone 5, and the cooling. After passing through zone 6 in the order of heat treatment, it was taken out from outlet 2b. At this time, the outputs of the electric heater and the microwave oscillator in the first heating zone 3, the second heating zone 4, and the third heating zone 5 are set as shown in Table 1, and the first heating zone 3 and the second heating zone 4. Each passing time in the third heating zone 5 was set as shown in Table 1.

上記のように加熱処理を行なったときの、第１加熱ゾーン３、第２加熱ゾーン４、第３加熱ゾーン５のそれぞれ最終位置に達したセメント硬化体１の表面温度を、放射温度計で測定した。 When the heat treatment is performed as described above, the surface temperature of the hardened cement body 1 reaching the final position in each of the first heating zone 3, the second heating zone 4, and the third heating zone 5 is measured with a radiation thermometer. did.

また加熱炉２から取り出したセメント硬化体１について、爆裂、変形の発生有無を検査した。さらにこの加熱処理後のセメント硬化体１に含まれるアスベストをＪＩＳＡ１４８１「建材製品中のアスベスト含有率測定方法」に準拠し判定した。これらの結果を表１に示す。 The hardened cement body 1 taken out from the heating furnace 2 was inspected for the occurrence of explosion and deformation. Furthermore, the asbestos contained in the hardened cement body 1 after the heat treatment was determined according to JIS A 1481 “Measurement method of asbestos content in building material products”. These results are shown in Table 1.

１アスベスト含有セメント硬化体
２加熱炉
３第１加熱ゾーン
４第２加熱ゾーン
５第３加熱ゾーン
６冷却ゾーン DESCRIPTION OF SYMBOLS 1 Asbestos containing cement hardening body 2 Heating furnace 3 1st heating zone 4 2nd heating zone 5 3rd heating zone 6 Cooling zone

Claims

セメント硬化体を外部から加熱する外部加熱手段と、セメント硬化体を内部から加熱する内部加熱手段とを併用してセメント硬化体を加熱することによって、セメント硬化体中に含有されるアスベストを変性して無害化処理するにあたって、セメント硬化体中の自由水及び結晶水を飛散させる加熱を行なう第１加熱工程と、セメント硬化体の内部の温度を表面の温度付近にまで高めるように加熱を行なう第２加熱工程と、セメント硬化体中のアスベストを変性させる温度で加熱を行なう第３加熱工程により、セメント硬化体を段階的に加熱処理することを特徴とするアスベストの無害化処理方法。 Asbestos contained in the hardened cement is modified by heating the hardened cement using both the external heating means for heating the hardened cement from the outside and the internal heating means for heating the hardened cement from the inside. In the detoxification treatment, the first heating step for heating to disperse free water and crystal water in the hardened cement body and the second heating to increase the temperature inside the hardened cement body to near the surface temperature. A detoxifying treatment method for asbestos, characterized in that the hardened cement body is heat-treated stepwise by two heating steps and a third heating step of heating at a temperature that denatures asbestos in the hardened cement body.

第１加熱工程では、セメント硬化体の温度が６５０〜７５０℃になるまで昇温させ、第２加熱工程では、セメント硬化体の内部の温度を表面の温度にまで高めるように昇温させ、第３加熱工程では、セメント硬化体の温度を８５０℃以上に保持するようしたことを特徴とする請求項１に記載のアスベストの無害化処理方法。 In the first heating step, the temperature of the hardened cement body is raised to 650-750 ° C., and in the second heating step, the temperature inside the hardened cement body is raised to the surface temperature, The asbestos detoxification method according to claim 1, wherein the temperature of the hardened cement body is maintained at 850 ° C or higher in the three heating step.

第１加熱工程での内部加熱手段の出力を、第３加熱工程において設定される内部加熱手段の出力の２０％以下に設定すると共に、第２加熱工程での内部加熱手段の出力を、第３加熱工程において設定される内部加熱手段の出力の２０％を超え８０％以下の範囲に設定することを特徴とする請求項１又は２に記載のアスベストの無害化処理方法。 The output of the internal heating means in the first heating process is set to 20% or less of the output of the internal heating means set in the third heating process, and the output of the internal heating means in the second heating process is set to the third The asbestos detoxification method according to claim 1 or 2, wherein the range is set in the range of more than 20% and not more than 80% of the output of the internal heating means set in the heating step.

第１加熱工程での加熱処理時間を３０分以上に設定することを特徴とする請求項１乃至３のいずれかに記載のアスベストの無害化処理法。 The asbestos detoxification method according to any one of claims 1 to 3, wherein the heat treatment time in the first heating step is set to 30 minutes or more.

外部加熱手段が電気ヒーターであり、内部加熱手段がマイクロ波発振器であることを特徴とする請求項１乃至４のいずれかに記載のアスベストの無害化処理方法。 The method for detoxifying asbestos according to any one of claims 1 to 4, wherein the external heating means is an electric heater and the internal heating means is a microwave oscillator.

セメント硬化体を外部から加熱する外部加熱手段と、セメント硬化体を内部から加熱する内部加熱手段とを備えた第１乃至第３の加熱ゾーンにこの順にセメント硬化体を通過させることによって、セメント硬化体を加熱するにあたって、上記第１加熱工程は第１加熱ゾーンで行なわれ、上記第２加熱工程は第２加熱ゾーンで行なわれ、上記第３加熱工程は第３加熱ゾーンで行なわれることを特徴とする請求項１乃至５のいずれかに記載のアスベストの無害化処理方法。 By passing the cement hardened body in this order through first to third heating zones provided with external heating means for heating the cement hardened body from the outside and internal heating means for heating the cement hardened body from the inside, cement hardening In heating the body, the first heating step is performed in the first heating zone, the second heating step is performed in the second heating zone, and the third heating step is performed in the third heating zone. An asbestos detoxification method according to any one of claims 1 to 5.