JP2010150477A - ポリウレタン樹脂組成物及びポリウレタン樹脂 - Google Patents
ポリウレタン樹脂組成物及びポリウレタン樹脂 Download PDFInfo
- Publication number
- JP2010150477A JP2010150477A JP2008332502A JP2008332502A JP2010150477A JP 2010150477 A JP2010150477 A JP 2010150477A JP 2008332502 A JP2008332502 A JP 2008332502A JP 2008332502 A JP2008332502 A JP 2008332502A JP 2010150477 A JP2010150477 A JP 2010150477A
- Authority
- JP
- Japan
- Prior art keywords
- polyurethane resin
- resin composition
- castor oil
- diisocyanate
- inorganic filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】
(A)ポリイソシアネートと、(B)ひまし油系ポリオールの水素添加物と、(C)無機充填材と、(D)可塑剤とを含有していることを特徴とするポリウレタン樹脂組成物と、これを硬化させることにより得られるポリウレタン樹脂である。
【選択図】 なし
Description
・ポリイソシアネート
デュラネートTKA-100(ヘキサメチレンジイソシアネート変性イソシアヌレート体、旭化成社製)
・ひまし油系ポリオールの水素添加物
URIC PH-5001(ヨウ素価:10g以下/100g、伊藤製油社製)
HS 2T-1208(ヨウ素価:10g以下/100g、豊国製油社製)
HS 2T-166H(ヨウ素価:10g以下/100g、豊国製油社製)
・無機充填材
水酸化アルミニウムA(平均粒子径:3.2μm)
水酸化アルミニウムB(平均粒子径:35μm)
酸化アルミニウムA(平均粒子径:45μm)
・酸化防止剤
BHT(ジブチルヒドロキシトルエン)
・吸湿剤
ゼオラムA4(ゼオライト、東ソー社製)
・比較例用のポリオール
エポール(ヨウ素価:7.9g/100g、ポリイソプレンポリオールの水素添加物、出光興産社製)
KRASOL HLBH P3000(ヨウ素価:1.1g/100g、ポリブタジエンポリオールの水素添加物、サートマー社製)
ひまし油D(ひまし油、伊藤製油社製)
また、(E)リン酸エステル成分については、以下のようにして合成した。
ラウリルアルコールを出発物質とし、プロピレンオキサイド2モルおよびエチレンオキサイド8モルを公知の方法でブロック付加して、ラウリルアルコールのアルキレンオキサイド付加物を得た。
トリデシルアルコールを出発物質とし、エチレンオキサイド10モルを公知の方法を用いて付加して、トリデシルアルコールのアルキレンオキサイド付加物Aを得た。
トリデシルアルコールを出発物質とし、エチレンオキサイド7モルを公知の方法を用いて付加して、トリデシルアルコールのアルキレンオキサイド付加物Bを得た。
表1に示す配合により、実施例1〜7及び比較例1〜3のポリウレタン樹脂組成物を調製した。調製に際しては、表1に示す成分のうち、(A)ポリイソシアネート成分を除く成分を、混合機(商品名:あわとり練太郎、シンキー社製)を用いて2000rpmで3分間混合した後、25℃に調整した。続いて、この混合物に25℃に調整したポリイソシアネート成分を加え、同上の混合機を用いて2000rpmで1分間混合することにより、各実施例のポリウレタン樹脂組成物を得た。
次に、上記で調製したポリウレタン樹脂組成物を用いてポリウレタン樹脂の試験片を作製した。まず、上記ポリウレタン樹脂組成物を110×110×10mmの金型に充填し、蓋をして23℃で48時間養生した後、これを脱型してポリウレタン樹脂の試験片を得た。但し、比較例1及び2のポリウレタン樹脂組成物の場合は、高粘度のため、均一なポリウレタン樹脂が得ることができなかった。
上記で得られた実施例1〜7及び比較例1〜3について、組成物調製時の混合初期の重合粘度の測定を行い、実施例1〜7及び脱型が可能であった比較例3の樹脂については、更に熱伝導率、硬度(タイプA)、耐熱性試験後の硬度(タイプA)の評価を行った。各試験結果を表1に併せて示した。各試験方法は、以下に示すとおりである。
得られたポリウレタン樹脂組成物を25℃に調整し、混合開始から10分後の粘度をBH型粘度計を用いて測定した。
熱伝導率は、JIS R2618に従い、熱伝導率計(京都電子工業(株)製、QTM−D3)を用いて測定した。
JIS K6253に従って測定した。
150℃の条件下に90時間の耐熱性試験を行った後のポリウレタン樹脂について、JIS K6253に従って硬度(タイプA)を測定した。
実施例1〜7のポリウレタン樹脂組成物は、何れも混合可能な粘度であった。特に、リン酸エステルを配合した場合には、より低粘度となった。一方、比較例3のポリウレタン樹脂組成物は混合可能な粘度ではあったが、比較例1及び2の組成物は粘度が非常に高く、混合か不可能となり、均一なポリウレタン樹脂を得ることができなかった。
Claims (4)
- (A)ポリイソシアネートと、(B)ひまし油系ポリオールの水素添加物と、(C)無機充填材と、(D)可塑剤とを含有していることを特徴とするポリウレタン樹脂組成物。
- 前記(C)無機充填材は、前記ポリウレタン樹脂組成物を100重量%とした場合に、30〜95重量%含有することを特徴とする請求項1に記載のポリウレタン樹脂組成物。
- 請求項1乃至3の何れかに記載のポリウレタン樹脂組成物を硬化させることにより得られるポリウレタン樹脂。