JP2009108110A - Resin composition for strands - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a resin composition for strands capable of producing a strand having an extremely small outer diameter without breaking the strand. <P>SOLUTION: This resin composition for strands comprises: (A) 20 to 95 mass% of a polyamide-based resin; (B) 80 to 5 mass% of a thermoplastic resin (except a polyamide-based resin) containing a styrene-based resin; and (C) one or more type(s) selected from an acid-modified styrene-based resin and an acid-modified olefin-based resin in an amount of 1 to 30 parts by mass relative to 100 parts by mass of the total of components (A) and (B), and in the composition, the calcium concentration is 200 ppm or less and the magnesium concentration is 100 ppm or less. <P>COPYRIGHT: (C)2009,JPO&INPIT

Description

本発明は、衣料用の合成繊維等に適したストランド用樹脂組成物とストランドに関する。   The present invention relates to a strand resin composition and a strand suitable for synthetic fibers for clothing and the like.

樹脂を押出して、直径が１ｍｍ以下の非常に細いストランドを製造するとき、部分的にダマが発生する（異物が付着したように径が大きくなったり、突出部が形成されたりする状態になる）ことがあり、そのような場合には、ダマが発生した部分で断線し易いという問題がある。
特許第３９５０４１０号公報 When a very thin strand having a diameter of 1 mm or less is produced by extruding the resin, a part of the dust is generated (the diameter increases as foreign matter adheres, or a protruding portion is formed). In such a case, there is a problem that the wire is easily disconnected at the portion where the lumps are generated.
Japanese Patent No. 3950410

本発明は、外径の小さなストランド状に押出成形した場合でも、断線の発生を防止できるストランド用樹脂組成物とそれから得られたストランドを提供することを課題とする。   An object of the present invention is to provide a resin composition for a strand that can prevent occurrence of disconnection and a strand obtained from the strand even when extrusion-molded into a strand having a small outer diameter.

本発明者は、ストランドを押出成形したとき、断線原因となるダマが発生する原因が、樹脂成分中に含まれるカルシウムやマグネシウムであることを見出し、前記カルシウムやマグネシウム含有量が低減された樹脂成分を使用することで、本発明を完成したものである。   The present inventor has found that the cause of the occurrence of lumps causing disconnection when the strand is extruded is calcium or magnesium contained in the resin component, and the resin component in which the calcium or magnesium content is reduced The present invention has been completed by using.

本発明は、課題の解決手段として、下記の請求項１〜４の発明を提供するものである。   The present invention provides the following claims 1 to 4 as means for solving the problems.

請求項１の発明は、
（Ａ）ポリアミド系樹脂２０〜９５質量％
（Ｂ）スチレン系樹脂を含む熱可塑性樹脂（ポリアミド系樹脂は除く）８０〜５質量％、
（Ｃ）酸変性スチレン系樹脂及び酸変性オレフィン系樹脂から選ばれる１種以上を（Ａ）及び（Ｂ）成分の合計１００質量部に対して１〜３０質量部を含んでおり、
カルシウム濃度が２００ppm以下で、マグネシウム濃度が１００ppm以下である、ストランド用樹脂組成物であり；
請求項２の発明は、芯材の周囲が樹脂被覆されたストランド成形用である、請求項１記載のストランド用樹脂組成物であり；
請求項３の発明は、外径が１ｍｍ以下のストランド成形用である、請求項１又は２記載のストランド用樹脂組成物であり；
請求項４の発明は、請求項１〜３のいずれか１項記載のストランド用樹脂組成物を押出成形して得られたストランドであり、外径が５００μm以下である、ストランドである。 The invention of claim 1
(A) Polyamide-based resin 20 to 95% by mass
(B) 80 to 5% by mass of a thermoplastic resin containing a styrene resin (excluding a polyamide resin),
(C) 1 to 30 parts by mass with respect to a total of 100 parts by mass of components (A) and (B) including at least one selected from acid-modified styrene-based resins and acid-modified olefin-based resins,
A resin composition for strands having a calcium concentration of 200 ppm or less and a magnesium concentration of 100 ppm or less;
Invention of Claim 2 is the resin composition for strands of Claim 1 which is an object for strand shaping | molding by which the circumference | surroundings of the core material were resin-coated;
Invention of Claim 3 is the resin composition for strands of Claim 1 or 2 which is an object for strand shaping | molding whose outer diameter is 1 mm or less;
Invention of Claim 4 is a strand obtained by extrusion-molding the resin composition for strands of any one of Claims 1-3, and an outer diameter is 500 micrometers or less.

本発明のストランド用樹脂組成物を用いると、外径が小さなストランドを製造したときにも断線の発生を抑制することができる。   When the strand resin composition of the present invention is used, the occurrence of disconnection can be suppressed even when a strand having a small outer diameter is produced.

＜ストランド用樹脂組成物＞
〔（Ａ）成分〕
（Ａ）成分のポリアミド系樹脂としては、ジアミンとジカルボン酸とから形成されるポリアミド樹脂及びそれらの共重合体、具体的にはナイロン６６、ポリヘキサメチレンセバカミド（ナイロン６・１０）、ポリヘキサメチレンドデカナミド（ナイロン６・１２）、ポリドデカメチレンドデカナミド（ナイロン１２１２）、ポリメタキシリレンアジパミド（ナイロンＭＸＤ６）、ポリテトラメチレンアジパミド（ナイロン４６）及びこれらの混合物や共重合体；ナイロン６／６６、６Ｔ成分が５０モル％以下であるナイロン６６／６Ｔ（６Ｔ：ポリヘキサメチレンテレフタラミド）、６Ｉ成分が５０モル％以下であるナイロン６６／６Ｉ（６Ｉ：ポリヘキサメチレンイソフタラミド）、ナイロン６Ｔ／６Ｉ／６６、ナイロン６Ｔ／６Ｉ／６１０等の共重合体；ポリヘキサメチレンテレフタルアミド（ナイロン６Ｔ）、ポリヘキサメチレンイソフタルアミド（ナイロン６Ｉ）、ポリ（２−メチルペンタメチレン）テレフタルアミド（ナイロンＭ５Ｔ）、ポリ（２−メチルペンタメチレン）イソフタルアミド（ナイロンＭ５Ｉ）、ナイロン６Ｔ／６Ｉ、ナイロン６Ｔ／Ｍ５Ｔ等の共重合体が挙げられ、そのほかアモルファスナイロンのような共重合ナイロンでもよく、アモルファスナイロンとしてはテレフタル酸とトリメチルヘキサメチレンジアミンの重縮合物等を挙げることができる。 <Resin composition for strand>
[Component (A)]
As the polyamide-based resin of component (A), polyamide resins formed from diamine and dicarboxylic acid and copolymers thereof, specifically nylon 66, polyhexamethylene sebacamide (nylon 6 · 10), poly Hexamethylene dodecanamide (nylon 6/12), polydodecamethylene dodecanamide (nylon 1212), polymetaxylylene adipamide (nylon MXD6), polytetramethylene adipamide (nylon 46) and mixtures thereof Polymer: Nylon 6/66, nylon 66 / 6T (6T: polyhexamethylene terephthalamide) in which 6T component is 50 mol% or less, nylon 66 / 6I (6I: polyhexa in which 6I component is 50 mol% or less) Methylene isophthalamide), nylon 6T / 6I / 66, nylon 6T / 6I / 61 Copolymers such as polyhexamethylene terephthalamide (nylon 6T), polyhexamethylene isophthalamide (nylon 6I), poly (2-methylpentamethylene) terephthalamide (nylon M5T), poly (2-methylpentamethylene) isophthal Copolymers such as amide (nylon M5I), nylon 6T / 6I, nylon 6T / M5T, and the like, may also be copolymer nylon such as amorphous nylon. As amorphous nylon, polycondensation of terephthalic acid and trimethylhexamethylenediamine And the like.

更に、環状ラクタムの開環重合物、アミノカルボン酸の重縮合物及びこれらの成分からなる共重合体、具体的には、ナイロン６、ポリ−ω−ウンデカナミド（ナイロン１１）、ポリ−ω−ドデカナミド（ナイロン１２）等の脂肪族ポリアミド樹脂及びこれらの共重合体、ジアミン、ジカルボン酸とからなるポリアミドとの共重合体、具体的にはナイロン６Ｔ／６、ナイロン６Ｔ／１１、ナイロン６Ｔ／１２、ナイロン６Ｔ／６Ｉ／１２、ナイロン６Ｔ／６Ｉ／６１０／１２等及びこれらの混合物を挙げることができる。   Further, a ring-opening polymer of cyclic lactam, a polycondensate of aminocarboxylic acid, and a copolymer comprising these components, specifically, nylon 6, poly-ω-undecanamide (nylon 11), poly-ω-dodecanamide. (Nylon 12) and other aliphatic polyamide resins and copolymers thereof, and copolymers with polyamides comprising diamines and dicarboxylic acids, specifically nylon 6T / 6, nylon 6T / 11, nylon 6T / 12, Mention may be made of nylon 6T / 6I / 12, nylon 6T / 6I / 610/12, and mixtures thereof.

〔（Ｂ）成分〕
本発明の組成物は、（Ｂ）成分の樹脂として、組成物中のカルシウムやマグネシウム濃度を減少させるため、塊状重合で製造したもの、乳化重合後、酸凝固で製造したものを用いることが好ましい。乳化重合度、塩凝固したものを用いる場合には、水洗等の方法で洗浄して、カルシウムやマグネシウム濃度を低減する。 [(B) component]
In the composition of the present invention, as the resin of the component (B), in order to reduce the calcium or magnesium concentration in the composition, it is preferable to use a product produced by bulk polymerization, or a product produced by emulsion coagulation and then acid coagulation. . In the case of using an emulsion polymerization degree and a salt-coagulated product, the calcium or magnesium concentration is reduced by washing with a method such as washing with water.

スチレン系樹脂としては、スチレン、α−メチルスチレン、ビニルトルエン等のスチレン系モノマーの単独又は共重合体のほか、これらのスチレン系モノマーと共重合可能なモノマー、例えばアクリロニトリル、メチルメタクリレート等のビニル系モノマーとの共重合体を挙げることができる。   Styrene resins include styrene monomers such as styrene, α-methylstyrene, vinyltoluene, or copolymers, as well as monomers copolymerizable with these styrene monomers, for example, vinyl monomers such as acrylonitrile and methyl methacrylate. Mention may be made of copolymers with monomers.

また、スチレン系樹脂は、ブタジエンゴム等のジエン系ゴム、エチレン／プロピレン系ゴム、アクリル系ゴム等に上記のスチレン系モノマー及びビニル系モノマーをグラフト重合させたゴム変性スチレン系樹脂にすることができる。このようなスチレン系樹脂としては、ポリスチレン、ハイインパクトポリスチレン、ＡＳ樹脂、ＡＢＳ樹脂、ＡＡＳ樹脂、ＡＥＳ樹脂、ＭＳ樹脂、ＭＢＳ樹脂等を挙げることができる。特に好ましくは、ポリスチレン、ＡＳ樹脂である。   The styrene resin can be a rubber-modified styrene resin obtained by graft polymerization of the above styrene monomer and vinyl monomer on a diene rubber such as butadiene rubber, ethylene / propylene rubber, acrylic rubber, or the like. . Examples of such a styrenic resin include polystyrene, high impact polystyrene, AS resin, ABS resin, AAS resin, AES resin, MS resin, MBS resin, and the like. Particularly preferred are polystyrene and AS resin.

スチレン系樹脂は、重量平均分子量が１００，０００〜６００，０００の範囲のものが好ましく、１００，０００〜５００，０００の範囲のものがより好ましく、１５０，０００〜４５０，０００の範囲のものがより好ましい。   The styrene resin preferably has a weight average molecular weight in the range of 100,000 to 600,000, more preferably in the range of 100,000 to 500,000, and in the range of 150,000 to 450,000. More preferred.

他の熱可塑性樹脂（ポリアミド系樹脂は除く）としては、オレフィン系樹脂、ポリフェニレンエーテル樹脂等を挙げることができる。   Examples of other thermoplastic resins (excluding polyamide resins) include olefin resins and polyphenylene ether resins.

オレフィン系樹脂は、エチレンのほか、プロピレン、１−ブテン、１−ペンテン、１−ヘキセン、１−ヘプテン、１−オクテン、３−メチル−１−ブテン、４−メチル−１−ペンテン等のα−オレフィンの単独ポリマー、エチレンとα−オレフィンの共重合体、異なるα−オレフィン同士の共重合体、エチレン又はα−オレフィンを主成分として、これと共重合可能な他のモノマー、例えば、アクリル酸エステル、メタクリル酸エステル等の共重合体等を挙げることができる。   Olefin-based resins include ethylene, α- such as propylene, 1-butene, 1-pentene, 1-hexene, 1-heptene, 1-octene, 3-methyl-1-butene and 4-methyl-1-pentene. Olefin homopolymer, copolymer of ethylene and α-olefin, copolymer of different α-olefins, other monomers having ethylene or α-olefin as a main component and copolymerizable therewith, for example, acrylic ester And copolymers such as methacrylic acid esters.

オレフィン系樹脂としては、高密度ポリエチレン、直鎖状低密度ポリエチレン、ポリプロピレン、プロピレンを主成分とし、更にエチレン又はプロピレン以外のα−オレフィンをブロック又はランダム共重合させた共重合体が好ましく、特にプロピレンを主成分とし、更にエチレン又はプロピレン以外のα−オレフィンをブロック又はランダム共重合させた共重合体（オレフィン系樹脂）が好ましい。ここで、エチレン又はプロピレン以外のα−オレフィンの割合（仕込み割合）は、０．１〜１０質量％が好ましい。   The olefin resin is preferably a copolymer mainly composed of high-density polyethylene, linear low-density polyethylene, polypropylene, and propylene, and further block or random copolymerized with α-olefin other than ethylene or propylene. A copolymer (olefin-based resin) in which an α-olefin other than ethylene or propylene is further blocked or randomly copolymerized is preferable. Here, the ratio (charge ratio) of α-olefin other than ethylene or propylene is preferably 0.1 to 10% by mass.

ポリフェニレンエーテル樹脂は、ポリフェニレンエーテル、ポリフェニレンエーテルと他の樹脂とのアロイ（変性ポリフェニレンエーテル）を挙げることができる。   Examples of the polyphenylene ether resin include polyphenylene ether and an alloy (modified polyphenylene ether) of polyphenylene ether and another resin.

本発明の組成物中、（Ａ）成分と（Ｂ）成分の含有割合は、（Ａ）成分が２０〜９５質量％、好ましくは３０〜８０質量％、より好ましくは４０〜７０質量％であり、（Ｂ）成分が８０〜５質量％、好ましくは７０〜２０質量％、より好ましくは６０〜３０質量％である。   In the composition of the present invention, the content ratio of the component (A) and the component (B) is such that the component (A) is 20 to 95% by mass, preferably 30 to 80% by mass, more preferably 40 to 70% by mass. , (B) component is 80-5 mass%, Preferably it is 70-20 mass%, More preferably, it is 60-30 mass%.

〔（Ｃ）成分〕
本発明の（Ｃ）成分である酸変性スチレン系樹脂及び酸変性オレフィン系樹脂から選ばれる１種以上は、（Ａ）成分と（Ｂ）成分の相溶化剤として作用する成分である。 [Component (C)]
One or more selected from the acid-modified styrene resin and the acid-modified olefin resin that are the component (C) of the present invention are components that act as compatibilizers for the components (A) and (B).

酸変性スチレン系樹脂としては、アクリル酸やマレイン酸等の酸変性ＡＢＳ樹脂、酸変性ＡＳ樹脂、スチレン-マレイミド-無水マレイン酸共重合体等を挙げることができ、酸変性ポリプレン系樹脂としては、アクリル酸やマレイン酸等の酸変性ポリプロピレン等を挙げることができる。   Examples of the acid-modified styrene resin include acid-modified ABS resins such as acrylic acid and maleic acid, acid-modified AS resins, styrene-maleimide-maleic anhydride copolymers, and the like. Examples include acid-modified polypropylene such as acrylic acid and maleic acid.

（Ｃ）成分は、（Ａ）成分と（Ｂ）成分の相溶化作用を高めるものであるため、酸量が０．５〜５質量％であることが好ましく、０．５〜３質量％であることがより好ましい。   Since (C) component is what improves the compatibilizing effect of (A) component and (B) component, it is preferable that acid amount is 0.5-5 mass%, and is 0.5-3 mass%. More preferably.

（Ｃ）成分の含有量は、（Ａ）及び（Ｂ）成分の合計１００質量部に対して１〜３０質量部であり、好ましくは２〜２０質量部、より好ましくは３〜１５質量部である。   (C) Content of a component is 1-30 mass parts with respect to a total of 100 mass parts of (A) and (B) component, Preferably it is 2-20 mass parts, More preferably, it is 3-15 mass parts. is there.

〔その他の成分〕
本発明の組成物には、本発明の課題を解決できる範囲内で、各種添加剤、熱安定化剤、酸性成分の中和剤、帯電防止剤、紫外線吸収剤、滑剤、結晶核剤、染料、顔料等を含有させることができる。 [Other ingredients]
The composition of the present invention includes various additives, heat stabilizers, acidic component neutralizers, antistatic agents, ultraviolet absorbers, lubricants, crystal nucleating agents, and dyes within a range that can solve the problems of the present invention. , Pigments and the like can be contained.

本発明の組成物では、組成物中におけるカルシウム量とマグネシウム量、好ましくは更にナトリウム量とカリウム量を所定値以下にすることにより、ストランドを押出成形するとき又は押出成形後の断線の発生を抑制することができる。カルシウム濃度とマグネシウム濃度は、実施例に記載の方法により測定する。   In the composition of the present invention, the amount of calcium and magnesium in the composition, preferably the amount of sodium and potassium, is controlled to a predetermined value or less to suppress the occurrence of disconnection when extruding a strand or after extrusion. can do. The calcium concentration and the magnesium concentration are measured by the method described in the examples.

本発明の組成物は、組成物中におけるカルシウム濃度が２００ppm以下であり、好ましくは１〜１５０ppmであり、より好ましくは１〜１００ppmである。   In the composition of the present invention, the calcium concentration in the composition is 200 ppm or less, preferably 1 to 150 ppm, more preferably 1 to 100 ppm.

本発明の組成物は、組成物中におけるマグネシウム濃度が１００ppm以下であり、好ましくは１〜８０ppmであり、より好ましくは１〜５０ppmである。   In the composition of the present invention, the magnesium concentration in the composition is 100 ppm or less, preferably 1 to 80 ppm, more preferably 1 to 50 ppm.

本発明の組成物では、組成物中におけるナトリウム量とカリウム量も所定値以下であることが好ましい。ナトリウム量は１００ppm以下であり、好ましくは１〜８０ppmであり、より好ましくは１〜５０ppmであり、カリウム量は２００ppm以下であり、好ましくは１〜１５０ppmであり、より好ましくは１〜１００ppmである。   In the composition of the present invention, the amount of sodium and the amount of potassium in the composition are preferably not more than predetermined values. The amount of sodium is 100 ppm or less, preferably 1 to 80 ppm, more preferably 1 to 50 ppm, and the amount of potassium is 200 ppm or less, preferably 1 to 150 ppm, more preferably 1 to 100 ppm.

本発明の組成物は、外径が１ｍｍ以下、例えば、外径が５００μm以下のストランド用として使用することができる。ストランドは、芯材の周囲が本発明の組成物で被覆されたものでもよい。   The composition of the present invention can be used for strands having an outer diameter of 1 mm or less, for example, an outer diameter of 500 μm or less. The strand may be one in which the periphery of the core is coated with the composition of the present invention.

芯材は用途に応じて適宜選択することができるものであり、合成樹脂製、天然繊維製、紙製、金属製等を用いることができる。本発明の組成物で金属製芯材の周囲を被覆したものは、例えば、袋口等を結束するために使用することができる。   The core material can be appropriately selected depending on the application, and synthetic resin, natural fiber, paper, metal, or the like can be used. What coated the circumference | surroundings of the metal core with the composition of this invention can be used in order to bind a bag mouth etc., for example.

＜ストランドとその製造方法＞
本発明の組成物を用いてストランドを製造する場合には、下記の方法を適用できる。本発明の組成物で用いる各成分を必要に応じてミキサー等で予備混合した後、押出機中で溶融混練した後、紡糸口金から所定径になるように押し出し、公知の湿式又は乾式凝固法で凝固させて得る。 <Strand and its manufacturing method>
When manufacturing a strand using the composition of this invention, the following method is applicable. Each component used in the composition of the present invention is premixed with a mixer or the like as necessary, and then melt-kneaded in an extruder, and then extruded from a spinneret to a predetermined diameter, and then a known wet or dry solidification method. Obtained by solidification.

本発明のストランドは、押出成形時にダマが発生し難いため、断線することなく、外径が５００μm以下にすることができる。   Since the strand of the present invention is less likely to cause lumps during extrusion, the outer diameter can be reduced to 500 μm or less without disconnection.

本発明のストランドは、衣料製造用の繊維、タイヤコード、ゴムやプラスチックの補強繊維、内装材ファブリックや各種繊維のコーテイング等に使用することができる。   The strand of the present invention can be used for clothing manufacturing fibers, tire cords, rubber and plastic reinforcing fibers, interior material fabrics, and coatings of various fibers.

（カルシウム濃度とマグシウム濃度の測定方法）
組成物中のカルシウム濃度とマグシウム濃度は、ＩＣＰ質量分析法を用いて測定した。 (Measurement method of calcium concentration and magnesium concentration)
The calcium concentration and the magnesium concentration in the composition were measured using ICP mass spectrometry.

実施例及び比較例で使用した成分は、次のとおりである。
（Ａ）成分
ＰＡ−１：標準ポリアミド（ポリアミド6，三菱エンジニアプラスチック社製，ノバミッド，ポリアミド6 1010J）
（Ｂ）成分
ＡＢＳ-１樹脂（スチレン量４５質量％、アクリロニトリル１6質量％、ゴム量４０質量％ ，酸凝固，Ｃａ：１１ｐｐｍ、Ｍｇ：２ｐｐｍ）
ＡＢＳ-２樹脂（スチレン量４５質量％、アクリロニトリル１５質量％、ゴム量４０質量％，酸凝固，Ｃａ：８ｐｐｍ、Ｍｇ：６００ｐｐｍ）
ＡＢＳ-３樹脂（スチレン量４５質量％、アクリロニトリル１５質量％、ゴム量４０質量％，塩凝固，Ｃａ：２３ｐｐｍ、Ｍｇ：１４００ｐｐｍ）
ＡＢＳ-４樹脂（スチレン量４５質量％、アクリロニトリル１５質量％、ゴム量４０質量％，塩凝固，Ｃａ：２８００ｐｐｍ、Ｍｇ：４ｐｐｍ）
（Ｃ）成分
（Ｃ-１）スチレン−Nフェニルマレイミド−無水マレイン酸共重合体（スチレン４７質量％、Nフェニルマレイミド５２質量％、無水マレイン酸が１質量％，重量平均分子量が１４万５千）
実施例及び比較例
表１記載の各成分をＶ型タンブラーで混合後、二軸押出機（日本製鋼製，ＴＥＸ３０，シリンダー温度２３０℃、回転数３５０rpm、吐出量３０kg/hr）にて溶融混練し、樹脂組成物を得た。 The components used in Examples and Comparative Examples are as follows.
(A) component PA-1: standard polyamide (polyamide 6, manufactured by Mitsubishi Engineer Plastics, Novamid, polyamide 6 1010J)
Component (B) ABS-1 resin (styrene content 45% by mass, acrylonitrile 16% by mass, rubber content 40% by mass, acid coagulation, Ca: 11 ppm, Mg: 2 ppm)
ABS-2 resin (styrene content 45% by mass, acrylonitrile 15% by mass, rubber content 40% by mass, acid coagulation, Ca: 8 ppm, Mg: 600 ppm)
ABS-3 resin (styrene content 45% by mass, acrylonitrile 15% by mass, rubber content 40% by mass, salt coagulation, Ca: 23 ppm, Mg: 1400 ppm)
ABS-4 resin (styrene content 45% by mass, acrylonitrile 15% by mass, rubber content 40% by mass, salt coagulation, Ca: 2800 ppm, Mg: 4 ppm)
Component (C) (C-1) Styrene-N-phenylmaleimide-maleic anhydride copolymer (styrene 47% by mass, N-phenylmaleimide 52% by mass, maleic anhydride 1% by mass, weight average molecular weight 145,000 )
Examples and Comparative Examples After mixing the components shown in Table 1 with a V-type tumbler, they were melt-kneaded in a twin-screw extruder (manufactured by Nippon Steel, TEX30, cylinder temperature 230 ° C., rotation speed 350 rpm, discharge rate 30 kg / hr). A resin composition was obtained.

東洋精機（株）製のキャピログラフ-1Bを用いて上記作成した樹脂を繊維状にして引き取リ、その繊維の外観、手触りでゲル等の発生を評価した。   Using the Capillograph-1B manufactured by Toyo Seiki Co., Ltd., the resin prepared as described above was made into a fiber and taken out, and the appearance of the fiber was evaluated for the appearance of the gel and the like.

条件：ダイの径１ｍｍ、長さ４０ｍｍ
シリンダー温度２５０℃
押出し速度５mm/min.
ストランド（繊維）引取り速度５０m
上記条件で作成したストランドを１ｍ取り出し、そのストランドを親指と人指指の間に挟み、凹凸の有無を評価した。 Conditions: Die diameter 1mm, length 40mm
Cylinder temperature 250 ° C
Extrusion speed 5mm / min.
Strand (fiber) take-up speed 50m
A strand prepared under the above conditions was taken out 1 m, and the strand was sandwiched between a thumb and a finger and evaluated for the presence or absence of irregularities.

Claims (4)

（Ａ）ポリアミド系樹脂２０〜９５質量％
（Ｂ）スチレン系樹脂を含む熱可塑性樹脂（ポリアミド系樹脂は除く）８０〜５質量％、
（Ｃ）酸変性スチレン系樹脂及び酸変性オレフィン系樹脂から選ばれる１種以上を（Ａ）及び（Ｂ）成分の合計１００質量部に対して１〜３０質量部を含んでおり、
カルシウム濃度が２００ppm以下で、マグネシウム濃度が１００ppm以下である、ストランド用樹脂組成物。 (A) Polyamide-based resin 20 to 95% by mass
(B) 80 to 5% by mass of a thermoplastic resin containing a styrene resin (excluding a polyamide resin),
(C) 1 to 30 parts by mass with respect to a total of 100 parts by mass of components (A) and (B) including at least one selected from acid-modified styrene-based resins and acid-modified olefin-based resins,
The resin composition for strands whose calcium concentration is 200 ppm or less and whose magnesium concentration is 100 ppm or less. 芯材の周囲が樹脂被覆されたストランド成形用である、請求項１記載のストランド用樹脂組成物。   The resin composition for a strand according to claim 1, which is for strand molding in which the periphery of the core material is resin-coated. 外径が１ｍｍ以下のストランド成形用である、請求項１又は２記載のストランド用樹脂組成物。   The resin composition for strands according to claim 1 or 2, which is used for forming a strand having an outer diameter of 1 mm or less. 請求項１〜３のいずれか１項記載のストランド用樹脂組成物を押出成形して得られたストランドであり、外径が５００μm以下である、ストランド。   A strand obtained by extrusion-molding the strand resin composition according to any one of claims 1 to 3, and having an outer diameter of 500 µm or less.