JP2004262144A

JP2004262144A - Validity judgement body and label for validity judgement body

Info

Publication number: JP2004262144A
Application number: JP2003056064A
Authority: JP
Inventors: Tae Saito; 多恵齋藤; Takashi Aono; 隆青野; Nobuo Konishi; 展臣小西
Original assignee: Dai Nippon Printing Co Ltd
Current assignee: Dai Nippon Printing Co Ltd
Priority date: 2003-03-03
Filing date: 2003-03-03
Publication date: 2004-09-24
Anticipated expiration: 2023-03-03
Also published as: JP4391103B2

Abstract

<P>PROBLEM TO BE SOLVED: To provide an optical validity judgement body excellent in designability and security properties and a label for the validity judgement body. <P>SOLUTION: The validity judgement body 1 is used in a verification medium 7. Trough parts between minute triangular column prisms of a prism sheet 23 in which the minute triangular column prisms 3 formed of a transparent material approximately in the shape of a straight line are arranged in parallel on a substrate film 2 are filled partially with a transparent or a colored resin 4, and other trough parts are unfilled to leave air layers 8, so that the prism sheet with a constant pattern formed is stuck to the verification medium 7 through an adhesive 5 etc. The label for the validity judgement body is a medium used in the validity judgement body and coated with a peelable protective sheet of paper. <P>COPYRIGHT: (C)2004,JPO&NCIPI

Description

【０００１】
【発明の属する技術分野】
この発明は真偽判定体と真偽判定体用ラベルに関する。
詳しくは、基材フィルム表面に三角柱状プリズム構造体を有し、当該微小三角柱状プリズム間の谷部が部分的に透明または着色樹脂等で充填されているため、認証媒体に使用した場合、目視方向によって特定のパターンが現われることを特徴とする真偽判定体とそれに使用する真偽判定体用ラベルに関する。
このような真偽判定体等は、証券、株券、商品券、ギフト券などの金券類、クレジットカード、プリペイドカード、パスポート、ＩＤカードなどの各種カード、ビデオソフト、パソコン用ソフトなどの、偽造防止、真贋証明用途、等に使用される。
【０００２】
【従来技術】
従来から、証券、株券、商品券、ギフト券などの金券類、クレジットカード、プリペイドカード、パスポート、ＩＤカードなどの各種カード、ビデオソフト、パソコン用ソフトなどの認証シールなど、偽造防止・真偽判定機能の付与が求められる分野において、ホログラムは優れた意匠性、およびカラー複写機で複製できない偽造・変造の困難性から数多く利用されてきた。
しかし、近年、ホログラムにも巧妙な模造品が出現し、一見しただけでは真偽の判別ができない場合があり、目視で容易に判別できる真偽判定体が求められてきている。
【０００３】
そこで、ホログラムを使用しない真偽判定体として光学的特性を有する媒体が考えられる。特許文献１は、光学的セキュリティ物品であるが構成が複雑であり、製造品はコスト高なものになると考えられる。
また、特許文献２は、光拡散シートの製造技術に関し真偽判定体に関わる技術ではないが、本発明の真偽判定体の製造に参照できる技術を記載している。
【０００４】
【特許文献１】特表平１０−５０８５４９号公報
【特許文献２】特開平５−１６９０１５号公報
【０００５】
【発明が解決しようとする課題】
そこで、本発明では、光学的機能を有する簡易な構成の真偽判定体または真偽判定体用ラベルを完成すべく、上記、特許文献２の光拡散シートの光学特性を利用することを着想し、本発明の完成に至ったものである。
【０００６】
【課題を解決するための手段】
上記課題を解決するための本発明の要旨の第１は、基材フィルム上に略直線状であって透明な材質からなる微小三角柱状プリズムが並行して配列しているプリズムシートの、当該微小三角柱状プリズム間の谷部を透明または着色樹脂で部分的に充填し、他の谷部分は充填しないで空気層を残すことにより、一定のパターンが形成されている当該プリズムシートが、粘着剤または接着剤と、支持体と、粘着剤または接着剤と、を介して認証媒体に貼着されている、ことを特徴とする真偽判定体、にある。
【０００７】
上記課題を解決するための本発明の要旨の第２は、基材フィルム上に略直線状であって透明な材質からなる微小三角柱状プリズムが並行して配列しているプリズムシートの、当該微小三角柱状プリズム間の谷部を粘着剤または接着剤で部分的に充填し、他の谷部分は充填しないで空気層を残すことにより、一定のパターンが形成されている当該プリズムシートが、支持体と、粘着剤または接着剤と、を介して認証媒体に貼着されている、ことを特徴とする真偽判定体、にある。
【０００８】
上記課題を解決するための本発明の要旨の第３は、基材フィルム上に略直線状であって透明な材質からなる微小三角柱状プリズムが並行して配列しているプリズムシートの、当該微小三角柱状プリズム間の谷部を粘着剤または接着剤で部分的に充填し、他の谷部分は充填しないで空気層を残すことにより、一定のパターンが形成されている当該プリズムシートが、前記粘着剤または接着剤、を介して認証媒体に貼着されている、ことを特徴とする真偽判定体、にある。
【０００９】
上記課題を解決するための本発明の要旨の第４は、基材フィルム上に略直線状であって透明な材質からなる微小三角柱状プリズムが並行して配列しているプリズムシートの、当該微小三角柱状プリズム間の谷部を透明または着色樹脂で部分的に充填し、他の谷部分は充填しないで空気層を残すことにより、一定のパターンが形成されている当該プリズムシートが、粘着剤または接着剤、を介して認証媒体に貼着されている、ことを特徴とする真偽判定体、にある。
【００１０】
上記課題を解決するための本発明の要旨の第５は、認証媒体に使用するラベルであって、基材フィルム上に略直線状であって透明な材質からなる微小三角柱状プリズムが並行して配列しているプリズムシートの、当該微小三角柱状プリズム間の谷部を透明または着色樹脂で部分的に充填し、他の谷部分は充填しないで空気層を残すことにより、一定のパターンが形成されている当該プリズムシートが、粘着剤または接着剤と、支持体と、粘着剤または接着剤を介して、剥離性保護紙に貼着されている、ことを特徴とする真偽判定体用ラベル、にある。
【００１１】
上記課題を解決するための本発明の要旨の第６は、認証媒体に使用するラベルであって、基材フィルム上に略直線状であって透明な材質からなる微小三角柱状プリズムが並行して配列しているプリズムシートの、当該微小三角柱状プリズム間の谷部を粘着剤または接着剤で部分的に充填し、他の谷部分は充填しないで空気層を残すことにより、一定のパターンが形成されている当該プリズムシートが、支持体と、粘着剤または接着剤を介して、剥離性保護紙に貼着されている、ことを特徴とする真偽判定体用ラベル、にある。
【００１２】
上記課題を解決するための本発明の要旨の第７は、認証媒体に使用するラベルであって、基材フィルム上に略直線状であって透明な材質からなる微小三角柱状プリズムが並行して配列しているプリズムシートの、当該微小三角柱状プリズム間の谷部を粘着剤または接着剤で部分的に充填し、他の谷部分は充填しないで空気層を残すことにより、一定のパターンが形成されている当該プリズムシートが、前記粘着剤または接着剤を介して、剥離性保護紙に貼着されている、ことを特徴とする真偽判定体用ラベル、にある。
【００１３】
上記課題を解決するための本発明の要旨の第８は、認証媒体に使用する真偽判定体であって、基材フィルム上に略直線状であって透明な材質からなる微小三角柱状プリズムが並行して配列しているプリズムシートの、当該微小三角柱状プリズム間の谷部を透明または着色樹脂で部分的に充填し、他の谷部分は充填しないで空気層を残すことにより、一定のパターンが形成されている当該プリズムシートが、粘着剤または接着剤を介して、剥離性保護紙に貼着されている、ことを特徴とする真偽判定体用ラベル、にある。
【００１４】
【発明の実施の形態】
本発明の実施形態を図面を参照して説明することとする。
図１は、本発明の真偽判定体の基本的形態を示す外観斜視図、図２は、第１実施形態、図３は、第２実施形態、図４は、第３実施形態、図５は、第４実施形態、をそれぞれ示す断面図、図６は、真偽判定体用ラベルを示す断面図、である。
図７は、プリズムシートの製造装置を示す図である。
なお、本発明において、真偽判定体とは真偽判定体用ラベルを認証媒体に適用した状態のものをいい、真偽判定体用ラベルとは認証媒体に貼着する前の状態であって、ラベル最下面の粘着剤または接着剤が剥離性の保護紙で被覆されている状態のものをいうものとする。
【００１５】
図１のように、本発明は、基材フィルム２の面上に微小三角柱状プリズム３が並行して配列して形成されているシートを用いる。当該シートをプリズムシート２３というものとする。
本発明の真偽判定体１は、このプリズムシート２３の微小三角柱状プリズム３間に形成される凹んだ谷部分に、透明または着色樹脂４（あるいは粘着剤等であっても良い。）を部分的に充填してから認証媒体７に貼着するための粘着剤または接着剤５を塗工した特徴がある。
図１の真偽判定体１の断面構造では、微小三角柱状プリズムの３ａと３ｂ間、３ｂと３ｃ間、３ｇと３ｈ間、３ｈと３ｉ間に透明または着色樹脂４が充填されていることを示し、充填部分は全体としてハッチングを施してあるパターンＰ部分を形成していることを表示している。
【００１６】
透明樹脂を充填する場合は、透明樹脂の屈折率を微小三角柱状プリズム３の屈折率と近似させることで、樹脂で充填した部分とプリズムが一体になって透明になるので、下面にある認証媒体７を透視することができるようになる。
良好な透明感が得られるためには、透明樹脂と微小三角柱状プリズムの屈折率差が、±０．２以内、より好ましくは±０．１以内であることが好ましい。
一方、樹脂が充填されない微小三角柱状プリズム間の谷部には空気層８が残存することになる。空気と微小三角柱状プリズム樹脂とでは比較的に大きな屈折率差があるので、その界面で全反射が生じ易く認証媒体７の視認が一定の視角範囲でのみ可能となる状態になる。すなわち、樹脂が充填された部分（図１においてＰ領域）は透明性になって認証媒体７が見易く、未充填の部分（同Ｇ領域）は界面で反射するため輝き、認証媒体７自体は見え難い状態になる。
逆にこの輝きを利用して未充填部分が微細なパターンとして残るようにすると、光輝性のある微細パターンが形成される効果を生じる。
【００１７】
樹脂が着色樹脂の場合は、用いる樹脂の屈折率や着色度合いによって一律ではないが、不透明着色樹脂の場合は、一般的には、明瞭な着色パターンが観察されることになる。
図１の場合、谷部の奥行きにおける充填状態が良く分るようには図示されていないが、ハッチングを施してあるパターンＰの下側部分には透明または着色樹脂（あるいは粘着剤等）４が充填されていることを示し、Ｇ部分は未充填の光輝性部分となることを示している。
透明樹脂等を充填したプリズムシート２３は、粘着剤または接着剤５を介して認証媒体７に貼着される。
【００１８】
微小三角柱状プリズム３の高さ（基材フィルム２面から三角柱の頂角部の稜線までの高さ）は１μｍ〜１００μｍ程度、より好ましくは５μｍから２５μｍ程度となる。１μｍ以下では、回折現象が生じ効果が現われなくなり、１００μｍ以上では認証媒体７に貼着する真偽判定体にしては厚みが厚くなり過ぎるからである。各微小三角柱状プリズム３の幅（斜辺長さ）も同程度なので、充填パターンを調整することにより微細な文字や模様を再現することが可能となる。
微小三角柱状プリズム３の断面形状は、二等辺三角形や直角二等辺三角形、あるいは直角三角形等が用いられる。各三角柱の稜線が認証媒体側に向き、斜辺が認証媒体７面に平行するように配置されている。
【００１９】
本発明は、この充填する樹脂と層構成の違いによって、各種の実施形態に分かれるので、以下、順次説明することとする。
本発明の第１実施形態の真偽判定体１は、図２のように、プリズムシート２３の谷部分に透明または着色樹脂４を充填した後、粘着剤または接着剤５ａ、支持体６を介して、粘着剤または接着剤５ｂにより認証媒体７に貼着した構成からなっている。
透明または着色樹脂４が充填されない微小三角柱状プリズム３間の谷部分には空気層８が残存している。第１実施形態の真偽判定体１の特徴は、認証媒体７との間に支持体６を用いることと、粘着剤または接着剤を谷部分に直接充填しないで、透明または着色樹脂４を充填してから粘着剤または接着剤５ａにより支持体６に接着している特徴がある。
【００２０】
このような構成にすることにより、谷部分に安定して樹脂を充填することができ、所望の微細文字や繊細な模様を正しく形成できる利点が生じる。
微細文字や繊細な模様はシルクスクリーン印刷またはグラビア印刷方式により好適に形成することができる。充填は谷部分の全体を稜線の高さまで一杯になるように、かつ稜線の高さを超えないように均一に充填するのが好ましいが、多少空気層が残るような充填であっても谷の深部を樹脂が埋めることにより、光の反射が緩和され、透明性を高める効果を生じる。
【００２１】
プリズムシート２３に印刷した後は、支持体６とプリズムシート２３とをラミネートし、ラミネート後は、剥離処理した保護紙に粘着剤または接着剤５ｂを塗工したものと支持体６を一体にすることにより、粘着剤または接着剤５ｂを設ける。したがって、認証媒体７に貼着する前の真偽判定体１は、図６に図示するように、粘着剤または接着剤５ｂに剥離性保護紙９が被覆された真偽判定体用ラベル１Ｌになる。
【００２２】
本発明の第２実施形態の真偽判定体１は、図３のように、プリズムシート２３の谷部分に粘着剤または接着剤５ａを充填した後、支持体６を全体に被覆している。この場合は、粘着剤または接着剤５ａが充填樹脂の役割と支持体６を接着する役割をしていることになる。したがって、充填する面積が僅かな場合は、支持体６を接着する部分も僅かになり、接着機能を果たさないことになる。
ただし、このような真偽判定体パターンでは微細文字を全面に設けるような場合が多いので、微細文字のネガパターンとして充填される粘着剤または接着剤５ａは通常はかなり広い面積になるので、安定した接着が確保できる。
充填されない微小三角柱状プリズム３間の谷部分には空気層８が残存するのは第１実施形態と同様である。
【００２３】
粘着剤または接着剤５ａの充填もシルクスクリーン印刷またはグラビア印刷方式により行うことができる。プリズムシート２３に印刷と同時に支持体６をラミネートするか、ホットメルト接着剤パターンを印刷してから別の工程で、支持体６をラミネートすることができる。
ラミネート後は、剥離処理した保護紙に粘着剤または接着剤５ｂを塗工したものと支持体６を一体にすることにより、粘着剤または接着剤５ｂを設ける。
【００２４】
本発明の第３実施形態の真偽判定体１は、図４のように、プリズムシート２３の谷部分に粘着剤または接着剤５を充填し、この状態のままで認証媒体７に貼着するものである。この場合は、粘着剤または接着剤５が充填樹脂の役割と認証媒体７を接着する役割をする必要があるので、粘着剤または接着剤５は谷部分を埋めるだけでなく、やや厚めに塗布する必要がある。
【００２５】
第３実施形態の真偽判定体は、粘着剤または接着剤５の充填と同時に剥離性保護紙９と一体にする工程が必要である。通常は、剥離性保護紙９側にパターン状に粘着剤または接着剤５を塗布し、プリズムシート２３と一体にする工程を行うが、プリズムシート２３側に粘着剤または接着剤５をパターン塗布してから、剥離性保護紙９と一体にする工程を行っても良い。
第３実施形態に使用する粘着剤または接着剤５は、塗布後、直ちに乾燥して固化するものではなく長期間にわたって粘着性を保持する状態にあるものが求められる。
第３実施形態の真偽判定体１は、使用材料が少ないので、安価品の製造には好適であるが、微細文字や繊細な模様の再現はやや困難となる。
【００２６】
本発明の第４実施形態の真偽判定体１は、図５のように、プリズムシート２３の谷部分に透明または着色樹脂４を充填した後、粘着剤または接着剤５をプリズムシート２３の下面全体に設けている。
この場合も通常は、剥離性保護紙９側にパターン状に粘着剤または接着剤５を塗布し、プリズムシートと一体にする工程を行うが、プリズムシート２３側に粘着剤または接着剤５を全面塗布してから、剥離性保護紙９と一体にする工程を行っても良い。
第４実施形態の真偽判定体１は、透明または着色樹脂４の充填されない谷部分に粘着剤または接着剤５が充填されると、樹脂パターンの鮮明が失われ易い問題がある。したがって、粘着剤または接着剤５を適切な粘度状態により塗布する工程が必要となる。
【００２７】
本発明の真偽判定体用ラベル１Ｌは、図６のようになる。図６（Ａ）は、第１実施形態の場合、図６（Ｂ）は、第２実施形態の場合の真偽判定体用ラベル、を示している。第３、第４の場合も同様であるので図示は省略している。
真偽判定体用ラベル１Ｌは、認証媒体７に貼着する前の状態であり、最下面の粘着剤または接着剤５，５ｂが剥離性保護紙９で覆われている。認証媒体に貼着する場合は、当該剥離性保護紙９を除去して貼着する。
保護紙９はシリコーン加工等により剥離性とする場合が多い。
【００２８】
以上のように、４種の実施形態の真偽判定体１および真偽判定体用ラベル１Ｌについて説明したが、本発明は各種の変形実施態様が可能である。
例えば、支持体６のプリズムシート２３側面に微細な文字、模様等の印刷を施せば、セキュリティー性を高めることができる。また、支持体６を透明な樹脂フィルムと印刷した紙またはフィルム基材のラミネート体とし、当該紙またはフィルム基材のプリズムシート２３側面に前記印刷を施したものとしても良い。
【００２９】
次に、真偽判定体に使用するプリズムシートの製造工程について説明する。
図７は、プリズムシートの製造装置である。図７において、１０は三角柱状プリズムの凹部が形成されたロール凹版、１１はそのロール凹版の凹部、１２は電離放射線硬化性樹脂液をロール凹版１０に塗工するための塗工装置、１３は電離放射線硬化性樹脂液、２は基材フィルム、１４は溶剤乾燥装置、１５，１６は硬化装置、１７はロール凹版に当接してロール凹版１０を押圧する押圧ロール、１８は送りロール、である。
なお、図７において、三角柱状プリズムを形成するための凹部１１が基材フィルム２の流れ方向に直交するように図示さているが、基材フィルム２の流れ方向に平行に形成されていても良いものとする。
【００３０】
プリズムシートの製造工程は、充填工程、接触工程、硬化工程、密着工程、剥離工程に分類することができる。
プリズムシートの製造工程における充填工程は、三角柱状プリズムの型が形成されたロール凹版１０を回転させ、そのロール凹版１０の少なくとも凹部１１に電離放射線硬化性樹脂液１３を充填する工程である。
接触工程は、充填工程で充填された電離放射線硬化性樹脂液１３に対して、ロール凹版１０の回転方向に同期して走行する基材フィルム２を接触させる工程である。
【００３１】
硬化工程は、接触工程で基材フィルム２がロール凹版１０に接触している間に、ロール凹版１０と基材フィルム２間にある電離放射線硬化性樹脂液１３に、硬化装置１５からの電離放射線を照射して硬化させる工程である。
密着工程は、硬化工程で硬化する電離放射線硬化性樹脂液１３と基材フィルム２とを密着させる工程である。なお、硬化工程と密着工程は、通常同時に進行する。剥離工程は、密着工程で密着した電離放射線硬化性樹脂液１３の半硬化物１３ａと基材フィルム２をロール凹版１０から剥離する工程である。
【００３２】
ロール凹版１０は、円筒状の版材に所定形状の凹部１１を設けたものである。このロール凹版は、版材を旋盤等で直接切削したり、電鋳法で型付けしたりすることができる。
塗工装置１２は、電離放射線硬化性樹脂液１３をロール凹版１０に塗工するための装置であって、ノズル塗工装置を用いることが多い。ノズル塗工装置は、所定寸法のノズルがＴダイ状の長方形または線状の吐出口を有し、その吐出口の長手方向がロール凹版回転方向と直交する方向に設置されていて、ロール凹版の全幅のうち所定の幅部分にのみ樹脂液を吐出するようにされている。
【００３３】
溶剤乾燥装置１４は、樹脂の溶剤を揮発させるための装置である。溶剤乾燥装置１４としては、温風や赤外線ヒータ等を用いることができる。この溶剤乾燥装置１４を設けることにより、溶剤型の樹脂を用いることができ、使用する樹脂の選択の幅を広げることができる。なお、無溶剤型の電離放射線硬化性樹脂液１３を用いる場合には、溶剤乾燥装置１４は不使用となる。
【００３４】
硬化装置１５は、電離放射線を照射して、電離放射線硬化性樹脂液１３を硬化させる装置である。なお、剥離工程後に脱離した電離放射線硬化性樹脂液の半硬化物１３ａを完全に硬化させるために、硬化装置１６を設けてもよい。
ここで、電離放射線とは、電磁波または荷電粒子線のうち、分子を重合、架橋し得るエネルギー量子を有するものを意味し、通常、紫外線、電子線等が用いられる。硬化装置１５，１６として紫外線の場合には、超高圧水銀灯、ブラックライトランプ、キセノンランプ、メタルハライドランプ灯の光源を用いることができる。
【００３５】
＜プリズムシートの製造＞
上記装置によるプリズムシートの製造方法は、まず、ロール凹版１０の凹部１１に、電離放射線硬化性樹脂液１３を塗工装置１２により充填し、基材フィルム２をロール凹版１０の凹部１１に充填させた電離放射線硬化性樹脂液１３に接するように接触させる。
電離放射線硬化性樹脂液１３を凹部１１に充填する方法としては、ロール凹版１０の表面に予め電離放射線硬化性樹脂液１３を所定量塗工しておいて、基材フィルム２をロール凹版１０面に供給したときに、押圧ロール１７の押圧により、基材フィルム２を介して、塗工されている電離放射線硬化性樹脂液１３を凹部１１内に配分充填させる。
【００３６】
この場合に、溶剤タイプの硬化性樹脂が使用でき、基材フィルム２に塗工された電離放射線硬化性樹脂液１３は、流動性をある程度制御するために、その樹脂液の溶剤を希釈するために使用した溶剤などを溶剤乾燥装置１４により乾燥除去し、さらに硬化装置１５により溶剤を乾燥した樹脂液を半硬化させる。
【００３７】
基材フィルム２がロール凹版１０に接している間に、硬化装置１５により電離放射線硬化性樹脂液１３を硬化させる。硬化装置は必要により、ロール凹版の回転方向に沿って複数個設けることができる。多段による硬化により硬化物の歪みや基材フィルム２のカール等を低減させることができる。
また、ロール凹版１０を石英、ガラス等の電離放射線の透過性がよい材質により形成して、ロール凹版１０の内部側から照射することもできる。
【００３８】
硬化装置１５により、ロール凹版１０の凹部１１内にある電離放射線硬化性樹脂液１３を基材フィルム２に密着させる。このとき、硬化度合は、少なくとも樹脂の流動性を失わせ、かつ、基材フィルム２との密着性を生じさせる程度であればよい。
硬化装置１５を通過した後、基材フィルム２をロール凹版１０から剥離する。これにより、半硬化した電離放射線硬化性樹脂液１３ａが基材フィルム２と一体になって、凹部１１から脱離され、三角柱状プリズム化された表面を有するプリズムシートが得られる。
【００３９】
＜材質に関する実施形態＞
（１）基材フィルム
基材フィルムとしては、透明性のある高分子フィルムが加工適性の点からも好ましい。高分子フィルムの素材のプラスチックとしてはポリエチレン樹脂、ポリプロピレン樹脂、ポリメチルペンテン樹脂、ポリ塩化ビニル樹脂、ポリ塩化ビニリデン樹脂、ポリビニルアルコール樹脂、塩化ビニル−酢酸ビニル共重合樹脂、エチレン−酢酸ビニル共重合樹脂、エチレン−ビニルアルコール共重合樹脂、ポリエチレンテレフタレート樹脂、ポリブチレンテレフタレート樹脂、ポリエチレンナフタレート−イソフタレート共重合樹脂、ポリメタクリル酸メチル樹脂、ポリカーボネート樹脂、ポリアリレート樹脂、ポリイミド樹脂、ポリスルホン樹脂、アクリル樹脂等が使用できる。また、液晶材料を使用することもできる。
この基材の厚みは、加工のしやすさ等の観点から１２〜１００μｍ程度の範囲、好ましくは１５〜５０μｍ程度のものが好ましい。あまり厚くない方が、認証媒体の視認のためには好ましいからである。
【００４０】
（２）三角柱状プリズム材料
三角柱状プリズム材料は特に制約はないが、加工適性の点から樹脂材料が好ましい。また、プリズム特性から透明または着色透明であることが求められる。
上述した紫外線硬化樹脂でプリズム形状を形成する製造方法では、紫外線硬化型の電離放射線硬化性樹脂液が好ましく使用される。
このような樹脂液の具体例としては、分子中に重合性不飽和結合またはエポキシ基を有するプレポリマー、オリゴマーおよび／または単量体を適宜混合した組成物を用いることができる。
【００４１】
前記プレポリマー、オリゴマーとしては、不飽和ジカルボン酸と多値アルコールの縮合物等の不飽和ポリエステル類、エポキシ樹脂、ポリエステルメタクリレート、ポリエーテルメタクリレート、ポリオールメタクリレート、メラミンメタクリレート等のメタクリレート類、ポリエステルアクリレート、エポキシアクリレート、ウレタンアクリレート、ポリエーテルアクリレート、ポリオールアクリレート、メラミンアクリレート等のアクリレート類等があげられる。
【００４２】
また、単量体としては、スチレン、α−メチルスチレン等のスチレン系単量体、アクリル酸メチル、アクリル酸−２−エチルヘキシル、アクリル酸メトキシエチル、アクリル酸ブチル、等のアクリル酸エステル類、メタクリル酸メチル、メタクリル酸エチル、メタクリル酸メトキシエチル、メタクリル酸メトキシメチル等のメタクリル酸エステル類、アクリル酸−２−（Ｎ，Ｎ−ジエチルアミノ）エチル等の不飽和の置換アミノアルコールエステル類、アクリルアミド、メタクリルアミド等の不飽和カルボン酸アミド、ジプロピレングリコールジアクリレート、エチレングリコールアクリレート、プロピレングリコールジメタクリレート、ジエチレングリコールジメタクリレート等の多官能性化合物、ビニルピロリドン、および／または分子中に２個以上のチオール基を有するポリチオール化合物、例えば、トリメチロールプロパントリチオグリコレート、トリメチロールプロパントリチオプロピレート、ペンタエリスリトールテトラチオグリコール等があげられる。
【００４３】
特に、紫外線によって硬化させる場合には、前記電離放射線硬化性樹脂の組成物に光重合開始剤として、アセトフェノン類、ベンゾフェノン類、ミヒラーベンゾイルベンゾエート、α−アミロキシムエステル、テトラメチルメウラムモノサルファイド、チオキサントン類、及び／又は光増感剤としてｎ−ブチルアミン、トリエチルアミン、トリ−ｎ−ブチルホスフィン等を混合して用いることもできる。また、プリズムの微細な凹部１１を持ったロール凹版１０の形状を忠実に再現するためには、粘度は５０００ｃｐｓ以下、特に１０００ｃｐｓ以下にすることが好ましい。なお、プリズムを着色透明にする場合は硬化を阻害しない染料を添加しても良い。
【００４４】
（３）透明または着色樹脂
三角柱状プリズムの谷部に充填する透明または着色樹脂は、特に材質を問われないが、三角柱状プリズム材料と屈折率が近いものを選択して使用する。
各種高分子樹脂の屈折率は、１．４〜１．６程度になり、例えば、ポリブチルアクリレート（１．４４）、ポリエチルアクリレート（１．４７）、ポリメチルアクリレート（１．４７）、ポリｎ−ブチルメタクリレート（１．４８）、ポリメチルメタクリレート（１．４９）、ポリ酢酸ビニル（１．４７）、ポリプロピレン（１．４９〜１．５０）、ポリエチレン（１．５〜１．５５）、ポリカーボネート（１．５８）、ポリスチレン（１．５９〜１．６０）、ポリエチレンテレフタレート（１．６４）、ポリ塩化ビニル（１．５４）、ポリ塩化ビニリデン（１．６０〜１．６３）、等の使用が可能である。
印刷法で充填する場合は、顔料や染料等の着色剤を用いないビヒクルのみからなるメジュームインキを用いてることができる。充填樹脂を着色する場合は、適宜に染料や顔料を使用する。
【００４５】
（４）支持体
第１、第２実施形態で使用する支持体６には、基材フィルムと同様な材料を使用できるが、厚みは、１０〜３０μｍのものであって良い。
ただし、必ずしも透明である必要はなく、目的により不透明なものも使用できる。平滑であれば紙であっても良く、支持体面に印刷が施されているものであっても良い。
【００４６】
（５）粘着剤または接着剤
透明性のある粘着剤または接着剤を種類を問わず使用することができる。
粘着剤または接着剤を充填樹脂の役割を兼ねて使用する場合は、前記の透明または着色樹脂と同様に屈折率を考慮する必要がある。
通常は、天然ゴム、再生ゴム、ＳＢＲ等のエラストマーと低分子量あるいは中程度の分子量の粘着付与剤、酸化防止剤などの混合物を溶液状態で粘着剤として用いることができる。熱可塑性エラストマーの場合は溶融状態での塗布が可能である。光および酸化に対する抵抗性が必要な場合は、アクリレートコポリマーやポリイソブチレン等の材料を使用する。
ホットメルト型のヒートシール剤を用いても良い。印刷法でパターン形成する場合は特に印刷適性を考慮したものが必要となる。
粘着剤または接着剤の塗工厚みは、１〜５０μｍ程度で、プリズムの高さによって調整する。
【００４７】
【実施例】
図１、図２、図３、図６等を参照して本発明の実施例を説明する。
（実施例１）
厚み５０μｍのポリエチレンテレフタレートフィルム（ＰＥＴ）基材フィルム２上に、ウレタンアクリレート系の紫外線硬化性樹脂液を硬化させる方法によって、図１のように、断面の高さ２５μｍ、頂角が９０度の直角二等辺三角形状プリズムシート２３を製造した。
その後、透明なアクリル系インキ（東洋インキ株式会社製「ＳＳ８−８００メジューム」）を用いて、上記プリズムシート２３のプリズム間の谷部を埋めるように、シルクスクリーン印刷法で「ＡＢＣ」の微細文字がネガパターンで印刷されるように印刷した。
【００４８】
次に、厚み２５μｍのＰＥＴフィルムに、ポリエステル系ヒートシール剤を厚み５μｍに塗布し、直後に前記印刷済みのプリズムシート２３のプリズム面に貼り合わせするラミネートを行った。ラミネートはロール温度１５０°Ｃで、速度０．８ｍ／ｍｉｎの条件で行った。最後に、シリコーン加工により剥離処理した保護紙９に粘着剤を塗工して、上記２５μｍ厚のＰＥＴフィルム面に貼り合わせする加工を行った。これにより本発明の第１実施形態の真偽判定体用ラベル１Ｌが完成した（図６（Ａ））。
【００４９】
この真偽判定体用ラベルの剥離性保護紙９を除去し、顔写真付き磁気カードの顔写真面に貼着することにより、本発明の真偽判定体１が得られた（図２）。
この真偽判定体１を観察すると顔写真が鮮明に観察できると共に、ある角度では「ＡＢＣ」の微細文字が輝いて見え、意匠性の高い磁気カードが得られた。
【００５０】
（実施例２）
厚み５０μｍのポリエチレンテレフタレートフィルム（ＰＥＴ）基材フィルム２上に、ウレタンアクリレート系の紫外線硬化性樹脂液を硬化させる方法によって、図１のように、断面の高さ１５μｍ、頂角が９０度の直角二等辺三角形状プリズムシート２３を製造した。
その後、透明なポリエステル系ホットメルトインキ（試作インキ）を用いて、上記プリズムシート２３のプリズム間の谷部を埋めるように、グラビア印刷法で「ＡＢＣ」の文字がネガパターンで印刷されるように印刷すると共に、同時に厚み２５μｍのＰＥＴフィルムとラミネートする加工を行った。
この際、ホットメルトインキのインキパンを加熱してインキが溶融状態を保つようにした。
【００５１】
最後に、シリコーン加工により剥離処理した保護紙９に粘着剤を塗工して、上記２５μｍ厚のＰＥＴフィルム面に貼り合わせる加工を行った。これにより本発明の第２実施形態の真偽判定体用ラベル１Ｌが完成した（図６（Ｂ））。
この真偽判定体用ラベル１Ｌの剥離性保護紙９を除去して、商品券面の微細模様上に貼着することにより、本発明の真偽判定体１が得られた（図３）。
この真偽判定体１を観察すると微細模様が鮮明に観察できると共に、ある角度では「ＡＢＣ」の微細文字が輝いて見え、意匠性の高い商品券が得られた。
【００５２】
【発明の効果】
以上、詳述のように本発明の真偽判定体または真偽判定体用ラベルによれば以下の効果が得られる。
本発明の真偽判定体は、反射層の形成等の特別の加工を行っていないが、目視方向によって光輝性の文字や模様を観察でき意匠性が高い認証媒体となる。
また、目視方向によって光輝性の文字や模様と認証媒体自体が有する模様や写真とが切り替わって見えるので、そのような状態変化を伴わない認証媒体と対比して、直ちに真偽を判定することができる。
真偽判定体用ラベルの貼着された認証媒体は複写機で正常に複写することができず、偽造、模造を防止できる。したがって、セキュリティー性の高い認証媒体となる。
【図面の簡単な説明】
【図１】本発明の真偽判定体の基本的形態を示す外観斜視図である。
【図２】第１実施形態を示す断面図である。
【図３】第２実施形態を示す断面図である。
【図４】第３実施形態を示す断面図である。
【図５】第４実施形態を示す断面図である。
【図６】真偽判定体用ラベルを示す断面図である。
【図７】プリズムシートの製造装置を示す図である。
【符号の説明】
１真偽判定体
１Ｌ真偽判定体用ラベル
２基材フィルム
３微小三角柱状プリズム
４透明または着色樹脂
５，５ａ，５ｂ粘着剤または接着剤
６支持体
７認証媒体
８空気層
９剥離性保護紙
１０ロール凹版
１１凹部
１２塗工装置
１３電離放射線硬化性樹脂液
１４溶剤乾燥装置
１５，１６硬化装置
１７押圧ロール
１８送りロール
２３プリズムシート[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to a true / false judgment body and a true / false judgment body label.
Specifically, since the base film has a triangular prism-shaped prism structure on the surface thereof and the valleys between the minute triangular prisms are partially filled with a transparent or colored resin or the like, when used as an authentication medium, The present invention relates to a genuine / judgment body characterized in that a specific pattern appears depending on a direction and a genuine / judgment body label used therefor.
Such authenticity determination bodies can be used to prevent counterfeiting of securities such as securities, stock certificates, gift certificates, gift certificates, various types of cards such as credit cards, prepaid cards, passports, ID cards, video software, and personal computer software. It is used for authentication verification.
[0002]
[Prior art]
Conventionally, counterfeiting prevention / authentication judgment, such as vouchers such as securities, stock certificates, gift certificates, gift certificates, various cards such as credit cards, prepaid cards, passports, ID cards, authentication seals for video software, personal computer software, etc. Holograms have been widely used in fields requiring the addition of functions because of their excellent design properties and the difficulty of counterfeiting or alteration that cannot be reproduced by a color copying machine.
However, in recent years, clever imitations have appeared in holograms, and in some cases, it is not possible to determine the authenticity at a glance.
[0003]
Therefore, a medium having optical characteristics as a true / false judgment body that does not use a hologram is conceivable. Patent Document 1 is an optical security article, but the configuration is complicated, and it is considered that the manufactured product is expensive.
Patent Document 2 describes a technology that can refer to the manufacturing of the authenticity determination body of the present invention, although the technology is not related to the authenticity determination body in the light diffusion sheet manufacturing technology.
[0004]
[Patent Document 1] Japanese Patent Publication No. Hei 10-508549
[Patent Document 2] Japanese Patent Application Laid-Open No. 5-169015
[0005]
[Problems to be solved by the invention]
Therefore, in the present invention, in order to complete a true / false judgment body or a true / false judgment body label having a simple configuration having an optical function, it is conceived to utilize the optical characteristics of the light diffusion sheet of Patent Document 2 described above. Thus, the present invention has been completed.
[0006]
[Means for Solving the Problems]
The first aspect of the present invention for solving the above-mentioned problem is that a prism sheet in which minute triangular prisms made of a substantially linear and transparent material are arranged in parallel on a base film, By partially filling the valleys between the triangular prisms with a transparent or colored resin and leaving the air layer without filling the other valleys, the prism sheet in which a certain pattern is formed is an adhesive or A genuine / judgment body characterized by being attached to an authentication medium via an adhesive, a support, and an adhesive or an adhesive.
[0007]
A second aspect of the present invention for solving the above-mentioned problem is that a prism sheet in which minute triangular prisms made of a substantially linear and transparent material are arranged in parallel on a base film, By partially filling the valleys between the triangular prisms with an adhesive or an adhesive and leaving the air layer without filling the other valleys, the prism sheet in which a certain pattern is formed is a support. And an adhesive or an adhesive, which is attached to the authentication medium via the authenticity determination body.
[0008]
A third aspect of the present invention for solving the above-mentioned problem is that a prism sheet in which fine triangular prisms made of a substantially linear and transparent material are arranged in parallel on a base film, By partially filling the valleys between the triangular prisms with an adhesive or an adhesive and leaving the air layer without filling the other valleys, the prism sheet in which a certain pattern is formed is formed by the adhesive. A true / false judgment body, which is attached to an authentication medium via an agent or an adhesive.
[0009]
A fourth aspect of the present invention for solving the above-mentioned problem is that a prism sheet in which minute triangular prisms made of a substantially linear and transparent material are arranged in parallel on a base film, By partially filling the valleys between the triangular prisms with a transparent or colored resin and leaving the air layer without filling the other valleys, the prism sheet in which a certain pattern is formed is an adhesive or A true / false judgment body, which is attached to an authentication medium via an adhesive.
[0010]
A fifth aspect of the present invention for solving the above problems is a label used for an authentication medium, in which a substantially triangular prism made of a substantially linear and transparent material is arranged in parallel on a base film. A certain pattern is formed by partially filling the valleys between the micro triangular prisms of the arranged prism sheets with the transparent or colored resin and leaving the air layer without filling other valleys. The prism sheet, which is an adhesive or an adhesive, a support, and an adhesive or an adhesive, is adhered to a peelable protective paper, a label for authenticity determination body, characterized in that It is in.
[0011]
A sixth aspect of the present invention for solving the above problems is a label used for an authentication medium, in which a substantially triangular prism made of a substantially linear and transparent material is arranged in parallel on a base film. A fixed pattern is formed by partially filling the valleys between the minute triangular prisms of the arranged prism sheet with the adhesive or the adhesive and leaving the air layer without filling other valleys. Wherein the prism sheet is attached to a peelable protective paper via a support and an adhesive or an adhesive.
[0012]
A seventh aspect of the present invention for solving the above problems is a label used for an authentication medium, in which a substantially triangular prism made of a substantially linear and transparent material is formed in parallel on a base film. A fixed pattern is formed by partially filling the valleys between the minute triangular prisms of the arranged prism sheet with the adhesive or the adhesive and leaving the air layer without filling other valleys. Wherein the prism sheet is adhered to the peelable protective paper via the pressure-sensitive adhesive or the adhesive.
[0013]
Eighth of the gist of the present invention for solving the above-mentioned problem is a true / false judgment body used for an authentication medium, wherein a fine triangular prism made of a substantially linear and transparent material is provided on a base film. A certain pattern is formed by partially filling the valleys between the micro triangular prisms of the prism sheets arranged in parallel with the transparent or colored resin and leaving the air layer without filling the other valleys. Wherein the prism sheet on which is formed is adhered to a peelable protective paper via an adhesive or an adhesive.
[0014]
BEST MODE FOR CARRYING OUT THE INVENTION
An embodiment of the present invention will be described with reference to the drawings.
FIG. 1 is an external perspective view showing a basic form of the authenticity determination body of the present invention, FIG. 2 is a first embodiment, FIG. 3 is a second embodiment, FIG. 4 is a third embodiment, and FIG. Is a sectional view showing a fourth embodiment, and FIG. 6 is a sectional view showing a label for authenticity determination body.
FIG. 7 is a view showing a prism sheet manufacturing apparatus.
In the present invention, the authenticity judgment body refers to a state in which the authenticity judgment body label is applied to the authentication medium, and the authenticity judgment body label is a state before being attached to the authentication medium. The lowermost surface of the label is covered with a pressure-sensitive adhesive or adhesive with a peelable protective paper.
[0015]
As shown in FIG. 1, the present invention uses a sheet in which minute triangular prisms 3 are arranged in parallel on the surface of a base film 2. The sheet is referred to as a prism sheet 23.
In the authenticity determination body 1 of the present invention, a transparent or colored resin 4 (or an adhesive or the like) may be provided in a concave valley portion formed between the minute triangular prisms 3 of the prism sheet 23. It is characterized in that a pressure-sensitive adhesive or an adhesive 5 for sticking to the authentication medium 7 is applied after the filling is completed.
The cross-sectional structure of the authenticity determination body 1 shown in FIG. 1 indicates that the transparent or colored resin 4 is filled between the small triangular prisms 3a and 3b, 3b and 3c, 3g and 3h, and 3h and 3i. This indicates that the filled portion forms a hatched pattern P portion as a whole.
[0016]
When the transparent resin is filled, the refractive index of the transparent resin is approximated to the refractive index of the small triangular prism 3 so that the resin-filled portion and the prism become transparent integrally, so that the authentication medium on the lower surface is formed. 7 can be seen through.
In order to obtain a good transparency, the difference in the refractive index between the transparent resin and the micro triangular prism is preferably within ± 0.2, more preferably within ± 0.1.
On the other hand, the air layer 8 remains in the valley between the minute triangular prisms not filled with the resin. Since there is a relatively large difference in the refractive index between air and the micro triangular prism resin, total reflection easily occurs at the interface, and the authentication medium 7 can be viewed only within a certain viewing angle range. That is, the portion filled with the resin (the P region in FIG. 1) is transparent and the authentication medium 7 is easy to see, and the unfilled portion (the G region) is reflected at the interface and shines, and the authentication medium 7 itself is visible. It becomes difficult.
Conversely, if the unfilled portion is left as a fine pattern by utilizing this brightness, an effect of forming a glittering fine pattern is produced.
[0017]
When the resin is a colored resin, it is not uniform depending on the refractive index and the degree of coloring of the resin used, but when the resin is an opaque colored resin, a clear colored pattern is generally observed.
In the case of FIG. 1, the filling state at the depth of the valley is not shown so as to be well understood, but a transparent or colored resin (or an adhesive or the like) 4 is provided below the hatched pattern P. It shows that it is filled, and the G portion shows that it is an unfilled glittering portion.
The prism sheet 23 filled with a transparent resin or the like is attached to the authentication medium 7 via an adhesive or an adhesive 5.
[0018]
The height of the triangular prism 3 (the height from the surface of the base film 2 to the ridgeline at the apex of the triangular prism) is about 1 μm to 100 μm, and more preferably about 5 μm to 25 μm. If the thickness is 1 μm or less, a diffraction phenomenon occurs, and no effect appears. If the thickness is 100 μm or more, the thickness becomes too large for the authenticity determination body to be attached to the authentication medium 7. Since the width (the length of the oblique side) of each of the triangular prisms 3 is substantially the same, fine characters and patterns can be reproduced by adjusting the filling pattern.
As the cross-sectional shape of the minute triangular prism 3, an isosceles triangle, a right-angled isosceles triangle, a right-angled triangle, or the like is used. The ridges of the triangular prisms are arranged so as to face the authentication medium, and the oblique sides are parallel to the surface of the authentication medium 7.
[0019]
The present invention is divided into various embodiments depending on the difference between the resin to be filled and the layer configuration, and will be sequentially described below.
As shown in FIG. 2, the authenticity determination body 1 according to the first embodiment of the present invention fills the valley portion of the prism sheet 23 with the transparent or colored resin 4 and then passes through the adhesive or the adhesive 5 a and the support 6. Thus, it is configured to be adhered to the authentication medium 7 with an adhesive or an adhesive 5b.
An air layer 8 remains in a valley between the small triangular prisms 3 not filled with the transparent or colored resin 4. The features of the authenticity determination body 1 of the first embodiment are that the support 6 is used between the authentication medium 7 and the transparent or colored resin 4 is filled without directly filling the valley with an adhesive or an adhesive. After that, it is characterized in that it is adhered to the support 6 with an adhesive or an adhesive 5a.
[0020]
With such a configuration, the resin can be stably filled in the valley portion, and there is an advantage that desired fine characters and delicate patterns can be formed correctly.
Fine characters and delicate patterns can be suitably formed by silk screen printing or gravure printing. It is preferable to uniformly fill the valley portion so as to fill the entire valley to the height of the ridgeline and not to exceed the height of the ridgeline. By filling the deep portion with the resin, the reflection of light is reduced, and an effect of increasing transparency is produced.
[0021]
After printing on the prism sheet 23, the support 6 and the prism sheet 23 are laminated, and after laminating, the support 6 is integrated with a protective paper that has been subjected to a release treatment and coated with an adhesive or an adhesive 5b. Thereby, an adhesive or an adhesive 5b is provided. Therefore, as shown in FIG. 6, the authenticity determination body 1 before being attached to the authentication medium 7 is attached to the authenticity determination body label 1L in which the adhesive or adhesive 5b is covered with the peelable protection paper 9. Become.
[0022]
In the authenticity determination body 1 according to the second embodiment of the present invention, as shown in FIG. 3, after filling a valley portion of the prism sheet 23 with an adhesive or an adhesive 5 a, the support body 6 is entirely covered. In this case, the pressure-sensitive adhesive or the adhesive 5a has a role of a filling resin and a role of bonding the support 6. Therefore, when the area to be filled is small, the portion where the support 6 is bonded becomes small, and the bonding function is not performed.
However, in such a true / false judgment body pattern, a fine character is often provided on the entire surface, so that the pressure-sensitive adhesive or the adhesive 5a filled as a negative pattern of the fine character usually has a considerably large area, and thus is stable. Adhered bonding can be secured.
As in the first embodiment, the air layer 8 remains in the valleys between the small triangular prisms 3 that are not filled.
[0023]
The filling of the adhesive or the adhesive 5a can also be performed by silk screen printing or gravure printing. The support 6 can be laminated at the same time as printing on the prism sheet 23, or the support 6 can be laminated in another step after printing a hot melt adhesive pattern.
After lamination, the adhesive or the adhesive 5b is provided by integrating the support 6 with the adhesive or the adhesive 5b coated on the peeled protective paper.
[0024]
In the authenticity determination body 1 according to the third embodiment of the present invention, as shown in FIG. 4, a trough portion of the prism sheet 23 is filled with an adhesive or an adhesive 5 and adhered to the authentication medium 7 in this state. Things. In this case, since the pressure-sensitive adhesive or the adhesive 5 needs to play the role of the filling resin and the role of bonding the authentication medium 7, the pressure-sensitive adhesive or the adhesive 5 not only fills the valleys but also is applied slightly thicker. There is a need.
[0025]
The authenticity determination body of the third embodiment requires a step of integrating with the releasable protection paper 9 at the same time as the filling of the adhesive or the adhesive 5. Usually, a step of applying a pressure-sensitive adhesive or an adhesive 5 on the side of the releasable protective paper 9 in a pattern and performing integration with the prism sheet 23 is performed. After that, a step of integrating with the peelable protective paper 9 may be performed.
The pressure-sensitive adhesive or adhesive 5 used in the third embodiment is not required to be dried and solidified immediately after application, but to be in a state of maintaining tackiness for a long period of time.
The authenticity determination body 1 of the third embodiment is suitable for the production of inexpensive products because it uses a small amount of material, but it is somewhat difficult to reproduce fine characters and delicate patterns.
[0026]
In the authenticity determination body 1 according to the fourth embodiment of the present invention, as shown in FIG. 5, after filling the valley portion of the prism sheet 23 with the transparent or colored resin 4, the adhesive or the adhesive 5 is applied to the lower surface of the prism sheet 23. Provided throughout.
Also in this case, usually, a step of applying an adhesive or an adhesive 5 in a pattern on the peelable protective paper 9 side and integrating the adhesive or the adhesive 5 with the prism sheet is performed. After the application, a step of integrating with the peelable protective paper 9 may be performed.
The authenticity determination body 1 according to the fourth embodiment has a problem in that the clearness of the resin pattern is easily lost when the adhesive or the adhesive 5 is filled in the valley portion where the transparent or colored resin 4 is not filled. Therefore, a step of applying the pressure-sensitive adhesive or the adhesive 5 in an appropriate viscosity state is required.
[0027]
The label 1L for authenticity determination body of the present invention is as shown in FIG. FIG. 6A shows a label for authenticity determination body in the case of the first embodiment, and FIG. 6B shows a label for authenticity determination body in the case of the second embodiment. Since the same applies to the third and fourth cases, illustration is omitted.
The label for authenticity determination body 1L is in a state before being attached to the authentication medium 7, and the adhesive or adhesive 5, 5b on the lowermost surface is covered with the peelable protective paper 9. When sticking on an authentication medium, the peelable protective paper 9 is removed before sticking.
The protection paper 9 is often made releasable by silicone processing or the like.
[0028]
As described above, the authenticity determination body 1 and the authenticity determination body label 1L of the four embodiments have been described, but the present invention is capable of various modified embodiments.
For example, if fine characters, patterns, or the like are printed on the side surface of the prism sheet 23 of the support 6, security can be improved. Further, the support 6 may be a laminate of a paper or a film base printed with a transparent resin film, and the printing may be performed on the side surface of the prism sheet 23 of the paper or the film base.
[0029]
Next, a manufacturing process of the prism sheet used for the authenticity determination body will be described.
FIG. 7 shows a prism sheet manufacturing apparatus. In FIG. 7, reference numeral 10 denotes a roll intaglio in which a concave portion of a triangular prism is formed, 11 denotes a concave portion of the roll intaglio, 12 denotes a coating device for applying an ionizing radiation-curable resin liquid to the roll intaglio 10, and 13 denotes a coating device. An ionizing radiation-curable resin liquid, 2 is a base film, 14 is a solvent drying device, 15 and 16 are curing devices, 17 is a pressing roll that abuts against the roll intaglio and presses the roll intaglio 10, and 18 is a feed roll. .
In FIG. 7, the concave portion 11 for forming the triangular prism is shown to be orthogonal to the flow direction of the base film 2, but may be formed parallel to the flow direction of the base film 2. Shall be.
[0030]
The manufacturing process of the prism sheet can be classified into a filling process, a contacting process, a curing process, a contacting process, and a peeling process.
The filling step in the manufacturing process of the prism sheet is a step in which the roll intaglio 10 on which the mold of the triangular prism is formed is rotated, and at least the concave portion 11 of the roll intaglio 10 is filled with the ionizing radiation-curable resin liquid 13.
The contacting step is a step of bringing the base film 2 running in synchronization with the rotation direction of the roll intaglio 10 into contact with the ionizing radiation-curable resin liquid 13 filled in the filling step.
[0031]
In the curing step, the ionizing radiation from the curing device 15 is applied to the ionizing radiation-curable resin liquid 13 between the roll intaglio 10 and the substrate film 2 while the base film 2 is in contact with the roll intaglio 10 in the contacting step. This is a step of irradiating and curing.
The adhesion step is a step in which the ionizing radiation-curable resin liquid 13 cured in the curing step and the base film 2 are adhered to each other. Note that the curing step and the adhesion step usually proceed simultaneously. The peeling step is a step of peeling the semi-cured product 13a of the ionizing radiation-curable resin liquid 13 and the base film 2 adhered in the contacting step from the roll intaglio 10.
[0032]
The roll intaglio 10 is provided with a concave portion 11 having a predetermined shape in a cylindrical plate material. The roll intaglio can be obtained by directly cutting the plate material using a lathe or the like, or can be formed by electroforming.
The coating device 12 is a device for applying the ionizing radiation-curable resin liquid 13 to the roll intaglio 10, and often uses a nozzle coating device. In the nozzle coating device, a nozzle having a predetermined size has a T-die-shaped rectangular or linear discharge port, and the longitudinal direction of the discharge port is installed in a direction orthogonal to the roll intaglio rotation direction, The resin liquid is discharged only to a predetermined width portion of the entire width.
[0033]
The solvent drying device 14 is a device for volatilizing the solvent of the resin. As the solvent drying device 14, warm air, an infrared heater, or the like can be used. By providing the solvent drying device 14, a solvent-type resin can be used, and the range of choice of the resin to be used can be expanded. When the solventless ionizing radiation-curable resin liquid 13 is used, the solvent drying device 14 is not used.
[0034]
The curing device 15 is a device that irradiates ionizing radiation to cure the ionizing radiation-curable resin liquid 13. A curing device 16 may be provided in order to completely cure the semi-cured product 13a of the ionizing radiation-curable resin liquid that has been detached after the peeling step.
Here, the ionizing radiation means an electromagnetic wave or a charged particle beam having an energy quantum capable of polymerizing and cross-linking a molecule, and usually, an ultraviolet ray, an electron beam, or the like is used. When ultraviolet light is used as the curing devices 15 and 16, a light source such as an ultra-high pressure mercury lamp, a black light lamp, a xenon lamp, or a metal halide lamp can be used.
[0035]
<Manufacture of prism sheet>
In the method of manufacturing a prism sheet by the above apparatus, first, the concave portion 11 of the roll intaglio 10 is filled with the ionizing radiation-curable resin liquid 13 by the coating device 12, and the base film 2 is filled in the concave portion 11 of the roll intaglio 10. The contact is made to be in contact with the ionized radiation-curable resin liquid 13.
As a method for filling the concave portion 11 with the ionizing radiation-curable resin liquid 13, a predetermined amount of the ionizing radiation-curable resin liquid 13 is applied to the surface of the roll intaglio 10 in advance, and the base film 2 is placed on the surface of the roll intaglio 10. When it is supplied, the applied ionizing radiation-curable resin liquid 13 is distributed and filled into the concave portion 11 through the base film 2 by the pressing of the pressing roll 17.
[0036]
In this case, a solvent-type curable resin can be used, and the ionizing radiation-curable resin liquid 13 applied to the base film 2 is used to dilute the solvent of the resin liquid in order to control fluidity to some extent. The solvent or the like used in the above is dried and removed by the solvent drying device 14, and the resin liquid obtained by drying the solvent by the curing device 15 is semi-cured.
[0037]
While the base film 2 is in contact with the intaglio roll 10, the curing device 15 cures the ionizing radiation-curable resin liquid 13. If necessary, a plurality of curing devices can be provided along the rotation direction of the roll intaglio. The multi-stage curing can reduce the distortion of the cured product, the curl of the base film 2, and the like.
Further, the roll intaglio 10 may be formed of a material having good transparency of ionizing radiation, such as quartz or glass, and may be irradiated from the inside of the roll intaglio 10.
[0038]
The curing device 15 causes the ionizing radiation-curable resin liquid 13 in the concave portion 11 of the roll intaglio 10 to adhere to the base film 2. At this time, the degree of curing may be at least such that the fluidity of the resin is lost and the adhesiveness to the base film 2 is generated.
After passing through the curing device 15, the base film 2 is peeled from the roll intaglio 10. As a result, the semi-cured ionizing radiation-curable resin liquid 13a is integrated with the base film 2 and detached from the concave portion 11 to obtain a prism sheet having a triangular prism-shaped prism surface.
[0039]
<Embodiment related to material>
(1) Base film
As the base film, a transparent polymer film is preferable from the viewpoint of processability. As plastics for polymer film materials, polyethylene resin, polypropylene resin, polymethylpentene resin, polyvinyl chloride resin, polyvinylidene chloride resin, polyvinyl alcohol resin, vinyl chloride-vinyl acetate copolymer resin, ethylene-vinyl acetate copolymer resin , Ethylene-vinyl alcohol copolymer resin, polyethylene terephthalate resin, polybutylene terephthalate resin, polyethylene naphthalate-isophthalate copolymer resin, polymethyl methacrylate resin, polycarbonate resin, polyarylate resin, polyimide resin, polysulfone resin, acrylic resin, etc. Can be used. Alternatively, a liquid crystal material can be used.
The thickness of the substrate is preferably in the range of about 12 to 100 μm, and more preferably about 15 to 50 μm, from the viewpoint of ease of processing. This is because not so thick is preferable for visual recognition of the authentication medium.
[0040]
(2) Triangular prism material
The triangular prism material is not particularly limited, but a resin material is preferable from the viewpoint of processability. Further, it is required to be transparent or colored and transparent from the characteristics of the prism.
In the above-described manufacturing method of forming a prism shape with an ultraviolet curable resin, an ultraviolet curable ionizing radiation curable resin liquid is preferably used.
As a specific example of such a resin liquid, a composition in which a prepolymer, an oligomer, and / or a monomer having a polymerizable unsaturated bond or an epoxy group in a molecule is appropriately mixed can be used.
[0041]
As the prepolymer and oligomer, unsaturated polyesters such as a condensate of an unsaturated dicarboxylic acid and a polyhydric alcohol, epoxy resins, polyester methacrylate, polyether methacrylate, polyol methacrylate, methacrylates such as melamine methacrylate, polyester acrylate, epoxy Examples include acrylates such as acrylate, urethane acrylate, polyether acrylate, polyol acrylate, and melamine acrylate.
[0042]
Examples of the monomer include styrene-based monomers such as styrene and α-methylstyrene, acrylates such as methyl acrylate, 2-ethylhexyl acrylate, methoxyethyl acrylate, and butyl acrylate, and methacrylic acid. Methacrylates such as methyl acrylate, ethyl methacrylate, methoxyethyl methacrylate, and methoxymethyl methacrylate; unsaturated substituted amino alcohol esters such as 2- (N, N-diethylamino) ethyl acrylate; acrylamide; methacryl Unsaturated carboxylic acid amides such as amides, polyfunctional compounds such as dipropylene glycol diacrylate, ethylene glycol acrylate, propylene glycol dimethacrylate, diethylene glycol dimethacrylate, vinylpyrrolidone, and / or molecules Polythiol compounds having two or more thiol groups, such as trimethylolpropane trithioglycolate, trimethylolpropane tri thio propylate, pentaerythritol thioglycolate and the like.
[0043]
In particular, when cured by ultraviolet light, the composition of the ionizing radiation-curable resin, as a photopolymerization initiator, acetophenones, benzophenones, Michler benzoyl benzoate, α-amyloxime ester, tetramethyl meuram monosulfide, Thioxanthones and / or n-butylamine, triethylamine, tri-n-butylphosphine, and the like as a photosensitizer can be used as a mixture. In order to faithfully reproduce the shape of the roll intaglio 10 having the fine concave portions 11 of the prism, the viscosity is preferably 5000 cps or less, particularly preferably 1000 cps or less. In the case where the prism is colored and transparent, a dye which does not inhibit curing may be added.
[0044]
(3) Transparent or colored resin
The transparent or colored resin filling the valleys of the triangular prism is not particularly limited in material, but a resin having a refractive index close to that of the triangular prism material is selected and used.
The refractive index of various polymer resins is about 1.4 to 1.6. For example, polybutyl acrylate (1.44), polyethyl acrylate (1.47), polymethyl acrylate (1.47), poly n-butyl methacrylate (1.48), polymethyl methacrylate (1.49), polyvinyl acetate (1.47), polypropylene (1.49-1.50), polyethylene (1.5-1.55), Polycarbonate (1.58), polystyrene (1.59-1.60), polyethylene terephthalate (1.64), polyvinyl chloride (1.54), polyvinylidene chloride (1.60-1.63), etc. Can be used.
When filling by a printing method, it is possible to use a medium ink comprising only a vehicle without using a coloring agent such as a pigment or a dye. When coloring the filling resin, a dye or pigment is appropriately used.
[0045]
(4) Support
The same material as the base film can be used for the support 6 used in the first and second embodiments, but the thickness may be 10 to 30 μm.
However, it is not necessary to be transparent, and an opaque material may be used depending on the purpose. As long as the surface is smooth, paper may be used, and the surface of the support may be printed.
[0046]
(5) Adhesive or adhesive
Any kind of transparent adhesive or adhesive can be used.
When the pressure-sensitive adhesive or the adhesive is used also as the filling resin, it is necessary to consider the refractive index similarly to the above-mentioned transparent or colored resin.
Generally, a mixture of an elastomer such as natural rubber, recycled rubber, or SBR, a low molecular weight or medium molecular weight tackifier, an antioxidant, or the like can be used as a pressure-sensitive adhesive in a solution state. In the case of a thermoplastic elastomer, application in a molten state is possible. If resistance to light and oxidation is required, materials such as acrylate copolymers and polyisobutylene are used.
A hot melt type heat sealant may be used. In the case of forming a pattern by a printing method, it is particularly necessary to consider a printability.
The coating thickness of the pressure-sensitive adhesive or the adhesive is about 1 to 50 μm, and is adjusted according to the height of the prism.
[0047]
【Example】
An embodiment of the present invention will be described with reference to FIG. 1, FIG. 2, FIG. 3, FIG.
(Example 1)
A method of curing a urethane acrylate-based ultraviolet curable resin liquid on a polyethylene terephthalate film (PET) base film 2 having a thickness of 50 μm, as shown in FIG. 1, has a cross-section height of 25 μm and a vertical angle of 90 degrees. An isosceles triangular prism sheet 23 was manufactured.
Then, using a transparent acrylic ink (“SS8-800 medium” manufactured by Toyo Ink Co., Ltd.), fine characters “ABC” are printed by a silk screen printing method so as to fill the valleys between the prisms of the prism sheet 23. Was printed in a negative pattern.
[0048]
Next, a polyester heat sealant was applied to a PET film having a thickness of 25 μm to a thickness of 5 μm, and immediately thereafter, a laminate was attached to the prism surface of the printed prism sheet 23. Lamination was performed at a roll temperature of 150 ° C. and a speed of 0.8 m / min. Finally, an adhesive was applied to the protective paper 9 which had been subjected to a release treatment by silicone processing, and the protective paper 9 was bonded to the 25 μm-thick PET film surface. Thereby, the label 1L for authenticity determination body of the first embodiment of the present invention was completed (FIG. 6A).
[0049]
The authenticity judgment body 1 of the present invention was obtained by removing the releasable protective paper 9 of the authenticity judgment body label and sticking it on the face photograph side of a magnetic card with a face photograph (FIG. 2).
By observing the authenticity determination body 1, a face photograph could be clearly observed, and at a certain angle, fine characters of "ABC" appeared to shine, and a magnetic card having a high design property was obtained.
[0050]
(Example 2)
A method of curing a urethane acrylate-based ultraviolet curable resin liquid on a polyethylene terephthalate film (PET) base film 2 having a thickness of 50 μm, as shown in FIG. An isosceles triangular prism sheet 23 was manufactured.
Then, using a transparent polyester hot melt ink (prototype ink), the characters “ABC” are printed in a negative pattern by a gravure printing method so as to fill the valleys between the prisms of the prism sheet 23. Printing and lamination with a 25 μm-thick PET film were performed at the same time.
At this time, the ink pan of the hot melt ink was heated to keep the ink in a molten state.
[0051]
Lastly, an adhesive was applied to the protective paper 9 which had been subjected to a release treatment by silicone processing, and was bonded to the 25 μm-thick PET film surface. Thereby, the label 1L for authenticity determination body of the second embodiment of the present invention was completed (FIG. 6B).
The authenticity judgment body 1 of the present invention was obtained by removing the releasable protective paper 9 of the authenticity judgment body label 1L and affixing it on a fine pattern on the surface of a gift certificate (FIG. 3).
By observing the authenticity determination body 1, a fine pattern can be clearly observed, and at a certain angle, a fine character of "ABC" appears to be shining, and a gift certificate with a high design property is obtained.
[0052]
【The invention's effect】
As described above, according to the authenticity judgment body or the authenticity judgment body label of the present invention, the following effects can be obtained.
Although the authenticity determination body of the present invention is not subjected to special processing such as formation of a reflective layer, it can be used as an authentication medium having a high design property in which glittering characters and patterns can be observed depending on the viewing direction.
Further, since the glittering characters or patterns and the pattern or photograph of the authentication medium itself appear to be switched depending on the viewing direction, it is possible to immediately determine whether the authentication medium is authentic or not by comparing the authentication medium without such a state change. it can.
The authentication medium to which the label for authenticity determination is adhered cannot be normally copied by the copying machine, and forgery and counterfeiting can be prevented. Therefore, it becomes an authentication medium with high security.
[Brief description of the drawings]
FIG. 1 is an external perspective view showing a basic form of a true / false judgment body of the present invention.
FIG. 2 is a sectional view showing the first embodiment.
FIG. 3 is a sectional view showing a second embodiment.
FIG. 4 is a sectional view showing a third embodiment.
FIG. 5 is a sectional view showing a fourth embodiment.
FIG. 6 is a cross-sectional view showing a label for authenticity determination body.
FIG. 7 is a diagram showing a prism sheet manufacturing apparatus.
[Explanation of symbols]
1 Authenticator
1L Label for authenticity judgment
2 Base film
3 Small triangular prism
4 Transparent or colored resin
5,5a, 5b adhesive or adhesive
6 Support
7 Certification medium
8 air layer
9 Peelable protective paper
10 Roll Intaglio
11 recess
12 Coating equipment
13 Ionizing radiation curable resin liquid
14 Solvent drying equipment
15,16 Curing device
17 Press roll
18 feed roll
23 Prism sheet

Claims

基材フィルム上に略直線状であって透明な材質からなる微小三角柱状プリズムが並行して配列しているプリズムシートの、当該微小三角柱状プリズム間の谷部を透明または着色樹脂で部分的に充填し、他の谷部分は充填しないで空気層を残すことにより、一定のパターンが形成されている当該プリズムシートが、粘着剤または接着剤と、支持体と、粘着剤または接着剤と、を介して認証媒体に貼着されている、ことを特徴とする真偽判定体。A prism sheet in which micro triangular prisms made of a substantially linear and transparent material are arranged in parallel on a base film, and the valleys between the micro triangular prisms are partially transparent or colored resin. Filling, leaving the air layer without filling other valleys, the prism sheet in which a certain pattern is formed, the adhesive or adhesive, the support, the adhesive or adhesive, A true / false judging body attached to an authentication medium via a personal computer.

基材フィルム上に略直線状であって透明な材質からなる微小三角柱状プリズムが並行して配列しているプリズムシートの、当該微小三角柱状プリズム間の谷部を粘着剤または接着剤で部分的に充填し、他の谷部分は充填しないで空気層を残すことにより、一定のパターンが形成されている当該プリズムシートが、支持体と、粘着剤または接着剤と、を介して認証媒体に貼着されている、ことを特徴とする真偽判定体。Partially valleys between the small triangular prisms of the prism sheet in which the substantially triangular prisms made of a transparent material are arranged in parallel on the base film are partially adhered with an adhesive or an adhesive. The prism sheet on which a certain pattern is formed is attached to the authentication medium via the support and the adhesive or the adhesive by leaving the air layer without filling the other valleys. A true / false judgment body which is worn.

基材フィルム上に略直線状であって透明な材質からなる微小三角柱状プリズムが並行して配列しているプリズムシートの、当該微小三角柱状プリズム間の谷部を粘着剤または接着剤で部分的に充填し、他の谷部分は充填しないで空気層を残すことにより、一定のパターンが形成されている当該プリズムシートが、前記粘着剤または接着剤、を介して認証媒体に貼着されている、ことを特徴とする真偽判定体。Partially valleys between the triangular prisms of the prism sheet in which the triangular prisms of a substantially linear and transparent material are arranged in parallel on the base film with an adhesive or an adhesive. By filling the other valley portions and leaving the air layer without filling, the prism sheet in which a certain pattern is formed is adhered to the authentication medium via the adhesive or the adhesive. A true / false judgment body characterized by the following.

基材フィルム上に略直線状であって透明な材質からなる微小三角柱状プリズムが並行して配列しているプリズムシートの、当該微小三角柱状プリズム間の谷部を透明または着色樹脂で部分的に充填し、他の谷部分は充填しないで空気層を残すことにより、一定のパターンが形成されている当該プリズムシートが、粘着剤または接着剤、を介して認証媒体に貼着されている、ことを特徴とする真偽判定体。A prism sheet in which micro triangular prisms made of a substantially linear and transparent material are arranged in parallel on a base film, and the valleys between the micro triangular prisms are partially transparent or colored resin. By filling and leaving the air layer without filling other valleys, the prism sheet in which a certain pattern is formed is adhered to the authentication medium via an adhesive or an adhesive. A true / false judgment body characterized by the following.

三角柱状プリズムの長さ方向に直交する断面が二等辺三角形または直角二等辺三角形であって、二等辺三角形の等辺でない辺が認証媒体に平行するようにされていることを特徴とする請求項１から請求項４のいずれか１の請求項に記載の真偽判定体。2. A cross section orthogonal to the length direction of the triangular prism is an isosceles triangle or a right-angled isosceles triangle, and sides of the isosceles triangle which are not equal are parallel to the authentication medium. A true / false determinant according to any one of claims 1 to 4.

三角柱状プリズムの長さ方向に直交する断面が直角三角形であって、直角三角形の斜辺が認証媒体に平行するようにされていることを特徴とする請求項１から請求項４のいずれか１の請求項に記載の真偽判定体。The cross section orthogonal to the longitudinal direction of the triangular prism is a right triangle, and the hypotenuse of the right triangle is parallel to the authentication medium. The authenticity determination body according to claim.

認証媒体に使用するラベルであって、基材フィルム上に略直線状であって透明な材質からなる微小三角柱状プリズムが並行して配列しているプリズムシートの、当該微小三角柱状プリズム間の谷部を透明または着色樹脂で部分的に充填し、他の谷部分は充填しないで空気層を残すことにより、一定のパターンが形成されている当該プリズムシートが、粘着剤または接着剤と、支持体と、粘着剤または接着剤を介して、剥離性保護紙に貼着されている、ことを特徴とする真偽判定体用ラベル。A label used for an authentication medium, wherein a valley between the triangular prisms is formed on a prism film in which triangular prisms each having a substantially linear shape and made of a transparent material are arranged in parallel on a base film. Part is filled with a transparent or colored resin, leaving the air layer without filling the other valleys, the prism sheet in which a certain pattern is formed, the adhesive or adhesive, And a label for authenticity judgment, which is attached to a peelable protective paper via an adhesive or an adhesive.

認証媒体に使用するラベルであって、基材フィルム上に略直線状であって透明な材質からなる微小三角柱状プリズムが並行して配列しているプリズムシートの、当該微小三角柱状プリズム間の谷部を粘着剤または接着剤で部分的に充填し、他の谷部分は充填しないで空気層を残すことにより、一定のパターンが形成されている当該プリズムシートが、支持体と、粘着剤または接着剤を介して、剥離性保護紙に貼着されている、ことを特徴とする真偽判定体用ラベル。A label used for an authentication medium, wherein a valley between the triangular prisms is formed on a prism film in which triangular prisms each having a substantially linear shape and made of a transparent material are arranged in parallel on a base film. Part of the prism sheet is partially filled with an adhesive or an adhesive, and the other valleys are left unfilled to leave an air layer. A label for authenticity judgment, which is attached to a peelable protective paper via an agent.

認証媒体に使用するラベルであって、基材フィルム上に略直線状であって透明な材質からなる微小三角柱状プリズムが並行して配列しているプリズムシートの、当該微小三角柱状プリズム間の谷部を粘着剤または接着剤で部分的に充填し、他の谷部分は充填しないで空気層を残すことにより、一定のパターンが形成されている当該プリズムシートが、前記粘着剤または接着剤を介して、剥離性保護紙に貼着されている、ことを特徴とする真偽判定体用ラベル。A label used for an authentication medium, wherein a valley between the triangular prisms is formed on a prism film in which triangular prisms each having a substantially linear shape and made of a transparent material are arranged in parallel on a base film. Part is partially filled with an adhesive or an adhesive, and the other valley portions are left unfilled to leave an air layer, so that the prism sheet in which a certain pattern is formed can be interposed through the adhesive or the adhesive. A label for authenticity judging body attached to a peelable protective paper.

認証媒体に使用する真偽判定体であって、基材フィルム上に略直線状であって透明な材質からなる微小三角柱状プリズムが並行して配列しているプリズムシートの、当該微小三角柱状プリズム間の谷部を透明または着色樹脂で部分的に充填し、他の谷部分は充填しないで空気層を残すことにより、一定のパターンが形成されている当該プリズムシートが、粘着剤または接着剤を介して、剥離性保護紙に貼着されている、ことを特徴とする真偽判定体用ラベル。A true / false judging body used for an authentication medium, wherein the micro triangular prisms of a prism sheet in which micro triangular prisms made of a substantially linear and transparent material are arranged in parallel on a base film. By partially filling the valleys between them with a transparent or colored resin and leaving the air layer without filling the other valleys, the prism sheet in which a certain pattern is formed is coated with an adhesive or an adhesive. A label for authenticity judgment, wherein the label is attached to a peelable protective paper through the intermediary.

三角柱状プリズムの長さ方向に直交する断面が二等辺三角形または直角二等辺三角形であって、二等辺三角形の等辺でない辺が剥離性保護紙に平行するようにされていることを特徴とする請求項７から請求項１０のいずれか１の請求項に記載の真偽判定体用ラベル。The cross section orthogonal to the length direction of the triangular prism is an isosceles triangle or a right-angled isosceles triangle, and the non-equilateral sides of the isosceles triangle are parallel to the peelable protective paper. The authenticity-determining body label according to any one of claims 7 to 10.

三角柱状プリズムの長さ方向に直交する断面が直角三角形であって、直角三角形の斜辺が剥離性保護紙に平行するようにされていることを特徴とする請求項７から請求項１０のいずれか１の請求項に記載の真偽判定体用ラベル。The cross section orthogonal to the longitudinal direction of the triangular prism is a right triangle, and the hypotenuse of the right triangle is parallel to the peelable protection paper. The label for authenticity determination body according to claim 1.