JP2004231456A

JP2004231456A - SILICON NITRIDE (Si3N4) NANOROD AND ITS MANUFACTURING METHOD

Info

Publication number: JP2004231456A
Application number: JP2003021044A
Authority: JP
Inventors: Yoshio Bando; 義雄板東; Gao Yihua; ガオ・イオハ
Original assignee: National Institute for Materials Science
Current assignee: National Institute for Materials Science
Priority date: 2003-01-29
Filing date: 2003-01-29
Publication date: 2004-08-19
Anticipated expiration: 2023-01-29
Also published as: JP4000371B2

Abstract

<P>PROBLEM TO BE SOLVED: To provide a silicon nitride (Si<SB>3</SB>N<SB>4</SB>) nanorod which has performance applicable to practical use and is easily synthesized in a large amount at a low cost; and a manufacturing method therefor. <P>SOLUTION: A silicon nitride (Si<SB>3</SB>N<SB>4</SB>) nanorod with a diameter of 20-80 nm and a length of 1-10 μm is obtained by heating a silicon oxide (SiO) powder to 1,350-1,400°C in a nitrogen gas atmosphere in the presence of an amorphous activated carbon (AAC) as a reducing agent. <P>COPYRIGHT: (C)2004,JPO&NCIPI

Description

【０００１】
【発明の属する技術分野】
この出願の発明は、窒化硅素（Ｓｉ_３Ｎ_４）ナノロッドとその製造方法に関するものである。
【０００２】
【従来の技術】
近年、炭素ナノチューブが発見されて以来、多くの一次元（１Ｄ）的ナノスケール物質が合成されてきている。たとえば、ナノチューブ構造の物質として窒化ホウ素（ＢＮ）等や、ナノロッドまたはナノワイヤー構造の物質として酸化マグネシウム（ＭｇＯ）、窒化ガリウム（ＧａＮ）等が合成されている。ところで、窒化硅素（Ｓｉ_３Ｎ_４）は機械的、化学的、電子的、および耐熱性に優れた特質を有していることから、そのナノスケール物質は応用への大きな潜在力を有している。このため、たとえば、シリカと硅素（ＳｉＯ_２＋Ｓｉ）の炭素加熱還元法によって窒化硅素（Ｓｉ_３Ｎ_４）のナノスケール構造体を合成することがすでに報告されている（文献１）。
【０００３】
しかしながら、この方法においては、還元剤として１Ｄカーボンナノチューブが用いられているために、窒化硅素（Ｓｉ_３Ｎ_４）ナノロッドの合成のためには高価過ぎて、現実的でなく、その応用においては限界を来すものと考えられる。このため、窒化硅素（Ｓｉ_３Ｎ_４）ナノロッドを、実用化に適用できる性能を有するとともに、安価で簡便に、しかも大量に合成することのできる新しい方策の実現が望まれている。
【０００４】
【文献１】
ＨａｎＷＱ，ＦａｎＳＳ，ＬｉＱＱ，ＧｕＢＬ，ｚｈａｎｇＸＢ，ＹｕＤＰ，Ａｐｐｌ．Ｐｈｙｓ．Ｌｅｔｔ．，７１：２２７１−２２７３（１９９７）
【０００５】
【発明が解決しようとする課題】
この出願の発明は、以上のとおりの従来の技術に鑑みなされたものであり、実用化に適用できる性能を有するとともに、安価で簡便に、しかも大量に合成することのできる、新しい窒化硅素（Ｓｉ_３Ｎ_４）ナノロッドとその製造方法を提供することを課題としている。
【０００６】
【課題を解決するための手段】
上記の課題を解決するものとして、この出願の発明の窒化硅素（Ｓｉ_３Ｎ_４）ナノロッドは、直径が２０〜８０ｎｍで長さが１〜１０ミクロンであることを特徴とする。そしてその製造方法としては、さらには、還元剤として非晶質活性化炭素（ＡＡＣ）粉末を用い、酸化硅素（ＳｉＯ）粉末を窒素ガス環境下において１３５０℃〜１４００℃に加熱することを特徴とし、還元剤の非晶質活性化炭素（ＡＡＣ）粉末が１〜１００μｍのサイズの炭素フレークからなるとともに、この炭素フレークが１〜１０ｎｍの炭素粒子により構成されていることを特徴とする。
【０００７】
【発明の実施の形態】
この出願の発明の窒化硅素（Ｓｉ_３Ｎ_４）ナノロッドとその製造方法の実施の形態を以下に詳細に説明する。
【０００８】
この出願の発明の窒化硅素（Ｓｉ_３Ｎ_４）ナノロッドは、還元剤として非晶質活性化炭素（ＡＡＣ）粉末を用い、炭素加熱還元法により、酸化硅素（ＳｉＯ）粉末を窒素ガス環境下において１３５０℃〜１４００℃、より好ましくは１３８０℃前後に加熱することにより製造される。
【０００９】
この場合、該ＡＡＣ粉末が１〜１００μｍのサイズの炭素フレークからなるとともに該炭素フレークが１〜１０ｎｍの炭素粒子からなるものがこの好ましい。
【００１０】
窒素ガスはできるだけ高純度のものが好ましいが、アルゴン等の不活性ガスが混合されていてもよい。
【００１１】
そこで、次に実施例を示し、さらに詳しく説明する。
【００１２】
【実施例】
長さが５０ｃｍ、直径１２ｃｍ、肉厚０．２５ｃｍの縦型石英管の中に、長さ７ｃｍ、外径４．５ｃｍ、内径３．５ｃｍの高純度グラファイト製の誘導加熱円筒管を設置する。この円筒管の中に、高さ２ｃｍ、直径２ｃｍのグラファイト製るつぼを入れ、るつぼの中に純度９９．９％の一酸化ケイ素粉末と非晶質活性炭を入れる。活性炭は一酸化ケイ素の上に覆うようにする。窒素雰囲気下で、１３８０℃、２時間加熱する。１３８０℃で一酸化ケイ素の粉末が蒸気化し、反応する。反応が終了した後、窒化珪素ナノロットがるつぼの底に生成した。なお、反応器は、以上の例には限定されず、炭素加熱還元法に用いられる反応器であればよい。
【００１３】
図１は、生成された窒化珪素（Ｓｉ_３Ｎ_４）ナノロッドを透過型電子顕微鏡を用いて観察した像の写真である。図２は、（ａ）：窒化珪素（Ｓｉ_３Ｎ_４）ナノロッドの直線状部位を透過型電子顕微鏡を用いて観察した像の写真と、（ｂ）（ｃ）：（ａ）に対応する電子線回折（ＥＤ）パターンと、（ｄ）：結晶化されていることを示す高分解能透過型電子顕微鏡（ＨＲＴＥＭ）像の写真である。
【００１４】
そして、図３は、わん曲部位を介して隣接する直線部位の角度が１２０度であることを透過型電子顕微鏡を用いて観察した像の写真である。さらに図４は、わん曲部位について例示した高分解能透過型電子顕微鏡（ＨＲＴＥＭ）像の写真である。
【００１５】
この出願の発明の窒化硅素（Ｓｉ_３Ｎ_４）ナノロッドは、形状が直線部位とわん曲部位とから構成されていて、直径が２０〜８０ｎｍで、長さが概ね１０μｍ以下であることがわかる。また、図２の（ｂ）および（ｃ）の電子線回折（ＥＤ）パターンおよび高分解能透過型電子顕微鏡（ＨＲＴＥＭ）像に示されているように、ナノロッドは良好に結晶化された単結晶体から構成されている。
【００１６】
【発明の効果】
この出願の発明によれば、実用化に適用できる性能を有するとともに安価で簡便にしかも大量に合成することができる、新しい窒化硅素（Ｓｉ_３Ｎ_４）ナノロッドとその製造方法が提供される。機械的、化学的、電子的、および耐熱性に優れた特質を有するとともにその応用への大きな潜在力を有している窒化硅素（Ｓｉ_３Ｎ_４）ナノロッドの広範な分野への応用が可能とされる。
【図面の簡単な説明】
【図１】この出願の発明の窒化硅素（Ｓｉ_３Ｎ_４）ナノロッドの形状の一例を示す透過型電子顕微鏡（ＴＥＭ）像の写真である。
【図２】（ａ）：窒化硅素（Ｓｉ_３Ｎ_４）ナノロッドの直線状部位を示す透過型電子顕微鏡（ＴＥＭ）像の写真である。
（ｂ）（ｃ）：（ａ）に対応する電子線回折（ＥＤ）パターンである。
（ｄ）：窒化硅素（Ｓｉ_３Ｎ_４）ナノロッドが結晶化されていることを示す高分解能透過型電子顕微鏡（ＨＲＴＥＭ）像の写真である。
【図３】ナノロッドの形状が直線部位とわん曲部位から構成されるとともにわん曲部位を介して隣接する直線部位の角度が約１２０度である特徴を示す透過型電子顕微鏡（ＴＥＭ）像の写真である。
【図４】窒化硅素（Ｓｉ_３Ｎ_４）ナノロッドのわん曲部位の一例を示す高分解能透過型電子顕微鏡（ＨＲＴＥＭ）像の写真である。[0001]
TECHNICAL FIELD OF THE INVENTION
The invention of this application relates to a silicon nitride (Si ₃ N ₄ ) nanorod and a method for manufacturing the same.
[0002]
[Prior art]
In recent years, many one-dimensional (1D) nanoscale materials have been synthesized since the discovery of carbon nanotubes. For example, boron nitride (BN) or the like is synthesized as a material having a nanotube structure, and magnesium oxide (MgO), gallium nitride (GaN), or the like is synthesized as a material having a nanorod or nanowire structure. By the way, since silicon nitride (Si ₃ N ₄ ) has properties excellent in mechanical, chemical, electronic, and heat resistance, its nanoscale material has great potential for application. I have. For this reason, for example, it has already been reported to synthesize a silicon nitride (Si ₃ N ₄ ) nanoscale structure by a carbon heating reduction method of silica and silicon (SiO ₂ + Si) (Reference 1).
[0003]
However, in this method, since 1D carbon nanotube is used as a reducing agent, it is too expensive for synthesis of silicon nitride (Si ₃ N ₄ ) nanorods, is not practical, and is limited in its application. Is thought to come. For this reason, it is desired to realize a new method capable of synthesizing silicon nitride (Si ₃ N ₄ ) nanorods, which has a performance applicable to practical use, is inexpensive, simple, and can be synthesized in large quantities.
[0004]
[Reference 1]
Han WQ, Fan SS, Li QQ, Gu BL, zhang XB, Yu DP, Appl. Phys. Lett. , 71: 2271-2273 (1997).
[0005]
[Problems to be solved by the invention]
The invention of this application has been made in view of the above conventional technology, and has a performance applicable to practical use, and is a new silicon nitride (Si) that can be synthesized in a large amount at low cost, easily and inexpensively. _{3 N} ₄₎ is an object to provide a nanorod and a manufacturing method thereof.
[0006]
[Means for Solving the Problems]
In order to solve the above problem, silicon nitride _(Si 3 _{N 4)} nanorods of the invention of this application is characterized in that a diameter of 1-10 microns in length in 20 to 80 nm. Further, the method for producing the same is characterized in that amorphous activated carbon (AAC) powder is used as a reducing agent, and silicon oxide (SiO) powder is heated to 1350 ° C. to 1400 ° C. in a nitrogen gas environment. The amorphous activated carbon (AAC) powder of the reducing agent is made of carbon flakes having a size of 1 to 100 μm, and the carbon flakes are made up of carbon particles of 1 to 10 nm.
[0007]
BEST MODE FOR CARRYING OUT THE INVENTION
Embodiments of the silicon nitride (Si ₃ N ₄ ) nanorod and the method of manufacturing the same according to the present invention will be described in detail below.
[0008]
The silicon nitride (Si ₃ N ₄ ) nanorods of the invention of this application use amorphous activated carbon (AAC) powder as a reducing agent, and heat silicon oxide (SiO) powder in a nitrogen gas environment by a carbon heating reduction method. It is manufactured by heating to 1350 ° C to 1400 ° C, more preferably about 1380 ° C.
[0009]
In this case, it is preferable that the AAC powder be made of carbon flakes having a size of 1 to 100 μm and the carbon flakes be made of carbon particles having a size of 1 to 10 nm.
[0010]
The nitrogen gas is preferably as pure as possible, but may be mixed with an inert gas such as argon.
[0011]
Then, an example is shown next and explained in more detail.
[0012]
【Example】
In a vertical quartz tube having a length of 50 cm, a diameter of 12 cm, and a thickness of 0.25 cm, an induction heating cylindrical tube made of high-purity graphite having a length of 7 cm, an outer diameter of 4.5 cm, and an inner diameter of 3.5 cm is placed. A graphite crucible having a height of 2 cm and a diameter of 2 cm is placed in the cylindrical tube, and 99.9% pure silicon monoxide powder and amorphous activated carbon are placed in the crucible. Activated carbon is coated over silicon monoxide. Heat at 1380 ° C. for 2 hours under a nitrogen atmosphere. At 1380 ° C., the powder of silicon monoxide vaporizes and reacts. After the reaction was completed, silicon nitride nano lots were formed at the bottom of the crucible. In addition, a reactor is not limited to the above example, What is necessary is just a reactor used for a carbon heating reduction method.
[0013]
FIG. 1 is a photograph of an image obtained by observing the generated silicon nitride (Si ₃ N ₄ ) nanorods using a transmission electron microscope. FIG. 2 shows (a) a photograph of an image obtained by observing a linear portion of a silicon nitride (Si ₃ N ₄ ) nanorod using a transmission electron microscope, and (b) and (c): electrons corresponding to (a). It is a line diffraction (ED) pattern and (d): The photograph of the high-resolution transmission electron microscope (HRTEM) image which shows being crystallized.
[0014]
FIG. 3 is a photograph of an image observed by using a transmission electron microscope that the angle of a straight line portion adjacent through a curved portion is 120 degrees. FIG. 4 is a photograph of a high-resolution transmission electron microscope (HRTEM) image illustrating a curved portion.
[0015]
It can be seen that the silicon nitride (Si ₃ N ₄ ) nanorod of the invention of this application has a linear shape and a curved shape, a diameter of 20 to 80 nm, and a length of about 10 μm or less. In addition, as shown in the electron diffraction (ED) patterns and the high-resolution transmission electron microscope (HRTEM) images of FIGS. 2B and 2C, the nanorods are well-crystallized single crystals. It is composed of
[0016]
【The invention's effect】
According to the invention of this application, there is provided a new silicon nitride (Si ₃ N ₄ ) nanorod having a performance applicable to practical use, being inexpensive, simple, and capable of being synthesized in large quantities, and a method for producing the same. It is possible to apply silicon nitride (Si ₃ N ₄ ) nanorods, which have excellent mechanical, chemical, electronic, and heat-resistant properties and have great potential for their applications, to a wide range of fields. Is done.
[Brief description of the drawings]
FIG. 1 is a photograph of a transmission electron microscope (TEM) image showing an example of the shape of a silicon nitride (Si ₃ N ₄ ) nanorod of the present invention.
FIG. 2A is a photograph of a transmission electron microscope (TEM) image showing a linear portion of a silicon nitride (Si ₃ N ₄ ) nanorod.
(B) and (c): electron beam diffraction (ED) patterns corresponding to (a).
(D): Photograph of a high-resolution transmission electron microscope (HRTEM) image showing that silicon nitride (Si ₃ N ₄ ) nanorods are crystallized.
FIG. 3 is a photograph of a transmission electron microscope (TEM) image showing a feature that the shape of a nanorod is composed of a straight portion and a curved portion, and the angle of a straight portion adjacent to the curved portion is about 120 degrees. It is.
FIG. 4 is a photograph of a high-resolution transmission electron microscope (HRTEM) image showing an example of a curved portion of a silicon nitride (Si ₃ N ₄ ) nanorod.

Claims

直径が２０〜８０ｎｍで長さが１〜１０ミクロンであることを特徴とする窒化硅素（Ｓｉ_３Ｎ_４）ナノロッド。Silicon nitride, wherein the diameter length at 20~80nm is from 1 to 10 microns _(Si 3 _{N 4)} nanorods.

還元剤として非晶質活性化炭素（ＡＡＣ）粉末を用い、酸化硅素（ＳｉＯ）粉末を窒素ガス環境下において１３５０℃〜１４００℃に加熱することを特徴とする窒化硅素（Ｓｉ_３Ｎ_４）ナノロッドの製造方法。An amorphous activated carbon (AAC) powder as a reducing agent, silicon oxide (SiO) nitride powder is characterized by heating to 1350 ° C. to 1400 ° C. in a nitrogen gas environment silicon _(Si 3 _{N 4)} nanorods Manufacturing method.

還元剤の非晶質活性化炭素（ＡＡＣ）粉末が１〜１００μｍのサイズの炭素フレークからなるとともに、この炭素フレークが１〜１０ｎｍの炭素粒子により構成されていることを特徴とする請求項２に記載の窒化硅素（Ｓｉ_３Ｎ_４）ナノロッドの製造方法。The amorphous activated carbon (AAC) powder as a reducing agent is formed of carbon flakes having a size of 1 to 100 μm, and the carbon flakes are formed of carbon particles having a size of 1 to 10 nm. The method for producing silicon nitride (Si ₃ N ₄ ) nanorods according to the above.