JP2002328615A - Surface structure of display equipment, display structure of information display equipment, and method for manufacturing surface structure of display equipment - Google Patents
Surface structure of display equipment, display structure of information display equipment, and method for manufacturing surface structure of display equipmentInfo
- Publication number
- JP2002328615A JP2002328615A JP2001133726A JP2001133726A JP2002328615A JP 2002328615 A JP2002328615 A JP 2002328615A JP 2001133726 A JP2001133726 A JP 2001133726A JP 2001133726 A JP2001133726 A JP 2001133726A JP 2002328615 A JP2002328615 A JP 2002328615A
- Authority
- JP
- Japan
- Prior art keywords
- information display
- display device
- fine particles
- synthetic resin
- spherical fine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明が属する技術分野】本発明は、計器類、携帯電
話、コンピュータ画面などの情報表示機器における表示
面を見やすくする技術に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a technique for making a display surface of an information display device such as an instrument, a mobile phone, or a computer screen easy to see.
【０００２】[0002]
【先行技術】計器類、携帯電話、コンピュータ画面など
の情報表示機器の表示面に表示された情報（文字、図形
など）は、情報表示機器の外部から入る光が、情報表示
機器の表示面を覆う表面材（保護パネル）によって、情
報表示機器を見る人の眼の方向へ平行に反射する場合が
ある。その場合、情報表示機器の表面が光ってみえるた
め、表示面に表示された情報が見えにくくなる。これを
防ぐ目的で、情報表示機器の表面材（保護パネル）を形
成する透明なガラス、合成樹脂などの上面に対して、
「防幻加工」を施すことが一般に行われている。[Prior Art] Information (characters, figures, etc.) displayed on the display surface of an information display device such as an instrument, a mobile phone, or a computer screen is reflected by light entering from the outside of the information display device. Depending on the surface material to be covered (protective panel), the information display device may be reflected parallel to the direction of the eyes of the viewer. In that case, the surface of the information display device looks shiny, so that the information displayed on the display surface is difficult to see. In order to prevent this, the top surface of transparent glass, synthetic resin, etc. forming the surface material (protection panel) of the information display device,
It is common practice to apply "anti-glare processing".
【０００３】表面材（保護パネル）への防幻加工は、表
面材（保護パネル）の材料として使用されるガラスや透
明な合成樹脂の表面に微細な凹凸を設けるというもので
あり、それら使用材料の表面に掻き傷をつける方法がそ
の一例である。外部から表面材（保護パネル）へ入射す
る光を、それらの微細な凹凸にて乱反射させることによ
り、その効果が達成される。The anti-glare processing on the surface material (protection panel) is to provide fine irregularities on the surface of glass or transparent synthetic resin used as the material of the surface material (protection panel). An example is a method of scratching the surface of a sheet. The effect is achieved by irregularly reflecting light incident on the surface material (protection panel) from outside from the fine irregularities.
【０００４】また、液晶を用いた情報表示機器に対して
光学特性を向上させることによって防幻性を高めるた
め、特開平７−２０９６３５号に開示されたような技術
もある。この技術は、液晶セルと保護パネルとの間に設
けられていた空気層の代わりに、透明なシリコンゲル剤
を封入するものである。There is also a technique disclosed in Japanese Patent Application Laid-Open No. 7-209635 for improving the anti-glare property by improving the optical characteristics of an information display device using a liquid crystal. This technique encloses a transparent silicone gel agent in place of the air layer provided between the liquid crystal cell and the protection panel.
【０００５】[0005]
【発明が解決しようとする課題】上述した防幻のための
技術では、情報表示機器の外部から入る光を乱反射させ
ることができる角度に限界がある。このため、表示面に
対する目の角度が例えば４５度以下になると情報表示機
器の外部の光が、目の方向へ反射してしまうため、見に
くくなってしまう。本発明が解決しようとする課題は、
情報表示機器における表示面に表示される情報を更に見
やすくする技術を提供するものである。In the above-described technology for preventing glare, there is a limit to the angle at which light entering from outside the information display device can be diffusely reflected. For this reason, if the angle of the eyes with respect to the display surface is, for example, 45 degrees or less, light outside the information display device is reflected in the direction of the eyes, making it difficult to see. The problem to be solved by the present invention is
It is an object of the present invention to provide a technique for making information displayed on a display surface of an information display device easier to see.
【０００６】[0006]
【課題を解決するための手段】本発明者らは、上記課題
を解決すべく鋭意検討を行った結果、本発明たる表示機
器の表面構造、表示機器の表面構造、および表示機器の
表面構造の製造方法を提供するに至った。The present inventors have conducted intensive studies to solve the above-mentioned problems, and as a result, have found that the surface structure of the display device, the surface structure of the display device, and the surface structure of the display device according to the present invention. A manufacturing method has been provided.
【０００７】（請求項１）請求項１記載の発明は、情報
表示機器の表面構造に係る。すなわち、情報表示機器に
おける情報表示面(12)を保護するための保護パネル(20)
に対し、 その保護パネル(20)における表面側に、透明
合成樹脂の球状微粒子を敷き詰めて形成した表面層(40)
を備えたことを特徴とする。(Claim 1) The invention according to claim 1 relates to a surface structure of an information display device. That is, a protection panel (20) for protecting the information display surface (12) of the information display device.
In contrast, a surface layer (40) formed by spreading spherical fine particles of a transparent synthetic resin on the surface side of the protective panel (20)
It is characterized by having.
【０００８】（用語説明）「情報表示機器」としては、
携帯電話、パーソナルコンピュータ、各種計測機器など
情報を出力する出力表示装置を備えた機器である。「情
報表示面」とは、情報表示機器の出力表示装置であり、
液晶表示装置における液晶セル(12)、ＣＲＴの表面など
となる。液晶においては、バックライトの有無を問わな
い。「保護パネル(20)」としては、ガラスのほか、メタ
クリル樹脂、ポリカーボネート樹脂などの透明な合成樹
脂が採用される。(Explanation of terms) As the "information display device",
It is a device including an output display device for outputting information, such as a mobile phone, a personal computer, and various measuring devices. "Information display surface" is an output display device of an information display device,
It is a liquid crystal cell (12) in a liquid crystal display device, the surface of a CRT, or the like. In a liquid crystal, the presence or absence of a backlight does not matter. As the “protection panel (20)”, besides glass, a transparent synthetic resin such as methacrylic resin and polycarbonate resin is used.
【０００９】「透明合成樹脂」としては、ポリエチレ
ン、ポリプロピレン、ポリテトラフルオロエチレン、ポ
リスチレン、スチレン−イソプレン共重合体、スチレン
−アクリル酸エステル又はメタクリル酸エステル共重合
体、メタクリル酸エステルの単独重合体又はスチレン以
外のコモノマーとの共重合体、ポリアクリルニトリル、
ポリビニルアルコール−アクリル酸共重合体、ポリビニ
リデンクロライド、ポリ塩化ビニル、シリコーン樹脂、
ナイロン、フェノール樹脂、尿素樹脂、メラミン樹脂、
ベンゾグアナミン樹脂、ポリエステル樹脂、ポリウレタ
ン樹脂、ポリエーテルブロックアミド樹脂などである。The "transparent synthetic resin" includes polyethylene, polypropylene, polytetrafluoroethylene, polystyrene, styrene-isoprene copolymer, styrene-acrylate or methacrylate copolymer, methacrylate homopolymer or Copolymers with comonomers other than styrene, polyacrylonitrile,
Polyvinyl alcohol-acrylic acid copolymer, polyvinylidene chloride, polyvinyl chloride, silicone resin,
Nylon, phenolic resin, urea resin, melamine resin,
Benzoguanamine resin, polyester resin, polyurethane resin, polyether block amide resin and the like.
【００１０】「球状微粒子」とは、真球あるいは真球に
近い状態の微粒子である。これら微粒子の平均粒径は
０．１乃至１００ミクロンメートルの範囲内にあること
が好ましく、１ないし３０ミクロンの範囲内にあればよ
り好ましい。当該平均粒子径が前記した好ましい範囲よ
りも小さ過ぎると光が散乱されずに透過してしまい、ま
た大き過ぎると光は平行に近い状態で反射してしまうか
らである。"Spherical fine particles" are fine particles in a true sphere or a state close to a true sphere. The average particle size of these fine particles is preferably in the range of 0.1 to 100 microns, more preferably in the range of 1 to 30 microns. If the average particle diameter is smaller than the preferable range, the light is transmitted without being scattered, and if the average particle diameter is too large, the light is reflected in a nearly parallel state.
【００１１】保護パネルが合成樹脂にて形成されている
場合、合成樹脂基層部分に対して５ないし６０容量％の
範囲内にあることが好ましく、１０乃至３０容量％の範
囲内にあればさらに好ましい。当該割合が小さ過ぎると
光が透過してしまう割合が大きくなり、当該割合が大き
過ぎると表面の配列状態が不規則になるからである。When the protective panel is made of synthetic resin, it is preferably in the range of 5 to 60% by volume, more preferably in the range of 10 to 30% by volume, based on the synthetic resin base layer. . If the ratio is too small, the ratio of transmitting light increases, and if the ratio is too large, the arrangement state of the surface becomes irregular.
【００１２】「透明合成樹脂の球状微粒子を敷き詰めて
形成した表面層(40)」は、球状微粒子が保護パネルを隙
間なく覆うことができれば、理論的には一層でよい。し
かし、一層を完全な状態手提供するのは製造上困難であ
ったり、外力を受けて部分的に欠落したりするおそれが
あるので、二層以上（複数層）の球状微粒子を敷き詰め
ることが多い。The "surface layer (40) formed by spreading spherical fine particles of a transparent synthetic resin" is theoretically sufficient as long as the spherical fine particles can cover the protective panel without gaps. However, it is difficult to provide one layer in perfect condition by hand, or there is a possibility that the layer is partially missing due to external force. Therefore, two or more layers (multiple layers) of spherical fine particles are often spread. .
【００１３】（作用）情報表示機器の外部にて発光され
た光の一部は、表面層(40)における透明合成樹脂の球状
微粒子の表面にて反射されたり、球状微粒子を透過する
際の内表面で反射されたりするが、球状微粒子が球体で
あるため、どのような角度で入っても乱反射する。この
ため、情報表示機器の情報表示面は、様々な角度から見
やすいものとなる。(Function) A part of the light emitted outside the information display device is reflected on the surface of the transparent synthetic resin spherical fine particles in the surface layer (40), and the light emitted when the spherical fine particles are transmitted through the spherical fine particles. Although the light is reflected on the surface, since the spherical fine particles are spherical, they are irregularly reflected at any angle. For this reason, the information display surface of the information display device is easy to see from various angles.
【００１４】（請求項２）請求項２記載の発明は、請求
項１記載の情報表示機器の表面構造を限定したものであ
り、表面層(40)の上面を平滑化した平滑化表面(41)を備
えたことを特徴とする。(Claim 2) The invention according to claim 2 limits the surface structure of the information display device according to claim 1, and has a smooth surface (41) obtained by smoothing the upper surface of the surface layer (40). ).
【００１５】（用語説明）「平滑化」とは、球状微粒子
のみでは凹凸があるという場合、たとえば手触りが良く
ないという場合に、その凹凸を小さくした構造をいう。
最上面の球状微粒子の平均粒径が小さければ、平滑化は
必要ない場合もある。平滑化の手段は、球状微粒子によ
る表面層(40)をどのように形成したかによって異なる。
塗装などの手法によって球状微粒子を固定する場合に
は、研磨加工による。表面保護フィルム(50)によって使
用前の表面層(40)を保護する場合には、その表面保護フ
ィルム(50)と表面層との間に塗布される剥離剤(51)を球
状微粒子側に残すような手法によって平滑化することも
できる。(Explanation of terms) The term "smoothing" refers to a structure in which when only spherical fine particles have irregularities, for example, when the touch is not good, the irregularities are reduced.
If the average diameter of the spherical fine particles on the uppermost surface is small, smoothing may not be required in some cases. The means for smoothing differs depending on how the surface layer (40) made of the spherical fine particles is formed.
When the spherical fine particles are fixed by a method such as painting, polishing is performed. When protecting the surface layer (40) before use with the surface protection film (50), the release agent (51) applied between the surface protection film (50) and the surface layer is left on the spherical fine particle side. Smoothing can also be performed by such a method.
【００１６】（作用）情報表示機器の外部にて発光され
た光の一部は、平滑化表面(41)や球状微粒子を透過する
際の内表面で反射されたりするが、球状微粒子が球体で
あるため、どのような角度で入っても乱反射する。この
ため、情報表示機器の情報表示面は、様々な角度から見
やすいものとなる。(Function) A part of the light emitted outside the information display device is reflected on the smoothing surface (41) or the inner surface when the spherical fine particles are transmitted. Because of this, diffuse reflection occurs at any angle. For this reason, the information display surface of the information display device is easy to see from various angles.
【００１７】（請求項３）請求項３記載の発明は、情報
表示機器における情報表示面(12)を保護するための保護
パネル(20)に対し、 その保護パネル(20)における表面
側に、透明合成樹脂の球状微粒子を敷き詰めて形成した
表面層(40)を備え、 情報表示機器の情報表示面(12)と
保護パネル(20)との間には、透明粘弾性物質を充填した
緩衝層(31)を備えた情報表示機器の情報表示構造に係
る。(Claim 3) The invention according to claim 3 is characterized in that a protection panel (20) for protecting an information display surface (12) of an information display device is provided on the front side of the protection panel (20). A buffer layer filled with a transparent viscoelastic substance is provided between the information display surface (12) of the information display device and the protective panel (20). The present invention relates to an information display structure of an information display device having (31).
【００１８】（用語説明）「透明粘弾性物質」として
は、ゲル状又はエラストマー状の粘弾性物質が好適であ
る。具体的には、例えば、シリコンゲル、ポリウレタン
エラストマーなどである。(Explanation of Terms) As the “transparent viscoelastic substance”, a gel or elastomer viscoelastic substance is suitable. Specifically, for example, silicone gel, polyurethane elastomer and the like are used.
【００１９】更に具体的に説明する。透明弾性ゲルとし
ては、寒天やコンニャクなどの天然ゲル状物質、ポリウ
レタンやポリビニルアルコールなどの高分子ゲル状物質
が例示される。高分子エラストマーとしては、顕著な弾
性を有する高分子物質、即ち軟質ポリ塩化ビニル樹脂、
スチレン−ブテン ブロック共重合体、エチレン−酢酸
ビニル共重合体、エチレン−アクリル酸エステル共重合
体、ポリウレタン、ポリエーテル系重合体、ポリエステ
ル系重合体などの熱可塑性エラストマー、さらに天然ゴ
ムやポリブタジエン及びその他イソプレン又はブタジエ
ン共重合体などのジエン系ゴム、アクリルゴムやポリサ
ルファイド系ゴムなどで代表される各種合成ゴムなどが
ある。This will be described more specifically. Examples of the transparent elastic gel include natural gel substances such as agar and konjac, and high molecular gel substances such as polyurethane and polyvinyl alcohol. As the polymer elastomer, a polymer material having remarkable elasticity, that is, a soft polyvinyl chloride resin,
Thermoplastic elastomers such as styrene-butene block copolymer, ethylene-vinyl acetate copolymer, ethylene-acrylate copolymer, polyurethane, polyether polymer, polyester polymer, natural rubber, polybutadiene and others There are various kinds of synthetic rubbers represented by diene rubbers such as isoprene or butadiene copolymers, acrylic rubbers and polysulfide rubbers.
【００２０】合成透明弾性ゲルとしては、ゲル化油など
の合成ゲル状物質が例示される。脂肪酸アルミニウムな
どの金属石鹸、12-ヒドロキシ ステアリン酸、ジベンジ
リデン ソルビトール、アミノ酸系油ゲル化剤などは、
各種の油類にこれらを添加した場合、当該油類をゲル状
に変える作用がある（本間，池田：化学の領域 36 (1
0), 697-701）。例えば流動パラフィンにオレイン酸ア
ルミニウムを添加して調製した流動パラフィン ゲル
は、本発明に使用し得る好適なゲル材料である。Examples of the synthetic transparent elastic gel include synthetic gel substances such as gelling oil. Metal soaps such as fatty acid aluminum, 12-hydroxystearic acid, dibenzylidene sorbitol, amino acid oil gelling agents, etc.
When these are added to various oils, they have the effect of converting the oils into a gel (Honma, Ikeda: Chemistry 36 (1
0), 697-701). For example, a liquid paraffin gel prepared by adding aluminum oleate to liquid paraffin is a suitable gel material that can be used in the present invention.
【００２１】高分子材料に可塑剤又はプロセス油を添加
して可塑化させた材料も、高分子ゲル状物質として使用
できる。このような材料には、軟質ポリ塩化ビニル、ポ
リビニルアルコール−エチレングリコール混合系の他
に、例えば高粘着性コスモゲルパッキン（株式会社 コ
スモ計器製 PEゲルパッキン HC04Nなど）のような製品
もある。これらの材料も、本発明の充填層として使用し
得る好適な粘弾性材料である。A plasticized material obtained by adding a plasticizer or a process oil to a polymer material can also be used as the polymer gel substance. Examples of such a material include, in addition to soft polyvinyl chloride and a mixture of polyvinyl alcohol and ethylene glycol, products such as highly adhesive cosmogel packing (such as Cosmo Keiki's PE gel packing HC04N). These materials are also suitable viscoelastic materials that can be used as the packing layer of the present invention.
【００２２】（作用）情報表示機器の外部にて発光され
た光の一部は、透明合成樹脂の球状微粒子の表面にて反
射されるが、表面が球体であるため、どのような角度で
入っても乱反射する。また、情報表示機器の情報表示面
と保護パネルとの間に透明粘弾性物質が充填されている
ので、情報表示面から発せられる光は、その錯乱が抑制
される。このため、情報表示面へ入ろうとする光も、情
報表示面から発せられる光も、情報表示面を様々な角度
から見やすいように作用させる。(Function) A part of the light emitted outside the information display device is reflected on the surface of the spherical fine particles of the transparent synthetic resin. However, since the surface is a sphere, it enters at any angle. Even diffusely reflected. Further, since the transparent viscoelastic substance is filled between the information display surface of the information display device and the protection panel, the light emitted from the information display surface is suppressed from being disturbed. For this reason, both the light entering the information display surface and the light emitted from the information display surface act so that the information display surface can be easily viewed from various angles.
【００２３】（請求項４）請求項４記載の発明は、情報
表示機器における情報表示面(12)を保護するための保護
パネル(20)に対し、その保護パネル(20)における表面側
に、透明合成樹脂の球状微粒子を敷き詰めて形成した表
面層(40)を備えた表示機器の表面構造の製造方法に係
る。すなわち、樹脂をベースとする塗料の中に球状微粒
子を分散させて混合塗料を作成する混合工程と、 前記
混合塗料を保護パネルの表面に塗布する塗布工程と、
塗布した混合塗料を乾燥させる乾燥工程とを備えた表示
機器の表面構造の製造方法である。(Claim 4) The invention according to claim 4 is characterized in that a protection panel (20) for protecting an information display surface (12) of an information display device is provided on a front surface side of the protection panel (20). The present invention relates to a method for manufacturing a surface structure of a display device having a surface layer (40) formed by spreading spherical fine particles of a transparent synthetic resin. That is, a mixing step of preparing a mixed paint by dispersing spherical fine particles in a resin-based paint, an application step of applying the mixed paint to the surface of the protective panel,
And a drying step of drying the applied mixed paint.
【００２４】（請求項５）請求項５記載の発明もまた、
情報表示機器における情報表示面を保護するための保護
パネル(20)に対し、その保護パネル(20)における表面側
に、透明合成樹脂の球状微粒子を敷き詰めて形成した表
面層(40)を備えた表示機器の表面構造の製造方法に係
る。すなわち、表面保護フィルム(50)の一面へ透明合成
樹脂の球状微粒子による表面層(40)を付着させる印刷工
程と、 その印刷工程によって形成された表面層(40)に
おける反表面保護フィルム(50)側の面へ保護パネル(20)
を固定する固定工程とを備えた表示機器の表面構造の製
造方法である。(Claim 5) The invention according to claim 5 also includes:
A protective panel (20) for protecting an information display surface of an information display device, on the front side of the protective panel (20), a surface layer (40) formed by spreading spherical fine particles of a transparent synthetic resin. The present invention relates to a method for manufacturing a surface structure of a display device. That is, a printing step of attaching a surface layer (40) of spherical fine particles of a transparent synthetic resin to one surface of the surface protection film (50), and an anti-surface protection film (50) on the surface layer (40) formed by the printing step. Protective panel to side surface (20)
And a fixing step of fixing the surface structure of the display device.
【００２５】印刷の手法は、熱転写、特にグラビア印刷
が代表的である。表面層(40)へ固定された表面保護フィ
ルム(50)は、固定工程が終了した後に剥離してもよい
が、情報表示機器の最終消費者によって剥離してもらう
こととしてもよい。A typical printing method is thermal transfer, particularly gravure printing. The surface protective film (50) fixed to the surface layer (40) may be peeled off after the fixing step is completed, or may be peeled off by the final consumer of the information display device.
【００２６】（請求項６）請求項６記載の発明もまた、
情報表示機器における情報表示面を保護するための保護
パネル(20)に対し、その保護パネル(20)における表面側
に、透明合成樹脂の球状微粒子を敷き詰めて形成した表
面層(40)を備えた表示機器の表面構造の製造方法に係
る。すなわち、表面保護フィルム(50)の一面へ透明合成
樹脂の球状微粒子による表面層(40)を付着させる付着工
程と、 その付着工程によって形成された微粒子付着フ
ィルムを、表面層(40)側の面を射出成型用金型の内面予
め固定する金型内面固定工程と、 その金型へ保護パネ
ル(20)用の透明樹脂成形材料を注入して成型する成型工
程とを備えた表示機器の表面構造の製造方法である。(Claim 6) The invention according to claim 6 also includes:
A protective panel (20) for protecting an information display surface of an information display device, on the front side of the protective panel (20), a surface layer (40) formed by spreading spherical fine particles of a transparent synthetic resin. The present invention relates to a method for manufacturing a surface structure of a display device. That is, an adhesion step in which a surface layer (40) of transparent synthetic resin spherical fine particles is adhered to one surface of the surface protection film (50), and the fine particle adhesion film formed in the adhesion step is attached to the surface on the surface layer (40) side. The surface structure of a display device comprising: a mold inner surface fixing step of fixing the inner surface of an injection molding mold in advance; and a molding step of injecting and molding a transparent resin molding material for the protection panel (20) into the mold. It is a manufacturing method of.
【００２７】ここにいう成型工程は、例えばインモール
ド成型である。またここでも、表面層(40)へ固定された
表面保護フィルム(50)は、固定工程が終了した後に剥離
してもよいが、情報表示機器の最終消費者によって剥離
してもらうこととしてもよい。The molding step here is, for example, in-mold molding. Also here, the surface protective film (50) fixed to the surface layer (40) may be peeled off after the fixing step is completed, but may be peeled off by the final consumer of the information display device. .
【００２８】[0028]
【発明の実施の形態】以下、本発明を実施の形態及び図
面に基づいて、更に詳しく説明する。ここで使用する図
面は、図１乃至図５である。DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, the present invention will be described in more detail with reference to embodiments and drawings. The drawings used here are FIGS. 1 to 5.
【００２９】（図１）図１に基づいて、第一の実施形態
について説明する。この実施形態は、発光源１１と液晶
セル１２とからなる液晶１０に対し、液晶セル１２側へ
中間層３０を介して保護パネル２０を備え、更にその保
護パネル２０の外表面に表面層４０を備えた情報表示機
器の表示構造である。(FIG. 1) A first embodiment will be described with reference to FIG. In this embodiment, a protective panel 20 is provided for a liquid crystal 10 composed of a light source 11 and a liquid crystal cell 12 via an intermediate layer 30 on the liquid crystal cell 12 side, and a surface layer 40 is further provided on the outer surface of the protective panel 20. 2 is a display structure of an information display device provided.
【００３０】中間層３０は、表面層４０および保護パネ
ル２０に対して外力が加わった際に液晶セル１２を保護
するための空気層となっている。表面層４０は、ポリウ
レタンの球状微粒子（ポリウレタンビーズ）によって形
成されている。このポリウレタンビーズの粒径は、５な
いし２０μｍであり、平均粒径は１０μｍである。ポリ
ウレタンビーズが二層を形成するようにしてから表面を
平滑化し、平滑化表面４１を形成している。The intermediate layer 30 is an air layer for protecting the liquid crystal cell 12 when an external force is applied to the surface layer 40 and the protection panel 20. The surface layer 40 is formed of polyurethane spherical fine particles (polyurethane beads). The particle size of the polyurethane beads is 5 to 20 μm, and the average particle size is 10 μm. After the polyurethane beads form two layers, the surface is smoothed to form a smoothed surface 41.
【００３１】（図２）図２に基づいて、第二の実施形態
について説明する。この実施形態は、第一の実施形態に
おける空気の中間層３０の代わりに透明ゲル剤を充填し
た緩衝層３１を形成している点が異なる。(FIG. 2) A second embodiment will be described with reference to FIG. This embodiment is different from the first embodiment in that a buffer layer 31 filled with a transparent gel agent is formed instead of the air intermediate layer 30 in the first embodiment.
【００３２】（図３）図３に基づいて、第三の実施形態
について説明する。この実施形態は、印刷技術を用いて
保護パネル２０および表面層４０を形成したものであ
る。保護パネル２０の両端には印刷部としてインク２１
が載っている。このインク２１は、例えば、携帯電話の
液晶表示部における外枠部分を形成するものである。表
面保護フィルム５０と表面層４０との間には、剥離剤５
１（離型剤）を存在させ、表面保護フィルム５０を剥が
しやすくしている。なお、この表面保護フィルム５０
は、本実施形態に係る情報表示機器、例えば携帯電話の
消費者が、購入後に剥がすものとして提供される。(FIG. 3) A third embodiment will be described with reference to FIG. In this embodiment, the protection panel 20 and the surface layer 40 are formed by using a printing technique. At both ends of the protection panel 20, ink 21 is used as a printing unit.
There is. The ink 21 forms, for example, an outer frame portion in a liquid crystal display of a mobile phone. A release agent 5 is provided between the surface protective film 50 and the surface layer 40.
1 (release agent) is present to make the surface protection film 50 easy to peel off. The surface protection film 50
Is provided as a product that the consumer of the information display device according to the present embodiment, for example, a mobile phone, peels off after purchasing.
【００３３】（図４）図４に基づいて、第四の実施形態
について説明する。この実施形態と第三の実施形態との
相違点は、剥離剤５１（離型剤）が表面層４０に残る点
である。すなわち、この剥離剤５１が表面層４０の平滑
化を達成している。(FIG. 4) A fourth embodiment will be described with reference to FIG. The difference between this embodiment and the third embodiment is that the release agent 51 (release agent) remains on the surface layer 40. That is, the release agent 51 achieves smoothing of the surface layer 40.
【００３４】（図５）図５に基づいて、第五の実施形態
について説明する。この実施形態では、保護パネル２０
へ直接固着する第一層となる球状微粒子の平均粒径を大
きなものし、最上面の球状微粒子の平均粒径が小さくし
ている。表面層４０を塗装工程などによって形成する場
合において、図５のような構成を採用すれば、平滑化工
程を省略することもできる。(FIG. 5) A fifth embodiment will be described with reference to FIG. In this embodiment, the protection panel 20
The average particle diameter of the spherical fine particles which directly adheres to the first layer is large, and the average particle diameter of the spherical fine particles on the uppermost surface is small. In the case where the surface layer 40 is formed by a painting process or the like, if the configuration shown in FIG. 5 is adopted, the smoothing process can be omitted.
【００３５】[0035]
【実施例１】厚さ１ mmのメタクリル樹脂透明板（三菱
レイヨン株式会社製品 アクリライトL-001）の保護紙を
剥がしてから表面をシクロヘキサンで脱脂し、その上に
ウレタン系微粒子を含む二液型ウレタン塗料を、乾燥皮
膜の厚さが８〜12 μmになるように塗布した。Example 1 A two-part liquid containing 1 mm thick methacrylic resin transparent plate (Acrylite L-001 manufactured by Mitsubishi Rayon Co., Ltd.) was peeled off, and the surface was degreased with cyclohexane. The urethane paint was applied so that the thickness of the dried film became 8 to 12 μm.
【００３６】ここで採用した塗料は、ポリエステルポリ
オール（大日本インキ化学工業株式会社製品 バーノッ
クD6-439）100重量部及びポリイソシアヌレート（大日
本インキ化学工業株式会社製品 バーノックDN-980）67
重量部をポリマー成分とし、これに微粒子成分として平
均粒径６ μmのウレタン系微粒子（根上工業株式会社製
品 アートパールC-800）26重量部、及び希釈剤としてキ
シレン35重量部、トルエン20重量部、酢酸ブチル30重量
部及び酢酸エチル15重量部の混合溶剤300重量部を希釈
剤として添加して調製されたものである。The coating material used here was 100 parts by weight of polyester polyol (product of Dainippon Ink and Chemicals, Inc., Burnock D6-439) and polyisocyanurate (product of Dainippon Ink and Chemicals, Inc., product of Burnock DN-980) 67.
Parts by weight of a polymer component, 26 parts by weight of a urethane-based fine particle having an average particle diameter of 6 μm (art pearl C-800 manufactured by Negami Kogyo Co., Ltd.), 35 parts by weight of xylene as a diluent, and 20 parts by weight of toluene And 300 parts by weight of a mixed solvent of 30 parts by weight of butyl acetate and 15 parts by weight of ethyl acetate as a diluent.
【００３７】次に、ポリビニルアルコール（クラレ株式
会社製品 PVA-424H）100重量部に対し、エチレングリコ
ール500重量部の混合比率からなるゲル状透明粘弾性体
（厚さ１ mm）を調製した。Next, a gel-like transparent viscoelastic body (thickness: 1 mm) was prepared by mixing 100 parts by weight of polyvinyl alcohol (PVA-424H, manufactured by Kuraray Co., Ltd.) with 500 parts by weight of ethylene glycol.
【００３８】上記微粒子付き透明板とゲル状透明粘弾性
体の界面、及びゲル状透明粘弾性体と文字板の界面に、
水97重量部とイソプロピルアルコール３重量部の混合液
及びを空気の泡が残留しないように充填して、これらの
各部分同士を接合した。当該混合液の量は空気の泡を排
除出来る最低限度の量で良く、当該混合液は最終的には
ゲル状のポリビニルアルコールに吸収され、これにより
当該ゲル状部分がやや膨潤して、極めて良好な界面の密
着状態が得られた。At the interface between the transparent plate with fine particles and the gel-like transparent viscoelastic body and the interface between the gel-like transparent viscoelastic body and the dial,
A mixed solution of 97 parts by weight of water and 3 parts by weight of isopropyl alcohol and a mixture of air were filled so that air bubbles did not remain, and these parts were joined to each other. The amount of the mixed solution may be the minimum amount that can eliminate air bubbles, and the mixed solution is eventually absorbed by the gel-like polyvinyl alcohol, whereby the gel-like portion swells a little and is very good. A good interface adhesion state was obtained.
【００３９】このようにして得られた本実施例１による
防幻性表示板を、ガラス表面に凹凸を付けた表示板と比
較したところ、前者は後者に対して遙かに優れた透明度
があり、液晶板の表示を非常にはっきりと読み取ること
が出来た。When the thus obtained antiglare display panel according to the first embodiment was compared with a display panel having a glass surface with irregularities, the former had much better transparency than the latter. The display on the liquid crystal plate could be read very clearly.
【００４０】[0040]
【比較例】のメタクリル樹脂透明板（三菱レイヨン株式
会社製品 アクリライトL-001）の保護紙を剥がしてから
表面をシクロヘキサンで脱脂し、その上にウレタン系微
粒子を含む二液型ウレタン塗料を、乾燥皮膜の厚さが８
〜12 μmになるように塗布した。[Comparative Example] The protective paper of a methacrylic resin transparent plate (Acrylite L-001 manufactured by Mitsubishi Rayon Co., Ltd.) was peeled off, the surface was degreased with cyclohexane, and a two-pack type urethane paint containing urethane-based fine particles was applied thereon. Dry film thickness 8
It was applied to a thickness of 1212 μm.
【００４１】ここで採用した塗料は、ポリエステルポリ
オール（大日本インキ化学工業株式会社製品 バーノッ
クD6-439）100重量部及びポリイソシアヌレート（大日
本インキ化学工業株式会社製品 バーノックDN-980）67
重量部をポリマー成分とし、これに微粒子成分として平
均粒径６ μmのウレタン系微粒子（根上工業株式会社製
品 アートパールC-800）26重量部、及び希釈剤としてキ
シレン35重量部、トルエン20重量部、酢酸ブチル30重量
部及び酢酸エチル15重量部の混合溶剤300重量部を希釈
剤として添加して調製したものである。The coating material used here was 100 parts by weight of a polyester polyol (Burnock D6-439 manufactured by Dainippon Ink and Chemicals, Inc.) and polyisocyanurate (Burnock DN-980 manufactured by Dainippon Ink and Chemicals, Inc.) 67
Parts by weight of a polymer component, 26 parts by weight of a urethane-based fine particle having an average particle diameter of 6 μm (art pearl C-800 manufactured by Negami Kogyo Co., Ltd.), 35 parts by weight of xylene as a diluent, and 20 parts by weight of toluene And a mixed solvent of 30 parts by weight of butyl acetate and 15 parts by weight of ethyl acetate as a diluent.
【００４２】このようにして調製した従来型の防幻性表
面板を、液晶面にそのまま重ねて従来型の防幻性表示板
を調製した。当該従来型防幻性表示板の透明度は、前記
した実施例１と比較してその透明度は遙かに劣った。ま
た、液晶板の表示は、実施例１ほどの明瞭さを得ること
ができなかった。The conventional anti-glare display panel was prepared by superposing the conventional anti-glare surface plate thus prepared on the liquid crystal surface as it was. The transparency of the conventional anti-glare display panel was much lower than that of Example 1 described above. In addition, the display on the liquid crystal plate could not be as clear as in Example 1.
【００４３】[0043]
【実施例２】厚さ１ mmのメタクリル樹脂透明板（三菱
レイヨン株式会社製品 アクリライトL-001）の保護紙を
剥がしてから表面をシクロヘキサンで脱脂し、その上に
ウレタン系微粒子を含む二液型ウレタン塗料を、乾燥皮
膜の厚さが８〜12 μmになるように塗布した。Example 2 A two-part liquid containing 1 mm thick methacrylic resin transparent plate (Acrylite L-001 manufactured by Mitsubishi Rayon Co., Ltd.) was peeled off, and the surface was degreased with cyclohexane. The urethane paint was applied so that the thickness of the dried film became 8 to 12 μm.
【００４４】ここで採用した塗料は、ポリエステルポリ
オール（大日本インキ化学工業株式会社製品 バーノッ
クD6-439）100重量部及びポリイソシアヌレート（大日
本インキ化学工業株式会社製品 バーノックDN-980）67
重量部をポリマー成分とし、これに微粒子成分として平
均粒径６ μmのウレタン系微粒子（根上工業株式会社製
品 アートパールC-800）26重量部、及び希釈剤としてキ
シレン35重量部、トルエン20重量部、酢酸ブチル30重量
部及び酢酸エチル15重量部の混合溶剤300重量部を希釈
剤として添加して調製したものである。The coating material used here was 100 parts by weight of a polyester polyol (Burnock D6-439, manufactured by Dainippon Ink and Chemicals, Inc.) and polyisocyanurate (Burnock DN-980, manufactured by Dainippon Ink and Chemicals, Inc.) 67
Parts by weight of a polymer component, 26 parts by weight of a urethane-based fine particle having an average particle diameter of 6 μm (art pearl C-800 manufactured by Negami Kogyo Co., Ltd.), 35 parts by weight of xylene as a diluent, and 20 parts by weight of toluene And a mixed solvent of 30 parts by weight of butyl acetate and 15 parts by weight of ethyl acetate as a diluent.
【００４５】次に透明体（ゲル）層として、株式会社
コスモ計器製 高粘着性PEゲルパッキン（0.5 mm厚；ポ
リエチレンとスチレンの共重合体60%と、プロセス オイ
ル40%で構成されるブレンド物であると言われている）H
C04N（アスカー硬度＝４）を使用し、これをアクリル板
と文字板の間に挟み、両方の面に圧着して、これらの面
に完全に密着させた。Next, as a transparent body (gel) layer,
High-viscosity PE gel packing made by Cosmo Keiki (0.5 mm thick; said to be a blend composed of 60% polyethylene-styrene copolymer and 40% process oil) H
C04N (Asker hardness = 4) was used, sandwiched between an acrylic plate and a dial, pressed against both surfaces, and completely adhered to these surfaces.
【００４６】このようにして得られた防幻性表示板を比
較例と比較したところ、前者は後者に対して遙かに優れ
た透明度を備えていた。そのために文字板の表示を非常
にはっきりと読み取ることが出来た。なお粘着剤は、特
に使用しなかった。When the antiglare display panel thus obtained was compared with the comparative example, the former had much higher transparency than the latter. Therefore, the display on the dial could be read very clearly. The pressure-sensitive adhesive was not particularly used.
【００４７】[0047]
【実施例３】厚さ１ mmのメタクリル樹脂透明板（三菱
レイヨン株式会社製品 アクリライトL-001）の保護紙を
剥がしてから表面をシクロヘキサンで脱脂し、その上に
ウレタン系微粒子を含む二液型ウレタン塗料を、乾燥皮
膜の厚さが８〜12 μmになるように塗布した。Example 3 A two-part liquid containing 1 mm thick methacrylic resin transparent plate (Acrylite L-001 manufactured by Mitsubishi Rayon Co., Ltd.) was peeled off, the surface was degreased with cyclohexane, and urethane-based fine particles were further placed on the surface. The urethane paint was applied so that the thickness of the dried film became 8 to 12 μm.
【００４８】ここで採用した塗料は、ポリエステルポリ
オール（大日本インキ化学工業株式会社製品 バーノッ
クD6-439）100重量部及びポリイソシアヌレート（大日
本インキ化学工業株式会社製品 バーノックDN-980）67
重量部をポリマー成分とし、これに微粒子成分として平
均粒径６ μmのウレタン系微粒子（根上工業株式会社製
品 アートパールC-800）26重量部、及び希釈剤としてキ
シレン35重量部、トルエン20重量部、酢酸ブチル30重量
部及び酢酸エチル15重量部の混合溶剤300重量部を希釈
剤として添加して調製されたものである。次に透明体
（ゲル）層として、流動パラフィンにオレイン酸アルミ
ニウム１%を添加して半流動性の流動パラフィン ゲル
（本間，池田：化学の領域 36 (10), 697-701, 1982参
照）を調製し、これをアクリル板と文字板の間に流し込
み、空気を完全に追い出して全体を固定した。The coating material used here was 100 parts by weight of a polyester polyol (product of Dainippon Ink and Chemicals, Inc., Burnock D6-439) and polyisocyanurate (product of Dainippon Ink and Chemicals, Inc., product of Burnock DN-980) 67.
Parts by weight of a polymer component, 26 parts by weight of a urethane-based fine particle having an average particle diameter of 6 μm (art pearl C-800 manufactured by Negami Kogyo Co., Ltd.), 35 parts by weight of xylene as a diluent, and 20 parts by weight of toluene And 300 parts by weight of a mixed solvent of 30 parts by weight of butyl acetate and 15 parts by weight of ethyl acetate as a diluent. Next, as a transparent (gel) layer, 1% aluminum oleate was added to liquid paraffin to give a semi-liquid liquid paraffin gel (Honma, Ikeda: Chemistry 36 (10), 697-701, 1982). It was prepared and poured between the acrylic plate and the dial, and the air was completely displaced and the whole was fixed.
【００４９】このようにして得られた防幻性表示板を前
記比較例と比較したところ、前者は後者に対して遙かに
優れた透明度を備えていた。そのために文字板の表示を
非常にはっきりと読み取ることが出来た。なお、粘着剤
層は、特に使用しなかった。When the antiglare display panel thus obtained was compared with the comparative example, the former had much higher transparency than the latter. Therefore, the display on the dial could be read very clearly. The pressure-sensitive adhesive layer was not particularly used.
【００５０】[0050]
【実施例４】厚さ１ mmのメタクリル樹脂透明板（三菱
レイヨン株式会社製品 アクリライトL-001）の保護紙を
剥がしてから表面をシクロヘキサンで脱脂し、透明板と
して使用した。Example 4 A protective plate of a 1 mm thick methacrylic resin transparent plate (Acrylite L-001 manufactured by Mitsubishi Rayon Co., Ltd.) was peeled off, the surface was degreased with cyclohexane, and used as a transparent plate.
【００５１】その上にウレタン系微粒子（平均粒径６
μm；根上工業株式会社製品 アートパールC-800）を表
面一面にグラビア印刷して付着させたPETフィルム（厚
さ38μm）を貼り付けた。接着層として、ポリエステル
樹脂（大日本インキ化学工業株式会社製バーノックD6-4
39）85重量部とアクリル樹脂（大日本インキ化学工業株
式会社製アクリデックBU-885）15重量部の混合物に、さ
らにポリイソシアネート30重量部を添加したものを介在
させた。次に透明体（ゲル）層として、流動パラフィン
にオレイン酸アルミニウム１%を添加して流動パラフィ
ン ゲル（本間，池田：化学の領域 36 (10), 697-701,
1982参照）を調製し、これをアクリル板と文字板の間に
流し込み、空気を完全に追い出して全体を固定した。On top of this, urethane-based fine particles (average particle size 6
μm; a PET film (38 μm in thickness) was attached by gravure printing onto Art Pearl C-800 manufactured by Negami Industry Co., Ltd. As an adhesive layer, a polyester resin (Varnock D6-4 manufactured by Dainippon Ink and Chemicals, Inc.)
39) A mixture of 85 parts by weight and 15 parts by weight of an acrylic resin (Acrydec BU-885 manufactured by Dainippon Ink and Chemicals, Inc.) was further added with 30 parts by weight of a polyisocyanate. Next, as a transparent (gel) layer, 1% aluminum oleate was added to liquid paraffin to form a liquid paraffin gel (Honma, Ikeda: Chemistry, 36 (10), 697-701,
1982) was prepared and poured between the acrylic plate and the dial, and the air was completely displaced to fix the whole.
【００５２】このようにして得られた防幻性表示板を前
記の比較例と比較したところ、前者は後者に対して遙か
に優れた透明度を備えていた。そのために文字板の表示
を非常にはっきりと読み取ることが出来た。When the antiglare display panel thus obtained was compared with the comparative example, the former had much better transparency than the latter. Therefore, the display on the dial could be read very clearly.
【００５３】[0053]
【実施例５】ウレタン系微粒子（平均粒径６ μm）をグ
ラビア印刷して付着させたポリエステル フィルム（厚
さ38 μm；実施例４を参照のこと）を、ウレタン系微粒
子を一方の金型面に向けて固定し、次にポリエステル樹
脂（85重量部）/アクリル樹脂（15重量部）/ポリイソシ
アネート（30重量部）のブレンド物（実施例４参照のこ
と；厚さ50 μm）を重ね、当該金型の反対側からアクリ
ル樹脂成形材料（三菱レイヨン株式会社製アクリペット
VH-001）を注入して透明板を形成させ、全体の厚さが１
mmになるように射出成形（所謂インモールド成形）し
た。Example 5 A polyester film (thickness: 38 μm; see Example 4) on which urethane-based fine particles (average particle diameter: 6 μm) were attached by gravure printing, was coated with the urethane-based fine particles on one mold surface. Then, a blend of polyester resin (85 parts by weight) / acrylic resin (15 parts by weight) / polyisocyanate (30 parts by weight) (see Example 4; thickness of 50 μm) is overlaid. Acrylic resin molding material (Acrypet manufactured by Mitsubishi Rayon Co., Ltd.)
VH-001) is injected to form a transparent plate.
Injection molding (so-called in-mold molding) was performed so as to obtain mm.
【００５４】次に透明体（ゲル）層として、流動パラフ
ィンにオレイン酸アルミニウム１%を添加して流動パラ
フィンゲル（本間，池田：化学の領域 36 (10), 697-70
1, 1982参照）を調製し、これをアクリル板と文字板の
間に流し込み、空気を完全に追い出して全体を固定し
た。Next, as a transparent body (gel) layer, 1% of aluminum oleate was added to liquid paraffin to form a liquid paraffin gel (Honma, Ikeda: Chemistry 36 (10), 697-70).
1, 1982) was prepared and poured between the acrylic plate and the dial, and the air was completely displaced and the whole was fixed.
【００５５】このようにして得られた防幻性表示板を前
述の比較例と比較したところ、前者は後者に対して遙か
に優れた透明度を備えていた。そのために文字板の表示
を非常にはっきりと読み取ることが出来た。When the antiglare display panel thus obtained was compared with the above-mentioned comparative example, the former had much higher transparency than the latter. Therefore, the display on the dial could be read very clearly.
【００５６】[0056]
【発明の効果】請求項１および請求項２記載の発明によ
れば、情報表示機器における表示面に表示される情報を
更に見やすくする表示機器の表面構造を提供することが
できた。また、請求項３記載の発明によれば、情報表示
機器における表示面に表示される情報を更に見やすくす
る表示機器の表面構造を提供することができた。また、
請求項４から請求項６記載の発明によれば、情報表示機
器における表示面に表示される情報を更に見やすくする
表示機器の表面構造の製造方法を提供することができ
た。According to the first and second aspects of the present invention, it is possible to provide a surface structure of a display device that makes it easier to view information displayed on a display surface of the information display device. According to the third aspect of the present invention, it is possible to provide a surface structure of a display device that makes it easier to view information displayed on a display surface of the information display device. Also,
According to the inventions described in claims 4 to 6, it is possible to provide a method of manufacturing a surface structure of a display device that makes it easier to see information displayed on a display surface of the information display device.
【図１】本発明の第一の実施形態を示す断面図である。FIG. 1 is a sectional view showing a first embodiment of the present invention.
【図２】本発明の第二の実施形態を示す断面図である。FIG. 2 is a sectional view showing a second embodiment of the present invention.
【図３】本発明の第三の実施形態を示す断面図である。FIG. 3 is a sectional view showing a third embodiment of the present invention.
【図４】本発明の第四の実施形態を示す断面図である。FIG. 4 is a sectional view showing a fourth embodiment of the present invention.
【図５】本発明の第五の実施形態を示す断面図である。FIG. 5 is a sectional view showing a fifth embodiment of the present invention.
１０ 液晶 １１ 発光源 １２ 液晶セル ２０ 保護パネル ３０ 中間層 ３１ 緩衝層 ４０ 表面層 ４１ 平滑化表面 ５０ 表面保護フィルム ５１ 剥離剤 DESCRIPTION OF SYMBOLS 10 Liquid crystal 11 Light emission source 12 Liquid crystal cell 20 Protective panel 30 Intermediate layer 31 Buffer layer 40 Surface layer 41 Smoothing surface 50 Surface protective film 51 Release agent
Claims (6)
るための保護パネルに対し、 その保護パネルにおける表面側に、透明合成樹脂の球状
微粒子を敷き詰めて形成した表面層を備えたことを特徴
とする情報表示機器の表面構造。1. A protective panel for protecting an information display surface of an information display device, comprising a surface layer formed by spreading spherical fine particles of a transparent synthetic resin on a surface side of the protective panel. Surface structure of information display equipment.
えたことを特徴とする請求項１に記載した表示機器の表
面構造。2. The surface structure of a display device according to claim 1, further comprising a smoothed surface obtained by smoothing an upper surface of the surface layer.
るための保護パネルに対し、 その保護パネルにおける
表面側に、透明合成樹脂の球状微粒子を敷き詰めて形成
した表面層を備え、 情報表示機器の情報表示面と保護パネルとの間には、透
明粘弾性物質を充填した緩衝層を備えた情報表示機器の
表示構造。3. A protection panel for protecting an information display surface of an information display device, comprising a surface layer formed by spreading spherical fine particles of a transparent synthetic resin on a surface side of the protection panel. A display structure of an information display device including a buffer layer filled with a transparent viscoelastic substance between an information display surface and a protection panel.
るための保護パネルに対し、 その保護パネルにおける
表面側に、透明合成樹脂の球状微粒子を敷き詰めて形成
した表面層を備えた表示機器の表面構造の製造方法であ
って、 樹脂をベースとする塗料の中に球状微粒子を分散させて
混合塗料を作成する混合工程と、 前記混合塗料を保護パネルの表面に塗布する塗布工程
と、 塗布した混合塗料を乾燥させる乾燥工程とを備えた表示
機器の表面構造の製造方法。4. A surface of a display device having a surface layer formed by spreading spherical fine particles of a transparent synthetic resin on a surface side of the protection panel for protecting an information display surface of the information display device. A method of manufacturing a structure, comprising: a mixing step of forming a mixed paint by dispersing spherical fine particles in a resin-based paint; an applying step of applying the mixed paint to a surface of a protective panel; A method for manufacturing a surface structure of a display device, comprising: a drying step of drying a paint.
るための保護パネルに対し、その保護パネルにおける表
面側に、透明合成樹脂の球状微粒子を敷き詰めて形成し
た表面層を備えた表示機器の表面構造の製造方法であっ
て、 表面保護フィルムの一面へ透明合成樹脂の球状微粒子に
よる表面層を付着させる印刷工程と、 その印刷工程によって形成された表面層における反表面
保護フィルム側の面へ保護パネルを固定する固定工程と
を備えた表示機器の表面構造の製造方法。5. A surface of a display device having a surface layer formed by spreading spherical fine particles of a transparent synthetic resin on a surface side of a protective panel for protecting an information display surface of the information display device. A method of manufacturing a structure, comprising: a printing step of attaching a surface layer of transparent synthetic resin spherical fine particles to one surface of a surface protection film; And a fixing step for fixing the surface structure of the display device.
るための保護パネルに対し、その保護パネルにおける表
面側に、透明合成樹脂の球状微粒子を敷き詰めて形成し
た表面層を備えた表示機器の表面構造の製造方法であっ
て、 表面保護フィルムの一面へ透明合成樹脂の球状微粒子に
よる表面層を付着させる付着工程と、 その付着工程によって形成された微粒子付着フィルム
を、表面層側の面を射出成型用金型の内面予め固定する
金型内面固定工程と、 その金型へ保護パネル用の透明樹脂成形材料を注入して
成型する成型工程とを備えた表示機器の表面構造の製造
方法。6. A surface of a display device having a surface layer formed by spreading spherical fine particles of a transparent synthetic resin on a surface side of the protection panel for protecting an information display surface of the information display device. A method for manufacturing a structure, comprising: an attaching step of attaching a surface layer of transparent synthetic resin spherical particles to one surface of a surface protection film; and a fine particle attachment film formed by the attaching step, wherein the surface on the surface layer side is injection-molded. A method for manufacturing a surface structure of a display device, comprising: a mold inner surface fixing step of fixing an inner surface of a mold in advance; and a molding step of injecting and molding a transparent resin molding material for a protective panel into the mold.