KR100775850B1 - Light-diffusing sheet for back light unit - Google Patents
Light-diffusing sheet for back light unit Download PDFInfo
- Publication number
- KR100775850B1 KR100775850B1 KR1020060069062A KR20060069062A KR100775850B1 KR 100775850 B1 KR100775850 B1 KR 100775850B1 KR 1020060069062 A KR1020060069062 A KR 1020060069062A KR 20060069062 A KR20060069062 A KR 20060069062A KR 100775850 B1 KR100775850 B1 KR 100775850B1
- Authority
- KR
- South Korea
- Prior art keywords
- particles
- light
- film
- average particle
- particle diameter
- Prior art date
Abstract
Description
도 1은 본 발명의 일 실시예에 따른 내부확산필름을 이용한 백라이트유니트용 광확산 시트의 단면도. 1 is a cross-sectional view of a light diffusion sheet for a backlight unit using an internal diffusion film according to an embodiment of the present invention.
도 2는 도 1의 평면도.2 is a plan view of FIG.
<도면의 주요부분에 대한 부호의 간단한 설명> <Brief description of symbols for the main parts of the drawings>
1 : 유기확산제 1' : 투명기재필름 1: Organic Diffusion 1 ': Transparent Substrate Film
2 : 내부확산필름 3a : 단분산 수지입자2:
3b, 3c : 수지입자 4 : 바인더 수지3b, 3c: resin particles 4: binder resin
5 : 광확산층 5: light diffusion layer
본 발명은 LCD의 백라이트 유닛에 사용되는 백라이트유니트용 광확산 시트에 관한 것으로, 보다 구체적으로는 박막트랜지스터 액정디스플레이(TFT-LCD) 또는 슈 퍼트위스티드네마틱 액정디스플레이(STN-LCD)에 사용되는 광확산 시트로, 디스플레이의 선명한 화상을 얻기 위하여 측면 또는 후면에 위치한 냉음극 형광 램프로부터 조사되는 선형 광으로부터의 빛을 통과시키면서 균일한 면광을 유도하여 선명한 광화상을 얻을 수 있는 백라이트유니트용 광확산 시트에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a light diffusion sheet for a backlight unit used in a backlight unit of an LCD, and more particularly, to a light used for a thin film transistor liquid crystal display (TFT-LCD) or a super twisted nematic liquid crystal display (STN-LCD). Diffusion sheet, a light diffusion sheet for backlight unit that can induce a uniform surface light while passing light from linear light emitted from a cold cathode fluorescent lamp located on the side or the back to obtain a clear image of the display and obtain a clear light image It is about.
일반적으로 LCD백라이트용 광확산 시트는 카네비게이션, 휴대폰, PDA, 디지탈 카메라, 휴대용TV, 캠코더 등의 소형용이나, 중 대형의 노트북 PC, 데스크 탑용 모니터 등에서 사용되는, 도광판 한쪽 단면에 선형 램프가 설치되는 것을 특징으로 하는 WEDGE형 백라이트 유닛 및 한 개 이상의 램프가 설치, 사용되는 SIDE형 백라이트 유닛에 있어서, 빛을 도광판에서 나온 불균일한 광원을 백라이트 유닛 전면 방향을 중심으로 한 균일한 광으로 전환하는 역할을 하며, TV나 일부 대형화된 모니터에 있어서 사용되는 직하형 즉 백라이트 후면에 다수의 냉음극형광 램프 또는 평면 램프가 설치되는 경우에 있어서도 선형으로 시인되는 광을 확산시켜 균일한 전방향 중심 분포의 면광원화 하는 기능을 수행하며, 빛의 분포 중심을 전면 방향으로 전환하는 기능으로부터 정면 방향의 휘도를 증가시키는 효과를 가져온다.Generally, the light diffusion sheet for LCD backlight is equipped with a linear lamp on one side of the light guide plate which is used in small size such as car navigation system, mobile phone, PDA, digital camera, portable TV, camcorder, etc. A SIDE type backlight unit in which a WEDGE type backlight unit and at least one lamp is installed and used, converting light from a light guide plate into a uniform light centered on a front side of a backlight unit. Even in the case of a large number of cold-cathode fluorescent lamps or flat lamps installed in the direct type, that is, the back of the backlight, which is used in TVs or some large-sized monitors, the light is linearly diffused so that the plane of the uniform omnidirectional center distribution can be obtained. Function to convert the light from the center of light distribution to the front It produces the effect of increasing the brightness of the face direction.
이러한 LCD 백라이트용 광확산 시트의 기능에 있어서 은폐기능과 확산 기능을 수행하고 휘도를 향상시키기 위하여 투명한 플라스틱 필름 위에 투명한 유기 수지입자 또는 무기 입자를 투명한 수지 바인더로 도포하는 방식이 개발되어 왔다(일본특허공개공보 특개평7-174909, 한국공개공보 제2000-0027862호, 한국공개공보 제1998-0020430호).In order to perform the function of concealment and diffusion in the function of the light diffusion sheet for LCD backlight and improve the brightness, a method of applying transparent organic resin particles or inorganic particles on a transparent plastic film with a transparent resin binder has been developed (Japanese Patent) Korean Laid-Open Patent Publication No. 7-174909, Korean Laid-Open Publication No. 2000-0027862, and Korean Laid-Open Publication No. 1998-0020430.
그러나, 위와 같은 종래의 기술들은 투명한 수지 필름 위에 수지입자를 도포 함으로 현재 박형화 추세의 백라이트에 요구되는 휘선에 대한 차폐 성능을 만족하지 못하고 있다.However, the conventional techniques as described above do not satisfy the shielding performance against the bright line required for the backlight of the current thinning trend by applying the resin particles on the transparent resin film.
본 발명은 상기와 같은 문제점을 해결하기 위해 안출한 것으로서, 본 발명의 목적은 종래 사용되고 있는 투명 수지 필름을 대체하여 내부에 유기확산제가 혼입되어 탁도를 높인 내부확산필름을 기재로 사용함으로써, 빛의 굴절, 산란성을 최대화하여 확산 기능을 향상시켜 휘선 차폐력을 뛰어나게 향상시킨 백라이트유니트용 광확산 시트를 제공하고자 하는 것이다.The present invention has been made to solve the above problems, the object of the present invention is to replace the transparent resin film used in the past by using an internal diffusion film with an organic diffusion agent is mixed therein to increase the turbidity, It is an object of the present invention to provide a light diffusion sheet for a backlight unit that maximizes refraction and scattering properties and improves a diffusion function so as to excellently shield light rays.
본 발명의 상기 및 다른 목적과 이점은 첨부 도면을 참조하여 바람직한 실시예를 설명한 하기의 설명으로부터 보다 분명해 질 것이다. The above and other objects and advantages of the present invention will become more apparent from the following description of the preferred embodiments with reference to the accompanying drawings.
상기 목적을 달성하기 위한 본 발명에 따른 백라이트유니트용 광확산 시트는 투명기재필름내에 유기확산제가 분포된 내부확산필름으로서, 헤이즈 40~95%, 투과율 50~95%의 광특성을 가진 내부확산필름과, 상기 내부확산필름 상의 적어도 일면에 바인더 수지와 투명한 수지 입자로 도포된 광확산층을 포함하는 것을 특징으로 한다.The light diffusion sheet for a backlight unit according to the present invention for achieving the above object is an internal diffusion film in which an organic diffusion agent is distributed in a transparent substrate film, the internal diffusion film having a light characteristic of haze 40 ~ 95%, transmittance 50 ~ 95% And a light diffusing layer coated with a binder resin and transparent resin particles on at least one surface of the inner diffusion film.
바람직하게는 상기 투명한 수지입자는 입경 분포가 평균입경의 ±20% 내에 80%~100% 존재하는 단분산입자와 상기 단분산 입자보다 작은 평균입경을 가진 입자 1종 이상 혼용된 입자인 것을 특징한다.Preferably, the transparent resin particles are monodispersed particles having a particle size distribution of 80% to 100% within ± 20% of the average particle diameter, and particles having at least one particle having an average particle diameter smaller than the monodisperse particles. .
보다 바람직하게는 상기 작은 평균입경을 가진 입자는 2종 이상의 입자로서, 각각 최대 평균입경이 3㎛ ~ 7㎛ 와 1㎛ ~ 3㎛ 인 것을 특징으로 한다.More preferably, the particles having a small average particle diameter are two or more kinds of particles, and the maximum average particle diameter is 3 μm to 7 μm and 1 μm to 3 μm, respectively.
또한 바람직하게는 상기 단분산입자의 최대 평균입경은 10㎛ ~ 50㎛인 것을 특징으로 한다.Also preferably, the maximum average particle diameter of the monodisperse particles is 10 μm to 50 μm.
더욱 바람직하게는 상기 바인더 수지의 굴절율과 상기 투명기재필름의 굴절율의 차이는 0 초과 0.22 이하이고, 상기 바인더 수지의 굴절율은 상기 투명기재필름의 굴절율보다 작은 것을 특징으로 한다.More preferably, the difference between the refractive index of the binder resin and the refractive index of the transparent base film is greater than 0 and 0.22 or less, and the refractive index of the binder resin is smaller than the refractive index of the transparent base film.
이하, 본 발명의 실시예와 도면을 참조하여 본 발명을 상세히 설명한다. 이들 실시예는 오로지 본 발명을 보다 구체적으로 설명하기 위해 예시적으로 제시한 것일 뿐, 본 발명의 범위가 이들 실시예에 의해 제한되지 않는다는 것은 당업계에서 통상의 지식을 가지는 자에 있어서 자명할 것이다.Hereinafter, the present invention will be described in detail with reference to embodiments and drawings of the present invention. These examples are only presented by way of example only to more specifically describe the present invention, it will be apparent to those skilled in the art that the scope of the present invention is not limited by these examples. .
도 1은 본 발명의 일 실시예에 따른 내부확산필름을 이용한 백라이트유니트용 광확산 시트의 단면도이고 도 2는 도 1의 평면도이다.1 is a cross-sectional view of a light diffusion sheet for a backlight unit using an internal diffusion film according to an embodiment of the present invention and FIG. 2 is a plan view of FIG.
도 1에서 알 수 있는 바와 같이, 내부확산필름(2)은 유기확산제(1)와 투명기재필름(1')으로 구성된다. 유기확산제(1)에 의한 내부 광확산층 형성에 있어서 광학적 기능은 유기확산제(1)에 의해 형성된 렌즈형상 또는 굴곡 형상에 의해 결정되는데, 유기확산제(1)의 렌즈 형상 또는 굴곡 형상이 많을수록 내부확산 필름의 차폐기능과 확산 기능이 커지게 된다.As can be seen in FIG. 1, the internal diffusion film 2 is composed of an organic diffusion agent 1 and a transparent base film 1 ′. In the formation of the internal light diffusion layer by the organic diffusion agent (1), the optical function is determined by the lens shape or the bending shape formed by the organic diffusion agent (1), the more the lens shape or bending shape of the organic diffusion agent (1) The shielding function and the diffusion function of the internal diffusion film are increased.
상기 내부확산필름(2)에 있어, 투명기재필름(1')은 열가소성 수지로서 폴리에틸렌테레프탈레이트, 폴리에틸렌-2,6-나프탈레이트 등과 이들을 주성분으로 하는 공중합체, 또는 이들 수지의 혼합물 등의 폴리에스테르계 수지가 바람직하고, 또한 유기확산제(1)도 열가소성 수지로서 폴리에틸렌, 폴리프로필렌, 폴리메틸펜텐 등과 이들을 주성분으로 하는 공중합체, 또는 이들 수지의 혼합물 등의 폴리올레핀계 수지 등이 바람직하다. In the internal diffusion film 2, the transparent base film 1 'is a thermoplastic resin, such as polyethylene terephthalate, polyethylene-2,6-naphthalate, a copolymer containing these as a main component, or a mixture of these resins or the like. Preferred resins are preferred, and the organic diffusing agent (1) is also preferably thermoplastic resins such as polyethylene, polypropylene, polymethylpentene, copolymers containing these as main components, or polyolefin resins such as mixtures of these resins.
여기서, 투명기재 필름(1')으로는 이축연신 폴리에틸렌테레프탈레이트 필름이 가장 바람직하다. 이 이축연신 폴리에틸렌테레프탈레이트 필름은 기계적 강도, 내열성, 투명성 및 평탄성 등이 우수하다는 것은 주지된 사실이고, 이 필름을 기재필름으로 사용함으로써, 광확산 시트에 있어서도 그 성능이 발휘될 수 있는 장점이 있다. Here, the biaxially stretched polyethylene terephthalate film is most preferable as the transparent base film 1 '. It is well known that this biaxially stretched polyethylene terephthalate film is excellent in mechanical strength, heat resistance, transparency, flatness, and the like. By using this film as a base film, there is an advantage that the performance can be exhibited even in a light diffusion sheet. .
한편, 내부확산필름의 일면에 형성되는 광확산층(5)에서는 표면 렌즈형상의 면적을 크게 하기 위하여 평균입경 7 마이크론 이상의 큰 입자를 사용하는 것이 좋으며, 더욱 바람직하기로는 10마이크론 이상 50마이크론 이하의 평균입경을 가진, 입경 분포가 평균입경의 ±20% 내에 80%~100% 존재하는 입자(이하 "단분산 입자"이라고 한다)를 사용하는 것이 바람직하다. On the other hand, in the light diffusing
이러한 입경분포는 콜터사의 입도 분포 측정기 LS PARTICLE SIZE ANALYZER로 빛의 산란을 이용하여 입경을 측정하는 방식을 이용할 수 있다. 특히 후면에 여러개의 램프 배열로 발광량을 크게 하여 TV용도로 사용하는 직하형 LAMP 방식에 의한 백라이트 유닛에 있어서는 확산 기능의 극대화를 통한 휘도 향상과 램프의 휘선을 지우는 역할에 있어서 내부 광확산제에 의한 굴절, 산란 없이 직접적으로 통과된 빛은 휘선을 만들어 빛의 품위를 떨어뜨린다. The particle size distribution may be a method of measuring particle size by using scattering of light with a particle size distribution measuring device LS PARTICLE SIZE ANALYZER of Coulter. In particular, in the backlight unit of the direct type LAMP type, which uses a large number of lamps on the rear to increase the amount of light emitted, the internal light diffusing agent plays a role in improving luminance by maximizing the diffusion function and erasing the bright lines of the lamp. Light passed directly without refraction or scattering creates a bright line, which reduces the dignity of the light.
따라서, 기재필름 내부에 유기확산제를 첨가한 내부확산필름 사용을 통해 확산성을 극대화하고 표면 렌즈 형상의 면적을 크게 함으로써 확산 기능 및 은폐력을 올리는 동시에 그에 따른 휘도 상승 효과를 얻기 위하여 표면의 투명한 구형 유기 입자(3a)의 최대 평균입경은 클수록 유리하며 7마이크론 이상, 더욱 바람직하게는 10마이크론 이상 50마이크론 이하의 단분산입자인 것이 좋다. 50마이크론 이상의 평균입경 입자를 사용한 경우에는 습식 도포가 어려우며 도포액 분산에도 어려움이 있기 때문에 50마이크론 이하로 하는 것이 좋다. 또한 차폐 기능을 최대화 하기 위하여 표면에 도포되는 수지 입자는 최대 평균입경 입자 보다 작은 1종 이상의 입자(3b 또는 3c), 바람직하게는 2종 이상의 입자(3b,3c)를 혼용하는 것이 좋다. 바람직한 실시예에서, 상기 작은 2종의 입자의 최대 평균입경은 각각 3㎛ 내지 7㎛와 1㎛ 내지 3㎛인 것이 바람직하다.Therefore, the use of an internal diffusion film in which an organic diffusion agent is added to the inside of the base film maximizes the diffusibility and increases the area of the surface lens shape to increase the diffusion function and hiding power, and at the same time to obtain a brightness increase effect according to the transparent spherical shape of the surface. The larger the maximum average particle diameter of the
광확산층(5)에 사용되는 광확산제로는 구형 투명 입자가 적합하며, 투명입자로는 아크릴 입자, 스티렌 입자, 실리콘입자 등의 유기입자와 합성 실리카, 그라스비드, 다이아몬드 등의 무기입자가 사용될 수 있으며 이들 광확산제를 단독 혹은 2종 이상을 혼합하여 사용할 수 있다.As the light diffusing agent used in the light diffusing
광확산필름의 광확산층(5)에 사용되는 바인더(binder) 수지는 투명하여야 하며 폴리메타크릴산메틸 또는 메타크릴산에스테르 공중합체 등의 아크릴계, 우레탄계, 에폭시계, 비닐계, 폴리에스테르계, 폴리아미드계 등의 수지 중에서 단독 또는 2종 이상을 혼합하여 사용할 수 있다. 이 투명한 바인더 수지의 굴절율은 투명기재필름(1')의 굴절율과의 차이가 0 초과 0.22 이하이면서 투명기재필름(1')의 굴절율보다 작은 값이어야 한다. 바인더수지의 굴절율이 투명기재필름(1')의 굴절율보다 큰 경우에는 투명수지층에서 광확산층로 향하는 빛의 진행방향에서 빛이 광확산층과 투명기재필름(1')의 경계면에서 투과보다는 반사가 많이 일어나 광투과율을 저하시키게 된다. 또한 굴절율의 차이가 0.22이상이 되면 광확산층(5)/ 투명기재필름(1')의 경계면에서 빛의 굴절 및 산란이 많이 일어나 높은 휘도를 얻을 수 있는 광확산필름을 제조하기 힘들어진다.The binder resin used for the light diffusing
투명한 기재필름에 상기 광확산제와 유기 수지 바인더를 용제에 희석하여 도포하는 방식으로는 나이프 도포 방식, 그라비아 전이 도포방식, 리버스 롤 도포방식 등의 통상적인 습식 도포 방식을 사용할 수 있다.As a method of diluting and applying the light diffusing agent and the organic resin binder to a transparent base film in a solvent, conventional wet coating methods such as a knife coating method, a gravure transfer coating method, and a reverse roll coating method may be used.
이때 도포 후도는 최대 평균입경을 가진 입자의 150%를 넘지 않도록 하면 균일한 도포 표면의 바람직한 효과를 얻는다.At this time, even after application, if it does not exceed 150% of the particle | grains which have the largest average particle diameter, the preferable effect of a uniform application surface will be obtained.
도포 후도가 최대평균입경을 가진 입자의 평균입경의 150%를 넘으면 단위 면적당 입자량의 과잉으로 인한 휘도 저하를 유발 할 수 있다. If the coating degree exceeds 150% of the average particle diameter of the particle having the maximum average particle diameter, it may cause a decrease in luminance due to the excessive amount of particles per unit area.
이러한 내부확산필름과 한 면에 형성된 광확산 층의 이면에는 슬립성을 부여하고, 제단 및 조립 작업시 발생하는 스크래치를 억제하기 위한 경도를 올리고, 이물 혼입을 방지할 목적의 대전방지 기능이 있는 도포층을 형성할 수도 있다.Application of an antistatic function for the purpose of imparting slip properties to the back surface of the light diffusing layer formed on one side of the inner diffusion film and increasing the hardness to suppress scratches generated during the cutting and assembling operations, and to prevent foreign substances from mixing. It may also form a layer.
[실시예]EXAMPLE
[실시예 1]Example 1
내부확산필름(도레이(주) QE31-125㎛, Haze:92 Transmittance:90)의 일면에 하기의 조성을 가진 도포액을 마이크로 그라비어를 이용하여 광확산 시트를 제조하였다.A light diffusion sheet was prepared by using microgravure in a coating liquid having the following composition on one surface of the internal diffusion film (QE31-125 µm, Haze: 92 Transmittance: 90).
도포액 조성Coating liquid composition
- 바인더 수지 (애경화학화학: A-811) : 18.2 중량부-Binder Resin (Aekyung Chemical Chemistry: A-811): 18.2 parts by weight
- 경화제 (애경화학화학 :DN980S): 1.8 중량부 -Curing agent (Aekyung Chemical Chemistry: DN980S): 1.8 parts by weight
- 합성수지 입자 (소켄케미칼: MX-1500 단분산 평균입경 15㎛) : 18.1 중량부-Synthetic resin particles (Soken Chemical: MX-1500 monodispersed average particle diameter: 15㎛): 18.1 parts by weight
- 합성수지 입자 (소켄케미칼: MX-500 단분산 평균입경 5㎛) : 5.0 중량부-Synthetic resin particles (Sokken Chemical: MX-500 monodispersed
- 메틸에틸케톤 : 28.3 중량부Methyl ethyl ketone: 28.3 parts by weight
- 톨루엔 : 28.3 중량부 Toluene: 28.3 parts by weight
[실시예 2]Example 2
내부확산필름(도레이(주) QE32-125㎛, Haze:40 Transmittance:92)의 일면에 하기의 조성을 가진 도포액을 마이크로 그라비어를 이용하여 광확산 시트를 제조하였다.A light diffusion sheet was prepared by using microgravure in a coating liquid having the following composition on one surface of an internal diffusion film (QE32-125 µm, Haze: 40 Transmittance: 92).
도포액 조성Coating liquid composition
바인더 수지 (애경화학: A-811) : 18.2 중량부Binder Resin (Aekyung Chemical: A-811): 18.2 parts by weight
- 경화제 (애경화학: DN980S): 1.8 중량부Curing agent (Aekyung Chemical: DN980S): 1.8 parts by weight
- 합성수지 입자 (소켄케미칼: MX-1500 단분산 평균입경 15㎛) : 18.1 중량부-Synthetic resin particles (Soken Chemical: MX-1500 monodispersed average particle diameter: 15㎛): 18.1 parts by weight
- 합성수지 입자 (소켄케미칼: MX-500 단분산 평균입경 5㎛) : 5.0 중량부-Synthetic resin particles (Sokken Chemical: MX-500 monodispersed
- 메틸에틸케톤 : 28.3 중량부Methyl ethyl ketone: 28.3 parts by weight
- 톨루엔 : 28.3 중량부 Toluene: 28.3 parts by weight
[실시예 3]Example 3
내부확산필름(도레이(주) PY-2-110㎛, Haze:85 Transmittance:90)의 일면에 하기의 조성을 가진 도포액을 마이크로 그라비어를 이용하여 광확산 시트를 제조하였다.A light diffusion sheet was prepared by using microgravure in a coating liquid having the following composition on one surface of an internal diffusion film (Toray Co., Ltd. PY-2-110 μm, Haze: 85 Transmittance: 90).
도포액 조성Coating liquid composition
- 바인더 수지 (애경화학: A-811) : 24.5 중량부-Binder Resin (Aekyung Chemical: A-811): 24.5 parts by weight
- 경화제 (애경화학: DN980S): 2.5 중량부Curing agent (Aekyung Chemical: DN980S): 2.5 parts by weight
- 합성수지 입자 (소켄케미칼: MX-1500H 단분산 평균입경 15㎛) : 14.0 중량부-Synthetic resin particles (Soken Chemical: MX-1500H monodisperse average particle diameter: 15㎛): 14.0 parts by weight
- 합성수지 입자 (소켄케미칼: MX-500 단분산 평균입경 5㎛) : 5.9 중량부-Synthetic resin particles (Soken Chemical: MX-500 Monodispersion Average particle size: 5㎛): 5.9 parts by weight
- 메틸에틸케톤 : 29.3 중량부-Methyl ethyl ketone: 29.3 parts by weight
- 톨루엔 : 29.3 중량부 Toluene: 29.3 parts by weight
[실시예 4]Example 4
내부확산필름(도레이(주) PY-3-110㎛, Haze:93 Transmittance:68)의 일면에 하기의 조성을 가진 도포액을 마이크로 그라비어를 이용하여 광확산 시트를 제조하였다. A light diffusion sheet was prepared by using microgravure in a coating solution having the following composition on one surface of an internal diffusion film (Toray Co., Ltd. PY-3-110 μm, Haze: 93 Transmittance: 68).
도포액 조성Coating liquid composition
- 바인더 수지 (애경화학: A-811) : 24.5 중량부-Binder Resin (Aekyung Chemical: A-811): 24.5 parts by weight
- 경화제 (애경화학: DN980S): 2.5 중량부Curing agent (Aekyung Chemical: DN980S): 2.5 parts by weight
- 합성수지 입자 (소켄케미칼: MX-1500H 단분산 평균입경 15㎛) : 14.0 중량부-Synthetic resin particles (Soken Chemical: MX-1500H monodisperse average particle diameter: 15㎛): 14.0 parts by weight
- 합성수지 입자 (소켄케미칼: MX-500 단분산 평균입경 5㎛) : 5.9 중량부-Synthetic resin particles (Soken Chemical: MX-500 Monodispersion Average particle size: 5㎛): 5.9 parts by weight
- 메틸에틸케톤 : 29.3 중량부-Methyl ethyl ketone: 29.3 parts by weight
- 톨루엔 : 29.3 중량부 Toluene: 29.3 parts by weight
[실시예 5]Example 5
내부확산필름(도레이(주) PY-4-110㎛, Haze:93 Transmittance:57)의 일면에 하기의 조성을 가진 도포액을 마이크로 그라비어를 이용하여 광확산 시트를 제조하였다. On one side of the internal diffusion film (Toray Co., Ltd. PY-4-110 μm, Haze: 93 Transmittance: 57), a light diffusion sheet was prepared by using microgravure in a coating solution having the following composition.
도포액 조성Coating liquid composition
- 바인더 수지 (애경화학: A-811) : 24.5 중량부-Binder Resin (Aekyung Chemical: A-811): 24.5 parts by weight
- 경화제 (애경화학: DN980S): 2.5 중량부Curing agent (Aekyung Chemical: DN980S): 2.5 parts by weight
- 합성수지 입자 (소켄케미칼: MX-1500H 단분산 평균입경 15㎛) : 14.0 중량부-Synthetic resin particles (Soken Chemical: MX-1500H monodisperse average particle diameter: 15㎛): 14.0 parts by weight
- 합성수지 입자 (소켄케미칼: MX-500 단분산 평균입경 5㎛) : 5.9 중량부-Synthetic resin particles (Soken Chemical: MX-500 Monodispersion Average particle size: 5㎛): 5.9 parts by weight
- 메틸에틸케톤 : 29.3 중량부-Methyl ethyl ketone: 29.3 parts by weight
- 톨루엔 : 29.3 중량부 Toluene: 29.3 parts by weight
[비교예1]Comparative Example 1
실시예 1에서 사용된 동일한 도포액을 내부확산필름이 아닌 투명수지필름(도레이새한(주) XU42, 188㎛)의 일면에 마이크로 그라비어를 이용하여 도포하여 광확산 시트를 제조하였다.The same coating liquid used in Example 1 was applied to one surface of the transparent resin film (Toray Saehan Co., Ltd. XU42, 188 μm) instead of the internal diffusion film to prepare a light diffusion sheet.
[비교예2]Comparative Example 2
실시예 3과 동일한 도포액을 내부확산필름이 아닌 투명수지필름(도레이새한(주) XU42, 188㎛)의 일면에 마이크로 그라비어를 이용하여 도포하여 광확산 시트를 제조하였다.The same coating liquid as in Example 3 was applied to one surface of the transparent resin film (Toray Saehan Co., Ltd. XU42, 188 μm) instead of the internal diffusion film to prepare a light diffusion sheet.
[실험예]Experimental Example
실험예 1 : 헤이즈(HAZE) 평가Experimental Example 1 HAZE Evaluation
실시예 1 내지 5및 비교예 1, 2에 의해 제조된 광확산 시트의 헤이즈(HAZE)를 평가하는 실험을 행하였다. ASTM D-1003에 의거하여 측정하였으며 측정기기는 NIPPON DENSHOKU KOGYO Co. Ltd. 모델1000을 이용하였다. The experiment which evaluated the haze (HAZE) of the light-diffusion sheet manufactured by Examples 1-5 and Comparative Examples 1 and 2 was done. It was measured according to ASTM D-1003, and the measuring device was NIPPON DENSHOKU KOGYO Co. Ltd. Model 1000 was used.
실험예 2 : 차폐력 평가Experimental Example 2 Evaluation of Shielding Force
실시예 1 내지 5및 비교예 1, 2에 의해 제조된 광확산 시트의 차폐력을 평가하는 실험을 행하였다. 탑콘사의 BM-7장비를 이용하여 백라이트 조립상의 정면 휘도를 등간격 30Point로 측정하여 아래 식 1과 같이 정의하여 수치화하였다.The experiment which evaluated the shielding force of the light-diffusion sheet manufactured by Examples 1-5 and Comparative Examples 1 and 2 was done. Using TopConn's BM-7 equipment, the front luminance on the backlight assembly was measured at equal intervals of 30 points and defined as shown in Equation 1 below.
[식 1][Equation 1]
[표 1] TABLE 1
상기 표 1에서 알 수 있는 바와 같이, 실시예 1~5와 같이 내부에 유기 확산제를 첨가한 내부확산필름을 기재로 제작한 광확산 시트는 비교예 1, 2와 같이 투명수지필름을 기재로 제작한 광확산 시트에 비하여 우수한 차폐력을 가짐을 알 수 있다. 또한 실시예1~5와 같이 내부 헤이즈가 높고 투과율이 낮은 내부확산 필름이 우수한 차폐력을 구현할 수 있음을 알 수 있다.As can be seen in Table 1, as in Examples 1 to 5, the light diffusing sheet prepared based on the internal diffusion film to which the organic diffusing agent was added is based on the transparent resin film as in Comparative Examples 1 and 2. It can be seen that it has an excellent shielding force compared to the light diffusion sheet produced. In addition, as in Examples 1 to 5, it can be seen that the internal diffusion film having high internal haze and low transmittance can realize excellent shielding force.
상술한 실시예는 본 발명을 구체적으로 예시하기 위한 것이며, 본 발명의 권리범위를 제한하는 것이 아니다. 또한 본 발명의 단순한 변형 내지 변경은 모두 본 발명의 영역에 포함되는 것으로 볼 수 있다.The above-described embodiments are intended to specifically illustrate the present invention, and do not limit the scope of the present invention. In addition, it can be seen that all simple modifications and variations of the present invention are included in the scope of the present invention.
본 발명에 따른 광확산 시트에 의하면, 기재 내부에 유기 확산제가 첨가된 내부확산필름을 사용함으로써 빛의 굴절, 산란성을 최대화하여 확산 기능을 향상시켜 높은 휘선 차폐력을 갖는 등의 우수한 광확산 시트를 제공할 수 있는 효과가 있 다. According to the light diffusing sheet according to the present invention, by using the internal diffusion film to which the organic diffusion agent is added to the inside of the substrate, the excellent light diffusion sheet such as having a high bright line shielding power by maximizing the refraction and scattering properties of light and improving the diffusion function There is an effect it can provide.
따라서 본 발명에 따른 광확산 시트는 높은 차폐 성능이 요구되는 슬림BLU 제조 등에 유용한 효과가 있다. Therefore, the light diffusion sheet according to the present invention has a useful effect such as manufacturing a slim BLU requiring high shielding performance.
Claims (5)