JP2002196887A - Transparent touch panel - Google Patents
Transparent touch panelInfo
- Publication number
- JP2002196887A JP2002196887A JP2000399590A JP2000399590A JP2002196887A JP 2002196887 A JP2002196887 A JP 2002196887A JP 2000399590 A JP2000399590 A JP 2000399590A JP 2000399590 A JP2000399590 A JP 2000399590A JP 2002196887 A JP2002196887 A JP 2002196887A
- Authority
- JP
- Japan
- Prior art keywords
- transparent
- touch panel
- transparent conductive
- conductive film
- transparent touch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明に属する技術分野】本発明は抵抗膜式の透明タッ
チパネルに関し、特に、製造工程が簡略化され、かつ製
造に際して環境負荷の少ない透明タッチパネルに関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a transparent touch panel of the resistive film type, and more particularly, to a transparent touch panel whose manufacturing process is simplified and which has a low environmental load in manufacturing.
【０００２】[0002]
【従来の技術】ＩＴＯ（錫添加酸化インジウム）に代表
される透明導電膜を使用したスイッチ（透明タッチパネ
ル）は、液晶や蛍光表示素子と組み合わせて家電製品、
情報機器等の操作盤として用いられている。透明タッチ
パネルでは、裏面に配した表示素子を切り替えて一つの
スイッチに複数の機能を付与できるため、限定された面
積に多機能な操作盤を配置することができる。同時に表
示の切り替えによって操作の順も分かりやすくなり、初
心者にとって取扱いが容易になる。2. Description of the Related Art A switch (transparent touch panel) using a transparent conductive film typified by ITO (tin-added indium oxide) is used in combination with a liquid crystal or a fluorescent display element for home electric appliances,
It is used as an operation panel for information equipment and the like. In the transparent touch panel, since a plurality of functions can be given to one switch by switching display elements arranged on the rear surface, a multifunctional operation panel can be arranged in a limited area. At the same time, by switching the display, the order of the operations becomes easy to understand, so that the handling is easy for a beginner.
【０００３】透明タッチパネルは、図１に示すように、
２枚の透明基板１、２のそれぞれ片面に透明導電膜３を
形成し、わずかな隙間４を保ちつつ両透明基板１、２の
透明導電膜３を対向させて接合した構造になっている。
図示例は、下側の透明基板１がガラス板等の板、上側の
透明基板２がＰＥＴ（ポリエチレンテレフタレート）フ
ィルム等の可撓性フィルムである。可撓性透明基板２側
を指などで押すことにより可撓性透明基板２を撓ませて
透明導電膜３同士を接触させ、スイッチ動作を行わせ
る。繰り返し接触後の可撓性透明基板２の劣化や不用意
な接触による誤動作を防止するため、少なくとも一方の
透明導電膜３上に多数の微少な絶縁物の突起（ドットス
ペーサー５）を一定の間隔で配置している。[0003] As shown in FIG.
A transparent conductive film 3 is formed on one surface of each of the two transparent substrates 1 and 2, and the transparent conductive films 3 of the two transparent substrates 1 and 2 are joined to face each other while maintaining a small gap 4.
In the illustrated example, the lower transparent substrate 1 is a plate such as a glass plate, and the upper transparent substrate 2 is a flexible film such as a PET (polyethylene terephthalate) film. By pressing the flexible transparent substrate 2 side with a finger or the like, the flexible transparent substrate 2 is bent to bring the transparent conductive films 3 into contact with each other, thereby performing a switch operation. In order to prevent deterioration of the flexible transparent substrate 2 after repeated contact or malfunction due to careless contact, a large number of minute insulating protrusions (dot spacers 5) are provided on at least one of the transparent conductive films 3 at regular intervals. It is arranged in.
【０００４】ところで、透明基板に形成する透明導電膜
は、透明基板の所定領域の全面に形成される場合だけで
なく、透明タッチパネルの動作方式の違い、あるいは絶
縁保持のために、例えば図２に示すような、パターン化
された透明導電膜６が用いられる場合もある。このよう
にパターン化された透明導電膜を持つ従来の透明タッチ
パネルでは、そのパターン形成方法として、スパッタ法
などにより堆積した透明導電膜にレジストを塗布し、フ
ォトリソグラフィー等によるパターン形成の後、湿式ま
たは乾式のエッチングにより不要な部分を除去する方法
がとられている。Incidentally, the transparent conductive film formed on the transparent substrate is not limited to the case where the transparent conductive film is formed on the entire surface of a predetermined region of the transparent substrate. As shown, a patterned transparent conductive film 6 may be used in some cases. In a conventional transparent touch panel having a transparent conductive film patterned in this manner, as a pattern forming method, a resist is applied to a transparent conductive film deposited by a sputtering method or the like, and after a pattern is formed by photolithography or the like, a wet or A method of removing unnecessary portions by dry etching is used.
【０００５】[0005]
【発明が解決しようとする課題】上記のように、パター
ン化された透明導電膜を持つ透明タッチパネルの製造に
は、湿式または乾式のエッチング工程が必要となるが、
このエッチング工程は、図３（イ）〜（ニ）に示すよう
に、湿式、乾式を問わず、透明導電膜７上へのレジスト
８塗布（図３（イ））、フォトリソグラフィー等による
パターン形成（図３（ロ））、エッチングによる不用部
分の除去（図３（ハ））、およびレジストの除去（図３
（ニ））からなるため、製造工程が煩雑で作業時間の短
縮が困難であるという問題がある。また、エッチングに
対する材料の耐性、エッチングに用いる薬剤やガスの安
全性、環境へ与える影響などの問題がある。本発明は上
記従来の欠点を解消するためになされたもので、製造工
程が簡略化され作業時間の短縮が可能であり、さらに、
製造に際して安全性が高く、環境への影響の少ない透明
タッチパネルを提供することを目的とする。As described above, the production of a transparent touch panel having a patterned transparent conductive film requires a wet or dry etching step.
This etching step includes, as shown in FIGS. 3A to 3D, application of a resist 8 on the transparent conductive film 7 (FIG. 3A), pattern formation by photolithography or the like irrespective of a wet type or a dry type. (FIG. 3B), removal of unnecessary parts by etching (FIG. 3C), and removal of the resist (FIG. 3C).
(D)), there is a problem that the manufacturing process is complicated and it is difficult to reduce the working time. There are also problems such as the resistance of the material to etching, the safety of chemicals and gases used for etching, and the effect on the environment. The present invention has been made in order to solve the above-mentioned conventional disadvantages, and the manufacturing process can be simplified and the working time can be reduced.
It is an object of the present invention to provide a transparent touch panel that is highly safe in manufacturing and has little effect on the environment.
【０００６】[0006]
【課題を解決するための手段】上記課題を解決する本発
明は、対向保持された２枚の透明基板のそれぞれ向き合
う面に透明導電膜を形成し、前記透明導電膜同士を接触
させることでスイッチ動作を行わせる抵抗膜式の透明タ
ッチパネルにおいて、少なくとも一方の透明導電膜が導
電性微粒子をフィラーとする透明導電ペーストの印刷面
により形成されていることを特徴とする。SUMMARY OF THE INVENTION In order to solve the above-mentioned problems, the present invention provides a switch by forming a transparent conductive film on two opposing surfaces of a transparent substrate and contacting the transparent conductive films with each other. In a resistive transparent touch panel that performs an operation, at least one transparent conductive film is formed of a printed surface of a transparent conductive paste containing conductive fine particles as a filler.
【０００７】請求項２は、請求項１の透明タッチパネル
において、透明導電ペースト中の導電性微粒子として、
少なくともインジウム、錫、亜鉛のいずれかを含む金属
の酸化物微粒子を用いたことを特徴とする。A second aspect of the present invention is the transparent touch panel according to the first aspect, wherein the conductive fine particles in the transparent conductive paste are:
It is characterized in that metal oxide fine particles containing at least one of indium, tin and zinc are used.
【０００８】請求項３は、請求項１の透明タッチパネル
において、印刷した導電ペーストの表面に透明レジスト
を塗布して透明性を向上させたことを特徴とする。According to a third aspect of the present invention, in the transparent touch panel of the first aspect, a transparent resist is applied to a surface of the printed conductive paste to improve transparency.
【０００９】[0009]
【発明の実施の形態】以下、本発明の実施の形態を図面
を参照して説明する。本発明の透明タッチパネルは、抵
抗膜式の透明タッチパネルであり、基本構造としては前
述した図１のような構造である（再度の説明は省略す
る）。そして、本発明は例えば図２に示したようなパタ
ーン化された透明導電膜６を持つ透明タッチパネルに適
用して好適である。Embodiments of the present invention will be described below with reference to the drawings. The transparent touch panel of the present invention is a transparent touch panel of a resistive film type, and has a basic structure as shown in FIG. 1 described above (repeated description is omitted). The present invention is suitably applied to, for example, a transparent touch panel having a patterned transparent conductive film 6 as shown in FIG.
【００１０】本発明の透明タッチパネルでは、２つの透
明基板の透明導電膜のうちの少なくとも一方の透明導電
膜が、例えばＩＴＯ微粒子等の導電性微粒子をフィラー
とする透明導電ペーストの印刷面により形成されてい
る。例えば図４に示すように、透明導電性ペーストを、
例えば図２に示したような所望のパターンが形成されて
いる刷版９を用いて、可撓性フィルムやガラス板等の透
明基板２１の上に印刷する。すると、刷版９を透明導電
ペーストが通過した場所のみに透明導電膜１０が形成さ
れる。この可撓性フィルムおよびガラス板を用いて、透
明タッチパネルを作成することで、エッチングによりパ
ターン化された透明導電膜を有する透明タッチパネルと
同等のパターン精度、絶縁性を有する透明タッチパネル
を製造することができる。In the transparent touch panel of the present invention, at least one of the transparent conductive films of the two transparent substrates is formed by a printed surface of a transparent conductive paste containing conductive fine particles such as ITO fine particles as a filler. ing. For example, as shown in FIG.
For example, using a printing plate 9 on which a desired pattern as shown in FIG. 2 is formed, printing is performed on a transparent substrate 21 such as a flexible film or a glass plate. Then, the transparent conductive film 10 is formed only at the place where the transparent conductive paste has passed through the printing plate 9. By making a transparent touch panel using this flexible film and a glass plate, it is possible to manufacture a transparent touch panel having the same pattern accuracy and insulating properties as a transparent touch panel having a transparent conductive film patterned by etching. it can.
【００１１】可撓性フィルムに透明導電ペーストによる
透明導電膜を形成した具体例を以下に述べる。図５に示
すように、ＰＥＴ（ポリエチレンテレフタレート）フィ
ルム１１の表面に、導電性微粒子１２をフィラーとした
透明導電ペーストを前述した刷版９を用いて印刷して、
パターン化された透明導電膜１３を作成した。導電性微
粒子１２として、ＩＴＯセラミックス（錫添加酸化イン
ジウムセラミックス）を粉体にしたものを用いた。粒子
の粒径は、以下に記す理由により、０．１μｍ以上、１
μｍ以下に分散するようにした。すなわち、粒径が０．
１μｍ未満であると、作成した透明導電膜のシート抵抗
が１０ｋΩ／□を超えてしまうものがあり、粒径が１μ
ｍを越えると、透明導電膜の透過率が著しく低下し、波
長５５０ｎｍにおける透過率が５０％に満たないものが
現れた。この透明導電膜を用いて透明タッチパネルを作
成したところ、透明タッチパネル背後の表示素子におい
て１０ポイント程度の大きさの文字が、透明タッチパネ
ル上では識別不能となってしまった。このため、上記の
ような粒径範囲とした。導電性微粒子の材料としては、
上述の実施形態で用いたＩＴＯ以外にもＳnＯ2、ＺnＯ
等の金属酸化物微粒子を用いることや、透明なプラスチ
ックの球状物の周りに導電膜を形成したものを用いるこ
とも可能である。前記により作成した透明導電膜１３の
膜厚は２μｍ、シート抵抗は１ｋΩ／□、透過率は波長
５５０ｎｍで７５％であった。透明導電膜の膜厚は低抵
抗を保ちつつできるだけ薄い方が望ましいが、本実施例
ではシート抵抗と透過率のバランスから２．０μｍとし
た。また、透明導電膜のパターン形状および寸法は、透
明タッチパネルの動作方式や仕様により決定されるが、
本実施例ではパターン幅１５０ｍｍ、パターン間隔０．
５ｍｍとした。A specific example in which a transparent conductive film made of a transparent conductive paste is formed on a flexible film will be described below. As shown in FIG. 5, a transparent conductive paste containing conductive fine particles 12 as a filler is printed on the surface of a PET (polyethylene terephthalate) film 11 using the printing plate 9 described above.
A patterned transparent conductive film 13 was formed. As the conductive fine particles 12, powdery ITO ceramics (tin-added indium oxide ceramics) was used. The size of the particles is 0.1 μm or more for the following reasons.
The dispersion was made to be less than μm. That is, when the particle size is 0.
If it is less than 1 μm, the sheet resistance of the formed transparent conductive film may exceed 10 kΩ / □, and the particle size may be 1 μm.
When m exceeds m, the transmittance of the transparent conductive film is remarkably reduced, and the transmittance at a wavelength of 550 nm is less than 50%. When a transparent touch panel was formed using this transparent conductive film, characters having a size of about 10 points on the display element behind the transparent touch panel could not be identified on the transparent touch panel. For this reason, the particle size range is set as described above. As a material for the conductive fine particles,
In addition to the ITO used in the above embodiment, SnO2, ZnO
It is also possible to use metal oxide fine particles such as those described above, or to use a transparent plastic spherical material with a conductive film formed around it. The transparent conductive film 13 prepared as described above had a thickness of 2 μm, a sheet resistance of 1 kΩ / □, and a transmittance of 75% at a wavelength of 550 nm. It is desirable that the film thickness of the transparent conductive film is as thin as possible while maintaining low resistance. In this embodiment, the thickness is set to 2.0 μm from the balance between sheet resistance and transmittance. In addition, the pattern shape and dimensions of the transparent conductive film are determined by the operation method and specifications of the transparent touch panel,
In this embodiment, the pattern width is 150 mm and the pattern interval is 0.
5 mm.
【００１２】ＰＥＴフィルムの対向電極となるガラス板
に透明導電ペーストによる透明導電膜を形成した具体例
を以下に述べる。図６に示すように、ソーダライムガラ
スのガラス板１４上に、上述した透明導電ペーストの印
刷による透明導電膜形成法により、パターン化された透
明導電膜１５を作成した。透明導電膜１５の膜厚は２．
０μｍ、シート抵抗は１ｋΩ／□でＰＥＴフィルム上の
透明導電膜１３と同じであるが、透過率がわずかに高く
波長５５０ｎｍで７８％であった。ガラス板上の透明導
電膜１５のパターンは、長手方向がＰＥＴフィルム上の
透明導電膜１３の長手方向と直交するように形成し、パ
ターン幅は１５０ｍｍ、パターン間隔は０．５ｍｍとし
た。A specific example in which a transparent conductive film made of a transparent conductive paste is formed on a glass plate serving as a counter electrode of a PET film will be described below. As shown in FIG. 6, a patterned transparent conductive film 15 was formed on a glass plate 14 of soda lime glass by the above-described method of forming a transparent conductive film by printing the transparent conductive paste. The film thickness of the transparent conductive film 15 is 2.
Although the sheet resistance was 0 μm and the sheet resistance was 1 kΩ / □, which was the same as that of the transparent conductive film 13 on the PET film, the transmittance was slightly higher and 78% at a wavelength of 550 nm. The pattern of the transparent conductive film 15 on the glass plate was formed such that the longitudinal direction was orthogonal to the longitudinal direction of the transparent conductive film 13 on the PET film, the pattern width was 150 mm, and the pattern interval was 0.5 mm.
【００１３】図７は図５の透明導電膜１３付きのＰＥＴ
フィルム１１と図６の透明導電膜１５付きガラス板１４
とを用いて作成した透明タッチパネルを示す。すなわ
ち、前記ＰＥＴフィルム１１およびガラス板１４に、透
明タッチパネルの作成に必要なＡｇ回路１６、ドットス
ペーサ１７等を印刷により形成し、両者を対向して貼り
合わせることで、４×４、計１６個のスイッチ部を持つ
マトリックス方式の透明タッチパネルを作成した。ＰＥ
Ｔフィルムを指で押して上部電極（ＰＥＴフィルムの透
明導電膜）１３と下部電極（ガラス板の透明導電膜）１
５とを接触させることでスイッチ動作の確認を行った。
その結果、すべてのスイッチ部で電気的接触を得ること
ができ、透明タッチパネルとしての動作を確認した。完
成した透明タッチパネルの波長５５０ｎｍにおける透過
率は５２％であった。FIG. 7 shows PET with the transparent conductive film 13 shown in FIG.
Film 11 and glass plate 14 with transparent conductive film 15 of FIG.
2 shows a transparent touch panel created using the above. That is, an Ag circuit 16, a dot spacer 17, and the like necessary for producing a transparent touch panel are formed on the PET film 11 and the glass plate 14 by printing, and the two are opposed to each other and bonded to each other. We have created a matrix-type transparent touch panel with a switch unit. PE
Pressing the T film with a finger, upper electrode (transparent conductive film of PET film) 13 and lower electrode (transparent conductive film of glass plate) 1
The switch operation was confirmed by contact with No. 5.
As a result, electrical contact was obtained in all the switch sections, and the operation as a transparent touch panel was confirmed. The transmittance of the completed transparent touch panel at a wavelength of 550 nm was 52%.
【００１４】本発明の透明タッチパネルの透過率を向上
させる方法について説明する。図８は下部電極１８に、
パターン化されたスパッタＩＴＯ薄膜を用いたものであ
る。この場合、波長５５０ｎｍにおける透過率が６３％
まで上昇した。A method for improving the transmittance of the transparent touch panel according to the present invention will be described. FIG. 8 shows the lower electrode 18
This uses a patterned sputtered ITO thin film. In this case, the transmittance at a wavelength of 550 nm is 63%.
Up.
【００１５】また、図９に示すように、上部電極１３と
下部電極１５の間に、例えばアクリル系樹脂等の透明レ
ジスト１９を薄く塗布しても、透過率向上に有効であ
る。この場合、両電極間の接触抵抗はやや大きくなるも
のの、作成した透明タッチパネルの透過率に上昇が認め
られた。完成した透明タッチパネルの波長５５０ｎｍで
の透過率は、図９のように下部電極１５も透明導電ペー
ストの印刷により形成されたもので５７％であった。ま
た、下部電極がスパッタ法により形成されたものでは６
８％であった。As shown in FIG. 9, even if a thin transparent resist 19 such as an acrylic resin is applied between the upper electrode 13 and the lower electrode 15, it is effective to improve the transmittance. In this case, although the contact resistance between both electrodes was slightly increased, an increase in the transmittance of the produced transparent touch panel was observed. The transmittance of the completed transparent touch panel at a wavelength of 550 nm was 57% when the lower electrode 15 was also formed by printing a transparent conductive paste as shown in FIG. In the case where the lower electrode is formed by a sputtering method, 6
8%.
【００１６】上述の実施例ではマトリックス式の透明タ
ッチパネルについて述べたが、上述の方法により、上部
または下部電極のいずれか一方を透明導電ペーストの印
刷で形成したアナログ式タッチパネルの作成も可能であ
る。In the above-described embodiment, a matrix type transparent touch panel has been described. However, an analog type touch panel in which one of the upper and lower electrodes is formed by printing a transparent conductive paste can be produced by the above-described method.
【００１７】[0017]
【発明の効果】本発明によれば、対向する２枚の透明基
板のそれぞれ向き合う面に形成される透明導電膜の少な
くとも一方を、導電性微粒子をフィラーとする透明導電
ペーストにより形成したので、従来エッチングで行って
きた透明導電膜のパターン形成を一連の印刷工程により
行うことが可能となり、製造工程が簡略化され、大幅な
作業時間短縮を達成することができた。また、材料や環
境に与える影響が懸念されるエッチング液、エッチング
ガス等の使用を極力制限できるため、従来の方法に比べ
より安全性を高めることができ、環境への影響を少なく
することができた。According to the present invention, at least one of the transparent conductive films formed on the opposing surfaces of two opposing transparent substrates is formed of a transparent conductive paste containing conductive fine particles as a filler. The pattern formation of the transparent conductive film, which has been performed by etching, can be performed by a series of printing processes, so that the manufacturing process is simplified, and a significant reduction in working time can be achieved. In addition, since the use of an etching solution, an etching gas, and the like, which are likely to affect materials and the environment, can be restricted as much as possible, the safety can be further improved as compared with the conventional method, and the effect on the environment can be reduced. Was.
【００１８】請求項３によれば、透明レジストの塗布に
より、透明タッチパネルの透過率を向上させることがで
きる。According to the third aspect, the transmittance of the transparent touch panel can be improved by applying the transparent resist.
【図１】透明タッチパネルの一般的な構造を説明するも
ので、透明タッチパネルの要部断面図である。FIG. 1 is a cross-sectional view of a main part of a transparent touch panel, for explaining a general structure of the transparent touch panel.
【図２】パターン化された透明導電膜を持つ透明タッチ
パネルの平面図である。FIG. 2 is a plan view of a transparent touch panel having a patterned transparent conductive film.
【図３】図２の構造の透明タッチパネルにおいて透明基
板に透明導電膜を形成する従来方法を説明する図で、
（イ）、（ロ）、（ハ）、（ニ）の工程順で透明導電膜
が形成される。FIG. 3 is a view for explaining a conventional method for forming a transparent conductive film on a transparent substrate in the transparent touch panel having the structure of FIG. 2;
A transparent conductive film is formed in the order of (a), (b), (c), and (d).
【図４】本発明の透明タッチパネルを製造する要領を説
明する図である。FIG. 4 is a view for explaining a point of manufacturing the transparent touch panel of the present invention.
【図５】本発明の一実施形態の透明タッチパネルにおけ
る一方の透明基板（ＰＥＴフィルム）の透明導電膜の断
面図である。FIG. 5 is a cross-sectional view of a transparent conductive film on one transparent substrate (PET film) in the transparent touch panel according to one embodiment of the present invention.
【図６】本発明の一実施形態の透明タッチパネルにおけ
る他方の透明基板（ガラス板）の透明導電膜の断面図で
ある。FIG. 6 is a cross-sectional view of a transparent conductive film on the other transparent substrate (glass plate) in the transparent touch panel according to one embodiment of the present invention.
【図７】図５の透明基板および図６の透明基板にそれぞ
れ回路等を形成した後に貼り合わせて構成した透明タッ
チパネルの平面図である。FIG. 7 is a plan view of a transparent touch panel formed by forming circuits and the like on the transparent substrate of FIG. 5 and the transparent substrate of FIG.
【図８】本発明の他の実施形態の透明タッチパネルの要
部の断面図である。FIG. 8 is a cross-sectional view of a main part of a transparent touch panel according to another embodiment of the present invention.
【図９】請求項３の透明タッチパネルの要部断面図であ
る。FIG. 9 is a sectional view of a main part of a transparent touch panel according to a third embodiment.
１、１４ 透明基板（ガラス板） ２、１１ 透明基板（可撓性透明基板・ＰＥＴフィル
ム） ３、１０、１３ 透明導電膜 ５、１７ ドットスペーサ ６、１５ パターン化された透明導電膜 ９ 刷版 １２ 導電性微粒子 １６ Ａｇ回路 １８ スパッタＩＴＯ薄膜による下部電極 １９ 透明レジスト1, 14 Transparent substrate (glass plate) 2, 11 Transparent substrate (flexible transparent substrate / PET film) 3, 10, 13 Transparent conductive film 5, 17 Dot spacer 6, 15, Patterned transparent conductive film 9 Printing plate 12 conductive fine particles 16 Ag circuit 18 lower electrode made of sputtered ITO thin film 19 transparent resist
───────────────────────────────────────────────────── フロントページの続き (72)発明者 永田 雅克 千葉県佐倉市六崎1440番地 株式会社フジ クラ佐倉事業所内 (72)発明者 水谷 宗幹 千葉県佐倉市六崎1440番地 株式会社フジ クラ佐倉事業所内 (72)発明者 遠藤 正徳 千葉県佐倉市六崎1440番地 株式会社フジ クラ佐倉事業所内 Ｆターム(参考） 5B087 AA00 CC13 CC14 CC16 CC36 ──────────────────────────────────────────────────続 き Continuing on the front page (72) Inventor Masakatsu Nagata 1440, Mukurosaki, Sakura-shi, Chiba Prefecture Inside Fujikura Sakura Office, Ltd. (72) Inventor Masanori Endo 1440 Mutsuzaki, Sakura-shi, Chiba Prefecture Fujikura Sakura Works Co., Ltd. F-term (reference) 5B087 AA00 CC13 CC14 CC16 CC36
Claims (3)
れ向き合う面に透明導電膜を形成し、前記透明導電膜同
士を接触させることでスイッチ動作を行わせる抵抗膜式
の透明タッチパネルにおいて、 少なくとも一方の透明導電膜が導電性微粒子をフィラー
とする透明導電ペーストの印刷面により形成されている
ことを特徴とする透明タッチパネル。1. A resistive transparent touch panel in which a transparent conductive film is formed on each facing surface of two transparent substrates held opposite to each other and a switching operation is performed by bringing the transparent conductive films into contact with each other. A transparent touch panel, wherein one of the transparent conductive films is formed by a printed surface of a transparent conductive paste containing conductive fine particles as a filler.
て、少なくともインジウム、錫、亜鉛のいずれかを含む
金属の酸化物微粒子であって、粒径が０．１μｍ〜１μ
ｍ以下に分岐しているものを用いたことを特徴とする請
求項１記載の透明タッチパネル。2. The conductive fine particles in the transparent conductive paste are metal oxide fine particles containing at least one of indium, tin and zinc, having a particle size of 0.1 μm to 1 μm.
2. The transparent touch panel according to claim 1, wherein the transparent touch panel is used.
ストを塗布して透明性を向上させたことを特徴とする請
求項１記載の透明タッチパネル。3. The transparent touch panel according to claim 1, wherein a transparent resist is applied to the surface of the printed conductive paste to improve transparency.