JP2001245814A - Bathroom wash place and manufacturing method thereof - Google Patents
Bathroom wash place and manufacturing method thereofInfo
- Publication number
- JP2001245814A JP2001245814A JP2000062837A JP2000062837A JP2001245814A JP 2001245814 A JP2001245814 A JP 2001245814A JP 2000062837 A JP2000062837 A JP 2000062837A JP 2000062837 A JP2000062837 A JP 2000062837A JP 2001245814 A JP2001245814 A JP 2001245814A
- Authority
- JP
- Japan
- Prior art keywords
- bathroom
- layer
- thermoplastic elastomer
- washing place
- laminated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は浴室洗い場とその製
造法に関するものである。The present invention relates to a bathroom washing place and a method for manufacturing the same.
【０００２】[0002]
【従来の技術】従来、浴室内に設置される洗い場はポリ
プロピレンなどの熱可塑性樹脂や、不飽和ポリエステル
樹脂とガラス繊維を用いた繊維強化プラスチック（以下
ＦＲＰという）や硬質磁性タイルであった。これらの洗
い場は高耐久性、高級感、重厚感あるものとするために
表面をできるだけ硬く、また高剛性化する傾向にあっ
た。2. Description of the Related Art Conventionally, washing places installed in bathrooms have been made of thermoplastic resins such as polypropylene, fiber reinforced plastics (hereinafter referred to as FRP) using unsaturated polyester resin and glass fibers, and hard magnetic tiles. These washing stations tend to have a hard surface as much as possible and high rigidity in order to provide high durability, high quality feeling, and solid feeling.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら幼児や足
腰の弱った高齢者などの場合には、不安定であり浴室洗
い場で滑ったり転倒したりして身体を強く打ち付けたり
することがある。この様な場合に、洗い場が硬くかつ剛
性の大きなものであると怪我をする危険が伴う。そこ
で、洗い場全体を軟質材で形成することが考えられる
が、このように洗い場全体を軟質材で形成すると、洗い
場自身が形状保持できなくなってしまう。However, in the case of an infant or an elderly person with weak legs, the body is unstable and may hit the body strongly by slipping or falling in the bathroom washing place. In such a case, if the washing place is hard and rigid, there is a risk of injury. Therefore, it is conceivable that the entire washing place is formed of a soft material. However, if the entire washing place is formed of a soft material, the shape of the washing place itself cannot be maintained.
【０００４】また、浴室内は高湿度であり、細菌やカビ
の増殖には最適な環境である。このことから手入れを少
しでも怠ると、特に洗い場の周辺部などには細菌やカビ
が増殖しやすく不潔になりやすい。[0004] Further, the bathroom has high humidity, which is an optimal environment for the growth of bacteria and mold. For this reason, if care is neglected even a little, bacteria and mold are likely to multiply and become dirty, especially in the periphery of the washing area.
【０００５】また、軟質の洗い場を製造し提供するに際
して、これを量産性のよいものとし、安価に洗い場を提
供できるようにすることが求められる。[0005] Further, when manufacturing and providing a soft washing place, it is required that the washing place be provided with good mass productivity and the washing place can be provided at low cost.
【０００６】[0006]
【課題を解決するための手段】本発明は上記課題を解決
するために、樹脂材料からなるバックアップ基材に対し
て、熱可塑性エラストマー層からなる軟質材を表面層と
して積層し一体化した浴室洗い場である。SUMMARY OF THE INVENTION In order to solve the above-mentioned problems, the present invention provides a bathroom washing area in which a soft material made of a thermoplastic elastomer layer is laminated as a surface layer on a backup base made of a resin material and integrated. It is.
【０００７】上記発明によれば、樹脂材料からなるバッ
クアップ基材によって浴室洗い場自体の形状が保持され
るとともに、表面層が熱可塑性エラストマー層の軟質材
料により形成されているため、たとえば幼児や高齢者な
どが洗い場で転倒してもその衝撃を軟質材料により良好
に吸収でき、安全性を向上させることができる。According to the above invention, the shape of the bathroom washing place itself is maintained by the backup base material made of the resin material, and the surface layer is formed of the soft material of the thermoplastic elastomer layer. Even if it falls down in the washing place, the impact can be better absorbed by the soft material, and the safety can be improved.
【０００８】[0008]
【発明の実施の形態】請求項１に記載の発明は、樹脂材
料からなるバックアップ基材に対して、熱可塑性エラス
トマー層からなる軟質材を表面層として積層し一体化し
たものである。DESCRIPTION OF THE PREFERRED EMBODIMENTS The first aspect of the present invention is such that a soft material made of a thermoplastic elastomer layer is laminated as a surface layer and integrated with a backup base made of a resin material.
【０００９】そして、樹脂材料からなるバックアップ基
材によって浴室洗い場自体の形状が保持されるととも
に、表面層が熱可塑性エラストマー層の軟質材料により
形成されているため、たとえば幼児や高齢者などが洗い
場で転倒してもその衝撃を軟質材料により良好に吸収で
き、安全性を向上させることができる。Further, the shape of the bathroom washing area itself is maintained by the backup base material made of the resin material, and the surface layer is formed of the soft material of the thermoplastic elastomer layer. Even if the vehicle falls, the impact can be better absorbed by the soft material, and the safety can be improved.
【００１０】また請求項２記載の発明は、樹脂材料から
なるバックアップ基材と表面層である熱可塑性エラスト
マー層との間に第二の弾性層を有する軟質材を積層し一
体化したものである。According to a second aspect of the present invention, a soft material having a second elastic layer is laminated and integrated between a backup base material made of a resin material and a thermoplastic elastomer layer as a surface layer. .
【００１１】そして、樹脂材料からなるバックアップ基
材と表面層である熱可塑性エラストマー層との間に第二
の弾性層を有する軟質材を積層し一体化することによ
り、浴室洗い場表面をより軟らかくすることができる。[0011] A soft material having a second elastic layer is laminated and integrated between a backup base material made of a resin material and a thermoplastic elastomer layer as a surface layer, thereby making the surface of the bathroom washing place softer. be able to.
【００１２】また請求項３記載の発明は、バックアップ
基材の樹脂材料がＦＲＰからなるものである。Further, in the invention according to claim 3, the resin material of the backup base material is made of FRP.
【００１３】そして、ＦＲＰは不飽和ポリエステル樹脂
などの熱硬化性樹脂とガラス繊維を混合して硬化させた
ものであり、軽くて高剛性のため、強度の大きい浴室洗
い場が可能となる。The FRP is obtained by mixing and curing a thermosetting resin such as an unsaturated polyester resin and glass fiber, and is light and has high rigidity, so that a bathroom washing place with high strength can be realized.
【００１４】また請求項４記載の発明は、塩素元素を含
まない化学構造を有する熱可塑性エラストマー層からな
る軟質材を表面層として積層し一体化したものである。According to a fourth aspect of the present invention, a soft material comprising a thermoplastic elastomer layer having a chemical structure containing no chlorine element is laminated and integrated as a surface layer.
【００１５】そして、熱可塑性エラストマー層が塩素元
素を含まないため、サーマルリサイクル時に塩化水素ガ
スやダイオキシンといった人体に悪影響を及ぼす排ガス
が生成しない。このため、環境に優しいクリーンな浴室
洗い場が可能となる。[0015] Since the thermoplastic elastomer layer does not contain chlorine element, exhaust gas such as hydrogen chloride gas and dioxin which adversely affects the human body is not generated during thermal recycling. For this reason, an environment-friendly clean bathroom washing place becomes possible.
【００１６】また請求項５記載の発明は、弾性層を発泡
層としたものである。According to a fifth aspect of the present invention, the elastic layer is a foamed layer.
【００１７】そして、このようにすれば軟質材層をより
いっそう軟らかくすることができ、安全性がさらに向上
する。[0017] By doing so, the soft material layer can be softened further, and the safety is further improved.
【００１８】また請求項６記載の発明は、熱可塑性エラ
ストマー層が抗菌剤を含有するものである。According to a sixth aspect of the present invention, the thermoplastic elastomer layer contains an antibacterial agent.
【００１９】また請求項７記載の発明は、熱可塑性エラ
ストマー層が無機系抗菌剤の少なくとも一種、および有
機系抗菌剤の少なくとも一種を含有するものである。According to a seventh aspect of the present invention, the thermoplastic elastomer layer contains at least one inorganic antibacterial agent and at least one organic antibacterial agent.
【００２０】そして、無機系抗菌剤の作用により主とし
て細菌の増殖を抑制し、さらには細菌の増殖に起因する
悪臭の発生、酵母の増殖に起因するぬめりの発生も抑制
する。また、有機系抗菌剤の作用により主としてカビの
増殖を抑制する。このように、カビ、細菌などの増殖を
抑制し、健康的で清潔な浴室洗い場が可能となる。The action of the inorganic antibacterial agent mainly suppresses the growth of bacteria, and further suppresses the generation of offensive odors caused by the growth of bacteria and the generation of slimming caused by the growth of yeast. In addition, the action of the organic antibacterial agent mainly suppresses the growth of mold. In this way, the growth of mold, bacteria and the like is suppressed, and a healthy and clean bathroom washing place becomes possible.
【００２１】また請求項８記載の発明は、樹脂材料から
なるバックアップ基材に対して、軟質材を表面層として
積層し一体化した浴室洗い場において、軟質材からなる
表面層は真空成形によりバックアップ基材と積層一体化
されてなる浴室洗い場の製造法である。The invention according to claim 8 is characterized in that, in a bathroom washing area where a soft material is laminated as a surface layer and integrated with a backup base material made of a resin material, the surface layer made of the soft material is backed up by vacuum forming. This is a method of manufacturing a bathroom washing area that is laminated and integrated with materials.
【００２２】そして、軟質材からなる表面層を真空成形
によりバックアップ基材と積層一体化することにより浴
室洗い場を簡単に安価に製造することができる。The surface layer made of a soft material is laminated and integrated with the backup substrate by vacuum forming, so that a bathroom washing place can be easily and inexpensively manufactured.
【００２３】[0023]
【実施例】（実施例１）以下本発明の実施例について説
明する。(Embodiment 1) An embodiment of the present invention will be described below.
【００２４】尚、本発明におけるバックアップ基体の樹
脂材料としては、熱可塑性樹脂としてポリエチレン、ポ
リプロピレン、アクリロニトリル・ブタジエン・スチレ
ン共重合物などが挙げられるが、これに限定するもので
はない。また、熱硬化性樹脂としてフェノール樹脂、尿
素樹脂、メラミン樹脂、ウレタン樹脂、不飽和ポリエス
テル樹脂、エポキシ樹脂、熱硬化性アクリル樹脂などが
挙げられるが、これに限定するものではない。また、Ｆ
ＲＰ用樹脂としては上記熱硬化性樹脂が使用可能であ
り、成形法としてはハンドレイアップ成形法、ホットプ
レス成形法、注型法、レジントランスファーモールデイ
ング法などを用いることが可能である。The resin material for the backup substrate in the present invention includes, but is not limited to, thermoplastic resins such as polyethylene, polypropylene, and acrylonitrile-butadiene-styrene copolymer. Examples of the thermosetting resin include a phenol resin, a urea resin, a melamine resin, a urethane resin, an unsaturated polyester resin, an epoxy resin, and a thermosetting acrylic resin, but are not limited thereto. Also, F
The above-mentioned thermosetting resin can be used as the resin for RP, and as a molding method, a hand lay-up molding method, a hot press molding method, a casting method, a resin transfer molding method, or the like can be used.
【００２５】また、熱可塑性エラストマーとしては、ス
チレン系、オレフィン系、ウレタン系、エステル系、ア
ミド系、塩化ビニル系などが挙げられるが、これに限定
するものではない。The thermoplastic elastomer includes, but is not limited to, styrene, olefin, urethane, ester, amide, and vinyl chloride.
【００２６】また、発泡層としては、ポリエチレン、ポ
リプロピレン、ポリスチレン、ポリウレタンなどが挙げ
られるが、これに限定するものではない。Examples of the foamed layer include, but are not limited to, polyethylene, polypropylene, polystyrene, and polyurethane.
【００２７】また、本発明における抗菌剤としては、無
機系抗菌剤として、硝酸銀、硫酸銀、塩化銀など。銀、
銅、亜鉛あるいは錫を担持したゼオライト。および銀、
銅、亜鉛あるいは錫を担持したシリカゲルなどが挙げら
れるが、これに限定するものではない。The antibacterial agent of the present invention includes silver nitrate, silver sulfate, silver chloride and the like as inorganic antibacterial agents. Silver,
Zeolite supporting copper, zinc or tin. And silver,
Examples include, but are not limited to, silica gel supporting copper, zinc or tin.
【００２８】また、有機系抗菌剤としては、１０，１
０’−オキシビスフェノキサアルシンなどフェニルエー
テル誘導体、シクロフルアニドなどＮ−ハロアルキルチ
オ系化合物、２−（４−チアゾリル）ベンズイミダゾー
ル（以下ＴＢＺと略称する）等イミダゾール誘導体、
２，３，５，６テトラクロル−４−（メチルスルホリ
ル）ピリジンなど第４級アンモニウム塩などが挙げられ
るが、これに限定するものではない。Further, as an organic antibacterial agent, 10,1
Phenyl ether derivatives such as 0′-oxybisphenoxaarsine, N-haloalkylthio compounds such as cyclofluanid, imidazole derivatives such as 2- (4-thiazolyl) benzimidazole (hereinafter abbreviated as TBZ),
Examples include, but are not limited to, quaternary ammonium salts such as 2,3,5,6 tetrachloro-4- (methylsulfolyl) pyridine.
【００２９】そして、ハンドレイアップ成形法により、
不飽和ポリエステル樹脂を用いたＦＲＰによりバックア
ップ基材を作成した。表層として１mm厚のポリオレフィ
ン系熱可塑性エラストマーと１０mm厚のポリウレタン発
泡層とを用い、真空成形によりバックアップ基材と積層
一体化し目的とする浴室洗い場を得た。Then, by a hand lay-up molding method,
A backup substrate was prepared by FRP using an unsaturated polyester resin. A 1 mm-thick polyolefin-based thermoplastic elastomer and a 10 mm-thick polyurethane foam layer were used as a surface layer, and were laminated and integrated with a backup substrate by vacuum molding to obtain a desired bathroom washing place.
【００３０】（実施例２）ハンドレイアップ成形法によ
り、不飽和ポリエステル樹脂を用いたＦＲＰによりバッ
クアップ基材を作成した。表層として１．５mm厚のポリ
オレフィン系熱可塑性エラストマーを用い、真空成形に
よりバックアップ基材と積層一体化し目的とする浴室洗
い場を得た。Example 2 A backup base material was prepared by FRP using an unsaturated polyester resin by a hand lay-up molding method. A 1.5 mm-thick polyolefin-based thermoplastic elastomer was used as a surface layer, which was laminated and integrated with a backup substrate by vacuum molding to obtain a desired bathroom washing place.
【００３１】（実施例３）ハンドレイアップ成形法によ
り、不飽和ポリエステル樹脂を用いたＦＲＰによりバッ
クアップ基材を作成した。表層として、ゼオライト銀系
抗菌剤を０．５％および有機系抗菌剤であるＴＢＺを
０．５％分散させた１．５mm厚のポリオレフィン系熱可
塑性エラストマーと１５mm厚のポリウレタン発泡層とを
用い、真空成形によりバックアップ基材と積層一体化し
目的とする浴室洗い場を得た。Example 3 A backup base material was prepared by FRP using an unsaturated polyester resin by a hand lay-up molding method. As a surface layer, a 1.5 mm-thick polyolefin-based thermoplastic elastomer in which 0.5% of a zeolite silver-based antibacterial agent and 0.5% of TBZ which is an organic antibacterial agent are dispersed, and a 15-mm-thick polyurethane foam layer are used. The backing substrate was laminated and integrated by vacuum forming to obtain the desired bathroom washing place.
【００３２】図１は本発明の一実施例における浴室洗い
場を示す模式図である。１は洗い場であり、２は浴槽で
ある。この洗い場１は、図１の部分拡大断面図に示して
いるようにＦＲＰに代表されるバックアップ基材３とポ
リウレタンに代表される発泡層４と熱可塑性エラストマ
ー層５と、熱可塑性エラストマー層中に分散されている
ゼオライト銀に代表される無機系抗菌剤６とＴＢＺに代
表される有機系抗菌剤７で構成されている。FIG. 1 is a schematic diagram showing a bathroom washing place in one embodiment of the present invention. 1 is a washing place and 2 is a bathtub. As shown in the partially enlarged cross-sectional view of FIG. 1, the washing place 1 includes a backup base material 3 typified by FRP, a foamed layer 4 typified by polyurethane, a thermoplastic elastomer layer 5, and a thermoplastic elastomer layer. It is composed of a dispersed inorganic antibacterial agent 6 represented by silver zeolite and an organic antibacterial agent 7 represented by TBZ.
【００３３】各実施例で得た洗い場の抗菌性能およびカ
ビ抵抗性について試験を行った。前記洗い場から５０mm
×５０mmの試料を切りだしそれぞれに菌液（黄色ブドウ
球菌および大腸菌）１ｃｃを滴下し、３７℃で２４時間
培養した。その後、滅菌済みリン酸緩衝液にて菌を洗い
出した。この洗い出した液中の生菌数を、菌数測定用培
地を用いて混釈平板法にて測定した。その結果を（表
１）に示す。A test was conducted on the antibacterial performance and the mold resistance of the washing place obtained in each of the examples. 50mm from the washing area
A sample of × 50 mm was cut out, and 1 cc of a bacterial solution (Staphylococcus aureus and Escherichia coli) was dropped on each of the samples, and cultured at 37 ° C. for 24 hours. Thereafter, the bacteria were washed out with a sterilized phosphate buffer. The viable cell count in the washed-out liquid was measured by a pour plate method using a cell count medium. The results are shown in (Table 1).
【００３４】[0034]
【表１】 [Table 1]
【００３５】寒天培地上においた各試料（５０mm×５０
mm）にアスペルギルス・ニガー菌液を噴霧し、２５℃で
７日間培養した。その結果を（表２）に示す。Each sample (50 mm × 50) on an agar medium
mm) was sprayed with Aspergillus niger bacterial solution and cultured at 25 ° C. for 7 days. The results are shown in (Table 2).
【００３６】[0036]
【表２】 [Table 2]
【００３７】（表１）から明らかなように、実施例３の
洗い場は実施例１および２の洗い場に比較し、黄色ブド
ウ球菌および大腸菌に対する著しい抗菌効果を得ること
ができた。As is clear from Table 1, the washing place of Example 3 was able to obtain a remarkable antibacterial effect on Staphylococcus aureus and Escherichia coli as compared with the washing places of Examples 1 and 2.
【００３８】（表２）から明らかなように、実施例３の
洗い場は実施例１および２の洗い場に比較し、良好な抗
カビ効果を得ることができた。As is clear from Table 2, the washing place of Example 3 was able to obtain a better antifungal effect than the washing places of Examples 1 and 2.
【００３９】[0039]
【発明の効果】以上のように、本発明の浴室洗い場とそ
の製造法によれば、次の効果が得られる。As described above, according to the bathroom washing place and the method of manufacturing the same according to the present invention, the following effects can be obtained.
【００４０】請求項１記載の発明によれば、樹脂材料か
らなるバックアップ基材に対して、熱可塑性エラストマ
ー層からなる軟質材を表面層として積層し一体化した浴
室洗い場とすることにより、樹脂材料からなるバックア
ップ基材によって浴室洗い場自体の形状が保持されると
ともに、表面層が熱可塑性エラストマー層の軟質材料に
より形成されているため、たとえば幼児や高齢者などが
洗い場で転倒してもその衝撃を軟質材料により良好に吸
収でき、安全性を向上させることができる。According to the first aspect of the present invention, the resin material is formed by laminating a soft material made of a thermoplastic elastomer layer as a surface layer on a backup base material made of a resin material and integrating them. The shape of the bathroom washing area itself is maintained by the backup base material, and the surface layer is formed of a soft material of the thermoplastic elastomer layer. It can be absorbed better by the soft material, and the safety can be improved.
【００４１】また、請求項２記載の発明によれば、樹脂
材料からなるバックアップ基材と表面層である熱可塑性
エラストマー層との間に第二の弾性層を有する軟質材を
積層し一体化した浴室洗い場とすることにより、浴室洗
い場表面をよりいっそう軟らかくすることができる。According to the second aspect of the present invention, a soft material having a second elastic layer is laminated and integrated between a backup base material made of a resin material and a thermoplastic elastomer layer as a surface layer. By providing a bathroom washing place, the surface of the bathroom washing place can be made even softer.
【００４２】また、請求項３記載の発明によれば、バッ
クアップ基材の樹脂材料がＦＲＰからなる浴室洗い場と
することにより、不飽和ポリエステル樹脂などの熱硬化
生樹脂とガラス繊維を混合分散して加熱硬化させたＦＲ
Ｐは軽くて高剛性のため、強度の大きい浴室洗い場を得
ることができる。According to the third aspect of the present invention, the resin material of the backup base material is a bathroom washing place made of FRP, so that a thermosetting raw resin such as an unsaturated polyester resin and glass fiber are mixed and dispersed. Heat cured FR
Since P is light and has high rigidity, a strong bathroom washing place can be obtained.
【００４３】また、請求項４記載の発明によれば、塩素
元素を含まない化学構造を有する熱可塑性エラストマー
層からなる軟質材を表面層として積層し一体化した浴室
洗い場とすることにより、サーマルリサイクル時に塩化
水素ガスやダイオキシンといった人体に悪影響を及ぼす
は燃焼排ガスが生成しない、環境に優しいクリーンな浴
室洗い場を得ることができる。According to the fourth aspect of the present invention, a bathroom washing place is formed by laminating and integrating a soft material comprising a thermoplastic elastomer layer having a chemical structure containing no chlorine element as a surface layer, thereby providing thermal recycling. It is possible to obtain a clean bathroom that is environmentally friendly and does not generate combustion exhaust gas, which sometimes has an adverse effect on the human body such as hydrogen chloride gas and dioxin.
【００４４】また、請求項５記載の発明によれば、弾性
層が発泡層である浴室洗い場とすることにより、軟質材
層をよりいっそう軟らかくすることができ、安全性およ
び快適性がさらに向上する。According to the fifth aspect of the present invention, the soft material layer can be further softened by providing a bathroom washing place where the elastic layer is a foamed layer, and safety and comfort are further improved. .
【００４５】また、請求項６記載の発明によれば、熱可
塑性エラストマー層が抗菌剤を含有する浴室洗い場とす
ることにより、ならびに、請求項７記載の発明によれ
ば、熱可塑性エラストマー層が無機系抗菌剤の少なくと
も一種、および有機系抗菌剤の少なくとも一種を含有す
る浴室洗い場とすることにより、無機系抗菌剤の作用に
より主として細菌の増殖を抑制し、さらには細菌の増殖
に起因する悪臭の発生、酵母の増殖に起因するぬめりの
発生も抑制する。また、有機系抗菌剤の作用により、主
としてカビの増殖を抑制する。このようにカビ、細菌な
どの増殖を抑制し、健康的で清潔な浴室洗い場を得るこ
とができる。According to the sixth aspect of the present invention, the thermoplastic elastomer layer is a bathroom washing place containing an antibacterial agent, and according to the seventh aspect of the present invention, the thermoplastic elastomer layer is made of an inorganic material. At least one type of antimicrobial agent and at least one type of organic antimicrobial agent in the bathroom wash area, the action of the inorganic antimicrobial agent mainly suppresses the growth of bacteria, and furthermore the odor caused by the growth of bacteria It also suppresses the occurrence of slime caused by the occurrence and growth of yeast. In addition, the action of the organic antibacterial agent mainly suppresses the growth of mold. Thus, growth of mold, bacteria, etc. can be suppressed, and a healthy and clean bathroom washing place can be obtained.
【００４６】また、請求項８記載の発明のように、樹脂
材料からなるバックアップ基材に対して、軟質材を表面
層として積層し一体化した浴室洗い場において、軟質材
からなる表面層は真空成形によりバックアップ基材と積
層一体化により浴室洗い場を製造することにより、より
簡単に、安価に浴室洗い場を得ることができる。Further, in a bathroom washing place where a soft material is laminated as a surface layer and integrated with a backup base material made of a resin material, the surface layer made of the soft material is vacuum formed. By manufacturing a bathroom washing place by laminating and integrating the backup base material, a bathroom washing place can be obtained more easily and inexpensively.
【図１】本発明の一実施例における浴室洗い場の模式図FIG. 1 is a schematic view of a bathroom washing place in one embodiment of the present invention.
【符号の説明】 １ 洗い場 ３ バックアップ基材 ４ 発泡層 ５ 熱可塑性エラストマー層 ６ 無機系抗菌剤 ７ 有機系抗菌剤[Description of Signs] 1 Washing place 3 Backup base material 4 Foam layer 5 Thermoplastic elastomer layer 6 Inorganic antibacterial agent 7 Organic antibacterial agent
───────────────────────────────────────────────────── フロントページの続き (72)発明者 今坂 喜信 大阪府門真市大字門真1006番地 松下電器 産業株式会社内 (72)発明者 ▲よし▼田 博明 大阪府門真市大字門真1006番地 松下電器 産業株式会社内 Ｆターム(参考） 2D032 GA00 4C058 AA23 BB07 JJ03 JJ07 JJ08 4C094 BA25 GG11 GG16 ──────────────────────────────────────────────────の Continued on the front page (72) Yoshinobu Imasaka, 1006 Kadoma Kadoma, Kadoma, Osaka Prefecture Inside Matsushita Electric Industrial Co., Ltd. (72) Inventor Company F term (reference) 2D032 GA00 4C058 AA23 BB07 JJ03 JJ07 JJ08 4C094 BA25 GG11 GG16
Claims (8)
て、熱可塑性エラストマー層からなる軟質材を表面層と
して積層し一体化した浴室洗い場。1. A bathroom washing area in which a soft material made of a thermoplastic elastomer layer is laminated as a surface layer on a backup base made of a resin material and integrated therewith.
層である熱可塑性エラストマー層との間に第二の弾性層
を有する軟質材を積層し一体化した浴室洗い場。2. A bathroom washing area in which a soft material having a second elastic layer is laminated and integrated between a backup base material made of a resin material and a thermoplastic elastomer layer as a surface layer.
からなる請求項１または２記載の浴室洗い場。3. The bathroom washing place according to claim 1, wherein the resin material is a backup base material which is FRP.
ない化学構造を有する請求項１ないし３のいずれか１項
記載の浴室洗い場。4. The bathroom washing place according to claim 1, wherein the thermoplastic elastomer layer has a chemical structure containing no chlorine element.
洗い場。5. The bathroom according to claim 2, wherein the elastic layer is a foam layer.
ることを特長とする請求項１ないし４のいずれか１項記
載の浴室洗い場。6. The bathroom washing place according to claim 1, wherein the thermoplastic elastomer layer contains an antibacterial agent.
種、および有機系抗菌剤の少なくとも一種からなる請求
項６記載の浴室洗い場。7. The bathroom washing area according to claim 6, wherein the antibacterial agent comprises at least one of inorganic antibacterial agents and at least one of organic antibacterial agents.
て、軟質材を表面層として積層し一体化した浴室洗い場
において、軟質材からなる表面層は真空成形によりバッ
クアップ基材と積層一体化されてなる浴室洗い場の製造
法。8. In a bathroom washroom where a soft material is laminated as a surface layer and integrated with a backup substrate made of a resin material, the surface layer made of the soft material is laminated and integrated with the backup substrate by vacuum forming. A method of manufacturing a bathroom washroom.