JPH0884691A - Warm-water washing seat - Google Patents
Warm-water washing seatInfo
- Publication number
- JPH0884691A JPH0884691A JP22469494A JP22469494A JPH0884691A JP H0884691 A JPH0884691 A JP H0884691A JP 22469494 A JP22469494 A JP 22469494A JP 22469494 A JP22469494 A JP 22469494A JP H0884691 A JPH0884691 A JP H0884691A
- Authority
- JP
- Japan
- Prior art keywords
- toilet seat
- water washing
- warm
- polypropylene resin
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は家庭用に広く用いられて
いる便座暖房機能、温水洗浄機能を有する温水洗浄便座
に関するものである。特に、清潔でクリーンでしかも耐
薬品性に優れた温水洗浄便座で便座シート、便蓋および
本体ケースなどに使用される樹脂材料に関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a warm water washing toilet seat having a toilet seat heating function and a hot water washing function which are widely used for home use. In particular, the present invention relates to a resin material used for a toilet seat sheet, a toilet lid, a main body case and the like in a warm water washing toilet seat that is clean and has excellent chemical resistance.
【０００２】[0002]
【従来の技術】従来の温水洗浄便座について、図１およ
び図２を用いて説明する。１は便座シート、２は温水を
吐出し局部を洗浄する洗浄ノズル、３は温水洗浄装置の
本体ケース、４は温水洗浄、乾燥機能を操作する操作
部、５は温水吐出を入切する洗浄スイッチ、６は便器、
７は便蓋である。便座シート１、本体ケース３や便蓋７
はアクリロニトリル・ブタジエン・スチレン共重合体樹
脂（以下ＡＢＳと云う）の成形品で主に構成されてい
る。便座シート１にはヒータが内蔵され、約３５から４
０℃に加熱保温され、冬寒いときには暖かく快適であ
る。使用するときは、便座シート１の上にお尻を当てて
座って使用する。大便あるいは、女性が小便を終えれば
洗浄スイッチ５を押して、洗浄ノズル２から温水を噴出
させて局部を洗浄する。また、男性が小便をするとき
は、便座シートを上げた状態で、便器６の中をめがけて
使用する。2. Description of the Related Art A conventional warm water washing toilet seat will be described with reference to FIGS. 1 is a toilet seat sheet, 2 is a cleaning nozzle for discharging hot water to wash a local part, 3 is a main body case of a hot water cleaning device, 4 is an operating unit for operating a hot water cleaning and drying function, and 5 is a cleaning switch for turning on / off the hot water discharge , 6 is a toilet bowl,
7 is a toilet lid. Toilet seat 1, body case 3 and toilet lid 7
Is mainly composed of a molded product of acrylonitrile / butadiene / styrene copolymer resin (hereinafter referred to as ABS). Toilet seat 1 has a built-in heater, about 35 to 4
It is heated and kept at 0 ℃, and it is warm and comfortable in the cold winter. When using, sit on the toilet seat 1 with your butt against it. When urine or a woman finishes urine, the cleaning switch 5 is pressed to eject hot water from the cleaning nozzle 2 to clean the local area. Further, when a man urinates, he uses it while aiming inside the toilet bowl 6 with the toilet seat seat raised.
【０００３】温水洗浄便座部材は皮膚に直接接する部分
が多く、その衛生面には配慮が払われ、多くの工夫が実
用化されてきた。最近では殺菌剤を含浸させた払拭布
や、無機系抗菌剤を分散させたＡＢＳで形成された便座
シートなどが一部使用されている。Many hot water washing toilet seat members are in direct contact with the skin, and due attention has been paid to their hygiene, many ideas have been put to practical use. Recently, a wiping cloth impregnated with a germicide, a toilet seat sheet made of ABS in which an inorganic antibacterial agent is dispersed, and the like have been partially used.
【０００４】また便器６の構造材料としては陶磁器が主
体であるため種々の界面活性剤あるいは酸などを主体と
した洗浄剤が広く使用されている。As the structural material of the toilet bowl 6, since ceramics are the main constituent, various detergents or cleaning agents mainly containing acids are widely used.
【０００５】[0005]
【発明が解決しようとする課題】しかしながら上記従来
の構成では使用するときに、大便であれば、便器内に落
下した大便が便器内に溜まった水を跳ね返し、便座シー
ト１の裏板に汚物の小片が付着したりする。また、便座
シート１を上げて小便をするときは、便座シート１の裏
板や本体ケース３の前面部に小便がかかったりする。ま
た、使用時にお尻の当たる便座シート１の表面、および
手で開閉を行う便蓋７についても、皮膚の汚れあるいは
皮膚常在菌などが付着し汚染される。日常これらの操作
が繰り返されると、汚れの増大や、雑菌、かびが増殖
し、非常に不衛生である。However, when used in the above-mentioned conventional structure, if the stool is stool, the stool that has fallen into the toilet repels the water accumulated in the toilet and the back plate of the toilet seat 1 is cleaned of dirt. Small pieces may adhere. Further, when the toilet seat 1 is raised to make a urine, the back plate of the toilet seat 1 or the front part of the body case 3 may be urinated. In addition, the surface of the toilet seat sheet 1 that touches the hips when used, and the toilet lid 7 that is opened and closed by hand are also contaminated by dirt on the skin or skin-resident bacteria. If these operations are repeated every day, stains increase, bacteria and mold grow, and it is very unsanitary.
【０００６】便座シート、便蓋および本体ケースなどの
構成材料であるＡＢＳは比較的その表面エネルギーが大
きく、その結果、汚染され易くしかも汚れが強固に付着
するため汚染物の除去がしにくいという欠点を有してい
る。そこで、これらの汚染物を除去するため種々の界面
活性剤入りの協力洗浄剤で温水洗浄便座表面を清掃する
ことが通常行われる。しかし、ＡＢＳは耐薬品性が悪
く、特に界面活性剤には浸されやすく、清掃時に拭き残
された界面活性剤により、また、完全に拭き取ったとし
ても清掃時の界面活性剤の短時間の接触が繰り返される
ことにより、便座シート、便蓋および本体ケースなどに
ソルベントクラックの発生、あるいは曲げ強度の大幅な
劣化を招き、使用に耐えられなくなる場合が生じるとい
う問題があった。そのために、温水洗浄便座専用の洗浄
剤が販売されているが、界面活性剤の量が少なく洗浄能
力に劣るためほとんど利用されていないのが現状であ
る。また、これらの専用洗浄剤でも長時間使用するとソ
ルベントクラックの発生あるいは曲げ強度の大幅な劣化
の原因となる。ABS, which is a constituent material for toilet seat sheets, toilet lids, body cases, etc., has a relatively large surface energy, and as a result, it is easy to be contaminated and stains adhere firmly, so that it is difficult to remove contaminants. have. Therefore, in order to remove these contaminants, it is usual to clean the surface of the toilet seat with warm water wash with a co-cleaning agent containing various surfactants. However, ABS has poor chemical resistance and is particularly apt to be dipped in a surfactant, and the surfactant is left uncleaned during cleaning, and even if it is completely wiped off, the surfactant does not come in contact for a short time during cleaning. By repeating the above, there is a problem that solvent cracks may occur in the toilet seat sheet, the toilet lid, the main body case, or the like, or the bending strength may be significantly deteriorated, and the product may not be usable. For that reason, a cleaning agent for hot-water washing toilet seats is on the market, but is rarely used because the amount of the surfactant is small and the cleaning ability is poor. Further, even if these special cleaning agents are used for a long time, they may cause solvent cracks or significantly deteriorate bending strength.
【０００７】なお、便器洗浄時、高濃度の界面活性剤入
り洗浄剤や、塩酸添加型洗浄剤の飛沫が便座シートなど
に付着し、ソルベントクラック発生の原因となったりし
た。[0007] During cleaning of the toilet bowl, a high-concentration detergent-containing detergent or a spray of a hydrochloric acid-added detergent adheres to the toilet seat sheet, causing solvent cracks.
【０００８】無機系抗菌剤を分散させたＡＢＳで形成し
た便座シートにおいては、マトリックス樹脂が非晶性の
ＡＢＳであり抗菌剤が便座シートに配向しにくいため、
抗菌効果に乏しくしかも防黴効果もほとんど期待できな
いという問題があった。界面活性剤などによるソルベン
トクラックあるいは曲げ強度劣化という問題は前述と同
様である。In a toilet seat sheet formed of ABS in which an inorganic antibacterial agent is dispersed, since the matrix resin is amorphous ABS and the antibacterial agent is difficult to be oriented in the toilet seat sheet,
There was a problem that the antibacterial effect was poor and the antifungal effect could hardly be expected. The problem of solvent cracking or bending strength deterioration due to a surfactant or the like is the same as described above.
【０００９】また、通常の一般ポリプロピレンは高結晶
性ポリプロピレンに比べ機械強度や表面硬度が劣悪であ
り便座シート、便蓋、本体ケースの使用には適さない。Further, ordinary general polypropylene is inferior in mechanical strength and surface hardness to highly crystalline polypropylene and is not suitable for use as a toilet seat sheet, a toilet lid, or a main body case.
【００１０】本発明は上記問題を解決するもので、汚れ
がつきにくく、除去し易い、また清掃時、界面活性剤等
の洗浄剤を使用してもソルベントクラックなどを発生せ
ず、また、大便や、小便の飛び散りなどによる雑菌や黴
の増殖を効果的に防止し、衛生的で、しかも高性能な温
水洗浄便座を提供することを目的としたものである。The present invention solves the above-mentioned problems, and it is easy to remove stains and is easy to remove. Even when a cleaning agent such as a surfactant is used at the time of cleaning, solvent cracks do not occur, and it is convenient. Another object of the present invention is to provide a sanitary and high-performance hot water washing toilet seat that effectively prevents the growth of bacteria and mold caused by stool scattering.
【００１１】[0011]
【課題を解決するための手段】本発明は上記目的を達成
するため、温水洗浄便座の便座シート、便蓋および本体
ケースの構成材料のうち少なくとも一部材が高結晶性ポ
リプロピレン樹脂、あるいは高結晶性ポリプロピレン樹
脂と弾性体からなる樹脂体で形成されたものである。In order to achieve the above object, the present invention has at least one of the constituent materials of the toilet seat sheet, toilet lid and body case of the hot water washing toilet seat made of a highly crystalline polypropylene resin or a highly crystalline material. It is formed of a resin body composed of a polypropylene resin and an elastic body.
【００１２】また、便座シート、便蓋および本体ケース
のうちの構成材料のうち少なくとも一部材が、抗菌剤を
分散した高結晶性ポリプロピレン樹脂、あるいは高結晶
性ポリプロピレン樹脂と弾性体とからなる樹脂体に抗菌
剤を分散して形成されたものである。Further, at least one member of the constituent materials of the toilet seat sheet, the toilet lid and the main body case is a highly crystalline polypropylene resin in which an antibacterial agent is dispersed, or a resin body composed of a highly crystalline polypropylene resin and an elastic body. It is formed by dispersing an antibacterial agent.
【００１３】[0013]
【作用】本発明は上記構成の高結晶性ポリプロピレン樹
脂の低表面エネルギー効果により、汚れがつきにくく、
しかも除去し易く、便座シート、便蓋および本体ケース
などの表面のクリーン性を保有する事が容易となる。ま
た、汚れがつきにくい為、汚れを栄養源として成長する
雑菌や黴の増殖も穏やかになり、クリーン性も改善され
る。The present invention has a low surface energy effect of the highly crystalline polypropylene resin having the above-mentioned structure, and thus is less likely to become dirty.
Moreover, it is easy to remove, and it becomes easy to maintain the cleanliness of the surfaces of the toilet seat sheet, the toilet lid, the body case, and the like. In addition, since dirt does not easily adhere, the growth of bacteria and mold that grow using dirt as a nutrient source is moderated, and cleanliness is improved.
【００１４】なお、長期間繰り返しの使用などにより清
掃が必要になった場合でも、高結晶性ポリプロピレン樹
脂の高耐薬品性能により界面活性剤と接触しても侵され
ることがないため、洗浄能力に優れた効力洗浄剤を使用
することができ清掃のスピードアップが可能である。し
かも洗浄剤によるソルベントクラックあるいは曲げ強度
劣化の心配も不要である。Even when cleaning is required due to repeated use over a long period of time, the highly crystalline polypropylene resin does not corrode even if it comes into contact with a surfactant due to its high chemical resistance. An excellent cleaning agent can be used to speed up cleaning. Moreover, there is no need to worry about solvent cracks or bending strength deterioration due to the cleaning agent.
【００１５】また、高結晶性ポリプロピレン樹脂と弾性
体とからなる構成の場合は、弾性体が抗結晶性ポリプロ
ピレン樹脂の粒子の間に入り込み、接着剤の役割をはた
すことになり、衝撃強度が向上し実使用上の特性が大幅
に改善される。Further, in the case of the constitution composed of the highly crystalline polypropylene resin and the elastic body, the elastic body penetrates between the particles of the anti-crystalline polypropylene resin and serves as an adhesive, so that the impact strength is improved. The characteristics in actual use are greatly improved.
【００１６】また、高結晶性ポリプロピレン樹脂中に抗
菌剤を分散した構成においては、抗菌剤の作用により便
座シート、便蓋および本体ケースなどの表面に付着した
汚物を栄養源として成長する雑菌や黴の増殖を防止す
る。なお、高結晶性ポリプロピレン樹脂の特徴として、
抗菌剤と親和性があまり良好ではなく、両者を分散した
場合均一に分散せず、樹脂成形体の表面により濃厚に抗
菌剤が分布する傾向にある。このため、より少量の抗菌
剤で効果的な抗菌作用を現出することが可能となる。Further, in the constitution in which the antibacterial agent is dispersed in the highly crystalline polypropylene resin, various bacteria and molds which grow by the action of the antibacterial agent as a nutrient source are the dirt attached to the surfaces of the toilet seat sheet, the toilet lid and the body case. Prevent the growth of. As a characteristic of the high crystalline polypropylene resin,
The affinity with the antibacterial agent is not so good, and when both are dispersed, the antibacterial agent tends not to be uniformly dispersed, and the antibacterial agent is more densely distributed on the surface of the resin molded body. Therefore, it becomes possible to exhibit an effective antibacterial action with a smaller amount of the antibacterial agent.
【００１７】[0017]
【実施例】以下本発明を実施例により詳細に説明する。EXAMPLES The present invention will be described in detail below with reference to examples.
【００１８】図１は本発明の温水洗浄便座を示す。１は
便座シート、２は温水を吐出し局部を洗浄する洗浄ノズ
ル、３は温水洗浄装置の本体ケースで、いずれも抗菌剤
の含有された高結晶性ポリプロピレン樹脂と弾性体成分
とからなる樹脂体で形成されている。FIG. 1 shows a warm water washing toilet seat of the present invention. Reference numeral 1 is a toilet seat sheet, 2 is a cleaning nozzle for discharging hot water to wash a local part, 3 is a main body case of a hot water cleaning device, and each is a resin body composed of a highly crystalline polypropylene resin containing an antibacterial agent and an elastic body component. Is formed by.
【００１９】本発明に於ける高結晶性ポリプロピレン樹
脂としては結晶化度６５％以上で、立体規則性度が９７
％以上のものがあげられる。特に立体規則性度９８％以
上のものは、その表面硬度が極めてたかく、傷つきにく
く良好である。なお、比較例で使用した一般ポリプロピ
レンの結晶化度は６０％である。The highly crystalline polypropylene resin used in the present invention has a crystallinity of 65% or more and a stereoregularity of 97.
% Or more can be given. Particularly, those having a stereoregularity of 98% or more have extremely high surface hardness and are not easily scratched and are good. The crystallinity of the general polypropylene used in the comparative example is 60%.
【００２０】本発明における弾性体成分としては、ポリ
エチレン、エチレン−プロピレンゴム、アクリル酸エス
テル共重合体、塩素化ポリエチレン、エチレンビニルア
セテート共重合他、ポリブタジエン、天然ゴム、イソプ
レンゴム、ブタジエンゴム、クロロプレンゴム、アクリ
ロニトリル−ブタジエンゴム、ブチルゴム、アクリルゴ
ム、シリコーンゴム、ウレタンゴムなどがあげられる。
また弾性体成分の配合割合は、高結晶性ポリプロピレン
樹脂１００重量部当たり５〜１５重量部が良好であるが
それにこだわるものではない。As the elastic component in the present invention, polyethylene, ethylene-propylene rubber, acrylic ester copolymer, chlorinated polyethylene, ethylene vinyl acetate copolymer, etc., polybutadiene, natural rubber, isoprene rubber, butadiene rubber, chloroprene rubber , Acrylonitrile-butadiene rubber, butyl rubber, acrylic rubber, silicone rubber, urethane rubber and the like.
Further, the compounding ratio of the elastic material component is preferably 5 to 15 parts by weight per 100 parts by weight of the highly crystalline polypropylene resin, but it is not limited thereto.
【００２１】本発明における抗菌剤としては、無機系抗
菌剤として、硝酸銀、硫酸銀、塩化銀など。銀、銅、亜
鉛あるいは錫を担持したゼオライト。および銀、銅、亜
鉛あるいは錫を担持したシリカゲルなどがあげられる。
抗菌剤の配合割合は、無機系抗菌剤については、樹脂１
００重量部に対し、０．１重量部未満では抗菌性が認め
られず、５重量部を超えると着色など樹脂組成物の特性
を著しく損なうので不適である。このましくは、０．５
から３重量部の範囲とするのがよい。The antibacterial agents in the present invention include inorganic antibacterial agents such as silver nitrate, silver sulfate and silver chloride. Zeolite supporting silver, copper, zinc or tin. And silica gel supporting silver, copper, zinc or tin.
The mixing ratio of the antibacterial agent is resin 1 for the inorganic antibacterial agent.
When the amount is less than 0.1 parts by weight, the antibacterial property is not recognized, and when the amount exceeds 5 parts by weight, the properties of the resin composition such as coloring are significantly impaired. This is 0.5
To 3 parts by weight is preferable.
【００２２】有機系抗菌剤として、１０、１０’−オキ
シビスフェノキサアルシンなどフェニルエーテル誘導
体、シクロフルアニドなどＮ−ハロアルキルチオ系化合
物、２−（４−チアゾリル）ベンズイミダゾール（ＴＢ
Ｚと略称）などイミダゾール誘導体、２、３、５、６デ
トラコロル−４−（メチルスルホニル）ピリジンなどス
ルホン誘導体およびセシルジメチルエチルアンモニウム
ブロミドなど第４級アンモニウム塩などがあげられる
が、これに限定するものではない。有機系抗菌剤につい
ては、樹脂１００重量部に対して、０．０２重量部未満
では防黴性はほとんど認められず、５重量部を超えると
ブルームするなど不具合がある。好ましくは０．０５か
ら１重量部の範囲とするのがよい。As organic antibacterial agents, phenyl ether derivatives such as 10,10'-oxybisphenoxaarsine, N-haloalkylthio compounds such as cyclofluanid, 2- (4-thiazolyl) benzimidazole (TB
Z) and other imidazole derivatives, 2,3,5,6 sulfone derivatives such as detracolol-4- (methylsulfonyl) pyridine, and quaternary ammonium salts such as ceryldimethylethylammonium bromide, but are not limited thereto. is not. With respect to the organic antibacterial agent, if it is less than 0.02 parts by weight with respect to 100 parts by weight of the resin, almost no antifungal property is recognized, and if it exceeds 5 parts by weight, there is a problem such as blooming. It is preferably in the range of 0.05 to 1 part by weight.
【００２３】具体的実施例を以下に説明する。 （実施例１）高結晶性ポリプロピレン樹脂（結晶化度６
５％、立体規則性度９８％）を用いて射出成形法により
便座シート、便蓋、本体ケースを成形し温水洗浄便座を
作成した。A concrete example will be described below. (Example 1) Highly crystalline polypropylene resin (crystallinity 6
5%, stereoregularity 98%), a toilet seat sheet, a toilet lid, and a main body case were molded by an injection molding method to prepare a warm water-washing toilet seat.
【００２４】（実施例２）高結晶性ポリプロピレン樹脂
（結晶化度６５％、立体規則性度９８％）１００重量
部、エチレンプロピレンゴム１０重量部をよく混合した
樹脂体を用いて射出成形法により、便座シート、便蓋、
本体ケースを成形し温水洗浄便座を作成した。Example 2 100% by weight of a highly crystalline polypropylene resin (65% crystallinity, 98% stereoregularity) and 10 parts by weight of ethylene propylene rubber were mixed well, and an injection molding method was used. , Toilet seat, toilet lid,
The body case was molded to prepare a warm water washing toilet seat.
【００２５】（実施例３）高結晶性ポリプロピレン樹脂
（結晶化度６５％、立体規則性度９８％）１００重量
部、ＴＢＺ０．０５重量部、銀ゼオライト０．７５重量
部をよく混合し、射出成形法により便座シート、便座シ
ート、便蓋、本体ケースを成形し温水洗浄便座を作成し
た。Example 3 100 parts by weight of a highly crystalline polypropylene resin (crystallinity 65%, stereoregularity 98%), TBZ 0.05 part by weight, and silver zeolite 0.75 part by weight were mixed well and injected. A toilet seat sheet, a toilet seat sheet, a toilet lid, and a body case were molded by a molding method to prepare a warm water washing toilet seat.
【００２６】（比較例１）ＡＢＳを用いて射出成形法に
より便座シート、便座シート、便蓋、本体ケースを成形
し温水洗浄便座を作成した。(Comparative Example 1) A toilet seat sheet, a toilet seat sheet, a toilet lid, and a body case were molded using ABS by an injection molding method to prepare a warm water washing toilet seat.
【００２７】（比較例２）ＡＢＳ１００重量部、ＴＢＺ
０．０５重量部、銀ゼオライト０．７５重量部をよく混
合し、射出成形法により便座シート、便座シート、便
蓋、本体ケースを成形し温水洗浄便座を作成した。(Comparative Example 2) ABS 100 parts by weight, TBZ
0.05 part by weight and 0.75 part by weight of silver zeolite were mixed well, and a toilet seat sheet, a toilet seat sheet, a toilet lid, and a main body case were molded by an injection molding method to prepare a warm water washing toilet seat.
【００２８】（比較例３）一般ポリプロピレン（結晶化
度６０％）を用い、射出成形法により便座シート、便
蓋、本体ケースを成形し温水洗浄便座を作成した。(Comparative Example 3) Using a general polypropylene (crystallinity 60%), a toilet seat sheet, a toilet lid and a body case were molded by an injection molding method to prepare a warm water washed toilet seat.
【００２９】各実施例および比較例で成形した便蓋の水
に対する接触角を、協和界面化学製の接触角測定装置
（ＣＡ−Ｚ型）で測定した。また、各々の便蓋の耐汚染
性をＪＩＳ Ｋ３３７０に準じて確認した。なお、耐汚
染性能の比較は目視で行い、比較例１における汚れ具合
を（△）とし、それより悪い場合（×）、よい場合を
（○）とし各々相対評価した。その結果を（表１）に示
す。The contact angle of the toilet lids molded in each of the examples and comparative examples with water was measured with a contact angle measuring device (CA-Z type) manufactured by Kyowa Interface Science. Moreover, the stain resistance of each toilet lid was confirmed according to JIS K3370. In addition, the comparison of the stain resistance performance was performed by visual observation, and the degree of stain in Comparative Example 1 was set as (Δ), and when it was worse (x) and when it was better (◯), relative evaluation was performed. The results are shown in (Table 1).
【００３０】[0030]
【表１】 [Table 1]
【００３１】次に、実施例１〜３および比較例１〜３で
成形した便蓋の抗菌性能および黴抵抗性について試験を
行った。各便蓋から５０×５０mmの試料を切り出し、そ
れぞれに菌液（一般細菌および大腸菌）１ccを滴下し、
３７℃で２４時間培養した。その後、滅菌済みリン酸緩
衝液にて菌を洗い出した。この洗い出した液中の生菌数
を、菌数測定用培地を用いて混釈平板法にて測定した。
その結果を（表２）に示す。Next, the toilet lids molded in Examples 1 to 3 and Comparative Examples 1 to 3 were tested for antibacterial performance and mold resistance. Cut 50 x 50 mm sample from each toilet lid, drop 1 cc of bacterial solution (general bacteria and E. coli) on each,
The cells were cultured at 37 ° C for 24 hours. Then, the bacteria were washed out with a sterilized phosphate buffer solution. The viable cell count in the washed-out solution was measured by the pour plate method using a cell count measuring medium.
The results are shown in (Table 2).
【００３２】[0032]
【表２】 [Table 2]
【００３３】寒天培地上においた各試料（５０×５０m
m）にアスペルギルス・ニガー菌液を噴霧し、２５℃、
７日間培養した。その結果を（表３）に示す。Each sample placed on the agar medium (50 × 50 m
m) sprayed with Aspergillus niger bacterium solution,
Cultured for 7 days. The results are shown in (Table 3).
【００３４】[0034]
【表３】 [Table 3]
【００３５】次に、各実施例および比較例で成形した便
蓋の耐溶剤性能について試験を行った。各便蓋から４０
×１００mmの試料を切り出し、各試料の中央部に１０kg
重量の力を加え、歪を加えた状態で洗浄剤（ファミリー
フレッシュ：商品名）に１０日間浸漬しソルベントクラ
ック発生の有無を調べた。Next, the solvent resistance performance of the toilet lids molded in each of the examples and comparative examples was tested. 40 from each toilet lid
Cut out a sample of × 100mm and put 10kg in the center of each sample.
The product was immersed in a detergent (Family Fresh: trade name) for 10 days in a strained state by applying a force of weight and examined for the occurrence of solvent cracks.
【００３６】その結果を（表４）に示す。×はクラック
発生、○は変化なし（クラック発生なし）である。The results are shown in (Table 4). X indicates cracking, ◯ indicates no change (no cracking).
【００３７】[0037]
【表４】 [Table 4]
【００３８】また同時に曲げ強度の変化を調べた。その
結果を（表５）に示す。At the same time, the change in bending strength was examined. The results are shown in (Table 5).
【００３９】[0039]
【表５】 [Table 5]
【００４０】次に、各実施例および比較例で成形した便
蓋の表面硬度をＪＩＳ Ｋ７２１５に基づきゴム硬度計
（Ｄ型）で測定した。その結果を（表６）に示す。Next, the surface hardness of the toilet lid molded in each of the examples and comparative examples was measured by a rubber hardness meter (D type) based on JIS K7215. The results are shown in (Table 6).
【００４１】[0041]
【表６】 [Table 6]
【００４２】次に、実施例１、２出成形した便蓋の衝撃
強度を測定した。１kgの重さの球を用いた落球試験法に
より試験を行った。試験環境は２３℃、０℃、−１０℃
の三環境で、１０cmから１００cmまで１０cm間隔で球を
落下させ、われの発生した高さで評価を行った。その結
果を（表７）に示す。Next, the impact strength of the toilet lid molded in Examples 1 and 2 was measured. The test was performed by the falling ball test method using a ball weighing 1 kg. Test environment 23 ℃, 0 ℃, -10 ℃
Spheres were dropped at 10 cm intervals from 10 cm to 100 cm in the three environments, and the height at which cracks occurred was evaluated. The results are shown in (Table 7).
【００４３】[0043]
【表７】 [Table 7]
【００４４】なお、上記実施例および比較例の成形品は
便蓋であったが、便座あるいは本体ケースでも同様な結
果が得られる。Although the molded articles of the above Examples and Comparative Examples were toilet lids, similar results can be obtained with a toilet seat or body case.
【００４５】[0045]
【発明の効果】以上説明したように本発明の温水洗浄便
座によれば次の効果が得られる。As described above, according to the warm water washing toilet seat of the present invention, the following effects can be obtained.
【００４６】（１）便座シート、便蓋および本体ケース
の少なくとも一部に高結晶性ポリプロピレン樹脂を用い
ることにより、耐薬品生が向上し、強力な洗浄剤を使用
してもソルベントクラックが発生せず、曲げ強度劣化の
問題も発生しない。(1) By using a highly crystalline polypropylene resin for at least a part of the toilet seat sheet, the toilet lid and the body case, the chemical resistance is improved and solvent cracks are not generated even when a strong cleaning agent is used. In addition, the problem of bending strength deterioration does not occur.
【００４７】また、低表面エネルギー効果により、汚れ
がつきにくくしかも除去し易く衛生的である。また、表
面硬度が大きく傷がつきにくい。Also, due to the low surface energy effect, dirt is less likely to adhere and is easy to remove, which is hygienic. Also, the surface hardness is large and scratches are unlikely to occur.
【００４８】（２）高結晶性ポリプロピレン樹脂と弾性
体成分とからなる樹脂耐を用いることにより、耐衝撃性
能が向上し、より良好な温水洗浄便座を作成することが
できる。(2) By using a resin resistance consisting of a highly crystalline polypropylene resin and an elastic material component, impact resistance is improved and a better warm water washing toilet seat can be prepared.
【００４９】（３）抗菌剤が高結晶性ポリプロピレン樹
脂に不均一に分散される（樹脂成形体の表面により高濃
度に分散される）ことにより、ＡＢＳに比べ効果的な抗
菌、抗黴効果が期待でき、雑菌や黴の繁殖を防止し、使
用者はいつも衛生的な使用感が得られると同時に、病気
の感染も防止することができる。(3) Since the antibacterial agent is non-uniformly dispersed in the highly crystalline polypropylene resin (dispersed in a higher concentration on the surface of the resin molding), the antibacterial and antifungal effects more effective than ABS are obtained. As expected, it prevents the propagation of various bacteria and mold, and the user can always get a hygienic feeling, and at the same time, prevent the infection of diseases.
【図１】本発明の一実施例を示す温水洗浄便座の外観図FIG. 1 is an external view of a warm water washing toilet seat showing an embodiment of the present invention.
【図２】従来の使用時の外観図[Figure 2] External view of conventional use
【符号の説明】 １ 便座シート ２ 洗浄ノズル ３ 本体ケース ４ 操作部 ５ 洗浄スイッチ ６ 便器 ７ 便蓋[Explanation of symbols] 1 toilet seat 2 cleaning nozzle 3 main body case 4 operation unit 5 cleaning switch 6 toilet 7 toilet cover
Claims (6)
材料のうちの少なくとも一部材が高結晶性ポリプロピレ
ン樹脂で形成された温水洗浄便座。1. A warm water washing toilet seat in which at least one member of the constituent materials of the toilet seat sheet, the toilet lid and the main body case is formed of a highly crystalline polypropylene resin.
材料のうちの少なくとも一部材が高結晶性ポリプロピレ
ン樹脂と弾性体成分とからなる樹脂体で形成された温水
洗浄便座。2. A warm water washing toilet seat in which at least one member of constituent materials of a toilet seat sheet, a toilet lid and a main body case is formed of a resin body composed of a highly crystalline polypropylene resin and an elastic body component.
度が９８％以上であることを特徴とする請求項１または
２記載の温水洗浄便座。3. The hot water washing toilet seat according to claim 1, wherein the highly crystalline polypropylene resin has a stereoregularity of 98% or more.
レン−プロピレンゴムの少なくとも一種からなることを
特徴とする請求項２記載の温水洗浄便座。4. The warm water washing toilet seat according to claim 2, wherein the elastic component is made of at least one of polyethylene resin and ethylene-propylene rubber.
部材のうちの少なくとも一部材に抗菌剤が分散されてい
ることを特徴とする請求項１または２記載の温水洗浄便
座。5. The warm water washing toilet seat according to claim 1, wherein an antibacterial agent is dispersed in at least one of the constituent members of the toilet seat sheet, the toilet lid and the main body case.
種、および有機系抗菌剤の少なくとも一種とからなるこ
とを特徴とする請求項５記載の温水洗浄便座。6. The warm water washing toilet seat according to claim 5, wherein the antibacterial agent comprises at least one inorganic antibacterial agent and at least one organic antibacterial agent.