JP2000302568A - Cement hardened body - Google Patents

Abstract

PROBLEM TO BE SOLVED: To make it possible to produce a cement hardened body with a relative simple process and improve its strength while utilizing an organic waste material by mixing a pulverized material of the organic waste material and water and then carbonating and curing the mixture. SOLUTION: This cement hardened body having a specific gravity of 1.0 to 1.8 is obtained by mixing 1 to 30 vol.%, especially 5 to 25 vol.% of a pulverized material of an organic waste material having particle sixes of 0.001 to 2 mm, especially 0.001 to 0.5 mm and a specific gravity of <=1.5 and the cement, then mixing the mixture of the organic waste material and the cement with 5 to 70 parts by weight, especially 30 to 40 parts by weight of water to obtain a mixture, after heating the mixture to a temp. of the room temp. to 300 deg.C, especially a temp. of >=50 deg.C and carbonating and curing the heat-treated mixture by introducing carbon dioxide in the form of liquid, gas or super critical state or the like under a pressure of 1 to 200 kg/cm2, especially >=5 kg/cm2 for a time of <=24 h, especially <=1 h. Thereby, it is possible to effectively use the organic waste material which is difficult to be recycled and may generate dioxins or the like when it is treated as the waste material.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、特に、プラスチッ
クリサイクル利用と共に、プラスチックを混入したセメ
ント硬化体のリサイクル利用を図った、炭酸化処理され
たセメント硬化体に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a carbonized hardened cement material, which is intended for recycling plastics and hardening a hardened cementitious material mixed with plastics.

【０００２】[0002]

【従来の技術】従来より、不要となったプラスチック系
廃棄物を粉砕して、セメント等の固化剤に混入し再利用
することが行われているが、得られる硬化体の強度は十
分満足できるものではなかった。例えば、特開平06-321
601 号公報には、セメントにプラスチック粉末と骨材を
添加してセメント硬化体を得ることが開示されている。
しかしながら、この方法では、得られる硬化体の耐衝撃
性能は向上するものの、一般に、プラスチックはセメン
トに対する親和性が低いことから、土木建材部材等ある
程度の強度を要求される部位に対しては、使用が困難で
あった。2. Description of the Related Art Conventionally, plastic wastes that are no longer needed have been pulverized, mixed with a solidifying agent such as cement, and reused. However, the strength of the obtained cured product is sufficiently satisfactory. It was not something. For example, JP-A-06-321
Japanese Patent Application No. 601 discloses that a cement hardened body is obtained by adding plastic powder and aggregate to cement.
However, in this method, although the impact resistance of the obtained cured product is improved, generally, plastics have low affinity for cement, so that they are used for parts requiring a certain level of strength such as civil engineering construction materials. Was difficult.

【０００３】また、特開平04-114978 号公報では、セメ
ントにプラスチック粉末を混入してセメント硬化体を得
た後、該プラスチックを溶融温度以上に熱処理して、セ
メント凝結物及び骨材に融着させ、強度及び耐久性の向
上を図る方法が開示されている。この方法によれば、確
かに得られるセメント硬化体の諸物性は向上するもの
の、使用するプラスチックによっては、その溶融温度が
高いためにその高温処理によってセメント水和物質が分
解されるおそれがあり、更に、温度、処理時間如何によ
っては、多大なエネルギーがかかることとなり、工業生
産上好ましくないものであった。In Japanese Patent Application Laid-Open No. 04-114978, after a cement powder is mixed with cement to obtain a hardened cement body, the plastic is heat-treated to a melting temperature or higher to be fused to cement aggregate and aggregate. A method for improving strength and durability is disclosed. According to this method, although various physical properties of the obtained cement hardened body are certainly improved, depending on the plastic used, there is a possibility that the cement hydrated substance is decomposed by the high temperature treatment due to its high melting temperature, Furthermore, a large amount of energy is required depending on the temperature and the processing time, which is not preferable for industrial production.

【０００４】[0004]

【発明が解決しようとする課題】本発明は、上記従来の
プラスチックを用いたセメント硬化体の問題点に鑑み、
従来技術に比して、有機系廃材を利用しながら、比較的
簡便に製造が可能でかつ強度が十分に保持されているセ
メント硬化体を提供することを目的とする。SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned problems of the above-mentioned conventional cement hardened body using plastic,
It is an object of the present invention to provide a hardened cement body that can be manufactured relatively easily and has sufficient strength while using an organic waste material as compared with the related art.

【０００５】[0005]

【課題を解決するための手段】上記目的を達成するため
に、請求項１記載の本発明は、有機系廃材粉砕物とセメ
ントと水とが混合された後に炭酸化処理と共に硬化され
てなるセメント硬化体を提供する。また、請求項２記載
の本発明は、有機系廃材粉砕物が、プラスチック粉砕
物、セメント及び水から得られた硬化体の粉砕物である
ことを特徴とする請求項１記載のセメント硬化体を提供
する。In order to achieve the above object, the present invention according to claim 1 is directed to a cement obtained by mixing a pulverized organic waste material, cement and water, followed by carbonation and curing. Provide a cured body. According to a second aspect of the present invention, the pulverized organic waste material is a pulverized product of a hardened product obtained from a plastic pulverized product, cement and water. provide.

【０００６】また、請求項３記載の本発明は、有機系廃
材粉砕物の粒径が0.001mm 〜10mmの範囲にある請求項１
記載のセメント硬化体を提供する。また、請求項４記載
の本発明は、プラスチックが塩化ビニル重合体である請
求項１記載のセメント硬化体を提供する。以下、本発明
について更に詳細に説明する。According to a third aspect of the present invention, the particle size of the crushed organic waste material is in the range of 0.001 mm to 10 mm.
A cured cement according to any one of the preceding claims. According to a fourth aspect of the present invention, there is provided the cured cement according to the first aspect, wherein the plastic is a vinyl chloride polymer. Hereinafter, the present invention will be described in more detail.

【０００７】本発明における有機系廃材粉砕物として
は、木片、パルプ、各種繊維からなる廃材等の木質系有
機材料や塩化ビニル重合体、ポリプロピレン、ポリエチ
レン、ポリスチレン、ポリエチレンテレフタレート等の
プラスチックの廃材等の有機系材料の廃材の粉砕物が挙
げられる。プラスチックの廃材とは、使用済のプラスチ
ック製品に限らず、成形時のバリ、ランナー等の不要物
等も含まれる。又、請求項２記載の如く、プラスチック
粉砕物をセメント及び水に混入して水和硬化させて得ら
れたセメント硬化体の粉砕物の使用は、廃プラスチック
又はセメント硬化体のリサイクルを図る観点から、より
好ましい。The pulverized organic waste materials in the present invention include woody organic materials such as wood chips, pulp and various fibers, and plastic waste materials such as vinyl chloride polymer, polypropylene, polyethylene, polystyrene and polyethylene terephthalate. Pulverized waste materials of organic materials can be used. The plastic waste material is not limited to used plastic products, but also includes unnecessary materials such as burrs and runners during molding. Further, as described in claim 2, the use of a crushed cement hardened material obtained by mixing a crushed plastic material with cement and water and hydrating and hardening the same is intended for recycling waste plastic or hardened cement material. Is more preferable.

【０００８】通常、セメント硬化体の比重が1.0 〜1.8
であることから、有機系材料としては、比重が1.5 以下
のものを使用することが好ましい。また、プラスチック
においては、難リサイクル性及び廃棄物処理時における
ダイオキシン発生等の点から、廃塩化ビニル重合体（塩
化ビニルの単独重合体もしくは共重合体）を使用するこ
とが環境対策上好ましい。[0008] Usually, the specific gravity of the hardened cement is 1.0 to 1.8.
Therefore, it is preferable to use an organic material having a specific gravity of 1.5 or less. Further, in the case of plastics, it is preferable in terms of environmental measures to use a waste vinyl chloride polymer (a homopolymer or a copolymer of vinyl chloride) from the viewpoints of difficulty in recycling and generation of dioxin during waste treatment.

【０００９】本発明におけるセメントとは、カルシウム
シリケート系セメント又はカルシウムアルミネート系セ
メントであれば特に限定されず使用することができる。
上記カルシウムシリケート系セメント又はカルシウムア
ルミネート系セメントとしては、例えば、普通ポルトラ
ンドセメント、中庸ポルトランドセメント、早強ポルト
ランドセメント、ジェットセメント、アルミナセメン
ト、白色ポルトランドセメント等のセメント、更には、
高炉セメント、シリカセメント、フライアッシュセメン
ト等の、水が共存するとポルトランドセメントと反応し
硬化性を発現する物質をポルトランドセメントに混合し
た混合セメントが挙げられる。尚、上記セメントには、
珪砂・川砂等のセメントモルタル用骨材；炭酸カルシウ
ム・珪藻土等の無機充填材等が添加されていても構わな
い。The cement in the present invention can be used without particular limitation as long as it is a calcium silicate cement or a calcium aluminate cement.
As the calcium silicate-based cement or calcium aluminate-based cement, for example, ordinary Portland cement, medium Portland cement, early strength Portland cement, jet cement, alumina cement, cement such as white Portland cement, further,
Blend cement, such as blast furnace cement, silica cement, and fly ash cement, is obtained by mixing a material that reacts with portland cement when water coexists and develops curability into portland cement. In addition, in the above cement,
Aggregates for cement mortar such as silica sand and river sand; inorganic fillers such as calcium carbonate and diatomaceous earth may be added.

【００１０】上記有機系材料の粉砕方法は、衝撃式粉砕
機、ハンマーミル、ロータリカッターの使用、冷凍後の
粉砕等、特に限定されないが、粉砕はより細かく行った
方が炭酸処理後に得られるセメント硬化体の強度発現性
の点で好ましい。The method of pulverizing the organic material is not particularly limited, such as use of an impact-type pulverizer, a hammer mill, a rotary cutter, and pulverization after freezing, but the finer the pulverization, the better the cement obtained after carbonation. It is preferable in view of the strength development of the cured product.

【００１１】有機系廃材粉砕物の粒径は、有機系材料粉
砕物そのものである場合も、有機系材料粉砕物をセメン
ト及び水に混入して水和硬化させて得られたセメント硬
化体の粉砕物である場合も、0.001mm 〜10mmの範囲内に
あることが好ましい。粒径が0.001 mm未満の場合は、粉
砕に多大なエネルギーと時間を要し、工業的に安定な入
手が困難である。一方、粒径が10mmを超えた場合は、得
られるセメント硬化体の強度発現が不十分である。より
好ましい粒径は、0.001mm 〜2mm であり、更に好ましく
は0.001mm 〜0.5mm である。The particle size of the pulverized organic waste material, whether it is the pulverized organic material itself, is obtained by mixing the pulverized organic material into cement and water and hydrating and hardening the cement-hardened material. If it is an object, it is preferable that it is in the range of 0.001 mm to 10 mm. When the particle size is less than 0.001 mm, crushing requires a lot of energy and time, and it is difficult to obtain industrially stable. On the other hand, when the particle size exceeds 10 mm, the strength of the obtained cement hardened body is insufficiently exhibited. A more preferred particle size is from 0.001 mm to 2 mm, and even more preferably from 0.001 mm to 0.5 mm.

【００１２】有機系廃材粉砕物の混入量は、有機系材料
粉砕物そのものである場合も、有機系材料粉砕物をセメ
ント及び水に混入して水和硬化させて得られたセメント
硬化体の粉砕物である場合も、セメント硬化体中に占め
る体積比で１％〜３０％であることが好ましい。１％未
満では、セメント硬化体中に殆んどプラスチックが混入
されていないこととなり、廃プラスチック等の有機系材
料の再利用という観点から好ましくない。一方、4 ０％
を超えた場合は、得られるセメント硬化体の強度発現が
不十分である。[0012] The amount of the pulverized organic waste material mixed with the pulverized organic material may be the pulverization of the hardened cementitious material obtained by mixing the pulverized organic material into cement and water and hydrating and hardening the same. It is preferable that the volume ratio is 1% to 30% in the hardened cement body. If it is less than 1%, hardly any plastic is mixed in the hardened cement, which is not preferable from the viewpoint of recycling organic materials such as waste plastic. On the other hand, 40%
When the value exceeds the above, the strength development of the obtained cement hardened body is insufficient.

【００１３】より具体的には、好ましい体積比は、用い
るプラスチックの粒径によって異なり、特に粒径のより
小さいプラスチックを用いた場合には、混練水の増加は
否めず、結果として著しい強度低下を招く結果となる。
従って、例えば、粒径が0.001mm 〜0.5mm のプラスチッ
クを用いた場合には、好ましい体積比は、５％〜２５％
であり、粒径が0.5mm 〜2mm のプラスチックを用いた場
合には、５％〜２０％であり、粒径が2mm 〜10mmのプラ
スチックを用いた場合には、５％〜15％である。More specifically, the preferable volume ratio depends on the particle size of the plastic used. Particularly, when a plastic having a small particle size is used, an increase in kneading water cannot be denied, and as a result, a remarkable decrease in strength occurs. Results.
Therefore, for example, when a plastic having a particle size of 0.001 mm to 0.5 mm is used, a preferable volume ratio is 5% to 25%.
When plastic having a particle size of 0.5 mm to 2 mm is used, the content is 5% to 20%, and when plastic having a particle size of 2 mm to 10 mm is used, the content is 5% to 15%.

【００１４】これは、セメント中のプラスチックの偏析
性に関係しており、粒径の細かいプラスチックを用いた
場合には、粒径の大きいプラスチックを用いた場合より
も、得られたセメント硬化体中のプラスチックの分散性
が高く、結果として高い強度発現性が得られることによ
る。This is related to the segregation property of the plastic in the cement. When a plastic having a small particle size is used, the obtained cement hardened material is more sized than when a plastic having a large particle size is used. This is because the dispersibility of the plastic is high, and as a result, high strength development is obtained.

【００１５】炭酸化処理における処理体には、上記有機
系廃材粉砕物と上記セメントと水とを混合した直後のも
の又は養生させて得られた硬化体が用いられる。このと
きの水の量は、有機系廃材粉砕物とセメントとの混合粉
体に対して、5 〜70重量部であることが好ましい。5 重
量部未満又は70重量部を超えると、後述する炭酸化処理
において、セメント等を中心とした混合物と二酸化炭素
との反応が十分に進行しなくなるおそれがあるためであ
る。炭酸化処理後の硬化体の十分な強度発現を考慮に入
れた場合、より好ましくは30〜40重量部である。養生時
間は特に限定されないが、二酸化炭素との反応活性を考
慮に入れた場合短い方が好ましい。As the treated body in the carbonation treatment, the one immediately after mixing the above-mentioned pulverized organic waste material, the above-mentioned cement and water, or a cured body obtained by curing is used. The amount of water at this time is preferably 5 to 70 parts by weight based on the mixed powder of the pulverized organic waste material and cement. If the amount is less than 5 parts by weight or exceeds 70 parts by weight, the reaction between carbon dioxide and a mixture mainly composed of cement or the like may not sufficiently proceed in the carbonation treatment described below. When sufficient strength development of the cured product after the carbonation treatment is taken into account, the amount is more preferably 30 to 40 parts by weight. The curing time is not particularly limited, but a shorter one is preferable in consideration of the reaction activity with carbon dioxide.

【００１６】本発明における炭酸化処理とは、セメント
の硬化過程においてアルカリ成分、特にカルシウム成分
が炭酸化される処理をいい、具体的には、加温加圧条件
下で二酸化炭素を反応させる方法が採用される。上記炭
酸処理における加温温度としては、室温〜300 ℃の範囲
内であれば特に制限されず、より好ましくは50℃以上で
ある。加温温度は、高温になるほど炭酸化反応が速くな
るため好ましいが、用いられる有機系廃材及び添加物に
含まれる有機系物質等の劣化が起こらない範囲の温度を
選択する必要がある。上記炭酸処理における加圧圧力と
しては、1 〜200kg/cm2 が好ましく、内部への炭酸化の
進行を促進したり、短時間で炭酸化するためには、5kg/
cm2 以上の加圧圧力がより好ましい。[0016] The carbonation treatment in the present invention refers to a treatment in which an alkali component, particularly a calcium component, is carbonated in the hardening process of cement, and specifically, a method of reacting carbon dioxide under heating and pressurizing conditions. Is adopted. The heating temperature in the carbonic acid treatment is not particularly limited as long as it is in the range of room temperature to 300 ° C, and is more preferably 50 ° C or more. The heating temperature is preferably higher as the temperature is higher, since the carbonation reaction is faster. However, it is necessary to select a temperature within a range that does not cause deterioration of the organic waste materials used and the organic substances contained in the additives. The pressurization pressure in the carbonation treatment is preferably 1 to 200 kg / cm2, and 5 kg / cm2 is required to promote the progress of carbonation into the inside or to perform carbonation in a short time.
A pressurization pressure of cm2 or more is more preferable.

【００１７】上記炭酸処理に用いられる二酸化炭素とし
ては、例えば、液体、気体、超臨界状態等の二酸化炭素
が挙げられる。上記炭酸処理の処理時間としては、セメ
ントや有機系廃材の種類、それらの混合比率等によって
異なるが、通常は24時間以内が好ましく、より好ましく
は１時間以内である。上記処理時間内で炭酸化反応が十
分に進行するような条件で処理した場合、処理時間を更
に長くしても問題はないが、それ以上の効果が得られな
いので非効率的である。また、より穏やかな条件で長時
間反応させた場合は処理効率が低下するばかりでなく、
強度発現の効果が十分に得られないことがある。The carbon dioxide used in the above carbonation treatment includes, for example, liquid, gas, and supercritical carbon dioxide. The treatment time of the carbonation treatment varies depending on the types of cement and organic waste materials, their mixing ratio, and the like, but is usually preferably 24 hours or less, more preferably 1 hour or less. If the treatment is carried out under such conditions that the carbonation reaction proceeds sufficiently within the above treatment time, there is no problem even if the treatment time is further increased, but no further effect is obtained, which is inefficient. In addition, when the reaction is performed for a long time under milder conditions, not only does the processing efficiency decrease,
In some cases, the effect of strength development may not be sufficiently obtained.

【００１８】上記炭酸処理を具体的に行う場合は、例え
ば、有機系廃材粉砕物とセメントとを所定比率で混合し
たものに水を所定量添加して混練後、所定時間養生して
セメント成形体を得て、この処理体を耐熱・耐圧試験機
に入れ、内部に二酸化炭素を所定圧力まで導入し、所定
の温度まで昇温させて所定時間炭酸化反応させる方法が
採用される。When the carbonation treatment is specifically performed, for example, a predetermined amount of water is added to a mixture of a crushed organic waste material and cement at a predetermined ratio, kneaded, kneaded, and cured for a predetermined time to form a cement molded product. Then, the treated body is put into a heat and pressure resistance tester, carbon dioxide is introduced thereinto to a predetermined pressure, the temperature is raised to a predetermined temperature, and a carbonation reaction is performed for a predetermined time.

【００１９】（作用）本発明のセメント硬化体は、有機
系廃材粉砕物が混入されていると共に炭酸化処理されて
いるので、従来の珪石等を充填剤として用いたセメント
硬化体と比較して、通常、骨材に比べてセメントとの親
和性が低いプラスチック等の有機系廃材粉砕物が混入さ
れても、同程度以上の強度を発現し得るのである。(Function) Since the hardened cement of the present invention contains a pulverized organic waste material and has been subjected to a carbonation treatment, the hardened cement of the present invention can be compared with a conventional hardened cement using silica or the like as a filler. Usually, even if a pulverized organic waste material such as plastic having a lower affinity for cement than the aggregate is mixed, the same strength or more can be exhibited.

【００２０】また、有機系廃材粉砕物が、プラスチック
粉砕物、セメント及び水から得られた硬化体の粉砕物で
ある場合は、粉砕が比較的困難な軟プラスチック又は難
形状のプラスチック等であっても、一旦セメントで硬化
させることにより、粉砕が容易となり、更に単にプラス
チックをそのまま充填材として使用する場合よりも、セ
メントとの親和性の高い充填材として使用できて、有機
系廃材のリサイクルが促進されると共にセメント硬化体
を廉価に提供することが可能となる。In the case where the pulverized organic waste material is a pulverized plastic, or a pulverized hardened material obtained from cement and water, the pulverized product is a soft plastic or a plastic having a difficult shape which is relatively difficult to pulverize. However, once hardened with cement, it becomes easier to grind, and can be used as a filler with a higher affinity for cement than when plastic is used as it is as it is, promoting the recycling of organic waste materials. In addition, it becomes possible to provide a hardened cement at low cost.

【００２１】また、有機系廃材粉砕物の粒径が強度発現
に好適な0.001mm 〜10mmの範囲にある場合は、十分な強
度を発現したセメント硬化体を提供し得る。更に、プラ
スチックが塩化ビニル重合体である場合は、塩化ビニル
重合体の難リサイクル性及び廃棄物処理時におけるダイ
オキシン発生等の恐れがある難処理性物質を積極的に利
用することが可能であるため、廃棄物処理技術としての
展開が図れ、環境対策に対する貢献度が高い。When the particle size of the pulverized organic waste material is in the range of 0.001 mm to 10 mm, which is suitable for developing the strength, it is possible to provide a hardened cement body having sufficient strength. Furthermore, when the plastic is a vinyl chloride polymer, it is possible to positively use the difficult-to-recycle substances that may cause the difficulty of recycling of the vinyl chloride polymer and the generation of dioxin during waste disposal. It can be developed as a waste treatment technology and has a high contribution to environmental measures.

【００２２】[0022]

【実施例】以下に実施例を挙げて本発明を更に詳しく説
明するが、本発明はこれら実施例のみに限定されるもの
ではない。 （実施例１〜5 ）表１に示した様に、ポルトランドセメ
ントと、プラスチック粉砕物及び水から一旦セメント硬
化体を得てそれを粉砕して得た粉砕物１〜３、並びにそ
の他の粉砕物４〜６を用いて、普通ポルトランドセメン
トと水とを表２に示すような配合で混合・混練後、表２
に示すような養生条件更には炭酸処理条件で炭酸化処理
することにより、150mm ×50mm×20mmのダンベル状セメ
ント硬化体を得た。セメント硬化体中に占める粉砕物の
割合（体積％）は、表２に示す通りであった。これらの
セメント硬化体の曲げ強度と比重を、後述の方法で測定
し、その結果を比較例と併せて表２に示した。EXAMPLES The present invention will be described in more detail with reference to the following examples, but the present invention is not limited to these examples. (Examples 1 to 5) As shown in Table 1, once cement hardened body was obtained from Portland cement, crushed plastic and water, and crushed to obtain crushed materials 1 to 3, and other crushed materials. After mixing and kneading the ordinary Portland cement and water with the composition shown in Table 2, using Tables 4 to 6,
By performing a carbonation treatment under the curing conditions and the carbonation treatment conditions shown in (1), a dumbbell-shaped cured cement of 150 mm × 50 mm × 20 mm was obtained. The ratio (volume%) of the pulverized material in the hardened cement was as shown in Table 2. The flexural strength and specific gravity of these hardened cement bodies were measured by the methods described below, and the results are shown in Table 2 together with Comparative Examples.

【００２３】（比較例１〜４）普通ポルトランドセメン
トと、必要により粉砕物３又は６を用いて、普通ポルト
ランドセメントと水とを表２に示すような配合で混合・
混練後、表２に示すような養生条件で養生することによ
り、150mm ×50mm×20mmのダンベル状セメント硬化体を
得た。 ＊ 上記実施例１〜５及び比較例１〜４で得られたセメ
ント硬化体について、ＪＩＳ A １１０６に準拠した曲
げ強度試験、及びＪＩＳ Ｒ ５２０１に準拠した比重
測定を行い、曲げ強度と比重を測定した。(Comparative Examples 1 to 4) Using ordinary Portland cement and, if necessary, pulverized material 3 or 6, mixed ordinary Portland cement and water in the composition shown in Table 2.
After kneading, the mixture was cured under the curing conditions shown in Table 2 to obtain a cured dumbbell-shaped cement of 150 mm × 50 mm × 20 mm. * For the cured cement bodies obtained in Examples 1 to 5 and Comparative Examples 1 to 4, a bending strength test according to JIS A 1106 and a specific gravity measurement according to JIS R 5201 are performed, and the bending strength and specific gravity are measured. did.

【００２４】[0024]

【表１】 [Table 1]

【００２５】[0025]

【表２】 [Table 2]

【００２６】[0026]

【発明の効果】本発明のセメント硬化体は、以上のよう
に構成され、有機系廃材粉砕物を混入されていると共に
炭酸化処理されているので、従来のセメント硬化体と同
程度以上の強度を発現し得るものである。有機系廃材粉
砕物が、プラスチック粉砕物、セメント及び水から得ら
れた硬化体の粉砕物である場合は、粉砕が比較的困難な
軟プラスチック又は難形状のプラスチック等であって
も、一旦セメントで硬化させることにより、粉砕が容易
となり、有機系廃材のリサイクルが促進されると共にセ
メント硬化体を廉価に提供することが可能となる。The hardened cement of the present invention is constituted as described above, is mixed with a pulverized organic waste material, and is subjected to a carbonation treatment. Can be expressed. When the pulverized organic waste material is a pulverized product of a hardened material obtained from plastic pulverized material, cement, and water, even if it is a soft plastic or a hard-shaped plastic that is relatively difficult to pulverize, it is once used in cement. By hardening, the pulverization becomes easy, the recycling of the organic waste material is promoted, and the hardened cement can be provided at low cost.

【００２７】有機系廃材粉砕物の粒径が0.001mm 〜10mm
の範囲にある場合は、十分な強度を発現したセメント硬
化体が提供される。プラスチックが塩化ビニル重合体で
ある場合は、塩化ビニル重合体の難リサイクル性及び廃
棄物処理時におけるダイオキシン発生等の恐れがある物
質を積極的に利用することが可能であるため、廃棄物処
理技術としての展開が図れ、環境対策に対する貢献度が
高い。The particle size of the crushed organic waste material is 0.001 mm to 10 mm.
When it is in the range, a hardened cement material exhibiting sufficient strength is provided. If the plastic is vinyl chloride polymer, it is possible to actively use substances that have difficulty in recycling vinyl chloride polymer and may generate dioxins during waste disposal. And a high degree of contribution to environmental measures.

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】 有機系廃材粉砕物とセメントと水とが混
合された後に炭酸化処理と共に硬化されてなることを特
徴とするセメント硬化体。1. A hardened cement material comprising a ground organic waste material, cement, and water mixed and then hardened together with a carbonation treatment. 【請求項２】 有機系廃材粉砕物が、プラスチック粉砕
物、セメント及び水から得られた硬化体の粉砕物である
ことを特徴とする請求項１記載のセメント硬化体。2. The cement hardened product according to claim 1, wherein the organic waste crushed material is a crushed product of a hardened product obtained from a plastic crushed product, cement and water. 【請求項３】 有機系廃材粉砕物の粒径が0.001mm 〜10
mmの範囲にあることを特徴とする請求項１記載のセメン
ト硬化体。3. The particle size of the pulverized organic waste material is from 0.001 mm to 10 mm.
2. The hardened cement body according to claim 1, wherein the hardened cement body is in a range of mm. 【請求項４】 プラスチックが塩化ビニル重合体である
ことを特徴とする請求項２記載のセメント硬化体。4. The hardened cement according to claim 2, wherein the plastic is a vinyl chloride polymer.