JP2000218972A - Thermal transfer recording-type magnetic coupon sheet - Google Patents
Thermal transfer recording-type magnetic coupon sheetInfo
- Publication number
- JP2000218972A JP2000218972A JP11024812A JP2481299A JP2000218972A JP 2000218972 A JP2000218972 A JP 2000218972A JP 11024812 A JP11024812 A JP 11024812A JP 2481299 A JP2481299 A JP 2481299A JP 2000218972 A JP2000218972 A JP 2000218972A
- Authority
- JP
- Japan
- Prior art keywords
- thermal transfer
- type magnetic
- transfer recording
- receiving layer
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、乗車券、定期券、
通行券等の券紙やプリペードカード等における磁気カー
ド類およびＰＯＳラベル等のラベル類への応用が可能な
熱転写記録型磁気券紙に関する。The present invention relates to a ticket, a commuter pass,
The present invention relates to a thermal transfer recording type magnetic ticket that can be applied to magnetic cards and POS labels and the like for tickets such as toll tickets and prepaid cards.
【０００２】[0002]
【従来の技術】近年、磁気回数券、道路通行券、定期
券、プリペードカード等における磁気カード類の普及に
は目覚しいものがある。この磁気カード類は顧客がカー
ドを使用する毎に変動する残金表示やカードの有効期
間、発行日等は記録されているものの顧客には見えない
ため、これらを可視情報として記録できるようにするこ
とが要求されている。そのような記録手段の一つとして
熱転写方式を用いたものが上市されている。該記録手段
は感熱記録方式であってもよい。前記熱転写方式を用い
たものとは、加熱により転写可能なインク層を設けたイ
ンクシートと組み合わせて、サーマルヘッド等の加熱に
より熱転写記録像を形成せしめるものである。これらの
磁気カード類は、磁気回数券、道路通行券、定期券、プ
リペードカード等に用いられるため、ある程度の強度や
腰が必要とされ、強度のあるプラスチックシートや比較
的厚い上質紙などが支持体に用いられる。しかし、その
腰の強さや厚みのために熱転写記録を行う際に、サーマ
ルヘッドとの密着性が低く、鮮明で濃度の高い記録像が
得られないという問題があり、インク転写を促進させる
ために該磁気カード類の熱転写記録側に熱転写インク受
容層を設けるなどの改良が図られている。2. Description of the Related Art In recent years, there has been a remarkable spread of magnetic cards such as magnetic coupons, road toll tickets, commuter passes, and prepaid cards. These magnetic cards have the balance display, which changes every time the customer uses the card, and the card's validity period and issuance date, etc., but are not visible to the customer. Is required. As one of such recording means, one using a thermal transfer method has been put on the market. The recording means may be of a thermal recording type. The method using the thermal transfer method is to form a thermal transfer recording image by heating a thermal head or the like in combination with an ink sheet provided with an ink layer that can be transferred by heating. Since these magnetic cards are used for magnetic coupons, road pass tickets, commuter passes, prepaid cards, etc., they require a certain amount of strength and waist, and support strong plastic sheets and relatively thick high-quality paper. Used for the body. However, when performing thermal transfer recording due to its stiffness and thickness, there is a problem that adhesion to the thermal head is low, and a clear and high-density recorded image cannot be obtained. Improvements have been made such as providing a thermal transfer ink receiving layer on the thermal transfer recording side of such magnetic cards.
【０００３】例えば、特開昭５７−１８２４８７号公報
には、感熱転写シートからの転写像を受ける受像シート
に吸油量（ＪＩＳ Ｋ５１０１）３０ｍｌ／１００ｇ以
上の吸油性顔料を含有させた受像シートが記載されてい
る。これによれば、画像品質の向上は図れるものの、そ
の裏面に磁気記録層を設けた場合、厚みや腰が増大して
サーマルヘッドとの密着性が低下して十分な効果は得ら
れない。特に支持体にプラスチックシートや厚めの上質
紙を用いた場合は、この傾向が顕著である。例えば磁気
券紙等の受容シートにおいては、磁気記録層が設けられ
て厚みが厚いためサーマルヘッドとの密着性が弱くなり
印字品質が劣る。すなわち画像濃度が低く、また画像均
一性が悪く、特に白抜け等が発生する。For example, JP-A-57-182487 discloses an image receiving sheet containing an oil absorbing pigment having an oil absorption (JIS K5101) of 30 ml / 100 g or more in an image receiving sheet for receiving a transfer image from a thermal transfer sheet. Have been. According to this, although the image quality can be improved, when the magnetic recording layer is provided on the back surface, the thickness and the stiffness increase, and the adhesion to the thermal head is reduced, so that a sufficient effect cannot be obtained. This tendency is remarkable especially when a plastic sheet or thick high quality paper is used for the support. For example, a receiving sheet such as a magnetic paper sheet is provided with a magnetic recording layer and has a large thickness, so that adhesion to a thermal head is weakened and printing quality is poor. That is, the image density is low and the image uniformity is poor, and particularly, white spots and the like occur.
【０００４】[0004]
【発明が解決しようとする課題】本発明は上記欠点を解
決するためになされたもので、熱転写画像の画像濃度お
よび画像均一性の優れた熱転写記録型磁気券紙を提供す
ることを目的とする。SUMMARY OF THE INVENTION The present invention has been made to solve the above-mentioned drawbacks, and has as its object to provide a thermal transfer recording type magnetic sheet having excellent image density and image uniformity of a thermal transfer image. .
【０００５】[0005]
【課題を解決するための手段】本発明によれば、第一
に、支持体の一方の面に強磁性体とバインダーを含有す
る磁気記録層を設け、もう一方の面に顔料とバインダー
を含有する熱転写インク受容層を設けた熱転写記録型磁
気券紙において、前記受容層の顔料が吸油量（ＪＩＳ
Ｋ５１０１）が２００ｍｌ／１００ｇ以上であることを
特徴とする熱転写記録型磁気券紙が提供される。According to the present invention, first, a magnetic recording layer containing a ferromagnetic material and a binder is provided on one surface of a support, and a pigment and a binder are contained on the other surface. In a thermal transfer recording type magnetic paper sheet provided with a thermal transfer ink receiving layer, the pigment of the receiving layer has an oil absorption (JIS).
K5101) is 200 ml / 100 g or more.
【０００６】第二に、上記第一に記載した熱転写記録型
磁気券紙において、上記受容層の顔料がシリカであるこ
とを特徴とする熱転写記録型磁気券紙が提供される。Secondly, there is provided a thermal transfer recording type magnetic paper sheet according to the first aspect, wherein the pigment of the receiving layer is silica.
【０００７】第三に、上記第一または第二に記載した熱
転写記録型磁気券紙において、上記受容層のバインダー
が非水溶性樹脂であることを特徴とする熱転写記録型磁
気券紙が提供される。Third, there is provided a thermal transfer recording type magnetic paper sheet according to the first or second aspect, wherein the binder of the receiving layer is a water-insoluble resin. You.
【０００８】第四に、上記第一、第二または第三に記載
した熱転写記録型磁気券紙において、該熱転写記録型磁
気券紙の厚さ（ＪＩＳ Ｐ８１１８）が１５０μｍ以上
であることを特徴とする熱転写記録型磁気券紙が提供さ
れる。Fourthly, in the thermal transfer recording type magnetic paper described in the first, second or third aspect, the thickness (JIS P8118) of the thermal transfer recording type magnetic paper is 150 μm or more. The present invention provides a thermal transfer recording type magnetic ticket.
【０００９】以下に本発明を詳細に説明する。上述のよ
うに、本発明は支持体の一方の面に強磁性体とバインダ
ーを含有する磁気記録層を設け、もう一方の面に顔料と
バインダーを含有する熱転写インク受容層を設けた熱転
写記録型磁気券紙において、上記受容層の顔料が吸油量
（ＪＩＳ Ｋ５１０１）が２００ｍｌ／１００ｇ以上で
あるとするものであり、このような構成によれば、従
来、吸油量３０ｍｌ／１００ｇ以上の顔料とバインダー
で形成された受容層では得ることができなかった、高い
画像濃度と画像均一性を得ることができる。Hereinafter, the present invention will be described in detail. As described above, the present invention provides a thermal transfer recording type in which a magnetic recording layer containing a ferromagnetic material and a binder is provided on one surface of a support, and a thermal transfer ink receiving layer containing a pigment and a binder is provided on the other surface. In the magnetic paper, the pigment of the receiving layer has an oil absorption (JIS K5101) of 200 ml / 100 g or more. According to such a configuration, the pigment and the binder having an oil absorption of 30 ml / 100 g or more are conventionally used. A high image density and image uniformity, which could not be obtained with the receiving layer formed by the method, can be obtained.
【００１０】上記画像濃度および画像均一性は、該受容
層顔料としてシリカを用いた場合は最も優れた効果が得
られる。また受容層バインダーとして非水溶性樹脂を用
いることによって印字品質をより向上させることができ
る。さらに本発明のこのような構成によれば該磁気券紙
の厚さを１５０μｍ以上としても十分に有効である。With respect to the above image density and image uniformity, the most excellent effects can be obtained when silica is used as the pigment for the receiving layer. Further, by using a water-insoluble resin as the binder for the receiving layer, the printing quality can be further improved. Further, according to such a configuration of the present invention, it is sufficiently effective even if the thickness of the magnetic paper sheet is 150 μm or more.
【００１１】[0011]
【発明の実施の形態】以下に本発明の実施の形態につい
て説明する。図１に本発明の熱転写記録型磁気券紙の概
略断面図を示す。図のように支持体２の一方の面に熱転
写インク受容層１、もう一方の面に磁気記録層３が設け
られる。まず、該熱転写インク受容層１には主成分とし
て顔料とバインダーが含有される。含有させる顔料とし
ては、例えば炭酸カルシウム、シリカ、酸化チタン、水
酸化アルミニウム、クレー、焼成クレー、ケイ酸マグネ
シウム、炭酸マグネシウム、ホワイトカーボン、酸化亜
鉛、硫酸バリウム、表面処理された炭酸カルシウムやシ
リカ、また尿素−ホルマリン樹脂、スチレン／メタクリ
ル酸共重合体、ポリスチレン等の微粉末等で、吸油量２
００ｍｌ／１００ｇ以上のものである。なかでもシリカ
を含有させることが最も好ましい。Embodiments of the present invention will be described below. FIG. 1 is a schematic sectional view of a thermal transfer recording type magnetic paper sheet of the present invention. As shown, a thermal transfer ink receiving layer 1 is provided on one side of a support 2 and a magnetic recording layer 3 is provided on the other side. First, the thermal transfer ink receiving layer 1 contains a pigment and a binder as main components. Examples of pigments to be contained include calcium carbonate, silica, titanium oxide, aluminum hydroxide, clay, calcined clay, magnesium silicate, magnesium carbonate, white carbon, zinc oxide, barium sulfate, surface-treated calcium carbonate and silica, and Urea-formalin resin, styrene / methacrylic acid copolymer, fine powder of polystyrene, etc., oil absorption 2
It is more than 00ml / 100g. Among them, it is most preferable to contain silica.
【００１２】次に熱転写インク受容層１に用いるバイン
ダーとしては、水溶性樹脂としてポリビニルアルコー
ル、デンプンおよびその誘導体、メトキシセルロース、
ヒドロキシエチルセルロース、カルボキシメチルセルロ
ース、メチルセルロース、エチルセルロース等のセルロ
ース誘導体、ポリアクリル酸ソーダ、ポリビニルピロリ
ドン、アクリルアミド／アクリル酸エステル共重合体、
アクリルアミド／アクリル酸エステル／メタクリル酸三
元共重合体、スチレン／無水マレイン酸共重合体アルカ
リ塩、イソブチレン／無水マレイン酸共重合体アルカリ
塩、ポリアクリルアミド、アルギン酸ソーダ、ゼラチ
ン、カゼイン等の水溶性高分子が用いられる。非水溶性
樹脂としてはスチレン／ブタジエン共重合体、スチレン
／アクリル酸エステル共重合体、酢酸ビニル／エチレン
共重合体、塩化ビニル／エチレン共重合体、酢酸ビニル
／エチレン／塩化ビニル共重合体、アクリル酸エステル
樹脂、ポリウレタン樹脂等が用いられる。なかでも非水
溶性樹脂は画像濃度や画像均一性を向上させる上で有効
であり、該樹脂を用いることがことが望ましい。Next, as a binder used in the thermal transfer ink receiving layer 1, polyvinyl alcohol, starch and its derivatives, methoxycellulose,
Hydroxyethyl cellulose, carboxymethyl cellulose, methyl cellulose, cellulose derivatives such as ethyl cellulose, sodium polyacrylate, polyvinylpyrrolidone, acrylamide / acrylate copolymer,
Water solubility of acrylamide / acrylic acid ester / methacrylic acid terpolymer, styrene / maleic anhydride copolymer alkali salt, isobutylene / maleic anhydride copolymer alkali salt, polyacrylamide, sodium alginate, gelatin, casein, etc. Molecules are used. Examples of water-insoluble resins include styrene / butadiene copolymer, styrene / acrylate copolymer, vinyl acetate / ethylene copolymer, vinyl chloride / ethylene copolymer, vinyl acetate / ethylene / vinyl chloride copolymer, acrylic Acid ester resins, polyurethane resins and the like are used. Among them, a water-insoluble resin is effective in improving image density and image uniformity, and it is desirable to use the resin.
【００１３】該熱転写インク受容層における顔料とバイ
ンダー樹脂の割合は、顔料１００重量部に対して樹脂２
０重量部から５００重量部とするのが好ましい。受容層
の厚みとしては２〜２０μｍ、券紙全体の厚みを１５０
μｍ以上としても好ましい。The ratio of the pigment to the binder resin in the thermal transfer ink receiving layer is such that the resin 2 is added to 100 parts by weight of the pigment.
It is preferably from 0 to 500 parts by weight. The thickness of the receiving layer is 2 to 20 μm, and the thickness of the whole paper is 150
It is also preferable that the thickness be not less than μm.
【００１４】次に磁気記録層３は強磁性体とバインダー
を主成分とし形成される。該強磁性体としては、バリウ
ムフェライト、ストロンチウムフェライト、Ｃｏ−γ−
Ｆｅ ２Ｏ３、γ−Ｆｅ２Ｏ３等の粉体が使用される。ま
た、該磁気記録層に用いるバインダーとしては、慣用の
種々のものを使用でき、その具体例としてはポリビニル
ブチラール、ポリ酢酸ビニル、ポリプロピオン酸ビニ
ル、ポリ酢酸ビニル、ポリメチルアクリレート、ポリエ
チルアクリレート、ポリプロピルアクリレート、ポリブ
チルアクリレート、ポリヘプチルアクリレート、ポリエ
チルへキシルアクリレート、スチレン−ブタジエンゴ
ム、ニトリルゴム、天然ゴム、ポリイソブチレンゴム、
ポリブタジエン、ポリアクリロニトリル、ポリメタクリ
ロニトリル、ポリ塩化ビニリデン、ポリジクロロスチレ
ン、ポリスチレン、ポリ塩化ビニル、ポリメタクリル
酸、ポリメチルメタクリレート、ポリエチルメタクリレ
ート、ポリプロピルメタクリレート、ポリブチルメタク
リレート、ポリエチルヘキシルメタクリレート、ポリビ
ニルアルコール、ポリビニルステアレート等の水性エマ
ルジョン樹脂等が挙げられる。Next, the magnetic recording layer 3 is made of a ferromagnetic material and a binder.
Is formed as a main component. The ferromagnetic material includes barium
Ferrite, strontium ferrite, Co-γ-
Fe 2O3, Γ-Fe2O3Etc. are used. Ma
Further, as a binder used for the magnetic recording layer, a conventional binder
Various types can be used, and specific examples thereof include polyvinyl.
Butyral, polyvinyl acetate, polypropionate vinyl
, Polyvinyl acetate, polymethyl acrylate, polyether
Chill acrylate, polypropyl acrylate, polybut
Tyl acrylate, polyheptyl acrylate, polyether
Cylhexyl acrylate, styrene-butadienego
Rubber, nitrile rubber, natural rubber, polyisobutylene rubber,
Polybutadiene, polyacrylonitrile, polymethacrylate
Lonitrile, polyvinylidene chloride, polydichlorostyrene
, Polystyrene, polyvinyl chloride, polymethacryl
Acid, polymethyl methacrylate, polyethyl methacrylate
, Polypropyl methacrylate, polybutyl methacrylate
Relate, polyethylhexyl methacrylate, polyvinyl chloride
Aqueous emma such as nyl alcohol and polyvinyl stearate
Lution resin and the like.
【００１５】[0015]
《バリウムフェライト分散液の調製》 バリウムフェライト （保持力：２７００ Ｏｅ、平均粒径：０．６μｍ） １００部 ポリアクリル酸ソーダ（２０％水溶液） １０部 カーボンブラック（３８％分散液） ２０部 水 ９０部 以上の組成からなる物をサンドグライダーで２４時間分
散してバリウムフェライト分散液を調製した。 《磁気塗布層形成液の調製》 バリウムフェライト分散液 ２２０部 塩化ビニリデンエマルジョン（４９％） １００部 水 ８０部 以上の液を混合攪拌して磁気塗布層形成液を調製した。
上記磁気塗布層形成液を紙厚１５０μｍの上質紙の片面
に乾燥重量が４２ｇ／ｍ２となるように塗布乾燥し磁気
記録層を形成した。 《Ａ液の調製》 シリカ （水澤化学社製Ｐ−５２６（吸油量：２００ｍｌ／１００ｇ）） １５部 ポリビニルアルコール（１０％水溶液） １５部 水 ７０部 以上の組成からなる液をサンドグラインダーで１５分間
分散して、顔料分散液Ａ液を調製した。 《Ｂ液の調製》 Ａ液 ４９部 スチレン／アクリル酸エステル共重合体ラテックス （ジョンソンポリマー社製Ｊ−７４Ｊ） １８部 水 ９部 以上の液を混合攪拌して受容層形成液Ｂを調製した。こ
のＢ液を支持体のもう一方の面に乾燥重量が５．０ｇ／
ｍ２となるように塗布し、熱転写インク受容層を形成し
た。次いでこのインク受容層表面を平滑度５００ｓｅｃ
となるようにキャレンダー処理を行い熱転写記録型磁気
券紙を得た。<< Preparation of Barium Ferrite Dispersion >> Barium Ferrite (holding power: 2700 Oe, average particle size: 0.6 μm) 100 parts Sodium polyacrylate (20% aqueous solution) 10 parts Carbon black (38% dispersion) 20 parts Water 90 Parts A barium ferrite dispersion was prepared by dispersing the composition having the above composition for 24 hours using a sand glider. << Preparation of Magnetic Coating Layer Forming Liquid >> Barium ferrite dispersion liquid 220 parts Vinylidene chloride emulsion (49%) 100 parts Water 80 parts The above liquids were mixed and stirred to prepare a magnetic coating layer forming liquid.
The magnetic coating layer forming solution was applied on one side of high quality paper having a paper thickness of 150 μm and dried so as to have a dry weight of 42 g / m 2 to form a magnetic recording layer. << Preparation of Liquid A >> Silica (P-526, manufactured by Mizusawa Chemical Co., Ltd. (oil absorption: 200 ml / 100 g)) 15 parts Polyvinyl alcohol (10% aqueous solution) 15 parts Water 70 parts A liquid having the above composition is sand-ground for 15 minutes. By dispersing, a pigment dispersion liquid A was prepared. << Preparation of Liquid B >> Liquid A 49 parts Styrene / acrylate copolymer latex (J-74J manufactured by Johnson Polymer Co.) 18 parts Water 9 parts The above liquid was mixed and stirred to prepare a receptor layer forming liquid B. The solution B was coated on the other side of the support with a dry weight of 5.0 g /
It was applied as a m 2, and to form a thermal transfer ink-receiving layer. Next, the surface of the ink receiving layer was smoothed for 500 seconds.
Then, a calendering process was performed to obtain a thermal transfer recording type magnetic paper sheet.
【００１６】〔実施例２〕実施例１のＡ液のシリカを水
澤化学社製Ｐ−７８Ａ（吸油量：２５０ｍｌ／１００
ｇ）に変えた以外は実施例１と同様にして熱転写記録型
磁気券紙を得た。[Example 2] The silica of the liquid A of Example 1 was replaced with P-78A manufactured by Mizusawa Chemical Co. (oil absorption: 250 ml / 100).
A thermal transfer recording-type magnetic ticket paper was obtained in the same manner as in Example 1 except that g) was changed.
【００１７】〔実施例３〕実施例１のＢ液のスチレン／
アクリル酸エステル共重合体ラテックスを住友化学社製
Ｓ−７５２（酢酸ビニル／エチレン共重合体ラテック
ス）に変えた以外は実施例１と同様にして熱転写記録型
磁気券紙を得た。Example 3 The styrene / liquid B of Example 1
A thermal transfer recording magnetic ticket paper was obtained in the same manner as in Example 1 except that the acrylic ester copolymer latex was changed to S-752 (vinyl acetate / ethylene copolymer latex) manufactured by Sumitomo Chemical Co., Ltd.
【００１８】 〔実施例４〕 《Ｃ液の調製》 Ａ液 ４９部 ポリビニルアルコール（１０％水溶液） ５１部 以上の液を混合攪拌して受容層形成液Ｃを調製した。こ
のＣ液を実施例１のＢ液の代わりに用い、それ以外は実
施例１と同様にして熱転写記録型磁気券紙を得た。Example 4 << Preparation of Liquid C >> Liquid A 49 parts Polyvinyl alcohol (10% aqueous solution) 51 parts The above liquids were mixed and stirred to prepare a receptor layer forming liquid C. This solution C was used in place of the solution B of Example 1, and the other conditions were the same as in Example 1 to obtain a thermal transfer recording type magnetic paper sheet.
【００１９】〔実施例５〕実施例１のＡ液のシリカをア
ルミノケイ酸塩（水澤化学社製シルトンＬＰ−７５（吸
油量：２５０ｍｌ／１００ｇ））に変えた以外は実施例
１と同様にして熱転写記録型磁気券紙を得た。Example 5 The procedure of Example 1 was repeated except that the silica of the solution A in Example 1 was changed to an aluminosilicate (Silton LP-75 manufactured by Mizusawa Chemical Co., Ltd. (oil absorption: 250 ml / 100 g)). A thermal transfer recording type magnetic paper was obtained.
【００２０】〔比較例１〕実施例１のシリカを水澤化学
社製Ｐ−７３（吸油量：１８０ｍｌ／１００ｇ）に変え
た以外は実施例１と同様にして熱転写記録型磁気券紙を
得た。 〔比較例２〕実施例１のシリカを水酸化アルミニウム
（昭和電工社製Ｈ−４２Ｍ（吸油量：４０ｍｌ／１００
ｇ）に変えた以外は実施例１と同様にして熱転写記録型
磁気券紙を得た。[Comparative Example 1] A thermal transfer recording type magnetic sheet was obtained in the same manner as in Example 1 except that the silica of Example 1 was changed to P-73 (oil absorption: 180 ml / 100 g) manufactured by Mizusawa Chemical Co., Ltd. . Comparative Example 2 The silica of Example 1 was replaced with aluminum hydroxide (H-42M manufactured by Showa Denko KK (oil absorption: 40 ml / 100).
A thermal transfer recording-type magnetic ticket paper was obtained in the same manner as in Example 1 except that g) was changed.
【００２１】上記のようにして得た実施例および比較例
の熱転写記録型磁気券紙について、次の試験法により画
像印字品質（画像濃度、画像均一性）の評価を行った。
その結果を表１に示す。 《熱転写印字試験》 プリンタ ：ＴＥＣ社製Ｂ−３０ リボン ：ゼネラル社製ＷＡＸリボン サーマルヘッド ：ＴＥＣ社製（５１０Ω） 印字速度（線速） ：２ｉｎ／ｓｅｃ 印字エネルギー ：Ｂ−３０標準エネルギー 画像濃度 ：マクベス反射濃度計Ｒ−９１４型使用The image transfer quality (image density, image uniformity) of the thermal transfer recording type magnetic paper sheets of the examples and comparative examples obtained as described above was evaluated by the following test method.
Table 1 shows the results. << Thermal transfer printing test >> Printer: TEC B-30 ribbon: General WAX ribbon Thermal head: TEC (510Ω) Printing speed (linear speed): 2 in / sec Printing energy: B-30 standard energy Image density: Using Macbeth R-914 reflection densitometer
【００２２】[0022]
【表１】 [Table 1]
【００２３】上表中、画像均一性の各評価ランクは次の
通りである。 ○：濃度のバラツキがなく、画像が均一である。 △：濃度のバラツキが若干ある。 ×：濃度のバラツキが激しい。In the above table, each evaluation rank of image uniformity is as follows. ：: There is no variation in density, and the image is uniform. Δ: There is some variation in density. X: The concentration variation is severe.
【００２４】上表から実施例の熱転写記録型磁気券紙
が、画像濃度、画像均一性共に優れた特性が得られてい
ること、そして、これらの特性を得るには顔料の吸油量
を２００ｍｌ／１００ｇ以上とする必要があること、ま
た、受容層のバインダーとしては水溶性樹脂より非水溶
性樹脂の方が有効であること、さらに、これらの特性が
券紙の厚さを１５０μｍ以上としても十分に得られるこ
とが明らかである。From the above table, it can be seen that the thermal transfer recording type magnetic paper sheets of the examples have excellent characteristics in both image density and image uniformity. In order to obtain these characteristics, the oil absorption of the pigment must be 200 ml / ml. The binder must be 100 g or more, and the water-insoluble resin is more effective than the water-soluble resin as a binder for the receiving layer. Further, these characteristics are sufficient even if the thickness of the paper is 150 μm or more. It is clear that it can be obtained.
【００２５】[0025]
【発明の効果】以上のように、請求項１の熱転写記録型
磁気券紙は、支持体の一方の面に強磁性体とバインダー
を含有する磁気記録層を設け、もう一方の面に顔料とバ
インダーを含有する熱転写インク受容層を設けた熱転写
記録型磁気券紙において、前記受容層の顔料が吸油量
（ＪＩＳ Ｋ５１０１）が２００ｍｌ／１００ｇ以上で
あることとするものであり、これによれば画像濃度、画
像均一性共に優れた、印字品質の高い熱転写記録型磁気
券紙を得ることができる。As described above, the thermal transfer recording type magnetic paper of claim 1 is provided with a magnetic recording layer containing a ferromagnetic material and a binder on one surface of a support, and a pigment on the other surface. In a thermal transfer recording-type magnetic paper sheet provided with a thermal transfer ink receiving layer containing a binder, the pigment of the receiving layer has an oil absorption (JIS K5101) of 200 ml / 100 g or more. It is possible to obtain a thermal transfer recording type magnetic sheet having excellent print quality and excellent density and image uniformity.
【００２６】請求項２の熱転写記録型磁気券紙は、上記
請求項１における受容層の顔料をシリカに特定したもの
で、これによれば他の顔料と比較して優れた画像濃度お
よび画像均一性を有する熱転写記録型磁気券紙を得るこ
とができる。The thermal transfer recording type magnetic paper according to the second aspect is characterized in that the pigment of the receiving layer in the first aspect is specified to be silica, and according to this, the image density and the image uniformity are superior to other pigments. It is possible to obtain a thermal transfer recording type magnetic paper sheet having a property.
【００２７】請求項３の熱転写記録型磁気券紙は、上記
請求項１における受容層のバインダーを非水溶性樹脂に
特定するもので、これによれば水溶性樹脂の場合と比較
してさらに画像濃度および画像均一性を向上させた熱転
写記録型磁気券紙を得ることができる（実施例１および
４参照）。In a third aspect of the present invention, the binder for the receiving layer is specified to be a water-insoluble resin. It is possible to obtain a thermal transfer recording type magnetic paper sheet having improved density and image uniformity (see Examples 1 and 4).
【００２８】請求項４の熱転写記録型磁気券紙は、上記
熱転写記録型磁気券紙において、該熱転写記録型磁気券
紙の厚さ（ＪＩＳ Ｐ８１１８）を１５０μｍ以上に特
定するもので、上記構成の磁気券紙によれば厚さ１５０
μｍ以上としても画像濃度および画像均一性を損なわな
い熱転写記録型磁気券紙を得ることができる。A thermal transfer recording type magnetic sheet according to a fourth aspect of the present invention is the thermal transfer recording type magnetic sheet, wherein the thickness (JIS P8118) of the heat transfer recording type magnetic sheet is specified to be 150 μm or more. According to magnetic paper, thickness 150
A thermal transfer recording type magnetic paper sheet which does not impair the image density and the image uniformity even when the thickness is at least μm can be obtained.
【図１】熱転写記録型磁気券紙の一例を示す概略断面図
である。FIG. 1 is a schematic sectional view showing an example of a thermal transfer recording type magnetic ticket paper.
１ 熱転写インク受容層 ２ 支持体 ３ 磁気記録層 Reference Signs List 1 thermal transfer ink receiving layer 2 support 3 magnetic recording layer
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｂ４１Ｍ 5/40 Ｇ０９Ｆ 3/00 Ｍ Ｇ０６Ｋ 19/06 Ｇ１１Ｂ 5/80 Ｇ０９Ｆ 3/00 Ｂ４１Ｍ 5/26 Ｈ Ｇ１１Ｂ 5/80 Ｇ０６Ｋ 19/00 Ａ (72)発明者 野毛 由文 東京都大田区中馬込１丁目３番６号 株式 会社リコー内 (72)発明者 折原 基 東京都大田区中馬込１丁目３番６号 株式 会社リコー内 (72)発明者 湯山 幸博 東京都大田区中馬込１丁目３番６号 株式 会社リコー内──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) B41M 5/40 G09F 3/00 M G06K 19/06 G11B 5/80 G09F 3/00 B41M 5/26 H G11B 5/80 G06K 19/00 A (72) Inventor Yoshifumi Noge 1-3-6 Nakamagome, Ota-ku, Tokyo Inside Ricoh Co., Ltd. (72) Motoi Orihara 1-3-6 Nakamagome, Ota-ku, Tokyo No. Ricoh Co., Ltd. (72) Inventor Yukihiro Yuyama 1-3-6 Nakamagome, Ota-ku, Tokyo Ricoh Co., Ltd.
Claims (4)
ーを含有する磁気記録層を設け、もう一方の面に顔料と
バインダーを含有する熱転写インク受容層を設けた熱転
写記録型磁気券紙において、前記受容層の顔料が吸油量
（ＪＩＳ Ｋ５１０１）が２００ｍｌ／１００ｇ以上で
あることを特徴とする熱転写記録型磁気券紙。1. A thermal transfer recording type magnetic paper having a magnetic recording layer containing a ferromagnetic material and a binder on one side of a support and a thermal transfer ink receiving layer containing a pigment and a binder on the other side. 3. The thermal transfer recording type magnetic sheet according to claim 1, wherein the pigment of the receiving layer has an oil absorption (JIS K5101) of 200 ml / 100 g or more.
おいて、前記受容層の顔料がシリカであることを特徴と
する熱転写記録型磁気券紙。2. The thermal transfer recording type magnetic sheet according to claim 1, wherein the pigment of the receiving layer is silica.
気券紙において、前記受容層のバインダーが非水溶性樹
脂であることを特徴とする熱転写記録型磁気券紙。3. The thermal transfer recording type magnetic sheet according to claim 1, wherein the binder of the receiving layer is a water-insoluble resin.
型磁気券紙において、該熱転写記録型磁気券紙の厚さ
（ＪＩＳ Ｐ８１１８）が１５０μｍ以上であることを
特徴とする熱転写記録型磁気券紙。4. The thermal transfer recording type magnetic sheet according to claim 1, wherein the thickness (JIS P8118) of the thermal transfer recording type magnetic sheet is 150 μm or more. Ticket paper.