JP3421762B2 - Thermal transfer recording type magnetic paper - Google Patents
Thermal transfer recording type magnetic paperInfo
- Publication number
- JP3421762B2 JP3421762B2 JP05981095A JP5981095A JP3421762B2 JP 3421762 B2 JP3421762 B2 JP 3421762B2 JP 05981095 A JP05981095 A JP 05981095A JP 5981095 A JP5981095 A JP 5981095A JP 3421762 B2 JP3421762 B2 JP 3421762B2
- Authority
- JP
- Japan
- Prior art keywords
- water
- thermal transfer
- transfer recording
- type magnetic
- receiving layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、乗車券、定期券、通行
券等の券紙やプリペードカード等における磁気カード類
およびＰＯＳラベル等のラベル類への応用が可能な熱転
写記録型磁気券紙に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention can be applied to thermal transfer recording type magnetic ticket paper which can be applied to ticket papers, commuter tickets, pass tickets and the like, magnetic cards such as prepaid cards and labels such as POS labels. Regarding
【０００２】[0002]
【従来の技術】近年、磁気回数券、道路通行券、定期
券、プリペードカード等における磁気カード類の普及に
は目覚ましいものがある。この磁気カード類は、顧客が
カードを使用する毎に変動する残金表示やカードの有効
期間、発行日等を可視情報として記録できることが要求
されている。そのような記録手段の一つとして熱転写方
式がある。この方式に用いられる磁気カード類は、通
常、プラスチックシートまたは上質紙等の支持体の片面
に磁気記録層を設けたものが知られているが、記録画像
の高感度化、高濃度化、画像均一化等の要求に耐えがた
く、熱転写記録側にインク受理層を設けるなどの改良が
図られている。2. Description of the Related Art In recent years, magnetic cards such as magnetic coupon tickets, road tickets, commuter passes, prepaid cards, etc. have been remarkably spread. The magnetic cards are required to be able to record visible information such as the balance display, the validity period of the card, the issue date, etc., which changes every time the customer uses the card. There is a thermal transfer system as one of such recording means. Magnetic cards used in this system are generally known to have a magnetic recording layer provided on one side of a support such as a plastic sheet or high-quality paper. Improvements such as providing an ink receiving layer on the thermal transfer recording side are being made because it is difficult to withstand the demands for uniformity and the like.
【０００３】例えば、特開昭５７−１８２４８７号公報
には、感熱転写シートからの転写像を受ける受像シート
に吸油量３０ｍｌ／１００ｇ以上の吸油性顔料を含有さ
せた受像シートが記載されている。これによれば、画像
品質の向上は図れるものの図１に示すように支持体の両
面にコーティング層が設けられることから夏期等の高
温、高湿下において、原反あるいはスリット状態で保管
すると、層のハガレ、転写等のブロッキング現象が発生
するという欠点があり、そのため熱転写記録だけでなく
磁気記録にも異常を来すという問題を起こす。For example, JP-A-57-182487 discloses an image-receiving sheet in which an oil-absorbing pigment having an oil absorption amount of 30 ml / 100 g or more is contained in an image-receiving sheet which receives a transferred image from a heat-sensitive transfer sheet. According to this, although the image quality can be improved, the coating layer is provided on both sides of the support as shown in FIG. 1, and therefore, when it is stored in a raw material or a slit state under high temperature and high humidity such as summer, the layer is However, there is a drawback that a blocking phenomenon such as peeling and transfer occurs, which causes a problem not only in thermal transfer recording but also in magnetic recording.
【０００４】[0004]
【発明が解決しようとする課題】本発明は、上記事情に
鑑みてなされたもので、熱転写画像の高感度化、高濃度
化、画像均一化の向上を図るとともにブロッキング性を
改善した熱転写記録型磁気券紙を得ることを目的とす
る。SUMMARY OF THE INVENTION The present invention has been made in view of the above circumstances, and is a thermal transfer recording type in which the sensitivity and the density of a thermal transfer image are improved, the image uniformity is improved, and the blocking property is improved. The purpose is to obtain magnetic ticket paper.
【０００５】[0005]
【課題を解決するための手段】本発明によると、以下の
発明が提供される。
（１）支持体の一方の面に強磁性体とバインダーを主成
分とする磁気記録層を設け、もう一方の面にフィラーと
水溶性樹脂を主成分とするインク受理層を設けたもので
あって、前記フィラーは吸油量５０〜２００ｍｌ／１０
０ｇを有し、前記フィラー対前記水溶性樹脂の含有比
（固形分）を１：０．１〜０．２、形成されるインク受
理層にさらに耐水化剤を含有させ、平滑度を５００秒以
上とすることを特徴とする熱転写記録型磁気券紙。
（２）前記耐水化剤がホルムアルデヒド、グリオキザー
ル、クロムミョウバン、メラミン−ホルムアルデヒド樹
脂、ポリアミド樹脂、ポリアミド−エピクロルヒドリン
樹脂であることを特徴とする請求項１記載の熱転写記録
型磁気券紙。
（３）前記水溶性樹脂と耐水化剤の含有比（固形分）
を、１：０．３〜０．５とすることを特徴とする請求項
１又は２記載の熱転写記録型磁気券紙。According to the present invention, the following is provided.
An invention is provided.
(1) A ferromagnetic material and a binder are mainly formed on one surface of the support.
The magnetic recording layer is
It has an ink-receiving layer mainly composed of water-soluble resin.
And the filler has an oil absorption of 50 to 200 ml / 10.
0 g, the content ratio of the filler to the water-soluble resin
(Solid content) of 1: 0.1 to 0.2
RisaTo further contain a waterproofing agent, Smoothness less than 500 seconds
A thermal transfer recording type magnetic ticket paper characterized by the above.
(2)The water-proofing agent is formaldehyde or glyoxer
Le, chrome alum, melamine-formaldehyde tree
Fat, polyamide resin, polyamide-epichlorohydrin
The thermal transfer recording according to claim 1, which is a resin.
Type magnetic ticket paper.
(3) Content ratio of the water-soluble resin and the waterproofing agent (solid content)
Is set to 1: 0.3 to 0.5.
1Or 2The thermal transfer recording type magnetic ticket paper described.
【０００６】以下に本発明を詳細に説明する。本発明に
おいて、インク受理層に含有させるフィラーとしては、
例えば、炭酸カルシウム、シリカ、酸化チタン、水酸化
アルミニウム、クレー、焼成クレー、ケイ酸マグネシウ
ム、炭酸マグネシウム、ホワイトカーボン、酸化亜鉛、
硫酸バリウム、表面処理された炭酸カルシウムやシリ
カ、尿素−ホルマリン樹脂、スチレン／メタクリル酸共
重合体、ポリスチレン等の微粉末等で、吸油量５０〜２
００ｍｌ／１００ｇの範囲にあるものである。The present invention will be described in detail below. In the present invention, as the filler contained in the ink receiving layer,
For example, calcium carbonate, silica, titanium oxide, aluminum hydroxide, clay, calcined clay, magnesium silicate, magnesium carbonate, white carbon, zinc oxide,
Fine powder of barium sulfate, surface-treated calcium carbonate or silica, urea-formalin resin, styrene / methacrylic acid copolymer, polystyrene, etc., oil absorption 50 to 2
It is in the range of 00 ml / 100 g.
【０００７】また、インク受理層に用いる水溶性樹脂と
しては、慣用の種々の水溶性樹脂を適宜用いることがで
き、具体例として以下のものが挙げられる。ポリビニル
アルコール、デンプンおよびその誘導体、メトキシセル
ロース、ヒドロキシエチルセルロース、カルボキシメチ
ルセルロース、メチルセルロース、エチルセルロース等
のセルロース誘導体、ポリアクリル酸ソーダ、ポリビニ
ルピロリドン、アクリルアミド／アクリル酸エステル共
重合体、アクリルアミド／アクリル酸エステル／メタク
リル酸三元共重合体、スチレン／無水マレイン酸共重合
体アルカリ塩、イソブチレン／無水マレイン共重合体ア
ルカリ塩、ポリアクリルアミド、アルギン酸ソード、ゼ
ラチン、カゼイン等の水溶性高分子。As the water-soluble resin used for the ink receiving layer, various conventionally used water-soluble resins can be appropriately used, and specific examples include the following. Polyvinyl alcohol, starch and its derivatives, cellulose derivatives such as methoxycellulose, hydroxyethylcellulose, carboxymethylcellulose, methylcellulose, ethylcellulose, sodium polyacrylate, polyvinylpyrrolidone, acrylamide / acrylic acid ester copolymer, acrylamide / acrylic acid ester / methacrylic acid Water-soluble polymers such as ternary copolymers, styrene / maleic anhydride copolymer alkali salts, isobutylene / maleic anhydride copolymer alkali salts, polyacrylamides, alginate swords, gelatin, and casein.
【０００８】インク受理層における前記フィラーと水溶
性樹脂の割合はブロッキング性に関わり、フィラー対水
溶性樹脂の含有比（固形分）を１：０．１〜０．２とす
ることが好ましい。また、インク受理層に用いる耐水化
剤の具体例としては、例えば、ホルムアルデヒド、グリ
オキザール、クロムミョウバン、メラミン、メラミン−
ホルムアルデヒド樹脂、ポリアミド樹脂、ポリアミド−
エピクロルヒドリン樹脂等が挙げられる。この耐水化剤
と水溶性樹脂の割合もブロッキング性に関わり、その含
有比（固形分）は水溶性樹脂１に対して耐水化剤０．３
〜０．５が好ましい。このように本発明のインク受理層
はフィラーおよび水溶性樹脂を、また、さらに、水溶性
樹脂と耐水化剤を特定の比率で含有させて形成させる
が、さらに、インク受理層の表面をキャレンダーなどに
より平滑度５００秒以上に処理することにより、前記フ
ィラーによる効果に加えて印字品質を一層向上させるこ
とができる。The ratio of the filler to the water-soluble resin in the ink receiving layer is related to the blocking property, and the content ratio (solid content) of the filler to the water-soluble resin is preferably 1: 0.1 to 0.2. Specific examples of the waterproofing agent used in the ink receiving layer include formaldehyde, glyoxal, chrome alum, melamine, and melamine.
Formaldehyde resin, polyamide resin, polyamide-
Examples include epichlorohydrin resin. The ratio of the water-proofing agent and the water-soluble resin also relates to the blocking property, and the content ratio (solid content) is 0.3 to the water-proofing resin.
~ 0.5 is preferred. As described above, the ink-receiving layer of the present invention is formed by containing the filler and the water-soluble resin, and further containing the water-soluble resin and the water-proofing agent in a specific ratio. Further, the surface of the ink-receiving layer is calendered. By processing the smoothness to 500 seconds or more by the above method, the printing quality can be further improved in addition to the effect of the filler.
【０００９】本発明の磁気記録層に用いる磁性体として
は、バリウムフェライト、ストロンチウムフェライト、
Ｃｏ−γ−Ｆｅ2Ｏ3、γ−Ｆｅ2Ｏ3等の強磁性体粉が使
用される。また、磁性記録層に用いるバインダーとして
は、慣用の種々のものを使用でき、その具体例として
は、ポリビニルブチラール、ポリ酢酸ビニル、ポリプロ
ピオン酸ビニル、ポリ酪酸ビニル、ポリメチルアクリレ
ート、ポリエチルアクリレート、ポリプロピルアクリレ
ート、ポリブチルアクリレート、ポリヘプチルアクリレ
ート、ポリエチルヘキシルアクリレート、スチレン−ブ
タジエンゴム、ニトリルゴム、天然ゴム、ポリイソブチ
レンゴム、ポリブタジエン、ポリアクリロニトリル、ポ
リメタクリロニトリル、ポリ塩化ビニリデン、ポリジク
ロロスチレン、ポリスチレン、ポリ塩化ビニル、ポリメ
タクリル酸、ポリメチルメタクリレート、ポリエチルメ
タクリレート、ポリプロピルメタクリレート、ポリブチ
ルメタクリレート、ポリエチルヘキシルメタクリレー
ト、ポリビニルアルコール、ポリビニルステアレート等
の水性エマルジョン樹脂が挙げられる。The magnetic material used in the magnetic recording layer of the present invention includes barium ferrite, strontium ferrite,
Ferromagnetic powders such as Co-γ-Fe 2 O 3 and γ-Fe 2 O 3 are used. As the binder used in the magnetic recording layer, various conventional binders can be used, and specific examples thereof include polyvinyl butyral, polyvinyl acetate, vinyl polypropionate, polyvinyl butyrate, polymethyl acrylate, polyethyl acrylate, Polypropyl acrylate, polybutyl acrylate, polyheptyl acrylate, polyethylhexyl acrylate, styrene-butadiene rubber, nitrile rubber, natural rubber, polyisobutylene rubber, polybutadiene, polyacrylonitrile, polymethacrylonitrile, polyvinylidene chloride, polydichlorostyrene, polystyrene , Polyvinyl chloride, polymethacrylic acid, polymethylmethacrylate, polyethylmethacrylate, polypropylmethacrylate, polybutylmethacrylate, polyethyl Hexyl methacrylate, polyvinyl alcohol, an aqueous emulsion resin, such as polyvinyl stearate and the like.
【００１０】[0010]
【実施例】以下に、本発明を実施例によりさらに具体的
に説明する。なお、以下で示す部および％はいずれも重
量基準である。EXAMPLES The present invention will be described in more detail below with reference to examples. The parts and% shown below are based on weight.
【００１１】実施例１
坪量１５０ｇ／ｍ2の上質紙の片面に下記磁気塗料を乾
燥重量が５０ｇ／ｍ2となるように塗布乾燥し磁気記録
層を得た。
〈バリウムフェライト分散液の作製 固形分５０％〉
バリウムフェライト(保持力：2700Ｏｅ、平均粒径：0.6μｍ) １００部
ポリアクリル酸ソーダ（２０％水溶液） １０部
カーボンブラック（３８％分散液） ２０部
水 ９０部
以上の組成からなる液をサンドグライダーで２４ｈｒ．
分散して、下記エマルジョンと調合する。
〈磁気塗料の作製〉
バリウムフェライト分散液（５０％分散液） ２２０部
塩化ビニリデンエマルジョン（４９％） １００部
水 ８０部
次に、支持体のもう一方の面に下記インク受理層形成液
を乾燥重量が５．０ｇ／ｍ2となるように塗布し、イン
ク受理層を設けた。
〈インク受理層形成液の作製〉
炭酸カルシウム（吸油量５０ｍｌ／１００ｇ） １００部
ポリビニルアルコール（１０％水溶液） ２００部
水 ５００部
次いで、このインク受理層表面を平滑度５００ｓｅｃと
なるようにキャレンダー処理を行ない熱転写記録型磁気
券紙を得た。Example 1 A magnetic recording layer was obtained by coating and drying the following magnetic paint on one side of a high-quality paper having a basis weight of 150 g / m 2 so that the dry weight was 50 g / m 2 . <Preparation of Barium Ferrite Dispersion Solid Content 50%> Barium ferrite (retention: 2700 Oe, average particle size: 0.6 μm) 100 parts Sodium polyacrylate (20% aqueous solution) 10 parts Carbon black (38% dispersion) 20 parts A solution consisting of 90 parts or more of water is used for 24 hours with a sand glider.
Disperse and blend with the following emulsion. <Preparation of magnetic paint> Barium ferrite dispersion liquid (50% dispersion liquid) 220 parts Vinylidene chloride emulsion (49%) 100 parts Water 80 parts Next, the following ink receiving layer forming liquid is dried on the other surface of the support. To be 5.0 g / m 2 to provide an ink receiving layer. <Preparation of Ink Receptive Layer Forming Liquid> Calcium carbonate (oil absorption 50 ml / 100 g) 100 parts Polyvinyl alcohol (10% aqueous solution) 200 parts Water 500 parts Next, the surface of this ink receiving layer is calendered so as to have a smoothness of 500 sec. Then, a thermal transfer recording type magnetic ticket paper was obtained.
【００１２】実施例２
インク受理層のフィラーとして吸油量１００ｍｌ／１０
０ｇのシリカを用いた以外は実施例１と同様にして熱転
写記録型磁気券紙を得た。Example 2 Oil absorption of 100 ml / 10 as a filler for the ink receiving layer
A thermal transfer recording type magnetic ticket paper was obtained in the same manner as in Example 1 except that 0 g of silica was used.
【００１３】実施例３
インク受理層のフィラーとして吸油量２００ｍｌ／１０
０ｇのシリカを用いた以外は実施例１と同様にして熱転
写記録型磁気券紙を得た。Example 3 200 ml / 10 oil absorption as a filler for the ink receiving layer
A thermal transfer recording type magnetic ticket paper was obtained in the same manner as in Example 1 except that 0 g of silica was used.
【００１４】実施例４
インク受理層の平滑度１０００ｓｅｃとなるようにキャ
レンダー処理を行なった以外は実施例１と同様にして熱
転写記録型磁気券紙を得た。Example 4 A thermal transfer recording type magnetic ticket paper was obtained in the same manner as in Example 1 except that the calendering treatment was carried out so that the smoothness of the ink receiving layer was 1000 sec.
【００１５】実施例５
インク受理層形成液の処方を下記のようにした以外は実
施例１と同様にして熱転写記録型磁気券紙を得た。
〈インク受理形成液の作製〉
シリカ（吸油量５０ｍｌ／１００ｇ） １００部
ポリビニルアルコール（１０％水溶液） ２００部
ポリアミドエピクロルヒドリン ６０部
水 ４４０部Example 5 A thermal transfer recording type magnetic ticket paper was obtained in the same manner as in Example 1 except that the formulation of the ink receiving layer forming liquid was changed as follows. <Preparation of Ink Receiving and Forming Liquid> Silica (oil absorption 50 ml / 100 g) 100 parts Polyvinyl alcohol (10% aqueous solution) 200 parts Polyamide epichlorohydrin 60 parts Water 440 parts
【００１６】比較例１
インク受理層のフィラーとして吸油量２０ｍｌ／１００
ｇの炭酸カルシウムを用いた以外は実施例１と同様にし
て熱転写記録型磁気券紙を得た。Comparative Example 1 Oil absorption amount of 20 ml / 100 as a filler for the ink receiving layer
A thermal transfer recording type magnetic ticket paper was obtained in the same manner as in Example 1 except that g of calcium carbonate was used.
【００１７】比較例２
インク受理層のフィラーとして吸油量３００ｍｌ／１０
０ｇのシリカを用いた以外は実施例１と同様にして熱転
写記録型磁気券紙を得た。Comparative Example 2 Oil absorption of 300 ml / 10 as a filler for the ink receiving layer
A thermal transfer recording type magnetic ticket paper was obtained in the same manner as in Example 1 except that 0 g of silica was used.
【００１８】比較例３
インク受理層形成液の処方を下記のようにした以外は実
施例１と同様にして熱転写記録型磁気券紙を得た。
〈インク受理形成液の作製〉
シリカ（吸油量５０ｍｌ／１００ｇ） １００部
ポリビニルアルコール（１０％水溶液） ３００部
水 ４００部Comparative Example 3 A thermal transfer recording type magnetic ticket paper was obtained in the same manner as in Example 1 except that the formulation of the ink receiving layer forming liquid was changed as follows. <Preparation of ink receiving and forming liquid> Silica (oil absorption 50 ml / 100 g) 100 parts Polyvinyl alcohol (10% aqueous solution) 300 parts Water 400 parts
【００１９】比較例４
インク受理層形成液の処方を下記のようにした以外は実
施例１と同様にして熱転写記録型磁気券紙を得た。
シリカ（吸油量５０ｍｌ／１００ｇ） １００部
ポリビニルアルコール（１０％水溶液） ４００部
水 ３００部Comparative Example 4 A thermal transfer recording type magnetic ticket paper was obtained in the same manner as in Example 1 except that the formulation of the ink receiving layer forming liquid was changed as follows. Silica (oil absorption 50 ml / 100 g) 100 parts Polyvinyl alcohol (10% aqueous solution) 400 parts Water 300 parts
【００２０】比較例５
インク受理層の平滑度２００ｓｅｃとなるようにキャレ
ンダー処理を行なった以外は実施例１と同様にして熱転
写記録型磁気券紙を得た。Comparative Example 5 A thermal transfer recording type magnetic ticket paper was obtained in the same manner as in Example 1 except that the calendering treatment was performed so that the smoothness of the ink receiving layer was 200 sec.
【００２１】比較例６
インク受理層を設けない以外は実施例１と同様にして熱
転写記録型磁気券紙を得た。Comparative Example 6 A thermal transfer recording type magnetic ticket paper was obtained in the same manner as in Example 1 except that the ink receiving layer was not provided.
【００２２】上記のようにして得た実施例および比較例
の熱転写記録型磁気券紙について画像印字品質（画像濃
度、画像均一性、細線ニジミ）およびブロッキング性の
評価を行なった。その結果を表１に示す。
〈熱転写印字試験〉
プリンタ ：ＴＥＣ製Ｂ−３０
リボン ：バイロット製ＡＴ−００３
サーマルヘッド：ＴＥＣ製（５１０Ω）
印字速度 ：２ｉｎ／ｓｅｃ
画像濃度 ：マクベス反射濃度計Ｒ−９１４型、Ｗ
−１０６フィルター使用
〈ブロッキング試験〉試料の磁気記録層表面とインク受
理層表面を重ね合わせ、０．５ｋｇ／ｃｍ2の圧力をか
けた状態で、４０℃、９０％ＲＨ環境下に１０時間放置
した後、重ね合わせ面を指で剥がしブロッキング状態を
観察する。Image printing quality (image density, image uniformity, fine line blurring) and blocking property were evaluated for the thermal transfer recording type magnetic ticket papers of the examples and comparative examples obtained as described above. The results are shown in Table 1. <Thermal transfer printing test> Printer: TEC B-30 ribbon: Bylot AT-003 Thermal head: TEC (510Ω) Printing speed: 2 in / sec Image density: Macbeth reflection densitometer R-914 type, W
-106 filter used <Blocking test> The surface of the magnetic recording layer of the sample and the surface of the ink receiving layer were superposed, and left under a pressure of 0.5 kg / cm 2 for 10 hours at 40 ° C. and 90% RH environment. After that, the overlapping surface is peeled off with a finger and the blocking state is observed.
【００２３】[0023]
【表１】 表中の各評価ランクは以下の通りである。 〈画像均一性〉 ○：濃度のバラツキがなく画像が均一である △：濃度のバラツキが若干ある ×：濃度のバラツキが激しい 〈細線ニジミ〉 ○：細線のニジミがなく鮮明である △：細線のニジミはあるが判読である ×：細線のニジミが強く判読できない 〈ブロッキング性〉 ○：剥がすときハクリ音がなく転写もない △：剥がすときやや剥離音はあるが転写はない ×：剥がすとき層転写する[Table 1] Each evaluation rank in the table is as follows. <Image uniformity> ○: The image is uniform without variations in density Δ: There is a slight variation in density ×: The variation in density is severe <Thin line bleeding> ○: Clear without fine line bleeding △: Fine line There is bleeding, but it is legible. ×: Thin line bleeding is not strongly readable. <Blocking property> ○: No peeling noise and no transfer when peeled. Do
【００２４】表１から明らかなように、インク受理層に
含有させるフィラーの吸油量、フィラー対水溶性樹脂の
比率、インク受理層表面の平滑度を特定の範囲に限定し
た実施例のものは、感度および画像濃度が高く、さら
に、画像均一性、細線ニジミなどの印字品質に優れるだ
けでなく良好なブロッキング性が得られる。また、イン
ク受理層にさらに耐水化剤を添加した場合はブロッキン
グ防止性を一層向上させることができる。As is clear from Table 1, the examples in which the oil absorption of the filler contained in the ink receiving layer, the ratio of the filler to the water-soluble resin, and the smoothness of the surface of the ink receiving layer are limited to specific ranges are as follows: The sensitivity and the image density are high, and further, not only the image uniformity and the printing quality such as thin line blurring are excellent, but also the good blocking property is obtained. Further, when a waterproofing agent is further added to the ink receiving layer, the antiblocking property can be further improved.
【００２５】[0025]
【発明の効果】以上のように、本発明によれば、感度、
濃度、画像均一性、細線ニジミなど印字品質に優れると
ともにブロッキング性の良好な熱転写記録型磁気券紙が
得られる。As described above, according to the present invention, the sensitivity,
It is possible to obtain a thermal transfer recording type magnetic ticket paper which is excellent in printing quality such as density, image uniformity and fine line blurring and has good blocking property.
【図１】本発明に係る熱転写記録型磁気券紙の層構成を
示す説明図である。FIG. 1 is an explanatory view showing a layer structure of a thermal transfer recording type magnetic ticket paper according to the present invention.
１ 支持体 ２ 磁気層 ３ インク受理層 1 support 2 magnetic layer 3 Ink receiving layer
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平３−274191（ＪＰ，Ａ) 特開 平１−221282（ＪＰ，Ａ) 特開 平２−88293（ＪＰ，Ａ) 特開 平３−275386（ＪＰ，Ａ) 特開 平４−70389（ＪＰ，Ａ) 特開 平２−3394（ＪＰ，Ａ) 特開 平６−8659（ＪＰ，Ａ) 特開 昭62−257888（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) B41M 5/38 - 5/40 B41D 15/10 G11B 5/735,5/80 ─────────────────────────────────────────────────── ─── Continuation of the front page (56) References JP-A-3-274191 (JP, A) JP-A 1-2221282 (JP, A) JP-A 2-88293 (JP, A) JP-A-3- 275386 (JP, A) JP 4-70389 (JP, A) JP 2-3394 (JP, A) JP 6-8659 (JP, A) JP 62-257888 (JP, A) (58) Fields investigated (Int.Cl. 7 , DB name) B41M 5/38-5/40 B41D 15/10 G11B 5/735, 5/80
Claims (3)
ーを主成分とする磁気記録層を設け、もう一方の面にフ
ィラーと水溶性樹脂を主成分とするインク受理層を設け
たものであって、前記フィラーは吸油量５０〜２００ｍ
ｌ／１００ｇを有し、前記フィラー対前記水溶性樹脂の
含有比（固形分）を１：０．１〜０．２、形成されるイ
ンク受理層にさらに耐水化剤を含有させ、平滑度を５０
０秒以上とすることを特徴とする熱転写記録型磁気券
紙。1. A support having a magnetic recording layer containing a ferromagnetic material and a binder as main components on one surface of the support, and an ink receiving layer containing a filler and a water-soluble resin as the main components on the other surface. And the filler has an oil absorption of 50 to 200 m.
1/100 g, the content ratio (solid content) of the filler to the water-soluble resin is 1: 0.1 to 0.2, and a water-proofing agent is further contained in the formed ink-receiving layer to improve smoothness. Fifty
A thermal transfer recording type magnetic ticket paper characterized by being set to 0 second or more.
オキザール、クロムミョウバン、メラミン−ホルムアル
デヒド樹脂、ポリアミド樹脂、ポリアミド−エピクロル
ヒドリン樹脂であることを特徴とする請求項１記載の熱
転写記録型磁気券紙。 2. The water resistant agent is formaldehyde or green.
Oxal, chrome alum, melamine-formal
Dehydrate resin, polyamide resin, polyamide-epichloro
Heat according to claim 1, characterized in that it is a hydrin resin.
Transfer recording type magnetic ticket paper.
分）を、１：０．３〜０．５とすることを特徴とする請
求項１又は２記載の熱転写記録型磁気券紙。3. A content ratio of the water-soluble resin and water-resistant agent (solid content), 1: thermal transfer recording magnetic ticket according to claim 1 or 2, characterized in that 0.3 to 0.5 paper.