JP2000185958A - Fluidity regulation of cement concrete containing high- performance water-reducing agent - Google Patents
Fluidity regulation of cement concrete containing high- performance water-reducing agentInfo
- Publication number
- JP2000185958A JP2000185958A JP36220598A JP36220598A JP2000185958A JP 2000185958 A JP2000185958 A JP 2000185958A JP 36220598 A JP36220598 A JP 36220598A JP 36220598 A JP36220598 A JP 36220598A JP 2000185958 A JP2000185958 A JP 2000185958A
- Authority
- JP
- Japan
- Prior art keywords
- reducing agent
- cement concrete
- fluidity
- cement
- metal salt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、一般土木工事、建
築工事に使用されるセメントペースト、モルタル又はコ
ンクリートに使用される高性能減水剤含有セメントコン
クリートの流動性調整方法に関する。本発明では、セメ
ントペースト、モルタル、及びコンクリートを総称して
セメントコンクリートという。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for adjusting the fluidity of a cement concrete containing a high-performance water-reducing agent used for cement paste, mortar or concrete used in general civil works and building works. In the present invention, cement paste, mortar, and concrete are collectively referred to as cement concrete.
【０００２】[0002]
【従来の技術とその課題】従来のセメントコンクリート
では、水／セメント比を低下し、硬化体の強度性状や耐
久性状を向上させるために、多くの場合高性能減水剤を
使用している。高性能減水剤は、セメントコンクリート
の流動性を向上し、施工を容易にするものである。セメ
ントコンクリートの施工性にとっては、混練直後の流動
性をいかに必要時間保持することができるかが問題であ
り、流動性の保持能力に優れた高性能減水剤が必要とさ
れている。2. Description of the Related Art In conventional cement concrete, a high-performance water reducing agent is used in many cases in order to lower the water / cement ratio and to improve the strength and durability of the cured product. The high-performance water reducing agent improves the fluidity of cement concrete and facilitates construction. For the workability of cement concrete, how to maintain the fluidity immediately after kneading for a required time is a problem, and a high-performance water reducing agent having excellent fluidity retention ability is required.
【０００３】また、注入モルタルや高流動コンクリート
などに見られるように、自己充填性に優れた材料・技術
の開発においても流動性の保持能力が大きいことも必要
とされている。しかしながら、流動性が保たれたセメン
トコンクリートは傾斜のある現場に打設した場合はダレ
を生じることになり、そのような現場には流動性のある
ことが逆に不向きであった。[0003] In addition, as in the case of pouring mortar, high-fluidity concrete, etc., it is required that the ability to retain fluidity is large even in the development of materials and techniques excellent in self-filling properties. However, when the cement concrete with the fluidity is cast on a sloped site, it will sag, and the fluidity is not suitable for such a site.
【０００４】また、ＮＡＴＭ工法等に用いられる吹付材
料においては、セメントコンクリートをポンプ圧送する
ときには流動性が求められるが、リバウンドを低減させ
るためには粘性がある方が好ましい。[0004] Spraying materials used in the NATM method or the like require fluidity when pumping cement concrete. However, in order to reduce rebound, a viscous material is preferable.
【０００５】さらに、建築構造物の耐震補強の一つであ
る鉄骨の周辺にグラウト材を注入するブレース工法には
注入モルタルが使用され、注入には流動性が求められる
が、注入後は粘性を付与させた方が自重圧を緩和する方
向になるので、打設したモルタルの型枠からの漏れを防
ぐことができるため好ましい。即ち、流動性が保たれる
セメントコンクリートが求められる一方で、流動性を自
由に制御する技術も必要とされるようになってきた。[0005] In addition, injecting mortar is used in the bracing method for injecting grout material around the steel frame, which is one of the seismic reinforcement of building structures, and the pouring is required to have fluidity. It is preferable that the applied mortar is applied in a direction in which the weight of the mortar is reduced, so that leakage of the poured mortar from the mold can be prevented. That is, while cement concrete that maintains fluidity is required, a technique for freely controlling fluidity has also been required.
【０００６】本発明者は高性能減水剤の持つセメントな
どの分散作用が金属塩によって瞬時に損なわれ、流動性
を失うことを見いだし、本発明を完成するに至った。The present inventor has found that the dispersing action of cement and the like possessed by the high-performance water reducing agent is instantaneously impaired by the metal salt and loses fluidity, and has completed the present invention.
【０００７】[0007]
【課題を解決するための手段】即ち、本発明は、高性能
減水剤を含有するセメントコンクリートに、アルカリ金
属塩を添加する高性能減水剤含有セメントコンクリート
の流動性調整方法であり、高性能減水剤が、ナフタレン
スルホン酸系減水剤、メラミンスルホン酸系減水剤、及
びポリカルボン酸系減水剤からなる群より選ばれた一種
又は二種以上である該高性能減水剤含有セメントコンク
リートの流動性調整方法であり、アルカリ金属塩が、リ
チウム、カリウム、及びナトリウム等のアルカリ金属の
炭酸塩又は硫酸塩である該高性能減水剤含有セメントコ
ンクリートの流動性調整方法である。That is, the present invention relates to a method for adjusting the fluidity of a cement concrete containing a high performance water reducing agent by adding an alkali metal salt to a cement concrete containing a high performance water reducing agent. The fluidity adjustment of the high-performance water-reducing agent-containing cement concrete, wherein the agent is one or more selected from the group consisting of a naphthalenesulfonic acid-based water reducing agent, a melaminesulfonic acid-based water reducing agent, and a polycarboxylic acid-based water reducing agent. A method of adjusting the fluidity of the cement concrete containing a high-performance water reducing agent, wherein the alkali metal salt is a carbonate or sulfate of an alkali metal such as lithium, potassium and sodium.
【０００８】以下、本発明を詳細に説明する。Hereinafter, the present invention will be described in detail.
【０００９】本発明で使用するセメントとしては、普通
や早強などの各種ポルトランドセメント、これらポルト
ランドセメントに高炉スラグ又はフライアッシュなどを
混合した各種混合セメント、白色セメント、及び高ビー
ライトセメント等、ＪＩＳに規定されたセメントの他、
ポルトランドセメントに膨張材を加えた膨張セメント
や、超速硬セメント、特殊セメントも使用可能であり、
特にその種類は限定されるものではない。The cement used in the present invention includes various portland cements such as ordinary and early strength, various mixed cements obtained by mixing blast furnace slag or fly ash with these portland cements, white cements, high belite cements and the like. In addition to the cement specified in
Expandable cement made by adding expander to Portland cement, ultra-rapid hardening cement, and special cement can also be used.
In particular, the type is not limited.
【００１０】また、本発明では、ポルトランドセメント
に各種セメント混和材を併用することも可能である。こ
こで、セメント混和材としては、各種急結材、急硬混和
材、及び高強度混和材等モルタルやコンクリートを高性
能化させる混和材も同様に使用可能である。また、ＪＩ
Ｓで規定する以上の高炉スラグやフライアッシュなどを
混合することも可能である。In the present invention, various cement admixtures can be used in combination with Portland cement. Here, as the cement admixture, various quick-setting admixtures, quick-hardening admixtures, and admixtures for improving the performance of mortar and concrete such as high-strength admixtures can also be used. Also, JI
It is also possible to mix blast furnace slag, fly ash, and the like that are more than specified in S.
【００１１】さらに、本発明では、セメントコンクリー
トの流動性を高めるために石灰石微粉を併用することも
可能である。石灰石微粉の併用は、セメントコンクリー
トの流動性を高めることにより、後述の減水剤と金属塩
の使用量を低減できるので好ましい。Further, in the present invention, it is possible to use limestone fine powder in combination to enhance the fluidity of cement concrete. The combined use of limestone fine powder is preferred because the flowability of cement concrete can be increased to reduce the amounts of the water reducing agent and metal salt described below.
【００１２】本発明で使用する高性能減水剤としては、
ナフタレンスルホン酸系減水剤、メラミンスルホン酸系
減水剤、及びポリカルボン酸系減水剤等が使用可能であ
り、その構造は特に限定されるものではなく、市販のも
のも使用可能である。高性能減水剤は、粉末状のもの液
体状のものいずれも使用可能である。本発明における高
性能減水剤の使用量は、一般工事に用いられている量が
使用可能であり、通常、セメント100重量部に対して、
0.1〜5.0重量部％である。The high-performance water reducing agent used in the present invention includes:
A naphthalene sulfonic acid-based water reducing agent, a melamine sulfonic acid-based water reducing agent, a polycarboxylic acid-based water reducing agent, and the like can be used, and the structure thereof is not particularly limited, and a commercially available product can also be used. As the high-performance water reducing agent, any of a powder type and a liquid type can be used. The amount of the high-performance water reducing agent used in the present invention, the amount used for general construction can be used, usually, 100 parts by weight of cement,
0.1 to 5.0 parts by weight.
【００１３】本発明のセメントコンクリートは通常使用
されるものが使用可能であり、その混練方法は特に限定
されるものではない。例えば、生コンプラント、バッチ
ミキサー、ハンドミキサー、及び連続練りミキサー等、
通常使用されるミキサーが使用可能であり、材料の投入
順序等も特に限定されるものではない。As the cement concrete of the present invention, those which are usually used can be used, and the kneading method is not particularly limited. For example, raw plant, batch mixer, hand mixer, and continuous kneading mixer,
A commonly used mixer can be used, and the order of charging the materials is not particularly limited.
【００１４】本発明で使用するアルカリ金属塩（以下、
金属塩という）とは、リチウム、ナトリウム、及びカリ
ウム等のアルカリ金属の炭酸塩又は硫酸塩であり、粉末
状又は水溶液状で使用可能である。金属塩の使用量は、
セメント100重量部に対して、0.1重量部以上が好まし
く、0.3〜10重量部がより好ましい。0.1重量部未満では
流動性の急激な低下がない場合がある。本発明において
金属塩は、あらかじめ混練したセメントコンクリートに
投入しする後添加する方法が必要であり、金属塩の添加
量や添加位置を変化させることで任意に流動性を低下す
ることが可能である。The alkali metal salt used in the present invention (hereinafter referred to as "the alkali metal salt")
The term “metal salt” refers to a carbonate or sulfate of an alkali metal such as lithium, sodium, and potassium, and can be used in the form of a powder or an aqueous solution. The amount of metal salt used is
0.1 part by weight or more is preferable with respect to 100 parts by weight of cement, and 0.3 to 10 parts by weight is more preferable. If the amount is less than 0.1 part by weight, there may be no rapid decrease in fluidity. In the present invention, the metal salt needs to be added to the cement concrete that has been previously kneaded and then added, and the fluidity can be arbitrarily reduced by changing the amount and position of the metal salt. .
【００１５】金属塩の添加方法は、例えば、連続練りミ
キサーの場合には排出口付近で、また、ポンプ圧送の場
合はホース先端近くで添加する方法が可能である。As a method of adding the metal salt, for example, in the case of a continuous kneading mixer, it is possible to add the metal salt in the vicinity of the outlet, and in the case of pumping, near the end of the hose.
【００１６】本発明法において、傾斜のある構造物へ打
設する場合、打設上面近くまでは、通常の高流動コンク
リートを使用し、バッチミキサー等を用いて現場で金属
塩を添加したセメントコンクリートをその上に打設する
方法が可能である。その他、ブレース工法や吹付工法な
どにも使用可能である。In the method of the present invention, when casting on a sloped structure, ordinary high-fluidity concrete is used up to near the casting upper surface, and cement concrete added with a metal salt on site using a batch mixer or the like. Can be cast on it. In addition, it can be used for a brace method, a spray method, and the like.
【００１７】[0017]
【実施例】以下、実験例に基づいて本発明をさらに説明
する。The present invention will be further described below based on experimental examples.
【００１８】実験例１ホバートミキサーを用いて混練し
た表１に示す配合のセメントペーストに、表１に示すよ
うに金属塩を添加し、その後60秒間再混練し、その流動
性の変化をフローによって測定した。結果を表１に併記
する。Experimental Example 1 A metal salt was added as shown in Table 1 to a cement paste having the composition shown in Table 1 and kneaded using a Hobart mixer, and then re-kneaded for 60 seconds. It was measured. The results are also shown in Table 1.
【００１９】＜使用材料＞ セメント ：普通ポルトランドセメント、市販品、比重
3.15 石灰石微粉；ブレーン値3,500cm2/g、比重2.70 減水剤Ａ ：高性能減水剤、ポリカルボン酸系減水剤、
市販品 減水剤Ｂ ：高性能減水剤、ナフタレンスルホン酸系減
水剤、市販品 金属塩ａ ：炭酸ナトリウム、試薬１級 金属塩ｂ ：炭酸リチウム、試薬１級<Material used> Cement: ordinary Portland cement, commercial product, specific gravity
3.15 Limestone fine powder; Blaine value 3,500cm 2 / g, specific gravity 2.70 Water reducing agent A: High performance water reducing agent, polycarboxylic acid type water reducing agent,
Commercially available water reducing agent B: High-performance water reducing agent, naphthalenesulfonic acid-based water reducing agent, commercially available metal salt a: sodium carbonate, reagent grade 1 metal salt b: lithium carbonate, reagent grade 1
【００２０】＜測定方法＞ フロー ：上直径70mm、下直径100mm、及び高さ60mmのJ
IS R 5201「セメントの物理試験方法 10.(5)」に記され
るフローコーンを使用し、コーンを引き上げた時のセメ
ントペーストの広がり幅<Measurement method> Flow: J with upper diameter of 70 mm, lower diameter of 100 mm, and height of 60 mm
Using the flow cone described in IS R 5201 “Physical test method of cement 10. (5)”, the spread width of the cement paste when the cone is pulled up
【００２１】[0021]
【表１】 [Table 1]
【００２２】実験例２ 表２に示す配合を用い、スランプフロー650mm、S/a70
％、セメントの単位量450kg/m3、及び石灰石微粉の単位
量100kg/m3で高流動コンクリートを山中式ジェットミキ
サーで混練した。10分経過した後金属塩ａを添加して30
秒再混練し、そのスランプフローを測定した。結果を表
２に併記する。Experimental Example 2 Using the composition shown in Table 2, slump flow 650 mm, S / a70
%, A unit amount of cement of 450 kg / m 3 and a unit amount of limestone fine powder of 100 kg / m 3 were kneaded with a Yamanaka jet mixer. After 10 minutes, add metal salt a and add 30
After re-kneading for 2 seconds, the slump flow was measured. The results are also shown in Table 2.
【００２３】＜使用材料＞ 細骨材 ；新潟県姫川水系、比重2.62 粗骨材 ；新潟県姫川水系、比重2.66<Materials> Fine aggregate: Himekawa water system, Niigata prefecture, specific gravity 2.62 Coarse aggregate: Himekawa water system, Niigata prefecture, specific gravity 2.66
【００２４】＜測定方法＞ スランプフロー：JSCE-F503 に準じ測定<Measurement method> Slump flow: Measured according to JSCE-F503
【００２５】[0025]
【表２】 [Table 2]
【００２６】[0026]
【発明の効果】以上のように、本発明の方法によれば、
セメントコンクリートの流動性を急激に低下させること
ができるようになり、傾斜のある打設現場に打設する場
合等でダレを生じさせずに施工できるようになった。ま
た、本発明法は、流動性のあるセメントコンクリートの
搬送性を損なわず、打設直後には流動性を失わせた方が
よい場合に非常に有効な方法である。そして、本発明に
よれば、金属塩を添加する前のセメントコンクリートの
流動性を高めることができるのでポンプ圧送等が可能で
あり、打設直前に金属塩を添加することによって、セメ
ントコンクリートの流動性を急激に低下させることがで
きる。さらに、本発明は擬凝結に似た状況を生じさせる
ので、早期にこて仕上げを行うことが可能となり、工期
の短縮も実現できるなどの効果を奏する。As described above, according to the method of the present invention,
The fluidity of the cement concrete can be rapidly reduced, and the concrete can be cast without causing sagging, for example, when casting at an inclined casting site. In addition, the method of the present invention is a very effective method in a case where it is better to lose the fluidity immediately after casting without impairing the transportability of the fluid cement concrete. According to the present invention, the fluidity of the cement concrete before the addition of the metal salt can be increased, so that pumping or the like can be performed, and by adding the metal salt immediately before casting, the flow of the cement concrete can be improved. Properties can be sharply reduced. Further, the present invention produces a situation similar to pseudo-condensation, so that it is possible to perform ironing at an early stage, and it is possible to shorten the construction period.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｃ０４Ｂ 24:30 22:10 22:14） 103:32 103:44 111:70 (72)発明者 安藤 哲也 東京都千代田区有楽町１丁目４番１号 電 気化学工業株式会社内 (72)発明者 入内島 克明 東京都千代田区有楽町１丁目４番１号 電 気化学工業株式会社内 Ｆターム(参考） 4G012 MB06 MB12 PA10 PB08 PB10 PB24 PC08 PC11 4G056 AA08 ──────────────────────────────────────────────────の Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) C04B 24:30 22:10 22:14) 103: 32 103: 44 111: 70 (72) Inventor Tetsuya Ando 1-4-1 Yurakucho, Chiyoda-ku, Tokyo Electrochemical Industry Co., Ltd. (72) Katsuaki Iriuchijima 4-4-1 Yurakucho, Chiyoda-ku, Tokyo F-term (reference) 4G012 MB06 MB12 PA10 PB08 PB10 PB24 PC08 PC11 4G056 AA08
Claims (3)
リートに、アルカリ金属塩を添加することを特徴とする
高性能減水剤含有セメントコンクリートの流動性調整方
法。1. A method for adjusting the fluidity of a cement concrete containing a high-performance water reducing agent, comprising adding an alkali metal salt to cement concrete containing the high-performance water reducing agent.
系減水剤、メラミンスルホン酸系減水剤、及びポリカル
ボン酸系減水剤からなる群より選ばれた一種又は二種以
上であることを特徴とする請求項１記載の高性能減水剤
含有セメントコンクリートの流動性調整方法。2. The high-performance water reducing agent is one or more selected from the group consisting of a naphthalenesulfonic acid-based water reducing agent, a melaminesulfonic acid-based water reducing agent, and a polycarboxylic acid-based water reducing agent. The method for adjusting the fluidity of a cement concrete containing a high-performance water reducing agent according to claim 1.
又は硫酸塩であることを特徴とする請求項１又は請求項
２記載の高性能減水剤含有セメントコンクリートの流動
性調整方法。3. The method for adjusting the fluidity of a cement concrete containing a high-performance water reducing agent according to claim 1, wherein the alkali metal salt is an alkali metal carbonate or sulfate.