JP2000152982A - Deodorizing filter and air conditioner - Google Patents
Deodorizing filter and air conditionerInfo
- Publication number
- JP2000152982A JP2000152982A JP10329476A JP32947698A JP2000152982A JP 2000152982 A JP2000152982 A JP 2000152982A JP 10329476 A JP10329476 A JP 10329476A JP 32947698 A JP32947698 A JP 32947698A JP 2000152982 A JP2000152982 A JP 2000152982A
- Authority
- JP
- Japan
- Prior art keywords
- apatite
- honeycomb
- deodorizing filter
- deodorizing
- filter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、消臭性フィルタ及
びそれを備えた空気調和機に関するものである。The present invention relates to a deodorizing filter and an air conditioner provided with the same.
【０００２】[0002]
【従来の技術】近年の気密性の高い家屋では、特に室内
に臭いがこもりやすく、室内で発生するたばこ臭や生活
臭（汗、生ゴミ、調理、ペット等）を取り除きたいとい
う要望が強まっている。特に、たばこ臭はたばこを吸わ
ない回りの人に不快感を与え、迷惑となるだけでなく、
たばこ臭に含まれる有害成分は生理的にも悪影響を及ぼ
すことが問題となっている。2. Description of the Related Art In recent years, in highly airtight houses, odors are particularly likely to be trapped in the room, and there is a growing demand for removing tobacco odor and living odor (sweat, garbage, cooking, pets, etc.) generated in the room. I have. In particular, the tobacco smell not only disturbs the people around you who do not smoke, and is not only annoying,
The problem is that harmful components contained in tobacco smell have a physiologically adverse effect.
【０００３】この要望に応えるため、脱臭・消臭の機能
を取り入れた空気調和機が開発されている。消臭方式と
しては、活性炭フィルタによる悪臭の吸着、光触媒酸
化、オゾン酸化によるものが多い。To meet this demand, air conditioners incorporating deodorizing and deodorizing functions have been developed. As a deodorizing method, there are many methods using adsorption of an odor by an activated carbon filter, photocatalytic oxidation, and ozone oxidation.
【０００４】また、近年人工酵素である遷移金属キレー
ト化合物をレーヨン遷移等に担持させて酸化触媒として
用い、臭気成分を分解する方法が「工業材料」１９９１
年１０月号等に提案されている。In recent years, a method of decomposing odor components by using a transition metal chelate compound, which is an artificial enzyme, on a rayon transition or the like and using it as an oxidation catalyst is described in "Industrial Materials" 1991
It is proposed in the October issue.
【０００５】この方法は、悪臭物質に含まれる移動性水
素を遷移金属化合物を触媒として脱水素酸化し、二量
化、水溶性化、不揮発化させることにより消臭を可能と
している。遷移金属キレート化合物の中でも、オクタカ
ルボキシ鉄（III）フタロシアニンは、酸素と水の存在
下で硫化水素やメルカプタンを分解してジサルファイド
類に変化させる。また、分子内のカルボキシル基により
アンモニア等の塩基性ガスをイオン結合で化学吸着させ
て除去することができる。According to this method, mobile hydrogen contained in a malodorous substance is dehydrogenated and oxidized by using a transition metal compound as a catalyst to make it dimerizable, water-soluble, and non-volatile, thereby enabling deodorization. Among the transition metal chelate compounds, octacarboxyiron (III) phthalocyanine decomposes hydrogen sulfide and mercaptan in the presence of oxygen and water to change to disulfides. In addition, a basic gas such as ammonia can be chemically adsorbed and removed by ionic bonding with a carboxyl group in the molecule.
【０００６】[0006]
【発明が解決しようとする課題】活性炭は、１０〜２０
オングストロームの無数の穴のあいた無極性の多孔質体
で、ほとんどの臭気性ガスに対して極めて優れた吸着性
を有する材料である。しかしながら、硫黄化合物、アル
デヒド類、低級脂肪酸に対する吸着性が低い。たばこの
臭気には、アセトアルデヒド、低級脂肪酸、アンモニ
ア、低級アミン、炭化水素、硫化水素、等が含まれてい
るが、特に活性炭の吸着性が弱いアセトアルデヒドや低
級脂肪酸の割合が高い。このため、活性炭によってたば
この臭気を除去することが困難であった。Activated carbon is 10-20
It is a non-polar porous material with countless holes in Angstrom, and has a very good adsorption property to most odorous gases. However, the adsorptivity to sulfur compounds, aldehydes, and lower fatty acids is low. The odor of tobacco contains acetaldehyde, lower fatty acids, ammonia, lower amines, hydrocarbons, hydrogen sulfide, and the like, and particularly, the ratio of acetaldehyde and lower fatty acids, which have low adsorptivity of activated carbon, is high. For this reason, it was difficult to remove the odor of tobacco using activated carbon.
【０００７】また、活性炭の悪臭分子に対する吸着量に
は限界があり、そのため活性炭フィルタによる脱臭効果
はおのずと一時的なものとなる。しかも、活性炭に吸着
された悪臭分子は平衡によって脱離して放出されるとい
う問題がある。Also, the amount of activated carbon adsorbed on malodorous molecules is limited, so that the deodorizing effect of the activated carbon filter is naturally temporary. In addition, there is a problem that the malodorous molecules adsorbed on the activated carbon are desorbed and released by equilibrium.
【０００８】光触媒酸化による消臭は、消臭速度が遅い
だけでなく、励起光源を併設する必要があり、コスト
高、装置の大型化、消費電力が大きいなどの問題があ
る。[0008] Deodorization by photocatalytic oxidation not only has a low deodorizing speed but also requires the use of an excitation light source, resulting in problems such as high cost, large-sized apparatus, and large power consumption.
【０００９】オゾン酸化による消臭においては、消臭作
用を有するオゾンそのものが人体に有害であるため、過
剰なオゾンを分解する装置が必要不可欠であり、これも
やはりコスト高、消費電力が大きいなどの問題がある。In the deodorization by ozone oxidation, ozone itself having a deodorizing action is harmful to the human body, and therefore, an apparatus for decomposing excessive ozone is indispensable, which also requires high cost and large power consumption. There is a problem.
【００１０】本発明は、従来方法の上述した欠点を克服
し、コンパクトかつ長寿命で、たばこの臭気を小さい圧
力損失で効率よく取り除くことができる消臭性フィルタ
及びそれを備えた空気調和機を低コストで提供すること
を目的とする。The present invention overcomes the above-mentioned drawbacks of the conventional method, and has a compact and long-life deodorizing filter capable of efficiently removing tobacco odor with a small pressure loss, and an air conditioner equipped with the same. The purpose is to provide at low cost.
【００１１】[0011]
【課題を解決するための手段】上記目的を達成するため
に請求項１の消臭性フィルタは、遷移金属キレート化合
物を樹脂成型品の表面にコーティングしたことを特徴と
する。In order to achieve the above object, a deodorizing filter according to claim 1 is characterized in that a transition metal chelate compound is coated on the surface of a resin molded product.
【００１２】この構成によると、消臭性フィルタを通過
する空気は、遷移金属キレート化合物を触媒として臭気
成分が分解される。According to this configuration, in the air passing through the deodorizing filter, the odor component is decomposed using the transition metal chelate compound as a catalyst.
【００１３】また、請求項２の消臭性フィルタは、請求
項１に記載の消臭性フィルタにおいて、前記遷移金属キ
レート化合物の水溶液と、バインダ樹脂を含むエマルジ
ョン液との混合液を前記樹脂成型品に塗布後乾燥させた
ことを特徴とする。The deodorizing filter according to a second aspect of the present invention is the deodorizing filter according to the first aspect, wherein a mixed solution of the aqueous solution of the transition metal chelate compound and the emulsion liquid containing a binder resin is formed by the resin molding. It is characterized by being dried after being applied to a product.
【００１４】この構成によると、遷移金属キレート化合
物の樹脂成型品へのコーティングが容易となる。According to this structure, the transition metal chelate compound can be easily coated on the resin molded product.
【００１５】また、請求項３の消臭性フィルタは、請求
項１又は請求項２に記載の消臭性フィルタにおいて、前
記遷移金属キレート化合物を金属ポリカルボキシフタロ
シアニンにしたことを特徴とするものである。According to a third aspect of the present invention, there is provided the deodorizing filter according to the first or second aspect, wherein the transition metal chelate compound is a metal polycarboxyphthalocyanine. is there.
【００１６】この構成によると、消臭性フィルタを通過
する空気は、金属ポリカルボキシフタロシアニンを触媒
として臭気成分が分解される。そして、消臭フィルタを
水洗いすることにより消臭性能の再生が行える。According to this configuration, in the air passing through the deodorizing filter, the odor component is decomposed using the metal polycarboxyphthalocyanine as a catalyst. Then, the deodorizing performance can be regenerated by washing the deodorizing filter with water.
【００１７】また、請求項４の消臭性フィルタは、請求
項１乃至請求項３のいずれかに記載の消臭性フィルタに
おいて、前記樹脂成型品をハニカム形状又は格子形状に
したことを特徴とする。According to a fourth aspect of the present invention, there is provided the deodorizing filter according to any one of the first to third aspects, wherein the resin molded product has a honeycomb shape or a lattice shape. I do.
【００１８】この構成によると、消臭性フィルタを通過
する空気は、ハニカム形状又は格子形状の通路を通り、
通路壁面にコーティングされた遷移金属キレート化合物
と接触することにより遷移金属キレート化合物を触媒と
して臭気成分が分解される。According to this configuration, the air passing through the deodorizing filter passes through the honeycomb-shaped or lattice-shaped passage.
By contacting the transition metal chelate compound coated on the passage wall surface, the odor component is decomposed by using the transition metal chelate compound as a catalyst.
【００１９】また、請求項５の消臭性フィルタは、請求
項１乃至請求項４のいずれかに記載の消臭性フィルタに
おいて、アパタイトを含有した不織布と活性炭を含有し
た不織布とを重ねあわせて形成したアパタイトハニカム
フィルタと、不織布または織布に遷移金属キレート化合
物を含浸したバイオネットを備えたことを特徴とする。The deodorizing filter according to claim 5 is the deodorizing filter according to any one of claims 1 to 4, wherein the nonwoven fabric containing apatite and the nonwoven fabric containing activated carbon are overlapped. It is characterized by comprising a formed apatite honeycomb filter and a bayonet in which a nonwoven fabric or a woven fabric is impregnated with a transition metal chelate compound.
【００２０】この構成によると、消臭性フィルタを通過
する臭気成分は、アパタイトハニカムフィルタに含有さ
せた活性炭に吸着されて除去されるとともに、バイオネ
ットに含浸した遷移金属キレート化合物に接触すること
により遷移金属キレート化合物を触媒として分解され
る。According to this configuration, the odor component passing through the deodorizing filter is removed by being absorbed by the activated carbon contained in the apatite honeycomb filter, and is brought into contact with the transition metal chelate compound impregnated in the bayonet. Decomposed by using a transition metal chelate compound as a catalyst.
【００２１】また、請求項６の空気調和機は、請求項１
乃至請求項５のいずれかに記載の消臭性フィルタを備え
たことを特徴とする。The air conditioner according to claim 6 is the same as the claim 1.
A deodorizing filter according to any one of claims 1 to 5 is provided.
【００２２】[0022]
【発明の実施の形態】以下、本発明の実施の形態を図面
を参照して説明する。図１は本発明に係る消臭性フィル
タの平面図であり、該消臭性フィルタはハニカム成型品
１、アパタイトハニカムフィルタ２及びバイオネット３
を組み合わせて形成されている。以下にそれぞれの構成
を具体的に説明する。尚、図１において、４はポリプロ
ピレン製の外枠であり、ハニカム成型品１及びアパタイ
トハニカムフィルタ３を装着するための取り付け部（図
示せず）を有している。Embodiments of the present invention will be described below with reference to the drawings. FIG. 1 is a plan view of a deodorizing filter according to the present invention. The deodorizing filter includes a honeycomb molded article 1, an apatite honeycomb filter 2, and a bayonet 3.
Are formed in combination. Hereinafter, each configuration will be specifically described. In FIG. 1, reference numeral 4 denotes an outer frame made of polypropylene, which has a mounting portion (not shown) for mounting the honeycomb molded product 1 and the apatite honeycomb filter 3.
【００２３】ハニカム成型品１は、厚さ（紙面に垂直な
方向）約５ｍｍの格子状もしくはハニカム状の構造体で
ある。図１は格子状の場合を示しているが、通気性を有
する構造であればよい。格子の各セルの開口部面積は約
０．５ｃｍ2である。このような筒状体の中に空気を通
過させるようにすれば、極めて圧損失の少ないフィルタ
を提供できる。The honeycomb molded article 1 is a lattice-shaped or honeycomb-shaped structure having a thickness (in the direction perpendicular to the paper) of about 5 mm. Although FIG. 1 shows the case of a lattice shape, any structure having air permeability may be used. The opening area of each cell of the grid is about 0.5 cm 2 . By allowing air to pass through such a cylindrical body, a filter with extremely low pressure loss can be provided.
【００２４】このハニカム成型品１の表面には遷移金属
キレート化合物をコーティングしているが、その手順を
以下に説明する。まず、オクタカルボキシ鉄（III）フ
タロシアニンを水溶液とし、アクリル酸エステル系エマ
ルジョン液もしくはポリビニルアルコール等のバインダ
樹脂が分散しているエマルジョン液と混合する。混合比
は、水溶性エマルジョン液１００ｍｌに対してオクタカ
ルボキシ鉄（III）フタロシアニン１ｇとする。尚、エ
マルジョン液はオクタカルボキシ鉄（III）フタロシア
ニンを安定に溶解させるため、アルカリ性に調製する。
その調製に際しては、水酸化ナトリウムまたは水酸化カ
リウムを用いるのが好ましい。The surface of the honeycomb molded article 1 is coated with a transition metal chelate compound. The procedure will be described below. First, octacarboxyiron (III) phthalocyanine is made into an aqueous solution and mixed with an acrylate-based emulsion or an emulsion in which a binder resin such as polyvinyl alcohol is dispersed. The mixing ratio is 1 g of octacarboxyiron (III) phthalocyanine per 100 ml of the water-soluble emulsion. The emulsion is prepared to be alkaline in order to stably dissolve octacarboxyiron (III) phthalocyanine.
In the preparation, it is preferable to use sodium hydroxide or potassium hydroxide.
【００２５】次に、この溶解液をハニカム成型品１の表
面に吹き付け塗布し、水分を蒸発させて塗膜層を形成さ
せた後、オーブンにより６０℃で２時間熱処理して硬化
させる。さらに、この塗装膜を中和するため、０．１規
定の希塩酸で洗浄してから、繰り返し水洗して塩化ナト
リウムと過剰の塩酸を洗い流し、水洗後に温風を当てて
表面を乾燥させた。こうして作製したハニカム成型品１
を外枠４に一体的に組み込む。Next, this solution is sprayed and applied to the surface of the honeycomb molded article 1 to evaporate water to form a coating layer, and then heat-treated at 60 ° C. for 2 hours in an oven to be cured. Further, in order to neutralize the coating film, the coating film was washed with 0.1 N dilute hydrochloric acid, and then repeatedly washed with water to wash away sodium chloride and excess hydrochloric acid. After washing with water, the surface was dried by applying hot air. Honeycomb molded product 1 thus produced
Are integrated into the outer frame 4.
【００２６】抗菌効果のあるアパタイトハニカムフィル
タ２は、アパタイトを含有させた不織布シートと活性炭
を含有させた不織布シートにより構成されている。不織
布シートにコルゲート加工を施して作製した波形板と仕
切板を交互に重ね合わせ、その重ね合わせた部分を接着
剤で接着して積層体を形成した。あらかじめ不織布シー
トに付着させたアパタイトは、ウイルスを不活化して繁
殖力を抑える抗菌作用をもっている。こうして作製した
アパタイトハニカムフィルタ３を外枠４の取り付け部に
装着することで、抗菌効果とたばこ臭気以外の臭気成分
も吸着により除去できる。The apatite honeycomb filter 2 having an antibacterial effect is composed of a nonwoven sheet containing apatite and a nonwoven sheet containing activated carbon. A corrugated plate and a partition plate produced by corrugating a nonwoven fabric sheet were alternately overlapped, and the overlapped portion was bonded with an adhesive to form a laminate. Apatite, which has been attached to the nonwoven fabric sheet in advance, has an antibacterial effect that inactivates viruses and suppresses the reproductive power. By mounting the thus produced apatite honeycomb filter 3 on the mounting portion of the outer frame 4, odor components other than the antibacterial effect and tobacco odor can be removed by adsorption.
【００２７】次に、バイオネット３は以下の手順によっ
てナイロンネットにオクタカルボキシ鉄（III）フタロ
シアニンを含浸して作製した。Next, Bayonet 3 was prepared by impregnating a nylon net with octacarboxyiron (III) phthalocyanine by the following procedure.
【００２８】水酸化カリウムを溶かしたアルカリ水溶液
に、消臭性材料であるオクタカルボキシ鉄（III）フタ
ロシアニンを加えて溶解させた。この溶液を６０℃に保
ち、これに複数枚の多孔質性ナイロンネットを一晩浸漬
して充分膨潤させた後、該ナイロンネットを取り出し、
濡れた状態で８０〜１５０℃、好ましくは１００℃の熱
風を約１０分送風して乾燥する。Octacarboxyiron (III) phthalocyanine as a deodorant material was added to and dissolved in an aqueous alkali solution in which potassium hydroxide was dissolved. This solution was kept at 60 ° C., and a plurality of porous nylon nets were immersed in the overnight to sufficiently swell, and then the nylon nets were taken out.
In a wet state, hot air at 80 to 150 ° C., preferably 100 ° C. is blown for about 10 minutes to dry.
【００２９】ナイロンネットに染み込んだ水酸化カリウ
ムを中和するため、該ナイロンネットを希塩酸に浸漬す
る。さらに、このナイロンネットを取り出し、過剰の塩
酸を水洗して十分に洗い流した後、再度乾燥してオクタ
カルボキシ鉄（III）フタロシアニンを含浸させたバイ
オネット３を作製した。これらのバイオネット３を図１
に示すように圧力損失を大きくしない程度の厚みで外枠
４に取り付けたハニカム成型品１及びアパタイトハニカ
ムフィルタ２の周囲に配置し、熱圧着法により外枠４に
固着させることによって、よりたばこ臭の除去効率を向
上させるように消臭性フィルタ（３５ｃｍ×３０ｃｍ）
を作製した。In order to neutralize potassium hydroxide permeated into the nylon net, the nylon net is immersed in dilute hydrochloric acid. Further, the nylon net was taken out, and excess hydrochloric acid was washed with water and sufficiently rinsed, and then dried again to produce a bionet 3 impregnated with octacarboxyiron (III) phthalocyanine. These bionets 3 are shown in FIG.
As shown in the figure, the honeycomb molded article 1 and the apatite honeycomb filter 2 attached to the outer frame 4 with a thickness that does not increase the pressure loss are arranged around the honeycomb molded article 1 and the apatite honeycomb filter 2. Deodorizing filter (35cm x 30cm) to improve the removal efficiency
Was prepared.
【００３０】以上のようにして作製した２枚の消臭性フ
ィルタ１５を図２に示すように空気調和機の室内機の空
気吸込み口１４と熱交換器１６との間に装着した。この
状態で空気調和機を例えば、冷房モードで運転させる
と、送風ファン１１が作動して室内の空気は空気吸込み
口１４から吸い込まれる。吸い込まれた空気は熱交換器
１６で冷却されて冷気となり、送風ファン１１によって
吹出し口１２から吹き出される。空気とともに空気吸込
み口１４から吸い込まれた臭気は、消臭性フィルタ１５
を通過する際に除去されるようになっている。この空気
調和機を用いて行った特性試験の結果を従来技術による
比較例とともに説明する。The two deodorizing filters 15 produced as described above were mounted between the air inlet 14 of the indoor unit of the air conditioner and the heat exchanger 16 as shown in FIG. When the air conditioner is operated in, for example, a cooling mode in this state, the blower fan 11 operates to draw indoor air from the air suction port 14. The sucked air is cooled by the heat exchanger 16 to become cool air, and is blown out from the outlet 12 by the blower fan 11. The odor sucked from the air inlet 14 together with the air is supplied to the deodorizing filter 15.
Is removed when passing through. The result of a characteristic test performed using this air conditioner will be described together with a comparative example according to the related art.
【００３１】この空気調和機の室内機を容積１ｍ3のア
クリル製ボックス内に設置してたばこ臭の消臭試験を次
のように行った。尚、ボックス内は一般的な家屋の室内
に近い雰囲気になるように温度２５℃、湿度６０％に調
整した。ボックス内でたばこ（マイルドセブン）５本を
機械喫煙させ、室内機の送風ファン１１を流速３ｍ3／
分で運転してボックス内部の空気を循環させた。送風フ
ァン１１の運転の前後で、アンモニア、アセトアルデヒ
ド、酢酸の各臭気性ガスの濃度をガス検知管で測定し、
各ガスの除去率を算出した。トータル除去率は、ＪＥＭ
１４６７に準拠した計算式［（アンモニア除去率＋２×
アセトアルデヒド除去率＋酢酸除去率）÷４］によって
求めた。The indoor unit of the air conditioner was installed in an acrylic box having a volume of 1 m 3 , and a test for deodorizing tobacco odor was conducted as follows. The inside of the box was adjusted to a temperature of 25 ° C. and a humidity of 60% so that the atmosphere was close to that of a general house. Five tobacco (mild seven) cigarettes are mechanically smoked in the box, and the blower fan 11 of the indoor unit is operated at a flow rate of 3 m 3 /
Minutes of operation circulated the air inside the box. Before and after the operation of the blower fan 11, the concentration of each odorous gas of ammonia, acetaldehyde and acetic acid was measured with a gas detector tube,
The removal rate of each gas was calculated. Total removal rate is JEM
Calculation formula [(ammonia removal rate + 2 ×
Acetaldehyde removal rate + acetic acid removal rate) {4].
【００３２】さらに、たばこを５本ずつ連続して機械喫
煙させ、その都度上述した方法で各ガスの除去率を測定
し、トータル除去率を算出した。この操作をたばこの累
積本数が２５本になるまで繰り返す。Further, five tobacco cigarettes were continuously machine-smoked, and each time, the removal rate of each gas was measured by the method described above, and the total removal rate was calculated. This operation is repeated until the cumulative number of cigarettes reaches 25.
【００３３】比較例として、外枠４の全体にアパタイト
ハニカムフィルタ２を装着した本実施形態と同じ大きさ
の消臭フィルタを２枚重ねて、空気吸込み口１４に臨ま
せて設置した空気調和機について消臭試験を行った。試
験方法は上記と同様である。得られた試験結果を表１に
示す。As a comparative example, an air conditioner in which two deodorizing filters having the same size as that of the present embodiment in which the apatite honeycomb filter 2 is mounted on the entire outer frame 4 is superimposed and installed facing the air suction port 14. A deodorizing test was performed on the sample. The test method is the same as described above. Table 1 shows the obtained test results.
【００３４】[0034]
【表１】 [Table 1]
【００３５】表１より明らかなように、アンモニア、ア
セトアルデヒド、酢酸の各臭気性ガスのすべてにおい
て、本発明に係る実施形態の方が従来品である比較例よ
り著しく高い除去率を与えている。たばこの累積本数が
増えるに従い、本実施形態及び比較例ともに各ガスの除
去率は低下するが、本実施形態ではたばこの累積本数が
２５本になっても、特に強い刺激臭のアンモニアに対し
ては、７０％以上の除去率が得られている。トータル除
去率については、比較例では初期でも４０％に満たない
不十分な結果しか得られていないのに対し、本実施形態
では、たばこの累積本数が２５本になっても、約５８％
のトータル除去率が得られ、依然として消臭性能の基準
値である５０％を超えている。As is evident from Table 1, the embodiment according to the present invention gives a significantly higher removal rate of each of the odorous gases of ammonia, acetaldehyde and acetic acid than the conventional comparative example. As the cumulative number of cigarettes increases, the removal rate of each gas decreases in both the present embodiment and the comparative example. However, in the present embodiment, even when the cumulative number of tobacco becomes 25, particularly against ammonia having a strong pungent odor. Has a removal rate of 70% or more. Regarding the total removal rate, in the comparative example, only an insufficient result of less than 40% was obtained at the initial stage, whereas in the present embodiment, even when the cumulative number of tobacco became 25, about 58% was obtained.
, And still exceeds the reference value of the deodorizing performance of 50%.
【００３６】以上の結果からも分かるように、従来品で
ある活性炭による悪臭物質の吸着によって消臭を行うア
パタイトハニカムフィルタに比べて、遷移金属キレート
化合物をコーティングしたハニカム成型品、アパタイト
ハニカムフィルタ及びバイオネットを組み合わせ複合化
した本発明に係る消臭性フィルタは消臭性能が極めて優
れている。As can be seen from the above results, as compared with the conventional apatite honeycomb filter which deodorizes by absorbing malodorous substances by activated carbon, a honeycomb molded product coated with a transition metal chelate compound, an apatite honeycomb filter, The deodorizing filter according to the present invention, which is formed by combining and combining nets, has extremely excellent deodorizing performance.
【００３７】本発明は空気調和機の室内機に消臭性フィ
ルタを取り付ける場合について説明したが、これに限ら
れず、室内に設置して空気を循環させる他の装置、例え
ば空気清浄機や除湿機にこの消臭性フィルタを搭載して
もよい。The present invention has been described with respect to the case where the deodorizing filter is attached to the indoor unit of the air conditioner. However, the present invention is not limited to this. Other devices installed indoors to circulate air, such as an air purifier and a dehumidifier The deodorizing filter may be mounted on the vehicle.
【００３８】[0038]
【発明の効果】本発明は以上の構成であるので、請求項
１、請求項２の発明によると樹脂成型品に遷移金属キレ
ート化合物をコーティングしているので、圧力損失が少
なく短時間で大量の空気を通過させて効率良く消臭でき
る消臭性フィルタを低コストで得ることができる。According to the present invention having the above construction, according to the first and second aspects of the present invention, since the transition metal chelate compound is coated on the resin molded product, the pressure loss is small and a large amount can be produced in a short time. A deodorizing filter that can efficiently deodorize by passing air can be obtained at low cost.
【００３９】また、請求項３の発明によると、消臭作用
を持つ材料として金属ポリカルボキシフタロシアニンを
採用しているので、たばこ臭に含まれるほとんどの臭気
性ガスを効果的に消臭することができるとともに、水洗
いにより簡単に消臭性能を再生することができる。According to the third aspect of the present invention, since metal polycarboxyphthalocyanine is employed as the material having a deodorizing effect, it is possible to effectively deodorize most odorous gas contained in tobacco odor. As well as being able to wash, the deodorizing performance can be easily regenerated by washing with water.
【００４０】また、請求項４の発明によると、消臭性フ
ィルタをハニカム形状または格子形状にしているので圧
力損失が小さくかつ空気との接触面積を大きくすること
ができ、より消臭効率を向上させることができる。According to the fourth aspect of the present invention, since the deodorizing filter has a honeycomb shape or a lattice shape, the pressure loss can be reduced and the contact area with air can be increased, thereby further improving the deodorizing efficiency. Can be done.
【００４１】また、請求項５の発明によると、遷移金属
キレート化合物をコーティングした樹脂成型品から成る
フィルタと、アパタイト及び活性炭を含むアパタイトフ
ィルタと、遷移金属キレート化合物を含浸したバイオネ
ットとを複合することによって、よりたばこ臭気の除去
量を増加させることができるとともに、他の臭気成分の
除去及び抗菌効果を得ることができる。According to the invention of claim 5, a filter composed of a resin molded article coated with a transition metal chelate compound, an apatite filter containing apatite and activated carbon, and a bayonet impregnated with a transition metal chelate compound are combined. This makes it possible to increase the amount of tobacco odor removed, to remove other odor components, and to obtain an antibacterial effect.
【００４２】また、請求項６の発明によると、樹脂成型
品に遷移金属キレート化合物をコーティングして消臭性
フィルタを形成しているので、圧力損失が少なく短時間
で大量の空気を通過させて効率良く消臭できる空気調和
機を低コストで得ることができる。According to the sixth aspect of the present invention, since the resin molded article is coated with the transition metal chelate compound to form the deodorizing filter, a large amount of air can be passed in a short time with low pressure loss. An air conditioner that can efficiently deodorize can be obtained at low cost.
【図１】 本発明に係る消臭性フィルタの平面図であ
る。FIG. 1 is a plan view of a deodorizing filter according to the present invention.
【図２】 本発明に係る消臭性フィルタを搭載した空
気調和機の構成を示す背面からの概略斜視図である。FIG. 2 is a schematic perspective view from the back showing the configuration of an air conditioner equipped with the deodorizing filter according to the present invention.
１ ハニカム成型品 ２ アパタイトハニカムフィルタ ３ バイオネット ４ 外枠 １１ 送風ファン １２ 空気吹出し口 １４ 空気吸込み口 １５ 消臭性フィルタ １６ 熱交換器 DESCRIPTION OF SYMBOLS 1 Honeycomb molded product 2 Apatite honeycomb filter 3 Bionette 4 Outer frame 11 Blower fan 12 Air outlet 14 Air inlet 15 Deodorant filter 16 Heat exchanger
───────────────────────────────────────────────────── フロントページの続き (72)発明者 野島 秀雄 大阪府大阪市阿倍野区長池町22番22号 シ ャープ株式会社内 (72)発明者 洗 暢茂 大阪府大阪市阿倍野区長池町22番22号 シ ャープ株式会社内 Ｆターム(参考） 3L053 BD03 4C080 AA03 AA05 AA07 BB02 BB05 CC02 CC08 HH05 HH09 JJ03 JJ05 MM01 MM05 MM19 NN22 NN28 QQ03 QQ11 QQ17 QQ20 4D019 AA01 AA10 BA13 BB02 BB03 BB10 BC05 BC06 BC07 BC20 CA01 CA02 CB01 CB03 ──────────────────────────────────────────────────続 き Continued on the front page (72) Inventor Hideo Nojima 22-22, Nagaikecho, Abeno-ku, Osaka-shi, Osaka Inside Sharp Co., Ltd. F-term (for reference) 3L053 BD03 4C080 AA03 AA05 AA07 BB02 BB05 CC02 CC08 HH05 HH09 JJ03 JJ05 MM01 MM05 MM19 NN22 NN28 QQ03 QQ11 QQ17 QQ20 4D019 AA01 AA10 BA13 BB02 BC03 BC03 BC03 BC03
Claims (6)
した樹脂成型品を備えたことを特徴とする消臭性フィル
タ。1. A deodorizing filter comprising a resin molded product coated with a transition metal chelate compound.
と、バインダ樹脂を含むエマルジョン液との混合液を前
記樹脂成型品に塗布後乾燥させたことを特徴とする請求
項１に記載の消臭性フィルタ。2. The deodorizing filter according to claim 1, wherein a mixture of the aqueous solution of the transition metal chelate compound and an emulsion containing a binder resin is applied to the resin molded product and then dried. .
カルボキシフタロシアニンにしたことを特徴とする請求
項１又は請求項２に記載の消臭性フィルタ。3. The deodorizing filter according to claim 1, wherein the transition metal chelate compound is a metal polycarboxyphthalocyanine.
形状にしたことを特徴とする請求項１乃至請求項３のい
ずれかに記載の消臭性フィルタ。4. The deodorizing filter according to claim 1, wherein the resin molded product has a honeycomb shape or a lattice shape.
含有した不織布とを重ね合わせて形成したアパタイトハ
ニカムフィルタと、不織布又は織布に遷移金属キレート
化合物を含浸したバイオネットとを備えたことを特徴と
する請求項１乃至請求項４のいずれかに記載の消臭性フ
ィルタ。5. An apatite honeycomb filter formed by laminating an apatite-containing nonwoven fabric and an activated carbon-containing nonwoven fabric, and a bionet comprising a nonwoven fabric or a woven fabric impregnated with a transition metal chelate compound. The deodorizing filter according to any one of claims 1 to 4.
の消臭性フィルタを備えたことを特徴とする空気調和
機。6. An air conditioner comprising the deodorizing filter according to any one of claims 1 to 5.