FR2681270A3 - Nozzle for the continuous casting of liquid metal, particularly steel - Google Patents
Nozzle for the continuous casting of liquid metal, particularly steel Download PDFInfo
- Publication number
- FR2681270A3 FR2681270A3 FR9111513A FR9111513A FR2681270A3 FR 2681270 A3 FR2681270 A3 FR 2681270A3 FR 9111513 A FR9111513 A FR 9111513A FR 9111513 A FR9111513 A FR 9111513A FR 2681270 A3 FR2681270 A3 FR 2681270A3
- Authority
- FR
- France
- Prior art keywords
- wall
- nozzle
- liquid metal
- layer
- continuous casting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
La présente invention concerne une busette pour la coulée continue de métal liquide, notamment d'acier, dont la paroi est réalisée en un matériau réfractaire, tel que l'alumine graphitée. The present invention relates to a nozzle for the continuous casting of liquid metal, in particular steel, the wall of which is made of a refractory material, such as graphite alumina.
On sait qu'après préchauffage, l'alumine graphitée n'est pas exempte d'une certaine porosité, du fait qu'une partie du carbone a été oxydée, dégageant de l'oxyde de carbone qui laisse un réseau creux s'ajoutant à la porosité naturelle du réfractaire. Il en résulte que de l'oxygène atmosphérique traverse inévitablement la paroi de la busette et vient former dans le métal liquide des inclusions d'oxydes qui nuisent à la propreté du métal coulé. It is known that after preheating, the graphitized alumina is not free from a certain porosity, owing to the fact that part of the carbon has been oxidized, releasing carbon monoxide which leaves a hollow network adding to the natural porosity of the refractory. As a result, atmospheric oxygen inevitably crosses the wall of the nozzle and comes to form in the liquid metal inclusions of oxides which harm the cleanliness of the cast metal.
Afin de bloquer les passages possibles d'air au travers de la paroi de la busette, on a déjà proposé de la revêtir extérieurement d'une couche d'émail vitrifié. Malheureusement, les busettes ainsi revêtues d'émail ne donnent pas satisfaction, l'émail perdant au cours du préchauffage ses propriétés d'étanchéité aux gaz. In order to block possible air passages through the wall of the nozzle, it has already been proposed to coat it externally with a layer of vitreous enamel. Unfortunately, the nozzles thus coated with enamel are not satisfactory, the enamel losing during preheating its gas tightness properties.
L'invention a donc pour but de proposer une solution satisfaisante au problème ci-dessus. The object of the invention is therefore to propose a satisfactory solution to the above problem.
Suivant l'invention, une couche d'un matériau imperméable aux gaz et pouvant adhérer au matériau constitutif de la paroi est noyée dans cette dernière, afin d'empêcher l'oxygène atmosphérique de traverser la paroi vers le métal liquide. According to the invention, a layer of a gas-impermeable material which can adhere to the material constituting the wall is embedded in the latter, in order to prevent atmospheric oxygen from passing through the wall towards the liquid metal.
Suivant un mode de réalisation de l'inven tison, dans lequel la paroi est en alumine graphitée, la couche de matériau imperméable aux gaz est une feuille de graphite lamellaire, matériau qui convient particuliè-rement bien à une telle utilisation. According to one embodiment of the invention, in which the wall is made of graphite alumina, the layer of gas-impermeable material is a sheet of lamellar graphite, a material which is particularly suitable for such use.
Suivant une particularité de l'invention, la couche imperméable aux gaz est avantageusement insérée sur toute la hauteur de la paroi et plus proche de la surface extérieure de ladite paroi que de sa surface intérieure. According to a feature of the invention, the gas impermeable layer is advantageously inserted over the entire height of the wall and closer to the outer surface of said wall than to its inner surface.
L'invention sera maintenant décrite en référence à la figure unique annexée qui en illustre un mode de réalisation à titre d'exemple non limitatif. The invention will now be described with reference to the single appended figure which illustrates an embodiment thereof by way of non-limiting example.
La figure unique annexée est une vue en perspective partielle, à échelle réduite, d'une busette de coulée continue de métal liquide conforme à l'invention. The single appended figure is a partial perspective view, on a reduced scale, of a nozzle for continuous casting of liquid metal according to the invention.
La busette 1, représentée au dessin, est destinée à la coulée continue d'un métal liquide tel que l'acier, et sa paroi 2 est réalisée en un matériau réfractaire approprié, tel que de l'alumine graphitée. The nozzle 1, shown in the drawing, is intended for the continuous casting of a liquid metal such as steel, and its wall 2 is made of an appropriate refractory material, such as graphite alumina.
Dans la paroi 2 est noyée, par une opération réalisée au cours de la fabrication de la busette, une couche 3 d'un matériau imperméable aux gaz et apte à adhérer au matériau réfractaire 2. La couche 3 doit, outre sa caractéristique d'imperméabilité aux gaz, satisfaire à deux autres conditions : être compatible avec l'alumine graphitée, c'est-à-dire présenter de bonnes caractéristiques d'adhérence avec celle-ci, et être apte à subir les conditions opératoires de fonctionnement de la busette.In the wall 2 is embedded, by an operation carried out during the manufacture of the nozzle, a layer 3 of a material impermeable to gases and capable of adhering to the refractory material 2. The layer 3 must, in addition to its waterproofing characteristic gas, meet two other conditions: be compatible with graphitized alumina, that is to say have good adhesion characteristics therewith, and be able to undergo the operating conditions of the nozzle.
Si le matériau réfractaire 2 est de l'alumine graphitée, un matériau imperméable convenant particulièrement bien pour réaliser la couche 3 est une feuille composée de graphite lamellaire, par exemple le produit connu sous la marque PAPYEX commercialisé par la société "Le Carbone Lorraine. If the refractory material 2 is graphitized alumina, an impermeable material which is particularly suitable for producing the layer 3 is a sheet composed of lamellar graphite, for example the product known under the brand PAPYEX marketed by the company "Le Carbone Lorraine.
Suivant un mode de réalisation avantageux, la feuille imperméable 3 est située à une distance dl de la surface extérieure de la paroi 2 inférieure à sa distance d2 de la surface intérieure de cette même paroi. Grâce au fait que par conséquent la feuille 3 est plus proche de la-surface extérieure que de la surface intérieure de la paroi 2, l'oxygène atmosphérique, dont le déplacement dans le matériau réfractaire 2 est symbolisé par les flèches portées sur le dessin, est arrêté très tôt dans sa progression à l'intérieur de la masse du réfractaire. I1 en résulte que seul le carbone résiduel se trouvant dans la partie extérieure de la paroi 2, d'épaisseur dl, peut être oxydé, l'oxygène étant arrêté par la feuille 3. According to an advantageous embodiment, the impermeable sheet 3 is located at a distance dl from the outside surface of the wall 2 less than its distance d2 from the inside surface of this same wall. Thanks to the fact that consequently the sheet 3 is closer to the outer surface than to the inner surface of the wall 2, atmospheric oxygen, the displacement of which in the refractory material 2 is symbolized by the arrows carried on the drawing, is stopped very early in its progression inside the mass of the refractory. As a result, only the residual carbon found in the external part of the wall 2, of thickness d1, can be oxidized, the oxygen being stopped by the sheet 3.
Cela accroit la durée de vie de la busette, en limitant l'oxydation du carbone résiduel donc en diminuant la corrosion chimique de la paroi 2. This increases the life of the nozzle, by limiting the oxidation of the residual carbon, therefore by reducing the chemical corrosion of the wall 2.
La propreté du métal liquide coulé dans la busette 1 ne peut plus, pratiquement, dans ces conditisons, être affectée par l'air atmosphérique, empêché de traverser la paroi 2. The cleanliness of the liquid metal poured into the nozzle 1 can no longer, practically, in these conditions, be affected by atmospheric air, prevented from passing through the wall 2.
L'invention n'est pas limitée au mode de réalisation décrit et peut comporter des variantes d'exécution. Ainsi d'autres matériaux ayant les mêmes propriétés que le graphite lamellaire pourraient etre utilisés, en association avec d'autres réfractaires que l'alumine graphitée. The invention is not limited to the embodiment described and may include variant embodiments. Thus other materials having the same properties as lamellar graphite could be used, in association with other refractories than graphitized alumina.
Claims (3)