FR2543062A1 - RECORDING MEDIUM BY INK JETS - Google Patents
RECORDING MEDIUM BY INK JETS Download PDFInfo
- Publication number
- FR2543062A1 FR2543062A1 FR8404654A FR8404654A FR2543062A1 FR 2543062 A1 FR2543062 A1 FR 2543062A1 FR 8404654 A FR8404654 A FR 8404654A FR 8404654 A FR8404654 A FR 8404654A FR 2543062 A1 FR2543062 A1 FR 2543062A1
- Authority
- FR
- France
- Prior art keywords
- recording
- ink
- recording medium
- ink jet
- jet recording
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
L'INVENTION CONCERNE UN SUPPORT D'ENREGISTREMENT AYANT UNE BONNE TRANSPARENCE ET DE BONNES PROPRIETES D'ENREGISTREMENT A L'ENCRE. IL EST CONCU POUR LA REALISATION D'ENREGISTREMENTS PAR JETS D'ENCRE ET POUR UNE UTILISATION DANS UN APPAREIL OPTIQUE TEL QU'UN RETROPROJECTEUR. IL EST COMPOSE D'UNE BASE TRANSPARENTE ET D'UNE COUCHE D'ABSORPTION D'ENCRE, ET SON COEFFICIENT DE TRANSMISSION LINEAIRE EST DE 10 ET PLUS. DOMAINE D'APPLICATION : ENREGISTREMENTS PAR IMPRESSION PAR JETS D'ENCRE, ETC.THE INVENTION RELATES TO A RECORDING MEDIA WITH GOOD TRANSPARENCY AND GOOD INK RECORDING PROPERTIES. IT IS DESIGNED FOR THE MAKING OF RECORDINGS BY INKJET AND FOR USE IN AN OPTICAL APPARATUS SUCH AS A RETROJECTOR. IT IS COMPOSED OF A TRANSPARENT BASE AND AN INK ABSORPTION LAYER, AND ITS LINEAR TRANSMISSION COEFFICIENT IS 10 AND MORE. FIELD OF APPLICATION: RECORDINGS BY INKJET PRINTING, ETC.
Description
R-543 062R-543 062
L'invention concerne un support d'enregistrement destiné à être utilisé dans l'enregistrement par jets The invention relates to a recording medium for use in jet recording
d'encre, et elle a trait plus particulièrement à un sup- in ink, and it relates more specifically to a
port d'enregistrement présentant une excellente transpa- recording port with excellent transparency
rence et une excellente absorption de l'encre. and excellent ink absorption.
Les dispositifs destinés à effectuer les enregis- Devices for recording
trements à l'aide d'un liquide sont très anciens et utilisés couramment pour effectuer des inscriptions, par exemple à l'aide de crayons à plume, etc On a récemment développé le dispositif dit "d'enregistrement à jets d'encre" qui utilise The use of a liquid is very old and is commonly used to make inscriptions, for example with the help of pencils, etc. Recently, the so-called "ink jet recording" device has been developed. uses
également un liquide d'enregistrement. also a recording liquid.
Le dispositif d'enregistrement par jets d'encre réalise l'enregistrement d'une image en produisant des gouttelettes du liquide d'enregistrement d'après divers The ink jet recording apparatus performs image recording by producing droplets of the recording liquid from various
principes de fonctionnement, puis en projetant les goutte- principles of operation and then projecting the
lettes vers l'élément ou support d'enregistrement et en les faisant adhérer à ce support sur lequel on souhaite enregistrer des images Ce dispositif d'enregistrement a attiré l'attention générale par ses caractéristiques de letters to the recording element or medium and adhering them to the medium on which images are to be recorded. This recording device has attracted general attention
faible bruit, de travail à grande vitesse et d'enregistre- low noise, high speed work and recording
ment polychrome En ce qui concerne le liquide d'enregistre- In the case of the recording liquid,
ment, on a utilisé principalement un liquide d'enregistre- mainly a recording liquid was used.
ment de type aqueux pour des raisons de sécurité et d'apti- aqueous type for reasons of safety and
tude à s'adapter à l'enregistrement. study to adapt to the recording.
En ce qui concerne l'élément ou support d'enregis- With regard to the element or medium of recordings
trement à utiliser dans un tel dispositif d'enregistrement par jets d'encre, on a fait appel jusqu'à présent, en général, à du papier uni En améliorant les performances de l'appareil d'enregistrement par jets d'encre, par exemple en offrant la possibilité d'effectuer un enregistrement à grande vitesse For use in such an ink jet recording device, so far, in general, plain paper has been used. By improving the performance of the ink jet recording apparatus, by example by offering the possibility of making a high-speed recording
ou un enregistrement polychrome, de nouveaux types de sup- or a polychrome recording, new types of
port d'enregistrement ont été développés et utilisés tels que celui appelé "papier d'enregistrement par jets d'encre", composé d'une base et d'une couche poreuse d'absorption d'encre appliquée sur la base afin d'accroître la propriété port have been developed and used such as the so-called "ink jet recording paper", consisting of a base and a porous ink absorption layer applied to the base to increase the property
d'absorption de l'encre présentée par le papier. absorption of the ink presented by the paper.
Un tel support d'enregistrement doit satisfaire les conditions indiquées ci-dessous pour produire des images enregistrées à l'aide d'un appareil à jets d'encre, images ayant une résolution élevée et une bonne-qualité: 1 > elle absorbe l'encre aussi rapidement que possible; 2) lorsque les points d'encre sont appliqués l'un après l'autre, il ne permet pas au dernier point de se déplacer sur le point précédent; 3) il ne permet pas au point d'encre d'accroître son diamètre plus qu'il n'est nécessaire; 4) il maintient le point d'encre suivant une forme sensiblement circulaire et donc suivant un contour régulier; 5) il conserve au point d'encre une densité élevée et donc une circonférence non obscurcie; et 6) il favorise une bonne propriété de formation de Such a recording medium must satisfy the conditions indicated below to produce images recorded using an ink jet apparatus, images having a high resolution and a good-quality: 1> it absorbs the ink as quickly as possible; 2) when the ink dots are applied one after the other, it does not allow the last point to move on the previous point; 3) it does not allow the ink point to increase its diameter more than is necessary; 4) it keeps the ink dot in a substantially circular shape and therefore in a regular outline; 5) it keeps in the ink point a high density and therefore a non-obscured circumference; and 6) it promotes a good training property of
couleur par l'encre.color by the ink.
Dans un appareil d'enregistrement par jets d'encre, In an ink jet recording apparatus,
on a également utilisé jusqu'à présent un autre type de sup- another type of support has been used so far.
port d'enregistrement sur lequel on souhaite obtenir une image enregistrée permettant une observation en surface de cette image En améliorant la technique d'enregistrement recording port on which you want to obtain a recorded image allowing a surface observation of this image By improving the recording technique
par jets d'encre et en étendant les applications des appa- by inkjet and extending the applications of
reils d'enregistrement par jets d'encre, il est apparu qu'un tel support d'enregistrement présentait une certaine utilité recording media, it appeared that such a recording medium was of some
à d'autres fins en utilisant avantageusement les caractéris- for other purposes by using advantageously the characteristics
tiques de l'enregistrement par jets d'encre. ticks of ink jet recording.
Comme utilisations autres que l'observation d'une image de surface, on peut citer: l'observation d'une image enregistrée sur un écran par projection de cette image à As uses other than the observation of a surface image, there may be mentioned: the observation of an image recorded on a screen by projection of this image to
l'aide d'un appareil optique tel qu'un projecteur de diapo- using an optical device such as a slide projector
sitives, un rétroprojecteur, etc; un photomasque pour - sitives, an overhead projector, etc .; a photomask for -
imprimante par contact, une plaquette à câblage par circuit imprimé, etc; une plaque de séparation de couleur pour la production d'une plaque positive pour l'impression en contact printer, printed wiring board, etc .; a color separator plate for the production of a positive plate for printing in
-2543062-2543062
couleur; un filtre mosaïque de couleurs pour l'affichage de couleur par cristaux liquides; etc. color; a color mosaic filter for liquid crystal color display; etc.
Des négatifs et des positifs transparents à uti- Transparent negatives and positives for use
liser dans des appareils et dispositifs optiques ou dans des appareils utilisant une technique optique sont obtenus in optical devices and devices or in apparatus using optical
par prise de photographies de sujets ou objets à enregis- by taking photographs of subjects or objects to be recorded
trer, ou par enregistrement direct de ces sujets ou objets déjà enregistrés, pour leur enregistrement sur un support transparent constitué d'une pellicule de matière plastique, or by direct recording of those subjects or objects already registered, for recording on a transparent support consisting of a film of plastic material,
etc Hormis ces procédés classiques l'appareil d'enregistre- etc. Apart from these conventional methods, the recording apparatus
ment par jets d'encre utilisant un support d'enregistrement transparent pour l'enregistrement par jets d'encre rend possible d'effectuer un tel enregistrement à une vitesse et d'obtenir une image enregistrée en couleurs complète, ayant une résolution élevée et une bonne qualité, qui peut être utilisée dans les appareils et dispositifs optiques ink jetting using a transparent recording medium for ink jet recording makes it possible to perform such recording at a speed and to obtain a full color recorded image having a high resolution and good quality, which can be used in optical devices and devices
mentionnés précédemment A cet effet, le support d'enregis- mentioned above. For this purpose, the recording support
trement doit présenter une transparence convenant à l'utili- must be transparent to the user.
sation finale, en plus des exigences demandées au support d'enregistrement pour l'enregistrement par jets d'encre et finalization, in addition to the requirements of the recording media for ink-jet recording and
telles qu'énumérées précédemment. as listed above.
L'invention a pour objet un support d'enregistre- The subject of the invention is a recording medium
ment destiné à un enregistrement par-jets d'encre, qui peut être utilisé à d'autres fins que l'observation d'une image de surface, par exemple dans des projecteurs de diapositives, des rétroprojecteurs, des imprimantes par contact et d'autres appareils et dispositifs optiques, et qui répond à toutes les exigences qui lui sont demandées pour l'enregistrement for inkjet recording, which may be used for purposes other than the observation of a surface image, for example in slide projectors, overhead projectors, contact printers and other optical devices and devices, and that meets all the requirements for registration
par jets d'encre.by ink jets.
Conformément à l'invention et d'une façon géné- According to the invention and in a general way
rale, il est prévu un support pour enregistrement par jets d'encre qui comprend: une base transparente et une couche d'absorption d'encre appliquée sur la base, le support d'enregistrement ayant un coefficient de transmission In addition, there is provided an ink jet recording medium which comprises: a transparent base and an ink absorption layer applied to the base, the recording medium having a transmission coefficient
linéaire de 10 % et plus.linear of 10% and more.
Les objets indiqués ci-dessus, ainsi que d'autres The objects listed above, as well as others
objets et les matières particulières entrant dans la consti- objects and the particular materials forming part of the
tution de la base, ainsi que les ingrédients et leurs pro- of the base, as well as the ingredients and their
portions de mélangegpour la couche d'absorption du support pour enregistrement par jets d'encre selon l'invention mixing portions for the absorption layer of the ink jet recording medium according to the invention
t ressortiront de la description détaillée qui suit, ainsi que will be apparent from the following detailed description, as well as
de la lecture de plusieurs exemples de formes de réalisation préférées. reading several examples of preferred embodiments.
La base transparente pour le support d'enre- The transparent base for recording support
gistrement selon l'invention peut être choisie parmi les matières suivantes: du polyester, du diacétate de cellulose, du triacétate de cellulose, des polymères du type acrylique, According to the invention, the recording material may be chosen from the following materials: polyester, cellulose diacetate, cellulose triacetate, polymers of the acrylic type,
de la "Cellophane" (une marque commerciale pour de la cellu- cellophane (a trade mark for cellu-
lose régénérée), du "Celluloid" (une marque commerciale pour une matière plastique constituée de camphre et de nitrate de cellulose), du -chlorure de polyvinyle du polycarbonate et d'autres matières plastiques sous forme de feuilles ou regenerated loses), "Celluloid" (a trade name for a plastic material consisting of camphor and cellulose nitrate), polyvinylchloride of polycarbonate and other plastic materials in the form of
de plaques, ainsi qu'une plaque de verre. of plates, as well as a glass plate.
La couche d'absorption d'encre du support d'enre- The ink absorption layer of the recording medium
gistrement selon l'invention peut être fabriquée à l'aide des matières suivantes, capables de former, sur la base according to the invention may be manufactured using the following materials, capable of forming, on the basis of
mentionnée ci-dessus, une pellicule continue de recouvre- mentioned above, a continuous film covering
ment ayant une transparence suffisante: de l'amidon, de la caséine, de l'albumine, de la gomme arabique, de l'alginate de sodium, de l'alcool polyvinylique, du polyacrylamide, de la carboxyméthyl cellulose, du polyacrylate de sodium, de la résine ionomère, de l'acétate polyvinylique, etc. Ces matières, séparément ou en combinaisons, sont dissoutes dans un solvant suivant la nécessité, et la solution est appliquée sur la base, puis séchée ou refroidie Suivant les cas, un ou plusieurs types de pigments inorganiques peuvent être dispersés en tant que charges dans la couche d'absorption d'encre mentionnée ci-dessus, dans une plage telle qu'ils n'affectent pas la transparence du support d'enregistrement, ces pigments étant destinés à augmenter with sufficient transparency: starch, casein, albumin, gum arabic, sodium alginate, polyvinyl alcohol, polyacrylamide, carboxymethyl cellulose, sodium polyacrylate , ionomeric resin, polyvinyl acetate, etc. These materials, separately or in combination, are dissolved in a solvent as necessary, and the solution is applied to the base, and then dried or cooled. Depending on the case, one or more types of inorganic pigments may be dispersed as fillers in the process. ink absorption layer mentioned above, in a range such that they do not affect the transparency of the recording medium, these pigments being intended to increase
les propriétés d'absorption et de fixage du liquide d'enre- the absorption and fixing properties of the recording liquid
gistrement sur le support d'enregistrement en formant une structure poreuse sur la surface de la couche d'absorption d'encre Des exemples de telles matières de charge sont une poudre pulvérisée de silice, d'argile, de talc, de terre de diatcmées, de carbonate de calcium, de sulfate de calcium, d'oxyde de titane, d'oxyde de zinc, de blanc satin, de silicate d'aluminium, de lithopone, d'alumine, de zéolite et autres. La couche d'absorption d'encre peut être appliquée sur la base par divers procédés connus tels qu'un procédé d'enduction au rouleau, un procédé d'enduction à la lame, Recording on the recording medium by forming a porous structure on the surface of the ink absorption layer Examples of such fillers are powdered silica, clay, talc, diatomaceous earth, calcium carbonate, calcium sulphate, titanium oxide, zinc oxide, white satin, aluminum silicate, lithopone, alumina, zeolite and others. The ink absorbing layer may be applied to the base by various known methods such as a roll coating process, a blade coating process,
un procédé d'enduction à la lame d'air, un procédé d'enduc- a coating process with an air knife, a coating process
tion à la barre, un procédé d'enduction par fusion à la at the helm, a process of fusion coating at the
chaleur, et ainsi de suite.heat, and so on.
L'expression "coefficient de transmission linéaire (T(%))" telle qu'utilisée dans le présent mémoire The expression "linear transmission coefficient (T (%))" as used herein
désigne une valeur obtenue, d'abord par mesure d'un coef- means a value obtained, first by measuring a coef-
ficient de transmission spectrale d'une lumière rectiligne qui arrive perpendiculairement sur un échantillon, passe à travers cet échantillon, puis dans une fente de réception ficient spectral transmission of a rectilinear light that arrives perpendicularly on a sample, passes through this sample, and then into a receiving slot
de lumière située à une distance d'au moins 8 cm de l'échan- of light at least 8 cm from the sample.
tillon et sur le prolongement du trajet de la lumière inci- and the prolongation of the path of the light inci-
dente, et arrive sur un détecteur, puis par calcul d'une valeur Y des valeurs trichromatiques de couleur à partir du coefficient de transmission spectrale tel que mesuré, et enfin par calcul du coefficient de transmission linéaire à l'aide de l'équation suivante: T Y/Yo x 100 ( 1) o T désigne le coefficient de -transmission linéaire, Y représente la valeur Y d'un échantillon, et Yo indique dente, and arrives on a detector, then by calculation of a Y value of the trichromatic color values from the spectral transmission coefficient as measured, and finally by calculation of the linear transmission coefficient using the following equation : TY / Yo x 100 (1) where T is the coefficient of linear transmission, Y is the Y value of a sample, and Yo indicates
une valeur Y d'un blanc.a Y value of a blank.
Le coefficient de transmission linéaire peut être mesuré, par exemple,à l'aide d'un spectrophotomètre du type autoenregistreur, modèle 323 (fabriqué par la firme The linear transmission coefficient can be measured, for example, using a spectrophotometer of the self-recording type, model 323 (manufactured by the firm
Hitachi Limited, Japon).Hitachi Limited, Japan).
Par conséquent, le coefficient de transmission linéaire tel qu'utilisé dans la présente invention est considéré par rapport à la lumière rectiligne, de sorte qu'il est différent d'une évaluation de la transparence d'un objet au moyen de lumière diffusée, utilisant un Therefore, the linear transmission coefficient as used in the present invention is considered with respect to the straight light, so that it is different from an evaluation of the transparency of an object by means of scattered light, using a
coefficient de transmission diffuse (pour établir un coef- diffuse transmission coefficient (to establish a coef-
ficient de transmission d'un échantillon, y compris de ficient transmission of a sample, including
lumière diffuse, par mise en place d'une sphère d'intégra- diffuse light, by setting up a sphere of integration
tion sur le côté arrière de l'échantillon) ou d'une non- transparence (pour trouver un degré de non-transparence d'un-échantillon à partir d'un taux de transmission de lumière entre un revêtement blanc et un revêtement noir appliqués sur la surface arrière de l'échantillon) Etant donné que clest le comportement de lumière rectiligne qui compte dans les appareils et dispositifs utilisés dans la technique optique, le fait d'établir le coefficient de on the back side of the sample) or non-transparency (to find a degree of non-transparency of a sample from a light transmission rate between a white coating and an applied black coating on the back surface of the sample) Since the rectilinear light behavior of the devices and devices used in the optical
transmission linéaire du support d'enregistrement est parti- linear transmission of the recording medium is parti-
culièrement important pour évaluer la transparence du sup- important for assessing the transparency of the
port devant être utilisé dans de tels appareils et disposi- port to be used in such devices and
tifs. Lorsque l'on observe une image projetée à l'aide d'un rétroprojecteur, par exemple, il est nécessaire qu'une partie non enregistrée de l'image projetée soit suffisamment brillante, c'est-à-dire que le coefficient de transmission linéaire du support d'enregistrement soit au moins à un certain niveau afin que l'on obtienne une image très claire, de contraste élevé, entre la partie enregistrée et la partie tive. When viewing an image projected with an overhead projector, for example, it is necessary for an unregistered part of the projected image to be sufficiently bright, i.e. the transmission coefficient linear recording medium is at least at a certain level so that a very clear, high-contrast image is obtained between the recorded part and the part
non enregistrée de l'image Conformément à des essais effec- unrecorded image in accordance with tests carried out
tués à l'aide d'une mire d'essai pour le rétroprojecteur, il est nécessaire que le coefficient de transmission linéaire du support d'enregistrement soit de 10 % ou plus pour que l'on obtienne une image convenant au but précité, et qu'il soit de préférence de 30 % en plus pour obtenir une image plus claire Par conséquent, le support d'enregistrement convenant au but de la présente invention doit posséder un killed by a test pattern for the overhead projector, it is necessary for the linear transmission coefficient of the recording medium to be 10% or more in order to obtain an image suitable for the purpose mentioned above, and preferably 30% more to obtain a clearer image Therefore, the recording medium suitable for the purpose of the present invention must have a
coefficient de transmission linéaire de 10 % ou plus. linear transmission factor of 10% or more.
Le support d'enregistrement selon l'invention peut The recording medium according to the invention can
également être utilisé comme support d'enregistrement chro- also be used as a recording medium
matique par coloration de la base transparente ou de la by coloring the transparent base or
couche d'absorption d'encre.ink absorption layer.
Comme décrit précédemment, le support pour l'enre- As previously described, the support for the recording
gistrement par jets d'encre, constitué de la base transpa- ink-jet recording, consisting of the transparent
rente et de la couche d'absorption d'encre appliquée sur cette base, présente une excellente propriété d'absorption d'encre et il est donc adapté à une utilisation pour des enregistrements à grande vitesse et des enregistrements polychromes et il convient donc hautement comme support d'enregistrement pouvant être utilisé dans divers appareils the ink absorption layer applied on this basis, has an excellent ink absorption property and is therefore suitable for use for high-speed recordings and polychromatic recordings and is therefore highly suitable as recording medium that can be used in various devices
et dispositifs optiques tels que des projecteurs de diaposi- and optical devices such as slide projectors
tives, des rétroprojecteurs, des imprimantes par contact, etc. Pour permettre à l'homme de l'art de mettre aisément screens, overhead projectors, contact printers, etc. To allow the person skilled in the art to easily
en pratique l'invention, on décrira ci-après plusieurs exem- In practice the invention will be described hereinafter several examples.
ples Il convient cependant-de noter que l'invention n'est It should be noted, however, that the invention is not
pas limitée uniquement à ces exemples, mais que des modifica- not limited to these examples only, but that modifications
tions et des changements peuvent être apportés aux matières and changes may be made to the materials
et aux ingrédients utilisés sans sortir du cadre de l'inven- ingredients used without departing from the scope of the invention.
tion.tion.
Exemple 1Example 1
Comme base transparente, on utilise une pellicule de triacétate de cellulose de 80 Am d'épaisseur (un produit de la firme Fuju Photo Film Co, Ltd, Japon), sur laquelle As a transparent base, an 80 Am thick cellulose triacetate film (a product of Fuju Photo Film Co., Ltd., Japan) is used, on which
la couche d'absorption d'encre, ayant la composition men- the ink absorption layer having the composition
tionnée ci-dessus, est appliquée par le procédé d'enduction à la barre, de façon que la pellicule revêtue, après séchage, puisse atteindre une épaisseur de 100 gm, après quoi on fait sécher le revêtement appliqué en le faisant séjourner dans un four de séchage pendant une heure, à une above, is applied by the bar coating method, so that the coated film, after drying, can reach a thickness of 100 gm, after which the coating applied is dried by being kept in an oven drying for one hour, at a
température de 80 WC.temperature of 80 WC.
Composition de la couche d'absorption d'encre Alcool polyvinylique "PVA117 " 10 parties en poids (produit de la firme Kuraray K K, Japon) Silice pulvérisée "NIPSIL E 200 " (produit de Nippon Silica Kogyo K K) 0,1 partie en-poids parties en poids Eau Composition of the ink-absorbing layer Polyvinyl alcohol "PVA117" 10 parts by weight (product of Kuraray KK, Japan) Sputtered silica "NIPSIL E 200" (product of Nippon Silica Kogyo KK) 0.1 part weight parts by weight Water
A l'aide du support d'enregistrement ainsi fabri- Using the recording medium thus manufactured
qué, on procède à un enregistrement par jets d'encre afin que l'on obtienne la matière enregistrée en utilisant une encre aqueuse en quatre couleurs jaune, rouge, bleue et noire, comme indiqué dans le tableau I cidessous, et on utilise à cet effet un appareil d'enregistrement comportant ink recording is performed to obtain the recorded material using an aqueous ink in four yellow, red, blue and black colors, as shown in Table I below, and is used for this purpose. effect a recording apparatus comprising
une tête d'enregistrement par jets d'encre du type fonction- an ink jet recording head of the function type
nant "à la demande", conçue pour éjecter le liquide d'enre- "on demand", designed to eject the liquid from the
gistrement à l'aide d'un vibrateur piézoélectrique (diamètre de l'orifice de 50 am; tension de commande du vibrateur recording with a piezoelectric vibrator (diameter of the 50 am orifice, control voltage of the vibrator
piézoélectrique: 60 V; et fréquence de commande: 4 k Hz). piezoelectric: 60 V; and control frequency: 4 kHz).
Tableau 1Table 1
r U Ln c os Composition Type (colorant) Colorant Diéthylène-glycol Eau Encre jaune (jaune acide 23 du CÌ) 2 parties en poids 15 parties en poids 85 parties en poid E Encre rouge (rouge acide 92 du Co 1) 2 parties en poids 15 parties en poids 85 parties en poid E Encre bleue (bleu direc# 86 du Co I) 2 parties en poids 15 parties en poids 85 parties en poid E Encre noire (noir direct 19 du Co I) 2 parties en poids 15 parties en poids 85 parties en poid L'adaptabilité à l'enregistrement du support pour enregistrement par jets d'encre est évaluée par mesure du temps de fixage de l'encre et de la densité des points, Composition Composition Type Dye Ethylene glycol Water Yellow ink (23 C jaune acid yellow) 2 parts by weight 15 parts by weight 85 parts by weight E Red ink (acid red 92 from Co 1) 2 parts by weight weight 15 parts by weight 85 parts by weight E Blue ink (blue, heading 86 I Co) 2 parts by weight 15 parts by weight 85 parts by weight E Black ink (direct black 19 from Co I) 2 parts by weight 15 parts by weight 85 parts by weight The recording adaptability of the ink jet recording medium is evaluated by measuring the fixing time of the ink and the density of the points,
tandis que son adaptabilité à un appareil optique est éva- while its adaptability to an optical device is
luée par mesure du coefficient de transmission linéaire et read by measurement of the linear transmission coefficient and
par un essai de compatibilité avec un rétroprojecteur consti- by a compatibility test with an overhead projector
tuant l'appareil optique représentatif. killing the representative optical apparatus.
Le temps de fixage de l'encre est mesuré de manière que, après achèvement de l'enregistrement par jets d'encre, le sujet enregistré soit laissé à la température ambiante pour sécher parfaitement et fixer l'encre sur le support d'enregistrement afin qu'elle ne puisse plus adhérer à un doigt touchant la partie enregistrée On trouve ainsi le temps écoulé de la fin de l'enregistrement jusqu'au séchage The ink fixing time is measured so that after completion of the ink jet recording, the recorded subject is left at room temperature to dry perfectly and fix the ink on the recording medium so that it can no longer adhere to a finger touching the recorded part Thus we find the time elapsed from the end of the recording until the drying
de l'encre.ink.
La densité de points est mesurée sur des points d'encre noire, à l'aide d'un micro-densitomètre "SAKURA The dot density is measured on black ink dots, using a micro-densitometer "SAKURA
PDM-5 " (fabriqué par Konishiroku Photo Industries, Co Ltd). PDM-5 "(manufactured by Konishiroku Photo Industries, Co Ltd).
On trouve le coefficient de transmission linéaire We find the linear coefficient of transmission
à l'aide de l'équation ( 1) mentionnée ci-dessus et en utili- using equation (1) above and using
sant le spectrophotomètre auto-enregistreur, modèle 323 the self-recording spectrophotometer model 323
(fabriqué par Hitachi, Ltd,Japon), dans lequel un échantil- (manufactured by Hitachi, Ltd, Japan), in which a sample of
lon est placé à une distance d'environ 9 cm d'une fenêtre de réception de la lumière, de façon que le coefficient de at a distance of about 9 cm from a light receiving window, so that the
transmission spectrale soit mesuré. spectral transmission be measured.
L'adaptabilité au rétroprojecteur est évaluée par projection du sujet enregistré sur l'écran à l'aide de ce rétroprojecteur et observation de l'image projetée à l'oeil nu, l'évaluation s'effectuant conformément aux critères suivants: o La partie non enregistrée est lumineuse; la partie enregistrée présente une densité optique élevée, et The adaptability to the overhead projector is evaluated by projecting the subject recorded on the screen using this overhead projector and observing the image projected with the naked eye, the evaluation being carried out in accordance with the following criteria: unregistered is bright; the recorded portion has a high optical density, and
l'image projetée est claire et d'un contraste élevé. the projected image is clear and of high contrast.
a.; La partie non enregistrée devient quelque peu sombre; la partie enregistrée présente une densité optique légèrement plus faible; et l'image projetée est d'un 1,1 at.; The unregistered part becomes somewhat dark; the recorded portion has a slightly lower optical density; and the projected image is of a 1.1
contraste plus faible.lower contrast.
X La partie non enregistrée devient sombre; la partie enregistrée est de densité optique très faible; et l'image projetée est sombre et difficile à observer, ou bien le sujet enregistré apparalt si sombre qu'il est impossible de distinguer les parties enregistrées X The unregistered part becomes dark; the recorded part is of very low optical density; and the projected image is dark and difficult to view, or the recorded subject appears so dark that it is impossible to distinguish the recorded parts
et non enregistrées.and not registered.
A partir des résultats donnés ci-dessus, on pro- From the results given above, it is
cède à une évaluation générale pour savoir si le support d'enregistrement sert à atteindre le but de-la présente invention ou non Le tableau II donné ci-dessous indique ces résultats. gives a general evaluation as to whether the recording medium serves to achieve the object of the present invention or not. Table II given below indicates these results.
Exemple 2Example 2
On utilise comme base transparente une pellicule We use as a transparent base a film
de "Mylar" de 80 Lxm d'épaisseur, traitée pour l'hydrophi- "Mylar" 80 Lxm thick, treated for hydrophilic
lité (produite par I C I, Grande-Bretagne), sur laquelle la couche d'absorption d'encre, de la composition indiquée ci-dessous, est appliquée par le procédé d'enduction à la barre, de manière que la pellicule revêtue, après séchage, atteigne une épaisseur de 100 gm, l'enduction étant suivie d'un séchage de la couche appliquée, dans un four de séchage, pendant 30 minutes à une température de 300 C. Composition de la couche d'absorption d'encre Albumine (albumine de blanc d'oeuf, produite par Tokyo Kasei Kogyo, K K) 10 parties en poids Eau 90 parties en poids A l'aide du support d'enregistrement ainsi obtenu, on procède à un enregistrement par jets d'encre de la manière décrite dans l'exemple 1 ci-dessus afin d'obtenir le the ink absorption layer, of the composition indicated below, is applied by the coating process to the bar, so that the coated film, after drying, reaches a thickness of 100 gm, the coating being followed by drying of the applied layer, in a drying oven, for 30 minutes at a temperature of 300 C. Composition of the albumin ink absorption layer (Egg white albumin, produced by Tokyo Kasei Kogyo, KK) 10 parts by weight Water 90 parts by weight With the aid of the recording medium thus obtained, ink jet recording is carried out in the manner described in Example 1 above in order to obtain the
sujet enregistré En outre, l'évaluation portant sur l'adap- In addition, the evaluation of the adaptation
tabilité du support à un enregistrement par jets d'encre supportability for ink jet recording
est effectuée conformément au procédé utilisé dans l'exem- is carried out in accordance with the method used in the
ple 1 ci-dessus, les résultats étant indiqués dans le ple 1 above, the results being indicated in
tableau Il ci-dessous.table II below.
Exemple 3Example 3
La même pellicule de "Mylar", traitée pour The same film of "Mylar", treated for
l'hydrophilité, que celle utilisée dans l'exemple 2 ci- hydrophilicity, as used in Example 2 below.
dessus est utilisée comme base transparente, puis la cou- above is used as a transparent base, then the
che d'absorption d'encre, de la composition mentionnée ink absorption tube, of the mentioned composition
ci-dessous, est appliquée sur la base par le procédé d'en- below, is applied on the basis by the method of
duction par fusion à chaud, l'enduction étant suivie d'un refroidissement de la couche appliquée à la température ambiante. Composition de la couche d'absorption d'encre Résine ionomère ("SURLYN", produit de E.I du Pont de Nemours & Co, E U A) 100 parties en poids Pigment bleu C I ("FASTGEN BLUE 5030 L", produit de Dai-Nippon Ink Co Ltd) 0,1 partie en poids On obtient un support d'enregistrement comportant hot melting, the coating being followed by cooling the applied layer to ambient temperature. Composition of the ink absorption layer Resin ionomer ("SURLYN", EI product from the Pont de Nemours & Co, USA) 100 parts by weight CI blue pigment ("FASTGEN BLUE 5030 L", product of Dai-Nippon Ink Co Ltd) 0.1 part by weight A recording medium is obtained comprising
une couche colorée d'absorption d'encre. a colored layer of ink absorption.
A l'aide du support d'enregistrement ainsi obtenu, on procède à un enregistrement par jets d'encre de la With the aid of the recording medium thus obtained, an ink jet recording of the
manière décrite dans l'exemple 1 ci-dessus de façon à obte- described in Example 1 above so as to obtain
nir le sujet enregistré L'adaptabilité de ce support d'enre- the recorded subject The adaptability of this recording medium
gistrement à un enregistrement par jets d'encre est évalué registration to an inkjet recording is evaluated
conformément au procédé décrit dans l'exemple 1 ci-dessus. according to the method described in Example 1 above.
Exemple comparatif 1 La même pellicule de "Mylar", traitée pour l'hydro philité, que celle utilisée dans l'exemple 2 ci-dessus, sans couche d'absorption d'encre, est utilisée comme support d'enregistrement, et l'enregistrement par jets d'encre est Comparative Example 1 The same "Mylar" film, treated for hydro phicity, as used in Example 2 above, without ink absorption layer, is used as the recording medium, and the ink jet recording is
effectué sur cette pellicule conformément aux étapes décri- carried out on this film in accordance with the steps
tes dans l'exemple 1 ci-dessus L'adaptabilité du support d'enregistrement à un enregistrement par jets d'encre et à l'appareil optique est évaluée et les résultats de cette in Example 1 above The adaptability of the recording medium to ink jet recording and to the optical apparatus is evaluated and the results of this
évaluation sont donnés dans le tableau II ci-dessous. evaluation are given in Table II below.
Exemple comparatif 2 On utilise, comme support d'enregistrement de faible transparence, du papier calque pour dessin, et on procède à un enregistrement par-jets d'encre conformément Comparative Example 2 Low-transparency recording medium is used as tracing paper for drawing, and ink-jet recording is carried out in accordance with the invention.
aux étapes décrites dans l'exemple 1 ci-dessus L'adaptabi- the steps described in Example 1 above.
lité du support d'enregistrement à un enregistrement par jets d'encre et à l'appareil optique est évaluée et les résultats de cette évaluation sont donnés dans le tableau II ci-dessous. Exemple comparatif 3 A l'aide d'une pellicule pour rétroprojecteur, disponible dans le commerce ("NP- DRY TRANSPARENCY", Canon Hanbai K K, Japon), on procède à un enregistrement par jets d'encre L'adaptabilité de ce support d'enregistrement à un enregistrement par jets d'encre et à l'appareil optique est évaluée de la même manière que celle décrite dans l'exemple 1 ci-dessus et les résultats de cette évaluation sont donnés The amount of recording medium to ink jet recording and the optical apparatus is evaluated and the results of this evaluation are given in Table II below. Comparative Example 3 Using a commercially available overhead projector film ("NP-DRY TRANSPARENCY", Canon Hanbai KK, Japan), ink jet recording is performed. recording to an ink jet recording and to the optical apparatus is evaluated in the same manner as described in Example 1 above and the results of this evaluation are given
dans le tableau 2 ci-dessous.in Table 2 below.
Exemple comparatif 4 La même pellicule pour rétroprojecteur que celle utilisée dans l'exemple comparatif 3 ci-dessus est stratifiée Comparative Example 4 The same overhead projector film as used in Comparative Example 3 above is laminated
en quatre couches et utilisée comme support d'enregistrement. in four layers and used as a recording medium.
On procède à un enregistrement par jets d'encre de la manière Ink jet recording is done in the same way
décrite dans l'exemple 1 ci-dessus On évalue ensuite l'adap- described in Example 1 above.
tabilité de ce support d'enregistrement à un enregistrement par jets d'encre et à l'appareil optique et les résultats tability of this recording medium to ink jet recording and to the optical apparatus and the results.
de cette évaluation sont donnés dans le tableau Il ci-dessous. of this evaluation are given in Table II below.
Exemple comparatif 5 La même pellicule pour rétroprojecteur que celle utilisée dans l'exemple comparatif 3 ci-dessus est stratifiée Comparative Example 5 The same overhead projector film as used in Comparative Example 3 above is laminated
en cinq couches et est utilisée comme support d'enregistre- in five layers and is used as a recording medium
ment Un enregistrement par jets d'encre est effectué de la même manière que dans l'exemple 1 ci-dessus Ensuite, Ink jet recording is performed in the same manner as in Example 1 above.
l'adaptabilité de ce support d'enregistrement à un enregis- the adaptability of this recording medium to a recording
trement par jets d'encre et à l'appareil optique est évaluée, by ink jets and to the optical apparatus is evaluated,
les résultats étant donnés dans le tableau Il ci-dessous. the results are given in Table II below.
Exemple 4Example 4
On utilise, comme base transparente, la même pellicule de "Mylar", traitée pour l'hydrophilité, que celle utilisée dans l'exemple 2 ci- dessus, sur laquelle la couche d'absorption d'encre, ayant la composition mentionnée ci-dessous, est appliquée par le procédé d'enduction à la barre, de manière que la couche appliquée atteigne, après séchage, une épaisseur de 10 am, l'enduction étant suivie d'un séchage de la couche appliquée, dans un four de séchage, As a transparent base, the same "Mylar" film treated for the hydrophilicity as used in Example 2 above, on which the ink absorption layer, having the composition mentioned above, is used is used. below, is applied by the coating method to the bar, so that the applied layer reaches, after drying, a thickness of 10 am, the coating being followed by drying of the applied layer, in a drying oven ,
pendant 10 minutes à une température de 50 'C. for 10 minutes at a temperature of 50 ° C.
Composition de la couche d'absorption d'encre Alcool polyvinylique, PVA217 (produit de Kurarary K K, Japon) 10 parties en poids Eau 90 parties en poids A l'aide de l'élément d'enregistrement ainsi obtenu, on procède à un enregistrement par jets d'encre de la même manière que celle décrite dans l'exemple 1 ci-dessus pour obtenir le sujet enregistré Ensuite, l'adaptabilité du support d'enregistrement à un enregistrement par jets d'encre et à l'appareil optique est évaluée conformément au procédé utilisé dans l'exemple 1 ci-dessus, et les Composition of the Ink Absorption Layer Polyvinyl alcohol, PVA217 (Kurarary KK product, Japan) 10 parts by weight Water 90 parts by weight With the aid of the recording element thus obtained, a recording is made by ink jets in the same manner as described in Example 1 above to obtain the recorded subject. Next, the adaptability of the recording medium to ink jet recording and to the optical apparatus is evaluated according to the method used in Example 1 above, and the
résultats sont donnés dans le tableau il ci-dessous. Results are given in Table II below.
Exemple 5Example 5
On utilise, comme base transparente, la même pellicule de "Mylar", traitée pour l'hydrophilité, que celle utilisée dans l'exemple 2 ci- dessus, pellicule sur As the transparent base, the same "Mylar" film treated for the hydrophilicity as used in Example 2 above is used.
laquelle la couche d'absorption d'encre, ayant la composi- which the ink absorption layer, having the composition
tion mentionnée ci-dessous, est appliquée par le procédé d'enduction à la barre de manière que la couche appliquée mentioned below, is applied by the coating process to the bar so that the applied layer
atteigne, après séchage, une épaisseur de 15 âm, l'enduc- reaches, after drying, a thickness of 15 μm, the
tion étant suivie d'un séchage de la couche appliquée, dans un four de séchage, pendant 15 minutes à une température de OC. Composition de la couche d'absorption d'encre Alcool polyvinylique, PVA-205 (produit de Kuraray K K, Japon) 20 parties en poids Bleu direct 86 du C I 0,5 partie en poids Eau 80 parties en poids A l'aide du support d'enregistrement ainsi obtenu, on procède à un enregistrement par jets d'encre de la même manière que celle décrite dans l'exemple-1 ci-dessus followed by drying of the applied layer in a drying oven for 15 minutes at a temperature of OC. Composition of the Ink Absorption Layer Polyvinyl alcohol, PVA-205 (Kuraray KK product, Japan) 20 parts by weight Direct blue 86 CI 0.5 part by weight Water 80 parts by weight Using the support thus obtained, ink jet recording is performed in the same manner as described in Example-1 above.
pour obtenir le sujet enregistré Ensuite, on évalue l'adap- to obtain the recorded subject Then, we evaluate the adaptation
tabilité du support-d'enregistrement à un enregistrement par tability of the recording medium to a recording by
jets d'encre et à l'appareil optique, conformément au pro- jets and the optical apparatus in accordance with the
cédé décrit dans l'exemple 1 ci-dessus, et les résultats described in Example 1 above, and the results
sont donnés dans le tableau 2 ci-dessous. are given in Table 2 below.
Il va de soi que de nombreuses modifications peu- It goes without saying that many modifications can
vent être apportées au support d'enregistrement décrit sans be made to the recording medium described without
sortir du cadre de l'invention.depart from the scope of the invention.
Tableau IITable II
Temps de fixage Taux de de l'encre transmission Densite Adaptabilité au Evéluation linéaire (%) de points rétroprojecteur Générale Exemple 1 10 minutes 32 1,0 o o " 2 15 " 78 1,1 o o 3 20 " 45 0,9 o o Fixing time Ink transmission rate Density Adaptability to linear evaporation (%) of points overhead projector General Example 1 10 minutes 32 1,0 o o "2 15" 78 1,1 o o 3 20 "45 0,9 o o
ExempleExample
Comparatif 1 7 jours 85 1,2 o X lComparative 1 7 days 85 1.2 o X l
" 2 1 " I 0,6 X X"2 1" I 0.6 X X
3 7 " 62 1,0 o X r 4 7 " 15 1,2 o X3 7 "62 1.0 o X r 4 7" 15 1.2 o X
7 " 9 1,2 A X7 "9 1.2 A X
Exemple 4 3 minutes 81 1,1 o o 3 " 12 0,9 o o o LM 1 o% t'> 0 x ri 1 7 Example 4 3 minutes 81 1.1 o o 3 "12 0.9 o o o LM 1 o% t '> 0 x ri 1 7
Claims (2)