DE3410828A1 - RECORDING ELEMENT - Google Patents
RECORDING ELEMENTInfo
- Publication number
- DE3410828A1 DE3410828A1 DE19843410828 DE3410828A DE3410828A1 DE 3410828 A1 DE3410828 A1 DE 3410828A1 DE 19843410828 DE19843410828 DE 19843410828 DE 3410828 A DE3410828 A DE 3410828A DE 3410828 A1 DE3410828 A1 DE 3410828A1
- Authority
- DE
- Germany
- Prior art keywords
- recording
- ink
- recording element
- ink jet
- transmission factor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Description
Die Erfindung betrifft ein Aufzeichnungselement für die Verwendung bei der Tintenstrahlaufzeichnung, das sich durch gute Transparenz und hohe Absorptionsfähigkeit für Tinte auszeichnet. The invention relates to a recording element for Used in ink jet recording, which is characterized by good transparency and high ink absorbency.
Aufzeichnungsflüssigkeiten werden seit langer Zeit verwendet, z.B. in Füllfederhaltern und dergleichen. Eine neuere Entwicklung stellt das sogenannte Tintenstrahlaufzeichnungssystera dar, bei dem ebenfalls Aufzeichnungsflüssigkeiten verwendet werden.Recording fluids have been used for a long time, e.g. in fountain pens and the like. A more recent development is the so-called ink jet recording system which also uses recording liquids will.
Beim Tintenstrahl-Aufzeichnungssystem erfolgt die Aufzeichnung von Bildern, indem nach verschiedenen Prinzipien Tröpfchen der Aufzeichnungsflössigkeit erzeugt werden. Diese Tröpfchen fliegen auf ein Aufzeichnungselement, auf dem die gewünschten Bilder aufgezeichnet werden sollen, und bleiben dort haften. Derartige Aufzeichnungssysteme haben insbesondere wegen ihrer geringen Geräuschentwicklung, ihrer hohen Aufzeichnungsgeschwindigkeit und der Möglichkeit zu mehrfarbigen Aufzeichnungen Beachtung gefunden. Als Aufzeichnungs-In the ink jet recording system, images are recorded by making droplets according to various principles the recording liquid can be generated. These droplets fly onto a recording element on which the desired images are to be recorded and remain there. Such recording systems have in particular because of their low noise generation, their high recording speed and the possibility of multicolored recordings received attention. As a recording
. .τ. 3* - —. .τ. 3 * - -
flüssigkeiten werden vorwiegend aus Gründen der Sicherheit und der guten Eignung wässrige Flüssigkeiten verwendet.liquids are mainly used for reasons of safety and suitability, aqueous liquids.
Als Aufzeichnungselemente für Tintenstrahl-Aufzeichnungssysteme wurde bisher im allgemeinen normales Papier verwendet. Gleichzeitig mit der Verbesserung der Eigenschaften der Tintenstrahl-Aufzeichnungsvorrichtungen, z.B. in bezug auf die Hochgeschwindigkeitsaufzeichnung oder die mehrfarbige Aufzeichnung, wurden neue Aufzeichnungselemente entwickelt und zum Einsatz gebracht. Diese sogenannten "Tintenstrahl-Aufzeichnungspapiere" sind aus einer Grundlage und einer auf der Grundlage vorgesehenen, porösen, Tinte absorbierenden Schicht, mit der die Absorptionsfähigkeit des Papiers für die Tinte erhöht werden soll, zusammengesetzt.Ordinary paper has heretofore been generally used as recording elements for ink jet recording systems. Simultaneously with the improvement of the properties of the ink jet recording devices, e.g. to the high-speed recording or the multicolored Recording, new recording elements were developed and put into use. These so-called "ink jet recording papers" are composed of a base and a base, porous, ink-absorbent Layer with which the absorption capacity of the paper for the ink is to be increased.
Um beim Tintenstrahl-Aufzeichnungssystem die Erzeugung von Bildern hoher Auflösung und hoher Bildqualität zu gewährleisten, müssen derartige Aufzeichnungselemente folgende Bedingungen erfüllen:In order to ensure the formation of high resolution and high image quality images in the ink jet recording system, Such recording elements must meet the following conditions:
1) Sie müssen die Tinte so rasch wie möglich absorbieren.1) You need to absorb the ink as soon as possible.
2) Wenn Tintenpunkte übereinander aufgebracht werden, darf der später aufgetragene Punkt nicht über dem früher aufgetragenen verlaufen.2) When ink dots are applied one on top of the other, the later applied dot must not be on top of the earlier applied get lost.
3) Die Vergrösserung des Durchmessers eines Tintenpunkts muss möglichst gering sein.3) The enlargement of the diameter of an ink dot must be as small as possible.
4) Die TirfEenpunkte müssen im wesentlichen die Form eines echten Kreises und somit glatte Ränder aufweisen.4) The entry points must essentially take the form of a have real circles and thus smooth edges.
5) Die Tintenpunkte müssen ihre hohe Dichte behalten, so dass die Umfangslinien nicht nachdunkeln.5) The ink dots must keep their high density so that the perimeter lines do not darken.
6) Die Aufzeichnungselemente müssen die guten Farbbildungseigenschaften der Tinte unterstützen.6) The recording elements must have good color-forming properties support the ink.
Beim Tintenstrahl-Aufzeichnungssystem wurden auch andere Arten von Aufzeichnungselementen verwendet, auf denen man Bilder erhält, die zur Oberflächenbetrachtung gedacht sind. Gleichzeitig mit der Verbesserung der Tintenstrahl-Aufzeichnungsverfahren und der starken Verbreitung der Tintenstrahl-Aufzeichnungsvorrichtungen wurden derartige Aufzeichnungselemente auch für die Verwendung bei anderen Anwendungszwecken in Betracht gezogen, wobei man die typischen Eigenschaften des Tintenstrahl-Aufζeichnungsverfahrens ausnutzt.Other types of recording elements have also been used in the ink jet recording system Receives images that are intended for surface viewing. Simultaneously with the improvement of ink jet recording methods and the proliferation of ink jet recording devices, such recording elements have become also considered for use in other applications, keeping the typical properties of the inkjet recording process.
Als von der Bildoberflächenbetrachtung abweichende Anwendungsgebiete seien erwähnt: Die Betrachtung von aufgezeichneten Bildern auf einer Bildwand,· indem man sie mittels einer optischen Vorrichtung, wie eines Diaprojektors, eines Overhead-Pro jektors und dergleichen, projiziert; Photomasken für Kontaktdrucker, gedruckte Schaltungen und dergleichen; Farbauszugsplatten zur Herstellung positiver Platten für den Farbdruck; Farbmosaikfilter (CMF) für die farbige An-As areas of application that differ from the viewing of the image surface the following should be mentioned: Viewing recorded images on a screen by viewing them using a optical device, such as a slide projector, an overhead pro projectors and the like, projected; Photomasks for contact printers, printed circuit boards and the like; Color separation plates for making positive plates for color printing; Color mosaic filter (CMF) for the colored
zeige mit Flüssigkristallen; und dergleichen.show with liquid crystals; and the same.
Durchsichtige Negative und Positive zur Verwendung in optischen Vorrichtungen und Verfahren der vorstehend genannten Art werden hergestellt, indem man Photographien aufnimmt oder eine direkte Aufzeichnung auf durchsichtigen Aufzeichnungselementen, die aus Kunststoffilmen oder dergleichen bestehen, durchführt. Neben diesen herkömmlichen Verfahren ermöglicht das Tintenstrahl-Aufzeichnungssystem bei Verwendung von durchsichtigen Aufzeichnungselementen eine Aufzeichnung mit erhöhter Geschwindigkeit und die Erzeugung von VoIlfarbenbildern von hoher Auflösung und guter Bildqualität, die in den vorerwähnten optischen Vorrichtungen und Verfahren eingesetzt werden können. Für derartige Zwecke soll das Aufzeichnungselement neben den vorerwähnten Eigenschaften, die bei der Tintenstrahlaufzeichnung notwendig sind, auch eine entsprechende Durchsichtigkeit aufweisen.Clear negatives and positives for use in the optical devices and methods of the aforesaid Types are produced by taking photographs or direct recording on transparent recording elements, made of plastic films or the like. In addition to these conventional methods the ink jet recording system uses clear recording elements to make a record at increased speed and the generation of full color images of high resolution and good image quality obtained in the aforementioned optical devices and methods can be used. For such purposes, the recording element should, in addition to the aforementioned properties, which are necessary for ink jet recording, also have a corresponding transparency.
Aufgabe der Erfindung ist es, ein Aufzeichnungselement für die Tintenstrahlaufzeichnung bereitzustellen, das neben der Oberflächenbildbetrachtung auch für andere Zwecke eingesetzt werden kann, z.B. in Diaprojektoren, Overhead-Projektoren, Kontaktdruckern und anderen optischen Vorrichtungen und Verfahren. Dieses Aufzeichnungselement soll sämtlichen Anforderungen, die bei Aufzeichnungselementen für die Tintenstrahlaufzeichnung gestellt werden, genügen.It is an object of the invention to provide a recording element for ink jet recording which, in addition to the Surface image viewing can also be used for other purposes, e.g. in slide projectors, overhead projectors, Contact printers and other optical devices and processes. This recording element should meet all requirements those of recording elements for ink jet recording are provided, are sufficient.
Gegenstand der Erfindung ist ein Aufzeichnungselement für die Tintenstrahlaufzeichnung, das eine durchsichtige Unterlage und eine auf der Unterlage vorgesehene, Tinte absorbierende Schicht aufweist, wobei das Aufzeichnungselement einen linearen Transmissionsfaktor von 10 Prozent oder mehr aufweist.The invention relates to a recording element for ink jet recording which comprises a transparent substrate and an ink absorbing layer provided on the base, the recording element has a linear transmission factor of 10 percent or more.
Nachstehend werden spezielle Materialien, die sich als durchsichtige Grundlage eignen, sowie Bestandteile und Mischungsverhältnisse der Tinte absorbierenden Schicht näher erläutertBelow are special materials that can be found to be clear Suitable basis, as well as components and mixing ratios of the ink-absorbing layer explained in more detail
Die durchsichtige Grundlage des erfindungsgemässen Aufzeichnungselements kann beispielsweise aus folgenden Materialien bestehen: Polyester, Cellulosediacetat, Cellulosetriacetat, Acrylpolymerisate, Cellophane (Handelsbezeichnung für regenerierte Cellulose), Celluloid (Handelsbezeichnung für einen aus Kampfer und Cellulosenitrat hergestellten Kunststoff), Polyvinylchlorid, Polycarbonat und andere Kunststoffmaterialien in Folien- oder Plattenform; sowie Glasplatten. The transparent base of the recording element according to the invention can for example consist of the following materials: polyester, cellulose diacetate, cellulose triacetate, Acrylic polymers, cellophane (trade name for regenerated Cellulose), celluloid (trade name for a plastic made from camphor and cellulose nitrate), Polyvinyl chloride, polycarbonate and other plastic materials in film or sheet form; as well as glass plates.
Die Tinte absorbierende Schicht des erfindungsgemässen Aufzeichnungselements kann unter Verwendung folgender Materialien, die zur Bildung einer kontinuierlichen Überzugsschicht von ausreichender Durchsichtigkeit auf den vorerwähnten Grundlagen geeignet sind, hergestellt werden: Stärke, Casein, Albumin, Gummi arabicum, Natriumalginat, Polyvinylalkohol, Polyacrylamid, Carboxymethylcellulose, Natrium-The ink-absorbing layer of the recording element according to the invention can be made using the following materials capable of forming a continuous coating layer of sufficient transparency on the aforesaid Basics are suitable to be produced: starch, casein, albumin, gum arabic, sodium alginate, polyvinyl alcohol, Polyacrylamide, carboxymethyl cellulose, sodium
polyacrylat, ionoraere Harze, Polyvinylacetat und "dergleichen. Diese Materialien werden einzeln oder in Kombination untereinander in einem entsprechend ausgewählten Lösungsmittel gelöst. Die Lösung wird schichtförmig auf die Grundlage aufgebracht und anschliessend getrocknet oder gekühlt. Je nach Bedarf können ein oder mehr anorganische Pigmente als Füllstoffe in einer Menge, die die Durchsichtigkeit des Aufzeichnungselements nicht beeinträchtigt, in der Tinte absorbierenden Schicht dispergiert werden, um die Absorptionsund Fixiereigenschaften der Aufzeichnungsflüssigkeit auf dem Aufzeichnungselement durch Bildung einer porösen Struktur auf der Oberfläche der Tinte absorbierenden Schicht zu verbessern. Beispiele für derartige Füllstoffe sind pulverisiertes Siliciumdioxid, Ton, Talcum, Diatomeenerde, Calciumcarbonat, Calciumsulfat, Titanoxid, Zinkoxid, Satinweiss, Aluminiumsilicat, Lithopone, Aluminiumoxid, Zeolith und dergleichen.polyacrylate, ionic resins, polyvinyl acetate and "the like." These materials are used individually or in combination with one another in an appropriately selected solvent solved. The solution is applied in layers to the base and then dried or chilled. Depending on requirements, one or more inorganic pigments can be used as fillers in an amount which does not impair the transparency of the recording element, in the absorbent ink Layer are dispersed in order to improve the absorption and fixing properties of the recording liquid on the Recording element by forming a porous structure to improve the surface of the ink absorbing layer. Examples of such fillers are powdered silicon dioxide, Clay, talc, diatomaceous earth, calcium carbonate, calcium sulfate, titanium oxide, zinc oxide, satin white, aluminum silicate, Lithopone, alumina, zeolite and the like.
Die Tinte absorbierende Schicht kann nach verschiedenen Verfahren aufgebracht werden, z.B. durch Walzenauftrag, Messerauftrag, Luftbürstenauftrag, Stabauftrag, Auftrag von heissen Schmelzen und dergleichen.The ink absorbing layer can be applied by various methods e.g. by roller application, knife application, air brush application, Rod application, application of hot melts and the like.
Der Ausdruck "linearer Transmissionsfaktor" (T '(%) bezieht sich auf den Wert, den man erhält, indem man zunächst den spektralen Transmissionsfaktor von geradlinigem Licht misst, das senkrecht auf eine Probe auftrifft, durch die Probe hindurchtritt, einen in einer Entfernung von mindestens 8 cm von der Probe und in der Verlängerung des einfallenden Lichtstrahls aufgestellten Lichtaufnahmeschlitz durchläuft und in einem Detektor emp-The term "linear transmission factor" (T '(%) refers to the Value obtained by first measuring the spectral transmission factor of straight-line light that strikes a sample perpendicularly the sample passes through, one placed at a distance of at least 8 cm from the sample and in the extension of the incident light beam Passes through the light receiving slit and received in a detector
fangen wird. Anschliessend wird ein Wert Y des Farbwerts aus dem gemessenen spektralen Transmissionsfaktor berechnet. Schliesslich wird der lineare Transmissionsfaktor gemäss folgender Gleichung berechnet:will catch. Then it becomes a value Y of the color value calculated from the measured spectral transmission factor. Finally, the linear transmission factor is according to calculated using the following equation:
T = Y/Yo χ 100 (1)T = Y / Yo χ 100 (1)
Dabei bedeutet T den linearen Transmissionsfaktor, Y den Y-Wert der Probe und Yo den Y-Leerwert.T means the linear transmission factor, Y the Y value the sample and Yo the Y blank.
Der lineare Transmissionsfaktor kann beispielsweise unter Verwendung des registrierenden Spektrophotometers Modell (Hitachi Ltd., Japan) gemessen werden. Demgemäss bezieht sich der erfindungsgemäss herangezogene lineare Transmissionsfaktor auf geradliniges Licht, so dass ein Unterschied zur Ermittlung der Durchsichtigkeit eines Gegenstands unter Verwendung von diffusem Licht durch Bestimmung des diffusen Transmissionsfaktors (Ermittlung des Transmissionsfaktors einer Probe unter Einschluss von diffusem Licht, indem man eine Integrationskugel an der Probenrückseite anordnet) oder zur Ermittlung der Undurchsichtigkeit (Ermittlung des Undurchsichtigkeitsgrads einer Probe aus dem Verhältnis der Lichttransmission bei Anbringen einer weissen Platte an der Probenrückseite zum entsprechenden Wert beim Anbringen einer schwarzen Platte) besteht. Da bei derartigen optischen Vorrichtungen und Verfahren es auf das Verhalten von geradlinigem Licht ankommt, ist der lineare Transmissionsfaktor des Aufzeichnungselements von besonderer Bedeutung für die Bewertung der Durchsichtigkeit der bei derartigen Vorrichtungen und Verfahren zu verwendenden Aufzeichnungselementen.The linear transmission factor can be modeled using the registering spectrophotometer, for example (Hitachi Ltd., Japan). The linear transmission factor used according to the invention relates accordingly on rectilinear light, making a difference for determining the transparency of an object using of diffuse light by determining the diffuse transmission factor (determination of the transmission factor a sample with inclusion of diffuse light by placing an integrating sphere on the back of the sample) or to determine the opacity (determination of the degree of opacity of a sample from the ratio of Light transmission when a white plate is attached to the back of the sample to the corresponding value when a black plate). Since such optical devices and methods rely on the behavior of rectilinear When light arrives, the linear transmission factor of the recording element is of particular importance for the Assessment of the transparency of the recording elements to be used in such devices and methods.
Zur Betrachtung eines beispielsweise mittels eines Overhead-Projektors
projizierten Bilds ist es zur Erzielung eines klaren Bilds von hohem Kontrast zwischen bedruckten und unbedruckten
Bereichen erforderlich, dass die unbedruckten Bereiche des projizierten Bilds ausreichend hell sind, d.h.
dass der lineare Transmissionsfaktor des Aufzeichnungselements einen bestimmten Mindestwert besitzt. Bei unter Verwendung
eines Testbilds für Overhead-Projektoren durchgeführten Tests hat es sich gezeigt, dass der lineare Transmissionsfaktor
des Aufzeichnungselements zur Erzielung eines für die vorerwähnten Zwecke ausreichenden Bilds mindestens
10 Prozent oder mehr betragen muss. Vorzugsweise beträgt
dieser Wert zur Erzielung von noch klareren Bildern 30 Prozent oder darüber. Infolgedessen weist das erfindungsgemässe
Aufzeichnungselement einen linearen Transmissionsfaktor von 10 Prozent oder mehr auf.To view an image projected by means of an overhead projector, for example, it is necessary to achieve a clear image of high contrast between the printed and unprinted areas that the unprinted areas of the projected image are sufficiently bright, ie
that the linear transmission factor of the recording element has a certain minimum value. In tests carried out using a test image for overhead projectors, it has been found that the linear transmission factor of the recording element must be at least 10 percent or more in order to achieve an image which is sufficient for the aforementioned purposes. Preferably is
this value to achieve even clearer images 30 percent or more. As a result, the inventive recording element has a linear transmission factor of 10 percent or more.
Das erfindungsgemässe Aufzeichnungselement kann durch Färben der durchsichtigen Grundlage oder der Tinte absorbierenden Schicht auch als chromatisches Aufzeichnungselement eingesetzt werden.The recording element of the present invention can be made absorbent by coloring the transparent base or the ink Layer can also be used as a chromatic recording element.
Wie bereits erwähnt, besitzt das Aufzeichnungselement für die Tintenstrahlaufzeichnung, das aus der durchsichtigen Grundlage und der auf der Grundlage aufgebrachten, Tinte absorbierenden Schicht konstruiert ist, hervorragende Tintenabsorptionseigenschaften und eignet sich daher für Hochge-As mentioned above, the recording element for ink jet recording is composed of the transparent base and the ink-absorbing layer applied thereon is constructed of excellent ink-absorbing properties and is therefore suitable for high
schwindigkeitsaufzeichnungen und polychromatische Aufzeichnungen. Somit können die Aufzeichnungselemente in verschiedenen optischen Vorrichtungen und Verfahren, wie Diaprojektoren, Overhead-Projektoren, Kontaktdruckern und dergleichen, eingesetzt werden.speed records and polychromatic records. The recording elements can thus be used in various optical devices and processes, such as slide projectors, Overhead projectors, contact printers and the like can be used.
Machstehend wird die Erfindung anhand der Beispiele näher erläutert. Änderungen in bezug auf Materialien und Bestandteile sind möglich, ohne dass der Erfindungsbereich verlassen wird.The invention is explained in more detail below with the aid of the examples explained. Changes in materials and components are possible without departing from the scope of the invention will.
Als durchsichtige Grundlage wird eine 80 ^im dicke Folie aus Cellulosetriacetat (Produkt der Fuji Photo Film Co., Ltd., Japan) verwendet. Darauf wird eine Tinte absorbierende Schicht der nachstehend angegebenen Zusammensetzung durch Stabauftrag so aufgebracht, dass die Dicke der beschichteten Folie nach dem Trocknen lOO^um beträgt. Die Trocknung des aufgebrachten Überzugs erfolgt durch 1-stündige Behandlung bei 800C in einem Trockenschrank.A 80 µm thick film made of cellulose triacetate (product of Fuji Photo Film Co., Ltd., Japan) is used as the transparent base. An ink-absorbing layer of the composition given below is applied to this by bar application so that the thickness of the coated film after drying is 100 μm. The applied coating is dried by treatment for 1 hour at 80 ° C. in a drying cabinet.
Polyvinylalkohol, "PVA-117" ■Polyvinyl alcohol, "PVA-117" ■
(Produkt der Kuraray K.K., Japan) 10 Gewichtsteile pulverisiertes Siliciumdioxid, "NIPSIL E 200" (Produkt der(Product of Kuraray K.K., Japan) 10 parts by weight of powdered silicon dioxide, "NIPSIL E 200" (product of
Nippon Silica Kogyo K.K.) 0,1 "Nippon Silica Kogyo K.K.) 0.1 "
Wasser 90 "Water 90 "
Mit dem auf diese Weise hergestellten Aufzeichnungselement werden Tintenstrahlaufzeichnungen unter Verwendung wässriger Tinten in den vier Farben gelb, rot, blau und schwarz, wie in Tabelle I angegeben, durchgeführt. Hierzu wird eine Aufzeichnungsvorrichtung verwendet, die einen nach Bedarf arbeitenden Tintenstrahl-Aufzeichnungskopf aufweist, der die Aufzeichnungsflüssigkeit mittels eine Piezovibrators (Durchmesser der Öffnung 50 um, Piezovibrator-Steuerspannung 60 V und Steuerfrequenz 4KHz) ejiziert.With the recording element prepared in this way, ink jet recordings using aqueous media are made Inks in the four colors of yellow, red, blue and black as indicated in Table I were carried out. To do this, a A recording apparatus having an on-demand ink jet recording head is used, the the recording liquid by means of a piezovibrator (diameter of the opening 50 µm, piezovibrator control voltage 60 V and control frequency 4KHz).
Tabelle I Art der Tinte Zusammensetzung Table I Type of Ink Composition
(Farbstoff) Farbstoff Diäthylenglykol Wasser(Dye) dye diethylene glycol water
Gelbe Tinte
(C.I.-Säuregelb 23) 2 Gew.-teile 15 Gew.-teile 85 Gew.-teileYellow ink
(CI acid yellow 23) 2 parts by weight 15 parts by weight 85 parts by weight
Rote TinteRed ink
CC.I.-Säurerot 92) 2 " 15 " 85 "CC.I. Acid Red 92) 2 "15" 85 "
Blaue TinteBlue ink
(C.I.-Direktblau 86) 2 " 15 " 85 "(C.I. Direct Blue 86) 2 "15" 85 "
Schwarze TinteBlack ink
(CI.-Direktschwarz 19) 2 " 15 " 85 "(CI.-Direktschwarz 19) 2 "15" 85 "
Die Eignung des Aufzeichnungselements für die Tintenstrahlaufzeichnung wird bewertet, indem man die Tintenfixierungszeit und die Punktdichte misst. Die Eignung für die optische Vorrichtung wird bewertet, indem man den linearen Transmissionsfaktor misst und einen Eignungstest mit einem Overheadprojektor als Beispiel für eine optische Vorrichtung durchführt.The suitability of the recording element for ink jet recording is evaluated by measuring the ink fixing time and the dot density. Suitability for the optical Apparatus is assessed by measuring the linear transmission factor and an aptitude test with an overhead projector as an example of an optical device.
Die Tintenfixierungszeit wird gemessen, indem man nach beendeter Tintenstrahlaufzeichnung die aufgezeichnete Probe bei Raumtemperatur bis zur vollständigen Trocknung und Fixierung der Tinte auf dem Aufzeichnungselement stehenlässt, so dass die Tinte bei Berührung des aufgezeichneten Bereichs mit einem Finger nicht mehr haften bleibt. Auf diese Weise ermittelt man die Zeitspanne ab Beendigung des Aufzeichnungsvorgangs bis zur Trocknung der Tinte. The ink fixing time is measured by taking the recorded sample after the ink jet recording is finished leave to stand at room temperature until the ink has completely dried and fixed on the recording element, so that the ink no longer adheres when a finger touches the recorded area. In this way the time from the end of the recording process to the drying of the ink is determined.
Die Punktdichte wird an schwarzen Tintenpunkten unter Verwendung eines "SAKURA Micro-Densitometers, PDM-5" (Konishiroku Photo Industries, Co., Ltd.) gemessen. Der lineare Transmissionsfaktor wird gemäss vorstehender Gleichung (1) unter Verwendung des registrierenden Spektrophotometers Modell (Hitachi, Ltd., Japan) ermittelt, wobei die Probe bei der Messung des spektralen Transmissionsfaktors sich in einem Abstand von etwa 9 cm vom Lichtaufnahmefenster befindet.The dot density is measured on black ink dots using a "SAKURA Micro-Densitometer, PDM-5" (Konishiroku Photo Industries, Co., Ltd.). The linear transmission factor is calculated according to the above equation (1) under Using the registering spectrophotometer model (Hitachi, Ltd., Japan) determined with the sample at the Measurement of the spectral transmission factor is at a distance of about 9 cm from the light receiving window.
Die Eignung für die Overhead-Projektion wird bewertet, indem
man das aufgezeichnete Bild mittels eines Overhead-Projektors auf eine Eildwand projiziert und das projezierte
Bild mit dem blossen Auge betrachtet. Dabei gelten folgende Bewertungsmasstäbe:
o: Der unbedruckte Bereich ist hell. Der bedruckte Bereich weist eine hohe optische Dichte auf. Das projizierte BildThe suitability for overhead projection is assessed by projecting the recorded image onto a projection screen by means of an overhead projector and observing the projected image with the naked eye. The following evaluation criteria apply:
o: The unprinted area is light. The printed area has a high optical density. The projected image
ist klar und kontrastreich.is clear and rich in contrast.
Δ: Der unbedruckte Bereich ist etwas dunkel. Der bedruckte Bereich weist eine geringfügig niedrigere optische Dichte auf. Der Kontrast des projizierten Bilds ist verringert.Δ: The unprinted area is a little dark. The printed area has a slightly lower optical density on. The contrast of the projected image is decreased.
X: Der unbedruckte Bereich ist dunkel. Der bedruckte Bereich weist eine sehr geringe optische Dichte auf. Das projizierte Bild ist dunkel und schwer erkennbar. Das aufgezeichnete Bild sieht so dunkel aus, dass sich bedruckte und unbedruckte Bereiche nicht unterscheiden lassen.X: The unprinted area is dark. The printed area has a very low optical density. That projected Image is dark and difficult to see. The recorded image looks so dark that it has been printed and unprinted areas cannot be distinguished.
Aufgrund der vorstehenden Ergebnisse wird eine allgemeine Bewertung durchgeführt, ob sich das Aufzeichnungselement für die erfindungsgemässen Zwecke eignet oder nicht. Die Ergebnisse sind in Tabelle II zusammengestellt.Based on the above results, a general evaluation is made as to whether the recording element is suitable for the purposes according to the invention are suitable or not. The results are summarized in Table II.
Als durchsichtige Grundlage wird eine 80 um dicke Folie aus "Mylar" (Polyäthylenterephthalat), die einer Hydrophilisierungsbehandlung unterzogen worden ist, verwendet (ICI, Großbritannien). Darauf wird eine Tinte absorbierende Schicht der nachstehend angegebenen Zusammensetzung durch Stabauftrag so aufgetragen, dass sich nach der Trocknung eine beschichtete Folie von 100 um Dicke ergibt. Die Trocknung des aufgebrachten Überzugs wird 30 Minuten, bei 30°C in einem Trockenschrank durchgeführt.An 80 µm thick film made of "Mylar" (polyethylene terephthalate), which is subjected to a hydrophilization treatment, is used as a transparent base has been used (ICI, UK). An ink absorbing layer as shown below is then formed Composition applied by stick application in such a way that after drying a coated film with a thickness of 100 μm results. The applied coating is dried for 30 minutes at 30 ° C. in a drying cabinet.
Zusammensetzung der Tinte absorbierenden Schicht Albumin (aus Eiweiß, Tokyo Kasei Composition of the ink-absorbing layer t albumin (made from egg white, Tokyo Kasei
Kogyo K.K.) 10 GewichtsteileKogyo K.K.) 10 parts by weight
Wasser 90 "Water 90 "
Unter Verwendung dieses Aufzeichnungselements wird gemäss Beispiel 1 eine Tintenstrahlaufzeichnung durchgeführt. Die Bewertung erfolgt gemäss Beispiel 1. Die Ergebnisse sind in Tabelle II zusammengestellt.Using this recording element, ink jet recording was carried out in accordance with Example 1. the Evaluation is carried out according to example 1. The results are in Table II compiled.
Die in Beispiel 2 verwendete, einer Hydrophilisierungsbehandlung
unterzogene "Mylar"-Folie wird als durchsichtige
Grundlage verwendet. Eine Tinte absorbierende Schicht der nachstehend angegebenen Zusammensetzung wird darauf durch
Auftrag einer heissen Schmelze, die man anschliessend auf Raumtemperatur abkühlen lässt, aufgebracht.The hydrophilization-treated "Mylar" film used in Example 2 is found to be transparent
Basis used. An ink-absorbing layer of the composition given below is applied to it by applying a hot melt, which is then allowed to cool to room temperature.
Zusammensetzung der Tinte absorbierenden Schicht Additionally at mensetzung the ink layer absorbi e leaders
Ionomeres Harz ("SURLYN", E.I. du PontIonomeric resin ("SURLYN", E.I. du Pont
de Nemours & Co., V.St.A.) 100 Gewichtsteilede Nemours & Co., V.St.A.) 100 parts by weight
C.I.-Pigmentblau ("FASTGEN BLUEC.I. pigment blue ("FASTGEN BLUE
5030L", Dai-Nippon Ink. Co., Ltd.) 0,1 "5030L ", Dai-Nippon Ink. Co., Ltd.) 0.1"
Man erhält ein Aufzeichnungselement mit einer gefärbten, Tinte absorbierenden Schicht.A recording element having a colored, ink-absorbing layer is obtained.
Unter Verwendung dieses Aufzeichnungselements wird eine Tintenstrahlaufzeichnung gemäss Beispiel 1 durchgeführt. Die Bewertung erfolgt gemäss Beispiel 1.Ink jet recording according to Example 1 is carried out using this recording element. The evaluation is carried out according to example 1.
Vergleichsbeispiel 1 Compare example 1
Die in Beispiel 2 verwendete, einer Hydrophilisierungsbehandlung unterworfene "Mylar"-Folie wird ohne Auftrag einer Tinte absorbierenden Schicht als Aufzeichnungselement verwendet. Die Aufzeichnung wird gemäss Beispiel 1 durchgeführt. Die Bewertung erfolgt gemäss Beispiel 1. Die Ergebnisse sind in Tabelle II zusammengestellt.The "Mylar" film used in Example 2 and subjected to a hydrophilization treatment is made without application of a Ink absorbent layer used as a recording element. The recording is carried out according to Example 1. The evaluation is carried out according to Example 1. The results are summarized in Table II.
Als Aufzeichnungselement geringer Durchsichtigkeit wird Pauspapier für Zeichenzwecke verwendet. Die Tintenstrahlaufzeichnung erfolgt gemäss Beispiel 1. Die Bewertung erfolgt ebenfalls gemäss Beispiel 1. Die Ergebnisse sind in Tabelle II zusammengestellt.As a low transparency recording element Tracing paper used for drawing purposes. The inkjet recording is carried out according to example 1. The evaluation is also carried out according to example 1. The results are in Table II compiled.
Vergleichsbeispie1_3 Comparative example 1_3
Die Tintenstrahlaufzeichnung wird mit einer handelsüblichen Folie für die Overhead-Frojektion ("NP-DRY TRANSPARENCY", Canon Hanbai K.K., Japan) durchgeführt. Die Aufzeichnung und die Bewertung erfolgt gemäss Beispiel 1. Die Ergebnisse sind in Tabelle II zusammengestellt.The inkjet recording is done with a commercially available film for overhead projection ("NP-DRY TRANSPARENCY", Canon Hanbai K.K., Japan). The recording and the evaluation are carried out according to Example 1. The results are compiled in Table II.
Vergleichsbeispiel 4 Ver gle ego for 4
Die F.olie für die Overhead-Projektion gerr.äss Vergleichsbeispiel 3 wird in vier Schichten laminiert und als Aufzeichnungselement verwendet. Die Aufzeichnung und die BewertungThe foil for the overhead projection according to the comparative example 3 is laminated in four layers and used as a recording element. The record and the evaluation
erfolgt gemäss Beispiel 1. Die Ergebnisse sind in Tabelle II zusammengestellt.takes place according to Example 1. The results are shown in Table II compiled.
Die Folie für die Overhead-Projektion gemäss Vergleichsbeispiel 3 wird in fünf Schichten laminiert und als Aufzeichnungselement verwendet. Die Aufzeichnung und die Bewertung erfolgen gemäss Beispiel 1. Die Ergebnisse sind in Tabelle II zusammengestellt .The film for the overhead projection according to the comparative example 3 is laminated in five layers and used as a recording element. The recording and the evaluation take place according to Example 1. The results are summarized in Table II .
Als durchsichtige Grundlage wird die einer Hydrophilisierungsbehandlung unterzogene "Mylar"-Folie von Beispiel 2 verwendet. Darauf wird eine Tinte absorbierende Schicht der nachstehend angegebenen Zusammensetzung durch Stabauftrag so aufgebracht, dass die Dicke des aufgebrachten Überzugs nach 10-minütigem Trocknen bei 5O0C in einem Trockenschrank 10^m beträgt.The "Mylar" film of Example 2 subjected to a hydrophilization treatment is used as the transparent base. Thereon an ink absorbing layer of the following composition is applied by bar coating so that the thickness of the applied coating after 10 minutes drying at 5O 0 C in a drying cabinet is 10 ^ m.
Zusammensetzung der Tinte absorbierenden Schicht Polyvinylalkohol, PVA-217 Zusamm e nset to ng of the ink absorb ere i layer of polyvinyl alcohol, PVA-217
(Kuraray K.K., Japan) 10 Gewichtsteile(Kuraray K.K., Japan) 10 parts by weight
Wasser 90 »Water 90 »
Unter Verwendung dieses Aufzeichnungselements wird gemäss Beisp'iel 1 eine Tintenstrahlaufzeichnung durchgeführt. Die Bewertung erfolgt gemäss Beispiel 1. Die Ergebnisse sind in Tabelle II zusammengestellt.Using this recording element, according to Example 1, ink jet recording was performed. the Evaluation is carried out according to Example 1. The results are summarized in Table II.
"-' 17 -"- '17 -
Als durchsichtige Grundlage wird die einer Hydrophilisierungsbehandlung unterzogene "Mylar"-Folie gemäss Beispiel 2 verwendet. Darauf wird eine Tinte absorbierende Schicht der nachstehend angegebenen Zusammensetzung durch Stabauftrag so aufgebracht, dass die Dicke des aufgebrachten Überzugs nach dem .Trocknen 15 pm beträgt. Die Trocknung der aufgebrachten Schicht wird 15 Minuten bei 500C in einem Trockenschrank durchgeführt.The "Mylar" film subjected to a hydrophilization treatment according to Example 2 is used as the transparent base. An ink-absorbing layer of the composition given below is applied to this by bar application so that the thickness of the applied coating after drying is 15 μm. The applied layer is dried for 15 minutes at 50 ° C. in a drying cabinet.
Zusammensetzung der Tinte absorbierenden Schicht Polyvinylalkohol, PVA-205 The composition of the ink absorbing layer is polyvinyl alcohol, PVA-205
(Kuraray K.K., Japan) 20 Gewichtsteile(Kuraray K.K., Japan) 20 parts by weight
C.I.-Direktschwarz 86 0,5 "C.I. direct black 86 0.5 "
Wasser 80 "Water 80 "
Unter Verwendung dieses Aufzeichnungselements wird gemäss Beispiel 1 eine Tintenstrahlaufzeichnung durchgeführt. Die Bewertung erfolgt gemäss Beispiel 1. Die Ergebnisse sind in Tabelle II zusammengestellt.Using this recording element, ink jet recording was carried out in accordance with Example 1. the Evaluation is carried out according to Example 1. The results are summarized in Table II.
zeitInk fixation
Time
dichtePoint
density
Overhead-ProjektionSuitability for the
Overhead projection
BewertungGeneral
valuation
missionsgrad (%)linear trans
emission level (%)
beispiel 1Comparison
example 1
O OO NJ OOO OO NJ OO
Claims (2)