JPS6149883A - Recording material - Google Patents

Abstract

PURPOSE:To enhance ink receptivity and clearness of recorded images, by constituting a recording material of an ink-holding layer comprising a water base ink absorbing resin, an ink-permeable layer comprising a resin comparable to or inferior to the above resin in hydrophilicity and a particulate material layer. CONSTITUTION:The ink-holding layer comprising a water base ink absorbing resin, the ink-permeable layer comprising a resin comparable to or inferior to the above resin in hydrophilicity, and the particulate material layer are laminated on a base to produce the recording material The ink absorbing resin may be a hydrophilic natural resin such as albumin, a hydrophilic synthetic resin such as polyamide and polyurethane, or the like. The thickness of the ink-holding layer is preferably 0.5-30mum, and that of the ink-permeable layer is preferably 1-5mum. A particulate material for forming the particulate material layer is preferably a fine powder having a particle diameter of not larger than 20mum, and may be an inorganic particulate material such as silica and clay or an organic particulate material such as calcium stearate.

Description

【発明の詳細な説明】 （産業上の利用分野） 本発明は、インクジェット記録法に好適に用も１られる
被記録材に関し、特にインク受容性と記録画像の鮮明性
等に優れ、１つ該被記録材が透光性被記録材であるとき
は、インク受容性とともに透光性に優れた被記録材に関
する。Detailed Description of the Invention (Industrial Application Field) The present invention relates to a recording material that is suitably used in inkjet recording methods, and particularly has excellent ink receptivity and sharpness of recorded images, and is one of the applicable recording materials. When the recording material is a translucent recording material, it relates to a recording material that is excellent in ink receptivity and light transmission.

（従来の技術） インクジェット記録法は、種々のインク（記録液）吐出
方式、例えば、静電吸引方式、圧電素子を用いて記録液
に機械的振動また変移を与える方式、記録液を加熱して
発泡させ、その圧力を利■する方式等により、インクの
小滴を発生さて飛翔させ、それらの一部若しくは全部を
紙などの被記録材に刺着させて記録を行うものであるが
、騒音の発生が少なく、高速印字、多色印字の行なえる
記録法として注目されている。(Prior Art) The inkjet recording method uses various ink (recording liquid) ejection methods, such as an electrostatic suction method, a method that applies mechanical vibration or displacement to the recording liquid using a piezoelectric element, and a method that applies mechanical vibration or displacement to the recording liquid using a piezoelectric element. Recording is performed by creating small ink droplets that are made to fly and stick to a recording material such as paper using a method that uses foaming and the resulting pressure. This method is attracting attention as a recording method that produces fewer blemishes and can perform high-speed printing and multicolor printing.

インクジェット記録用のインクとしては、安全性、記録
特性の面から、主に水を主成分とするものが使用され、
ノズルの目詰り防止および吐出特性の向上のために多価
アルコール等が添加されている場合が多い。Inks for inkjet recording are mainly water-based in terms of safety and recording properties.
Polyhydric alcohols and the like are often added to prevent nozzle clogging and improve ejection characteristics.

このインクジェット記録法に使用される被記録材としと
は、従来、通常の紙やインクジェット記録用紙と称され
る基材−Ｌに多孔質のインク吸収層を設けてなる被記録
材が使用されてきた。しかし、記録の高速化あるいは多
色化等、インクジェット記録装置の性能の向−Ｌと普及
に伴ない。The recording material used in this inkjet recording method has conventionally been a recording material made of ordinary paper or a base material L called inkjet recording paper provided with a porous ink absorption layer. Ta. However, as the performance of inkjet recording apparatuses improves and becomes more widespread, such as faster recording and multicolor recording.

被記録材に対してもより高度で広範な特性が要求されつ
つある。すなわち、高解像度、高品質の記録画像を得る
ためのインクジェット記録用の被記録材としては、 （１）インクの被記録材への定着が可及的速やかである
こと、 （２）インクドツトが重複した場合でも、後でイ・１着
したインクが前に付着したドラｊ・中に／ｉすれ出さな
いこと、 （３）インク液滴が被記録材上である程度拡散するが、
インクドツトの径が必要以上に大きくならず、所望の大
きさになること、 （４）インクドツトの形状が真円に近く、またその円周
が滑めらかであること、 （５）インクドラ）・のＯＤ（光学濃度）が高く。Recording materials are also required to have more sophisticated and wide-ranging properties. In other words, in order to obtain high-resolution, high-quality recorded images, the recording material for inkjet recording must (1) be able to fix the ink to the recording material as quickly as possible, and (2) have overlapping ink dots. (3) Although the ink droplets will spread to some extent on the recording material,
(4) The shape of the ink dot is close to a perfect circle and its circumference is smooth; (5) The ink dot diameter is the desired size; has a high OD (optical density).

ドラ）・周辺がぼけないこと、 等の基本的諸要求を満足させる必要がある。Dora)・The surrounding area should not be blurred, It is necessary to satisfy basic requirements such as:

更に、多色インクジェット記録法によりカラー写真に匹
敵する程度の高解像度の記録画質を得るには、上記要求
性能に加え、 （６）インクの着色成分の発色性に優れたものであるこ
と、 （７）インクの色の数と同数の液滴が同一箇所に重ねて
付着することがあるので、インク定着性が特に優れてい
ること、 （８）表面に光沢があること１ 、（９）白色度の高いこと、 （］０）プリンターにかけたときに、スムースな搬送が
可能なこと、 等の性能が加重して要求される。Furthermore, in order to obtain high-resolution recorded image quality comparable to color photography using multicolor inkjet recording, in addition to the above-mentioned required performance, (6) the coloring components of the ink must have excellent color development; 7) Since the same number of droplets as the number of ink colors may adhere to the same spot, the ink fixation properties are particularly excellent; (8) The surface must be glossy1; (9) White color ()0) Smooth conveyance when applied to a printer, etc. are required.

また、インクジェット記録法による記録画像は、従来は
専ら表面画像観察用に使用されてきたが、インクジェッ
ト記録装置の性能の向上や普及に伴ない表面画像観察用
以外の用途に適した被記録材が要求されつつある。表面
画像観察用以外の被記録材の用途としては、スライドや
０ＨＰ（オーバーヘットプロジェクタ−）等の光学機器
により、記録画像をスクリーン等へ投影して、それらの
画像を観察するのに用いるもの、カラー印刷のポジ版を
作成する際の色分解版、液晶等のカラーディスプレイに
用いるＣＭＦ（カラーモザイクフィルター）等が挙げら
れる。In addition, images recorded by inkjet recording have traditionally been used exclusively for surface image observation, but as the performance of inkjet recording devices has improved and become more widespread, recording materials suitable for purposes other than surface image observation have become available. It is becoming demanded. Applications of recording materials other than surface image observation include those used to project recorded images onto a screen or the like using an optical device such as a slide or OHP (overhead projector) and observe those images; Examples include color separation plates used to create positive plates for color printing, and CMF (color mosaic filters) used in color displays such as liquid crystals.

被記録材が表面画像観察用に使用される場合には、主に
記録画像の拡散光が観察されるのに対し、これらの用途
における被記録材においては主に記録画像の透過光が問
題となる。従って、透光性、特に直線透光率に優れたも
のであることが前述の一般的なインクジェット記録用の
被記録材の要求性能に加重されて要求される。When a recording material is used for surface image observation, the diffused light of the recorded image is mainly observed, whereas for recording materials used in these applications, the problem is mainly the transmitted light of the recorded image. Become. Therefore, it is required to have excellent light transmittance, especially linear light transmittance, in addition to the above-mentioned performance requirements of the general recording material for inkjet recording.

（発明が解決しようとしている問題点）しかしながら、
これら要求性能を全て満たした被記録材は未だ知られて
いないのが実状である。□また、従来の表面画像観察用
の被記録材の多くは、表面に多孔性のインク吸収層を設
け、その多孔性空隙中に記録液を吸収させ記録剤を定着
させる方式を用いている。(The problem that the invention is trying to solve) However,
The reality is that there is still no known recording material that satisfies all of these required performances. □Furthermore, most conventional recording materials for surface image observation use a method in which a porous ink absorbing layer is provided on the surface, and the recording liquid is absorbed into the porous voids to fix the recording agent.

一方、インク吸収層の表面が非多孔性の場合には、記録
実施後インク中の多価アルコール等の不揮発性成分が被
記録材表面に長時間残存し、インクの乾燥定着時間が長
いために、記録画像に接触すると衣服が汚れたり、記録
画像が損なわれたりするという欠点があった。On the other hand, when the surface of the ink absorption layer is non-porous, non-volatile components such as polyhydric alcohols in the ink remain on the surface of the recording material for a long time after recording, and the drying and fixing time of the ink is long. However, there are disadvantages in that clothing may get dirty or the recorded image may be damaged if it comes into contact with the recorded image.

本発明の目的は、特にインク受容性および記録画像の鮮
明性に優れたインクジェット記録用の被記録材を提供す
ることにある。An object of the present invention is to provide a recording material for inkjet recording that is particularly excellent in ink receptivity and the clarity of recorded images.

本発明の更にもラ一つの目的は、スライドやＯＨＰ等の
光学機器により記録画像をスクリーン等への投影により
観察に用いるもの、カラー印刷のポジ版を作成する際の
色分解版、あるいは液晶等のカラーディスプレイに用い
るＣＭＦ等の透過光観測用に用いることのできるインク
ジェット記録用の透光性被記録材を提供することにある
。A further object of the present invention is to use an optical device such as a slide or an OHP to project a recorded image onto a screen for observation, a color separation plate for creating a positive plate for color printing, or a liquid crystal display. An object of the present invention is to provide a translucent recording material for inkjet recording that can be used for transmitted light observation such as CMF used in color displays.

上記および他の本発明の目的は、以下の本発明のよって
達成される。The above and other objects of the invention are achieved by the following invention.

（発明の開示） すなわち、本発明は、インク保持層とインク透過層とを
有する被記録材において、インク透過層上に粉体が付与
されていることを特徴とする被記録材である。(Disclosure of the Invention) That is, the present invention is a recording material having an ink retaining layer and an ink permeable layer, characterized in that powder is applied on the ink permeable layer.

本発明の詳細な説明すると、本発明の被記録材は、その
インク保持層の上に、特定の性状のインク透過層を設け
、更にその上に粉体が付与されていることを主たる特徴
としており、主としてそれにより本発明の目的が達成さ
れた。To explain the present invention in detail, the main feature of the recording material of the present invention is that an ink permeable layer with specific properties is provided on the ink retaining layer, and powder is further applied thereon. The object of the present invention was mainly achieved thereby.

本発明の被記録材は、一般に支持体としての基材、その
表面に設けたインク保持層、該インク保持層上に設けた
インク透過層およびインク透過層上に付ケされた粉体か
らなるものであり、例えば特に好ましい主たる態様とし
て、 （１）基材、インク保持層、インク透過層および粉体層
のいずれも透光性であり、被記録材全体として透光性で
ある態様、 （２）基材、インク保持層、インク透過層および粉体層
の少なくとも１層が不透明であり、被記録材全体として
不透明である態様等があげられる。The recording material of the present invention generally comprises a base material as a support, an ink retaining layer provided on the surface thereof, an ink permeable layer provided on the ink retaining layer, and a powder deposited on the ink permeable layer. For example, particularly preferred main embodiments include (1) an embodiment in which the base material, the ink retaining layer, the ink permeable layer, and the powder layer are all translucent, and the recording material as a whole is translucent; 2) At least one of the base material, ink retaining layer, ink permeable layer, and powder layer is opaque, and the recording material as a whole is opaque.

尚、上記いずれの場合においても、インク保持層に支持
体としての機能を併せ持たせてもよい。In any of the above cases, the ink retaining layer may also have the function of a support.

以１−の如き２種の好ましい態様を代表例として、発明
を更に詳しく説明すると、本発明で支持体として用いる
ことのできる基材としては、透明性、不透明性等従来公
知の基材はいずれも使用でき、透明性基材として好適な
例としては、例えばポリエステル系樹脂、ジアセテート
系樹脂、トリアセテート系樹脂、アクリル系樹脂、ポリ
カーボネート系樹脂、ポリ塩化ビニル系樹脂、ポリイミ
Ｆ　ａ　ｍ　脂、セロハン、セルロイド等のフィルムも
しくは板およびガラス板等があげられる。また不透明性
基材として好ましいものとしては、例えば一般の紙、布
、木材、金属板、合成紙等の外、上記の透明性基材を公
知の手段により不透明性化処理したものがあげられる。The invention will be explained in more detail using the two preferred embodiments as shown in 1- below as representative examples.As the base material that can be used as a support in the present invention, any of the conventionally known base materials such as transparent and opaque base materials can be used. Examples of suitable transparent substrates include polyester resins, diacetate resins, triacetate resins, acrylic resins, polycarbonate resins, polyvinyl chloride resins, polyimide resins, and cellophane. , films or plates such as celluloid, and glass plates. Preferred examples of the opaque substrate include, for example, general paper, cloth, wood, metal plates, synthetic paper, and the like, as well as the above-mentioned transparent substrates treated to make them opaque by known means.

このような基材はその厚さが約１０〜２００　Ｂｍの範
囲のものであるのが好ましい。Preferably, such substrates have a thickness in the range of about 10-200 Bm.

本発明において、１−記基材」二に設けるインク保持層
は、主として水性のインキを受容できる親水性の材料か
ら形成されるものであって、このような材料として好ま
しいものは、アルブミン、ゼラチン、カゼイン、でんぷ
ん、カチオンでんぷん、アラビアゴム、アルギン酸ソー
ダ等の天然樹脂、ポリアミド、ポリアクリルアミド、ポ
リビニルピロリドン、四級化ポリビニルピロリドン、ポ
リエチレンイミン、ポリビニルピリシリウムハライド、
メラミン樹脂、ポリウレタン、カルボキシメチルセルロ
ース、ポリビニルアルコール、カチオン変性ポリビニル
アルコール、ポリエステル、ポリアクリル酸ソーダ等の
合成樹脂があげられ、これらの材料の１種以上・が所望
により使用される。In the present invention, the ink retaining layer provided on the base material 2 is mainly made of a hydrophilic material that can accept water-based ink, and preferable examples of such materials include albumin and gelatin. , casein, starch, cationic starch, gum arabic, natural resins such as sodium alginate, polyamide, polyacrylamide, polyvinylpyrrolidone, quaternized polyvinylpyrrolidone, polyethyleneimine, polyvinylpyricillium halide,
Synthetic resins such as melamine resin, polyurethane, carboxymethyl cellulose, polyvinyl alcohol, cation-modified polyvinyl alcohol, polyester, and sodium polyacrylate can be mentioned, and one or more of these materials can be used as desired.

更に、インク保持層の強度補強および／または基有との
密着性を改善するために、必要に応じて、ＳＢＲラテッ
クス、ＮＢＲラッテクス、ポリビニルホルマール、ポリ
メチルメタクリレート、ポリビニルブチラール、ポリア
クリロニトリル、ポリｍ化ビニル、ポリ酢酸ビニル、フ
ェノール樹脂、アルッキド樹脂等の樹脂を併用してもよ
い。Furthermore, in order to reinforce the strength of the ink retaining layer and/or improve the adhesion with the base, SBR latex, NBR latex, polyvinyl formal, polymethyl methacrylate, polyvinyl butyral, polyacrylonitrile, polymated Resins such as vinyl, polyvinyl acetate, phenol resin, and alkyd resin may be used in combination.

このようなインク保持層を形成する方法としては、１−
記の如きポリマーの単独あるいは混合物を、適当な溶剤
に溶解または分散させて塗工液を調製し、該塗工液を、
例えばロールコーティング法、ロットバーコーチインク
法、エアナイフコーティング法、スプレーコーティング
法等の公知の方法により前記基材トに塗工し、その後速
やかに乾燥させる方法が好ましく、また、に記の如き材
料から、熱展伸法、Ｔダイ法等の公知の方法により、単
独のインク保持層を形成して、インク保持層に、支持体
としての機能を併せ持つようにして用いるか、あるいは
、該シートを」二記基材にラミネートするＭ法、１−記
ボリマー材料をホットメルトコーティングする方法等に
より、基材１−にインク保持層を形成してもよい。As a method for forming such an ink retaining layer, 1-
A coating solution is prepared by dissolving or dispersing the following polymers alone or in a mixture in an appropriate solvent, and the coating solution is
For example, it is preferable to apply the coating to the base material by a known method such as a roll coating method, a lot bar coat ink method, an air knife coating method, or a spray coating method, and then dry it immediately. A single ink-retaining layer is formed by a known method such as , heat stretching method, T-die method, etc., and the ink-retaining layer is used to have the function of a support, or the sheet is used. The ink retaining layer may be formed on the base material 1- by the M method of laminating on the base material described in 2, the method of hot melt coating the polymer material described in 1-, or the like.

このようにして形成されるインク保持層の厚さは、イン
クを保持できる範囲であればよく、記録するインクの量
にもよるが、０　、１　ｇｍ以上あれば、特に限定され
るものではない。実用的には、０．５〜３０＃１．ｍの
範囲が好適である。The thickness of the ink retaining layer formed in this way may be within a range capable of retaining ink, and although it depends on the amount of ink to be recorded, it is not particularly limited as long as it is 0.1 gm or more. . Practically speaking, 0.5 to 30#1. A range of m is preferred.

本発明で使用し、本発明を第１に特徴づけるインク透過
層とは、上記の如くして形成されたインク保持層上に設
けられた天然または合成樹脂製の薄層であって、その表
面にインクの小滴が付着′したときに、該小滴が、互い
に隣接する他の小滴と過大に重複しない程度に接触面積
を速やかに（例えば数秒間内）拡大させ、■一つインク
保持層への浸透、およびインク保持層によるインクの受
容を併進させる機能を有するものである。The ink permeable layer used in the present invention and which primarily characterizes the present invention is a thin layer made of natural or synthetic resin provided on the ink retaining layer formed as described above. When a droplet of ink adheres to a surface, the contact area of the droplet is quickly expanded (for example, within a few seconds) to the extent that the droplet does not overlap excessively with other droplets adjacent to each other, and ■ One ink droplet is retained. It has the function of simultaneously promoting ink penetration into the layer and reception of the ink by the ink retaining layer.

本発明者は、上述の如き機能をインク保持層に賦ケすべ
く鋭意研究したところ、全く予想外にも、前記インク保
持層上へ、インク保持層を構成するポリマーと同程度ま
たは親水性の程度の劣るポリマーからなる薄層を形成す
ることにより、上記の機能が容易に達成されることを知
見したものである。このような機能が、例えば水に対し
て全く、あるいは殆ど溶解しないポリマーの薄膜によっ
ても達成されたことは、誠に驚くべきことであった。The inventor of the present invention conducted intensive research to impart the above-mentioned functions to the ink-retaining layer, and unexpectedly discovered that a polymer having the same degree of hydrophilicity as that of the polymer constituting the ink-retaining layer or It has been discovered that by forming a thin layer of inferior polymer, the above function is easily achieved. It was truly surprising that such a function could be achieved even with thin films of polymers that, for example, have no or little solubility in water.

上記の如き機能を有するインク透過層は、インク保持層
を形成しているポリマー材料に対して同等または相対的
に親水性の劣るポリマーにより、約１０ｇｍ以下、好ま
しくは約０．１〜５ＩＬｍの範囲の厚さの薄層な形成す
ることにより達成された。このような薄層の形成に有用
なポリマー材＄１としては、酢酸ビニル、アクリル酸エ
ステル、エチレン、塩化ビニル、その他のビニル千ツマ
−からなるホモポリマーあるいはコポリマー、および上
記の如きビニル千ツマ−と各種親木性ビニルモノマーと
からなるポリマー、更に、ビニロン、ポリウレタン、セ
ルロース誘導体、ポリエステル、ポリアミド等のポリマ
ー、および前述のインク保持層形成用親木性ポリマーの
単独、あるいは混合物からインク保持層に対比してイン
ク保持層よりも親水性の劣るものとして選択するのが好
適である。The ink permeable layer having the above-mentioned functions is made of a polymer having hydrophilicity equivalent to or relatively inferior to the polymer material forming the ink retaining layer, and has a hydrophilicity of about 10 gm or less, preferably in the range of about 0.1 to 5 ILm. This was achieved by forming a thin layer with a thickness of . Polymeric materials useful in forming such thin layers include homopolymers or copolymers of vinyl acetate, acrylic esters, ethylene, vinyl chloride, other vinyl polymers, and vinyl polymers such as those described above. and various wood-philic vinyl monomers, as well as polymers such as vinylon, polyurethane, cellulose derivatives, polyester, polyamide, and the above-mentioned wood-philic polymers for forming an ink-retaining layer, singly or in combination, to form an ink-retaining layer. In contrast, it is preferable to select a layer having lower hydrophilicity than the ink retaining layer.

また、選択するポリマーは、有機溶剤の溶液でもよいが
、水性媒体中のエマルジョン、有機溶剤あるいは水性媒
体中の微分散体としての形状で使用するのが好ましい。Further, the selected polymer may be a solution in an organic solvent, but it is preferably used in the form of an emulsion in an aqueous medium, an organic solvent, or a fine dispersion in an aqueous medium.

有機溶剤溶液として使用する場合は、比較的稀薄な溶液
あるいは形成される層が上記範囲内となる濃度で使用す
るのが好ましい。When used as an organic solvent solution, it is preferable to use a relatively dilute solution or a concentration such that the formed layer falls within the above range.

上記の如き材料を使用して、インク透過層を形成する方
法は、前記のインク保持層を形成するのと同様な方法が
採用できる。The method for forming the ink permeable layer using the above materials may be the same as that for forming the ink retaining layer.

以上の如き基本的構成を有する被記録材は、そのインク
透過層の親水性が、インク保持層の親木性と同等または
劣るにもかかわらず、この被記録材は、この様なインク
透過層の存在しない従来の被記録材に比して、インク受
容性およびインク定着性が顕著に向−ヒしているのは驚
くべきことである。現在、その理論的根拠は不明である
が、本発明者の単なる想像によれば（本発明は、このよ
うな単なる想像によって、何ら限定されるものではない
）、上記インク透過層は、必ずしも連続被膜ではなく、
水性インクが、インク保持層へ浸透できる極微な間隙が
インク透過層中に無数に存在しているとともに、その表
面がミクＯ＠位で不規則であり、その結果、付着したイ
ンク小滴が素早くその表面で拡散して、それらの接触面
積が拡大し、従ってインク保持層によるインク吸収性お
よび定着性が顕著に促進されているものと考えられる。Although the hydrophilicity of the ink-permeable layer of the recording material having the above-mentioned basic structure is equal to or inferior to the wood-philicity of the ink-retaining layer, this recording material has such an ink-permeable layer. It is surprising that the ink receptivity and ink fixing properties are significantly improved compared to conventional recording materials without the presence of . Although the theoretical basis for this is currently unknown, according to the inventor's mere imagination (the present invention is not limited by such mere imagination), the above-mentioned ink permeable layer is not necessarily continuous. Not a coating,
There are countless microscopic gaps in the ink-permeable layer that allow the water-based ink to penetrate into the ink-retaining layer, and the surface is irregular to the extent that the ink droplets adhere to the layer. It is thought that the ink absorbency and fixing properties of the ink retaining layer are significantly promoted by diffusing on the surface and expanding the contact area between them.

また、この被記録材はそのインク透過層が、インク保持
層に比較して同等または親水性の低いポリマーから形成
されているので、例えば高温高湿の雰囲気においても、
一旦受容されたインクが表面に浸出して、機器、オペレ
ーターあるいは周囲を汚染することがなく、また、高温
高湿下で表面がベタついたりすることもない。In addition, since the ink permeable layer of this recording material is made of a polymer with the same or lower hydrophilicity than the ink retaining layer, it can be used even in a high temperature and high humidity atmosphere, for example.
Once received, the ink will not leak to the surface and contaminate the equipment, operator, or surroundings, and the surface will not become sticky under high temperature and high humidity conditions.

更に、本発明で使用し、本発明を第２に特徴づける粉体
とは、インク保持層上のインク透過層上に付与される粉
体であり、被記録材をプリンターにかけた時、優れたイ
ンク定着性およびスムースな搬送性を発現させる機能を
有するものである。Further, the powder used in the present invention and which is the second characteristic of the present invention is a powder applied on the ink permeable layer on the ink retaining layer, and when the recording material is applied to a printer, it has excellent properties. It has the function of exhibiting ink fixability and smooth conveyance.

本発明者等は上述の如き機能を発現させるべく鋭意研究
の結果、ある種の粉体をインク透過層上に付与すること
により、上記機能が達成されることを知見したものであ
る。The inventors of the present invention have conducted intensive research to realize the above-mentioned functions, and have discovered that the above-mentioned functions can be achieved by applying a certain type of powder onto the ink-permeable layer.

一ヒ述の如き機能を有する粉体としては、粒径２０ｐＬ
ｍ以下の微粉末が好ましく、例えば、シリカ、クレー、
タルク、ケイソウ土、炭酸カルシウム、硫酸カルシウム
、硫酸バリウム、ケイ酸アルミニウム、合成ゼオライト
、アルミナ、酸化亜鉛、リトポン、サチンホワイト等の
無機粉体が挙げられ、有機粉体としては、高級脂肪酸あ
るいはその塩、例えば、ステアリン酸、アルミニウム、
ステアリン酸カルシウム等が挙げられる。このような粉
体は、インク透過層上に約ｏ　、　ｏ　Ｉｇ〜１　、０
ｇ　／ｒｒ？の割合で伺与することが好ましい。As a powder having the above-mentioned functions, the particle size is 20pL.
A fine powder of m or less is preferable, such as silica, clay,
Inorganic powders such as talc, diatomaceous earth, calcium carbonate, calcium sulfate, barium sulfate, aluminum silicate, synthetic zeolite, alumina, zinc oxide, lithopone, and sachin white are listed, and organic powders include higher fatty acids or their salts. , such as stearic acid, aluminum,
Examples include calcium stearate. Such powder is deposited on the ink permeable layer at approximately o, o Ig~1,0
g/rr? It is preferable to ask at a ratio of .

１−記の如き材料を付ゲするには、粉体粒子を直接千１
与してもよく、また適当な液体（例えば水）に分散ある
いは懸濁させて＋ｔ　、’Ｔ−してもよい。インク透過
層に上記材料を付与する方法としては、浸漬、へケ塗り
、スプレー、ローラー塗布、静電吸着等が挙げられる。1- To apply the materials listed below, powder particles are directly
It may also be dispersed or suspended in a suitable liquid (for example, water) to form +t, 'T-. Examples of methods for applying the above-mentioned materials to the ink-permeable layer include dipping, brushing, spraying, roller coating, and electrostatic adsorption.

以１−の如き基本的構成を有する本発明の被記録材は、
インク透過層の１に粉体を有しない被記録材に比し、イ
ンク受容性、インク定着性および記録装置中の搬送性が
顕著に向１−シているのは驚くべきことである。The recording material of the present invention having the basic configuration as shown in 1- below is:
It is surprising that the ink receptivity, ink fixability, and transportability in a recording device are significantly improved compared to a recording material that does not have powder in the ink permeable layer.

透過層ｌ−にイ；１！ｊされた粉体は、粉体量およびそ
の粉体自身が、毛細管的空隙を多数有しており、その毛
細管現象によりインクは粉体中を速い速度で拡散し、広
い面積となって透過層に達する。そこで透過層に付与さ
れた粉体との相乗作用により、インク受容性、インク定
着性、搬送性を著しく向−１ニさせているものと考えら
れる。To the transparent layer l-;1! The amount of powder and the powder itself have many capillary voids, and due to the capillary action, the ink diffuses through the powder at a high speed, forming a large area and passing through the permeable layer. reach. Therefore, it is thought that the synergistic effect with the powder applied to the permeable layer significantly improves ink receptivity, ink fixing performance, and transportability.

更に、粉体が最−１一層に付与されている為に、例えば
指紋がつかない、積み重ね詩のブロッキングが起こらな
い等、実用面で重要視きれる機能を併せて発現させるこ
とが出来るのである。Furthermore, since the powder is applied to the first layer, it is possible to achieve functions that are important from a practical standpoint, such as preventing fingerprints from forming and blocking of stacked poems.

以上が本発明の基本的構成であるが、本発明の被記録材
が透光性である態様では、基材として透光性の材ネ１を
使用し、インク保持層、インク透過層および粉体層の形
成に際しては、それらの層も透光性を損なわない様にす
る必要がある。しかしながら、その透光性を損なわない
程度に、例えばシリカ、クレー、タルク、ケイソウ上、
炭酸カルシウム、硫酸カルシウム、硫酸バリウム、ケイ
酸アルミニウム、合成ゼオライト、アルミナ、酸化亜鉛
、リトポン、サチンホワイト等の充填剤をインク保持層
および／またはインク透過層中に分散させることもでき
る。The above is the basic configuration of the present invention, but in an embodiment in which the recording material of the present invention is translucent, a translucent material 1 is used as the base material, and an ink retaining layer, an ink permeable layer and a powder are used. When forming the body layers, it is necessary to ensure that these layers do not impair their translucency. However, to the extent that the translucency is not impaired, for example, on silica, clay, talc, diatomaceous material, etc.
Fillers such as calcium carbonate, calcium sulfate, barium sulfate, aluminum silicate, synthetic zeolite, alumina, zinc oxide, lithopone, satin white, etc. can also be dispersed in the ink retaining layer and/or the ink permeable layer.

本発明で言う充分な透光性とは、被記録材の直線透光率
が、少なくとも２％以上呈することを言い、好ましくは
直線透光率が１０％以Ｉ−であることが望ましい。In the present invention, sufficient light transmittance means that the recording material exhibits a linear light transmittance of at least 2% or more, and preferably a linear light transmittance of 10% or more I-.

直線透光率が２％以上であれば、例えばＯＨＰにより記
録画像をスクリーンへ投影して観察することが可能であ
り、更に記録画像の細部が鮮明に観察されるためには、
直線透光率が１０％以−にであることが望ましい。If the linear light transmittance is 2% or more, it is possible to project and observe the recorded image onto a screen using OHP, for example, and in order to clearly observe the details of the recorded image,
It is desirable that the linear light transmittance is 10% or more.

ここで言う直線透光率Ｔ（％）とは、サンプルに垂直に
入射し、サンプルを透過し、サンプルから少なくとも８
ｃｍ以上はなれた入射光路の延長線トにある受光側スリ
ットを通過し、検出器に受光される直線光の分光透過率
を、例えば３２３型日立自記分光光度計（日立製作所製
）等を使用して測定し、更に測定された分光透過率より
、色の三刺激値のＹ値を求め、次式より求められる値で
ある。The linear transmittance T (%) here refers to the amount of light incident perpendicularly to the sample, transmitted through the sample, and at least 8
The spectral transmittance of the straight light that passes through the light-receiving side slit located on the extension line of the incident optical path separated by more than cm and is received by the detector is measured using, for example, the 323-type Hitachi self-recording spectrophotometer (manufactured by Hitachi, Ltd.). Then, from the measured spectral transmittance, the Y value of the tristimulus value of the color is determined, and the value is determined by the following formula.

Ｔ＝Ｙ／Ｙ、　　Ｘ１００　　　　　（１）Ｔ　；直線
透光率 Ｙ　；サンプルのＹ値 Ｙｏ　；ブランクのＹ値 従って、本発明で言う直線透光率は、直線光に対するも
のであり、拡散透光率（サンプルの後方に積分球を設け
て拡散光をも含めて透光率を求める。）や、不透明度（
サンプルの裏に、白および黒の裏当てを当ててそれらの
比から求める。）等の拡散光により透光性を評価する方
法とは異なる。T=Y/Y, rate (install an integrating sphere behind the sample to determine the transmittance including diffused light), opacity (
The white and black backings are placed on the back of the sample and the ratio is calculated. ), which evaluates translucency using diffused light.

光学技術を利用した機器などで問題となるのは直線光の
挙動であるから、それらの機器で使用しようとする被記
録材の透光性を評価する上で、被記録材の直線透光率を
求めることは、特に重要である。The problem with devices that use optical technology is the behavior of straight-line light, so when evaluating the light transmittance of the recording material to be used in those devices, it is important to check the straight-line transmittance of the recording material. It is particularly important to seek

例えば、ＯＨＰで投影画像を観察する場合、記録部と」
１三記録部とのコントラストが高く、鮮明で見やすい画
像を得るためには、投影画像における非記録部が明るい
こと、すなわち被非記録材の直線透光率がある一定以上
の水準にあることが要求される。ＯＨＰでのテストチャ
ートによる試験では、１−品目的に適した画像を得るた
めには、被記録材の直線透過率が２％以−１−１より鮮
明な画像を得るためには、好ましくは、１０％以−１−
であることが必要とされ、更に好適には、５０％以ト以
上ることが望ましい。従って、この目的に適した被記録
材は、その直線透過率が２％以１−であることが必要で
ある。For example, when observing a projected image on an OHP, the recording section and
13. In order to obtain a clear and easy-to-see image with high contrast with the recorded area, the non-recorded area in the projected image must be bright, that is, the linear light transmittance of the non-recorded material must be at a certain level or higher. required. In a test using an OHP test chart, 1-In order to obtain an image suitable for the purpose of the product, the in-line transmittance of the recording material is preferably 2% or more.1-1 In order to obtain a clearer image, it is preferable. , 10% or more -1-
More preferably, it is 50% or more. Therefore, a recording material suitable for this purpose must have a linear transmittance of 2% or more and 1-.

また、本発明の被記録材が不透明である態様では、基材
、インク保持層、インク透過層および粉体層のうち少な
くとも一層を不透明性材料を使用すればよい。Further, in an embodiment in which the recording material of the present invention is opaque, an opaque material may be used for at least one layer among the base material, ink retaining layer, ink permeable layer, and powder layer.

この様な態様において使用する各層の形成方法は、１−
記の透明性の態様におけると同様である。The method for forming each layer used in this embodiment is 1-
This is the same as in the transparency aspect described above.

この不透明の１ハ１様においては、インク保持層および
インク透過層の形成に際し、成膜性を損なわない程度に
、多量の前記充填剤を使用し、更に優れたインク受容Ｐ
１および定着性を向１−させることができる。In this opaque type 1/1, when forming the ink retaining layer and the ink permeable layer, a large amount of the filler is used to the extent that film formability is not impaired, and even more excellent ink receptivity is achieved.
1 and fixing properties can be improved.

以１−．、本発明の被記録材の代表的な態様を例示して
本発明を説明したが、勿論本発明の被記録、材はこれら
の態様に限定されるものではない。なお、いずれのＩＥ
様の場合においても、インク保持層には、分散剤、蛍光
染料、ｐＨ調節剤、消泡剤、ｎ」滑剤、防腐剤、界面活
性剤等の公知の各種添加剤を包含させることができる。Below 1-. Although the present invention has been described by exemplifying typical aspects of the recording material of the present invention, the recording material and recording material of the present invention are of course not limited to these aspects. In addition, which IE
In any case, the ink retaining layer may contain various known additives such as a dispersant, a fluorescent dye, a pH adjuster, an antifoaming agent, an n' lubricant, a preservative, and a surfactant.

なお、本発明の被記録材は必ずしも無色である必要はな
く、着色された被記録材であってもよい。Note that the recording material of the present invention does not necessarily have to be colorless, and may be a colored recording material.

以１−の如き本発明の被記録材は、前述の説明の通り、
また後述の実施例において実証する通り、インクの受容
および定着が顕著瞥こ改善されており、例えば、モノカ
ラーの場合は勿論、フルカラーの記録に際して、異色の
記録液が短時間内に同一箇所に重複して付着した場合に
も記録液の渣れ出しやしみ出し現象がなく、高解像度の
鮮明で優れた発色性のある画像が得られる。また、スラ
イドやＯＨＰ等の光学機器により記録画像をスクリーン
等への投影により観察に用いる場合にも、４４着したイ
ンク小滴が、従来の被記録材の場合と比較し、隣接する
他の領域と過度に重なり合わない程度に拡大されて定着
しているので、透過光がより一層均−になり、すぐれた
均一濃度の投影画像を与えるものである。更に、カラー
印刷のポジ版を作成する際の色分解版、あるいは液晶等
のカラーディスプレイに用いるＣＭＦ等、従来の表面画
像観察用以外の用途に好適に適用することができる。As explained above, the recording material of the present invention as described in 1- below has the following features:
In addition, as will be demonstrated in the examples below, the reception and fixation of ink has been significantly improved. Even when the recording liquid is adhered in duplicate, there is no scum or seepage phenomenon of the recording liquid, and a high-resolution, clear image with excellent color development can be obtained. Furthermore, when using an optical device such as a slide or an OHP for observation by projecting a recorded image onto a screen, the ink droplets that land on the recording material are more likely to fall on other adjacent areas than in the case of conventional recording materials. Since the image is enlarged and fixed to such an extent that it does not overlap excessively, the transmitted light becomes even more uniform, and a projected image with excellent uniform density is provided. Furthermore, it can be suitably applied to uses other than conventional surface image observation, such as a color separation plate when creating a positive plate for color printing, or a CMF used in a color display such as a liquid crystal.

以下、参考例および実施例に従って本発明の方法を更に
詳細に説明する。なお、文中、部とあるのは型部基準で
ある。Hereinafter, the method of the present invention will be explained in more detail according to Reference Examples and Examples. In addition, in the text, the word ``part'' refers to the type part standard.

参考例１ 透光性基材として厚さ１００　ｇｔｎのポリエチレンテ
レフタレートフィルム（東し製）を使用し、このフィル
ム１−に下記の組成の塗工液Ａを、乾燥後の膜厚がｌｏ
ｐ、ｍとなるようにパーコーター法により塗下し、６０
℃で２０分間の条件で乾燥し、インク保持層を形成した
。次いで、下記塗工液Ｂをインク保持層Ｉ−に、乾燥膜
厚が３ルｍとなるように塗布し、６０℃で１５分間乾燥
させて、インク透過層を形成し、参考用の透光性被記録
材を得た。Reference Example 1 A polyethylene terephthalate film (manufactured by Toshi) with a thickness of 100 gtn was used as a translucent base material, and coating liquid A having the following composition was applied to this film 1- so that the film thickness after drying was lo
Apply by percoater method so that it becomes p, m, 60
It was dried at ℃ for 20 minutes to form an ink retaining layer. Next, coating liquid B below was applied to the ink holding layer I- so that the dry film thickness was 3 m, and dried at 60°C for 15 minutes to form an ink permeable layer. A recording material was obtained.

塗に液Ａ組成： ポリビニルピロリドン に−９０（ＧＡＦ製）　　　　　　　　１５部水　　　
　　　　　　　　　　　　　　　　　　　　　　　８５
部塗工液Ｂ組成； 力Ｊレボキシメチルセルロース（七ロ ゲンＢＳ、第−工業製薬製）　　　　　　２部水　　　
　　　　　　　　　　　　　　　　　　　　　　９８部
このようにして得られた本発明の被記録材は、無色透明
なものであった。Coating liquid A composition: polyvinylpyrrolidone -90 (manufactured by GAF) 15 parts water
85
Part Coating liquid B composition; Chikara J levoxymethyl cellulose (Shichirogen BS, manufactured by Dai-Kogyo Seiyaku) 2 parts water
98 parts The thus obtained recording material of the present invention was colorless and transparent.

参考例２ 基材としてアート紙を用いたことを除き、参考例１と同
様な方法により参考用の被記録材を得た。この被記録材
は白色の不透明なものであった。Reference Example 2 A reference recording material was obtained in the same manner as in Reference Example 1, except that art paper was used as the base material. This recording material was white and opaque.

参考例３ 厚さ１ＯＯｐＬ■のポリエチレンテレフタレートフィル
ム（音大製）を使用し、このフィルム上に下記の組成の
塗工液Ａを、乾燥後の膜厚が１ｏ。Reference Example 3 A polyethylene terephthalate film (manufactured by Music University) with a thickness of 1OOpL was used, and coating liquid A having the following composition was applied onto the film to give a film thickness of 1Op after drying.

ｊＬ　ｍとなるようにバーコーター法により塗工し、８
０℃で１１１Ｇ間の条件で乾燥し、インク保持層を形成
ｌ〜だ。次いで、下記塗工液Ｂをインク保持層ｌ−に、
乾燥膜厚が５ｐ、ｍとなるように塗布し、８０°Ｃで２
０分間乾燥させて、インク透過層を形成し、更に、ポリ
エチレンテレフチレートフィルムからインク保持層とイ
ンク透過層を併せて剥離して、参考用の透光性被記録材
を得た。Coat by bar coater method so that jL m, 8
Dry at 0° C. and 111 G to form an ink retaining layer. Next, apply the following coating liquid B to the ink retaining layer l-,
Coat to a dry film thickness of 5p, m and heat at 80°C for 2
The film was dried for 0 minutes to form an ink permeable layer, and the ink retaining layer and ink permeable layer were both peeled off from the polyethylene terephthylate film to obtain a reference transparent recording material.

塗−「液Ａ組成； ポリビニルアルコール （ＰＶＡ　　４２０　　り’ｙし製）　　　　１０部水
　　　　　　　　　　　　　　　　　　　　　　　　　
　９０部塗工液Ｂ組成； アクリル酸エステル （ダイカラツク５１２３５）　　　　　５部エタノール
　　　・　　　　　　　　９５部参考例４ 基材としてアート紙を使用し、この基材上に下記の組成
の塗工液Ａを、乾燥後の膜厚が２５ｐ、ｍとなるように
八−コーター法により塗工し、５０°Ｃで２０分間の条
件で乾燥し、インク保持層を形成した。次いで、Ｆ記塗
工液Ｂをインク保持層１−に、乾燥膜厚が２μｍとなる
ように塗布し、７０℃で１０分間乾燥させてインク透過
層を形成し、参考用の不透光性被記録材を得た。Coating - "Liquid A composition; Polyvinyl alcohol (PVA 420 manufactured by Ri'yshi) 10 parts water
90 parts Coating liquid B composition: Acrylic acid ester (Daikaratsuk 51235) 5 parts ethanol ・95 parts Reference example 4 Art paper was used as a base material, and coating liquid A with the following composition was applied onto this base material after drying. The ink-retaining layer was formed by coating by an 8-coater method to a film thickness of 25p, m, and drying at 50°C for 20 minutes. Next, coating liquid B described in F was applied to the ink retaining layer 1- so that the dry film thickness was 2 μm, and dried at 70°C for 10 minutes to form an ink permeable layer. A recording material was obtained.

塗工液Ａ　ＩＩ成； 水溶性アクリル樹脂（コーガム ＨＷ−７、昭和高分子）　　　　　　２０部微粉シリカ
（サイロイド ＃２４４　富士デビソン）　　　　　５部水　　　　　
　　　　　　　　　　　　　　　　　　　　　７５部塗
工液Ｂ、ｌ成； ポリ酢酸ビニル（モビニール３０３、 ヘキスト製）　　　　　　　　　　　１０部水　　　　
　　　　　　　　　　　　　　　　　　　　　９０部実
施例１ 参考例１にて作成されたインク透過層に対し、クレー（
粒度分布０．１〜５ｇｍ、土産カオリン製）またはセピ
オライト（粒度分布０．５〜５川ｍ、武田薬品製）を刷
毛にて、夫々０　、５　ｇ／ｒｎ’および１　、０　ｇ
／ｒｒｆの割合で塗布し、余分の粉体を布又は刷毛にふ
き取り、本発明の透光性被記録材を得た。Coating liquid A II composition: Water-soluble acrylic resin (Corgam HW-7, Showa Kobunshi) 20 parts Finely divided silica (Syroid #244 Fuji Davison) 5 parts Water
75 parts Coating solution B, l composition; polyvinyl acetate (Movinyl 303, manufactured by Hoechst) 10 parts water
90 parts Example 1 Clay (
Particle size distribution 0.1 to 5 gm, made by souvenir kaolin) or sepiolite (particle size distribution 0.5 to 5 gm, made by Takeda Pharmaceutical Co., Ltd.) with a brush at 0, 5 g/rn' and 1, 0 g, respectively.
/rrf, and excess powder was wiped off with a cloth or brush to obtain a translucent recording material of the present invention.

実施例２ 参考例２にて作成されたインク透過層に対し、炭酸カル
シウム（粒度分布０．０５〜３ルｍ、　　１１束粉化製
）または含水二酸化ケイ素（粒子径約１５ｐＬｍ、富士
デビソン製）を刷毛にて、夫々０゜５ｇ／ｒｒ＋′およ
び０　、２　ｇ／ｍ’（１）割合で塗布し、余分の粉体
を布又は刷毛にふき取り、本発明の被記録材を得た。Example 2 Calcium carbonate (particle size distribution: 0.05 to 3 m, manufactured by 11 Bundle Powder) or hydrous silicon dioxide (particle size: approximately 15 pLm, manufactured by Fuji Davison) was added to the ink permeable layer created in Reference Example 2. were applied with a brush at a ratio of 0.5 g/rr+' and 0.2 g/m' (1), respectively, and the excess powder was wiped off with cloth or a brush to obtain a recording material of the present invention.

実施例３ 参考例３にて作成されたインク透過層に対し、無水二酸
化ケイ素（粒子径３０ｍμｍ、日本アエロジル酸）また
はケイソウ士（粒度分布０．０５〜５ＪＬｍ、日東粉化
製）を刷毛にて、夫々０．１ｇｅｍ’およびｏ　、　４
　ｇ／ｒｒｆの割合で塗布し、余分の粉体を布又は刷毛
にふき取り、本発明の被記録材を得た。Example 3 Anhydrous silicon dioxide (particle size 30 mμm, Nippon Aerosilic Acid) or Keisoushi (particle size distribution 0.05 to 5 JLm, manufactured by Nitto Funka) was applied with a brush to the ink permeable layer created in Reference Example 3. , 0.1 gem' and o, 4, respectively
g/rrf, and excess powder was wiped off with a cloth or brush to obtain a recording material of the present invention.

実施例４ 参考例４にて作成されたインク透過層に対し、クレー（
粒度分布０．１〜５ｇｍ、上屋カオリン製）または炭酸
カルシウム（粒度分布０．０５〜３ＩＬｍ、Ｈ粉粒化製
）を刷毛にて、夫々０．８ｇ／ｒｎ′および０．５ｇ／
ｍ’の割合で塗布し、余分の粉体な布又は刷毛にふき取
り、本発明の被記録材を得た。Example 4 Clay (
Particle size distribution: 0.1-5 gm, made by Ueya Kaolin) or calcium carbonate (particle size distribution: 0.05-3 ILm, made by H Kofunka Co., Ltd.) were applied with a brush to 0.8 g/rn' and 0.5 g/rn', respectively.
m' and wiped off the excess powder with a cloth or brush to obtain a recording material of the present invention.

上記の参考例および実施例で得られた被記録材に対して
、下記の４種のインクを用いて、ピエゾ振動子によって
インクを吐出させるオンデマンド型インクジェット記録
ヘッド（吐出オリフィス径６５ｐ、ｍ、ピエゾ振動子駆
動電圧７０Ｖ、周波数３ＫＩＩｚ）を有する記録装置を
使用してインクジェット記録を実施した。An on-demand inkjet recording head (discharge orifice diameter 65p, m, Inkjet recording was performed using a recording device having a piezo vibrator drive voltage of 70 V and a frequency of 3 KIIz.

イエローインク（組成） Ｃ，１，ダイレクトイエロー８６　　　２部Ｎ−メチル
−２−ピロリドン　　１０部ジエチレングリコール　　
　　　２０部ポリエチレングリコール＃２００　１５部
水　　　　　　　　　　　　　　　　　　　　　　　５
５部マゼンタインク（組成） Ｃ，１，アシッドレッド３５　　　　　２部Ｎ−メチル
−２−ピロリドン　　１０部ジエチレングリコール　　
　　　２０部ポリエチレングリコール＃２００　１５部
水　　　　　　　　　　　　　　　　　　　　　　　　
５５部シアンインク（組成） Ｃ，１，ダイレクトブルー８６　　　２部Ｎ−メチル−
２−ピロリドン　　１０部ジエチレングリコール　　　
　　２０部ポリエチレングリコール＃２００　　１５部
水　　　　　　　　　　　　　　　　　　　　　　　５
５部ブラックインク（組成） Ｃ，１，フードブラック２　　　　　　２部Ｎ−メチル
−２−ピロリドン　　ｔｏ部ジエチレングリコール　　
　　　２０部ポリエチレングリコール＃２００　１５部
水　　　　　　　　　　　　　　　　　　　　　　　５
５部被記録材の評価結果は第１表に示した。第１表にお
ける各評価項目の測定は下記の方法に従った。Yellow ink (composition) C, 1, Direct Yellow 86 2 parts N-methyl-2-pyrrolidone 10 parts diethylene glycol
20 parts polyethylene glycol #200 15 parts water 5
5 parts Magenta ink (composition) C, 1, Acid Red 35 2 parts N-methyl-2-pyrrolidone 10 parts diethylene glycol
20 parts polyethylene glycol #200 15 parts water
55 parts Cyan ink (composition) C, 1, Direct Blue 86 2 parts N-methyl-
2-pyrrolidone 10 parts diethylene glycol
20 parts polyethylene glycol #200 15 parts water 5
5 parts black ink (composition) C, 1, food black 2 2 parts N-methyl-2-pyrrolidone to part diethylene glycol
20 parts polyethylene glycol #200 15 parts water 5
The evaluation results for the 5-part recording material are shown in Table 1. Each evaluation item in Table 1 was measured according to the following method.

（１）インク定着時間は、記録実施後被記録材を室温下
に放置し、記録画像に指触したときに、インクが乾燥し
て指に付着しなくなる時間を測定した。(1) Ink fixation time was measured by leaving the recording material at room temperature after recording and measuring the time taken for the ink to dry and stop adhering to the finger when touching the recorded image with the finger.

（２）ドツト濃度は、ＪＩＳ　Ｋ　７５０５を印字マイ
クロドツトに応用してサクラマイクロデンシドメーター
ＰＤＭ−５（小西六写真工業製）を用いて黒ドツトにつ
き測定した。(2) The dot density was measured for black dots using Sakura Microdensidometer PDM-5 (manufactured by Konishiroku Photo Industries) by applying JIS K 7505 to printed microdots.

（３）ＯＨＰ適性は、光学機器の代表例として測定した
もので、記録画像を０１（Ｐによりスクリーンに投影し
、■視により観察して判定したもので、非記録部が明る
く、記録画像のＯＤ（オプチカルデンシティ）が高く、
コントラストの高い鮮明で見やすい投影画像の得られる
ものをＯ１非記録部がやや暗く、記録画像のＯＤがやや
低く、ピッチ巾０．５ｍｍ、太さ０．２５ｍｍの線が明
瞭に判別できないものを△、非記録部がかなり暗く、記
録画像のＯＤがかなり低く、ピッチ巾１ｍｍ、太さ０．
３ｍｍの線が明瞭に判別できないものあるいは非記録部
と記録画像の見分けがつかないものを×とした。(3) OHP suitability was measured as a representative example of optical equipment, and was determined by projecting the recorded image onto a screen using 01 (P) and observing it visually. High OD (optical density)
△: A clear and easy-to-see projected image with high contrast is obtained.The non-recorded area is slightly dark, the OD of the recorded image is slightly low, and the lines with a pitch width of 0.5 mm and a thickness of 0.25 mm cannot be clearly distinguished. , the non-recorded area is quite dark, the OD of the recorded image is quite low, the pitch width is 1 mm, and the thickness is 0.
A case where the 3 mm line could not be clearly distinguished or a case where the non-recorded area and the recorded image could not be distinguished was rated as "x".

（４）直線透光率は、３２３型日立自記分光光度計（日
立製作所製）を使用し、サンプルから受光側のマドまで
の距離を約９ｃｍに保ち、分光透過率を測定し、前記（
１）式により求めた。(4) Straight line transmittance was measured using a 323-type Hitachi self-recording spectrophotometer (manufactured by Hitachi, Ltd.), keeping the distance from the sample to the light-receiving side at approximately 9 cm, and measuring the spectral transmittance as described above (
1) It was calculated using the formula.

（ｊ、（”ｊ’余白） 一首（−１−！ 一実施例− １名　　　　　旦　　　　　４ イレ２外定ＪＬＩ−間 ２０℃　８５＄ＲＨ１分　　　１分　　　３０秒　　　
４５秒２０°Ｃ８５ＸＲＨ４５秒　　　　４５秒　　　
　２０秒　　　　３０秒直−線−透一光一率　　　　　
７６％　　　　　　　　　　７７％　　　　−下−２−
上一濃一度　　　　　０．９　　　　１．２　　　　１
．０　　　　１．Ｏｑ□旦−！−適適性性　　　　０　
　　　　　　　　　　０−２０°Ｃ８５騨１　　　１．
５分　　１．５分　　４５秒　　１．５分２０℃８５ｚ
Ｒ１（１分　　１分　　３０秒　　４５秒直−線−透一
犬一率　　　　　７６％　　　　　　　　　　７８％　
　　　−下一ヱー上−濃一度　　　　　０．９　　　　
１．２　　　　　　Ｃｏ　　　　　１．ＯＱ賢二ｌ□≦
１−ｊ酷−」生　　　　　　　○　　　　　　　　　　
　　　　　　Ｏ−特許出願人　　　キャノン株式会社 ’ｉ？’１告−・、１ 手続補正書（１′１釦 昭和６０年　９月１８日(j, ("j' margin) One poem (-1-! One example - 1 person Dan 4 Ire 2 External JLI-20℃ 85$RH1 minute 1 minute 30 seconds
45 seconds 20°C85XRH45 seconds 45 seconds
20 seconds 30 seconds Straight line - Transmission one light rate
76% 77% -Bottom-2-
Kamiichino 1 0.9 1.2 1
．． 0 1. Oq□dan-! -Suitability 0
0-20°C85 1 1.
5 minutes 1.5 minutes 45 seconds 1.5 minutes 20℃85z
R1 (1 minute 1 minute 30 seconds 45 seconds straight line - Toruichi dog rate 76% 78%
- Lower 1 - Upper - Dark 0.9
1.2 Co 1. OQ Kenjil□≦
1-j Kuru-” raw ○
O-Patent applicant Canon Co., Ltd.'i? '1 Notice - 1 Procedural Amendment (1'1 button September 18, 1985)

Claims (1)

【特許請求の範囲】[Claims] インク保持層とインク透過層とを有する被記録材におい
て、インク透過層上に粉体が付与されていることを特徴
とする被記録材。A recording material having an ink retaining layer and an ink permeable layer, characterized in that powder is applied on the ink permeable layer.