FR2535710A1 - CONSTRUCTION MATERIAL BASED ON FIBER-REINFORCED HYDRAULIC BINDER AND PROCESS FOR PRODUCING THE SAME - Google Patents
CONSTRUCTION MATERIAL BASED ON FIBER-REINFORCED HYDRAULIC BINDER AND PROCESS FOR PRODUCING THE SAME Download PDFInfo
- Publication number
- FR2535710A1 FR2535710A1 FR8219187A FR8219187A FR2535710A1 FR 2535710 A1 FR2535710 A1 FR 2535710A1 FR 8219187 A FR8219187 A FR 8219187A FR 8219187 A FR8219187 A FR 8219187A FR 2535710 A1 FR2535710 A1 FR 2535710A1
- Authority
- FR
- France
- Prior art keywords
- fibers
- material according
- cement
- hydraulic binder
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
L'INVENTION CONCERNE UN MATERIAU DE CONSTRUCTION DU TYPE CONSTITUE PRINCIPALEMENT PAR UN LIANT HYDRAULIQUE RENFORCE PAR DES FIBRES. DE PREFERENCE, LES FIBRES INCLUSES DANS LE MATERIAU SANS AMIANTE ONT UN DIAMETRE COMPRIS ENTRE 3 ET 8 MICRONS ET UNE RESISTANCE A LA RUPTURE SUPERIEURE A 800NMM2. LA FABRICATION DU MATERIAU S'EFFECTUE SUR DES MACHINES POUR AMIANTE-CIMENT DANS DE BONNES CONDITIONS DE FILTRATION ET LE MATERIAU OBTENU PRESENTE UN RENFORCEMENT MECANIQUE SUFFISANT. APPLICATION A LA FABRICATION DE PRODUITS POUR BATIMENT.THE INVENTION RELATES TO A CONSTRUCTION MATERIAL OF THE TYPE CONSTITUTED MAINLY BY A HYDRAULIC BINDER REINFORCED BY FIBERS. PREFERREDLY, THE FIBERS INCLUDED IN THE ASBESTOS-FREE MATERIAL HAVE A DIAMETER BETWEEN 3 AND 8 MICRONS AND A RUPTURE STRENGTH OF MORE THAN 800NMM2. THE MANUFACTURING OF THE MATERIAL IS CARRIED OUT ON ASBESTOS-CEMENT MACHINES UNDER GOOD FILTRATION CONDITIONS AND THE MATERIAL OBTAINED SHOWS SUFFICIENT MECHANICAL REINFORCEMENT. APPLICATION TO THE MANUFACTURING OF BUILDING PRODUCTS.
Description
25357 1 O25357 1 O
La présente invention est relative à un matériau de construction constitué principalement par un liant hydraulique renforcé par des The present invention relates to a construction material consisting mainly of a hydraulic binder reinforced with
fibres, ainsi qu'au procédé de fabrication dudit matériau. fibers, as well as the method of manufacturing said material.
Il est connu de remplacer, dans les produits de construction à base de ciment ou de liant hydraulique et d'amiante, des fibres It is known to replace, in cementitious or hydraulic binder and asbestos-based construction products, fibers
d'amiante par des fibres d'autre nature, organique et/ou minérale - asbestos fibers of other nature, organic and / or mineral -
Comme la fabrication de produits en amiante-ciment s'effectue généralement à partir d'un mélange de fibres d'amiante et de ciment mis en suspension dans l'eau, puis filtré pour obtenir une couche qui est ensuite transformée en plaques ou tuyaux, il est nécessaire d'utiliser des fibres de substitution qui permettent la filtration, d'une part, et qui assurent le renforcement du produit fini, d'autre As asbestos-cement products are generally manufactured from a mixture of asbestos fibers and cement suspended in water, then filtered to obtain a layer which is then transformed into plates or pipes. it is necessary to use substitute fibers which allow the filtration, on the one hand, and which ensure the reinforcement of the finished product, on the other hand
part Par filtration on entend la rétention, sur une paroi filtrante,. By filtration is meant the retention on a filter wall.
des fibres qui forment alors un réseau et empêchent ainsi le passage des particules de ciment au travers de ladite paroi De même, les fibres de renforcement ont pour but de remédier à la fragilité inhérente à un produit qui serait constitué de ciment pur Si les fibres d'amiante satisfont simultanément à ces deux conditions, il n'en va pas de même avec les fibres de substitution actuellement utilisées et il faut alors faire appel à deux types de fibres différents, dont l'un facilite la filtration et l'autre apporte la fibers which then form a network and thus prevent the passage of cement particles through said wall Similarly, the reinforcing fibers are intended to remedy the fragility inherent in a product which would be made of pure cement. Asbestos satisfies both conditions at the same time, but the same is not true of the currently used substitute fibers, and two different types of fiber must be used, one of which facilitates filtration and the other provides the
résistance mécanique au produit final grâce au renforcement. mechanical resistance to the final product thanks to reinforcement.
C'est ainsi que les fibres de cellulose, ne procurant que peu de résistance mécanique au produit élaboré, améliorent la filtrabilité des suspensions contenant d'autres fibres de renforcement Mais ces Thus, the cellulose fibers, providing little mechanical strength to the product developed, improve the filterability of the suspensions containing other reinforcing fibers.
fibres sont sensibles à l'humidité-qui en provoque un gonflement - fibers are sensitive to moisture - which causes swelling -
générateur de microfissures et sont sujettes à des dégradations du fait des microorganismes, de sorte qu'il est préférable d'éviter la pose d'un produit contenant des fibres de cellulose dans des-ambiances microcracking generator and are subject to degradation due to microorganisms, so it is preferable to avoid laying a product containing cellulose fibers in ambiances
humides ou à l'extérieur des bâtiments. wet or outside buildings.
La présente invention remédie à ces inconvénients Elle a pour objet un matériau de construction du type constitué principalement par un liant hydraulique renforcé par des fibres et ne contenant pas d'amiante, caractérisé en ce que les fibres ont un diamètre compris entre 3 et 8 microns et une résistance à la traction supérieure à The present invention overcomes these disadvantages. It relates to a construction material of the type consisting mainly of a hydraulic binder reinforced with fibers and containing no asbestos, characterized in that the fibers have a diameter of between 3 and 8 microns. and a higher tensile strength than
800 N/mm 2.800 N / mm 2.
25357 1 O25357 1 O
De manière surprenante, il a été constaté que dès lors que les fibres de substitution de l'amiante respectent cette double condition, elles peuvent satisfaire aux deux exigences de commodité de filtration Surprisingly, it has been found that since the asbestos substitution fibers meet this dual condition, they can satisfy both filtration convenience requirements.
et de renforcement mécanique suffisant. and sufficient mechanical reinforcement.
Comme indiqué précédemment, les fibres utilisées peuvent avoir un diamètre moyen compris entre 3 et 8 microns Il est possible-qu'un diamètre des fibres inférieur à 3 microns puisse convenir, mais la technologie actuelle ne permet pas de les obtenir Si le diamètre dépasse 8 microns, le réseau des fibres retenues a une maille trop grande, qui laisse alors passer une fraction trop importante des particules de ciment au cours de la filtration La nature des fibres est indifférente, dés lors qu'elles résistent à l'action alcaline du liant hydraulique et qu'elles présentent une résistance à la traction supérieure à 800 N/mm 2 Cette valeur a été déterminée après examen des caractéristiques mécaniques du produit fini, qui selon l'utilisation envisagée, tuyau ou plaque de couverture, doivent être suffisantes, au moins dans le sens longitudinal, correspondant au sens de défilement du feutre sur lequel est recueilli le gâteau de filtration Les fibres organiques synthétiques conviennent bien, notamment le polyéthylène, le polypropylène, le polyacrylonitrile, le polyacrylamide, l'alcool de polyvinyle Les fibres minérales peuvent être également employées avec As indicated above, the fibers used may have an average diameter of between 3 and 8 microns It is possible-that a fiber diameter of less than 3 microns may be suitable, but the current technology does not allow to obtain them If the diameter exceeds 8 micron, the network of fibers retained has a mesh too large, which then leaves a too large fraction of the cement particles during the filtration The nature of the fibers is indifferent, as long as they resist the alkaline action of the binder hydraulic and have a tensile strength greater than 800 N / mm 2 This value has been determined after examination of the mechanical characteristics of the finished product which, depending on the intended use, pipe or cover plate, shall be sufficient, less in the longitudinal direction, corresponding to the direction of travel of the felt on which the filter cake is collected Synthetic organic fibers are suitable, especially polyethylene, polypropylene, polyacrylonitrile, polyacrylamide, polyvinyl alcohol. Mineral fibers can also be used with
profit, sous réserve qu'elles présentent une composition alcali- benefit, provided that they have an alkaline
résistante adéquate.adequate resistance.
Les fibres fines sont employées soit sous la forme vendue par le fournisseur, soit après traitement de surface qui améliore leur ancrage dans la matrice cimentaire Ces fibres sont généralement de section circulaire, mais une forme de lobe, simple ou multiple ou de ruban peut convenir également Dans un tel cas, on remplacera le diamètre des fibres par le diamètre équivalent The fine fibers are used either in the form sold by the supplier or after surface treatment which improves their anchorage in the cement matrix. These fibers are generally of circular section, but a single or multiple lobe shape or ribbon may also be suitable. In such a case, the diameter of the fibers will be replaced by the equivalent diameter
équiv = 2 -equiv = 2 -
o S est la section.o S is the section.
La longueur des fibres est d'au moins lmm, de manière à ce que la liaison entre la fibre et la matrice cimentaire reste assurée, même si des microfissures venaient à apparaître dans le produit fini Elle est inférieure à l Omm, longueur au-delà de laquelle des difficultés de The length of the fibers is at least 1 mm, so that the bond between the fiber and the cementitious matrix remains assured, even if microcracks appear in the finished product. It is less than 1 mm, length beyond which difficulties in
mise en oeuvre apparaissent.implementation appear.
2 5 3 5 7 1 02 5 3 5 7 1 0
Le matériau suivant l'invention comprend également un liant hydraulique, tel que le ciment, avec ou sans ajout, qui peut être un The material according to the invention also comprises a hydraulic binder, such as cement, with or without an addition, which may be a
ciment alumineux, un ciment de laitier, ou un ciment de haut fourneau. aluminous cement, slag cement, or blast furnace cement.
De même, le plâtre, le gypse ou la chaux peuvent convenir. Similarly, plaster, gypsum or lime may be suitable.
Suivant la manière connue, le matériau contient -encore des charges inertes ou actives qui confèrent au produit final les caractéristiques désirées,-comme la tenue à la chaleur ou l'inhibition According to the known manner, the material contains - still inert or active fillers which confer on the final product the desired characteristics, as resistance to heat or inhibition
de la chaux libérée lors de la prise-du ciment. lime released during the setting-cement.
Il est également avantageux de prévoir des floculants de type connu, tels que ceux à base de polymères solubles, qui ont pour fonction d'accroître la rétention des particules solides, et des agents dispersants dont l'action évite la formation d'amas ou de It is also advantageous to provide flocculants of known type, such as those based on soluble polymers, whose function is to increase the retention of solid particles, and dispersing agents whose action avoids the formation of clusters or
flocons de fibres dans la suspension soumise à la-filtration. fiber flakes in the suspension subjected to filtration.
Le.procédé de fabrication du matériau selon l'invention s'effectue de la manière suivante Les fibres sont d'abord mises en suspension dans l'eau, en une quantité qui est déterminée par les conditions _de bon fonctionnement de la machine Cette quantité se situe entre 1 et 5 % en volume de fibres par rapport au produit fini; toutefois, pour tenir compte des différentes natures de fibres utilisables, on introduit un paramètre qui fait intervenir la densité de fibres, à savoir la "proportion spécifique" Pf/e o Pf est le pourcentage en poids de fibres par rapport au poids total des matières sèches et, la masse volumique des fibres exprimée en g/cm 3 Cette proportion spécifique est The process for producing the material according to the invention is carried out in the following manner. The fibers are first suspended in water, in an amount which is determined by the conditions of good operation of the machine. is between 1 and 5% by volume of fibers relative to the finished product; However, in order to take into account the different types of fibers that can be used, a parameter is introduced which makes use of the fiber density, namely the "specific proportion". Pf / eo Pf is the percentage by weight of fibers relative to the total weight of the dry materials. and the density of the fibers expressed in g / cm 3 This specific proportion is
avantageusement comprise entre l et 5 - advantageously between 1 and 5 -
Le ciment est ensuite ajouté, à raison de 60 à 98 parties en poids par rapport au total des matières sèches Lorsque les produits sont fabriqués sur des machines du type "machine à carton", les charges actives ou inertes n'excèdent pas en principe 30 % en poids de ciment, ce -qui représente O à 30 parties en poids du total des matières sèche-s La proportion de charge peut être plus importante lorsque la technique de fabrication-diffère: coulée, moulage, The cement is then added, in a proportion of 60 to 98 parts by weight relative to the total dry matter. When the products are manufactured on machines of the "cardboard machine" type, the active or inert charges do not in principle exceed 30 % by weight of cement, which represents 0 to 30 parts by weight of the total dry matter content. The proportion of filler may be greater when the manufacturing technique differs: casting, molding,
centrifugation, extrusion par exemple. centrifugation, extrusion for example.
Après homogénéisation par brassage de la suspension aqueuse, cette dernière est introduite dans des machines dont les deux principaux types sont ceux mettant en oeuvre le procédé avec tamis, comme la machine HATSCHEK, et ceux relevant du procédé sans tamis, After homogenization by stirring of the aqueous suspension, the latter is introduced into machines of which the two main types are those using the sieve process, such as the HATSCHEK machine, and those under the sieveless method,
tels que la machine MAGNANI.such as MAGNANI machine.
Dans le procédé avec tamis, une cuve reçoit la suspension aqueuse, qui est filtrée à travers une toile métallique disposée sur un cylindre tournant Il se dépose alors sur le tamis une fine couche de fibres et de ciment qui, après transfert sur le feutre, forme une couche élémentaire La superposition de plusieurs couches In the sieve process, a tank receives the aqueous suspension, which is filtered through a wire mesh disposed on a rotating cylinder. A thin layer of fibers and cement is then deposited on the sieve which, after transfer onto the felt, forms an elementary layer The superposition of several layers
élémentaires, dans le cas de plusieurs cuves à tamis, donne une mono- in the case of several sieves, gives a mono-
couche qui est enroulée sur un cylindre jusqu'à obtention de l'épaisseur désirée du produit Lorsque celle-ci est atteinte, un dispositif de découpe suivant une génératrice permet de dérouler la pâte sous forme d'une feuille plane qui est ensuite mûrie sous forme plane, ondulée ou profilée Une autre utilisation courante de ce layer that is wound on a cylinder until the desired thickness of the product When it is reached, a cutting device along a generator allows unrolling the dough in the form of a flat sheet which is then matured in form flat, corrugated or contoured Another common use of this
mélange-est la fabrication de tuyaux. mixing-is the manufacture of pipes.
Dans les deux cas, les produits obtenus sont mûris soit à l'air libre, soit dans l'eau, soit en étuve pendant plusieurs heures dans In both cases, the products obtained are ripened either in the open air or in the water or in an oven for several hours in
une ambiance saturée en humidité.an atmosphere saturated with humidity.
Plusieurs mélanges sont préparés dans les conditions suivant l'invention, en vue de-la confection d'éprouvettes planes qui sont soumises à des essais de rupture, tels que ceux prévus par la norme ASTM D-38 80-80 Le tableau final annexé regroupe les résultats obtenus avec plusieurs types de fibres, en fonction de différents paramètres de machines, ainsi qu'à titre de référence, les résultats Several mixtures are prepared under the conditions according to the invention, for the preparation of flat specimens which are subjected to rupture tests, such as those provided by the ASTM D-38 80-80 standard. The attached final table groups together the results obtained with several types of fibers, according to different machine parameters, and for reference, the results
obtenus sur une éprouvette contenant de l'amiante. obtained on a specimen containing asbestos.
EXEMPLE 1EXAMPLE 1
Suivant un premier exemple-de fabrication, on met en oeuvre un mélange contenant du ciment et des fibres de viscose commercialisées par RHONE POULENC TEXTILES sous la marque déposée "FIBRANNE", dont le diamètre est 6,5 microns, la longueur 5 mm et la résistance à la rupture, 800 N/mm 2 Le mélange est constitué de 5 % en poids de fibres et on y a rajouté un floculant de type connu (E 318) à raison de 3 g/litre La feuille plane obtenue à partir de la monocouche résultant de la filtration est comprimée sous une pression de 100 bars, puis on la laisse mûrir à température ambiante On procède alors aux essais de-casse, après 14 jours, à l'état saturé et on relève la résistance à la flexion, aussi bien dans le sens de défilement L du tapis de la machine que dans le sens perpendiculaire T à ce défilement. According to a first example of manufacture, a mixture containing cement and viscose fibers marketed by RHONE POULENC TEXTILES under the brand name "FIBRANNE", whose diameter is 6.5 microns, the length 5 mm and the tensile strength, 800 N / mm 2 The mixture consists of 5% by weight of fibers and there is added a flocculant of known type (E 318) at a rate of 3 g / liter The flat sheet obtained from the The monolayer resulting from the filtration is compressed under a pressure of 100 bars, then it is allowed to mature at room temperature. Then, the test is carried out after 14 days in the saturated state and the flexural strength is measured. well in the direction of scrolling L of the carpet of the machine than in the perpendicular direction T to this scroll.
25357 1025357 10
ss
EXEMPLE 2EXAMPLE 2
Le même type de fibres que dans l'exemple 1 est employé dans les mêmes conditions, mais les essais sont réalisés après 21 jours, à The same type of fibers as in Example 1 is used under the same conditions, but the tests are carried out after 21 days, at
l'état sec La densité est alors 1,65. the dry state The density is then 1.65.
EXEMPLE 3EXAMPLE 3
Les fibres utilisées sont en viscose haute ténacité, de diamètre 6 microns, longueur 5 mm et résistance à la rupture 930 N/mm 2 Le mélange soumis à la filtration contient 2 % de fibres et 98 % en poids de ciment, et le mûrissement s'effectue à la température ambiante, en ambiance confinée La densité de la plaque soumise en l'état aux The fibers used are high tenacity viscose, 6 microns in diameter, 5 mm in length and breaking strength 930 N / mm 2 The mixture subjected to the filtration contains 2% fibers and 98% by weight of cement, and the curing at room temperature, in a confined environment The density of the plate subjected as it is to
essais de rupture après 14 jours est de 1,75. Break testing after 14 days is 1.75.
EXEMPLE 4EXAMPLE 4
Des fibres en alcool polyvinylique (PVA), de diamètre 7 microns, longueur 6 mm et résistance à la rupture 1100 N/mm 2, sont mélangées à du ciment à raison de 4 parties en poids pour 96 parties de ciment La plaque n'est pas comprimée après fabrication Elle subit un mûrissement en ambiance saturée et les essais de casse sont effectués Polyvinyl alcohol (PVA) fibers with a diameter of 7 microns, length 6 mm and breaking strength 1100 N / mm 2 are mixed with cement at a rate of 4 parts by weight for 96 parts of cement. not compressed after manufacture It undergoes a ripening in saturated atmosphere and the tests of breakage are carried out
en l'état, après 14 jours La densité de la plaque est de 1,55. in the state, after 14 days The density of the plate is 1.55.
EXEMPLE 5EXAMPLE 5
Les fibres de même nature qu'à l'exemple 4 sont ajoutées au ciment à raison de 4 parties pour 96 parties de ciment en poids La plaque est comprimée sous 200 bars après fabrication mais les autres conditions de mûrissement et d'essais restent identiques à celles de The fibers of the same kind as in Example 4 are added to the cement at a rate of 4 parts per 96 parts of cement by weight. The plate is compressed to 200 bars after manufacture but the other conditions of maturing and testing remain identical to those of
l'exemple 4.example 4.
EXEMPLE 6EXAMPLE 6
Une quantité de 1,5 % en poids de fibres d'alcool polyvinylique, de diamètre 12 microns, longueur 6 mm et résistance à la rupture 1100 N/mm 2 est ajoutée à 98,5 % de ciment et le mélange est filtré Au cours de cette opération, on constate qu'il est-impossible d'obtenir une couche élémentaire de composition convenable sur le tamis, car 80 à 90 % des particules de ciment sont rejetées avec l'eau de filtration A quantity of 1.5% by weight of polyvinyl alcohol fibers, of diameter 12 microns, length 6 mm and breaking strength 1100 N / mm 2 is added to 98.5% of cement and the mixture is filtered. from this operation, it is found that it is impossible to obtain a basic layer of suitable composition on the sieve, since 80 to 90% of the cement particles are rejected with the filtration water
et le feutre ne recueille presque que des fibres. and the felt collects almost nothing but fibers.
EXEMPLE 7EXAMPLE 7
L'élément de référence est constitué par de l'amiante, du type chrysotile sous forme de mélange, de grade 4-5-6; 80 % des fibres ont un diamètre compris entre 1 et 10 microns Comme précédemment, une plaque est préparée, sans compression après fabrication mais avec mûrissement à la température ambiante en ambiance confinée Cette The reference element consists of asbestos, of the chrysotile type in the form of a mixture, of grade 4-5-6; 80% of the fibers have a diameter of between 1 and 10 microns As previously, a plate is prepared, without compression after manufacture but with maturing at ambient temperature in a confined environment.
plaque subit ensuite les essais de rupture. plate then undergoes breaking tests.
-On constate à la lecture du tableau qu'après durcissement, le matériau se distingue de l'amiante-ciment par une capacité de -It is noted from the table that after hardening, the material is distinguished from asbestos cement by a capacity of
déformation plus importante, qui procure une sécurité d'usage accrue. greater deformation, which provides increased safety of use.
On peut en effet admettre un ou plusieurs dépassements fortuits de la limite élastique sans qu'il ne se produise nécessairement des fissures One can indeed admit one or more fortuitous exceedances of the elastic limit without that it does not necessarily occur cracks
ou une rupture dangereuse.or a dangerous break.
On remarque également que la densité du filtrat ou densité de l'échappement, au cours de la fabrication, est représentative de la bonne filtration du mélange en suspension, procurée par les fibres It is also noted that the density of the filtrate or density of the exhaust, during manufacture, is representative of the good filtration of the mixture in suspension, provided by the fibers
suivant l'invention.according to the invention.
L'utilisation de ces fibres apporte une simplification notable de la préparation des mélanges et des suspensions, car elles ne nécessitent pas de traitement préalable de raffinage ou autres The use of these fibers provides a significant simplification of the preparation of mixtures and suspensions, because they do not require prior treatment of refining or other
traitements qui sont grands consommateurs d'énergie. treatments that are high energy consumers.
En variante, le matériau de construction suivant l'invention peut être élaboré à partir d'un mélange de fibres différentes et de liant hydraulique, les seules conditions à respecter étant celles relatives aux caractéristiques dimensionnelles des fibres (diamètre, longueur), Alternatively, the building material according to the invention can be produced from a mixture of different fibers and hydraulic binder, the only conditions to be respected being those relating to the dimensional characteristics of the fibers (diameter, length),
à la résistance mécanique et à la résistance aux alcalis. mechanical resistance and alkali resistance.
EXEM 4 PLES I 2 t 3 4 I 16 1 7 Nature de fibre Viscose Viscose Hte tenaPVA PVA PVA A C. Diamètre des fibres (Q)6,5 6,5 6,5 6 7 I 7 I 12 I I à 10 Longueur (mm) 5 5 5 6 6 6 Résistance à laI 800 800 930 1100 1100 |I 800 rupture (N/mm 2) ' I, I I Composition de mélangeI 5 5 I 2 I 4 I 4 j 1, 5 | 11 (% poids fibres/ total) I' j I I I Densité cuve tamis 1,020 1,020 1,0481,036| 1,070 | 1,070 j 1,0501,060 Densité échappement| 1,0031,004|1, 0031,004j 1,0061,012t 1,0031,026|1,0031,026I 1,0031,004 EXEM 4 PLES I 2 t 3 4 I 16 1 7 Nature of fiber Viscose Viscose Hte tenaPVA PVA PVA A C. Diameter of fibers (Q) 6.5 6.5 6.5 6 7 I 7 I 12 II to 10 Length ( mm) 5 5 5 6 6 6 Resistance to I 800 800 930 1100 1100 | I 800 rupture (N / mm 2) 'I, II Mixing composition I 5 5 I 2 I 4 I 4 j 1, 5 | 11 (% fiber weight / total) Density vat sieve 1,020 1,020 1,0481,036 | 1,070 | 1,070 d 1,0501,060 Exhaust density | 1,0031,004 | 1, 0031,004d 1,0061,012t 1,0031,026 | 1,0031,026I 1,0031,004
Compression après fabjoui ( 100 bars)Q Oui ( 100 bars)I Non Non Oui ( 200 bars) Non - Compression after fabjoui (100 bars) Q Yes (100 bars) I No No Yes (200 bars) No -
M Hrissement j Ta eau I Ta eau| Ta ambianceITa ambiancejTa ambiance | Ta ambiance Ij confinée saturée saturée confinée Densité produit finij 1,63 I 1,65 I 1,75 I 1,55 j 1,80 1,58 M owing to water I Your water | Your ambienceIts atmosphere | Your environment Ij confined saturated saturated confined Density product finij 1,63 I 1,65 I 1,75 I 1,55 j 1,80 1,58
Conditions de'casse1 14 j 21 j 14 14 '14 j14 j 14 4 j. Conditions of absence1 14 d 21 d 14 14 '14 d 14 d 14 4 d.
j saturé sec | en l'état|en l'état en l'état ' j saturé Résistance L j 17, 7 I 22,8 j 18,2 j 27,3 j 35,5 i j 29 flexion (M Pa)Tj 14,1 j 16,5 12,0 j 18,5 25,2 j _ 22 Déformation HnLj 1,8 j 1,9 2,61 j 32,6 | 17,9 | j_{ 2,92 Dformaion(xl O-" 17 T 9 121,39 12 flexion(xl O) T j 1,3 1,3 1,48 j 13,8 3, 7 2,28 Module en flexionLj 12 500 | 14 600 j 12 700 I 14 400 j 21 900 j j 13 850 (M Pa) T j 10 800 j 12 100 il 500 11 59 30 12 800 l N ul Ln a > j saturated dry | in the state | in the state in the saturated state Resistance L d 17, 7 I 22.8 d 18.2 d 27.3 d 35.5 ij 29 flexion (M Pa) Tj 14.1 d 16.5 12.0 d 18.5 25.2 d _ 22 Deformation HnLj 1.8 d 1,9 2,61 d 32,6 | 17.9 | 2.92 Dmaxion (xl O- "17 T 9 121.39 12 flexion (xl O) Tj 1.3 1.3 1.48 j 13.8 3, 7 2.28 Flexural modulusLj 12 500 | 14,600 d 12,700 I 14,400 d 21,900 dd 13,850 (M Pa) T d 10,800 d 12 100 il 500 11 59 30 12,800 l N ul Ln a>
Claims (9)