ES2479665T3 - Procedimiento para la preparación de composiciones de polímeros de propileno, con resistencia al impacto - Google Patents
Procedimiento para la preparación de composiciones de polímeros de propileno, con resistencia al impacto Download PDFInfo
- Publication number
- ES2479665T3 ES2479665T3 ES10782232.2T ES10782232T ES2479665T3 ES 2479665 T3 ES2479665 T3 ES 2479665T3 ES 10782232 T ES10782232 T ES 10782232T ES 2479665 T3 ES2479665 T3 ES 2479665T3
- Authority
- ES
- Spain
- Prior art keywords
- optionally
- propylene polymer
- ethylene
- minutes
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Un procedimiento para la preparación de composiciones de polímeros de propileno, el cual se lleve a cabo en presencia de un sistema catalizador, el cual comprende el producto obtenido procediendo a poner en contacto (a) un componente catalizador sólido, el cual tiene un tamaño medio de partícula, correspondiente a un valor comprendido dentro de uno márgenes que van desde los 15 μm hasta los 80 μm, el cual comprende un haluro de magnesio, un compuesto de titanio que tiene por lo menos un eslabón de Ti-halógeno, y por lo menos dos compuestos donantes de electrones, encontrándose presente, uno de ellos, en una cantidad correspondiente a un porcentaje comprendido dentro de unos márgenes que van desde un 50 % molar hasta un 90 % molar, con respecto a la cantidad total de los donantes, y que se selecciona de entre succinatos, y seleccionándose, el otro de entre ellos, de entre 1,3-diéteres, (b) un compuesto de hidrocarbilo de aluminio, en el cual, el hidrocarbilo, se selecciona de entre radicales aromáticos o alifáticos, ramificados, C3-C10 y, de una forma opcional (c) un compuesto donante de electrones, externo, y que comprende las siguientes etapas: (i) poner en contacto los componentes catalizadores (a), (b) y, de una forma opcional, (c), durante un transcurso de tiempo comprendido dentro de unos márgenes que van desde los 0,1 minutos hasta los 120 minutos, a una temperatura comprendida dentro de unos márgenes que van desde los 0 °C hasta los 90 °C; (ii) polimerizar propileno, de una forma opcional, en presencia de etileno y / o de alfaolefinas C4-C10, produciendo un (co)polímero de propileno, el cual sea insoluble en xileno, en un porcentaje de por lo menos un 85%, en peso, a una temperatura de 25 °C, determinado en la sección experimental, y (iii) en una etapa sucesiva, realizada en una fase de gas, en presencia del producto procedente de (ii), polimerizando mezclas de etileno con α-olefinas CH2-CHR, en las cuales, R es un radical hidrocarburo, el cual tiene 1 - 10 átomos de carbono, para producir un copolímero de etileno.
Description
etileno, en presencia de un homopolímero de propileno, el cual procede de la primera etapa. Como regulador del peso molecular, se utiliza el hidrógeno.
La fase de gas (propileno, etileno e hidrógeno), se analiza, de una forma continua, vía cromatografía de gases.
5 Al final de la serie de procesado, se procede a descargar la materia en polvo, y ésta se seca, bajo un flujo de nitrógeno.
Las condiciones principales de la polimerización, y los datos de análisis, referentes a los polímeros producidos en los 10 tres reactores, se encuentran recopilados en la Tabla 1.
Ejemplo comparativo 1
El proceso de polimerización, se llevó a cabo mediante la utilización del mismo catalizador, y bajo las condiciones 15 que se encuentran descritas en el ejemplo 1, con las diferencias consistentes en el hecho de que se utilizó el trietilaluminio (TEAL), en lugar del TIBAL (triisobutilaluminio).
Tabla 1
- CONDICIONES DEL PROCESO
- Ejemplo 1
- Ejemplo comparativo 1
- Precontacto
- Tiempo de resiendencia (minutos)
- 19 20
- Factor de relación Tibal / donante
- 8 10 (Teal)
- T (° C)
- 15 15
- 1er reactor en fase líquida – Homopolímero de propileno
- Temperatura, °C
- 70 70
- Presión, bar
- 40 40
- Tiempo de residencia, minutos
- 58 65
- H2 introducido, mol, ppm
- 4100 4000
- Separación, % en peso
- 83 81
- Reactor de fase de gas Polimerización C2 -/ C3 -
- Temperatura, °C
- 80 80
- Presión, bar
- 15 15
- Tiempo de residencia, minutos
- 13 25
- C2 -/ C2 -+ C3 -, %
- 0,33 0,29
11
Continuación Tabla 1
- CONDICIONES DEL PROCESO
- Ejemplo 1
- Ejemplo comparativo 1
- Reactor de fase de gas Polimerización C2 -/ C3 -
- H2 -/ C2 -, %
- 0,07 0,08
- Separación, % en peso
- 17 19
- % C2 en copolímero
- 44 41
- Factor de relación de actividad (Kg / g)
- 1,01 0,59
- Densidad aparente g / cm3
- 0,45 0,46
- Propiedades del polímero
- MFR ( g / 10’)
- 40 46
- Solubles en xileno (%)
- 16,1 17,9
- XSIV (dl / g)
- 2,43 2,37
- Módulo de elasticidad (flexión) (MPa)
- 1518 1466
- Izod a 23 °C (KJ / m2)
- 4,8 4,8
- Izod a 0 °C (KJ / m2)
- 4,2 4,6
- Izod a -20 °C (KJ / m2)
- 3,0 3,8
- Resistencia a la tracción al límite de elasticidad (MPa)
- 27,3 26,3
- Notas: concentr. de H2 = concentración de hidrógeno, en el monómero líquido; C2 -= etileno; /C3 -= propileno; Separación = cantidad de polímero preparada en el reactor concernido, referido al peso total;
12
Claims (1)
-
imagen1 imagen2