DE3716751A1 - METHOD FOR PRODUCING A DIAMOND-BASED GRINDING TOOL - Google Patents
METHOD FOR PRODUCING A DIAMOND-BASED GRINDING TOOLInfo
- Publication number
- DE3716751A1 DE3716751A1 DE19873716751 DE3716751A DE3716751A1 DE 3716751 A1 DE3716751 A1 DE 3716751A1 DE 19873716751 DE19873716751 DE 19873716751 DE 3716751 A DE3716751 A DE 3716751A DE 3716751 A1 DE3716751 A1 DE 3716751A1
- Authority
- DE
- Germany
- Prior art keywords
- blank
- diamond
- diamond grains
- layer
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Die vorliegende Erfindung bezieht sich auf das Gebiet der Technologie des Maschinenbaues, genauer auf ein Verfahren zur Herstellung eines diamanthaltigen Schleifwerkzeuges.The present invention relates to the field the technology of mechanical engineering, more precisely on a Process for the production of a diamond-containing Grinding tool.
Die nach dem vorliegenden Verfahren hergestellten Werkzeuge, welche zur Bearbeitung von Diamant, Glas, Keramik und anderen harten Stoffen bestimmt sind, können in der Schmuckwarenindustrie, bei der Fertigung von optisch-mechanischen Geräten sowie in der Bauindustrie verwendet werden.The tools manufactured according to the present process, which for processing diamond, glass, ceramics and other hard substances can be determined in the Jewelry industry, in the manufacture of optical-mechanical Devices as well as used in the construction industry.
Bekannt ist ein Verfahren zur Herstellung von diamanthaltigen Facettierscheiben, bei dem man auf die Oberfläche einer Metallscheibe ein diamanthaltiges Ölgemisch aufträgt und das Einbetten durch Einreiben dieses Gemisches mit Hilfe eines Hartmetallelementes, beispielsweise einer Gußeisenläppscheibe, durchführt. Das Einbetten erfolgt bei statischer Belastung des Hartmetallelementes, wobei gleichzeitig dessen Drehung mit einer Frequenz von 2-40 s-1 gewährleistet wird (Epifanov V. I. u. a. "Bearbeitungstechnologie von Diamanten zur Erzeugung von Brillanten", M., Verlag "Vysshaya Shkola", 1982, S. 233).A method for producing diamond-containing faceting disks is known, in which a diamond-containing oil mixture is applied to the surface of a metal disk and embedding is carried out by rubbing in this mixture with the aid of a hard metal element, for example a cast iron lapping disk. The embedding takes place under static loading of the hard metal element, while at the same time ensuring its rotation with a frequency of 2-40 s -1 (Epifanov VI, inter alia "Processing technology of diamonds for the production of brilliants", M., publisher "Vysshaya Shkola", 1982, P. 233).
Das bekannte Verfahren besitzt jedoch eine niedrige Produktivität, weil die Einbettung 20-30 min in Anspruch nimmt. Darüber hinaus gestattet dieses Verfahren nicht, eine hohe Diamantkörnerkonzentration im Scheibenmetall zu erzielen und sicherzustellen, daß die Diamantkörner beim Betrieb [nicht] aus der Scheibe ausbrechen. Dies bedingt niedrige Betriebseigenschaften von Facettierscheiben sowie einen erhöhten Verbrauch an teurem Diamantrohstoff.However, the known method has a low one Productivity because the embedding in 20-30 min Takes up. This procedure also allows not, a high diamond grain concentration in the disc metal to achieve and ensure that the diamond grains break out of the pane during operation [not]. This requires low operating properties of faceting discs as well an increased consumption of expensive diamond raw material.
Dieses Verfahren ist zur Herstellung von dünnwandigen Schleifscheiben, deren Dicke mit der Diamantkorngröße vergleichbar ist, wegen einer Verformung der Scheiben ungeeignet.This process is used to manufacture thin-walled Grinding wheels, the thickness of which is comparable to the diamond grain size is unsuitable because of a deformation of the discs.
Bekannt ist ferner ein Verfahren zur Herstellung eines diamanthaltigen Schleifwerkzeuges, das das Auftragen einer Diamantkörner enthaltenden Schleifpulverschicht auf einen Rohling mit nachfolgender Einwirkung eines Hartmetallstempels auf die gesamte Oberfläche desselben einschließt. Die Stempeleinwirkung besitzt statischen Charakter und erfolgt bei einem Druck von über 400-500 MPa.A method for producing a is also known diamond-containing grinding tool that the application a layer of abrasive powder containing diamond grains a blank with the subsequent action of a hard metal stamp on the entire surface of the same. The effect of the stamp has a static character and takes place at a pressure of over 400-500 MPa.
Allerdings gestattet das bekannte Verfahren nicht, einen höheren Grad der Adhäsion von Diamantkörnern am Rohlingsmetall zu erzielen, da diese nicht vollständig in das Metall eindringen.However, the known method does not allow a higher degree of adhesion of diamond grains to the blank metal to achieve as this is not completely in penetrate the metal.
Da die Eindringungsrichtung der Diamantkörner mit der Wirkungsrichtung der statischen Belastung übereinstimmt, kann man beim Einbringen der Diamantkörner in den Rohling nur eine Konzentration von höchstens 40 Vol.% erreichen. Die genannten Faktoren wirken sich auf die Betriebseienschaften des Werkzeugs nachteilig aus.Since the direction of penetration of the diamond grains with the Direction of action of the static load corresponds, can be done by inserting the diamond grains into the blank achieve a concentration of at most 40% by volume. The Factors mentioned affect the business properties of the tool.
Außerdem setzt dieses Verfahren den Einsatz von energieintensiven Preßausrüstungen voraus.In addition, this process requires the use of energy-intensive Press equipment ahead.
Der Erfindung liegt die Aufgabe zugrunde, ein Verfahren zur Herstellung eines diamanthaltigen Schleifwerkzeuges durch entsprechende Wahl von technologischen Parametern für das Einbringen der Diamantkörner in den Rohling zu entwickeln, das eine hohe Produktivität hat und hohe Betriebseigenschaften des Schleifwerkzeuges gewährleistet.The invention is based on the object Process for producing a diamond-containing grinding tool through appropriate choice of technological parameters for the introduction of the diamond grains to develop in the blank, which is high productivity and has high operating properties of the grinding tool guaranteed.
Diese Aufgabe wird gelöst durch ein Verfahren zur Herstellung eines diamanthaltigen Schleifwerkzeuges, das das Auftragen einer Diamantkörner enthaltenden Schleifpulverschicht auf einen Rohling und die Einwirkung auf den Rohling auf der Seite dieser Schicht mittels eines Hartmetallelements zum Einbringen des Schleifpulvers in denselben einschließt, in dem erfindungsgemäß das Einbringen des Schleifpulvers durch Einwirkung auf den Rohling mit einem Schlagimpuls von 200-800 kN/s und einem Hartmetallelement erfolgt, das mit einer Frequenz von 900- 2500 s-1 rotiert.This object is achieved by a method for producing a diamond-containing grinding tool, which includes the application of a layer of grinding powder containing diamond grains to a blank and the action on the blank on the side of this layer by means of a hard metal element for introducing the grinding powder into the same, in which, according to the invention, the introduction of the grinding powder by acting on the blank with an impact pulse of 200-800 kN / s and a hard metal element that rotates at a frequency of 900- 2500 s -1 .
Eine solche Einwirkung auf den Rohling gewährleistet die günstigsten Bedingungen für ein völliges Einbringen der Diamantkörner in den Rohling und deren sicheres Befestigen. Dadurch wird die Herstellung eines dünnwandigen Werkzeuges, beispielsweise eines Trennwerkzeugs mit einer Dicke bis 0,05 mm bei einer Diamantkörnerkonzentration bis zu 60-65 Vol.% ermöglicht. Außerdem nimmt die Lebensdauer des hergestellten Werkzeuges um 40-45%, die Schnittintensität beispielsweise beim Zerspanen von Diamant um 50- 55% und die Arbeitsleistung bei der Herstellung desselben um das 3- bis 4fache zu.Such an effect on the blank ensures most favorable conditions for a full contribution the diamond grains in the blank and securely fastening them. This will make a thin-walled one Tool, for example a cutting tool with up to 0.05 mm thick with a diamond grain concentration enables up to 60-65 vol.%. It also decreases the lifespan of the tool produced by 40-45%, the cutting intensity for example when cutting diamond by 50- 55% and the work done in manufacturing the same by 3 to 4 times.
Erfindungsgemäß erfolgt das Auftragen der Schleifpulverschicht auf einen scheibenförmigen Rohling bei gleichzeitigem Formen desselben zu einem Kugelsegment mit einem Halbmesser, der den Ausgangshalbmesser desselben um das 3- bis 10fache übersteigt.According to the invention, the abrasive powder layer is applied on a disc-shaped blank with simultaneous Form the same with a spherical segment a radius that is the same as the output radius exceeds 3 to 10 times.
Die Formgebung des Rohlings beim Aufbringen des Schleifpulvers gewährleistet eine optimale Verteilung der Diamantkörner im Rohlingsvolumen, was die Lebensdauer des Werkzeuges erhöht.The shape of the blank when applying the grinding powder ensures an optimal distribution of the diamond grains in the blank volume, which is the life of the tool elevated.
Zweckmäßig wird für das Auftragen auf den Rohling ein Schleifpulver verwendet, das die folgende Zusammensetzung besitzt (Vol.%):It is useful for application to the blank an abrasive powder used that has the following composition owns (vol.%):
Diamantkörner20-60 leichtschmelzendes MetallRest,Diamond grains 20-60 easily melting metal residue,
oder eine aus Diamantkörnern bestehende Schleifpulverschicht auf einen vorher mit leichtschmelzendem Metall plattierten Rohling aufgetragen.or a layer of abrasive powder consisting of diamond grains on a previously clad with slightly melting metal Blank applied.
Das im Gemisch vorhandene leichtschmelzende Metall bzw. die Vorplattierung des Rohlings mit einem leichtschmelzenden Metall gestattet es, den Gehalt von Diamantkörnern mit einer Größe 200-250 µm im Werkzeuggefüge bis auf die höchstmögliche Konzentration zu steigern.The easily melting metal or pre-plating the blank with a low melting point Metal allows the content of diamond grains with a size of 200-250 µm in the tool structure except for the to increase the highest possible concentration.
Das erfindungsgemäße Verfahren wird folgendermaßen durchgeführt.The method according to the invention is as follows carried out.
Man bringt auf den Rohling eine Diamantkörner enthaltende Schleifpulverschicht auf. Über dem Rohling wird in unmittelbarer Nähe der Schleifpulverschicht ein Hartmetallelement, z. B. eine Wolframkarbidplatte, angeordnet und mit einer Frequenz von 900-2500 s-1 in Drehung versetzt. Man läßt auf den Rohling von der entgegengesetzten Seite her einen Schlagimpuls von 200-800 kN/s einwirken, der über die gesamte Oberfläche des Rohlings wirkt und eine sehr schnelle Bewegung desselben in Richtung auf das Hartmetallelement zu und den Zusammenstoß mit diesem gewährleistet. An abrasive powder layer containing diamond grains is applied to the blank. A hard metal element, e.g. B. a tungsten carbide plate, arranged and rotated at a frequency of 900-2500 s -1 . A blank impulse of 200-800 kN / s is allowed to act on the blank from the opposite side, which acts over the entire surface of the blank and allows it to move very quickly in the direction of the hard metal element and to ensure collision with it.
Die Einwirkung eines Schlagimpulses der angegebenen Stärke auf den Rohling gewährleistet bei seiner Berührung mit dem rotierenden Hochgeschwindigkeits-Hartmetallelement das Eindringen der Diamantkörner in das Rohlingsmetall längs einer komplizierten Bahn bis auf eine Tiefe, die zum sicheren Festhalten derselben ausreicht.The action of a shock pulse of the specified Strength on the blank ensures at its Contact with the rotating high-speed carbide element the penetration of the diamond grains into the blank metal along a complicated path except for one Depth sufficient to hold them securely.
Dies gestattet es, die Konzentration der Diamantkörner im Werkzeug zu erhöhen, ihr Ausbrechen aus dem Werkzeug während des Betriebes zu vermeiden und dadurch die Betriebseigenschaften desselben zu verbessern.This allows the concentration of the diamond grains in the tool to increase their breaking out to avoid the tool during operation and thereby to improve the operational characteristics of the same.
Außerdem trägt die kurzzeitige Einwirkung des Schlagimpulses beim qualitätsgerechten Einbringen der Diamantkörner zur Erhöhung der Produktivität des Prozesses bei.In addition, the short-term impact of the stroke impacts when the quality of the diamond grains is introduced to increase the productivity of the process.
Das Aufbringen des Pulvermaterials auf die Rohlingsoberfläche kann durch freie Formung, durch Aufstäuben und mittels eines Netzes erfolgen. Dabei geschieht das Auftragen des Schleifpulvers auf den scheibenförmigen Rohling zweckmäßigerweise bei gleichzeitigem Formen desselben zu einem Kugelsegment mit einem Halbmesser, der den Ausgangshalbmesser des Rohlings um das 3- bis 10fache übersteigt. Dies ermöglicht es, die Diamantkörner im Rohling aufgrund plastischen Fließens des Rohlingsmetalls während des Einbringens fester anzubringen.Applying the powder material to the blank surface can by free shaping, by dusting and by means of a network. This is where the application takes place of the grinding powder on the disc-shaped blank expediently at the same time it is formed a spherical segment with a radius that is the starting radius of the blank exceeds 3 to 10 times. This makes it possible to due to the diamond grains in the blank plastic flow of the blank metal during insertion attach more firmly.
Über dem oberen Grenzwert des Segmenthalbmessers ist keine Verbesserung der Betriebseigenschaften des Werkzeuges zu verzeichnen, während bei Unterschreitung des unteren Grenzwertes es unmöglich wird, dem Rohling diese Form ohne Wellenbildung zu geben.Is above the upper limit of the segment radius no improvement in the operating properties of the tool recorded while falling below the lower limit it becomes impossible to shape the blank without undulation give.
Je nach der funktionalen Bestimmung des Werkzeuges gestattet es das Verfahren, Schleifpulver mit verschiedenem Gehalt an Diamantkörnern mit einem weiten Korngrößenbereich zu verwenden.Depending on the functional purpose of the tool allows the process to use grinding powder with various Diamond grain content with a wide grain size range to use.
Erfindungsgemäß wird vorgeschlagen, ein Schleifpulver folgender Zusammensetzung (Vol.%) zu verwenden:According to the invention, a grinding powder is proposed following composition (vol.%) to be used:
Diamantkörner20-60 leichtschmelzendes MetallRest.Diamond grains 20-60 easily melting metal residue.
Das leichtschmelzende Metall erfüllt bei der Strukturbildung des Werkzeugmaterials die Funktion eines Bindemittels, das Diamantkörner mit einer Größe von über 200- 250 µm fest anzubringen erlaubt.The light-melting metal fulfills the structure formation the function of the tool material as a binder, the diamond grains with a size of over 200 250 µm fixed allowed.
Ein ähnlicher Effekt wird auch beim vorherigen Plattieren der Rohlingsoberfläche mit einem leichtschmelzenden Metall erreicht. Dabei ist zu beachten, daß die Plattierschichtdicke nicht übersteigt, weil sonst der Effekt ihrer maximalen Eindringung in den Rohling nicht eintritt.A similar effect is also seen with the previous plating the blank surface with a slightly melting Metal reached. It should be noted that the cladding thickness not exceed, because otherwise the effect of their maximum penetration into the blank does not occur.
Nachstehend sind konkrete Ausführungsbeispiele des erfindungsgemäßen Verfahrens angeführt.Below are specific embodiments of the cited method according to the invention.
Man stellt Trennschleifscheiben zum Zersägen von Diamantkristallen her. Als Rohlinge werden Stahlscheiben mit einem Durchmesser von 80 mm und einer Dicke von 0,08 mm verwendet.Cut-off wheels for sawing diamond crystals are made forth. Steel disks are used as blanks a diameter of 80 mm and a thickness of 0.08 mm used.
Das Diamantpulver mit einer Körnigkeit von 20/16 µm wird mit Hilfe eines Klebers auf die Rohlingsoberfläche gleichmäßig aufgetragen. Der Rohling wird auf der Oberfläche eines vorher auf einer Kupferplatte angebrachten elastischen Elementes aus Polyurethan angeordnet. Hierbei sind das elastische Element und die Platte axial verschiebbar. In unmittelbarer Nähe der Kupferplatte wird ein flacher Induktor einer magnetischen Impulsanlage angeordnet. Über der Rohlingsoberfläche wird eine Platte aus einem Hartmetall von Typ WC-CO angebracht und in axiale Drehung mit einer Frequenz von 900-2500 s-1 versetzt. Danach erfolgt die Entladung des kapazitiven Speichers der magnetischen Impulsanlage auf den flachen Induktor, wodurch eine impulsartige Schlageinwirkung auf den Rohling mittels des elastischen Elements und der Kupferplatte gewährleistet wird. Die Schlagimpulsstärke erreicht 200-800 kN/s.The diamond powder with a granularity of 20/16 µm is evenly applied to the blank surface with the help of an adhesive. The blank is placed on the surface of a polyurethane elastic element previously attached to a copper plate. Here, the elastic element and the plate are axially displaceable. A flat inductor of a magnetic pulse system is arranged in the immediate vicinity of the copper plate. A plate made of a hard metal of the WC-CO type is attached above the blank surface and set in axial rotation at a frequency of 900-2500 s -1 . Then the capacitive memory of the magnetic pulse system is discharged onto the flat inductor, which ensures a pulsed impact on the blank by means of the elastic element and the copper plate. The impact pulse strength reaches 200-800 kN / s.
Aufgrund des Zusammenstosses des Rohlings mit der Hartmetallplatte wird das Eindringen der Diamantkörner in den Rohling und ihr Befestigen in diesem erreicht.Due to the collision of the blank with the hard metal plate the penetration of the diamond grains into the blank and achieved their attachment in this.
In der nachstehenden Tabelle 1 sind Betriebscharakteristiken der hergestellten Trennschleifscheiben je nach den Prozeßparametern angeführt. Table 1 below shows operational characteristics of the cut-off wheels produced depending on the Process parameters listed.
Man stellt Trennschleifscheiben zum Zersägen von Diamantkristallen her. Als Rohlinge werden Bronzescheiben mit einem Durchmesser von 50 mm und einer Wandstärke von 0,05 mm verwendet.Cut-off wheels for sawing diamond crystals are made forth. Bronze disks are used as blanks with a diameter of 50 mm and a wall thickness of 0.05 mm is used.
Das Diamantpulver wird auf die Rohlingsoberfläche nach der Methode der freien Formung gleichmäßig aufgetragen.The diamond powder is applied to the blank surface evenly applied using the free shaping method.
In einen Behälter mit beweglicher Kupferplatte werden ein Element aus Polyurethan und ein Rohling nacheinander eingebracht. Über dem Behälter ordnet man eine Hartmetallplatte mit konkaver sphärischer Oberfläche mit einem Halbmesser von 150 bis 500 mm an. Auf die Kupferplatte wirkt dann ein impulsartiges magnetisches Feld mit einer Stärke von 6.108 A/m ein.An element made of polyurethane and a blank are placed one after the other in a container with a movable copper plate. A hard metal plate with a concave spherical surface with a radius of 150 to 500 mm is arranged above the container. An impulsive magnetic field with a strength of 6.10 8 A / m then acts on the copper plate.
Dadurch wird dem Rohling eine Kugelsegmentform bei gleichzeitiger teilweiser Eindringung der Diamantkörner in denselben erteilt.This gives the blank a spherical segment shape simultaneous partial penetration of the diamond grains in granted the same.
Dann tauscht man die Platte mit sphärischem Profil gegen eine Platte mit flachem Profil aus, die mit einer Frequenz von 1000 s-1 rotiert, wonach erneut eine magnetische Impulseinwirkung auf die Kupferplatte erfolgt. Die Stärke des auf den Rohling wirkenden Schlagimpulses beträgt 450 kN/s.Then the plate with a spherical profile is exchanged for a plate with a flat profile that rotates at a frequency of 1000 s -1 , after which the copper plate is subjected to a magnetic impulse again. The strength of the impact pulse acting on the blank is 450 kN / s.
In der nachstehenden Tabelle 2 sind Betriebscharakteristiken der hergestellten Trennschleifscheiben je nach Halbmesser des Kugelsegmentes des Rohlings angeführt.Table 2 below shows operational characteristics of the cut-off wheels produced depending on Radius of the spherical segment of the blank.
Es werden Schleifscheiben zum Trennen von tafelförmigem Hartgewebe mit 40 mm Dicke hergestellt.There are grinding wheels for separating tabular Hard tissue made with a thickness of 40 mm.
Als Rohlinge werden Stahlscheiben mit einem Durchmesser von 200 mm und einer Dicke von 1,0 mm verwendet.Steel disks with a diameter are used as blanks of 200 mm and a thickness of 1.0 mm.
Ein Gemisch, das aus Diamantpulver mit einer Körnigkeit von 315/250 µm und Zinnpulver mit einer Teilchengröße von 300-320 µm besteht, wird auf die Rohlingsoberfläche gleichmäßig aufgestäubt. Über dem Rohling wird in unmittelbarer Nähe der Schleifpulverschicht eine flache Hartmetallplatte (WC-CO) angebracht und mit einer Frequenz von 1500 s-1 in Drehung versetzt. Auf den Rohling wirkt dann von der entgegengesetzten Seite her ein Schlagimpuls von 650 kN s ein, der durch eine Wasserschlaganlage erzeugt wird.A mixture consisting of diamond powder with a grain size of 315/250 µm and tin powder with a particle size of 300-320 µm is dusted evenly onto the blank surface. A flat hard metal plate (WC-CO) is placed over the blank in the immediate vicinity of the grinding powder layer and rotated at a frequency of 1500 s -1 . An impact pulse of 650 kN s, which is generated by a water hammer system, then acts on the blank from the opposite side.
Infolge des Zusammenstoßes des Rohlings mit der Hartmetallplatte wird das Eindringen der Diamantkörner in denselben gewährleistet. Das Festhalten der Diamantkörner im Rohling wird aufgrund ihres tiefen Eindringens und des eingeschmolzenen Zinns erreicht, das die Funktion eines Lötmittels erfüllt.As a result of the blank colliding with the hard metal plate the penetration of the diamond grains into them guaranteed. Holding the diamond grains in the Blank becomes due to its deep penetration and the melted Tin achieves the function of a solder Fulfills.
In der nachstehenden Tabelle 3 sind Betriebskenndaten der hergestellten Schleifscheiben je nach dem spezifischen Verhältnis von Diamantkörnern und Zinn bei einer Schnittgeschwindigkeit von 60 m/s und einer Zustellung von 0,6 mm je Umdrehung angeführt.Table 3 below shows operating characteristics of the grinding wheels produced depending on the specific Ratio of diamond grains to tin at a cutting speed of 60 m / s and an infeed of 0.6 mm each Revolution listed.
Es werden Scheiben zum Trennen von Hartgewebe mit 50 mm Dicke hergestellt.There are disks for cutting hard tissue with 50 mm thick.
Als Rohlinge werden Stahlscheiben mit einem Durchmesser von 200 mm und einer Dicke von1,0 mm verwendet. Vorher wurden die Rohlinge mit einer Zinnschicht mit einer Dicke von 18 µm plattiert. Das Gemenge, das aus einem Gemisch von Diamantpulvern mit einer Körnigkeit von 400/250 und einer Körnigkeit von 63/40 sowie aus Zinnpulver besteht (Verhältnis der Bestandteile im Gemenge jeweils 30 : 30 : 40), wird auf die Rohlingsoberfläche aufgetragen. Danach erfolgen Operationen, die den im Beispiel 3 beschriebenen ähnlich sind.Steel disks with a diameter are used as blanks of 200 mm and a thickness of 1.0 mm. Before the blanks with a layer of tin with a thickness of 18 microns plated. The batch consisting of a mixture of diamond powders with a grain size of 400/250 and a grain size of 63/40 and tin powder (ratio of the components in the batch 30: 30: 40), is on applied the blank surface. Then there are operations which are similar to those described in Example 3.
Die Verschleißfestigkeit der hergestellten Scheiben beträgt 0,83 mg/m2, die Bearbeitungsfläche des Hartgewebes - 9290 m2.The wear resistance of the disks produced is 0.83 mg / m 2 , the processing area of the hard tissue - 9290 m 2 .
Es werden Schleifscheiben zum Schleifen von Diamantkristallen hergestellt. Das Diamantpulver mit einer Körnigkeit von 50/40 µm wird auf einen stählernen Rohling aufgetragen. In unmittelbarer Nähe der mit dem Diamantpulver bedeckten Rohlingsoberfläche wird eine Hartmetallplatte (WC-CO) angebracht und mit einer Frequenz von 2200 s-1 in Drehung versetzt. Von der entgegengesetzten Seite her wirkt auf den Rohling ein Schlagimpuls von 750 kN/ ein, der durch eine Druckluftschlaganlage erzeugt wird.Grinding wheels for grinding diamond crystals are manufactured. The diamond powder with a grain size of 50/40 µm is applied to a steel blank. A hard metal plate (WC-CO) is attached in the immediate vicinity of the blank surface covered with the diamond powder and rotated at a frequency of 2200 s -1 . An impact pulse of 750 kN / acts on the blank from the opposite side, which is generated by a compressed air impact system.
Nach dem Zusammenstoß mit der rotierenden Platte bildet sich in der oberflächennahen Rohlingsschicht eine diamanthaltige Schicht mit einer Diamantkörnerkonzentration von bis 60 Vol.% aus.After collision with the rotating plate forms there is a diamond-containing layer in the near-surface blank layer Layer with a diamond grain concentration from up to 60 vol.%.
Das hergestellte Werkzeug besitzt eine Schleifintensität von 1,9-2,0 mg/min.The tool produced has a grinding intensity from 1.9-2.0 mg / min.
Claims (4)